Synthesis and electrochemical performances of Li4Ti4.95Al0.05O12/C as anode material for lithium-ion batteries

Spinel compounds Li₄Ti_5−xAl_xO₁₂/C (x=0, 0.05) were synthesized via solid state reaction in an Ar atmosphere, and the electrochemical properties were investigated by means of electronic conductivity, cyclic voltammetry, and charge-discharge tests at different discharge voltage ranges (0-2.5 V and 1-2.5 V). The results indicated that Al³⁺ doping of the compound did not affect the spinel structure but considerably improved the initial capacity and cycling performance, implying the spinel structure of Li₄Ti₅O₁₂ was more stable when Ti⁴⁺ was substituted by Al³⁺, and Al³⁺ doping was beneficial to the reversible intercalation and deintercalation of Li⁺. Al³⁺ doping improved the reversible capacity and cycling performance effectively especially when it was discharged to 0 V.     

Physical properties of BaMg1/3Nb2/3O3-BaCo1/3Nb2/3O3 solid solutions

Structural, electric and magnetic properties of Ba₃Mg_1−xCo_xNb₂O₉ based dielectric ceramic compounds have been studied. The samples, prepared by a solid state reaction method, were characterised by X-ray powder diffraction (XRPD), electron microscopy (SEM), dielectric (ε(T)) and magnetic measurements (χ⁻¹(T)). The XRPD analyses showed that the crystal structure of these compounds does change by the increase of substitution degree, passing from a superstructure hexagonal-type, (no. 164), space group (SG) to a simple structure cubic-type, (no. 221), SG. However, the evolution of the elementary unit cell lattice parameter can be followed and it exhibit a linear increasing tendency with increase in the substitution, indicating the existence of a solid solution through out the investigated range of substitution (0-1). The microstructure analysis shows a variation in the grain size and also the porosity of the samples with the degree of substitution. The results are in good agreement with that of dielectric measurements, which also showed that the dielectric constant (ε) increases with the increase of cobalt content. The magnetic characterization of cobalt substituted samples showed an antiferromagnetic type super-exchange interaction between these magnetic ions. At the same time, the values of effective magnetic momentum (μ_eff) are close to the value that corresponds to Co²⁺ free ions. The study highlights the possibility of modelling these materials by substitutions, in order to improve properties of negative-positive-zero (NPO) type dielectric applications.     

Charge order melting and magnetic transition in Nd0.5(1+x)Ca0.5(1−x)Mn(1−x)CrxO3 system

The magnetic property of double doped manganite Nd_0.5(1+x)Ca_0.5(1−x)Mn_(1−x)Cr_xO₃ with a fixed ratio of Mn³⁺:Mn⁴⁺=1:1 has been investigated. For the undoped sample, it undergoes one transition from charge disordering to charge ordering (CO) associated with paramagnetic (PM)-antiferromagnetic (AFM) phase transition at T<250 K. The long range AFM ordering seems to form at 35 K, rather than previously reported 150 K. At low temperature, an asymmetrical M-H hysteresis loop occurs due to weak AFM coupling. For the doped samples, the substitution of Cr³⁺ for Mn³⁺ ions causes the increase of magnetization and the rise of T_c. As the Cr³⁺ concentration increases, the CO domain gradually becomes smaller and the CO melting process emerges. At low temperature, the FM superexchange interaction between Mn³⁺ and Cr³⁺ ions causes a magnetic upturn, namely, the second FM phase transition.     

Observation of higher magnetization on the substitution of Al for Co in La2MnCoO6

Upon substitution of non-magnetic Al³⁺ for diamagnetic, low-spin, Co³⁺ in ferromagnetic La₂MnCoO₆, the ferromagnetic moment, measured at 82 K and 15 kOe, is found to increase initially with Al content and then decreases, though the magnetic transition temperature decreases continuously on increasing x in La₂MnCo_1−xAl_xO₆.     

Structural and magnetic properties of Mg(In2−xMnx)O4 system

We synthesized the Mn-doped Mg(In_2−xMn_x)O₄ oxides with 0.03?x?0.55 using a solid-state reaction method. The X-ray diffraction patterns of the samples were in a good agreement with that of a distorted orthorhombic spinel phase. Their lattice parameters and unit-cell volumes decrease with x due to the substitution of the smaller Mn³⁺ ions to the larger In³⁺ ions. The undoped MgIn₂O₄ oxide presents diamagnetic signals for 5 K?T?300 K. The M(H) at T=300 K reveals a fairly negative-sloped linear relationship. Neither magnetic hysteresis nor saturation behavior was observed in this parent sample. For the Mn-doped samples, however, positive magnetization were observed between 5 and 300 K even if the x value is as low as 0.03. The mass susceptibility enhances with Mn content and it reaches the highest value of 1.4×10⁻³ emu/g Oe (at T=300 K) at x=0.45. Furthermore, the Mn-doped oxides with x=0.06 and 0.2, respectively, exhibit nonlinear magnetization curves and small hysteretic loops in low magnetic fields. Susceptibilities of the Mn-doped samples are much higher than those of MnO₂, Mn₂O₃ oxides, and Mn metals. These results show that the oxides have potential to be magnetic semiconductors.     

Cr-doping effect on the structural, magnetic, transport properties and Raman spectroscopy of La(2+x)/3Sr(1−x)/3Mn1−xCrxO3 perovskites

A series of the double-doping samples La_(2+x)/3Sr_(1−4x)/3Mn_1−xCr_xO₃ (0?x?0.25) with the Mn³⁺/Mn⁴⁺ ratio fixed at 2:1 have been fabricated. The structural, magnetic, transport properties and Raman spectroscopy have been investigated, and no apparent crystal structure change is introduced by Cr doping up to x=0.25. But the Curie temperature T_C and metal-insulator transition temperature T_MI are strongly affected by Cr substitution. The room temperature Raman spectra start exhibiting some new features following the increasing concentration of Cr substitutions. Moreover, it is worth noting that the frequency of the A_1g phonon mode can also be well correlated with the A-site mismatch effect (σ²), which is influenced mainly by the variety of the Sr content.     

Site occupancy and magnetic study of Al and Cr co-substituted Y3Fe5O12

Single-phased polycrystalline Y₃Fe_5−2xAl_xCr_xO₁₂ garnet samples (x=0, 0.2, 0.4 and 0.6) have been prepared by the conventional ceramic technique. Rietveld refinement of X-ray diffraction patterns of the samples shows them to crystallize in the Ia3d space group and the corresponding lattice constant to decrease with increasing Al³⁺ and Cr³⁺ contents (x). Mössbauer results indicate that Cr³⁺ substitutes for Fe³⁺ at the octahedral sites whilst Al³⁺ essentially replaces Fe³⁺ at the tetrahedral sites. This result indicates that co-doping of Y₃Fe₅O₁₂ does not affect the preferential site occupancy for separate individual substitution of either Cr³⁺ or Al³⁺. The magnetization measurements reveal that the Curie temperature (T_c) monotonically decreases with increasing x while the magnetic moment per unit formula decreases up to x=0.4 and then slightly increases for x=0.6. This reflects a progressive weakening of the ferrimagnetic exchange interaction between the Fe³⁺ ions at octahedral and tetrahedral sites due to co-substitution. The magnetic moment was calculated using the cations distribution inferred from the Mössbauer data and the collinear ferrimagnetic model, and was found to agree reasonably with the experimentally measured value. The phenomenological amplitude crossover, characterized by the temperature T*, has also been observed in the doped YIG and briefly discussed.     

Specific heat and magnetic susceptibility of single-crystalline ZnCr2−xAlxSe4 (x=0.15, 0.23)

A correlation between the second critical field H_c2 of the helix to paramagnetic transition and the magnetic specific heat C-peak was found in ZnCr_2−xAl_xSe₄ spinel single crystals with x=0.15, 0.23. The specific heat peak is anomalously sharp for all finite magnetic fields used here and this points to a first order magneto-structural transition (from cubic to tetragonal symmetry). The C(T)-peak is increasingly suppressed as the external field increases. Approaching the Neel temperature T_N, a broad ac-magnetic susceptibility peak is observed for zero dc-magnetic field. That peak does not show an energy loss and thus points towards a return to a second order type of transition. The magnetic contribution to the specific heat displays a sharp peak at T_N and is maximal at the spin fluctuation temperature T_sf=34 K. T_sf is related to the maximum of the magnetic susceptibility at T_m=40 K (at 50 kOe) in the spin fluctuation region, as evidenced by the entropy exceeding 90% of the entropy calculated classically for the complete alignment of the Cr spins, (2−x)R ln(2S+1). The X-ray photoelectron spectroscopy (XPS) data indicate that Al-substitution does not affect Cr³⁺ 3d³ electronic configuration.     

Microstructure characterization and magnetic behavior of NiAlxFe2−xO4 and Ni1−yMnyAl0.2Fe1.8O4 ferrites

NiAl_xFe_2−xO₄ and Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites were prepared by the conventional ceramic method and were characterized by X-ray diffraction, scanning electron microscopy, and magnetic measurements. The single spinel phase was confirmed for all prepared samples. A proper explanation of data is possible if the Al³⁺ ions are assumed to replace Fe³⁺ ions in the A and B sites simultaneously for NiAl_xFe_2−xO₄ ferrites, and if the Mn²⁺ ions are assumed to replace Ni²⁺ ions in the B sites for Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites. Microstructural factors play an important role in the magnetic behavior of Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites with large Mn²⁺ content.     

Double metal-insulator peaks and effect of Sm substitution on magnetic and transport properties of hole-doped La0.85Ag0.15MnO3

La_0.85−xSm_xAg_0.15MnO₃ (x=0−0.2) ceramics were prepared using the conventional solid-state synthesis method to investigate the effect of Sm³⁺ substitution on magnetic and electrical transport properties. Magnetic susceptibility versus temperature measurements showed all samples exhibit ferromagnetic to paramagnetic transition with Curie temperature, T_c decreasing from 283 K (x=0) to 164 K (x=0.2) with increasing Sm³⁺. The observed slope in susceptibility, χ′ versus temperature curves below T_c indicates the possible presence of FM and AFM phases in the metallic region. In addition, a deviation from the Curie-Weiss law above T_c in 1/χ′ versus T curves indicates the existence of a Griffith's phase in the x=0.05−0.2 samples due to the Sm³⁺ ion substitution. The Griffith temperature, T_G was found to decrease from 295 K (x=0.05) to 229 K (x=0.2). Electrical resistivity measurements of the samples in zero field showed transition from metallic behavior to insulating behavior as the temperature was increased. For x=0, two metal-insulator, MI transition peaks were observed at T_p1=282 K and at T_p2=250 K. Both peaks shifted to lower temperatures with the increase in Sm³⁺. The relative resistivity of the first peak to the second peak decreases with increasing Sm³⁺ for x>0.05 while at x=0.2 the T_p1 peak was strongly suppressed. Magnetoresistance, MR was observed to weaken with Sm³⁺ substitution. The metallic region of the ρ(T) curve of the x=0−0.15 samples was fitted to the model of electron-electron and electron-magnon scattering while the insulating region was fitted to the variable range hopping, VRH model. The resistivity behavior indicated that the substitution of Sm³⁺ weakened the double exchange process and enhanced the Jahn-Teller effect. Our results indicated that the T_p1 peak is strongly related to the double-exchange mechanism while the T_p2 peak is suggested to originate from magnetic inhomogeneity.     

Effects of Cr doping in bilayered manganite LaSr2Mn2O7: Resistivity, thermoelectric power, and thermal conductivity

Systematic studies of resistivity, thermoelectric power, and thermal conductivity have been performed on polycrystalline bilayered manganites LaSr₂Mn_2−xCr_xO₇ (0≤x≤0.2). It is found that the temperature dependence of both Seebeck coefficient S(T) and resistivity ρ(T) in the high temperature region follows the small polaron transport mechanism for all the samples. But in the low temperature region, variable-range-hopping (VRH) model matches the experimental data better. In addition, the maximum of absolute S(T) at low temperatures is gradually suppressed for the sample with Cr-doping level of x>0.04, implying that a new FM order probably arises. With decreasing the temperatures further, S(T) has a sign change and becomes positive for the sample with Cr-doping level of x>0.04, indicating that there may occur a variation of the type of charge carrier. As to thermal conduction κ(T), the low-temperature peak is suppressed due to Cr-doping. The variation of κ(T) is analyzed based on the combined effect due to the suppression of local Mn³⁺O₆ Jahn-Teller (JT) lattice distortion because of the substitution of Cr³⁺ ions for Mn³⁺ ions, which results in the increase in thermal conduction, and the introduction of the disorder due to Cr-doping, which contributes to the decrease in thermal conduction.     

Studies on Structural, Magnetic and Thermal Properties of xFe2TiO4-(1−x)Fe3O4 (0≤x≤1) Pseudo-binary System

The xFe₂TiO₄-(1−x)Fe₃O₄ pseudo-binary systems (0≤x≤1) of ulvöspinel component were synthesized by solid-state reaction between ulvöspinel Fe₂TiO₄ precursors and commercial Fe₃O₄ powders in stochiometric proportions. Crystalline structures were determined by X-ray powder diffraction (XRD) and it was found that the as-obtained titanomagnetites maintain an inverse spinel structure. The lattice parameter a of synthesized titanomagnetite increases linearly with the increase in the ulvöspinel component. ⁵⁷Fe room temperature Mössbauer spectra were employed to evaluate the magnetic properties and cation distribution. The hyperfine magnetic field is observed to decrease with increasing Fe₂TiO₄ component. The fraction of Fe²⁺ in both tetrahedral and octahedral sites increases with the increase in Ti⁴⁺ content, due to the substitution and reduction of Fe³⁺ by Ti⁴⁺ that maintains the charge balance in the spinel structure. For x in the range of 0 ≤x≤0.4, the solid solution is ferrimagnetic at room temperature. However, it shows weak ferrimagnetic and paramagnetic behavior for x in the range of 0.4<x≤0.7. When x>0.70, it only shows paramagnetic behavior, with the appearance of quadrupole doublets in the Mössbauer spectra. Simultaneous differential scanning calorimetry and thermogravimetric analysis (DSC-TGA) studies showed that magnetite is not stable, and thermal decomposition of magnetite occurs with weight losses accompanying with exothermic processes under heat treatment in inert atmosphere.     

Effect of Al doping on the magnetic and electrical properties of layered perovskite La1.3Sr1.7Mn2−xAlxO7

The effect of Al substitution for Mn site in layered manganese oxides La_1.3Sr_1.7Mn_2−xAl_xO₇ on the magnetic and electrical properties has been investigated. It is interesting that all the samples undergo a similar and complex transition with lowing temperature; they transform from the two-dimensional short-range ferromagnetic order at T*, then enter the three-dimensional long-range ferromagnetic state at T_C, at last they display the canted antiferromagnetic state below T_N. T*, T_C and T_N are all reduced with Al content. Resistivity increases sharply with increasing Al concentration, and the metal-insulator transition disappears when x reaches 10%. Additionally, magnetoresistance (MR) effect is weakened. Al substitution dilutes the magnetic active Mn-O-Mn network and weakens the double exchange interaction, and further suppresses FM ordering and metallic conduction. Owing to the anisotropic interaction in the layered perovskite, the magnetic and electrical properties are more sensitive to Al doping level than those in ABO₃-type perovskite.     

The ESR study of single crystal spinel ZnCr2Se4 diluted with Sb and V

The single crystal of Sb³⁺ and V³⁺ doped zinc chromium selenide spinel ZnCr₂Se₄ were prepared by a chemical transport method and characterized by ESR spectroscopy in order to examine the effect of nonmagnetic antimony and magnetic vanadium on properties of the system. For antimony admixtures the Neel temperature is very similar to that of the parent spinel ZnCr₂Se₄ (22 K). However, upon incorporating vanadium ions, the T_N temperature decreases down to 17.5 K, determined for the maximum vanadium content (x=0.06). The temperature dependence of the ESR linewidth over paramagnetic region is interpreted by an occurrence of spin-phonon interaction. The strong broadening linewidth together with its strong temperature dependence for vanadium doped ZnCr₂Se₄ is explained by the complex paramagnetic relaxation model.     

Study of the magnetization and transport properties of the La(2+x)/3Sr(1−x)/3Mn1−xCrxO3 (0≤x≤0.2) system

The samples with the Mn³⁺/Mn⁴⁺ ratio fixed at 2:1 La_(2+x)/3Sr_(1−x)/3Mn_1−xCr_xO₃ (0≤x≤0.20) have been prepared. The magnetic, electrical transport, and magnetoresistance properties have been investigated. Remarkable transport and colossal magnetoresistance (CMR) effect, as well as cluster glass (CG) behaviors have been clearly observed in the samples studied. It was found that the Curie temperature T_c and insulator−metal transition temperature T_p1 are strongly affected by Cr substitution. The experiment observations are discussed by taking into account the variety of tolerance factors t; the effects of A-site radius 〈r_A〉 and the A-site mismatch effect (σ²).     

Effects of Cr doping in electron-doped manganites La0.9Te0.1MnO3

The effects of Cr doping on Mn sites in the electron-doped manganites La_0.9Te_0.1MnO₃ have been studied by preparing the series La_0.9Te_0.1Mn_1−xCr_xO₃ (0.05≤x≤0.20). Upon Cr doping, both the Curie temperature T_C and magnetization M are suppressed. The resistivity measurements indicate that there exists a weak metal-insulator (M-I) transition for the sample with x=0.05, with an increase in the doping level, the M-I transition disappears and the resistivity increases. Thermopower S(T) exhibits a maximum near T_C for all samples. By fitting the S(T) and ρ(T) curves, it is found that the temperature dependences of both S(T) and ρ(T) in the high temperature paramagnetic (PM) region follow the small polaron conduction (SPC) mechanism for all samples. The fitting parameters obtained imply changes of both the average-hopping distance of the polarons and the polaron concentration with Cr doping in our studied samples. In the case of the thermal conductivity κ(T), the variation of κ(T) is analyzed based on the combined effects due to the suppression of the local Mn³⁺O₆ Jahn-Teller (JT) lattice distortion because of the substitution of Cr³⁺ for Mn³⁺ ions, which results in the increase in κ, and the introduction of the disorder due to Cr-doping, which contributes to the decrease in κ.     

High-temperature thermoelectric properties of Ca3Co4O9+δ with Eu substitution

We have prepared polycrystalline Ca_3−xEu_xCo₄O_9+δ (x=0, 0.15, 0.3 and 0.45) samples using a sol-gel process followed by SPS sintering and investigated the Eu substitution effects on their high-temperature thermoelectric properties. With the Eu substitution, both the electrical resistivity and thermopower increase monotonously. This could be attributed to the decrease of hole concentrations by substitution of trivalent Eu³⁺ for divalent Ca²⁺. The Eu substituted samples (x=0.15, x=0.3) have lower thermal conductivity than Ca₃Co₄O_9+δ due to their lower electronic and lattice thermal conductivity. The dimensionless figure of merit ZT reaches 0.3 at 1000 K for the sample of Ca_2.7Eu_0.3Co₄O_9+δ.     

Enhancement of microstructure and initial permeability due to Cu substitution in Ni0.50−xCuxZn0.50Fe2O4 ferrites

Structural and magnetic properties of Cu substituted Ni_0.50−xCu_xZn_0.50Fe₂O₄ ferrites (where x=0.0-0.25) prepared by an auto combustion method have been investigated. The X-ray diffraction patterns of these compositions confirmed the formation of the single phase spinel structure. The lattice parameter increases with the increase in Cu²⁺ content obeying Vegard's law. The particle size of the starting powder compositions varied from 22 to 72 nm. The theoretical density increases with increase in copper content whereas the Néel temperature decreases. The bulk density, grain size and permeability increases up to a certain level of Cu²⁺ substitution, beyond that all these properties decrease with increase in Cu²⁺ content. The bulk density increases with increase in sintering temperatures up to 1250 °C for the parent composition, while for substituted compositions it increases up to 1200 °C. Due to substitution of Cu²⁺, the real part of the initial permeability increases from 97 to ∼390 for the sample sintered at 1100 °C and from 450 to 920 for the sample sintered at 1300 °C. The ferrites with higher initial permeability have a relatively lower resonance frequency, which obey Snoek's law. The initial permeability strongly depends on average grain size and intragranular porosity. The saturation magnetization, M_s, and the number of Bohr magneton, n(μ_B)_, decreases up to x=0.15 due to the reduction of the A-B interaction in the AB₂O₄ spinel type ferrites. Beyond that value of x, the M_s and the n(μ_B) values are enhanced. The substitution of Cu²⁺ influences the magnetic parameters due to modification of the cation distribution.     

The correlation between structure and magnetic properties in the manganites La0.7Ca0.3−xTexMnO3 (0≤x≤0.15)

The effect of Te-doping at La-site on structural, magnetic and transport properties in the manganites La_0.7Ca_0.3−xTe_xMnO₃ (0≤x≤0.15) has been investigated. All samples show an orthorhombic structure (O′-Pbnm) at room temperature. It shows that the Mn-O-Mn bond angle decreases and the Mn-O bond length increases with the increase in the Te content. All samples exhibit an insulator-metal (I-M) transition and the resistivity increases with the increase in the Te-doping level. Additionally, the Curie temperature T_c decreases and the transition becomes broader with increasing Te-doping level, in contrast, the magnetization of Te-doping samples at low temperatures decrease with increasing x as x≤0.10 and then increase with further increasing x to 0.15. The results are discussed in terms of Jahn-Teller (JT) vibrational anisotropy Q₃/Q₂ and the opening of the new DE channel between Mn²⁺-O-Mn³⁺ due to the introduction of Mn²⁺ ions because of the substitution of Te⁴⁺ ions for Ca²⁺ ions.     

Al-doping effect on the structural and physical properties of delafossite-type oxide CuCrO2

The structure, Raman spectroscopy, magnetization, and dielectric properties of delafossite-type oxide CuCr_1−xAl_xO₂ have been characterized. It was found that Al substitution generates an anisotropic effect on the structure, besides magnetic dilution. The temperature dependence of all samples exhibits paramagnetic behavior at high temperature. Above x=0.2 the ferromagnetic transition at 120 K disappears. It is argued that Al substitution destabilizes the antiferromagnetic order of Cr³⁺ ions and modulates the spin configuration, leading to a weak ferromagnetism. The coupling between the magnetic order and ferroelectric order is also characterized.