Work of Fracture and Strain-induced Cold Crystallization Behavior of Amorphous Copolyester Sheets

The toughness of amorphous copolyester sheets was assessed by the essential work of fracture (EWF) concept. While the yielding-related work of fracture terms did not change significantly, the necking-related parameters strongly decreased with decreasing entanglement density of the copolyesters having different amounts of cyclohexylenedimethylene (CHDM) units in their backbones. Furthermore, copolyesters with high CHDM content and thus less entanglement density showed full recovery of the necked region beyond the glass transition temperature, i.e. the ‘plastic’ zone in the related specimens formed by cold drawing and not by true plastic deformation. By contrast, the copolyester with negligible amount of CHDM did not show this shape recovery. Modulated differential scanning calorimetry (MDSC) revealed that the necking in the latter system was accompanied by strain-induced crystallization. The superior work hardening in the necking stage of the respective poly(ethylene terephthalate) (PET) specimens can thus be ascribed to stretching of the entanglement network with superimposed crystallization. This revised version was published online in August 2006 with corrections to the Cover Date.     

Nonisothermal cold crystallization behavior and kinetics of polylactide/clay nanocomposites

The nonisothermal cold crystallization behavior of intercalated polylactide (PLA)/clay nanocomposites (PLACNs) was studied using differential scanning calorimetry, polarized optical microscope, X‐ray diffractometer, dynamic mechanical thermal analysis, and Fourier transform infrared spectrometer. The results show that both the cold crystallization temperature (T_cc) and melting point (T_m) of PLA matrix decreases monotonously with increasing of clay loadings, accompanied by the decreasing degree of crystallinity (X_c%) at the low heating rates (≤5 °C/min). However, the X_c% of PLACNs presents a remarkable increase at the high heating rate of 10 °C/min in contrast to that of neat PLA. The crystallization kinetics was then analyzed by the Avrami, Jezioney, Ozawa, Mo, Kissinger and Lauritzen–Hoffman kinetic models. It can be concluded that at the low heating rate, the cold crystallization of both the neat PLA and nanocomposites proceeds by regime III kinetics. The nucleation effect of clay promote the crystallization to some extent, while the impeding effect of clay results in the decrease of crystallization rate with increasing of clay loadings. At the high heating rate of 10 °C/min, crystallization proceeds mainly by regime II kinetics. Thus, the formation of much more incomplete crystals in the PLACNs with high clay loadings due to the dominant multiple nucleations mechanism in regime II, may have primary contribution to the lower crystallization kinetics, also as a result to the higher degree of crystallinity and lower melting point in contrast to that of neat PLA. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1100–1113, 2007     

Visualization of strain-induced structural rearrangements in amorphous poly(ethylene terephthalate)

A direct microscopic observation procedure is applied to study the deformation of amorphous PET decorated with a thin metal layer when stretching is performed at different draw rates and at temperatures below and above the glass transition temperature T _g. Analysis of the formed microrelief allows stress fields responsible for the deformation of the polymer to be visualized and characterized. When tensile drawing is performed at temperatures above T _g, inhomogeneity of stress fields increases with the increasing draw rate; at high draw rates, the stress-induced crystallization of PET takes place. In the case of drawing the polymer at temperatures below T _g, direct microscopic observations make it possible to visualize the development of shear bands that appear in the unoriented part of the polymer specimen adjacent to the neck. The shear bands are oriented at an angle of about 45° with respect to the draw direction. When necking involves the unoriented part of the polymer, shear bands abruptly change their orientation and become aligned practically parallel to the draw axis.     

Crystallization and melting of the system isotactic polystyrene + poly(2,6-dimethyl phenylene oxide)

From glass transition T_g measurements on isotactic polystyrene (IPS)–poly(2,6-dimethyl phenylene oxide) (PPO) blends, it was concluded that thoroughly annealed, freeze-dried samples, or samples evaporated from solution at high temperature, are homogeneous. Without annealing, the freeze-dried blends show two to three T_g's characteristic of the presence of different phases. The overall crystallization rate of these samples is much higher than that observed with annealed samples. The presence of dissolved PPO in annealed samples reduces the overall crystallization rate and the spherulitic growth rate, compared to IPS. The melting behavior of the blends is influenced by the extent of mixing of both polymers. Without annealing, isothermally crystallized, freeze-dried blends show the same melting behavior as IPS (i.e., multiple melting). In homogeneous annealed samples the rate of reorganization is strongly reduced and multiple melting only occurs at low scanning rate (e.g., 1°C/min). This behavior is influenced by the crystallization temperature and by the composition of the blends. The addition of PPO has no influence on the relation between melting point and crystallization temperature and the same equilibrium melting point is found by extrapolation.     

Cold crystallization and thermal shrinkage of uniaxially drawn poly(ethylene 2,6-naphthalate) by solid-state coextrusion

Solid-state coextrusion has been used to prepare uniaxially drawn films from isotropic poly(ethylene 2,6-naphthalate) (PEN) of a minimum degree of crystallinity (ca. 5%) both below and above its glass transition temperature T_g. The onset of cold crystallization (T_c) of the drawn films has been studied as a function of the extrusion temperature (ET) and the draw ratio (EDR). It has been shown that T_c decreases markedly on draw, as much as 95°C, and, at constant draw ratio T_c goes through a minimum in the T_g region. For undrawn PEN, annealing below 153°C has no significant effect on T_c. To evaluate the crystallization rate constant (k) and the activation energy (E_a) of the drawn specimens, a nonisothermal DSC procedure has been used. With increasing EDR, k increases markedly and E_a goes down over threefold compared with the undrawn polymer. At high ET, strain-induced crystallization has also been shown to play an important role in lowering E_a for cold crystallization. Thermal shrinkage above T_m indicates a high elastic recovery, underlining the efficiency of deformation, ca. 93%, achieved by solid-state coextrusion.     

Cold crystallization and postmelting crystallization of PLA plasticized by compressed carbon dioxide

The cold crystallization at temperature T_cc (melting > T_cc > glass transition) and the postmelting crystallization of polylactic acid plasticized by compressed carbon dioxide (CO₂) were studied using a high-pressure differential scanning calorimeter. The kinetics of the two kinds of crystallization were evaluated by the Avrami equation as a function of pressure at certain temperatures. The effects of using talc as a nucleation agent on the two types of crystallization under pressure were also investigated. The results show that compressed CO₂ increased the mobility of the polymer chains in solid state, resulting in an increased rate of cold crystallization. The decreased rate of postmelting crystallization was mainly in the nucleation-controlled region, which indicates that the number of nuclei was decreased by the compressed CO₂. The growth rate of the two crystallization types followed the Avrami equation, but the kinetics of each depended upon temperature and pressure. The inclusion of talc accelerated postmelting crystallization but had little effect on cold crystallization. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2630–2636, 2008     

Study of the Crystallization of an Aromatic Poly-ether-ketone (PK99) by Calorimetric and X-ray Analysis

An analysis of the crystallization behaviour of a new poly(aryl-ether-ether-ketone-ketone), PK99, by differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) is presented. Isothermal crystallization TG were obtained in the whole range between the glass transition temperature (T _g) and the melting temperature (T _m) as a consequence of the slow crystallization kinetics stemming from the closeness of these transitions. The calorimetric results, compared with WAXD data, were applied to determine the theoretical melting temperature and crystallization enthalpy. The DSC and WAXD data were combined in order to calculate the total amount of the crystallizable fraction of the polymer, and a model was proposed to explain the difference between the fractions of crystallinity observed with these techniques. The thermal and X-ray data were also correlated with different lamellar morphologies arising from the crystallization conditions. Finally, DSC experiments on the crystallized sample were used to detect the presence of a rigid amorphous phase which does not relax at T _g. This revised version was published online in July 2006 with corrections to the Cover Date.     

Impact of plasticizers and tackifiers on the crystallization of isotactic poly(1-butene)

Crystallization of a semi-crystalline polyolefin in the presence of low molecular weight modifiers was quantified by differential scanning calorimetry and optical microscopy. The polyolefin was a commercial grade of isotactic poly(1-butene) (iPB). Two modifiers were used: an oligomeric plasticizer, designated HOAO, which decreased the glass transition temperature (T_g) of the system, and an oligomeric tackifier, designated HOCP, which increased T_g. Binary iPB/modifier blends containing 10% or 20% by weight of HOAO or HOCP were examined to determine how their addition affects T_g, while ternary iPB/HOAO/HOCP blends containing 10% or 20% by weight of total modifier were examined to determine the effects of dilution by using a ratio of HOAO to HOCP that matched the T_g of iPB. The addition of modifier decreased the nucleation rate, spherulitic crystal growth rate, and final crystallinity of each blend. However, only the nucleation rate showed a dependence on the type of modifier, with nucleation retarded more by HOCP than by HOAO. A Hoffman-Weeks analysis of the melting point as a function of crystallization temperature confirmed that the driving force for nucleation was reduced, and that the effect was larger for HOCP. An Avrami analysis of the bulk crystallization kinetics was consistent with these observations, as the Avrami exponents were in the range of 3-4.     

SAXS/WAXS/DSC studies on crystallization of a polystyrene-b-poly(ethylene oxide)-b-polystyrene triblock copolymer with lamellar morphology and low glass transition temperature

Crystallization of a polystyrene-b-poly(ethylene oxide)-b-polystyrene (S-EO-S) triblock copolymer, S₄₀EO₁₃₆S₄₀, with lamellar morphology in the melt and low glass transition temperature (T_g=47 °C) of the S block was studied. The triblock copolymer was cooled from ordered melt and isothermal crystallization was conducted at crystallization temperatures (T_c) near the T_g of the S block. It is found that crystallization behavior of S₄₀EO₁₃₆S₄₀ strongly depends on T_c. When T_c is far below T_g, an Avrami exponent n=0.5 is observed, which is attributed to diffusion-controlled confined crystallization. As T_c slightly increases, the Avrami exponent is 1.0, indicating that crystallization is confined and crystallization rate is determined by the rate of homogeneous nucleation. When T_c is just below the T_g of the S block, crystallization tends to become breakout and accordingly Avrami exponent changes from 1.0 to 3.2. Crystallinity and melting temperature of the EO block in breakout crystallization are slightly higher than those in confined crystallization. Time-resolved small and wide angle X-ray scattering (SAXS/WAXS) were used to monitor isothermal crystallization of S₄₀EO₁₃₆S₄₀. It shows that the long period is constant in confined crystallization, but it gradually increases during breakout crystallization. WAXS result reveals that confined or breakout crystallization has no effect on the crystal structure of the EO block.     

Crystallization of poly(N-methyldodecano-12-lactam) in blends with poly(styrene-stat-acrylic acid)

Crystallization behaviour of blends of poly(N-methyldodecano-12-lactam) (PMDL) with statistical copolymer poly(styrene-stat-acrylic acid) (PSAA) has been studied by the DSC and WAXD methods. The blend films prepared from dioxane solutions were crystallized at laboratory temperature for five days. Approximate crystallinities of as-prepared neat lower- PMDL 5 and higher-molecular weight PMDL 45 were 28% and 19%, respectively. With increasing PSAA content in the blends the crystallinities decreased sharply. The melting point of the primary crystalline structure of PMDL showed a decreasing dependence on PSAA content in the blends, confirming miscibility of the PMDL-PSAA pair. Recrystallization was strongly suppressed in the blends. The lower-melting endotherm appearing at about 10-15 °C above the crystallization temperature was attributed to melting to less perfect structures formed during secondary crystallization. In neat PMDL, the extent of secondary crystallization was approximately 5-10%. In the blends containing 20% PSAA approximate relative proportion of secondary crystallites on total crystallinity was 40% and 60% for the blends with PMDL 5 and PMDL 45, respectively. WAXD measurements did not reveal any change in crystal modification on blending. Increased T_g in blends of flexible PMDL cannot play a significant role in suppression of primary in favour of secondary crystallization. This was attributed to low mobility of PMDL chains due to dilution effect and specific interactions with the amorphous copolymer component, and, in case of the higher-molecular-weight PMDL, a greater involvement of entanglements. Higher T_g of blends was involved in retardation of non-isothermal crystallization on cooling and subsequent cold crystallization.     

Thermal properties of freezing bound water restrained by sodium lignosulfonate-based polyurethane hydrogels

In order to develop a new functional product from lignin, sodium lignosulfonate (LS)-based polyurethane (LSPU) hydrogels were prepared from LS and hexamethylene diisocyanate (HDI) derivatives in water. Isocyanate/hydroxyl group ratio (NCO/OH ratio) was varied from 0.05 to 0.8 mol mol⁻¹, and water content (W_c = mass of water/mass of dry sample) of the obtained LSPU hydrogels was varied from 0 to 3.0 g g⁻¹. Phase transition behavior of hydrogels with various W_c’s was investigated by differential scanning calorimetry (DSC) and thermogravimetry (TG). In DSC heating curve of LSPU hydrogels, glass transition, cold crystallization, melting and liquid crystallization were observed. Cold crystallization, two melting peaks and variation of melting enthalpy indicate that three kinds of water, i.e., non-freezing water, freezing bound water and free water, exist in LSPU hydrogel. Glass transition temperature (T_g) decreased from 230 to 190 K in a W_c range where non-freezing water was formed in the hydrogel. T_g increased when freezing bound water was formed in the system. T_g leveled off in a W_c range where normal ice was formed. The effect of NCO/OH ratio on molecular motion of LSPU hydrogel is examined based on T_g and heat capacity difference at T_g (ΔC_p). Water vaporization curve measured by TG also indicates the presence of bound water which evaporates at a temperature higher than ca. 410 K. By atomic force microscopic observation, the size of molecular bundle of LSPU hydrogel is calculated and compared with that of LS-water system. By cross-linking, the height of molecular bundle decreased from ca. 3–1 nm and lignin molecules extend in a flat structure.

     

Thermal properties of random copolyesters of PET and 3- and 3,5-bromo-substituted p-hydroxybenzoic acids. II

Melt-polycondensation of poly(ethylene terephthalate) (PET) and 3-bromo-p-acetoxybenzoic acid or 3,5-dibromo-p-acetoxybenzoic acid in different mole ratios yielded random copolyesters. The copolyesters have higher T_gs than PET because of an increase in mol % of the substituted p-oxy-benzoate units and follow Wood's equation for copolymer T_gs. Using this equation, we calculated the T_gs of the homopolymers of 3-bromo-p-oxybenzoate and 3,5-dibromo-p-oxybenzoate, which are not available experimentally, to be 113 and 123°C, respectively. Up to certain percentages of the comonomer composition the copolyesters exhibited cold crystallization and melt transitions which we attribute to the crystallizable segments of PET. The variation in melting temperatures in the composition of the copolymer was explained by Flory's theory. The differences in the melting behavior of the polymer, annealed at various crystallization temperatures for a constant time interval, throws light on the morphological changes that took place in it. Using the Hoffman and Weeks method, we determined the extrapolated equilibrium melting temperatures of these copolyester which were used to calculate the enthalpy of melting for the crystallizable units.     

Energy storage and strain‐recovery processes in highly deformed semicrystalline poly(butylene terephthalate)

Nonelastic deformation of semicrystalline poly(butylene terephtalate) (PBT) was investigated by calorimetric measurements and strain‐recovery tests. Differential scanning calorimetry on PBT specimens deformed both below and above their glass‐transition temperature (T_g ≈ 50 °C) showed the presence of a broad exothermal peak whose area represents the energy released for the nonelastic strain recovery. This energy became more and more pronounced as the strain level increased, and it decreased as the deformation temperature increased, even if a significant contribution was detected on specimens deformed at temperatures much higher than T_g. For two temperature conditions (21 and 100 °C), strain‐recovery master curves were built showing the following two distinct deformation components: one recoverable with time and another one irreversible, this latter one arising from relatively low levels of strain. The recoverable component can be erased by heating the material at temperatures much higher than its T_g, close to the onset of the melting process. On the other hand, the irreversible strain component does not recover even if the material is brought close to the onset of the crystals melting. The shift factor for the strain‐recovery master curves was compared with the shift factor for the construction of the dynamic storage modulus master curve obtained in the linear viscoelastic regime (small strain). © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 40: 236–243, 2002     

Phase transition of locust bean gum-, tara gum- and guar gum-water systems

Phase transition behaviour of neutral galactomannans, i.e., locust bean gum (LBG), tara gum (Tara-G) and guar gum (GG)-water systems is investigated. In this study, water content {W_c=(gram of water)/(gram of dry sample)} of these systems was varied from 0.2 to 3.6 g g^-1. In the DSC heating curves, glass transition (T_g), cold crystallization (T_cc) and melting (T_m) were observed in all three samples. In addition, liquid crystal transition (T*) was observed in GG-water systems at a temperature higher than Tm. Using T_g, T_cc, Tm and T*, phase diagrams of each system were established. From the melting enthalpy of ice in the systems, three types of water, non-freezing water (W_nf), freezing bound water (W_fb) and free water were calculated. The maximum amount of Wnf was observed at Wc=0.7 g g-1, where Tg showed the lowest temperature. The amount of Wnf in LBG and GG is higher than that of Tara-G, whereas the highest amount of Wfb is found in GG. T* was only observed in GG-water systems. It is concluded that frequency of the side chains in the repeating unit of the main chains of these three galactomannan affects the frozen structure of the glassy state in the presence of water. This revised version was published online in July 2006 with corrections to the Cover Date.     

Mechanical properties and transition temperatures of crosslinked-oriented gelatin

 This second part of a systematic study of the properties of crosslinked-oriented gelatin involves the effects of orientation and water content on the glass transition temperature T _g and on the melting behavior. The samples were the same as those in the preceding study, and their transition temperatures were determined by both differential scanning calorimetry and dynamic mechanical thermal analysis. The crosslinked gelatin which had been room-conditioned showed two transition temperatures: the lower one was attributed to T _g of the water-plasticized gelatin, and the higher one was interpreted as T _g of dried gelatin superimposed by melting. A rather unusual situation arose because of the fact that the T _g and melting temperatures T _m (217 and 230 ^°C, respectively) are so similar. Using water as plasticizer not only decreases T _g but produces imperfect crystallites which melt below the T _g of the system. The presence of the amorphous phase in the glassy state would presumably make it essentially impossible to define a melting point or crystallization temperature in the normal manner, as an equilibrium between crystalline and amorphous phases. Received: 8 October 1996 Accepted: 2 November 1995     

CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID

The crystallization kinetics of the copolyester, poly(ethylene terephthalate) (PET) modified by sodium salt of 5-sulpho-isophthalic acid(SIPM), was investigated by means of differential scanning calorimeter. The experimental results and polari-microscopy observation all showed that the introduction of SIPM did not affect the nucleation of crystallization. Within the temperature range between their glass transition temperature T_θand melting point T_m, the crystallization rate of the copolyester sample decreased with increasing content of SIPM. The relative crystallization rate constant Z of SIPM/DMT (dimethyl terephthalate) 4mol % sample was about 1% pure PET's Z value. For isothermal crystallized copolyester samples, DSC heating curves displayed multi-melting behavior. This was interpreted by molecular weight fractionation during crystallization and premelting-recrystallization mechanism. This interpretation showed why the second melting point T_(m2) will change according to Hoffman-Weeks(H-W) equation and the first melting point T_(m1) will increase with increasing SIPM. The principal cause of these phenomena is the high temperature crystallization rate decreases rapidly with increasing SIPM.     

Revisiting the crystallization of poly(2‐alkyl‐2‐oxazoline)s

Poly(2‐alkyl‐2‐oxazoline)s (PAOx) exhibit different crystallization behavior depending on the length of the alkyl side chain. PAOx having methyl, ethyl, or propyl side chains do not show any bulk crystallization. Crystallization in the heating cycle, that is, cold crystallization, is observed for PAOx with butyl and pentyl side chains. For PAOx with longer alkyl side chains crystallization occurs in the cooling cycle. The different crystallization behavior is attributed to the different polymer chain mobility in line with the glass transition temperature (T_g) dependency on alkyl side chain length. The decrease in chain mobility with decreasing alkyl side chain length hinders the relaxation of the polymer backbone to the thermodynamic equilibrium crystalline structure. Double melting behavior is observed for PButOx and PiPropOx which is explained by the melt‐recrystallization mechanism. Isothermal crystallization experiments of PButOx between 60 and 90 °C and PiPropOx between 90 and 150 °C show that PAOx can crystallize in bulk when enough time is given. The decrease of T_g and the corresponding increase in chain mobility at T > T_g with increasing alkyl side chain length can be attributed to an increasing distance between the polymer backbones and thus decreasing average strength of amide dipole interactions. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 721–729     

Thermal properties and applications of low molecular weight polyhydroxybutyrate

The properties of the low molecular weight polyhydroxybutyrate (LMWPHB) and LMWPHB plasticized polyhydroxybutyrate (PHB) are studied using differential scanning calorimetry (DSC), thermogravimetric analysis, wide-angle X-ray diffraction (WAXD), polarized optical microscope (POM), mechanical, and biodegradation tests. The results of DSC, WAXD, and POM indicate that LMWPHB has a lower glass transition temperature (T _g), crystallinity, crystallization rate, melting temperature (T _m), and crystal size than PHB due to its much smaller molecular weight. The tensile strength, T _g, T _m, crystallinity, crystallization rate, and thermal stability of LMWPHB plasticized PHB decrease, while the flexibility and biodegradation rate increase with the increasing content of the added LMWPHB. It is confirmed that LMWPHB can be used to improve the brittleness and control the biodegradation rate of PHB.     

Thermal behavior of polytriazole films: A thermal analysis study

The thermal behavior of poly(1,3-phenyl-1,4-phenyl)-4-phenyl-1,2,4-triazole has been investigated using different scanning calorimetry (DSC) and thermogravimetry (TG). Processes are studied for this thermally stable polymer that take place between 200 and 500°C. While the polycondensation reaction product in powder from appeared to be partially crystalline, films prepared by casting from a formic acid solution appeared to be completely amorphous. A thermal treatment between T_g(～ 270°C) and T_m(～ 430°C) can introduce crystallinity in the films because of the polymer's ability to cold crystallize. The cold crystallization temperature T_c seems to be dependent on the preparation history of the solid polymer phase. Thermal annealing of the films just below T_g does not introduce crystallinity but inhibits subsequent cold crystallization at higher temperatures. Crystallization upon cooling from the crystalline melt has not been observed either. At temperatures just above the crystalline melting point the polymer starts to decompose in an exothermic reaction.     

Thermal stability and nonisothermal crystallization of short fiber-reinforced poly(ether ether ketone) composites

The thermal stability of a short carbon-fiber-reinforced PEEK composite was assessed by thermogravimetry and by a Rheometrics dynamic analyzer. The results indicated that holding for 10 min at 380°C was a suitable melting condition to avoid the thermooxidative degradation under air. After proving that the heating rate of 50°C/min can be used to evaluate the crystallinity, a heating stage was used to prepare nonisothermally crystallized specimens using cooling rates from 1 to 100°C/min after melting at 400°C for 3 or 15 min. The degree of crystallinity and the melting behavior of these specimens were investigated by DSC at a heating rate of 50°C/min. The presence of three or four regions indicated that the upper melting temperature, T_m, changed with the crystallization temperature. The first region with the highest T_m, which corresponded to the cooling rate of 1°C/min, can be associated with the crystallization in regime II. There was a second region where T_m decreased as the amount of crystals formed in regime II decreased with increasing cooling rate from 5 to 20°C/min. The third region, a plateau region, corresponded to regime III condition in which the crystals were imperfect. In the fourth region, the cooling was so fast that crystallization was incomplete during the cooling for the melting condition of 400°C for 15 min. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. B Polym. Phys. 36: 2225–2235, 1998