Ultrathin nickel oxide films grown on Ag(0 0 1): a study by XPS, LEIS and LEED intensity analysis

The structure of a nickel oxide film 2 ML thick has been investigated by LEED intensity analysis. The NiO film was prepared by evaporating Ni in presence of O₂ at a pressure in the 10⁻⁶ mbar range. The growth of the oxide film was followed by XPS, LEIS and LEED. In the early stages of deposition, the film shows a (2 × 1) superstructure in LEED. After deposition of 2 ML of NiO, a sharp (1 × 1) LEED pattern is observed. The intensity versus electron energy curves of the LEED spots were measured for this NiO(1 × 1) film and analysed by means of the tensor LEED method. A good level of agreement of the experimental LEED intensities with those calculated for a pseudomorphic NiO(0 0 1) film was obtained. We found that oxygen atoms at the oxide-substrate interface are on-top silver atoms. The interlayer distance in the oxide does not differ significantly from that in bulk NiO(0 0 1), within the accuracy of the analysis. An outward displacement (0.05 ± 0.05 Å) of oxygen atoms with respect to nickel atoms was found at the oxide film surface. The interlayer distance at the silver-nickel oxide interface is 2.43 ± 0.05 Å.     

Growth and oxidation of a Ni3Al alloy on Ni(1 0 0)

The growth and oxidation of a thin film of Ni₃Al grown on Ni(1 0 0) were studied using Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and high resolution electron energy loss spectroscopy (EELS). At 300 K, a 12 Å thick layer of aluminium was deposited on a Ni(1 0 0) surface and subsequently annealed to 1150 K resulting in a thin film of Ni₃Al which grows with the (1 0 0) plane parallel to the (1 0 0) surface of the substrate. Oxidation at 300 K of Ni₃Al/Ni(1 0 0) until saturation leads to the growth of an aluminium oxide layer consisting of different alumina phases. By annealing up to 1000 K, a well ordered film of the Al₂O₃ film is formed which exhibits in the EEL spectra Fuchs-Kliewer phonons at 420, 640 and 880 cm⁻¹. The LEED pattern of the oxide shows a twelvefold ring structure. This LEED pattern is explained by two domains with hexagonal structure which are rotated by 90° with respect to each other. The lattice constant of the hexagonal structure amounts to ∼2.87 Å. The EELS data and the LEED pattern suggest that the γ^′-Al₂O₃ phase is formed which grows with the (1 1 1) plane parallel to the Ni(1 0 0) surface.     

CO2 adsorption on Cr(1 1 0) and Cr2O3(0 0 0 1)/Cr(1 1 0)

We attempt to correlate qualitatively the surface structure with the chemical activity for a metal surface, Cr(1 1 0), and one of its surface oxides, Cr₂O₃(0 0 0 1)/Cr(1 1 0). The kinetics and dynamics of CO₂ adsorption have been studied by low energy electron diffraction (LEED), Aug er electron spectroscopy (AES), and thermal desorption spectroscopy (TDS), as well as adsorption probability measurements conducted for impact energies of E_i = 0.1-1.1 eV and adsorption temperatures of T_s = 92-135 K. The Cr(1 1 0) surface is characterized by a square shaped LEED pattern, contamination free Cr AES, and a single dominant TDS peak (binding energy E_d = 33.3 kJ/mol, first order pre-exponential 1 × 10¹³ s⁻¹). The oxide exhibits a hexagonal shaped LEED pattern, Cr AES with an additional O-line, and two TDS peaks (E_d = 39.5 and 30.5 kJ/mol). The initial adsorption probability, S₀, is independent of T_s for both systems and decreases exponentially from 0.69 to 0.22 for Cr(1 1 0) with increasing E_i, with S₀ smaller by ∼0.15 for the surface oxide. The coverage dependence of the adsorption probability, S(Θ), at low E_i is approx. independent of coverage (Kisliuk-shape) and increases initially at large E_i with coverage (adsorbate-assisted adsorption). CO₂ physisorbs on both systems and the adsorption is non-activated and precursor mediated. Monte Carlo simulations (MCS) have been used to parameterize the beam scattering data. The coverage dependence of E_d has been obtained by means of a Redhead analysis of the TDS curves.     

In situ XPS study of Pd(1 1 1) oxidation. Part 1: 2D oxide formation in 10 mbar O2

The oxidation of the Pd(1 1 1) surface was studied by in situ XPS during heating and cooling in 3 × 10⁻³ mbar O₂. A number of adsorbed/dissolved oxygen species were identified by in situ XPS, such as the two dimensional surface oxide (Pd₅O₄), the supersaturated O_ads layer, dissolved oxygen and the R 12.2° surface structure.Exposure of the Pd(1 1 1) single crystal to 3 × 10⁻³ mbar O₂ at 425 K led to formation of the 2D oxide phase, which was in equilibrium with a supersaturated O_ads layer. The supersaturated O_ads layer was characterized by the O 1s core level peak at 530.37 eV. The 2D oxide, Pd₅O₄, was characterized by two O 1s components at 528.92 eV and 529.52 eV and by two oxygen-induced Pd 3d_5/2 components at 335.5 eV and 336.24 eV. During heating in 3 × 10⁻³ mbar O₂ the supersaturated O_ads layer disappeared whereas the fraction of the surface covered with the 2D oxide grew. The surface was completely covered with the 2D oxide between 600 K and 655 K. Depth profiling by photon energy variation confirmed the surface nature of the 2D oxide. The 2D oxide decomposed completely above 717 K. Diffusion of oxygen in the palladium bulk occurred at these temperatures. A substantial oxygen signal assigned to the dissolved species was detected even at 923 K. The dissolved oxygen was characterised by the O 1s core level peak at 528.98 eV. The “bulk” nature of the dissolved oxygen species was verified by depth profiling.During cooling in 3 × 10⁻³ mbar O₂, the oxidised Pd²⁺ species appeared at 788 K whereas the 2D oxide decomposed at 717 K during heating. The surface oxidised states exhibited an inverse hysteresis. The oxidised palladium state observed during cooling was assigned to a new oxide phase, probably the R 12.2° structure.     

The catalytic reduction of NO by H2 on Ru(0 0 0 1): Observation of NHads species

Adsorption of NO and the reaction between NO and H₂ were investigated on the Ru(0 0 0 1) surface by X-ray photoelectron spectroscopy (XPS). Surface composition was measured after NO adsorption and after the selective catalytic reduction of nitric oxide with hydrogen in steady-state conditions at 320 K and 390 K in a 30:1 mixture of H₂ and NO (total pressure = 10⁻⁴ mbar). After steady-state NO reduction, molecularly adsorbed NO in both the linear on-top and threefold coordinations, NH_ads and N_ads species were identified by XPS. The coverage of the NH_ads and N_ads species was higher after the reaction at 390 K than the corresponding values at 320 K. Strong destabilisation of N_ads by O_ads was detected. A possible reaction mechanism is discussed.     

Autocatalytic partial reduction of FeO(1 1 1) and Fe3O4(1 1 1) films by atomic hydrogen

The interaction of atomic hydrogen with thin epitaxial FeO(1 1 1) and Fe₃O₄(1 1 1) films was studied by TDS, XPS and LEED. On the thin, one Fe-O bilayer thick FeO film, partial reduction occurs in two steps during exposure. It ends after removal of 1/4 monolayer (ML) of oxygen with a 2 × 2 pattern appearing in LEED. This FeO_0.75 film is passive against further reduction. The first reduction step saturates after removal of ∼0.2 ML and shows autocatalytic kinetics with the oxygen vacancies formed during reduction causing acceleration. The second step is also autocatalytic and is related with reduction to the final composition and an improvement of the 2 × 2 order. A structure model explaining the two-step reduction is proposed. On the thick Fe₃O₄ film, irregular desorption bursts of H₂O and H₂ were observed during exposure. Their occurrence appears to depend on the film quality and thus on surface order. Because of the healing of reduction-induced oxygen vacancies by exchange of oxygen or iron with the bulk, a change of the surface composition was not visible. The existence of partially reduced oxide phases resistant even to atomic hydrogen is relevant to the mechanism of dehydrogenation reactions using iron oxides as catalysts.     

Impact of O2 exposure on surface crystallinity of clean and Ba terminated Ge(1 0 0) surfaces

In analogy with the case of Sr on Si [Y. Liang, S. Gan, M. Engelhard, Appl. Phys. Lett. 79 (2001) 3591], we studied surface crystallinity and oxidation behaviour of clean and Ba terminated Ge(1 0 0) surfaces as a function of oxygen pressure and temperature. The structural and chemical changes in the Ge surface layer were monitored by LEED, XPS and real-time RHEED. In contrast to the oxidation retarding effect, observed for 1/2 monolayer of Sr on Si, the presence of a Ba termination layer leads to a pronounced increase in Ge oxidation rate with respect to clean Ge. In fact, while the Ge(1 0 0) surface terminated with 1/2 ML Ba amorphizes for a pO₂ of 10⁻² Torr, LEED indicates that clean Ge forms a thin (4.5 Å), 1 × 1 ordered oxide upon aggressive O₂ exposure (150 Torr, 200 °C, 30 min). We briefly discuss the origins for the difference in behaviour between Ba on Ge and Sr on Si.     

On the preparation and electronic properties of clean W(1 1 0) surfaces

We have studied the influence of oxygen pressure during the cyclic annealing used for the cleaning of W(1 1 0) surfaces. For this purpose the surface morphology and electronic properties are measured by means of scanning tunneling microscopy (STM) and spectroscopy (STS), respectively. It is found that the surfaces with impurity atom densities as low as 2 × 10⁻³ can be obtained by gradually reducing the oxygen pressure between subsequent annealing cycles down to about 2 × 10⁻⁸ mbar in the final cycle. Only on the clean surface a bias-dependent spatial modulation of the local density of states (LDOS) is observed at step edges and around impurity sites by STS. In addition, we find a pronounced peak in the occupied states. In combination with density functional theory calculations these features can be traced back to a dispersive p_z-d_xz-type surface resonance band and the lower band edge of a surface state, respectively.     

The growth and structure of titanium dioxide films on a Re(1 0 −1 0) surface: Rutile(0 1 1)-(2 × 1)

Titanium dioxide films were grown on Re(1 0 −1 0) by Ti vapor deposition in oxygen at T = 830 K and studied by means of low-energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), low-energy ion scattering (LEIS) and X-ray diffraction (XRD). The Ti oxide stoichiometry was determined by XPS as Ti:O = 1:2, with the Ti oxidation state (4+). The TiO₂ growth was monitored by means of LEED as a function of film thickness. Extending the coverage from the submonolayer into the multilayer regime gives rise to a p(2 × 2) pattern, a (poorly ordered) (1 × 1), and, finally, a stable (2 × 2) structure, the latter being associated with a homogeneous TiO₂ phase. For normal electron incidence, the (2 × 2) LEED pattern exhibits systematically extinguished beams at (n ± 1/2, 0) positions, indicating a glide mirror plane. The pg(2 × 2) structure could be explained by both a rutile(0 1 1)-(2 × 1) reconstructed surface and a bulk truncated brookite(0 0 1) surface. Faceting phenomena, i.e. running LEED spots, observed with thin TiO₂ films point to the formation of a rutile(0 1 1)-(2 × 1) surface with two domains and {0 1 1}-(2 × 1) facets and rule out the brookite alternative. Confirmation of this assignment was obtained by an XRD analysis performed at the Berlin synchrotron facility BESSY.     

Scanning tunneling microscopy study on a BC3 covered NbB2(0 0 0 1) surface

We have investigated a BC₃ covered NbB₂(0 0 0 1) surface using scanning tunneling microscopy (STM), scanning tunneling spectroscopy (STS), and low energy electron diffraction (LEED). The STM images reveal characteristic features of a Moiré pattern reflecting an incommensurate relation of the BC₃ sheet with the substrate: bright protrusions with the periodicity of the substrate lattice are modulated in intensity with the periodicity of the BC₃ lattice. As a result, the surface exhibits nm-scale patchy regions with either the √3 × √3 or the 1 × 1 structure of the substrate. The two-dimensional Fourier transformation pattern of the STM image is consistent with the LEED pattern proving the epitaxial and incommensurate relationship between BC₃ surface sheet and substrate. No feature of a predicted superconducting gap was found in STS spectra measured at 5 K.     

Pt interactions with annealed and chemically-etched Nb-doped SrTiO3(0 0 1) surfaces: Metal/oxide surface chemical effects on band bending behavior

XPS and LEED have been used to characterize the interaction of sputter-deposited Pt (maximum coverage <5 ML) with Nb-doped SrTiO₃(0 0 1) surfaces prepared either by annealing in O₂ and then UHV, or by chemical-etching in aqua regia. The annealed surface exhibits an ordered (1 × 1) LEED pattern, with additional diffraction spots and streaks indicating the presence of oxygen vacancies. Increasing Pt coverage results in the decrease of the observed Pt(4f_7/2) binding energy and the uniform shift of the Sr(3d), Ti(2p) and O(1s) levels to smaller binding energies, as expected for Pt cluster growth and surface-to-Pt charge donation on an n-type semiconductor. The etched surface is disordered, and exhibits a hydroxylated surface with a contaminant C film of ∼23 ? average thickness. Pt deposition on the etched surface results in an immediate decrease in the intensity of the OH feature in the O(1s) spectrum, and a uniform shift of the Sr(3d), Ti(2p) and O(1s) levels to larger binding energies with increasing Pt coverage. The observed Pt(4f_7/2) binding energy on the etched surface (∼72 eV) is independent of Pt coverage, and indicates substantial electronic charge donation from the Pt to surface hydroxyl species. The observation of band bending towards higher binding energies upon Pt deposition (behavior normally associated with p-type semiconductors) demonstrates that sub-monolayer quantities of adsorbates can alter metal/oxide interfacial charge transfer and reverse the direction of band bending, with important consequences for Schottky barrier heights and device applications.     

Growth and decay of the Pd(1 1 1)-Pd5O4 surface oxide: Pressure-dependent kinetics and structural aspects

Growth and decomposition of the Pd₅O₄ surface oxide on Pd(1 1 1) were studied at sample temperatures between 573 and 683 K and O₂ gas pressures between 10⁻⁷ and 6 × 10⁻⁵ mbar, by means of an effusive O₂ beam from a capillary array doser, scanning tunnelling microscopy (STM) and thermal desorption spectrometry (TDS). Exposures beyond the p(2 × 2)O adlayer (saturation coverage 0.25) at 683 K (near thermodynamic equilibrium with respect to Pd₅O₄ surface oxide formation) lead to incorporation of additional oxygen into the surface. To initiate the incorporation, a critical pressure beyond the thermodynamic stability limit of the surface oxide is required. This thermodynamic stability limit is near 8.9 × 10⁻⁶ mbar at 683 K, in good agreement with calculations by density functional theory. A controlled kinetic study was feasible by generating nuclei by only a short O₂ pressure pulse and then following further growth kinetics in the lower (10⁻⁶ mbar) pressure range.Growth of the surface oxide layer at a lower temperature (573 K) studied by STM is characterized by a high degree of heterogeneity. Among various metastable local structures, a seam of disordered oxide formed at the step edges is a common structural feature characteristic of initial oxide growth. Further oxide nucleation appears to be favoured along the interface between the p(2 × 2)O structure and these disordered seams. Among the intermediate phases one specifically stable phase was detected both during growth and decomposition of the Pd₅O₄ layer. It is hexagonal with a distance of about 0.62 nm between the protrusions. Its well-ordered form is a superstructure.Isothermal decay of the Pd₅O₄ oxide layer at 693 K involves at first a rearrangement into the structure, indicating its high-temperature stability. This structure can break up into small clusters of uniform size and leaves a free metal surface area covered by a p(2 × 2)O adlayer. The rate of desorption increases autocatalytically with increasing phase boundary metal-oxide. We propose that at close-to-equilibrium conditions (693 K) surface oxide growth and decay occur via this intermediate structure.     

Carbon monoxide adsorption on the metastable fcc-Co/Cu(1 0 0) surface

The adsorption properties of CO on the epitaxial five-monolayer Co/Cu(1 0 0) system, where the Co overlayer has stabilized in the metastable fcc-phase, are reported. This system is known to exhibit metallic quantum well (MQW) states at energies 1 eV or greater above the Fermi level, which may influence CO adsorption. The CO/fcc-Co/Cu(1 0 0) system was explored with low energy electron diffraction (LEED), inverse photoemission (IPE), reflection-absorption infrared spectroscopy (RAIRS) and temperature programmed desorption (TPD). Upon CO adsorption, a new feature is observed in IPE at 4.4 eV above E_F and is interpreted as the CO 2π^∗ level. When adsorbed at room temperature, TPD exhibits a CO desorption peak at ∼355 K, while low temperature adsorption reveals additional binding configurations with TPD features at ∼220 K and ∼265 K. These TPD peak temperatures are correlated with different C-O stretch vibrational frequencies observed in the IR spectra. The adsorption properties of this surface are compared to those of the surfaces of single crystal hcp-Co, as well as other metastable thin film systems.     

The ν1 + 3ν2 + 3ν3 and 4ν1 + ν2 + ν3 bands of ozone by CW-cavity ring down spectroscopy between 5900 and 5960 cm

The absorption spectrum of ozone, ¹⁶O₃, has been recorded in the 5903-5960 cm⁻¹ region by high sensitivity CW-cavity ring down spectroscopy (α_min ∼ 5 × 10⁻¹⁰ cm⁻¹). The ν₁ + 3ν₂ + 3ν₃ and 4ν₁ + ν₂ + ν₃ A-type bands centred at 5919.15 and 5947.07 cm⁻¹ were newly observed. A set of 173 and 168 energy levels could be experimentally determined for the (1 3 3) and (4 1 1) states, respectively. Except for a few K_a = 5 levels of the (4 1 1) state, the rotational structure of the two states was found mostly unperturbed. The spectroscopic parameters were determined from a fit of the corresponding line positions by considering the (1 3 3) and (4 1 1) states as isolated. The determined effective Hamiltonian and transition moment operators were used to generate a list of 785 transitions given as Supplementary Material.     

Formation and hydrogenation of p(2 × 2)-N on Pt(1 1 1)

The formation of a well-ordered p(2 × 2) overlayer of atomic nitrogen on the Pt(1 1 1) surface and its reaction with hydrogen were characterized with reflection absorption infrared spectroscopy (RAIRS), temperature programmed desorption (TPD), low energy electron diffraction (LEED), Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS). The p(2 × 2)-N overlayer is formed by exposure of ammonia to a surface at 85 K that is covered with 0.44 monolayer (ML) of molecular oxygen and then heating to 400 K. The reaction between ammonia and oxygen produces water, which desorbs below 400 K. The only desorption product observed above 400 K is molecular nitrogen, which has a peak desorption temperature of 453 K. The absence of oxygen after the 400 K anneal is confirmed with AES. Although atomic nitrogen can also be produced on the surface through the reaction of ammonia with an atomic, rather than molecular, oxygen overlayer at a saturation coverage of 0.25 ML, the yield of surface nitrogen is significantly less, as indicated by the N₂ TPD peak area. Atomic nitrogen readily reacts with hydrogen to produce the NH species, which is characterized with RAIRS by an intense and narrow (FWHM ∼ 4 cm⁻¹) peak at 3322 cm⁻¹. The areas of the H₂ TPD peak associated with NH dissociation and the XPS N 1s peak associated with the NH species indicate that not all of the surface N atoms can be converted to NH by the methods used here.     

The far-infrared spectrum of acrolein, CH2CHCHO: The ν18 fundamental and (ν17 + ν18) − ν18 hot bands

The ν₁₈ fundamental band (∼158 cm⁻¹) of acrolein is studied at high resolution (0.0015 cm⁻¹) using synchrotron radiation from the Canadian Light Source facility and a Bruker IFS 125HR Fourier transform spectrometer. By fitting this band, together with some pure rotational transitions, molecular parameters are obtained to accurately determine the energies of the ν₁₈ = 1 state levels for values of (J, K_a) up to at least (45, 24). These parameters should be useful for future high resolution studies of acrolein hot bands. This is demonstrated here by a detailed analysis of the (ν₁₇ + ν₁₈) − ν₁₈ hot band at ∼589 cm⁻¹. The upper state (ν₁₇ + ν₁₈) of this band is found to be perturbed by Coriolis interactions analogous to those affecting the ν₁₇ state.     

Initial stages of the autocatalytic oxidation of the InAs(0 0 1)-(4 × 2)/c(8 × 2) surface by molecular oxygen

The initial stages of oxidation of the In-rich InAs(0 0 1)-(4 × 2)/c(8 × 2) surface by molecular oxygen (O₂) were studied using scanning tunneling microscopy (STM) and density functional theory (DFT). It was shown that the O₂ dissociatively chemisorbs along the rows in the [1 1 0] direction on the InAs surface either by displacing the row-edge As atoms or by inserting between In atoms on the rows. The dissociative chemisorption is consistent with being autocatalytic: there is a high tendency to form oxygen chemisorption sites which grow in length along the rows in the [1 1 0] direction at preexisting oxygen chemisorption sites. The most common site size is about 21-24 Å in length at ∼25% ML coverage, representing 2-3 unit cell lengths in the [1 1 0] direction (the length of ∼5-6 In atoms on the row). The autocatalysis was confirmed by modeling the site distribution as non-Poisson. The autocatalysis and the low sticking probability (∼10⁻⁴) of O₂ on the InAs(0 0 1)-(4 × 2)/c(8 × 2) are consistent with activated dissociative chemisorption. The results show that is it critical to protect the InAs surface from oxygen during subsequent atomic layer deposition (ALD) or molecular beam epitaxy (MBE) oxide growth since oxygen will displace As atoms.     

High sensitivity ICLAS of D2O between 12 450 and 12 850 cm

The weak absorption spectrum of dideuterated water, D₂O, has been recorded between 12 450 and 12 850 cm⁻¹ by high sensitivity Intracavity Laser Absorption Spectroscopy (ICLAS). This spectral region corresponds to the (ν₁ + ν₂/2 + ν₃) = 5 polyad, dominated by the 4ν₁ + ν₃ band centered at 12 743.035 cm⁻¹. The achieved sensitivity has allowed for the detection of lines with a minimum intensity of 2 × 10⁻²⁸ cm/molecule i.e. typically two orders of magnitude lower than previous observations in the region considered. A total of 586 energy levels belonging to 11 vibrational states were determined. The rovibrational assignment process of 1025 lines ascribed to D₂O was based on new results of variational calculations by Shirin et al. [S.V. Shirin, N.F. Zobov, O.L. Polyansky, J. Quant. Spectrosc. Radiat. Transfer, in press, doi:10.1016/j.jqsrt.2007.07.010]. The overall agreement between these calculations and the observed spectrum is good both for the line positions and line intensities. The difficulties encountered while performing the rovibrational labeling and the assignment of the weakest transitions not included in Combination Differences relations, are discussed.     

Band offsets at the epitaxial anatase TiO2/n-SrTiO3(0 0 1) interface

We have used high-energy resolution X-ray photoelectron spectroscopy to measure valence band offsets at the epitaxial anatase TiO₂(0 0 1)/n-SrTiO₃(0 0 1) heterojunction prepared by molecular beam epitaxy. The valence band offsets range between −0.06 ± 0.05 and +0.16 ± 0.05 eV for anatase thicknesses between 1 and 8 monolayers and three different methods of substrate surface preparation, with no systematic dependence on film thickness. The conduction band offset (CBO) varies over a comparable range by virtue of the fact that anatase and SrTiO₃ exhibit the same bandgap (∼3.2 eV). In contrast, density functional theory predicts the VBO to be +0.55 eV. The lack of agreement between theory and experiment suggests that either some unknown factor in the interface structure or composition excluded from the modeling is influencing the band offset, or that density functional theory cannot accurately calculate band offsets in these oxide materials. The small experimental band offsets have important implications for the use of this interface for fundamental investigations of surface photocatalysis. Neither electrons nor holes are likely to become trapped in the substrate and thus be unable to participate in surface photocatalytic processes.     

Atomic and electronic structures of thin NaCl films grown on a Ge(0 0 1) surface

Density functional theory (DFT) with LDA and GGA have been employed to study the interface and thin film properties of NaCl on a Ge(0 0 1) surface. The atomic and electronic structures of thin NaCl films from one to ten monolayers were analyzed. The layer adsorption energies show that a quasi-crystalline (0 0 1) fcc NaCl film is built up via a layer-by-layer growth mode with NaCl thickness above 2 ML. Simulated STM images show a well-resolved (1 × 1) NaCl atomic structure for sample bias voltage V_s < −2.5 V and the bright protrusions should be assigned to the Cl⁻ ions of the NaCl film. The Ge substrate dimer is reserved and buckled like a clean Ge(0 0 1)-p(2 × 2) surface as the result of weak interface interaction between the dangling bonds coming from valence π states of the Ge substrate and the 3p states of the interfacial Cl⁻ ion. These results are consistent with the experiments of STM, LEED and EELS.