Influence of low Co substitution on magnetoelastic properties of HoFe11Ti intermetallic compound

The thermal expansion and magnetostriction of HoFe_11−xCo_xTi (x=0, 0.3, 0.7 and 1) intermetallic compounds were measured, using the strain gauge method in the temperature range 77–590 K under applied magnetic fields up to 1.5 T. Results show that for samples with x=0 and 0.3, both linear thermal expansion and linear thermal expansion coefficient exhibit anomalies below the Curie temperature. Below room temperature, the spontaneous volume magnetostriction decreases with Co content. For all compounds studied, the anisotropic magnetostriction shows similar behaviour in the measured temperature range. The magnetostriction compensation occurs above room temperature in all samples. The volume magnetostriction shows a linear dependence on the applied field and by approaching the Curie temperature this trend changes to parastrictive behaviour. The results of the spontaneous magnetostriction are discussed based on the local magnetic moment model. The contribution of magnetostriction attributed to the magnetic sublattices R and T (Fe or Co) is discussed.     

A study on magnetoelastic properties of Tb3 (Fe28−xCox) V1.0 (x=0, 3, 6) compounds

In this work, The magnetoelastic properties of polycrystalline samples of Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) intermetallic compounds are investigated by means of linear thermal expansion and magnetostriction measurements in the temperature range of 77–515 K under applied magnetic fields up to 1.5 T. The linear thermal expansion increases with the Co content. The well-defined anomalies observed in the linear thermal expansion coefficients for Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) compounds are associated with the magnetic ordering temperature for x=0 and spin reorientation temperatures for x=3, 6. Below transition temperatures, the value of the longitudinal magnetostriction (λ_Pa) at 1.6 T increases with Co content.     

A comparative study of the magnetoelastic properties of the YFe10V2 and NdFe10V2 compounds

The magnetoelastic properties of iron-rich REFe₁₀V₂ (RE=Nd, Y) compounds were studied via magnetostriction and thermal expansion measurements in the 5–300 K range of temperature in up to 6 T external fields. Results of thermal expansion analysis show that the spontaneous magnetostriction of the compounds mostly originates from itinerant magnetization. Besides, the small volume striction appearing in the thermal expansion of the Nd compound close to 50 K suggests the existence of a basal to conical spin re-orientation transition. The volume magnetostriction isotherms of both compounds take minimum values for external field corresponding to the anisotropy field. In addition, the anisotropic and the volume magnetostriction traces of the NdFe₁₀V₂ take marked maxima under low field, with a relatively large initial magnetostrictivity, again more pronounced at the conical–axial spin re-orientation transition (T_SR=130 K). Analysis of the anisotropic magnetostriction of the Nd compound leads to the conclusion that the contribution of Nd–Fe interactions is negligible. The temperature dependence of volume magnetostriction is in good agreement with prediction of a phenomenological model based upon a fluctuating local band theory. This analysis shows that the difference between the forced volume strictions of Y and Nd compounds below and above T_SR originates from the Nd sublattice magnetization.     

High magnetostriction at low fields of (Tb1−xDyx)0.2Pr0.8(Fe0.4Co0.6)1.88C0.05 intermetallic compounds

The structure and magnetostriction of the (Tb_1−xDy_x)_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 intermetallic compounds (0≤x≤1) were studied by X-ray diffraction and magnetic measurements. The formation of an approximate single Laves phase with a MgCu2-type cubic structure was observed in this series of compounds. It was found that the Curie temperature and the saturation magnetization of the compounds would decrease with increase in the Dy content up to x=1. The magnetostriction λ_a (λ_a=λ_‖-λ_⊥) gently rises when x≤0.6, and follows with a precipitous fall when x exceeds 0.6, with the highest value of λ_a being reached in the compounds with x=0.6. The magnetostriction of all the samples was observed to approach their own saturation in the magnetic fields higher than 4 kOe. This indicates that the addition of a small amount of Dy could effectively improve the low-field magnetostriction of the Tb_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 compounds, which could become a kind of promising magnetostrictive material.     

Study on dielectric and magnetic properties of Ho3Fe5O12 ceramics

Ho₃Fe₅O₁₂ ceramics with garnet structure were prepared by the solid-state reaction method. The results revealed the existence of Fe²⁺ ions have intensive influence on dielectric and magnetic properties of Ho₃Fe₅O₁₂ ceramics, which could be further confirmed by oxygen treatment. With a magnetic field lower than 10 kOe, the ME coefficient reaches 33 ps m⁻¹ at room temperature. And the ME coupling was further verified by dielectric anomaly near Néel temperature.     

Forced volume magnetostriction in Mn3.3Sn0.7C compound at room temperature

The negative volume magnetostriction in the external magnetic field for antiperovskite Mn_3.3Sn_0.7C compound is discovered. Its magnetic transition temperature from paramagnetism to ferrimagnetism is 348 K. The linear and volume magnetostrictions were investigated by measuring the change in length along the three-dimensional directions of the square samples at room temperature. Volume contraction was observed along all of the three directions throughout the whole magnetization. The value of volume magnetostriction is −44×10⁻⁶ at 1.5 T. The magnetization saturates basically at 1.5 T, however the volume magnetostriction should be higher with further increase in magnetic field.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Magnetic exchange driven magnetoelastic properties in GdCu2

The magnetoelastic properties of GdCu₂ have been investigated by thermal expansion and magnetostriction measurements. GdCu₂ orders antiferromagnetically with a noncollinear magnetic structure. The anisotropic magnetostriction is of similar magnitude as in other RCu₂ compounds and can be explained by a contribution of the bilinear exchange interaction to the magnetoelastic energy. For several compounds this contribution is as important as the single ion magnetoelastic exchange. The pressure dependence of the Néel temperature of GdCu₂ is found to be in agreement with the data of thermal expansion.     

Structure and magnetostriction of Tb0.2Pr0.8(Fe0.4Co0.6)1.93−xCx intermetallic compounds

The structure and magnetostriction of Tb_0.2Pr_0.8(Fe_0.4Co_0.6)_1.93−xC_x intermetallic compounds were studied by X-ray diffraction and magnetic measurements. Almost a single cubic Laves phase forms in the alloys for x ≤0.20, and a small amount of C can inhibit the formation of the 1:3 phase. The lattice parameter increases when 0≤x≤0.15, while the T_c and the spontaneous magnetization decreases with increasing x. The lattice parameter decreases slowly when 0.15≤x≤0.30, while the T_c decreases evidently with increasing x. The magnetostriction λ_a (=λ_∥-λ_⊥) is improved at low magnetic fields at room temperature for the compounds with 0.05≤x≤0.10, indicating that these C-containing compounds are promising magnetostrictive materials.     

Neutron powder diffraction and magnetic studies of mesoporous Co3O4

Samples of mesoporous Co₃O₄, created by using mesoporous silicas KIT-6 and SBA-16 as hard templates to control the growth of Co₃O₄ have been investigated with SQUID magnetometry and neutron powder diffraction, to reveal the effects of high surface area on the magnetic and electronic properties. DC magnetic susceptibility measurements show lower Néel ordering temperatures and lower magnetic moments than in a “bulk” reference. A lower second transition temperature is also observed in the mesoporous samples, associated with the freezing of the surface (shell) magnetic moments. Measurements taken with increasing applied field at constant temperature show the materials to be antiferromagnetic as expected. Complementary parametric neutron powder diffraction studies show similar trends between the two mesoporous samples when looking at their Néel temperatures, and verify long range order within the samples.     

Magnetoelastic properties of GdMn6Sn6 intermetallic compound

We studied the thermal expansion and magnetostriction of polycrystalline samples of GdMn₆Sn₆ intermetallic compound with hexagonal HfGe₆Fe₆-type structure in the temperature range of 77-520 K. The thermal expansion measurement of the sample shows anomalous behavior around its T_C=434 K and T_M=309 K, possibly the point of collapse-like reduction of Mn moments. In addition, the isofield curves of anisotropic and volume magnetostriction reveal anomalies around paramagnetic to ferrimagnetic phase transition. The obtained experimental results are discussed in the framework of two-magnetic sublattices by bearing in mind the lattice parameter dependence of interlayer Mn-Mn exchange interaction in this layered compound. From the temperature dependence of magnetostriction values and considering the magnetostriction relation of a hexagonal structure, we attempt to determine the signs of some of the magnetostriction constants as well as a comparison of their orders of magnitude for this compound.     

Irreversible magnetovolume effect in Nd7Rh3 single crystal

Magnetovolume effect in Nd₇Rh₃ single crystal has been studied by measuring the magnetostriction as a function of external magnetic field at 4.2 K. An irreversible magnetovolume effect having a negative remanent volume magnetostriction was observed when the external magnetic field was applied along the b-axis. The irreversible magnetostrictive effect takes place in the longitudinal magnetostriction along the b-axis. The remanent magnetostriction along the b-axis relaxes after removing external magnetic field for several hours and equilibrium state is stabilized.     

Magnetoelastic properties of ErMn6Sn6 intermetallic compound

The thermal expansion and magnetostriction of polycrystalline sample of the ErMn₆Sn₆ intermetallic compound with hexagonal HfFe₆Ge₆-type structure are investigated in the temperature range of 77 K to above 400 K. The thermal expansion measurement of the sample shows anomalous behavior around its T_N=340 K. The isofield curves of volume magnetostriction also reveal anomalies at paramagnetic-antiferromagnetic and antiferromagnetic-ferrimagnetic phase transitions. In the antiferromagnetic state, the transition to ferrimagnetism can be induced by an applied magnetic field. The threshold field for the metamagnetic transition H_th increases from 0.18 T at 84 K to about 1 T around 220 K, and then decreases monotonously to T_N. This behavior is well consistent with that observed earlier on magnetization curves attributed to exchange-related metamagnetic transition rather than the anisotropy-related one. Furthermore, the low H_th values suggest that the Mn-Mn coupling in ErMn₆Sn₆ is not so strong. The experimental results obtained are discussed in the framework of two-magnetic sublattice by bearing in mind the lattice parameter dependence of the interlayer Mn-Mn exchange interaction in this layered compound. From the temperature dependence of magnetostriction values and considering the magnetostriction relation of a hexagonal structure, we attempt to determine the signs of some of the magnetostriction constants for this compound.     

Influence of H and N insertion on the magnetostriction and thermal expansion of YFe10V2Zx (Z=N,H) compositions

Experimental results on the thermal expansion and magnetostriction of YFe₁₀V₂ composites are reported and the influence of H and N interstitial atoms is studied. The anisotropic magnetostriction is about 30% larger in the composite than in the starting alloy. Also, the anisotropic magnetostriction remains positive after insertion of H (N) ion while the sign of volume magnetostriction changes by hydrogenation. The anisotropic magnetoelastic interactions are enhanced by insertion of H and especially N interstitial atoms. The results are discussed considering the effect of H and N, and of temperature on magnetic anisotropy and microstructure.     

Magnetocrystalline anisotropy in RAu2Ge2 (R = La, Ce and Pr) single crystals

Anisotropic magnetic properties of single crystalline RAu₂Ge₂ (R=La, Ce and Pr) compounds are reported. LaAu₂Ge₂ exhibits a Pauli-paramagnetic behaviour whereas CeAu₂Ge₂ and PrAu₂Ge₂ show an antiferromagnetic ordering with Nèel temperatures T_N = 13.5 and 9 K, respectively. The anisotropic magnetic response of Ce and Pr compounds establishes [0 0 1] as the easy axis of magnetization and a sharp spin-flip type metamagnetic transition is observed in the magnetic isotherms with H // [0 0 1]. The transport and magnetotransport behaviour of these compounds, in particular LaAu₂Ge₂, indicate an anisotropic Fermi surface. The magnetoresistivity of CeAu₂Ge₂ apparently reveals the presence of a residual Kondo interaction. A crystal electric field analysis of the anisotropic susceptibility in conjunction with the experimentally inferred Schottky heat capacity enables us to propose a crystal electric field level scheme for Ce and Pr compounds. For CeAu₂Ge₂ our values are in excellent agreement with the previous reports on neutron diffraction. The heat capacity data in LaAu₂Ge₂ show clearly the existence of Einstein contribution to the heat capacity.     

A survey on the effect of vanadium content on the magnetoelastic properties of YFe12−xVx alloys

Experimental results on the thermal expansion and magnetostriction of YFe_12−xV_x (1.5≤x≤3.5) alloys are reported. The results show that the anisotropic magnetostriction (Δλ) at a finite field (1.5 T) increases with increasing vanadium content in the range of x<2. But for x>2, a decrease in the magnetic anisotropy with increasing vanadium content causes a decrease in the saturation values of Δλ. In addition, the thermal expansion coefficient becomes a minimum for x≈2. Experimental curves exhibit that the forced volume magnetostriction (ΔV/V) is positive and increases linearly with the applied field at high fields. But in the low field region (≤0.5 T), a minimum appears in the isothermal curves of ΔV/V around the saturation field. The results are explained by considering the influence of vanadium content on the magnetization anisotropy of YFe_12−xV_x compounds.     

Magnetic structure of TbNiAl4

Magnetisation and specific heat measurements, in the range 2 K to room temperature, demonstrate that three magnetic phases exist for the intermetallic compound TbNiAl₄. Powder neutron diffraction, also carried out over a wide temperature range, establishes that the intermediate magnetic phase is incommensurate, and confirms that the lowest temperature phase has a linear antiferromagnetic structure with a (0 1 0) propagation vector. The respective transition (Néel) temperatures, in zero applied magnetic field are 34.0 and 28.0 K.     

Field induced phase transitions on NdRhIn5 and Nd2RhIn8 antiferromagnetic compounds

In this work, we have investigated the low temperature magnetic phase diagram of the tetragonal NdRhIn₅ and Nd₂RhIn₈ single crystals by means of temperature and field dependent heat capacity and magnetic susceptibility measurements. These compounds order antiferromagnetically with a Néel temperature (T_N) of 11 and 10.7 K for NdRhIn₅ and Nd₂RhIn₈, respectively. The constructed magnetic phase of both compounds are anisotropic and show, as expected, a decrease of T_N as a function of the magnetic field for c crystallographic direction. However when the magnetic field is applied along of the c-axis, which is the magnetic easy axis, first-order-like field induced transitions are observed within the antiferromagnetic state. We compare the phase diagrams obtained for NdRhIn₅ and Nd₂RhIn₈ with those for their cubic relative NdIn₃.     

Magnetoelectric behavior in the complex CaMn7O12 perovskite

We report a magnetoelectric effect in the double perovskite CaMn₇O₁₂, that shows a complex magnetic behavior below 90 K with two magnetic phases coexisting (one ferrimagnetic and the other modulated). A second magnetic transition, associated with changes in the magnetic modulation and magnetic ordering coherence lengths of the two magnetic phases occurs at 50 K (T_N2). A detailed structural characterization of this compound, that we have carried out by means of high-resolution X-ray powder diffraction, reveals an anisotropic thermal expansion of its lattice parameters at 50 K (T_N2). In addition, our study of the complex permittivity of this sample as a function of temperature, frequency and magnetic field shows very interesting results below 90 K and specially below 50 K: the dielectric constant ε′_r that was decreasing continuously on cooling experiences an upturn, and even more, on application of a magnetic field it shows a moderate magnetoelectric response. We attribute such dielectric behavior to the formation of electric dipoles by magnetostriction in this charge and spin ordered system, that are sensible to the presence of an external magnetic field.     

Exchange bias in thin-film (Co/Pt)3/Cr2O3 multilayers

We have fabricated exchange-biased Co/Pt layers ((0.3 nm/1.5 nm)×3) on (0 0 1)-oriented Cr₂O₃ thin films. The multilayered films showed extremely smooth surfaces and interfaces with root mean square roughness of ≈0.3 nm for 10 μm×10 μm area. The Cr₂O₃ films display sufficient insulation with a relative low leakage current (1.17×10⁻² A/cm² at 380 MV/m) at room temperature which allowed us to apply electric field as high as 77 MV/m. We find that the sign of the exchange bias and the shape of the hysteresis loops of the out-of-plane magnetized Co/Pt layers can be delicately controlled by adjusting the magnetic field cooling process through the Néel temperature of Cr₂O₃. No clear evidence of the effect of electric field and the electric field cooling was detected on the exchange bias for fields as high as 77 MV/m. We place the upper bound of the shift in exchange bias field due to electric field cooling to be 5 Oe at 250 K.