Synthesis of GaN phase by ion implantation

GaN phase is synthesized using systemic implantation of nitrogen ions of multiple energies (290, 130 and 50 keV) into Zn-doped GaAs (1 0 0) at room temperature and subsequent annealing at 850 °C for 30 min in Ar + H₂ atmosphere. The implanted doses of nitrogen ions are 5 × 10¹⁶ and 1 × 10¹⁷ ions-cm⁻². Glancing angle X-ray diffraction studies show that hexagonal phase of GaN were formed. The photoluminescence studies show the emission from the band edge as well as from point defects.     

Crystalline quality of 3C-SiC formed by high-fluence C-implanted Si

Carbon ions at 40 keV were implanted into (1 0 0) high-purity p-type silicon wafers at 400 °C to a fluence of 6.5 × 10¹⁷ ions/cm². Subsequent thermal annealing of the implanted samples was performed in a diffusion furnace at atmospheric pressure with inert nitrogen ambient at 1100 °C. Time-of-flight energy elastic recoil detection analysis (ToF-E ERDA) was used to investigate depth distributions of the implanted ions. Infrared transmittance (IR) and Raman scattering measurements were used to characterize the formation of SiC in the implanted Si substrate. X-ray diffraction analysis (XRD) was used to characterize the crystalline quality in the surface layer of the sample. The formation of 3C-SiC and its crystalline structure obtained from the above mentioned techniques was finally confirmed by transmission electron microscopy (TEM). The results show that 3C-SiC is directly formed during implantation, and that the subsequent high-temperature annealing enhances the quality of the poly-crystalline SiC.     

Structural and optical properties of Au-implanted ZnO films

The structural and luminescence related optical behaviours of Au ion implanted ZnO films grown by magnetic sputtering and their post implantation annealing behaviours in the temperature range of 100-700 °C have been investigated. Optical absorption and transmittance spectra of the films indicate that band edge of Au-implanted ZnO has shifted to high energy range and optical band gap has increased, because the sharp difference of thermal expansion induces the lattice mismatch between ZnO and SiO₂. PL spectra reveal that UV and visible luminescence bands of ZnO films can be improved after thermal annealing due to recovery of defects and Au ions incorporation. Importantly, green luminescence band of 530 nm has been only observed in the Au-implanted and subsequently annealed ZnO films and it enhances with the increasing annealing temperature, which can be related to Au atoms or clusters in ZnO films. Furthermore, X-ray photoelectron spectroscopy measurements reveal that the Au⁰ is dominant state in Au implanted and annealed ZnO films. Possible mechanisms, such as optical transitions of Au atoms or clusters and deep level luminescence of ZnO, have been proposed for green emission.     

Optical study of implantation damage recovery from Si-implanted GaN

Comprehensive and systematic optical activation studies of Si-implanted GaN grown on sapphire substrates have been made as a function of ion dose and anneal temperature. Silicon ions were implanted at 200 keV with doses ranging from 1×10¹³ to 5×10¹⁵ cm⁻² at room temperature. The samples were proximity cap annealed from 1250 to 1350 °C with a 500-Å-thick AlN cap in a nitrogen environment. The results of photoluminescence measurements made at 3 K show a very sharp neutral-donor-bound exciton peak along with a sharp donor-acceptor pair peak after annealing at 1350 °C for 20 s, indicating excellent implantation damage recovery. The results also indicate the AlN cap protected the implanted GaN layer very well during high temperature annealing without creating any significant anneal-induced damage. This observation is consistent with the electrical activation results for these samples.     

Room temperature magnetic properties of Fe and C implanted ZnO films

ZnO films prepared by radio frequency magnetron sputtering were singly or sequentially implanted with 120 keV Fe ions at a fluence of 5 × 10¹⁶ ions/cm² and 20 keV C ions at a fluence of 3 × 10¹⁵ ions/cm². Magnetic and optical properties as well as structures of the films have been investigated using various techniques. Magnetic measurements show that the as-deposited ZnO film presents room temperature ferromagnetism. Single Fe or C ion implantation has no contribution to enhancement in the film magnetism, while magnetic moment increases distinctly in the Fe and C ions sequentially implanted film. Results from structural measurements reveal that Fe nanoparticles are formed in the Fe singly implanted ZnO film. The post C implantation induces dissolution of Fe nanoparticles and promotes Fe atoms to substitute Zn atoms in the lattice. Based on the structural results, the effect of magnetic enhancement has been tentatively interpreted.     

Blue-cathodoluminescent layers synthesis by high-dose N, C and B SiO2 implantation

Thermal silicon oxide layers have been implanted at 600 °C with N⁺+C⁺, N⁺+B⁺ and N⁺+C⁺+B⁺ ions. Two different implantation doses have been chosen in order to introduce peak concentrations at the projected range comparable to the SiO₂ density. Some pieces of the samples have been annealed in conventional furnace at 1200 °C for 3 h. After annealing, cathodoluminescence measurements show in all cases a main broad band centered at 460 nm (2.7 eV). High doses of C implantation give rise to an intensity attenuation. Phases formed in the oxides have been investigated by Fourier transform infrared spectroscopy before and after annealing. The spectra suggest that N incorporates as BN and probably as a ternary BCN phase in the triply implanted samples, while C seems to bond mainly with B. Boron is also bonded to O in B-O-Si configuration. Depth structure and quantitative composition of the films were deduced from fittings of the spectroscopic ellipsometry measurements.     

Ferromagnetism in ZnO doped with Co by ion implantation

The importance of doping ZnO with magnetic ions is associated with the fact that this oxide is a good candidate for the formation of a magnetic-diluted semiconductor. Most of the studies reported in Co-doped ZnO were carried out in thin films, but the understanding of the modification of the magnetic behaviour due to doping demands the study of single-crystalline samples. In this work, ZnO single crystals were doped at room temperature with Co by ion implantation with fluences ranging between 2×10¹⁶ and 1×10¹⁷ ions cm⁻² and implantation energy of 100 keV. As implanted samples show a superparamagnetic behaviour attributed to the formation of Co clusters, room temperature ferromagnetism is attained after annealing at 800 °C, but no magnetoresistance was detected in the temperature range from 10 to 300 K.     

XPS investigation of ion beam induced conversion of GaAs(0 0 1) surface into GaN overlayer

For the advance of GaN based optoelectronic devices, one of the major barriers has been the high defect density in GaN thin films, due to lattice parameter and thermal expansion incompatibility with conventional substrates. Of late, efforts are focused in fine tuning epitaxial growth and in search for a low temperature method of forming low defect GaN with zincblende structure, by a method compatible to the molecular beam epitaxy process. In principle, to grow zincblende GaN the substrate should have four-fold symmetry and thus zincblende GaN has been prepared on several substrates including Si, 3C-SiC, GaP, MgO, and on GaAs(0 0 1). The iso-structure and a common shared element make the epitaxial growth of GaN on GaAs(0 0 1) feasible and useful. In this study ion-induced conversion of GaAs(0 0 1) surface into GaN at room temperature is optimized. At the outset a Ga-rich surface is formed by Ar⁺ ion bombardment. Nitrogen ion bombardment of the Ga-rich GaAs surface is performed by using 2-4 keV energy and fluence ranging from 3 × 10¹³ ions/cm² to 1 × 10¹⁸ ions/cm². Formation of surface GaN is manifested as chemical shift. In situ core level and true secondary electron emission spectra by X-ray photoelectron spectroscopy are monitored to observe the chemical and electronic property changes. Using XPS line shape analysis by deconvolution into chemical state, we report that 3 keV N₂⁺ ions and 7.2 × 10¹⁷ ions/cm² are the optimal energy and fluence, respectively, for the nitridation of GaAs(0 0 1) surface at room temperature. The measurement of electron emission of the interface shows the dependence of work function to the chemical composition of the interface. Depth profile study by using Ar⁺ ion sputtering, shows that a stoichiometric GaN of 1 nm thickness forms on the surface. This, room temperature and molecular beam epitaxy compatible, method of forming GaN temperature can serve as an excellent template for growing low defect GaN epitaxial overlayers.     

Effect of thermal treatment on linear optical properties of Cu nanoclusters

Silica glass was implanted with 50 keV Cu⁺ ions at various fluences from 6×10¹⁵ to 8×10¹⁶ ions/cm² and thermally-annealed in air between room temperature to 1200 °C. UV/visible spectroscopy measurements reveal absorption bands at characteristics surface plasmon resonance (SPR) frequencies, signifying the formation of copper colloids in silica, even without thermal treatments. Such copper nanoclusters can be attributed to the relatively high mobility of copper atoms, even at ambient conditions. Using the equation derived from the framework of free-electron theory, the average radii of the Cu particles were found to be in the range 2-4 nm from the experimental surface plasmon absorption peaks. Radioluminescence (RL) spectra exhibited broad bands at 410 and 530 nm, associated with the presence of Cu⁺ ions in the as-implanted samples. The effect of thermal annealing in air on absorption and emission spectra of these Cu-implanted samples, as well as the formation of copper nanoclusters from original Cu⁺ ions, is discussed.     

Epitaxial growth of Sc-doped ZnO films on Si by sol-gel route

The epitaxial growth of doped ZnO films is of great technological importance. Present paper reports a detailed investigation of Sc-doped ZnO films grown on (1 0 0) silicon p-type substrates. The films were deposited by sol-gel technique using zinc acetate dihydrate as precursor, 2-methoxyethanol as solvent and monoethanolamine (MEA) as a stabilizer. Scandium was introduced as dopant in the solution by taking 0.5 wt%¹ of scandium nitrate hexahydrate. The effect of annealing on structural and photoluminescence properties of nano-textured Sc-doped films was investigated in the temperature range of 300-550 °C. Structural investigations were carried out using X-ray diffraction, scanning electron microscopy and atomic force microscopy. X-ray diffraction study revealed that highly c-axis oriented films with full-width half maximum of 0.21° are obtained at an annealing temperature of 400 °C. The SEM images of ZnO:Sc films have revealed that coalescence of ZnO grains occurs due to annealing. Ostwald ripening was found to be the dominant mass transport mechanism in the coalescence process. A surface roughness of 4.7 nm and packing density of 0.93 were observed for the films annealed at 400 °C. Room temperature photoluminescence (PL) measurements of ZnO:Sc films annealed at 400 °C showed ultraviolet peak at about (382 nm) with FWHM of 141 meV, which are comparable to those found in high-quality ZnO films. The films annealed below or above 400 °C exhibited green emission as well. The presence of green emission has been correlated with the structural changes due to annealing. Reflection high energy electron diffraction pattern confirmed the nearly epitaxial growth of the films.     

Improvement of electrical and optical properties of Ga and N co-doped p-type ZnO thin films with thermal treatment

Ga and N co-doped p-type ZnO thin films were epitaxially grown on sapphire substrate using magnetron sputtering technique. The process of synthesized Ga and N co-doped ZnO films was performed in ambient gas of N₂O. Hall measurement shows a significant improvement of p-type characteristics with rapid thermal annealing (RTA) process in N₂ gas flow, where more N acceptors are activated. The film rapid thermal annealed at 900 °C in N₂ ambient revealed the highest carrier concentration of 9.36 × 10¹⁹ cm⁻³ and lowest resistivity of 1.39 × 10⁻¹ Ω cm. In room and low temperature photoluminescence measurements of the as grown and RTA treated film, donor acceptor pair emission and exciton bound to acceptor recombination at 3.25 and 3.357 eV, respectively, were observed.     

Analysis of the effect of annealing on the photoluminescence spectra of Cu ion implanted ZnS nanoparticles

In the present study, we report the photoluminescence (PL) study of nanoparticles of ZnS implanted with Cu⁺ ions at the doses of 5×10¹⁴, 1×10¹⁵ and 5×10¹⁵ ions/cm² and annealed at 200 and 300 °C. The photoluminescence spectra of the samples implanted at lower doses of 5×10¹⁴ and 1×10¹⁵ ions/cm² and annealed at 200 and 300 °C showed peaks at around 406, 418 and 485 nm. The PL emission peak at 485 nm was attributed to the transition of electrons from conduction band of ZnS to the impurity level formed by the implanted Cu⁺ ions. In the PL spectrum of the sample implanted at the highest dose of 5×10¹⁵ ions/cm², in addition to the emission peaks observed in the PL spectra of the samples implanted at lower doses, a peak at around 525 nm, the intensity of which decreased with increase in the annealing temperature, was observed. The emission peak at 525 nm was attributed to the transitions between sulfur and zinc vacancy levels. The full width at half maximum (FWHM) of the emission peak at 406 nm was observed to decrease with increase in annealing temperature, indicating lattice reconstruction. The observation of copper ion impurity related peak at 485 nm in the PL spectra of samples of the present study indicated that the doping of copper ions into the ZnS lattice is achievable by implanting Cu⁺ ions followed by annealing.     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

The morphology and optical properties of Cr-doped ZnO films grown using the magnetron co-sputtering method

Undoped ZnO and Zn_0.9Cr_0.1O films were prepared on Al₂O₃ (0 0 0 1) substrates using the magnetron co-sputtering technique. X-ray diffraction scans show that all films exhibit nearly single-phase wurtzite structure with c-axis orientation. Both chromium doping and growth ambient have a significant impact on the lattice constants and nucleation processes in ZnO film. A large quantity of subgrains (10 nm in size) has been observed on Zn_0.9Cr_0.1O film grown under Ar + O₂, while irregular plateau-like grains 40-50 nm in size were observed on Zn_0.9Cr_0.1O film grown under Ar + N₂. The ultraviolet-visible transmittance and optical bandgap of all films were also examined. The photoluminescence spectra of all films exhibit a broad emission located around 400 nm, which is composed of one weak ultraviolet luminescence and another rather intense near-violet one, as determined by Gaussian peak fitting. The near-violet emission centered on 400 nm might originate from the electron transition between the band tail state levels of surface defects and/or lattice imperfection in the ZnO film.     

Surface treatments toward obtaining clean GaN(0 0 0 1) from commercial hydride vapor phase epitaxy and metal-organic chemical vapor deposition substrates in ultrahigh vacuum

We studied processes of cleaning GaN(0 0 0 1) surfaces on four different types of wafers: two types were hydride vapor phase epitaxy (HVPE) free-standing substrates and two types were metal-organic chemical vapor deposition (MOCVD) films grown on these HVPE substrates and prepared by annealing and/or Ar ion sputtering in ultra high vacuum. We observed the surfaces through treatments using in situ low-energy electron diffraction (LEED), reflection high-energy electron diffraction (RHEED), scanning tunneling microscopy (STM), and Auger electron spectroscopy, and also using ex situ temperature programmed desorption, X-ray photoelectron spectroscopy, X-ray diffraction, and secondary ion mass spectrometry. For HVPE samples, we obtained relatively clean surfaces under optimized three-step annealing conditions (200 °C for 12 h + 400 °C for 1 h + 500 °C for 5 min) without sputtering, after which the surface contamination of oxide and carbide was reduced to ∼20% of that before annealing. Clear GaN(0 0 0 1)1×1 patterns were obtained by LEED and RHEED. STM images showed flat terraces of ∼10 nm size and steps of ∼0.5 nm height. Upon annealing the HVPE-GaN samples at a much higher temperature (C), three-dimensional (3D) islands with facets were formed and the surface stoichiometry was broken down with the desorption of nitrogen in the form of ammonia, since the samples include hydrogen as an impurity. Ar⁺ sputtering was effective for removing surface contamination, however, postannealing could not recover the surface roughness but promoted the formation of 3D islands on the surface. For MOCVD/HVPE homoepitaxial samples, the surfaces are terminated by hydrogen and the as-introduced samples showed a clear 1×1 structure. Upon annealing at 500-600 °C, the surface hydrogen was removed and a 3×3 reconstruction structure partially appeared, although a 1×1 structure was dominant. We summarize the structure differences among the samples under the same treatment and clarify the effect of crystal quality, such as dislocations, the concentration of hydrogen impurities, and the residual reactant molecules in GaN films, on the surface structure.     

Luminescence properties of Tb implanted ZnO

ZnO [0 0 0 1] crystals were irradiated at room temperature with Tb⁺ ions of 400 keV with fluences from 1×10¹⁶ to 2×10¹⁷ cm⁻². The implanted layer was examined by several methods, including radioluminescence (RL), Rutherford backscattering spectrometry (RBS) and optical spectroscopy. The optical extinction spectra were simulated using Mie scattering theory. Absorption spectra predicted by Mie theory for particles of decreasing diameter were compared with those obtained experimentally. Some qualitative agreement between theoretical and experimental data was achieved. It was also shown that the intensities of the characteristic green emission bands associated with Tb produced by ⁵D₄→⁷F_j=5,4 transitions have increased about 8 times after annealing. Optical spectroscopy and radioluminescence data have revealed that the ion implantation is a promising tool for synthesizing Tb nanoparticles in the ZnO surface. The Tb nanoparticles exhibit a rather weak plasma resonance.     

Study of nitrogen ion implantation and diffusion phenomena on thin chromium layers followed by the atomic force microscopy and secondary ion mass spectroscopy techniques characterization

This research investigates the effect of ion implantation dosage level and further thermal treatment on the physical characteristics of chromium coatings on Si(1 1 1) substrates. Chromium films had been exposed to nitrogen ion fluencies of 1 × 10¹⁷, 3 × 10¹⁷, 6 × 10¹⁷ and 10 × 10¹⁷ N⁺ cm⁻² with a 15 keV energy level. Obtained samples had been heat treated at 450 °C at a pressure of 2 × 10⁻² Torr in an argon atmosphere for 30 h. Atomic force microscopy (AFM) images showed significant increase in surface roughness as a result of nitrogen ion fluence increase. Secondary ion mass spectroscopy (SIMS) studies revealed a clear increased accumulation of Cr₂N phase near the surface as a result of higher N⁺ fluence. XRD patterns showed preferred growth of [0 0 2] and [1 1 1] planes of Cr₂N phase as a result of higher ion implantation fluence. These results had been explained based on the nucleation-growth of Cr₂N phase and nitrogen atoms diffusion history during the thermal treatment process.     

Change of sheet resistance of high purity alumina ceramics implanted by Cu and Ti ions

High purity alumina ceramics (99% Al₂O₃) was implanted by copper ion and titanium ion in a metal vapour vacuum arc (MEVVA) implanter, respectively. The influence of implantation parameters was studied varying ion fluence. The samples were implanted by 68 keV Cu ion and 82 keV Ti ion with fluences from 1 × 10¹⁵ to 1 × 10¹⁸ ions/cm², respectively. The as-implanted samples were investigated by scanning electron microscopy (SEM), glancing X-ray diffraction (GXRD), scanning Auger microscopy (SAM), and four-probe method. Different morphologies were observed on the surfaces of the as-implanted samples and clearly related to implantation parameters. For both ion implantations, the sheet resistances of the alumina samples implanted with Cu and Ti ion fluences of 1 × 10¹⁸ ions/cm², respectively, reached the corresponding minimum values because of the surface metallization. The experimental results indicate that the high-fluence ion implantation resulted in conductive layer on the surface of the as-implanted high purity alumina ceramics.     

Rapid thermal annealing induced changes on the contact of Ni/Au to N-doped ZnO

N-doped p-type ZnO (p ∼ 10¹⁸cm^-3) was grown on sapphire(0 0 0 1) substrate by metal-organic chemical vapor deposition method. Ni/Au metal was evaporated on the ZnO film to form contacts. As-deposited contacts were rectifying while ohmic behavior was achieved after thermally annealing the contacts in nitrogen environment. Specific contact resistance was determined by circular transmission line method and a minimum specific contact resistance of 8 × 10⁻⁴ Ω cm² was obtained for the sample annealed at 650 °C for 30 s. However, Hall effect measurements indicate that, as the rapid thermal annealing temperature increased up to 550 °C or higher the samples’ conductive type have changed from p-type to n-type, which may be due to the instability nature of the present-day p-type N-doped ZnO or the dissociation of ZnO caused by annealing process in N₂ ambient. Evolution of the sample's electric characteristics and the increment of metal/semiconductor interface states induced by rapid thermal annealing process are supposed to be responsible for the improvement of electrical properties of Au/Ni/ZnO.     

Ripple topography on thin ZnO films by grazing and oblique incidence ion sputtering

We have investigated the formation and growth of nano sized ripple topography on ZnO thin films by 10 keV O¹⁺ bombardment at impact angles of 80° and 60°, varying the ion fluence from 5 × 10¹⁶ to 1 × 10¹⁸ ions/cm². At 80° the ripples are oriented along the ion beam direction whereas at 60° it is perpendicular to the ion beam direction. The developed ion induced structures are characterized by atomic force microscopy (AFM) and the alignment, variation of rms roughness, wavelength and correlation length of the structures are discussed with the existing model and basic concept of ion surface interaction.