Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Effects of gold catalysts and thermal evaporation method modifications on the growth process of Zn1−xMgxO nanowires

In this paper, we investigate the roles of gold catalysts and thermal evaporation method modifications in the growth process of Zn_1−xMg_xO nanowires. Zn_1−xMg_xO nanowires are fabricated on silicon substrates with and without using a gold catalyst. Characterizations reveal that Mg acts in a self-catalyst role during the growth process of Zn_1−xMg_xO nanowires grown on catalyst-free substrate. The optical properties and crystalline quality of the Zn_1−xMg_xO nanowires are characterized by room temperature photoluminescence (PL) measurements and Raman spectroscopy, respectively. The Raman and PL studies demonstrate that the Zn_1−xMg_xO nanowires grown using the catalyst-free method have good crystallinity with excellent optical properties and have a larger band-gap in comparison to those grown with the assistance of gold.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Defect structure of Sb2−xMnxTe3 single crystals

Incorporation of the transition metal elements in the tetradymite structure of Sb₂Te₃ has a strong influence on electronic properties. Recent studies have indicated that Mn substitutes on the Sb sublattice increases the carrier concentration of holes. However, the doping efficiency of Mn appears rather low in comparison to what it should be based on the measurements of magnetization, structural analysis, and transport properties. In this paper we address this issue by making detailed studies of the Hall effect and electrical resistivity and we explain the results with the aid of a model that takes into account interactions of the Mn impurity with the native defects in antimony telluride. Specifically, we find that Mn atoms interact with antisite defects (antimony atoms located on the tellurium sublattice), a process that decreases the density of antisite centers and generates free electrons. These, in turn, recombine with holes and thus decrease their concentration and the apparent Mn doping efficiency.     

Electrical properties and sulfur tolerance of La0.75Sr0.25Cr1−xMnxO3 under anodic conditions

Complex metal oxides with composition of La_0.75Sr_0.25Cr_1−xMn_xO₃(x=0.4,0.5,0.6) (LSCM) have been synthesized and examined as anode materials for solid oxide fuel cells (SOFCs). LSCM compositions show excellent tolerance to both reduction and oxidation but the crystal structure transforms from hexagonal in air to orthorhombic in H₂. The volume change associated with this phase transformation is only about 1%, thus having little effect on other properties. The total electrical conductivity increases with the content of Mn, whereas the resistance to sulfur poisoning increases with the content of Cr. Fuel cells using LSCM as the anode show very good performance when pure hydrogen is used as the fuel. However, they do not appear to be stable in fuels containing 10% of H₂S.     

Thermochemistry of Li1+xMn2−xO4 (0?x?1/3) spinel

Lithium substituted Li_1+xMn_2−xO₄ spinel samples in the entire solid solution range (0?x?1/3) were synthesized by solid-state reaction. The samples with x<0.25 are stoichiometric and those with x?0.25 are oxygen deficient. High-temperature oxide melt solution calorimetry in molten 3Na₂O·4MoO₃ at 974 K was performed to determine their enthalpies of formation from constituent binary oxides at 298 K. The cubic lattice parameter was determined from least-squares fitting of powder XRD data. The variations of the enthalpy of formation from oxides and the lattice parameter with x follow similar trends. The enthalpy of formation from oxides becomes more exothermic with x for stoichiometric compounds (x<0.25) and deviates endothermically from this trend for oxygen-deficient samples (x?0.25). This energetic trend is related to two competing substitution mechanisms of lithium for manganese (oxidation of Mn³⁺ to Mn⁴⁺ versus formation of oxygen vacancies). For stoichiometric spinels, the oxidation of Mn³⁺ to Mn⁴⁺ is dominant, whereas for oxygen-deficient compounds both mechanisms are operative. The endothermic deviation is ascribed to the large endothermic enthalpy of reduction.     

Synthesis and characterization of metal substituted AlxCr1−x(acetylacetonate)3 single-source precursors for their application to MOCVD of thin films

A detailed study, involving the synthesis of a single-source precursor containing two metal ions sharing the same crystallographic site, has been undertaken to elucidate the use of such a single-source precursor in a CVD process for growing thin films of oxides comprising these two metals, ensuring a uniform composition and distribution of metal ions. The substituted complexes Cr_1−xAl_x(acac)₃, where acac = acetylacetonate, have been prepared by a co-synthesis method, and characterized using UV–Vis spectroscopy, TGA/DTA measurements, and single crystal X-ray diffraction at low temperature. All the studied compositions crystallize in the monoclinic space group P2₁/c with Z = 4 in the unit cell. It was observed that the ratio (Al:Cr) of the site occupancy for the metal ions, obtained from single crystal refinement, is in agreement with the results obtained from complexometric titrations. All the solid state structures have the metal in an octahedral environment forming six-membered chelate rings. M–O acac bond lengths and disorder in the terminal carbon have been studied in detail for these substituted metal–organic complexes. One composition among these was chosen to evaluate their suitability as a single-source precursor in a LPMOCVD process (low-pressure metal–organic chemical vapour deposition) for the deposition of a substituted binary metal oxide thin film. The resulting thin films were characterized by X-ray diffraction, scanning electron microscopy, and infrared spectroscopy.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

Local environment in Ba2In2−xWxO5+3x/2 oxide ion conductors

The actual oxygen environment of the tungsten dopant in the Ba₂In_2−xW_xO_5+3x/2 solid solution was revealed by combining X-ray absorption spectroscopy at the tungsten L_I and L_III edges and at the indium L_I edge. Whatever the substitution ratio, the tungsten atoms exhibit a regular octahedral environment. When the substitution ratio increases, the oxygen vacancies are progressively filled until their total occupancy for x=2/3. For x?0.3, the perovskite structure is stabilised; the tungsten atoms are randomly distributed in the structure. Although X-ray diffraction revealed a cubic symmetry for these compositions, a local distortion of the indium environment is observed when a tungsten atom is in its surrounding.     

Formation of crystalline TiO2−xNx and its photocatalytic activity

Amorphous precursors to nitrogen-doped TiO₂ (NTP) and pure TiO₂ (ATP) powders were synthesized by hydrolytic synthesis and sol-gel method (SGM), respectively. Corresponding crystalline phases were obtained by thermally induced transformation of these amorphous powders. From FT-IR and XPS data, it was concluded that a complex containing titanium and ammonia was formed in the precipitate stage while calcination drove weakly adsorbed ammonium species off the surface, decomposed ammonia bound on surface of precipitated powder and led to substitution of nitrogen atom into the lattice of TiO₂ during the crystallization. The activation energies required for grain growth in amorphous TiO_2−xN_x and TiO₂ samples were determined to be 1.6 and 1.7 kJ/mol, respectively. Those required for the phase transformation from amorphous to crystalline TiO_2−xN_x and TiO₂ were determined to be 129 and 142 kJ/mol, respectively. A relatively low temperature was required for the phase transformation in NTP sample than in ATP sample. The fabricated N-doped TiO₂ photocatalyst absorbed the visible light showing two absorption edges; one in UV range due to titanium oxide as the main edge and the other due to nitrogen doping as a small shoulder. TiO_2−xN_x photocatalyst demonstrated its photoactivity for photocurrent generation and decomposition of 2-propanol (IPA) under visible light irradiation ().     

New synthesis of excellent visible-light TiO2−xNx photocatalyst using a very simple method

An excellent visible-light-responsive (from 400 to 550 nm) TiO_2−xN_x photocatalyst was prepared by a simple wet method. Hydrazine was used as a new nitrogen resource in this paper. Self-made amorphous titanium dioxide precursor powders were dipped into hydrazine hydrate, and calcined at low temperature (110 °C) in the air. The TiO_2−xN_x was successfully synthesized, following by spontaneous combustion. The photocatalyst was characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), transmission electron microscope (TEM), UV-Vis diffuse reflectance spectrometer (DRS), and X-ray photoelectron spectroscopy (XPS). Analysis of XPS indicated that N atoms were incorporated into the lattice of the titania crystal during the combustion of hydrazine on the surface of TiO₂. Ethylene was selected as a target pollutant under visible-light excitation to evaluate the activity of this photocatalyst. The newly prepared TiO_2−xN_x photocatalyst with strong photocatalytic activity and high photochemical stability under visible-light irradiation was firstly demonstrated in the experiment.     

Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Evolution of structure and magnetic properties in electron-doped double perovskites, Sr2−xLaxMnWO6 (0?x?1)

Powder neutron and X-ray diffraction studies show that the double perovskites in the region 0?x?1 exhibit two crystallographic modifications at room temperature: monoclinic P2₁/n and tetragonal I4/m, with a boundary at 0.75<x<0.9. Magnetic susceptibility measurements indicate that for x=0 and 0.5 Sr_2−xLa_xMnWO₆ orders antiferromagnetically (AFM) at 15 and 25 K, respectively, for 0.75?x<1.0, a contribution of weak ferromagnetism (FM), probably due to canted-AFM order, increases with increasing x. The end point compound SrLaMnWO₆ shows the strongest FM cluster effect; however, no clear evidence of magnetic order is discernable down to 4.2 K. X-ray absorption spectroscopy (XAS) confirms Mn²⁺ and mixed-valent W^6+/5+ formal oxidation states in Sr_2−xLa_xMnWO₆.     

Crystal structures of RPt3−xSi1−y(R=Y, Tb, Dy, Ho, Er, Tm, Yb) studied by single crystal X-ray diffraction

The crystal structures of ternary compounds RPt_3−xSi_1−y(R=Y, Tb, Dy, Ho, Er, Tm, Yb) have been elucidated from X-ray single crystal CCD data. All compounds are isotypic and crystallize in the tetragonal space group P4/mbm. The general formula RPt_3−xSi_1−y arises from defects: x≈0.20, y≈0.14. The crystal structure of RPt_3−xSi_1−y can be considered as a packing of four types of building blocks which derive from the CePt₃B-type unit cell by various degrees of distortion and Pt, Si-defects.     

Visible light-sensitive yellow TiO2−xNx and Fe-N co-doped Ti1−yFeyO2−xNx anatase photocatalysts

Nitrogen substituted yellow colored anatase TiO_2−xN_x and Fe-N co-doped Ti_1−yFe_yO_2−xN_x have been easily synthesized by novel hydrazine method. White anatase TiO_2−δ and N/Fe-N-doped samples are semiconducting and the presence of ESR signals at g ∼1.994-2.0025 supports the oxygen vacancy and g∼4.3 indicates Fe³⁺ in the lattice. TiO_2−xN_x has higher conductivity than TiO_2−x and Fe/Fe-N-doped anatase and the UV absorption edge of white TiO_2−x extends in the visible region in N, Fe and Fe-N co-doped TiO₂, which show, respectively, two band gaps at ∼3.25/2.63, ∼3.31/2.44 and 2.8/2.44 eV. An activation energy of ∼1.8 eV is observed in Arrhenius log resistivity vs. 1/T plots for all samples. All TiO₂ and Fe-doped TiO₂ show low 2-propanol photodegradation activity but have significant NO photodestruction capability, both in UV and visible regions, while standard Degussa P-25 is incapable in destroying NO in the visible region The mid-gap levels that these N and Fe-N-doped TiO₂ consist may cause this discrepancy in their photocatalytic activities.     

Composition-induced structural phase transitions in the (Ba1−xLax)2In2O5+x (0?x?0.6) system

Composition-induced structural phase changes across the high temperature, fast oxide ion conducting (Ba_1−xLa_x)₂In₂O_5+x, 0?x?0.6, system have been carefully analysed using hard mode infrared (IR) powder absorption spectroscopy, X-ray powder diffraction and electron diffraction. An orthorhombic brownmillerite to three-dimensionally disordered cubic perovskite phase transition in this system is signalled by a drastic change in slope of both wavenumber and average line widths of IR spectra as a function of composition. Some evidence is found for the existence of an intermediate tetragonal phase (previously reported to exist from electron diffraction data) around x∼0.2. The new spectroscopic data have been used to compare microscopic and macroscopic strain parameters arising from variation in composition. The strain and spectroscopic data are consistent with first-order character for the tetragonal→orthorhombic transition, while the cubic→tetragonal transition could be continuous. Differences between the variation with composition of spectral parameters and of macroscopic strain parameters are consistent with a substantial order/disorder component for the transitions. There is also evidence for precursor effects within the cubic structure before symmetry is broken.     

X-ray and neutron powder diffraction studies of Ba(NdxY2−x)CuO5

Ba(R,R′)₂CuO₅ (R,R′=lanthanides and Y) plays an important role as a flux-pinning agent in enhancing the superconducting properties of the Ba₂(R,R′)Cu₃O_6+x (R,R′=lanthanides and Y) coated conductors. Using X-ray diffraction and neutron diffraction, we found that the Ba(Nd_xY_2−x)CuO₅ solid solution adopts two structure types. In the Nd-rich region (1.8?x?2.0), the materials are of brown color (commonly referred to as the ‘brown phase’), and the structure is tetragonal with space group I4/mbm (no. 127). In the Y-rich region (0.0?x?1.4), the materials are green (commonly referred to as the ‘green phase’) and the structure is orthorhombic with space group Pnma (no. 62). A two-phase region (1.4<x<1.8) exists between the orthorhombic and tetragonal phases. The crystal chemistry and crystallography of the orthorhombic ‘green phase’ series, Ba(Nd_xY_2−x)CuO₅ (isostructural to BaY₂CuO₅), are discussed in this paper.     

A novel route to synthesize cubic ZrW2−xMoxO8 (x=0-1.3) solid solutions and their negative thermal expansion properties

Cubic ZrW_2−xMo_xO₈ (c-ZrW_2−xMo_xO₈) (x=0-1.3) solid solutions were prepared by a novel polymorphous precursor transition route. X-ray diffraction (XRD) analysis reveals that the solid solutions are single phase with α- and β-ZrW₂O₈ structure for 0?x?0.8 and 0.9?x?1.3, respectively. The optimum synthesis conditions of ZrWMoO₈ are obtained from differential scanning calorimetry-thermal gravimetric analysis (DSC-TGA), XRD and mass loss-temperature/time curves. Following the above experience, the stoichiometric solid solutions of c-ZrW_2−xMo_xO₈ (x=0-1) are obtained within 1 wt% of mass loss. The relationships of lattice parameters (a), phase transition temperatures (T_c) and instantaneous coefficients of thermal expansion (α_i) against the content x of Mo are discussed based on the variation of order degree parameters of ZrW_2−xMo_xO₈.