Mechanical and electrochemical characterization of vanadium nitride (VN) thin films

Vanadium nitride (V-N) thin films were grown using a reactive d.c. magnetron sputtering process, from a vanadium target (99.999%) in an Ar/N₂ gas mixture at different deposition bias voltage. Films were deposited onto silicon (1 0 0) and RUS-3 steel substrates at 400 °C. Structural, compositional, mechanical and electrochemical characterizations were performed by X-ray diffraction (XRD), elastic forward analysis (EFA), nanoindentation, electrochemical impedance spectroscopy (EIS), and Tafel polarization curves, respectively. X-ray diffraction patterns show the presence of (1 1 1) and (2 0 0) crystallographic orientations associated to the V-N cubic phase. Nanoindentation measurements revealed that when the bias voltage increases from 0 V to −150 V the hardness and elastic modulus are increased from 11 GPa to 20 GPa and from 187 GPa to 221 GPa, respectively. EIS and Tafel curves showed that the corrosion rate of steel, coated with V-N single layer films deposited without bias voltage, diminishes 90% compared to the steel without this coating. On the other hand, when the V-N coating was deposited at the highest d.c. bias voltage (−150 V), the corrosion rate was greater than in the steel coated with zero-voltage (0 V) V-N films. This last result could be attributed to the formation of porosities produced by the ion bombardment during the deposition process.     

Enhanced ferroelectric properties of vanadium doped bismuth titanate (BTV) thin films grown by pulsed laser ablation technique

Bi_3.99Ti_2.97V_0.03O₁₂ (BTV) thin films were grown by pulsed laser deposition at substrate temperatures ranging between 650 and 750 °C. The structural phase, and orientation of the deposited films were investigated in order to understand the effect of the deposition parameters on the properties of the BTV films. As the substrate temperature was increased to 700 °C, the films started showing a tendency of assuming a c-axis preferred orientation, while at lower temperatures polycrystalline films were formed. The Au/BTV/Pt capacitor showed an interesting dependence of the remnant polarization (P_r) as well as dc leakage current values on the growth temperature. The film deposited at 675 °C showed a very large 2P_r of 42 μC cm⁻², which is the largest for BTV thin films among the values reported so far.     

Structure and properties of DLC–MoS2 thin films synthesized by BTIBD method

Diamond-like carbon (DLC)–MoS₂ composite thin films were synthesized using a biased target ion beam deposition (BTIBD) technique in which MoS₂ was produced by sputtering a MoS₂ target using Ar ion beams while DLC was deposited by ion beam deposition with CH₄ gas as carbon source. The structure and properties of the synthesized films were characterized by X-ray diffraction, X-ray absorption near edge structure (XANES), Raman spectroscopy, nanoindentation, ball-on-disk testing, and corrosion testing. The effect of MoS₂ target bias voltage, ranging from −200 to −800 V, on the structure and properties of the DLC–MoS₂ films was further investigated. The results showed that the hardness decreases from 9.1 GPa to 7 GPa, the Young?s modulus decreases from 100 GPa to 78 GPa, the coefficient of friction (COF) increases from 0.02 to 0.17, and the specific wear rate coefficient (k) increases from 5×10⁻⁷ to 5×10⁻⁶ mm³ N⁻¹ m⁻¹, with increasing the biasing voltage from 200 V to 800 V. Also, the corrosion resistance of the DLC–MoS₂ films decreased with the raise of biasing voltage. Comparing with the pure DLC and pure MoS₂ films, the DLC–MoS₂ films deposited at low biasing voltages showed better tribological properties including lower COF and k in ambient air environment.     

Infrared optical properties of Ba(Zr0.20Ti0.80)O3 and Ba(Zr0.30Ti0.70)O3 thin films prepared by sol-gel method

Ba(Zr_xTi_1−x)O₃ (BZT) (x = 0.20 and 0.30) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrate by sol-gel method. X-ray diffraction patterns show that the thin films have a good crystallinity. Optical properties of the films in the wavelength range of 2.5-12 μm are studied by infrared spectroscopic ellipsometry (IRSE). The optical constants of the BZT thin films are determined by fitting the IRSE data using a classical dispersion formula. As the wavelength increases, the refractive index decreases, while the extinction coefficients increase. The effective static ionic charges are derived, which are smaller than that in a purely ionic material for the BZT thin films.     

Enhanced ferroelectric properties of (Pb0.90La0.10)Ti0.975O3 multilayered thin films prepared by RF magnetron sputtering

The (Pb_0.90La_0.10)Ti_0.975O₃/PbTiO₃ (PLT/PT), PbTiO₃/(Pb_0.90La_0.10)Ti_0.975O₃/PbTiO₃ (PT/PLT/PT) multilayered thin films with a PbO_x buffer layer were in situ deposited by RF magnetron sputtering at the substrate temperature of 600 °C. With this method, highly (1 0 0)-oriented PLT/PT and PT/PLT/PT multilayered thin films were obtained. The PbO_x buffer layer leads to the (1 0 0) orientation of the films. The dielectric, ferroelectric and pyroelectric properties of the PLT multilayered thin films were investigated. It is found that highly (1 0 0)-oriented PT/PLT/PT multilayered thin films possess higher remnant polarization 2P_r (44.1 μC/cm²) and better pyroelectric coefficient at room temperature p (p = 2.425 × 10⁻⁸ C/cm² K) than these of PLT and PLT/PT thin films. These results indicate that the design of the PT/PLT/PT multilayered thin films with a PbO_x buffer layer should be an effective way to enhance the dielectric, ferroelectric and pyroelectric properties. The mechanism of the enhanced ferroelectric properties was also discussed.     

Optical properties of selenium-tellurium nanostructured thin film grown by thermal evaporation

Se-Te nanostructured thin films were deposited on glass substrates in the presence of oxygen and argon by thermal evaporation. The properties of Se-Te thin films strongly depend on the deposition method. During the process used, the substrate is cooled to a temperature of 77 K employing liquid nitrogen. The nanostructured thin films of Se_100−xTe_x (where x=4, 8 and 16) are deposited on glass substrate. The surface morphology of the deposited films was investigated through Scanning Electron Microscopy (SEM). The typical size of these nanostructures is in the range 40-100 nm and the length is of the order of several micrometers. The optical parameters i.e. optical gap (E_g), absorption coefficient (α), and extinction coefficient (k) are calculated in the wavelength range 190-1100 nm. It was found that the optical band gap decreased from 3.4 to 2.9 eV when Te concentration was increased in the Se_100−xTe_x nanostructured thin films. The large bandgap may be attributed to the decrease in particle size which clearly exhibits a quantum size effect. XRD analysis was performed to confirm glassy nature of the nanostructured thin films.     

C-V studies on metal-ferroelectric bismuth vanadate (Bi2VO5.5)-semiconductor structure

Ferroelectric bismuth vanadate Bi₂VO_5.5 (BVO) thin films have been successfully grown on p-type Si(100) substrate by using chemical solution decomposition (CSD) technique followed by rapid thermal annealing (RTA). The crystalline nature of the films has been studied by X-ray diffraction (XRD). Atomic force microscopy (AFM) was used to study the microstructure of the films. The dielectric properties of the films were studied. The capacitance-voltage characteristics have been studied in metal-ferroelectric-insulator-semiconductor (MFIS) configuration. The dielectric constant of BVO thin films formed on Si(100) is about 146 measured at a frequency of 100 kHz at room temperature. The capacitance-voltage plot of a Bi₂VO_5.5 MFIS capacitor subjected to a dc polarizing voltages shows a memory window of 1.42 V during a sweep of ±5 V gate bias. The flatband voltage (V_f) shifts towards the positive direction rather than negative direction. This leads to the asymmetric behavior of the C-V curve and decrease in memory window. The oxide trap density at a ramp rate of 0.2 V/s was estimated to be as high as 1.45×10¹² cm⁻².     

Effect of substrate bias voltages on the diffusion barrier properties of Zr-N films in Cu metallization

Zr-N diffusion barriers were deposited on the Si substrates by rf reactive magnetron sputtering under various substrate bias voltages. Cu films were subsequently sputtered onto the Zr-N films by dc pulse magnetron sputtering without breaking vacuum. The Cu/Zr-N/Si specimens were then annealed up to 650 °C in N₂ ambient for an hour. The effects of deposition bias on growth rate, film resistivity, microstructure, and diffusion barrier properties of Zr-N films were investigated. An increase in negative substrate bias resulted in a decrease in deposition rate together with a decrease in resistivity. It was found that the sheet resistances of Cu/Zr-N(−200 V)/Si contact system were lower than those of Cu/Zr-N(−50 V)/Si specimens after annealing at 650 °C. Cu/Zr-N(−200 V)/Si contact systems showed better thermal stability so that the Cu₃Si phase could not be detected.     

Exchange bias and negative magnetoresistance in [Co/Bi/Co]/IrMn thin films]

The artificial control of grain-boundary resistance and its contribution to magnetic and magneto-transport properties in [Co(3 nm)/Bi(2.5 nm)/Co(3 nm)]Ir₂₀Mn₈₀(12 nm) thin films that exhibit exchange bias is studied. Transverse magnetoresistance (MR) loops exhibit a negative MR in thin films grown by magnetron sputtering on Si/SiN_x(100 nm) substrates. This negative MR effect is of the giant-MR (GMR) type, although its magnitude is less than 1%. A considerable exchange bias (EB) effect is observed only at lower temperatures, where both, GMR and isothermal magnetization loops exhibit a shift of −600 Oe at 5 K.     

Structural and optical properties of a-Si1−xCx:H films synthesized by dc magnetron sputtering technique

Hydrogenated amorphous SiC films (a-Si_1−xC_x:H) were prepared by dc magnetron sputtering technique on p-type Si(1 0 0) and corning 9075 substrates at low temperature, by using 32 sprigs of silicon carbide (6H-SiC). The deposited a-Si_1−xC_x:H film was realized under a mixture of argon and hydrogen gases. The a-Si_1−xC_x:H films have been investigated by scanning electronic microscopy equipped with an EDS system (SEM-EDS), X-ray diffraction (XRD), secondary ions mass spectrometry (SIMS), Fourier transform infrared spectroscopy (FTIR), UV-vis-IR spectrophotometry, and photoluminescence (PL). XRD results showed that the deposited film was amorphous with a structure as a-Si_0.80C_0.20:H corresponding to 20 at.% carbon. The photoluminescence response of the samples was observed in the visible range at room temperature with two peaks centred at 463 nm (2.68 eV) and 542 nm (2.29 eV). In addition, the dependence of photoluminescence behaviour on film thickness for a certain carbon composition in hydrogenated amorphous SiC films (a-Si_1−xC_x:H) has been investigated.     

Enhanced ferroelectric property of (Pb0.95Ca0.05)(Nb0.02Zr0.80Ti0.20)O3 thin films prepared by RF magnetron sputtering

(Pb_0.95Ca_0.05)(Nb_0.02Zr_0.80Ti_0.20)O₃ [PCNZT] thin films were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by RF magnetron sputtering with and without a LaNiO₃ [LNO] buffer layer. Ca and Nb elements in PZT films enhance the ferroelectric property, LaNiO₃ buffer layer improves the crystal quality of the PCNZT thin films. PCNZT thin films possess better ferroelectric property than that of PZT films for Ca and Nb ion substitution, moreover, PCNZT thin films with a LNO buffer layer possess (1 0 0) orientation and good ferroelectric properties with high remnant polarization (P_r = 38.1 μC/cm²), and low coercive field (E_c = 65 kV/cm), which is also better than that of PCNZT thin films without a LNO buffer layer (P_r = 27.9 μC/cm², E_c = 74 kV/cm). The result shows that enhanced ferroelectric property of PZT films can be obtained by ion substitution and buffer layer.     

The influence of substrate temperature and annealing on the properties of pulsed laser-deposited YIG films on fused quartz substrate

Yttrium iron garnet (YIG) thin films were deposited on fused quartz substrate at different substrate temperatures (T_s) varying from room temperature (RT) to 850 °C using pulsed laser deposition (PLD) technique. All the films in the as-deposited state were X-ray amorphous and non-magnetic at RT. The film deposited at RT after annealing at temperatures T_a?700 °C showed both X-ray peaks and the magnetic order. The films deposited at higher T_s (500–850 °C) and then annealed at 700 °C resulted in better-quality films with higher 4πM_s value. The highest value of magnetization was for the sample deposited at 850 °C and annealed at 700 °C, which is 68% of the bulk 4πM_s value.     

Laser synthesis of semiconductor nanostructures with narrow band gap

Semiconductor nanostructures with narrow band gap were synthesized by means of laser chemical vapor deposition (LCVD) of elements from iron carbonyl vapors [Fe(CO)₅] under the action of Ar⁺ laser radiation (λ_L = 488 nm) on the Si substrate surface. The temperature dependence of the specific conductivity of these nanostructures in the form of thin films demonstrated typical semiconductor tendency and gave the possibility to calculate the band gap for intrinsic conductivity (E_g) and the band gap assigned for impurities (E_i), which were depended upon film thickness and applied electrical field. Analysis of deposited films with scanning electron microscopy (SEM) and atomic force microscopy (AFM) demonstrated their cluster structure with average size not more than 100 nm. Semiconductor properties of deposited nanostructures were stipulated with iron oxides in different oxidized phases according to X-ray photoelectron spectroscopy (XPS) analysis.These deposited nanostructures were irradiated with Q-switched YAG laser (λ_L = 1064 nm) at power density about 6 × 10⁷ W/cm². This irradiation resulted in the crystallization process of deposited films on the Si substrate surface. The crystallization process resulted in the synthesis of iron carbide-silicide (FeSi_2−xC_x) layer with semiconductor properties too. The width of the band gap E_g of the synthesized layer of iron carbide-silicide was less than for deposited films based on iron oxides Fe₂O_3−x (0 ≤ x ≤ 1).     

Analysis of the Ge1−xCx films deposited by MFMST

Ge_1−xC_x films deposited by using a medium frequency magnetron sputtering technique (MFMST) were analyzed with X-ray photoelectron and Raman spectroscopy. The deposited Ge_1−xC_x films consist of C, Ge, GeC and GeO_y. The GeC content in the Ge_1−xC_x films linearly decreases, and the C content linearly increases with increasing deposition temperature from 150 to 350 °C. The GeC content decreases from 11.6% at a substrate bias of 250 V to a lowest value of 9.6% at 350 V, then increases again to 10.4% at 450 V. While the C content increases from 49.0% at the bias of 250 V to a largest value of 58.0% at 350 V and then maintains this level at 450 V. It is found that selecting a bias parameter seems more effective than deposition temperature if we want to obtain a higher content of GeC in the deposited films. In addition, a new method is presented in this paper to estimate the changes of GeC content in the Ge_1−xC_x films by observing the shifts of Ge-Ge LO phonon peak in Raman spectra for the Ge_1−xC_x films. The related mechanism is also discussed in this paper.     

Stress induced preferred orientation and phase transition for ternary WCxNy thin films

We deposit ternary WC_xN_y thin films on Si (1 0 0) substrates at 500 °C using direct current (DC) reactive magnetron sputtering in a mixture of CH₄/N₂/Ar discharge, and explore the effects of substrate bias (V_b) on the intrinsic stress, preferred orientation and phase transition for the obtained films by virtue of X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and selective area electron diffraction (SAED). We find that with increasing the absolute value of V_b up to 200 V the carbon (x) and nitrogen (y) atom concentrations of WC_xN_y films keep almost constant with the values of 0.75 and 0.25, respectively. The XPS and SAED results, combined with the density-functional theory (DFT) calculations on the electronic structure of WC_0.75N_0.25, show our obtained WC_xN_y films are single-phase of carbonitrides. Furthermore, we find that the compressive stress sharply increases with increasing the absolute value of V_b, which leads to a pronounced change in the preferred orientation and phase structure for the film, in which a phase transition from cubic β-WC_xN_y to hexagonal α-WC_xN_y occurs as V_b is in the range of −40 to −120 V. In order to reveal the relationship between the stress and phase transition as well as preferred orientation, the DFT calculations are used to obtain the elastic constants for β-WC_xN_y and α-WC_xN_y. The calculated results show that the preferred orientation is dependent on the competition between strain energy and surface energy, and the phase transition can be attributed to a decrease in the strain energy.     

Effects of seed layer on the structure and property of zinc oxide thin films electrochemically deposited on ITO-coated glass

ZnO films with different morphologies were deposited on the ITO-coated glass substrate from zinc nitrate aqueous solution at 65 °C by a seed-layer assisted electrochemical deposition route. The seed layers were pre-deposited galvanostatically at different current densities (i_sl) ranging from −1.30 to −3.0 mA/cm², and the subsequent ZnO films had been done using the potentiostatic technique at the cathode potential of −1.0 V. Densities of nucleation centers in the seed layers varied with increasing the current density, and the ZnO films on them showed variable morphologies and optical properties. The uniform and compact nanocrystalline ZnO film with (0 0 2) preferential orientation was obtained on seed layer that was deposited under the current density (i_sl) of −1.68 mA/cm², which exhibited good optical performances.     

Electrochemical synthesis and optical properties of ZnO thin film on In2O3:Sn (ITO)-coated glass

ZnO thin films were electrochemically deposited onto the ITO-coated glass substrate from an electrolyte consisted of 0.1 M Zn(NO₃)₂ aqueous solution at 65 ± 1 °C. A compact ZnO film with (0 0 2) preferred orientation was obtained at the applied potential of −1.3 V for 1200 s. It was also found that the morphology of the ZnO films grown at the potential of −1.3 V was characterized of single or coalescent hexagonal platelets. However, the ZnO crystals grown at the potential of −2.0 V was changed to be a bimodal size distribution. The band gap energy of the as deposited ZnO films, about 3.5 eV, was independent of both the applied potential and the deposition time, respectively. The minor amount of Zn(OH)₂ might be co-deposited with the formation of ZnO revealed by the FT-IR spectroscopy. Three strategies to improve the ZnO crystal quality based on the photoluminescence properties were proposed in the paper, which were (a) adopting the lower deposition potential, (b) increasing the deposition time at a certain potential, and (c) annealing after as-deposition, respectively.     

Multiferroic properties of Bi0.8La0.2FeO3/CoFe2O4 multilayer thin films

Bi_0.8La_0.2FeO₃/CoFe₂O₄ (BLFO/CFO) multilayer thin films (totally 20 layers BLFO and 19 layers CFO) were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and transmission electron microscope measurements show that the films are polycrystalline and consisted of multilayered structure. Ferroelectric hysteresis loops with remnant polarization and saturated polarization of 4.2 and 13.3 μC/cm², respectively, were observed. On the other hand, the films show well-shaped magnetization hysteresis loops with saturated and remnant magnetization of 34.7 and 11.4 emu/cm³, respectively, which are significantly larger than pure BLFO thin films deposited under the same conditions. These results indicate that constructing epitaxial superlattice might be a promising way to fabricate multiferroics with improved properties.     

AlF3 film deposited by IAD with end-Hall ion source using SF6 as working gas

A novel and effective process to fabricate high quality fluoride thin films was presented. Aluminum fluoride films deposited by a conventional thermal evaporation with an ion-assisted deposition (IAD) using SF₆ as a working gas at around room temperature were investigated. In this study, the optimal voltage and current, 50 V and 0.25 A, were found according to the optical properties of the films: high refractive index (1.489 at 193 nm), low optical absorption and extinction coefficient (<10⁻⁴ at 193 nm) in the UV range. The physical properties of the film are high packing density and amorphous without columnar structure. It was proved that using SF₆ working gas in IAD process is a good choice and significantly improves the quality of AlF₃ films.     

Effect of growth time on the structure, Raman shift and photoluminescence of Al and Sb codoped ZnO nanorod ordered array thin films

Al and Sb codoped ZnO nanorod ordered array thin films have been deposited on glass substrate with a ZnO seed layer by hydrothermal method at different growth time. The effect of growth time on structure, Raman shift, and photoluminescence (PL) was studied. The thin films at growth time of 5 h consist of nanorods growth vertically oriented with ZnO seed layer, and the nanorods with an average diameter of 27.8 nm and a length of 1.02 μm consist of single crystalline wurtzite ZnO crystal and grow along [0 0 1] direction. Raman scattering analysis demonstrates that the thin films at the growth time of 5 h have great Raman shift of 15 cm⁻¹ to lower wavenumber and have low asymmetrical factor Г_a/Г_b of 1.17. Room temperature photoluminescence reveals that there is more donor-related PL in films with growth time of 5 h.