Chimie douce preparation of CuxZn3−xV2O7(OH)2·yH2O isostructural to trigonal zinc pyrovanadate

New Cu_xZn_3−xV₂O₇(OH)₂·yH₂O (0 < x ≤ 1.5) isostructural to zinc pyrovanadate Zn₃V₂O₇(OH)₂·2H₂O, were successfully prepared by using a chimie douce technique. The method consists in mixing zinc nitrate and copper nitrate with a boiling solution of vanadium oxide (obtained by reacting V₂O₅ with few millilitres of 30 vol.% H₂O₂ followed by addition of distilled water). When ammonium hydroxide NH₄OH 10% was added (pH ≈ 6), a precipitate was obtained. Using powder X-ray diffraction data, the crystal structures of as-prepared samples were determined by Rietveld refinement. Copper substitutes zinc in the zinc pyrovanadate lattice and is found to introduce distortion in the structure, which is mainly due to the Jahn–Teller effect. Distortion becomes more pronounced when the amount of copper is increased. This restricts the amount of copper which can be incorporated in the hexagonal zinc pyrovanadate lattice.     

Solvothermal synthesis and crystal structure of the Mo(VI)-bridged helical chain containing Mo2(V) dimers: (C4H12N2)2[(MoV2O4)(MoVIO4)(C2O4)2]·2H2O

A new molybdenum complex (C₄H₁₂N₂)₂[(Mo^V₂O₄)(Mo^VIO₄)(C₂O₄)₂]·2H₂O, was solvothermally synthesized and characterized by single-crystal X-ray diffraction. The structure of the compound consists of oxalate acid-coordinated mixed-valent [Mo^V₂O₄][Mo^VIO₄] helical chains and protonated piperazine cations. The helical chains are built up from the [Mo^V₂O₄] units and [Mo^VIO₄] tetrahedral. The central axis about helical chain is a 2-fold screw axis. The compound crystallizes in the space group P2₁/n of monoclinic system with a = 11.396(2) Å, b = 14.107(3) Å, c = 15.805(3) Å, β = 102.09(3)°, V = 2484.6(9) Å³, Z = 4. Other characterizations by elemental analysis, IR, and thermal analysis for this compound are also given.     

V2O5·0.6H2O nanoribbons as cathode material for asymmetric supercapacitor in K2SO4 solution

V₂O₅·0.6H₂O nanoribbons were prepared and their electrochemical behaviors in K₂SO₄ aqueous solution were investigated. Results show for the first time that K⁺ ions could intercalate/deintercalate reversibly in the V₂O₅·0.6H₂O lattice. An asymmetric supercapacitor activated carbon/0.5 mol/l K₂SO₄/V₂O₅·0.6H₂O was successfully assembled, which could be cycled reversibly in the voltage region of 0–1.8 V. This supercapacitor presents an energy density of 29.0 Wh/kg based on the total mass of the active electrode materials, a very good rate behavior with energy density of 20.3 Wh/kg at power density of 2 kW/kg, and also a rather good cycling performance.     

Two novel Keggin tungstocobaltates grafted by cobaltII complex group(s): K[Co(phen)2(H2O)]2[HCoW12O40]·2H2O and [Co(2,2′-bipy)3]1.5{[Co(2,2′-bipy)2(H2O)][HCoW12O40]}·0.5H2O

Two novel inorganic–organic hybrid compounds composed of Keggin tungstocobaltate framework and cobalt(II)–N coordination complexes, K[Co(phen)₂(H₂O)]₂[HCoW₁₂O₄₀]·2H₂O (1) (phen = 1,10-phenanthroline) and [Co(2,2′-bipy)₃]_1.5{[Co(2,2′-bipy)₂(H₂O)][HCoW₁₂O₄₀]·0.5H₂O (2) (bipy = bipyridine), have been synthesized under hydrothermal conditions by directly using Keggin POMs as starting materials, which were characterized by elemental analyses, IR, TG analyses and X-ray single crystal diffraction. Crystal data for compound 1: C₄₈H₄₁Co₃KN₈O₄₄W_12, triclinic, space group P-1, a = 10.918(5) Å, b = 13.401(5) Å, c = 13.693(5) Å, α = 69.291(5)°, β = 71.568(5)°, γ = 78.421(5)°, V = 1768.9(12) Å³, Z = 1; for compound 2: C₁₃₀H₁₀₄Co₇N₂₆O₈₃W_24, orthorhombic, space group, C2/c, a = 46.839(9) Å, b = 14.347(3) Å, c = 26.147(5) Å, α = β = γ = 90°, V = 17,570(6) Å³, Z = 4. Compound 1 exhibits a pseudo-1D chainlike structure, in which potassium ions act as linkages of Keggin unit doubly grafted by [Co(phen)₂(H₂O)] complex. Compound 2 represents a [Co(2,2′-bipy)₂(H₂O)]²⁺ mono-grafted Keggin tungstocobaltate derivative with 1.5[Co(2,2′-bipy)₃]²⁺ countercations. The cyclic voltammetric behavior of 1-CPE is similar to the parent 3-CPE, but the cyclic voltammetric behavior of Co^II shows a little difference. Variable-temperature magnetic susceptibility measurement of compound 1 demonstrates the presence of antiferromagnetic interactions.     

Organic derivatives of tin (II/IV): Investigation of their structure

The structures of tin(II)-oxalate, tin(IV)Na–EDTA and tin(IV)Na₈-inositol hexaphosphate were investigated using XRD analysis. Samples were identified using the Mössbauer study, thermal analysis and FTIR spectrometry. The Mössbauer study determined two different oxidation states of tin atoms, and consequently two different tin surroundings in the end products. The tin oxalate was found to be orthorhombic with space group Pnma, a=9.2066(3) Å, b=9.7590(1) Å, c=13.1848(5) Å, V=1184.62 Å³ and Z=8. SnNa–EDTA was found to be monoclinic with space group P2₁/c₁, a=10.7544(3) Å, b=10.1455(3) Å, c=16.5130(6) Å, β=98.59(2)°, V=1781.50(4) Å³ and Z=4. Sn(C₆H₆Na₈O₂₄P₆) was found to be amorphous.     

(Solid + liquid) isothermal evaporation phase equilibria in the aqueous ternary system (Li2SO4 + MgSO4 + H2O) at T = 308.15 K

The solubility and the density in the aqueous ternary system (Li₂SO₄ + MgSO₄ + H₂O) at T = 308.15 K were determined by the isothermal evaporation. Our experimental results permitted the construction of the phase diagram and the plot of density against composition. It was found that there is one eutectic point for (Li₂SO₄ · H₂O + MgSO₄ · 7H₂O), two univariant curves, and two crystallization regions corresponding to lithium sulphate monohydrate (Li₂SO₄ · H₂O) and epsomite (MgSO₄ · 7H₂O). The system belongs to a simple co-saturated type, and neither double salts nor solid solution was found. Based on the Pitzer ion-interaction model and its extended HW models of aqueous electrolyte solution, the solubility of the ternary system at T = 308.15 K has been calculated. The predicted solubility agrees well with the experimental values.     

Excess thermodynamic properties of binary mixtures of N,N-dimethylacetamide with water or water-d2 at temperatures from 277.13 K to 318.15 K

Densities of binary mixtures of N,N-dimethylacetamide (DMA) with water (H₂O) or water-d₂ (D₂O) were measured at the temperatures from T=277.13 K to T=318.15 K by means of a vibrating-tube densimeter. The excess molar volumes V_m^E, calculated from the density data, are negative for the (H₂O + DMA) and (D₂O + DMA) mixtures over the entire range of composition and temperature. The V_m^E curves exhibit a minimum at x(DMA)≅0.4. At each temperature, this minimum is slightly deeper for the (D₂O + DMA) mixtures than for the corresponding (H₂O + DMA) mixtures. The difference between D₂O and H₂O systems becomes smaller when the temperature increases. The V_m^E results were correlated using a modified Redlich–Kister expansion. The partial molar volume of DMA plotted against x(DMA) goes through a sharp minimum in the water-rich region around x(DMA)≅0.08. This minimum is more pronounced the lower the temperature and is deeper in D₂O than in H₂O at each temperature. Again, the difference becomes smaller as the temperature increases. The excess expansion factor α^E plotted against x(DMA) exhibit a maximum in the water rich region of the mole fraction scale. At each temperature, this maximum is higher for the (D₂O + DMA) mixtures than for the corresponding (H₂O + DMA) mixtures, and the difference becomes smaller as the temperature increases. At its maximum, α^E can be even more than 25 per cent of total value of the cubic expansion coefficient α in the (H₂O + DMA) and (D₂O + DMA) mixtures.     

Esterification of acetic acid with n-Butanol using vanadium oxides supported on γ-alumina

Esterification of acetic acid with n-Butanol has been studied in a heterogeneous reaction system using two γ-alumina-supported vanadium oxide catalysts with different V loadings, which were prepared by the impregnation of a precipitated alumina. The alumina support and the supported catalysts were characterized using X-ray diffraction, N₂ adsorption, EDX analysis and NH₃-TPD techniques. The effects of the reaction time, of the molar ratio of the reactants, of the speed of agitation and of the mass fraction of the catalyst on the catalytic properties were studied. In the presence of the supported catalyst containing 10 wt % V₂O₅ (10V-Al₂O₃ sample) the conversion reached 87.7% after 210 min of reaction at 100 °C with an n-Butanol-to-acetic acid mole ratio equal to one. The conversion as well as the total acidity measured by TPD of NH₃ increased in the following order: Al₂O₃ < 5V-Al₂O₃ (5 wt % V₂O₅/Al₂O₃) < 10V-Al₂O₃. In all cases the reaction was completely selective to n-butyl acetate. Nevertheless, a loss in catalytic activity after three reaction cycles with 10 V₂O₅–Al₂O₃ catalyst was observed.     

Inhibitors for magnesium corrosion: Metal organic frameworks

Electrochemical measurements demonstrate that magnesium surfaces can be protected by alkyl carboxylate. In a nearly neutral pH solution of sodium decanoate, the reduced corrosion rate and a passivation behaviour are attributed to the formation of Mg(C₁₀H₁₉O₂)₂(H₂O)₃ (Mg(C10)₂) at the magnesium surface whereas heptanoate Mg(C₇H₁₃O₂)₂(H₂O)₃ (Mg(C7)₂) is not efficient in such media. The crystal structures of the two metal carboxylates Mg(C7)₂ and Mg(C10)₂ are determined by X-ray diffraction. Single crystal data: Mg(C7)₂, P2₁/a, a = 9.130(5) Å, b = 8.152(5) Å, c = 24.195(5) Å, β = 91.476(5)°, V = 1800.3(15) Å³, D_x = 1.242 g cm⁻³, Z = 4. Synchrotron powder data: Mg(C10)₂, P2₁/a, a = 9.070(3) Å, b = 8.165(1) Å, c = 32.124(1) Å, β = 98.39(1)°, V = 2353.85(8) Å³, D_x = 1.188 g cm⁻³, Z = 4. Their layered structures are quite similar and differ mainly by the length of the hydrophobic chains. They consist of two planes of O-octahedra centred by Mg atoms, parallel to (001). The distorted octahedra are constituted by three oxygen atoms from carboxylate groups and by three oxygen atoms coming from water molecules. The layers are connected by hydrogen bonds. The carboxylate chains are located perpendicularly and on both sides of these planes. One carboxylate chain is bridging the Mg atom along [010] while the other is monodendate. The presence of structural water is confirmed by thermal analyses.     

(Liquid + solid) metastable equilibria in quinary system Li2CO3 + Na2CO3 + K2CO3 + Li2B4O7 + Na2B4O7 + K2B4O7 + H2O at T=288 K for Zhabuye salt lake

An experimental study on metastable equilibria at T=288 K in the quinary system Li₂CO₃ + Na₂CO₃ + K₂CO₃ + Li₂B₄O₇ + Na₂B₄O₇ + K₂B₄O₇ + H₂O was done by isothermal evaporation method. Metastable equilibrium solubilities and densities of the solution were determined experimentally. According to the experimental data, the metastable equilibrium phase diagram under the condition saturated with Li₂CO₃ was plotted, in which there are four invariant points; nine univariant curves; six fields of crystallization: K₂CO₃ · 3/2H₂O, K₂B₄O₇ · 5H₂O, Li₂B₂O₄ · 16H₂O, Na₂B₂O₄ · 8H₂O, Na₂CO₃ · 10H₂O, NaKCO₃ · 6H₂O. Some differences were found between the stable phase diagram at T=298 K and the metastable one at T=288 K.     

Thermodynamic study of the system (LiCl + CaCl2 + H2O)

Solubility isotherms of the ternary system (LiCl + CaCl₂ + H₂O) were elaborately determined at T = (283.15 and 323.15) K. Several thermodynamic models were applied to represent the thermodynamic properties of this system. By comparing the predicted and experimental water activities in the ternary system, an empirical modified BET model was selected to represent the thermodynamic properties of this system. The solubility data determined in this work at T = (283.15 and 323.15) K, as well as those from the literature at other temperatures, were used for the model parameterization. A complete phase diagram of the ternary system was predicted over the temperature range from (273.15 to 323.15) K. Subsequently, the Gibbs free energy of formation of the solid phases CaCl₂ · 4 H₂O_(s), CaCl₂ · 2 H₂O_(s), LiCl · 2H₂O_(s), and LiCl · CaCl₂ · 5H₂O_(s) was estimated and compared with the literature data.     

High capacity Li[Li0.2Mn0.54Ni0.13Co0.13]O2–V2O5 composite cathodes with low irreversible capacity loss for lithium ion batteries

With an aim to suppress the huge irreversible capacity loss encountered in high capacity layered oxide solid solutions between Li₂MnO₃ and LiMO₂ (M = Mn, Ni, and Co), layered Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂–V₂O₅ composite cathodes with various V₂O₅ contents have been investigated. The irreversible capacity loss decreases from 68 mAh/g at 100% Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂ to 0 mAh/g around 89 wt.% Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂–11 wt.% V₂O₅ as the lithium-free V₂O₅ serves as an insertion host to accommodate the lithium ions that could not be inserted back into the layered lattice after the first charge. The Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂–V₂O₅ composite cathodes with about 10–12 wt.% V₂O₅ exhibit an attractive discharge capacity of close to 300 mAh/g with little irreversible capacity loss and good cyclability.     

Oxygen reduction behavior of RuO2/Ti,IrO2/Ti and IrM (M: Ru,Mo, W,V) Ox/Ti binary oxide electrodes in a sulfuric acid solution

Some oxide catalysts, such as RuO₂/Ti, IrO₂/Ti and IrM(M: Ru, Mo, W, V)O_x/Ti binary oxide electrodes, were prepared by using a dip-coating method on a Ti substrate. Their catalytic behavior for the oxygen reduction reaction (ORR) was evaluated by cyclic voltammetry in 0.5 M H₂SO₄ at 60 °C. These catalysts were found to exhibit considerably high activity, and the most active one among them was Ir_0.6V_0.4O₂/Ti prepared at 450 °C, showing onset potential for the ORR at about 0.86 V–0.90 (vs RHE).     

Vanadium oxide-porous phosphate heterostructure catalysts for the selective oxidation of H2S to sulphur

Vanadium oxide–containing mesoporous materials, based on a surfactant expanded zirconium phosphate with silica galleries into the interlayer space, named porous phosphate heterostructure (PPH), were prepared by using TEOS and vanadium oxytripropoxide in n-propanol as sources of Si and V, respectively; with different Si/V molar ratios of 1, 2, 5 and 25; and calcining at 550 °C for 6 h. Using this method, vanadium can be partially incorporated to the structure of the gallery, but the surface area strongly decreases and the appearance of V₂O₅ crystallites increases when increasing the vanadium content. The catalysts were characterized by XRD, XPS, TEM, and Raman, and tested in the selective catalytic oxidation of H₂S using a fixed bed reactor, at atmospheric pressure, at 180–260 °C. The catalysts with high contents of vanadium are very active at 200 °C, showing H₂S conversions of 85–99%, with a high selectivity to elemental sulphur and with a low formation of SO₂. Accordingly V₂O₅ crystallites can be proposed as active and selective although the catalytic behavior is related to the number of accessible V-sites in the surface of the catalyst.     

Two metal-organic frameworks with infinite indium hydroxide chains connected through tetradentate carboxylate linkers

Two indium-based metal-organic framework have been hydrothermally synthesized by using 1,2,4,5-benzenetetracarboxylate (pyromellitate) or 3,3′,4,4′-benzophenonetetracarboxylate as linkers. Their structures have been characterized by means of single-crystal X-ray diffraction analysis and reveal closely related networks consisting of identical infinite chains of indium-centered trans-connected octahedra, linked to each other through the tetradentate carboxylate linkers. The structure of the indium pyromellitate (MIL-60) delimits a 3D frameworks with one-dimensional 4.0 × 2.7 Å² channels running along [001] encapsulating water. The second compound (MIL-119) is built up from the compact stacking of the 3,3′,4,4′-benzophenonetetracarboxylate molecules connected to four distinct inorganic chains. In the latter, water species are found to be trapped between two indium hydroxide chains or in terminal positions, bonded to the indium cations. Strong hydrogen interactions are observed between these types of water molecules. Both compounds do not exhibit any significant porosity.Crystal data: In₂(OH)₂[C₁₀O₈H₂]·2H₂O (MIL-60): monoclinic, C2/m, a = 7.1854(7) Å, b = 17.1940(17) Å, c = 6.5167(7) Å, β = 100.639(2)°, V = 791.27(14) Å³, Z = 2. In₂(OH)₂(H₂O)[C₁₇O₉H₆]·H₂O (MIL-119), monoclinic, P2₁/c, a = 14.2530(11) Å, b = 14.4024(10) Å, c = 11.7027(9) Å, β = 93.018(2)°, V = 2399.0(3) Å³, Z = 4.     

Sensing characteristics of aged zirconia-based hydrogen sensor utilizing Zn–Ta-based oxide sensing-electrode

We report here the enhanced sensing characteristics to H₂ for a potentiometric sensor using an yttria-stabilized zirconia (YSZ) solid electrolyte and a ZnO(+ 84 wt.% Ta₂O₅) sensing electrode (SE) after aging at 500 °C. The emf response toward 400 ppm H₂ was found to gradually increase up to − 800 mV after 40 days operation (aging) and was stabilized at this value until the 90th day. The aged and stabilized sensor exhibited highly sensitive response to H₂, with minor responses toward other examined gases such as NOx and HCs. The 90% response time toward 100 ppm H₂ was approximately 70 s. The H₂ sensitivity of the stabilized sensor was hardly affected by changes in water vapor as well as O₂ concentration, with repeatable and reproducible responses to H₂.     

Thermodynamic properties of two zinc borates: 3ZnO·3B2O3·3.5H2O and 6ZnO·5B2O3·3H2O

Two pure zinc borates with microporous structure 3ZnO·3B₂O₃·3.5H₂O and 6ZnO·5B₂O₃·3H₂O have been synthesized and characterized by XRD, FT-IR, TG techniques and chemical analysis. The molar enthalpies of solution of 3ZnO·3B₂O₃·3.5H₂O(s) and 6ZnO·5B₂O₃·3H₂O(s) in 1 mol · dm⁻³ HCl(aq) were measured by microcalorimeter at T = 298.15 K, respectively. The molar enthalpies of solution of ZnO(s) in the mixture solvent of 2.00 cm³ of 1 mol · dm⁻³ HCl(aq) in which 5.30 mg of H₃BO₃ were added were also measured. With the incorporation of the previously determined enthalpy of solution of H₃BO₃(s) in 1 mol · dm⁻³ HCl(aq), together with the use of the standard molar enthalpies of formation for ZnO(s), H₃BO₃(s), and H₂O(l), the standard molar enthalpies of formation of −(6115.3 ± 5.0) kJ · mol⁻¹ for 3ZnO·3B₂O₃·3.5H₂O and −(9606.6 ± 8.5) kJ · mol⁻¹ for 6ZnO·5B₂O₃·3H₂O at T = 298.15 K were obtained on the basis of the appropriate thermochemical cycles.     

About the OH yield in the radiolysis of an aqueous/H2O2 system. Its optimisation for water treatment

Unless the radiolytic reducing species are neutralised or converted into oxidising species, an EB remediation system cannot be considered a true Advanced Oxidation Processes (AOP). A water/H₂O₂ system irradiated by UVC mercury lamps constitutes a widely used OH production method. Employing H₂O₂ in radiolysis as well, an enhancement of the oxidative efficiency of an EB treatment can be obtained. Pulse radiolysis measurements of an aerated aqueous/H₂O₂/KSCN system have been systematically undertaken to assess the optimal H₂O₂ concentration. By linearly fitting a competition kinetics relationship, it is found that the scavengeable extra-yield of OH is ΔG(OH)=0.24 μmol J^?1 (R=0,9958), while the maximum experimental yield is measured G(OH)_max=(0.52±0.02) μmol J^?1 when [H₂O₂]=5–10 mM. Exceeding these concentrations the OH yield drops off.     

Synthesis,thermal behaviour and crystal structure of RbSrP3O9·3 H2O

Rubidium strontium cyclo-triphosphate trihydrate, RbSrP₃O₉·3 H₂O, was synthesized by reaction between cyclo-triphosphoric acid H₃P₃O₉ and rubidium and strontium carbonates. It crystallizes in the othorhombic system, space group Pnma, with a = 9.120(1) Å, b = 8.141(1) Å, c = 15.234(1) Å, V = 1 131.1(3) Å³, Z = 4. Crystal structure determination from single crystal data collected at 300 K shows that the P₃O₉ groups exhibit C_s symmetry and are not connected to each other. Rubidium (distorted octahedron) and strontium (distorted square antiprism) are coordinated by oxygen and water molecules yielding the formation of infinite chains interconnected to each other and to the P₃O₉ groups. The IR valence vibration bands of the P₃O₉ cycle have been identified in the domain 1 400–650 cm^–1 and related to the structural results. After water loss, the anhydrous phase crystallizes from an intermediate amorphous phase and further decomposes into Rb₂SrP₄O₁₂ and SrP₂O₆.     

The new high-pressure borate Co7B24O42(OH)2·2 H2O—Formation of edge-sharing BO4 tetrahedra in a hydrated borate

The new borate hydrate Co₇B₂₄O₄₂(OH)₂·2 H₂O was synthesized under high-pressure/high-temperature conditions of 6 GPa and 880 °C in a Walker-type multianvil apparatus. The compound crystallizes in the orthorhombic space group Pbam (Z=2) with the lattice parameters a=819.0(2), b=2016.9(4), c=769.9(2) pm, V=1.2717(4) nm³, R₁=0.0758, wR₂=0.0836 (all data). The new structure type of Co₇B₂₄O₄₂(OH)₂·2 H₂O is built up from corner-sharing BO₄ tetrahedra forming corrugated layers, that are interconnected among each other by two edge-sharing BO₄ tetrahedra (B₂O₆ units) forming Z-shaped channels. Interestingly, the here presented structure of Co₇B₂₄O₄₂(OH)₂·2 H₂O is closely related to the structures of M₆B₂₂O₃₉·H₂O (M=Fe, Co), which exhibit BO₄ tetrahedra in an intermediate state on the way to edge-sharing BO₄ tetrahedra.