A novel group of glycosphingolipids was identified in the nervous tissue and skin of the mollusc, Aplysia kurodai, which lacks gangliosides. More than 30 glycolipids were detected on HPTLC plates and the structures of 9 major glycolipids were determined. They were pentaosylglycosphingolipids and their common core structure was GalNAcα1→3Galβ1→4Glcβ1→1ceramide, except for one glycolipid in which Galβ of the core structure was replaced by Galα. 3-O-MeGalβ or 4-O-MeGlcNAcα or 3,4-O-carboxyethylideneGalβ was at their non-reducing ends. Galα or Fucα binds to Gal of the core structure at 2C as a side chain sugar. One to three 2-aminoethylphosphonic acids and/or phosphoethanolamine link to the glycolipids. Immunohistochemically, glycolipids having carboxyethylideneGal at their non-reducing ends were localized exclusively in nerve bundles. Glycolipids activated cAMP-dependent protein kinase in the rat brain and may directly activate cAMP-dependent protein kinase in a manner similar, but not identical, to that of cAMP. The biological functions of glycolipids may share neurobiological functions proposed for gangliosides in vertebrates.     

The investigation of room temperature ferromagnetism in (1 0 0) oriented BaNb2O6 PLD films on LaAlO3 (1 0 0) substrate

(1 0 0) oriented BaNb₂O₆ films have been successfully grown on LaAlO₃ (1 0 0) substrate at 750 °C or 450 °C in vacuum by pulsed laser deposition. The deposited BaNb₂O₆ PLD films exhibit room-temperature ferromagnetism. Ab initio calculations demonstrate that stoichiometric BaNb₂O₆ and that with barium vacancy are nonmagnetic, while oxygen and niobium vacancy can induce magnetism due to the spin-polarization of Nb s electrons and O p electrons respectively. Moreover, ferromagnetic coupling is energetically more favorable when two Nb/O vacancies are located third-nearest-neighbored. The observed room temperature ferromagnetism in BaNb₂O₆ films should be mainly induced by oxygen vacancies introduced during vacuum deposition, with certain contribution by Nb vacancies.     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.     

Epitaxial MoOx nanostructures on TiO2(1 1 0) obtained using thermal decomposition of Mo(CO)6

Stoichiometric and highly-defective TiO₂(1 1 0) surfaces (called as yellow and blue, respectively) were exposed to Mo(CO)₆ vapours in UHV and in a reactive O₂ atmosphere. In the case of yellow-TiO₂, an O₂ reactive atmosphere was necessary to obtain the Mo(CO)₆ decomposition at 450 °C with deposition of MoO_x nanostructures where, according to core level photoemission data, the Mo⁺⁴ state is predominant. In the case of blue-TiO₂ it was possible to obtain Mo deposition both in UHV and in an O₂ atmosphere. A high dose of Mo(CO)₆ in UHV on blue-TiO₂ allowed the deposition of a thick metallic Mo layer. An air treatment of this sample at 580 °C led to the elimination of Mo as MoO₃ and to the formation of a transformed layer of stoichiometry of Ti_(1−x)Mo_xO₂ (where x is close to 0.1) which, according to photoelectron diffraction data, can be described as a substitutional near-surface alloy, where Mo⁺⁴ ions are embedded into the titania lattice. This embedding procedure results in a stabilization of the Mo⁺⁴ ions, which are capable to survive to air exposure for a rather long period of time. After exposure of the blue-TiO₂(1 1 0) substrate to Mo(CO)₆ vapours at 450 °C in an O₂ atmosphere it was possible to obtain a MoO₂ epitaxial ultrathin layer, whose photoelectron diffraction data demonstrate that is pseudomorphic to the substrate.     

Effect of substrate temperature on the morphology, structural and optical properties of Zn1−xCoxO thin films

Zn_1−xCo_xO thin films with c-axis preferred orientation were deposited on sapphire (0 0 0 1) by pulsed laser deposition (PLD) technique at different substrate temperatures in an oxygen-deficient ambient. The effect of substrate temperature on the microstructure, morphology and the optical properties of the Zn_1−xCo_xO thin films was studied by means of X-ray diffraction (XRD), atomic force microscopy (AFM), UV-visible-NIR spectrophotometer, fluorescence spectrophotometer. The results showed that the crystallization of the films was promoted as substrate temperature rose. The structure of the samples was not distorted by the Co incorporating into ZnO lattice. The surface roughness of all samples decreased as substrate temperature increased. The Co concentration in the film was higher than in the target. Emission peak near band edge emission of ZnO from the PL spectra of the all samples was quenched because the dopant complexes acted as non-radiative centers. While three emission bands located at 409 nm (3.03 eV), 496 nm (2.5 eV) and 513 nm (2.4 eV) were, respectively, observed from the PL spectra of the four samples. The three emission bands were in relation to Zn interstitials, Zn vacancies and the complex of V_O and Zn_i (V_OZn_i). The quantity of the Zn interstitials maintained invariable basically, while the quantity of the V_OZn_i slightly decreased as substrate temperature increased.     

Confirmation of sable QTL that modifies the effects of the Ay allele on yellow coat color on mouse chromosome 1

F₁-A^y mice between RR (aabbCC) and C57BL/6J-A^y (A^yaBBCC) have a much darker yellow coat color than do C57BL/6J-A^y. Quantitative trait locus (QTL) analysis was carried out to identify genes responsible for the darker modification of the yellow coat color (this has been traditionally termed “sable”). A significant sable QTL was identified on chromosome 1 (Dmyaq4, LOD score 15.5 for lightness, and 13.4 for color difference), in a chromosomal position similar to that of Dmyaq2, a sable QTL previously identified in C3H/HeJ. Another significant sable QTL was identified on chromosome 4 (Dmyaq5, LOD score 5.6 for lightness, and 4.3 for color difference) near the tyrosinase-related protein 1 (Tyrp1) locus. The effect of Dmyaq5 was significant only in the presence of the RR allele at Dmyaq4, suggesting that the Dmyaq4 (as well as Dmyaq2) is a novel coat color gene that may act up-stream of Tyrp1 signaling to increase eumelanin production.     

Super strong nuclear force caused by migrating K? mesons - Revival of the Heitler-London-Heisenberg scheme in kaonic nuclear clusters

We have studied the structure of K⁻pp comprehensively by solving this threebody system in a variational method, starting from the Ansatz that the Λ(1405) resonance (≡Λ^*) is a K⁻p bound state. The structure of K⁻pp reveals a molecular feature, namely, the K⁻ in Λ^* as an “atomic center” plays a key role in producing strong covalent bonding with the other proton. We point out that strongly bound $\bar{K}$ nuclear systems are formed by “super strong” nuclear force due to migrating real bosonic particles $\bar{K}$ a la Heitler-London-Heisenberg, whereas the normal nuclear force is caused by mediating virtual mesons. We have shown that the elementary process, p + p → K⁺ + Λ^* + p, which occurs in a short impact parameter and with a large momentum transfer, leads to unusually large self-trapping of Λ^* by the involved proton, since the Λ^*-p system exists as a compact doorway state propagating to K⁻pp.     

Influence of the substrate material on the properties of pulsed laser deposited thin Li1+xMn2O4−δ films

Thin Li_1+xMn₂O_4−δ films were deposited on several substrate materials (stainless steel, p-doped silicon and glassy carbon) by pulsed laser deposition. To obtain the correct thin film stoichiometries, targets with a different amount of excess lithium were required (Li_1.03Mn₂O₄ + xLi₂O; x = 2.5 and 7.5 mol%). The resulting polycrystalline thin films were characterized with respect to their morphology and electrochemical activity. It was found that only thin Li_1+xMn₂O_4−δ films deposited on stainless steel and glassy carbon showed the typical insertion and deinsertion peaks of Li⁺ during cycling.     

High-throughput characterization of BixY3−xFe5O12 combinatorial thin films by magneto-optical imaging technique

Bi_xY_3−xFe₅O₁₂ thin films have been grown on GGG (Gd₃Ga₅O₁₂) (1 1 1) substrates by the combinatorial composition-spread techniques under substrate temperature (T_sub) ranging from 410 to 700 °C and O₂ pressure of 200 mTorr. In order to study the effect of substrates on the deposition of Bi_xY_3−xFe₅O₁₂ thin films, garnet substrates annealed at 1300 °C for 3 h were also used. Magneto-optical properties were characterized by our home-designed magneto-optical imaging system. From the maps of Faraday rotation angle θ_F, it was evident that the Faraday effect appears only when T_sub = 430-630 °C. θ_F reaches to the maximum value (∼6°/μm, λ = 632 nm) at 500 °C, and is proportional to the Bi contents. XRD and EPMA analyses showed that Bi ions are easier to substitute for Y sites and better crystallinity is obtained for annealed substrates than for commercial ones.     

Oxygen flux influence on the morphological, structural and optical properties of Zn1−xMgxO thin films grown by plasma-assisted molecular beam epitaxy

The Zn_1−xMg_xO thin films were grown on Al₂O₃ substrate with various O₂ flow rates by plasma-assisted molecular beam epitaxy (P-MBE). The growth conditions were optimized by the characterizations of morphology, structural and optical properties. The Mg content of the Zn_1−xMg_xO thin film increases monotonously with decreasing the oxygen flux. X-ray diffractometer (XRD) measurements show that all the thin films are preferred (0 0 2) orientated. By transmittance and absorption measurements, it was found that the band gap of the film decreases gradually with increasing oxygen flow rate. The surface morphology dependent on the oxygen flow rate was also studied by field emission scanning electron microscopy (FE-SEM). The surface roughness became significant with increasing oxygen flow rate, and the nanostructures were formed at the larger flow rate. The relationship between the morphology and the oxygen flow rate of Zn_1−xMg_xO films was discussed.     

Abnormal positive thermal expansion in Mo substituted ZrW2O8

ZrW₂O₈ displays the unusual property of an isotropic bulk contraction in volume as a function of temperature. We report here on the positive thermal expansion (PTE) property caused by substituting Mo for W sites in ZrW₂O₈ at room temperature. The room temperature crystal structure of ZrW_2−xMo_xO₈ compounds, which were synthesized using a low temperature route, could be divided into ordered phase with α-ZrW₂O₈ structure (0≤x≤0.5) and disordered phase with β-ZrW₂O₈ (0.5<x≤1.5) and c-ZrMo₂O₈ structure (1.5<x≤2). ZrW_2−xMo_xO₈ adopting β-ZrW₂O₈ structure shows abnormal PTE property at room temperature due to the existence of water molecules, while ZrW_2−xMo_xO₈ adopting the other two structures (α-ZrW₂O₈ and c-ZrMo₂O₈) shows negative thermal expansion (NTE) property from room temperature until decomposition for α-ZrW₂O₈ structure or trigonal phase transition for c-ZrMo₂O₈ structure. The reason lies in the fact that the oxygen migration caused by the Mo substitution leads to the re-arrangement of W(Mo)O₄ tetrahedra lying along the 3-fold axis, only particular W/Mo ratio (0.5<x≤1.5) produces a special crystal structure, which allows the entrance of water molecules.     

Physical and electrical characteristics of a high-k Yb2O3 gate dielectric

High-k ytterbium oxide (Yb₂O₃) gate dielectrics were deposited on Si substrate by reactive sputtering. The structural features of these films after postdeposition annealing treatment were studied by X-ray diffraction and X-ray photoelectron spectroscopy. It is found that the Yb₂O₃ gate dielectrics annealed at 700 °C exhibit a larger capacitance value, a lower frequency dispersion and a smaller hysteresis voltage in C-V curves compared with other annealing temperatures. They also show negligible charge trapping under high constant voltage stress. This phenomenon is mainly attributed to the decrease in the amorphous silica thickness.     

Chemical quenching of positronium in Fe2O3/Al2O3 catalysts

Fe₂O₃/Al₂O₃ catalysts were prepared by solid state reaction method using α-Fe₂O₃ and γ-Al₂O₃ nano powders. The microstructure and surface properties of the catalyst were studied using positron lifetime and coincidence Doppler broadening annihilation radiation measurements. The positron lifetime spectrum shows four components. The two long lifetimes τ₃ and τ₄ are attributed to positronium annihilation in two types of pores distributed inside Al₂O₃ grain and between the grains, respectively. With increasing Fe₂O₃ content from 3 wt% to 40 wt%, the lifetime τ₃ keeps nearly unchanged, while the longest lifetime τ₄ shows decrease from 96 ns to 64 ns. Its intensity decreases drastically from 24% to less than 8%. The Doppler broadening S parameter shows also a continuous decrease. Further analysis of the Doppler broadening spectra reveals a decrease in the p-Ps intensity with increasing Fe₂O₃ content, which rules out the possibility of spin-conversion of positronium. Therefore the decrease of τ₄ is most probably due to the chemical quenching reaction of positronium with Fe ions on the surface of the large pores.     

Exchange coupling behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe₂O₄ and ferrimagnetic oxide/ferromagnetic metal CoFe₂O₄/CoFe₂ nanocomposite. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupled. Two steps were followed to synthesize the bimagnetic CoFe₂O₄/CoFe₂ nanocomposite: (i) first, preparation of CoFe₂O₄ nanoparticles using a simple hydrothermal method, and (ii) second, reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe₂O₄ nanoparticles were investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50 K. The mean diameter of CoFe₂O₄ particles is about 16 nm. Mossbauer spectra revealed two sites for Fe³⁺. One site is related to Fe in an octahedral coordination and the other one to the Fe³⁺ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe₂O₄. TEM measurements of nanocomposite showed the formation of a thin shell of CoFe₂ on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of the nanocomposite showed a hysteresis loop that is characteristic of exchange coupled systems. A maximum energy product (BH)_max of 1.22 MGOe was achieved at room temperature for CoFe₂O₄/CoFe₂ nanocomposites, which is about 115% higher than the value obtained for CoFe₂O₄ precursor. The exchange coupling interaction and the enhancement of product (BH)_max in nanocomposite CoFe₂O₄/CoFe₂ are discussed.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Effect of nitrogen content on the properties of CrNxOyCz coating prepared by DC reactive magnetron sputtering

The CrN_xO_yC_z coatings were deposited by planar DC reactive magnetron sputtering onto AZ31 Mg alloy and high speed tool steel (HSTS) substrates at a substrate temperature of 200 °C. The effect of N₂ content on composition and structure of the CrN_xO_yC_z coatings was investigated. The structure of the CrN_xO_yC_z coatings was analyzed by a glancing angle X-ray diffraction (GXRD). The cross-section morphology and thickness of the CrN_xO_yC_z coatings were checked by a field emission scanning electron microscope (FESEM), and the composition profile and chemical state were carried out by an X-ray photoelectron spectroscopy (XPS). The experimental results showed that the structure and phase composition of the CrN_xO_yC_z coatings depended on N₂ content. The evolution of the structure of CrN_xO_yC_z coatings was consistent with CrN_x-based coatings, and the CrN_xO_yC_z coatings contained Cr₂O₃, CrO₂, CrO, Cr₃C₂, CrN_x (Cr, CrN, Cr₂N), as well as different chromium oxynitride. However, the carbide and oxynitride were oxidized after annealing.     

Rare-earth gate oxides for GaAs MOSFET application

Rare-earth oxide films for gate dielectric on n-GaAs have been investigated. The oxide films were e-beam evaporated on S-passivated GaAs, considering interfacial chemical bonding state and energy band structure. Rare-earth oxides such as Gd₂O₃, (Gd_xLa_1−x)₂O₃, and Gd-silicate were employed due to high resistivity and no chemical reaction with GaAs. Structural and bonding properties were characterized by X-ray photoemission, absorption, and diffraction. The electrical characteristics of metal-oxide-semiconductor (MOS) diodes were correlated with material properties and energy band structures to guarantee the feasibility for MOS field effect transistor (FET) application.Gd₂O₃ films were grown epitaxially on S-passivated GaAs (0 0 1) at 400 °C. The passivation induced a lowering of crystallization temperature with an epitaxial relationship of Gd₂O₃ (4 4 0) and GaAs (0 0 1). A better lattice matching relation between Gd₂O₃ and GaAs substrate was accomplished by the substitution of Gd with La, which has larger ionic radius. The in-plane relationship of (Gd_xLa_1−x)₂O₃ (4 4 0) with GaAs (0 0 1) was found and the epitaxial films showed an improved crystalline quality. Amorphous Gd-silicate film was synthesized by the incorporation of SiO₂ into Gd₂O₃. These amorphous Gd-silicate films excluded defect traps or current flow path due to grain boundaries and showed a relatively larger energy band gap dependent on the contents of SiO₂. Energy band parameters such as ΔE_C, ΔE_V, and E_g were effectively controlled by the film composition.     

Adsorption of SO2 on Li atoms deposited on MgO (1 0 0) surface: DFT calculations

The adsorption of sulfur dioxide molecule (SO₂) on Li atom deposited on the surfaces of metal oxide MgO (1 0 0) on both anionic and defect (F_s-center) sites located on various geometrical defects (terrace, edge and corner) has been studied using density functional theory (DFT) in combination with embedded cluster model. The adsorption energy (E_ads) of SO₂ molecule (S-atom down as well as O-atom down) in different positions on both of O⁻² and F_s sites is considered. The spin density (SD) distribution due to the presence of Li atom is discussed. The geometrical optimizations have been done for the additive materials and MgO substrate surfaces (terrace, edge and corner). The oxygen vacancy formation energies have been evaluated for MgO substrate surfaces. The ionization potential (IP) for defect free and defect containing of the MgO surfaces has been calculated. The adsorption properties of SO₂ are analyzed in terms of the E_ads, the electron donation (basicity), the elongation of S-O bond length and the atomic charges on adsorbed materials. The presence of the Li atom increases the catalytic effect of the anionic O⁻² site of MgO substrate surfaces (converted from physisorption to chemisorption). On the other hand, the presence of the Li atom decreases the catalytic effect of the F_s-site of MgO substrate surfaces. Generally, the SO₂ molecule is strongly adsorbed (chemisorption) on the MgO substrate surfaces containing F_s-center.     

Spectroscopy of X2Y4 (D2h) molecules: tensorial formalism adapted to the O(3)⊃D2h chain, Hamiltonian and transition moment operators

A tensorial formalism adapted to the case of the X₂Y₄ molecules with D_2h symmetry has been developed in the same way as in the previous works on XY₄ (T_d) and XY₆ (O_h) spherical tops and XY₅Z (C_4v) symmetric tops. Here, we use the O(3)⊃D_2h group chain. All the coupling coefficients and formulas for the computation of matrix elements are given for this chain and used in the case of the Hamiltonian and transition moment operators.