ITO/Au/ITO multilayer thin films for transparent conducting electrode applications

Transparent and conducting ITO/Au/ITO multilayered films were deposited without intentional substrate heating on polycarbonate (PC) substrate using a magnetron sputtering process. The thickness of ITO, Au and ITO metal films in the multilayered structure was constant at 50, 10 and 40 nm, respectively.Although the substrate temperature was kept constant at 70 °C, ITO/Au/ITO films were polycrystalline with an (1 1 0) X-ray diffraction peak, while single ITO films were amorphous. Surface roughness analysis indicated ITO films had a higher average roughness of 1.76 nm, than the ITO/Au/ITO film roughness of 0.51 nm. The optoelectrical properties of the ITO/Au/ITO films were dependent on the Au thin film, which affected the ITO film crystallinity. ITO/Au/ITO films on PC substrates were developed with a resistivity as low as 5.6 × 10⁻⁵ Ω cm and a high optical transmittance of 71.7%.     

Dependence of intermediated noble metals on the optical and electrical properties of ITO/metal/ITO multilayers

Sn doped In₂O₃ (ITO) single layer and a sandwich structure of ITO/metal/ITO (IMI) multilayer films were deposited on a polycarbonate substrate using radio-frequency and direct-current magnetron sputtering process without substrate heating. The intermediated metal films in the IMI structure were Au and Cu films and the thickness of each layer in the IMI films was kept constant at 50 nm/10 nm/40 nm. In this study, the ITO/Au/ITO films show the lowest resistivity of 5.6 × 10⁻⁵ Ω cm.However the films show the lower optical transmission of 71% at 550 nm than that (81%) of as deposited ITO films. The ITO/Cu/ITO films show an optical transmittance of 54% and electrical resistivity of 1.5 × 10⁻⁴ Ω cm. Only the ITO/Au/ITO films showed the diffraction peaks in the XRD pattern. The figure of merit indicated that the ITO/Au/ITO films performed better in a transparent conducting electrode than in ITO single layer films and ITO/Cu/ITO films.     

Properties of ITO–AZO bilayer thin films prepared by magnetron sputtering for applications in thin-film silicon solar cells

In this paper we study the electro-optical behavior and the application of indium–tin oxide (ITO) and aluminum-doped zinc oxide (AZO) bilayer thin films for silicon solar cells. ITO–AZO bilayer thin films were deposited on glass substrates using radio-frequency magnetron sputtering. The experimental results show that a decrease in the electrical resistivity of the ITO–AZO bilayer thin films has been achieved without significant degradation of optical properties. In the best case the resistivity of the bilayer films reached a minimum of 5.075×10^?4 Ω?cm when the thickness of the AZO buffer layer was 12 nm. The ITO–AZO bilayer films were applied as the front electrodes of amorphous silicon solar cells and the short-circuit current density of the solar cells was considerably increased.     

透光导电ITO膜的制备及其光电特性的研究

采用溶胶-凝胶方法制备ITO膜,并从制备工艺上研究了各种因素对ITO膜光电特性的影响.最后制出的ITO膜厚度约为50nm,在可见光区平均透射比达97%,最高达99.55%,电阻率在2.0Ω·cm左右,最低达到0.31Ω·cm.     

Fabrication and characterization of Pt intermediate transparent and conducting ITO/Pt/ITO multilayer films

Platinum intermediate transparent and conducting ITO/metal/ITO (IMI) multilayered films were deposited by RF and DC magnetron sputtering on polycarbonate substrates without intentional substrate heating. Changes in the microstructure and optoelectrical properties of the films were investigated with respect to the thickness of the intermediate Pt layer in the IMI films. The thickness of Pt film was varied from 5 to 20 nm.In XRD measurements, neither ITO single-layer films nor IMI multilayer films showed any characteristic diffraction peaks for In₂O₃ or SnO₂. Only a weak diffraction peak for Pt (1 1 1) was obtained in the XRD spectra. Thus, it can be concluded that the Pt-intermediated films in the IMI films did not affect the crystallinity of the ITO films. However, equivalent resistivity was dependent on the presence and thickness of the Pt-intermediated layer. It decreased as low as 3.3×10⁻⁴ Ω cm for ITO 50 nm/Pt 20 nm/ITO 30 nm films. Optical transmittance was also strongly influenced by the Pt-intermediated layer. As Pt thickness in the IMI films increased, optical transmittance decreased to as low as 30% for ITO 50 nm/Pt 20 nm/ITO 30 nm films.     

Rapid thermal annealing of ITO films

Tin-doped indium oxide (ITO) films with 200 nm thickness were deposited on glass substrates by DC magnetron sputtering at room temperature. And they were annealed by rapid thermal annealing (RTA) method in vacuum ambient at different temperature for 60 s. The effect of annealing temperature on the structural, electrical and optical properties of ITO films was investigated. As the RTA temperature increases, the resistivity of ITO films decreases dramatically, and the transmittance in the visible region increases obviously. The ITO film annealed at 600 °C by RTA in vacuum shows a resistivity of 1.6 × 10⁻⁴ Ω cm and a transmittance of 92%.     

Low temperature deposition of transparent conducting ITO/Au/ITO films by reactive magnetron sputtering

Transparent conducting indium tin oxide/Au/indium tin oxide (ITO) multilayered films were deposited on unheated polycarbonate substrates by magnetron sputtering. The thickness of the Au intermediated film varied from 5 to 20 nm. Changes in the microstructure, surface roughness and optoelectrical properties of the ITO/Au/ITO films were investigated with respect to the thickness of the Au intermediated layer. X-ray diffraction measurements of ITO single layer films did not show characteristic diffraction peaks, while ITO/Au/ITO films showed an In₂O₃ (2 2 2) characteristic diffraction peak. The optoelectrical properties of the films were also dependent on the presence and thickness of the Au thin film. The ITO 50 nm/Au 10 nm/ITO 40 nm films had a sheet resistance of 5.6 Ω/□ and an average optical transmittance of 72% in the visible wavelength range of 400-700 nm. Consequently, the crystallinity, which affects the optoelectrical properties of ITO films, can be enhanced with Au intermediated films.     

Pulsed Nd:YAG laser depositions of ITO and DLC films for OLED applications

Indium-tin oxide (ITO) films deposited on heated and non-heated glass substrates by a pulsed Nd:YAG laser at 355 nm and ∼2.5 J/cm² were used in the fabrication of simple organic light-emitting diodes (OLEDs), ITO/(PVK + Alq₃ + TPD)/Al. The ITO was deposited on heated glass substrates which possessed resistivity as low as ∼3 × 10⁻⁴ Ω cm, optical transmission as high as ∼92% and carrier concentration of about ∼5 × 10²⁰ cm⁻³, were comparable to the commercial ITO. Substrate heating transformed the ITO microstructure from amorphous to polycrystalline, as revealed by the XRD spectrum. While the polycrystalline ITO produced higher OLED brightness, it was still lower than that on the commercial ITO due to surface roughness. A DLC layer of ∼1.5 nm deposited on this ITO at laser fluence of >12.5 J/cm² improved its device brightness by suppressing the surface roughness effect.     

Highly transparent and conductive indium tin oxide thin films for solar cells grown by reactive thermal evaporation at low temperature

Transparent conductive tin-doped indium oxide (In₂O₃:Sn, ITO) thin films with various Sn-doping concentrations have been prepared using the low cost reactive thermal evaporation (RTE) technique at a low growth temperature of ~160 °C. The structural characteristics, optical and electrical properties of the ITO thin films were investigated. These polycrystalline ITO films exhibited preferential orientation along (222) plane and possessed low resistivities ranging from 3.51 to 5.71 × 10^?4 Ω cm. The decreased mobility was attributed to the scattering by ionized and neutral impurities at high doping concentrations. The optimized ITO thin film deposited with 6.0 wt% Sn-doping concentration exhibited a high average transparency of 87 % in the wavelength range of 380–900 nm and a low resistivity of 3.74 × 10^?4 Ω cm with a high Hall mobility of 47 cm² V^?1s^?1. A hydrogenated amorphous silicon and silicon–germanium (a-Si:H/a-SiGe:H) double-junction solar cell fabricated with the RTE-grown ITO electrodes presented a conversion efficiency of 10.51 %.     

Plasma-based sputtering of indium tin oxide for the application of photovoltaic cells

Transparent and conducting indium tin oxide (ITO) thin films were deposited on soda lime glass substrates by RF plasma magnetron sputtering at room temperature. The effect of thickness (100, 200 and 300?nm) on the physical (structural, optical, electrical) properties of ITO thin films was investigated systematically. It is observed that with an increase in thickness, the X-ray diffraction data indicate polycrystalline films with grain orientations predominantly along (222) and (400) directions; the average grain size increases from 10 to 30?nm; the optical band gap increases from 3.68 to 3.73?eV and the transmission decrease from 80% to 70% . Four-point probes show a low resistivity (2.4×10^?5?Ω?cm) values for film with a thickness 300?nm. Present work shows that the ITO is a promising transparent conductive oxide material for the solar cell application.     

Effect of substrate temperature on the growth of ITO thin films

Indium tin oxide (ITO) thin films were deposited onto glass substrates by rf magnetron sputtering of ITO target and the influence of substrate temperature on the properties of the films were investigated. The structural characteristics showed a dependence on the oxygen partial pressure during sputtering. Oxygen deficient films showed (4 0 0) plane texturing while oxygen-incorporated films were preferentially oriented in the [1 1 1] direction. ITO films with low resistivity of 2.05 × 10⁻³ Ω cm were deposited at relatively low substrate temperature (150 °C) which shows highest figure of merit of 2.84 × 10⁻³ square/Ω⋅     

Preparation and characterization of indium tin oxide films formed by oxygen ion beam assisted deposition

Indium tin oxide (ITO) films were produced by low-energy oxygen ion beam assisted electron-beam evaporation. The dependence of surface morphology, electrical and optical properties on evaporation rate, oxygen ion beam energy and density, as well as substrate temperatures was characterized by atomic force microscopy, X-ray photoelectron spectroscopy, Hall-effect and optical transmittance measurements. The results show that high-quality ITO films (resistivity of 7.0×10⁻⁴ Ω cm, optical transmittance above 85% at wavelength 550 nm, surface roughness of 0.6 nm in root mean square) can be obtained at room temperature.     

Characterization of dip-coated ITO films derived from nanoparticles synthesized by␣low-pressure spray pyrolysis

In₂O₃:Sn (Indium Tin Oxide; ITO) films were prepared from a sol solution with highly crystalline ITO nanoparticles (less than 20 nm in size with 10 at.% Sn) which had been prepared by low-pressure spray pyrolysis (LPSP) in a single step. The ITO sol solution was prepared by dispersing LPSP-prepared ITO nanoparticles into ultra pure water. The nanoparticle ITO film was deposited on a glass substrate using a dip-coating method and then annealed in air at various temperatures. The optical transmittances of the ITO films were measured by UV–Vis spectrometry, and the films were found to have a high transparency to visible light (in the case of a film thickness of 250 nm annealed at 400°C, the transparency was in excess of 95% over the range λ=450–800 nm, with a maximum value near 100% at wavelengths above λ=700 nm). The optical transmittances of the films were influenced by the size of the ITO particle used, the film thickness and the annealing temperature. The ITO films showed a minimum resistivity of 9.5×10⁻² Ω cm, and their resistivity was affected by both the ITO particle size and the annealing temperature used.     

Characteristic difference between ITO/ZrCu and ITO/Ag bi-layer films as transparent electrodes deposited on PET substrate

The metallic-glass film of ZrCu layer deposited by co-sputtering was utilized as the metallic layer in the bi-layer structure transparent conductive electrode of ITO/ZrCu (IZC) deposited on the PET substrate using magnetron sputtering at room temperature. In addition, the pure Ag metal layer was applied in the same structure of transparent conductive film, ITO/Ag, in comparison with the IZC film. The ZrCu layer could form a continuous and smooth film in thickness lower than 6 nm, compared with the island structure of pure Ag layer of the same thickness. The 30 nm ITO/3 nm ZrCu films could show the optical transmittance of 73% at 550 nm wavelength. The 30 nm ITO/12 nm ZrCu films could show the better sheet resistance of 20 Ω/sq, but it was still worse than that of the ITO/Ag films. It was suggested that an alloy system with lower resistivity and negative mixing heat between atoms might be another way to form a continuous layer in thickness lower than 6 nm for metal film.     

Effect of Al doping on structural,optical and electrical properties of SnO2 thin films synthesized by pulsed laser deposition

Aluminium-doped (Al = 0–5?wt.%) SnO₂ thin films with low-electrical resistivity and high optical transparency have been successfully synthesized by pulsed laser deposition technique at 500 °C. Structural, optical and electrical properties of the as-deposited and post-annealed thin films were investigated. X-ray diffraction patterns suggest that the films transform from crystalline to amorphous state with increasing aluminium content. The root mean square (R_q) surface roughness parameter, determined by atomic force microscopy decreases upon annealing of the as-deposited film. While resistivity of the film is the lowest (9.49 × 10^?4 Ω-cm) at a critical doping level of 1?wt.% Al, optical transparency is the highest (nearly 90%) in the as-deposited condition. Temperature dependence of the electrical resistivity suggests that the Mott’s variable range hopping process is the dominant carrier transport mechanism in the lower temperature range (40–135 K) for all the films whereas, thermally activated band conduction mechanism seems to account for conduction in the higher temperature region (200–300 K).     

Electrical, structural, and optical properties of ITO thin films prepared at room temperature by pulsed laser deposition

Indium tin oxide (ITO) thin films were prepared by pulsed laser deposition (PLD) on glass substrate at room temperature. Structural, optical, and electrical properties of these films were analyzed in order to investigate its dependence on oxygen pressure, and rapid thermal annealing (RTA) temperature. High quality ITO films with a low resistivity of 3.3 × 10⁻⁴ Ω cm and a transparency above 90% were able to be formed at an oxygen pressure of 2.0 Pa and an RTA temperature of 400 °C. A four-point probe method, X-ray diffraction (XRD), atomic force microscopy (AFM), and UV-NIR grating spectrometer are used to investigate the properties of ITO films.     

Chromium-doped diamond-like carbon films deposited by dual-pulsed laser deposition

Diamond-like carbon (DLC) and Cr-doped diamond-like carbon layers were studied. DLC and Cr-DLC were deposited on silicon and titanium substrates (Ti-6Al-4V) by dual-pulsed laser ablation using two KrF excimer lasers and two targets (graphite and chromium). The composition was analyzed using wavelength-dependent X-ray spectroscopy. The Cr content increased from 2.2 to 17.9 at%. The topology and surface properties as roughness of layers were studied using scanning electron microscopy and atomic force microscopy. With the chromium concentration increased the roughness and the number of droplets. Carbon and chromium bonds were determined by Raman spectroscopy. With an increase in chromium content the I _D/I _G ratio increased. Mechanical properties of DLC films with various chromium content were evaluated. Hardness (reduced Young’s modulus) was determined by nanoindentation and reached of 51 GPa (309 GPa). Films adhesion was studied using scratch test and with concentration of chromium increased up to 20 N.     

Laser annealing process of ITO thin films using beam shaping technology

In this study, we develop a laser annealing system for In₂O₃Sn (ITO) to carry out heat treatment on oxides with high melting temperature on substrates with low melting temperature. It is known that the working temperature of traditional heat treatments is usually limited by the melting point of the substrate materials. To overcome this problem, we apply a laser annealing technique to modify the film properties, and to measure the electrical and surface properties, we use Hall measurement, a four-point probe, and an atomic force microscope in our experiment. We will discuss how the annealing is affected by the laser machining parameters, including the beam profile, intensity distribution, laser spot overlap, and laser operation mode. We will further show through experimental results that the beam profile greatly affects the surface roughness of the ITO films. With the use of a uniform beam profile with proper laser intensity, the surface roughness and the sheet resistance of the ITO films can be reduced from 23 nm to 4.2 nm and from 417 Ω/sq to 400.4 Ω/sq, respectively.     

Preparation and characterization of nanocrystalline ITO thin films on glass and clay substrates by ion-beam sputter deposition method

Nanocrystalline indium tin oxide (ITO) thin films were prepared on clay-1 (Clay-TPP-LP-SA), clay-2 (Clay-TPP-SA) and glass substrates using ion-beam sputter deposition method. X-ray diffraction (XRD) patterns showed that the as-deposited ITO films on both clay-1 and clay-2 substrates were a mixture of amorphous and polycrystalline. But the as-deposited ITO films on glass substrates were polycrystalline. The surface morphologies of as-deposited ITO/glass has smooth surface; in contrast, ITO/clay-1 has rough surface. The surface roughnesses of ITO thin films on glass and clay-1 substrate were calculated as 4.3 and 83 nm, respectively. From the AFM and SEM analyses, the particle sizes of nanocrystalline ITO for a film thickness of 712 nm were calculated as 19.5 and 20 nm, respectively. Optical study showed that the optical transmittance of ITO/clay-2 was higher than that of ITO/clay-1. The sheet resistances of as-deposited ITO/clay-1 and ITO/clay-2 were calculated as 76.0 and 63.0 Ω/□, respectively. The figure of merit value for as-deposited ITO/clay-2 (12.70 × 10⁻³/Ω) was also higher than that of ITO/clay-1 (9.6 × 10⁻³/Ω), respectively. The flexibilities of ITO/clay-1 and ITO/clay-2 were evaluated as 13 and 12 mm, respectively. However, the ITO-coated clay-2 substrate showed much better optical and electrical properties as well as flexibility as compared to clay-1.     

Giant temperature coefficient of resistance in Co-doped ZnO thin films

A novel high-performance thermistor material based on Co-doped ZnO thin films is presented. The films were deposited by the pulsed laser deposition technique on Si (111) single-crystal substrates. The structural and electronic transport properties were correlated as a function of parameters such as substrate temperature and Co-doped content for Zn_1?x Co _x O (x=0.005,0.05,0.10 and 0.15) to prepare these films. The Zn_1?x Co _x O films were deposited at various substrate temperatures between 20 and 280 °C. A value of 20 %/K for the negative temperature coefficient of resistance (TCR) with a wide range near room temperature was obtained. It was found that both TCR vs. temperature behavior and TCR value were strongly affected by cobalt doping level and substrate temperature. In addition, a maximal TCR value of over 20 %?K^?1 having a resistivity value of 3.6 Ω?cm was observed in a Zn_0.9Co_0.1O film near 260 °C, which was deposited at 120 °C and shown to be amorphous by X-ray diffraction. The result proved that the optimal Co concentration could help us to achieve giant TCR in Co-doped ZnO films. Meanwhile, the resistivities of the films ranged from 0.4 to 270 Ω?cm. A Co-doped ZnO/Si film is a strong candidate of thermometric materials for non-cooling and high-performance bolometric applications.