Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Oxygen overdoping in superconducting and non-superconducting Y1−xPrxBa2Cu3Oy

We present the evolution of magnetic and structural properties of Y_1−xPr_xBa₂Cu₃O_y (x0.5 and x=1) single crystals and polycrystalline materials when the oxygen concentration y is varied from under- to overdoping. We have found a monotonous evolution of the Pr Néel temperature for x=1 samples and a maximum of the superconducting critical temperature for the x0.5 samples. The structural properties as detected by X-ray diffraction and Raman spectroscopy show no instabilities when crossing the optimal doping region as was found in the x=0 material.     

The order of magnetic phase transition in La(Fe1−xCox)11.4Si1.6 compounds

Magnetic transitions in La(Fe_1−xCo_x)_11.4Si_1.6 compounds with x=0–0.08, have been studied by DC magnetic measurements and Mössbauer spectroscopy. The temperature dependence of the Landau coefficients has been derived by fitting the magnetization, M(μ₀H), using the Landau expansion of the magnetic free energy. For x0.02 there is a strongly first-order magnetic phase transition between ferromagnetic and paramagnetic (F–P) states in zero external field and a metamagnetic transition from paramagnetic to ferromagnetic (P–F) above T_c. Increasing the cobalt content drives the F–P transition towards second order and eliminates the metamagnetic transition.     

Superconductivity and crystallographic properties of La2 − xMxCuO4 − δ (M = Na, K)

Superconductivity and crystallographic properties of La_{2 − x}M_xCuO_{4 − δ} (M = Na, K) are studied. In the La_{2 − x}M_xCuO_{4 − δ} system, superconductivity is detected for x 0.2. Oxygen content analysis shows that the system has more oxygen vacancies than the La_{2 − x}Sr_xCuO_{4 − δ} system. These oxygen vacancies may reduce the hole concentration, and high Na-doping is needed to produce superconductivity. In the La_{2 − x}K_xCuO_{4 − δ} system, superconductivity is observed for the first time. Resistivity and magnetic susceptibility measurements show that T_c(onset) is 40 K and the Meissner volume fraction is about 4% for x = 0.7. The system changes from orthorhombic to a tetragonal K₂NiF₄ structure at x ≈ 0.3 and only tetragonal samples show superconductivity.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part II: Al NMR investigation and proposal of clustering process

A ²⁷Al nuclear magnetic resonance (NMR) investigation at room temperature of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is carried out. Two different types of aluminium ions are identified and their ratio is determined as a function of x. A clustering process based on the formation of column clusters, more and more extended when x increases, is proposed on the basis of results issued from the ¹⁹F (Part I) and ²⁷Al NMR investigations.     

Magnetic behavior of Pr1 − xMxCo5 compounds (M = Ti, Zr and Hf)

Magnetic characteristics of Ti-, Zr- and Hf-substituted PrCo₅ alloys have been studied over the temperature range from 77 to 300 K and for applied fields up to 20 kOe. It is established that Ti, Zr and Hf substitute for Pr. Single-phase materials are formed for all values of x up to 0.2 in the system Pr_1−xZr_xCo₅ but for x only up to 0.1 for Pr_1−xTi_x Co₅ and Pr_1−xHfxCo₅ alloys. Larger amounts of Zr can be substituted if the material is made hyperstoichiometric in Co, e.g., Pr_0.7Zr_0.3Co_5.5. All the alloys show a decrease in magnetic moment and an increase in Curie temperature as x increases. Anisotropy fields decrease as x increases at 295 K. Anomalous behavior is observed at 77 K, suggested that these ternary alloys may have a cone structure at this temperature.     

Effect of Pr and Ca substitution on superconductivity in Y(1−x−yPrxCay)Ba2Cu3O7−δ

Pr substituted at constant Ca concentration for Y in (Y_1−x−yPr_xCa_y)Ba₂Cu₃O_7−δ superconductors have been prepared under identical conditions and the temperature dependence of the electrical resistivity of these samples are measured. The resistively determined values of T_c decrease linearly with increasing x (0 ≤ x ≤ 0.2) for constant y = 0.10 and 0.15 which provides convincing evidence that the suppression of superconductivity by Pr is mainly due to magnetic pair breaking. The suppression of superconductivity can also be correlated to the observed changes in oxygen content determined by iodometric analysis and to the average Cu-valences. However, it is found that the observed suppression of T_c cannot be compensated by appropriate hole doping with Ca.     

Dielectric behavior of hexaferrites BaCo2−xZnxFe16O27

The dielectric constant (′) and dielectric loss (tan δ) for hexaferrites BaCo_2−xZn_xFe₁₆O₂₇ have been studied as a function of frequency (f), temperature (T) and composition (x). The experimental results indicate that ′ and tan δ above the relaxation frequency only decrease as the frequency increases and as the temperature decreases. Tan δ shows the dielectric relaxation at certain critical frequencies which rise as temperature increases. The activation energy for the dielectric relaxation (E_D), ′, and tan δ are found to be minimum for x = 0.8.     

Crystal structure, electrical and magnetic properties of La1 − xSrxCoO3 − y

The crystal structure and properties of La_{1 − x}Sr_xCoO_{3 − y} with strontium contents ranging from x = 0.1 to x = 0.7 have been studied. The lattice parameters were measured as a function of temperature (4.2–400 K) and the crystal structure was found to change from rhombohedral (at low temperatures and values of x) to cubic. While LaCoO₃ is paramagnetic the oxides in the composition range 0.2 < x < 0.6 are soft ferromagnets. The strontium additions are compensated by the formation of Co⁴⁺ (cobalt ions with one positive effective charge, Co_Co^.) and oxygen vacancies (V_o^..). From the results it is concluded that the relative importance of oxygen vacancies increases with increasing temperature and decreasing oxygen activity. As a result the concentration of electronic charge carriers — and the resultant electrical conductivity — decrease with increasing temperature. The defect structure is discussed and it is concluded that defect associations — probably between oxygen vacancies and strontium ions — and formation of microdomains of perovskite-related phases are important aspects of the overall structure of these perovskite phases.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Effective Ru moment in RuSr2Eu2−xCexCu2O10 from high-temperature magnetic susceptibility

We have made high-temperature (250 K<T<800 K) DC susceptibility measurements in the compounds RuSr₂Eu_2−xCe_xCu₂O₁₀ for x=0.6,0.8, and 1.0 in order to determine the Ru effective magnetic moment. After carefully subtracting all contributions to the magnetic susceptibility except that of the Ru ions, we have been able to fit the Ru susceptibility with a law χ_Ru=χ₀+C_Ru/(T−Θ_Ru). We have found that the Ru effective moment falls between the values expected for Ru⁵⁺ in spin states and . We have also found a dependence of μ_eff(Ru) and Θ_Ru with the Ce content x.     

NMR study of coexistence of ferro- and antiferromagnetism in (Zr1−xNbx)Fe2

The magnetic phase diagram has been investigated in the C14 type (Zr_1−xNb_x)Fe₂ with x0.7 from ⁹³Nb NMR and magnetization measurements. In the compound with x = 0.825 a first order-like transition has been found to occur around 25 K from a canted state with the ferromagnetic moment in the basal plane to a ferromagnetic state with decreasing temperature.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Magnetic properties and percolation threshold in diluted B-spinel ZnCr2xAl2−2xS4: a study through high-temperature expansions

By making use of high-temperature series expansions (HTSE) of the correlation functions, we study the thermal and disorder variation of the short-range order (SRO) in the particular B-spinel ZnCr_2xAl_2−2xS₄. We developed the HTSE for the q-dependent static structure factor S(q) to the order 6 in reciprocal temperature including both the nearest- and next-nearest-neighbour interactions J₁ and J₂, respectively. Respecting the experimental fact that the broad diffuse peak of the neutron is situated at the particular wave vector q₀=[0 0 0.79] and is insensitive to the temperature for a given ratio of dilution x, we have estimated the thermal variation of J₁ and J₂ in the case of the pure compound.

The bond percolation threshold x_p of the ZnCr_2xAl_2−2xS₄ is determined by studying the disorder variation of the correlation length ξ. The x_p is considered as the concentration at which ξ vanishes. The obtained values are x_p=0.27 when only J₁ is considered and 0.23 when both J₁ and J₂ are taken into account.     

The relationship between crystal structure and electrical conductivity in the LaY1−xInxO3 (x=0.0–0.7) system

The electrical conductivity of the LaY_1−xIn_xO₃ (x=0.0–0.7) system has been studied from the viewpoint of crystal chemistry. The high temperature form of LaYO₃ (x=0.0) was ascertained to be the Sm₂O₃-type (B-type rare earth) structure, not perovskite-type one. The X-ray diffraction (XRD) experiments revealed that the samples with x=0.05 and 0.10 were the mixed phase of Sm₂O₃-type and perovskite-type structure, and changed to perovskite phase in the range of x0.20. From oxygen partial pressure dependence of the electrical conductivity, it was found that both the Sm₂O₃-type and the perovskite-type single phases showed hole conduction, but the mixed phase did oxide-ion one. The electrical conductivity of the LaY_1−xIn_xO₃ (x=0.0–0.7) system increased with increasing x, and showed the maximum value in the range of x=0.05–0.10, and then decreased with increasing x. The occurrence of oxide-ion conduction was discussed from the viewpoint of lattice distortion in the mixed phase.     

Oxygen nonstoichiometry and phase transitions of the neodymium-rich Nd1+xBa2−xCu3Oz solid solution

On the basis of chemical, thermal analysis and Cu K-edge X-ray absorption measurements, oxygen content in the Nd_1+xBa_2−xCu₃O_z solid solution was determined between 1000°C in air and 400°C in oxygen for x=0.05–0.9 compositions. It has been observed that the oxygen nonstoichiometry Δz of the Nd_1+xBa_2−xCu₃O_7+x/2−Δz solid solution decreases 2–2.5 times for a large substitution (Δz≈0.3–0.33 for x=0.9), despite of the acclaimed higher total oxygen content. The difference in nonstoichiometry is explained by a higher average value of the copper oxidation state (ACV), which is vital for the solid solution with large x even at elevated temperatures (ACV≈2–2.05 for x>0.3 at 1000°C, PO₂=0.21 atm). On the contrary, the ACV after complete oxygenation is almost constant (about 2.25–2.3) for the whole series. The x-dependence of the oxygen content is not monotonous and structural phase transitions can be observed at x=0.3 and x=0.6, as confirmed by the X-ray diffraction and the Raman scattering spectroscopy. The first well-known transition is connected with the oxygen disorder due to the Nd substitution for Ba at random Ba-sites. In the present work, it is proved by the apical oxygen mode broadening in Raman spectra. Ordering of the Nd and Ba atoms with a subsequent orthorhombic distortion of the lattice may occur even at 1000°C in air due to the second transformation at x≈0.6. The invariable orthorhombicity of the Nd-rich solid solution with x>0.6 is not caused by the oxygen absorption as in the x=0.05 case. Existence of high- and low-temperature orthorhombic modifications of this solid solution has been observed for the first time. Finally, a tentative 3D (z–x–T) diagram is suggested for the Nd_1+xBa_2−xCu₃O_z solid solution up to 1000°C in air, including the new x=0.6–0.9 region.     

Oxygen tracer diffusion in La1 − xSrxCoO3

Tracer diffusion of ¹⁸O in dense, polycrystalline La_1−xSr_xCoO₃ for x = 0.1 has been measured in the temperature range 400 to 600 °C and at 500 °C for x = 0.2 at an oxygen partial pressure of 1 × 10⁵ Pa. Depth profiles were obtained by secondary ion mass spectrometry. The diffusion coefficient for La_0.9Sr_0.1CoO₃ is given by D = (17–247) exp[(−232 ± 8 kJ/mole)/RT] cm²/s. This value is several orders of magnitude lower than D extrapolated from the results for x = 0.2 measured in the 700–900 °C temperature range. One possible explanation for the discrepancy is that the two measurements reflect different diffusion paths. As expected, La_0.8Sr_0.2CoO₃ exhibits a higher diffusivity at 500 °C than does La_0.9Sr_0.1CoO₃.     

Positive linear magnetoresistance in Fex–C1−x composites

A large positive magnetoresistance (MR) has been found in micro-sized Fe_x–C_1−x composites. At a magnetic field of 5 T, the Fe_0.2–C_0.8 composite has the largest MR, 53.8% and 190% at room temperature and at 5 K, respectively. The magnetic field dependence of the MR can be described approximately as MR∝Bⁿ, and the value of exponent n is determined by the Fe weight concentration and temperature, ranging from 1/4 to 6/4. It appears that Fe_x–C_1−x has a linear field dependence of the positive MR at different temperatures. The possible mechanism for the positive MR is discussed.