Growth and properties of Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 single crystals directly from melt

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by a modified Bridgman method directly from melt using an allomeric Pb[(Mg_1/3Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal as a seed. X-ray diffraction (XRD) measurement confirmed that the as-grown PZNT91/9 single crystals are of pure perovskite structure. Electrical properties and thermal stabilization of PZNT91/9 crystals grown directly from melt exhibit different characters from those of PZNT91/9 crystals grown from flux, although segregation and the variation of chemical composition are not seriously confirmed by X-ray fluorescence analysis (XPS). The [0 0 1]-oriented PZNT91/9 crystals cut from the middle part of the as-grown crystal boules exhibit broad dielectric-response peaks at around 105 °C, accompanied by apparent frequency dispersion. The values of piezoelectric constant d₃₃, remnant polarization P_r, and induced strain are about 1800–2200 pC/N, 38.8 μC/cm², and 0.3%, respectively, indicating that the quality of PZNT crystals grown directly from melt can be comparable to those of PZNT91/9 single crystals grown from flux. However, further work deserves attention to improve the dielectric properties of PZNT crystals grown directly from melt. Such unusual characterizations of dielectric properties of PZNT crystals grown directly from melt are considered as correlating with defects, microinhomogeneities, and polar regions.     

Thermal and laser properties of Yb:YAl3(BO3)4 crystal

Large optical-quality Yb:YAl₃(BO₃)₄(Yb:YAB) crystals have been grown by the flux method. The thermal properties of Yb:YAB crystal were measured for the first time. The thermal properties of Yb:YAB crystal with different Yb³⁺ ion concentrations are also reported. The results show that the ytterbium concentration influences the properties of Yb:YAB crystal. The specific heat decreases with the increase of Yb³⁺ ion concentrations in the experiment range. Apparently, the thermal expansion coefficient increases along the c-direction with the increase of Yb³⁺ ion concentrations, while it changes slightly along the a-direction. The output laser in 1120–1140 nm ranges has been demonstrated pumped by InGaAs laser. The slope efficiency is 3.8%. The self-frequency-doubling output power of 1 mW is achieved.     

Growth, dielectric, ferroelectric and optical properties of Ca0.28Ba0.72Nb2O6 single crystals

Calcium barium niobate Ca_0.28Ba_0.72Nb₂O₆ (CBN-28) crystals were grown by the Czochralski method. The effective segregation coefficients of Ca, Ba, Na elements in CBN-28 crystal growth were measured, and the rocking curve from 0 0 2 reflection of CBN-28 wafer was also measured by the high-resolution X-ray diffractometer D5005, and the full-width at half-maximum value was measured to be 70.6″. The measured dependence of dielectric constants on temperature showed the Curie temperature of the CBN-28 crystals is between 246.8 and 260 °C. Typical polarization–electric field (P–E) hysteresis loops were measured at room temperature. Ferroelectric 180° domains were observed by scanning electron microscopy (SEM) on the etched (0 0 1) surface of the CBN-28 crystals. The transmittance of [0 0 1]-oriented CBN-28 crystals was measured and the result shows that optical properties of CBN-28 crystal are almost the same as those of SBN for wavelengths between 2500 and 7500 nm.     

Preparation and characterization of Ni-incorporated FeS2 single crystals

Nickel-incorporated FeS₂ single crystals with various Ni compositions of Fe_0.99S₂:Ni_0.01, Fe_0.98S₂:Ni_0.02, Fe_0.96S₂:Ni_0.04, and Fe_0.9S₂:Ni_0.1 were grown by chemical vapor transport (CVT) method using ICl₃ as a transport agent. Physical properties of the Ni-incorporated FeS₂ single crystals were characterized using X-ray diffraction, Raman spectroscopy, electrical conductivity, and photoconductivity (PC) measurements. By means of the analyses of the X-ray diffraction patterns, the whole series of Ni-doped FeS₂ single crystals were determined to be single-phase and isostructural. Raman spectroscopy of the Ni-doped FeS₂ crystals was carried out at room temperature. Raman resonant peaks of the Ni-doped FeS₂ crystals demonstrate an energy red-shift behavior with respect to the increase of the dopant densities. Conductivity measurements show the resistivity of the Ni-doped FeS₂ decreased as the doping concentration of Ni is increased. Nickel is an n-type dopant, which behaves like a donor level existed near the conduction band edge of the synthetic FeS₂. On the other hand, dopant effect of nickel on the synthetic FeS₂ also destroys the photoconductive sensitivity in the photoconductivity measurements.     

Growth and spectroscopic properties of Er single doped and Er–Yb co-doped YAl3(BO3)4 crystals

Er³⁺-doped and Er³⁺–Yb³⁺ co-doped yttrium aluminum borate (YAB) single crystals have been grown by the top-seeded solution growth method using a new flux system, namely NaF–MoO₃–B₂O₃. The Er³⁺ concentrations were 1.3 mol% for both single doped and co-doped crystals and the Yb³⁺ concentration in the Er³⁺–Yb³⁺ co-doped crystal was 20.0 mol% in the raw materials. The distribution coefficients of Er³⁺ single doped and Er³⁺–Yb³⁺ co-doped crystals were measured. The polarized absorption and fluorescence spectra of Er³⁺–Yb³⁺ co-doped crystal were recorded and compared with those of Er³⁺ single doped crystal. The results demonstrate that Er³⁺–Yb³⁺ co-doped YAB crystal is a potential candidate for 1.55 μm laser materials.     

Flux growth of PbMg1/3Ta2/3O3 single crystals

Single crystals of PbMg_1/3Ta_2/3O₃ (PMT) were grown by the flux method. The PbO–Pb₃O₄–B₂O₃ system was used as a solvent. Transparent and light yellow PMT single crystals of rectangular shape and dimensions up to 10×6×4 mm³ were obtained. For the applied growth conditions only, the crystals of the perovskite structure were grown. X-ray diffraction tests showed that at room temperature PMT exhibits cubic symmetry with lattice parameter a=4.042(1) Å. Dielectric studies pointed to relaxor properties of PMT. The characteristic broad and frequency-dependent maximum of dielectric permittivity was observed at 179.7 K (1 kHz).     

Synthesis, growth, thermal, optical, dielectric and mechanical properties of semi-organic NLO crystal: Potassium hydrogen malate monohydrate

Potassium hydrogen malate monohydrate (PHMM), a semi-organic nonlinear optical material, has been synthesized and single crystals were grown from aqueous solution. Single crystals of PHMM have been grown by slow evaporation of solvent at room temperature up to dimensions of 22 mm×16 mm×14 mm. Single-crystal X-ray diffraction study on grown crystals shows that they belong to monoclinic system and non-centrosymmetry spacegroup Cc. The structural perfection of the grown crystals has been analyzed by high-resolution X-ray diffraction (HRXRD) rocking curve measurements. Fourier transform infrared (FTIR) spectroscopic study was performed for the identification of different modes of functional groups present in the compound. The UV–Vis transmission spectrum has been recorded in the range 200–1100 nm. The thermal stability of the compound has been determined by TG-DTA curves. The dielectric studies were performed. From the microhardness measurements, Vicker's hardness number (H_v), Stiffness constant (C₁₁), fracture toughness (k_c), Brittle index (B_i) and yield strength (σ_y) have been calculated. The Young's modulus was calculated using the Knoop hardness measurement. The SHG relative efficiency of PHMM crystal was found to be 1.2 times higher than that of KDP.     

Homogeneous SiGe crystals grown by using the traveling liquidus-zone method

It is indispensable to estimate a diffusion coefficient in a solution zone in order to grow a homogeneous crystal by using the traveling liquidus-zone (TLZ) method. To estimate the diffusion coefficient of Ge in the SiGe solution zone, result of a two-dimensional numerical simulation is compared with an experimental result. From the comparison, the diffusion coefficient is estimated to be 9.5×10⁻⁵ cm²/s. By using this coefficient, a sample translation rate for obtaining a homogeneous SiGe crystal is determined. By translating samples with appropriate rates, homogeneous Si_0.5Ge_0.5 crystals are successfully grown. The typical Ge composition is 0.496±0.006 for more than 13 mm long. The experimental result shows the homogeneity of ±1.2% in the mole fraction. This deviation corresponds to the variation of less than ±0.03% in the lattice constant. Since this variation is negligibly small, the homogeneity is excellent. Thus it is found that the TLZ method is the universal growth technique, which is applicable to the crystal growth of not only the III–V compounds but also the IV–IV compounds.     

Growth and morphology of ruby crystals with unusual chromium concentration

Single crystals of ruby have been obtained from fluxed melts based on the systems Li₂O–MoO₃, Li₂O–WO₃, Na₂O–WO₃, 2PbO–3V₂O₅, PbO–V₂O₅–WO₃, PbF₂–Bi₂O₃ and Na₃AlF₆ by both the TSSG method and spontaneous crystallization at the temperatures 1330–900 °C. Al₂O₃ solubility has been measured for the flux composition of 2Bi₂O₃–5PbF₂ in the temperature range 1200–1000 °C and dissolution enthalpy has been defined as 29.4 KJ/Mol. The composition of grown crystals was studied by electron microprobe analysis. The synthetic ruby contains from 0.51 to 6.38 at% of chromium admixture depending on the crystal growth conditions. Experimental results on growth conditions, composition and morphology of grown crystals are presented for each flux and temperature interval.     

Characteristic crystal growth from amorphous WO3 film by vacuum heating

Selective growth of WO₂, W and WO_3−x crystals from amorphous WO₃ film by vacuum heating at 400–900°C was clarified. The grown WO_3−x crystals were incommensurate structure based on crystallographic share structure. The growth process of WO₂ crystal in the amorphous film was directly observed at high temperature in the electron microscope. The growth front of the WO₂ crystal consumes WO₃ microcrystallites with various orientations. The growth speed of the WO₂ depended on WO₃ microcrystallites orientation. The origin of the wavy growth front of WO₂ was due to an orientation dependence of the WO₃ microcrystallites.     

Growth and characterization of a new nonlinear optical material: Potassium p-nitrophenolate dihydrate (NO2–C6H4–OK·2H2O) with new bonding properties

Single crystals of potassium p-nitrophenolate dihydrate (NPK·2H₂O) have been grown successfully using the isothermal solvent evaporation technique. It is a new semiorganic nonlinear optical crystal, possessing a d_eff of about 1.5 times that of lithium niobate and in which the K⁺ ions are bonded to the nitro group instead of bonding with the phenolic O⁻. Large single crystals of dimension upto 20×6×4 mm³ are harvested within a period of 60 days. The grown crystals are subjected to single crystal X-ray, FTIR and DRS-UV visible spectral, thermal and microhardness analyses. Single crystal X-ray analysis confirms the molecular formula and the structure of the crystal. FTIR spectral studies verify the functional groups present in the crystal. The DRS-UV visible spectrum proved the optical transparency of the crystal in the entire visible and near infrared region. Thermal studies reveal that the crystals are stable upto 180 °C. Microhardness measurements on the cleaved plane (1 1 0) explain the strength and slip direction in the crystal. The SHG efficiency of the crystal is examined by performing the Kurtz powder test using Nd:YAG laser.     

Edge-defined film-fed growth of Yb:YVO4 single crystal plates

The applicability of the edge-defined film-fed growth (EFG) technique for Yb_xY_(1−x)VO₄ (x=0.05, 0.1 and 1) was approved by successful growth of crystals up to 80 mm in length as the thin plates. Low-angle grain boundaries and the crystal coloration as main defects were found. Optimal seed orientation was suggested on the strength of vanadate crystal plate morphology. Optical properties, chemical composition and the crystalline quality were investigated.     

Flux growth of BPO4 crystals

Single crystals of BPO₄ with sizes up to 15×10×12 mm³ were grown by top-seeded solution growth method using Li₂O–Li₄P₂O₇ as fluxes. The components volatilized from the melt were characterized by the method of X-ray powder diffraction. The defects of grown crystals have also been investigated. The measured ultraviolet cutoff edge of BPO₄ was about 130 nm. Its density was 2.82 g/cm³ determined using drainage method.     

Growth of Na modified potassium lithium niobate crystal by the Czochralski method

Transparent Na modified potassium lithium niobate (Na_0.23K_2.60Li_1.82Nb_5.35O_15.70; NKLN) crystal was successively grown by the Czochralski method using RF induction heating from melt composition Na₂O:K₂O : Li₂O:Nb₂O₅=2:30:25:43 mol%. NKLN crystal showed a tetragonal tungsten bronze structure with lattice constants a=12.5446±0.0010 Å and c=4.0129±0.0005 Å at room temperature. The dielectric constant along the c-axis ε₃₃ showed a sharp maximum around 480 °C. Optical transmission edge was 370 nm and optical transmission spectra showed no absorption at wavelengths ranging from 380 to 800 nm. The structural and optical properties of NKLN were similar to those of the near stoichiometric KLN crystals. We believe that the growth of NKLN by the Czochralski method has an advantage for a large size and high-quality crystal.     

Effect of lattice oxygen on optical absorption, radiation hardness and thermally stimulated luminescence of BaF2 crystal

The influence of the presence of BaO impurity on the optical absorption, radiation hardness and thermally stimulated luminescence of BaF₂ has been investigated. The presence of oxygen impurity gives rise to three absorption bands in the UV region, peaking around 220, 280 and 335 nm. Further, the impurity is found to be detrimental to crystal hardness against ionizing radiations. The thermally stimulated luminescence (TSL) has been studied from gamma-irradiated crystals containing different fractions of BaO impurity. Four prominent glow peaks around 100°C (peak I), 150°C (peak II), 220°C (peak III) and 290°C (peak IV) are observed for crystals containing BaO impurity concentrations lower than 0.5% (by wt). For crystals containing higher impurity concentrations, two additional peaks around 75°C and 260°C are also observed. The kinetics of TSL emission is observed to be of first order, implying that the absorption and the emission centers responsible for TSL are the same. The normalized TSL output for peak I is found to vary linearly with the concentration of oxide impurity. This fact can be utilized to detect the presence of minute amounts of oxygen in BaF₂ lattice, which is crucial to the growth of crystals exhibiting high radiation hardness.     

Growth of NaBi(WO4)2 crystal by modified-Bridgman method

NaBi(WO₄)₂ (NBW) crystals have been grown for the first time by modified-Bridgman method. Influences of some factors on the crystal growth process are discussed. X-ray powder diffraction experiments show that the unit cell parameters of NBW crystal are a=b=0.5284 nm, c=1.1517 nm, and V=0.3215 nm³. The differential thermal analysis shows that the NBW crystal melts at 923°C.     

Improved growth of PbI2 single crystals

The phase equilibrium and the crystallization process of lead iodide (PbI₂) melt have been primarily investigated according to the lead–iodine phase diagram. It is found that the iodine evaporation and the segregated lead deposition are the two important factors that affect the PbI₂ crystal quality. The new method of Pulling U-type quartz growth ampoule has been made to impede the decomposition of PbI₂ and the vaporization and condensation of iodine. An orange and translucent PbI₂ single crystal of large size was obtained by the improved growth method, i.e. U-type ampoule pulling. Resistivity of the as-grown crystal is up to 4×10¹¹ Ω cm, and IR transmission is up to 45% in the region from 7800 to 450 cm⁻¹. Therefore, the improved growth method is a promising convenient new method for the growth of high quality PbI₂ crystals.     

Environmental SEM investigation on surface defects in 0.92Pb(Zn1/3Nb2/3)O3–0.08PbTiO3 single crystal

In this paper, the technique of environmental scanning electron microscopy (ESEM) has been employed to investigate the surface defects of the (1 1 1) appearing face in 0.92Pb(Zn_1/3Nb_2/3)O₃–0.08PbTiO₃ (PZN–8%PT) crystals. From the ESEM images, we succeeded in observing and studying the growth hillocks and etch pits, low-angle grain boundaries, and sub-grain boundaries in (1 1 1) face, which were related to the generation of dislocation and stacking faults, respectively. On the other hand, an image of a unique multi-layer lamellar structure and fine step structure obtained in the (1 1 1) face reveals that the dominant fast growth mechanism of PZN–8%PT crystal grown by the flux method is a sub-step mechanism, unlike the screw dislocation growth mechanism.     

Ambient-condition growth of superconducting YBa2Cu4O8 single crystals using KOH flux

YBa₂Cu₄O₈ is a stoichiometric oxide superconductor of T_c80 K. Unlike YBa₂Cu₃O_7−δ, this compound is free from oxygen vacancy or twin formation and does not have any microscopic disorder in the crystal. Doping with Ca raises its T_c to 90 K. The compound is a promising superconductor for technological application. Up to now, single crystals have not been grown without using specialized apparatus with extremely high oxygen pressure up to 3000 bar and at over 1100 °C due to the limited range of reaction kinetics of the compound. This fact has delayed the progress in the study of its physical properties and potential applications. We present here a simple growth method using KOH as flux that acts effectively for obtaining high-quality single crystals in air/oxygen at the temperature as low as 550 °C. As-grown crystals can readily be separated from the flux and exhibit a perfect orthorhombic morphology with sizes up to 0.7×0.4×0.2 mm³. Our results are reproducible and suggest that the crystals can be grown using a conventional flux method under ambient condition.     

Gel growth of α and γ glycine and their characterization

The microbial free single crystals of α and γ glycine were grown from gel at room temperature in a new chemical route. These crystals showed a superior quality than the solution grown crystals. The metastable α-form and the stable γ-form of glycine were crystallized in silica gel by solubility reduction method. The form of crystallization is confirmed by single crystal and powder X-ray diffraction analyses. The crystals of α and γ glycine were found to crystallize in monoclinic and hexagonal crystal systems, respectively. For analyzing the functional group and thermal stability of α and γ glycine crystals, spectroscopic and thermal analyses have been carried out. The dielectric studies were performed to find the dielectric constant of the grown crystals and the results are discussed. Second harmonic generation efficiency of the crystal was measured by Kurtz’s powder method using Nd:YAG laser and it was found to be 2.68 times that of potassium dihydrogen phosphate crystals.