Structure and redox properties of CexPr1−xO2−δ mixed oxides and their catalytic activities for CO, CH3OH and CH4 combustion

A series of Ce_xPr_1−xO_2−δ mixed oxides were synthesized by a sol–gel method and characterized by Raman, XRD and TPR techniques. The oxidation activity for CO, CH₃OH and CH₄ on these mixed oxides was investigated. When the value x was changed from 1.0 to 0.8, only a cubic phase CeO₂ was observed. The samples were greatly crystallized in the range of the value x from 0.99 to 0.80, which is due to the formation of solid solutions caused by the complete insertion of Pr into the CeO₂ crystal lattices. Raman bands at 465 and 1150 cm⁻¹ in Ce_xPr_1−xO_2−δ samples are attributed to the Raman active F_2g mode of CeO₂. The broad band at around 570 cm⁻¹ in the region of 0.3 ≤ x ≤ 0.99 can be linked to oxygen vacancies. The new band at 195 cm⁻¹ may be ascribed to the asymmetric vibration caused by the formation of oxygen vacancies. The TPR profile of Pr₆O₁₁ shows two reduction peaks and the reduction process is followed: . The reduction temperature of Ce_xPr_1−xO_2−δ mixed oxides is lower than those of Pr₆O₁₁ or CeO₂. TPR results indicate that Ce_xPr_1−xO_2−δ mixed oxides have higher redox properties because of the formation of Ce_xPr_1−xO_2−δ solid solutions. The presence of the oxygen vacancies favors CO and CH₃OH oxidation, while the activity of CH₄ oxidation is mostly related to reduction temperatures and redox properties.     

Synthesis, structure and oxygen nonstoichiometry of La0.4Sr0.6Co1−yFeyO3−δ

The samples of La_0.4Sr_0.6Co_1−yFe_yO_3−δ (y = 0.2 and 0.4) were prepared using both conventional ceramic technique and nitrate–citrate precursors technique. The phase identification was made by X-ray diffraction method. The refinement of structural parameters from the XRD and neutron diffraction measurements was performed by full profile Rietveld analysis. Neutron diffraction showed that both samples possess distorted perovskite-type structure. Oxygen nonstoichiometry was measured by chemical analysis and thermogravimetry (TG) analysis in the range 20 ≤ T/°C ≤ 900 and 2E-5 ≤ pO₂/atm ≤ 4E-1. TG-experiments indicate a relatively fast and reversible oxygen exchange at pO₂ > 1E-2 atm. Mass saturation occurs at T < 300 °C upon cooling. The absolute value of oxygen nonstoichiometry was determined by iodometric titration measurements. It was found that both samples have practically stoichiometric composition at 300 °C in air and δ increases with increasing temperature and decreasing oxygen partial pressure.     

Synthesis and low temperature fluorination of the alkaline-earth palladates Ba2−xSrxPdO3 (x = 0–2)

Since the discovery of superconductivity in Sr₂CuO₂F_2+δ there has been an increased interest in ternary oxide-fluorides. Sr₂CuO₂F_2+δ is prepared via low temperature (T = 220 °C) reaction routes. Low temperature fluorination induces an interesting structural rearrangement in the parent compound Sr₂CuO₃, which is a one-dimensional material containing linear chains of vertex sharing CuO₄ squares along the crystallographic b axis. Upon fluorination, one oxide is substituted by two fluorides and Cu²⁺ becomes octahedrally coordinated by four oxides and two fluorides. The fluorinated compound Sr₂CuO₂F_2+δ displays the T-type structure (La₂CuO₄). Insertion of excess fluorine, δ, also takes place and this fluorine occupies interstitial sites in the T structure. Although the starting material Ca₂CuO₃ is isostructural to Sr₂CuO₃, Ca₂CuO₂F_2+δ displays the T′ (Nd₂CuO₄) structure due to the smaller radius of Ca²⁺ compared to that of Sr²⁺.

The alkaline-earth palladates with the general formula A₂PdO₃ (A = Ba, Sr) are isostructural with the A₂CuO₃(A = Ca, Sr) materials. We prepared the Ba_2−xSr_xPdO₃ (x = 0–2) series and performed low temperature fluorination, which led to the synthesis of the series Ba_2−xSr_xPdO₂F_2+δ (0 ≤ x ≤ 1.5). All the compounds in the Ba_2−xSr_xPdO₂F_2+δ series show T′ structure (Ca₂CuO₂F_2+δ). Similarities and differences with Sr₂CuO₂F_2+δ and Ca₂CuO₂F_2+δ will be discussed.     

Mechanical stability and transport properties of the Sn-promoted SrCo0.8Fe0.2O3−δ ceramic membrane

In this article, the phase compositions, thermal, mechanical and transport properties of both the SrCo_0.8Fe_0.2O_3−δ (SCF) and the SrCo_0.8Fe_0.1Sn_0.1O_3−δ (SSCF) ceramic membranes were investigated systematically. As compared with the SCF membrane, the SSCF one had a more promoted thermal shock resistance, which related to its small thermal expansion coefficient between them and an enhanced composite structure for it. For the SCF membrane, a permeation rate of 1.9 × 10⁻⁶ mol cm⁻² s⁻¹ was obtained at 1000 °C and under the oxygen partial pressure gradient of P_O2 (h)/P_O2 (l) = 0.209 atm/0.012 atm; however, the permeation rate was 2.5 × 10⁻⁶ mol cm⁻² s⁻¹ for the SSCF one in the same measuring condition. In addition, both peak values of total electrical conductivity (σ_e) for SSCF sample appeared with increasing temperature. The second peak value of σ_e for SSCF one was regarded as the contribution from its minor phase, which appeared with the mixed conducting behavior resulting from partly Co-dissolving into its lattice.     

Influence of composition and thermal treatment on the properties of Cu2+xTa4O12+δ

Polycrystalline samples of Cu_2+xTa₄O_12+δ were prepared by solid-state reactions. Copper tantalate shows a remarkable compositional flexibility with respect to both the copper and oxygen stoichiometry. Single phase compounds could be synthesised for 0.125 ≤ x ≤ 0.5. Slowly cooled samples are green and possess a pseudo-tetragonal unit cell, which changes to a pseudo-cubic symmetry for x ≥ 0.45. Rapidly cooled aliquots are brown and have a (pseudo-) cubic structure. For both the slow-cooled and quenched samples a linear increase of the oxygen content with x was observed, the values of δ for the latter being significantly smaller. Magnetic measurements reveal a ferrimagnetic transition at 12.5 K, the strength of which is strongly reduced both by increasing the copper content and by quenching.     

Improved dielectric properties of BaxSr1−xTiO3-based composite ceramics derived from core–shell structured nanopowders

We performed a study on the dielectric properties of Ba_xSr_1−xTiO₃–Mg_0.9Zn_0.1O (BST–MZO) composite ceramics derived from core–shell structured nanopowders with the shell of zinc doped MgO and core of Ba_xSr_1−xTiO₃. It was found that the ceramics exhibit a significant improvement in dielectric response under a DC electric field. The Curie temperature decreases more significantly in the BST–MZO composite ceramics compared to that of pure BST ceramics. The tunability of Ba_0.75Sr_0.25TiO₃–40%MZO is 23.49% at 20 °C. The dielectric properties at high frequency also show low dielectric constant and great reduction in dielectric loss. These ceramics are expected to be useful in microwave devices.     

Thermogravimetric study on perovskite-like oxygen permeation ceramic membranes

The oxygen permeation properties of mixed-conducting ceramics SrFeCo_0.5O_3−δ (SFCO), Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ (BSCFO), La_0.2Sr_0.8Co_0.8Fe_0.2O_3−δ (LSCFO) and Ba_0.95Ca_0.05Co_0.8Fe_0.2O_3−δ (BCCFO) were studied by thermogravimetric method in the temperature range 600–900 °C. The results show that the oxygen adsorption rate constants k_a of all material are larger than oxygen desorption rate constants k_d and both k_a and k_d are not strongly dependent on temperature in the studied temperature range. The oxygen vacancy contents δ(N₂) and δ(O₂) in nitrogen and oxygen and their difference Δδ = δ(N₂) − δ(O₂) play an important role in determining the temperature behavior of oxygen permeation flux J_O2.     

Preparation of epitaxial La0.6Ca0.4Mn1−xFexO3 (x = 0, 0.2) thin films: Variation of the oxygen content

Perovskite thin films with a nominal composition of La_0.6Ca_0.4Mn_1−xFe_xO₃ (x = 0, 0.2) were deposited by pulsed reactive crossed beam laser ablation. The film properties, such as electrical conductivity and magnetoresistance are studied as a function of the oxygen content and substrate type. The oxygen content of the thin films was determined by Rutherford Backscattering and controlled by varying the background gas pressure, pressure of the gas pulse and by using alternatively O₂ and N₂O as the gas pulse.

LaAlO₃ and SrTiO₃ were used as substrates at deposition temperature of 650 °C. The grown films were analyzed by X-ray diffraction in order to optimize the growth conditions, i.e. to obtain epitaxial thin films. Thin films doped with 20% Fe were grown under the same experimental conditions as the undoped LCMO films and the effect of the doping on the structural and transport properties of the thin films has been investigated.

The temperature of the metal–insulator transition was measured as a function of the oxygen content and substrate type.     

Excess molar enthalpies for binary mixtures of trimethyl phosphate with alkanols {CH3(CH2)nOH, n = 0–3} at 298.15 K

The excess molar enthalpies () for the binary mixtures of trimethyl phosphate (TMP) with alkanols {CH₃(CH₂)_nOH, n = 0–3} have been measured with an isothermal calorimeter at 298.15 K and atmospheric pressure. The values are positive for all the mixtures over the whole composition range. The values increase in the order methanol < ethanol < 1-propanol < 1-butanol. The experimental results have been correlated with the Redlich–Kister equation.     

Single crystal growth of Bi1−xSrxMnO3—Thermodynamics and experiment

The primary crystallization field of a perovskite solid solution Bi_1−xSr_xMnO_3−δ was delimited by calculating the respective phase equilibria in the quaternary Bi–Sr–Mn–O system. The calculations are based on the recent assessment involving all three ternary subsystems, a quaternary liquid approximated as a mixture of Mn, MnO, Mn₂O₃, SrO and Bi₂O₃ species with binary Redlich–Kister coefficients and the perovskite phase described in terms of a point defect model allowing Sr²⁺ for Bi³⁺ substitution, oxygen vacancy formation and the related Mn³⁺/Mn⁴⁺ mixing on Mn-sublattice. The crystallization path and the composition of the crystallized solid solution are compared with single crystal growth experiments performed by self-flux method from a Bi-rich melt. The crystallization path obtained for a selected feed composition for which the largest and high quality single crystal have been grown, turns out to end very close to the global eutectic point.     

Effects of sintering atmospheres on sintering behavior, electrical conductivity and oxygen permeability of mixed-conducting membranes

Effects of sintering atmospheres on properties of SrCo_0.4Fe_0.5Zr_0.1O_3−δ mixed-conducting membranes were in detail studied in terms of sintering behavior, electrical conductivity and oxygen permeability. The sintering atmospheres were 100% N₂, 79% N₂–21% O₂, 60% N₂–40% O₂, 40% N₂–60% O₂, 20% N₂–80% O₂ and 100% O₂ (in vol.%), and the prepared membranes were correspondingly denoted as S-0, S-21, S-40, S-60, S-80 and S-100, respectively. It was found that the properties of membranes were strongly dependent on the sintering atmosphere. As the oxygen partial pressure in the sintering atmosphere (P_O2) increased, sintering ability, electrical conductivity and oxygen permeability decreased at first, which was in the order of S-0 > S-21 > S-40. However, as P_O2 increased further, sintering ability, electrical conductivity and oxygen permeability increased gradually: S-40 < S-60 < S-80 < S-100. And the S-100 membrane had the best sintering ability, electrical conductivity and oxygen permeability in all membranes.     

A simple method for predicting the frequency of the infrared inactive carbonyl stretching mode in LM(CO)5 molecules with C4V symmetry

The paper presents a new method for predicting the frequency of the b₁ mode, which is infrared-inactive, in complexes of the type LM(CO)₅ belonging to C_4V point group. The method was based on the relation λ₃=λ₄+[(1−δ/δ)](λ₁−λ₂), where δ=(λ₁−λ₂)/(λ₁−λ₂+λ₃−λ₄), λ₁, λ₂, λ₃ and λ₄ are the λ parameters of the , , b₁ and e modes, respectively. For a large numbers of complexes of the type LM(CO)₅ the average value of δ was found to be 0.80, with a standard deviation of 0.02. With the use of average value of δ, the frequencies of b₁ mode were estimated. The result obtained indicated that there exists a rather good fit between observed and calculated frequencies, with a mean error of 2.7 cm⁻¹. In addition, it was shown that the δ parameter can be used as a criterion of the correct band assignment for the complexes understudy.     

Survey of the quasi-ternary system La0.8Sr0.2MnO3–La0.8Sr0.2CoO3–La0.8Sr0.2FeO3

An overview on the variation of the thermal expansion, the electrical conductivity as well as non-stoichiometry of the oxide content as a function of composition within the quasi-ternary system La_0.8Sr_0.2MnO_3−δ–La_0.8Sr_0.2CoO_3−δ–La_0.8Sr_0.2FeO_3−δ in air is presented. The various powders were synthesized under identical conditions. The DC electrical conductivity values of the compositions at 800 °C in air vary in a wide range from 15 to 1338 S cm⁻¹. The magnitude of electrical conductivity of the perovskites is mainly determined by the percentage of cobalt in the compositions. A similar behaviour was observed for the measured thermal expansion coefficients between room temperature and 1000 °C in air, increasing from 10.9 to 19.4 × 10⁻⁶ K⁻¹ as a function of cobalt content. Changes in the oxygen stoichiometry of the materials were characterized by temperature-programmed oxidation measurements.     

Hydrothermal synthesis and intercalation behavior of a layered titanium phosphate Ti2(H2PO4)(HPO4)(PO4)2 · 0.5C6N2H16, with an extended γ-phase intercalated into organic amine

With a hydrothermal technique, a layered titanium phosphate with the formula Ti₂(H₂PO₄)(HPO₄)(PO₄)₂ · 0.5C₆N₂H₁₆ (denoted TP-J2) has been prepared by treating the Ti/H₃PO₄/H₂O/1-methylpiperazine system directly. The as-synthesized products were characterized by powder X-ray diffraction, CP-MAS solid-state ³¹P NMR spectroscopy, thermogravimetric and differential thermal analyses (TG-DTA). The structure was solved by single-crystal X-ray diffraction analysis and it presents an extended γ-phase intercalated with organic amine. Crystal data: triclinic, , a = 8.106 (2) Å, b = 8.197 (2) Å, c = 11.658 (2) Å.  = 78.32 (3)°, β = 80.85 (3)°, γ = 77.90 (3)°, Z = 2. Additionally, the intercalation behavior of TP-J2 with n-alkyl monoamine (n = 2, 3, 4, 6, 8, 10 and 12) was investigated. Owing to the strong brønsted base, N,N′-dimethylpiperazine, resides in the interlayer, it presented unusual features of TP-J2 in contrast with that of γ-Tip.     

I NQR and spectroscopic investigation of impurity-doped and mixed lithium iodate Li1−xHxIO3 crystals

The ¹²⁷I NQR, IR absorption and Raman spectra of impurity-doped and mixed lithium iodate Li_1−xH_xIO₃ crystals grown from water solutions with different LiIO₃/HIO₃ ratios were investigated depending on the content of the impurity hydrogen x. The NQR results suggested that, at small concentration of doping iodic acid x<0.22, the lattice dynamics of the crystal grown from water solution changes significantly though the crystal retains hexagonal symmetry. Spectroscopic studies are compatible with average hexagonal symmetry of the grown doped crystals. From the results of Raman studies at room temperature and 100 K, the concentration range of hydrogen dopant 0.22<x<0.36 was found where disordered solid solution crystals Li_1−xH_xIO₃ are formed.     

Preparation of MoVTe(Sb)Nb mixed oxide catalysts using a slurry method for selective oxidative dehydrogenation of ethane

The preparation of bulk MoVTe(Sb)Nb mixed oxide catalysts using a traditional slurry method, results in highly active catalysts for oxidative dehydrogenation of ethane to ethene. Several major phases including orthorhombic M1, hexagonal M2 or Mo_xM_1−xO_2.8 (M = V or Nb) have been detected in the catalysts from characterization results such as X-ray diffraction (XRD), SEM and EDX analyses. Ethane conversion and yield to ethene increase with increasing content of the M1 phase in the catalysts. The maximum yield of ethene (ca. 87% selectivity and ca. 90% conversion, STY_C2H4 of 176 g  h⁻¹) has been obtained with a MoV_0.31Te_0.2Nb_0.14 mixed oxide catalyst, calcined at 873 K under nitrogen, containing almost pure orthorhombic M1 phase and small amounts of unidentified impurity phases, operating at a relatively low reaction temperature of 673 K. The orthorhombic M1 phase has been shown to be the most active in ethane activation and the most selective for ethene formation. The hexagonal M2 phase is relatively inactive in ethane activation and less selective for ethene formation. The Te-free phases such as Sb₄Mo₁₀O₃₁ and Mo_xM_1−xO_2.8 (M = V or Nb) show the lowest selectivity to ethene.     

Oxygen permeation through a Ce0.8Sm0.2O2−δ–La0.8Sr0.2CrO3−δ dual-phase composite membrane

A composite of oxygen ion conducting oxide Ce_0.8Sm_0.2O_2−δ (60 vol.%) and electron conducting oxide La_0.8Sr_0.2CrO_3−δ was prepared by sintering a powder compact at a temperature of 1550 °C. No significant reaction between the two constituent oxides was observed under preparation and oxygen permeation conditions. Appreciable oxygen permeation fluxes through the composite membrane were measured at elevated temperatures with one side of it exposed to the ambient air and the other side to a flowing helium gas stream. The oxygen flux initially increased with time, and took a long time to reach a steady value. A steady oxygen permeation flux as high as 1.4 × 10⁻⁷ mol cm⁻² s⁻¹ was obtained with a 0.3 mm thick membrane at 950 °C under a relatively small oxygen partial pressure difference of 0.21 bar/0.0092 bar. It was revealed that the overall oxygen permeation process was mainly limited by the transport in the bulk of the membrane in the range of the membrane thickness greater than 1.0 mm, and the limitation by the surface oxygen exchange came into play at reduced thickness of 0.6 mm.     

Refined heat capacity of LaPO4 in the temperature range 0–1600 K

In the present work temperature dependence of heat capacity of cesium tantalum tungsten oxide has been measured first in the range from 7 to 350 K and then between 330 and 630 K, respectively, by precision adiabatic vacuum and dynamic calorimetry. The experimental data were used to calculate standard thermodynamic functions, namely the heat capacity C_p° (T), enthalpy H°(T) − H°(0), entropy S°(T) − S°(0) and Gibbs function G°(T) − H°(0), for the range from T → 0 to 630 K. The structure of CsTaWO₆ is refined by the Rietveld method: space group F d3m, Z = 8, a = 10.3793(2) Å, V = 1118.14(4) Å³. The high-temperature X-ray diffraction was used for the determination of temperature of phase transition and coefficient of thermal expansion.     

Studies of sorption-desorption processes in the CexLa1−xNi5H2 system by DSC

The dependence of the integral enthalpy of hydrogenation (or dehydrogenation) of the intermetallic compounds (IMCs) Ce_xLa_1−xNi₅ (x = 0, 0.05, 0.1 or 0.3) on pressure in the range 0.5–6 MPa was studied by the method of differential scanning calorimetry. It has been shown that at x = 0 and x = 0.05 the absorption (or desorption) proceeds via the formation of a stable intermediate hydride phase.     

Structure analysis and the standard molar enthalpy of formation of a coordination polymer [Co(TO)2Cl2]n (TO = 1,2,4-triazole-5-one)

A coordination polymer was synthesized by the reaction of CoCl₂ with 1,2,4-triazole-5-one (TO) and charaterized by means of IR and TG–DTG. Single-crystal structure analysis showed that the complex crystallized in the monoclinic space group C2/c: a = 23.105(9) Å, b = 3.5683(2) Å, c = 13.589(6) Å,  = 90°, β = 124.038(4)°, γ = 90°, V = 928.4(7) Å³, Z = 4. The standard molar enthalpy of formation of the complex was determined to be (−1034.28 ± 0.95) kJ mol⁻¹.