Thermal,morphology, and NMR characterizations on phase behavior and miscibility in blends of isotactic polystyrene with poly(cyclohexyl methacrylate)

The miscibility and phase behavior in a binary blend of isotactic polystyrene (iPS) and poly(cyclohexyl methacrylate) (PCHMA) were investigated by differential scanning calorimetry, optical microscopy (OM), and solid‐state ¹³C cross‐polarity/magic‐angle spinning NMR. The iPS/PCHMA blend was miscible when all compositions showed a single composition‐dependent glass‐transition temperature (T_g) and when the blend went through a thermodynamic phase transition upon heating to above the lower critical solution temperature as determined by OM measurements. The ¹H NMR spin‐relaxation times in the laboratory frame (T) and in the rotating frame (T) for iPS/PCHMA blends with various compositions and neat components were directly measured through solid‐state¹³C NMR. The results of T indicated that the blends are homogeneous, at least on a scale of 75–85 nm, confirming the miscibility of the system. The single decay and composition‐dependent T values for each blend further demonstrated the blends are homogeneous on a scale of 2.5–3.5 nm. The results suggested that iPS and PCHMA are intimately mixed at the molecular level within the blends at all compositions. The tacticity of polystyrene does not seem to adversely influence the miscibility in blends of iPS/PCHMA. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 772–784, 2003     

A Flory–Huggins thermodynamic approach for predicting sorption equilibrium in ternary polymer systems

The Flory–Huggins theory as modified by Pouchlý has been applied to calculate preferential (λ) and total (Y) sorption coefficients for a ternary polymer system. The ternary interaction function (?₁?₂?₃G_T(u₁, ?₃)) is described as the product of three independent binary functions. This expression allows prediction of λ and Y from binary interaction parameters χ, χ, g, g, and g₁₂(?₁₀). Three ternary polymer systems are used to check the validity of the expression. Moreover for polymer systems in which the parameters g and/or g are unknown, a procedure to evaluate them has been developed and verified on systems for which sufficient experimental information is available.     

Entanglement friction and dynamics in blends of starlike and linear polymer molecules

We investigate relaxation dynamics in a series of six‐arm star/linear 1,4‐polybutadiene blends with mechanical rheometry measurements. Blend systems are formulated to systematically probe constraint release and arm relaxation dynamics. Zero shear viscosity and terminal relaxation times of star/linear polymer blends with fixed star arm molecular weights (M_a) and compositions (?_S) are found to follow nonmonotonic dependencies on the linear polymer molecular weight (M_L). At low values of ?_S, at least two scaling regimes are apparent from the data (ξ₀ ～ M and ξ₀ ～ M), where ξ₀ refers to the zero shear viscosity or terminal relaxation time of the blend. The two regimes are separated by a critical linear polymer molecular weight M^* that is more than 20 times larger than the critical molecular weight for entanglements. When the linear polymer contribution to blend properties is removed, a clear transition from dilution dynamics, ξ₀ ～ M, to Rouse‐like constraint‐release dynamics, ξ₀ ～ M, is apparent at low values of ?_S. At higher ?_S values, a new activated constraint‐release dynamic regime is evident in which ξ₀ ～ M and ξ₀ ～ ?, where α changes continuously from approximately 2 to 0.5 as ?_S increases and β varies from 2.0 to 1.0 as M_L increases. The experimental results are compared with theoretical predictions based on a drag coupling model for entangled polymer liquids. All features observed experimentally are captured by this model, including the value of M^* for the transition from dilution to Rouse constraint‐release dynamics. Predictions of the drag coupling model are also compared with published data for the zero shear viscosity and terminal relaxation time in bidisperse linear polymer blends and pure entangled starlike molecules. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2501–2518, 2001     

Thermodynamics of miscible polymer blends using a concentration-dependent χ parameter

The Flory equation-of-state theory, as expressed by Patterson and co-workers, has been applied to two miscible polymer blends: poly(vinyl chloride)/poly(ε-caprolactone) and poly(methyl methacrylate)/poly(vinylidene chloride). For both blends, the variation of the polymer-polymer interaction parameter, χ, as a function of composition, is mostly small and can be accounted for by the Flory theory. However, for poly(vinyl chloride)/poly(ε-caprolactone) blends, at high poly(ε-caprolactone content), the large variation of χ as a function of concentration can be explained by a variation of the surface-to-volume ratio of the polymers in the mixture with blend composition. The variations of the surface-to-volume ratios determined in this study agree with those reported in the literature using small-angle x-ray scattering.     

Intrinsic birefringence of poly(trimethylene terephthalate)

Highly oriented poly(trimethylene terephthalate) (PTT) fiber has a low birefringence that is unexpected for an aromatic polyester with a high refractive index. To explain this observation, the intrinsic birefringence Δn of PTT crystal was calculated from its bond polarizabilities to be 0.029. This Δn is almost an order of magnitude smaller than poly(ethylene terephthalate)'s value at 0.22, although both polymers have nearly identical crystal refractive indices. The small Δn is due to the arrangement of PTT's methylene groups in gauche conformations, causing the chain‐repeating unit to be tilted ～53° away from the c axis toward the basal plane. Because of the small Δn, the crystalline‐phase orientation made only a small contribution to the overall birefringence despite the fiber's high crystallinity and orientation. To understand the effect of the number of methylene groups on polyester optical anisotropy, the Δn's of a series of poly(m‐alkylene terephthalates) with m = 2–5 were compared and correlated with ψ: an angle made by the normal of the benzene ring with the crystal's axis. As ψ′ decreases, Δn of the polyesters diminishes. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1513–1520, 2002     

Molecular orientation in biaxially oriented sheets of poly(ethylene terephthalate). I. Characterization of orientation and comparison with models

A study of molecular orientation in a series of five one-way-drawn sheets of poly(ethylene terephthalate) is reported. Five orientation averages P which characterize the benzene-ring orientation were determined directly by Raman spectroscopy. Two further averages P and P were determined from a combination of Raman spectroscopy and refractive index measurements on the basis of two different conformational models. As in a previous publication, the seven averages P were used to estimate all the P up to fourth order for the benzene rings on the assumption that in each case the actual distribution of orientations is close to the most probable distribution. The seven orientation averages P for each drawn sheet were also compared with those calculated on the basis of two simple models for the development of molecular orientation during drawing, the pseudoaffine deformation scheme and the rubber network model. It was shown that the orientation of the chain axes is closer to that predicted by the rubber network model, the pseudoaffine deformation scheme greatly overestimating the degree of chain biaxiality. The results also show that the benzene ring planes are preferentially oriented toward the planes of the sheets. The chain axis orientation is, however, nearly uniaxial and similar to that observed for uniaxially drawn samples, suggesting that there is no direct connection between the processes of chain axis orientation and preferential orientation of the benzene-ring planes.     

Structure and viscoelasticity of matched asymmetric diblock and triblock copolymers in the cylinder and sphere microstructures

A polystyrene–polyisoprene (PS–PI) diblock copolymer (10,000–50,000 g/mol) and a matched PS&ndashPI–PS triblock (10,000–100,000–10,000 g/mol) were employed to study the effect of chain architecture on the rheological response of ordered block copolymer melts. Both samples adopt hexagonal microstructures with PS cylinders embedded in a PI matrix; on further heating, an order–order transition (OOT) into a cubic array of spheres takes place prior to the order–disorder transition. Each morphology was verified by SAXS and TEM. Interestingly, at the OOT the low-frequency elastic modulus of the diblock increased abruptly, whereas that of the triblock decreased. In contrast, the modulus of the cubic phase was roughly independent of chain architecture. Chain relaxation parallel and perpendicular to the cylinders was probed by measuring the elastic modulus of a macroscopically aligned sample in directions parallel G and perpendicular (G) to the cylinder orientation. For both materials G < G < G where G is the elastic modulus of a randomly oriented sample. This result is attributed to the ability of the unentangled PS blocks to move along the direction of the cylinder axis, and thus relax the stress in the PI matrix in the parallel alignment. In each of the three cylindrical orientations the triblock had a larger modulus than the diblock, which is attributed to the presence of bridging PI blocks that connect distinct PS domains. About 20° below the OOT G showed a distinct change in its temperature dependence, which, coupled with SAXS measurements, is indicative of the onset of an undulation in the cylinder diameter that presages the pinching off of cylinders into spheres, as recently predicted by theory. The use of oriented samples also permitted SAXS confirmation of an approximate epitaxial relationship between the cylinder and the sphere unit cells, although a distinct change in the location of the structure factor maximum, q^*, is noted at the OOT. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35: 2811–2823, 1997     

Thermal characterization of polycarbonate/polycaprolactone blends

In this work, we prepared blends of bisphenol A polycarbonate (PC) and poly(ϵ‐caprolactone) (PCL) in a wide composition range by melt mixing and solution mixing. Two different molecular weights of PCL were used (nominally, 10.000 g/mol, PCL10, and 80.000 g/mol, PCL80). The thermal behavior of both systems was studied via differential scanning calorimetry under dynamic and isothermal conditions. The blends were miscible in the entire composition range in the liquid and amorphous states, as indicated by the single glass‐transition temperature (T_g) exhibited by both the PC/PCL10 and PC/PCL80 blends. The compositional variation of the T_g was accurately described by the Fox equation for the PC/PCL80 blends, whereas slight deviations from this equation were exhibited by the PC/PCL10 blends. For blend compositions containing 40% or more PCL, either one or both blend components crystallized. Crystallization occurred during cooling from the melt or during subsequent heating in the form of cold crystallization. Although PCL crystallization was reduced and its crystallization rate decreased with the addition of PC, PCL was a very effective macromolecular plasticizer for PC, to the extent that crystallization during the scan was detected for some blend compositions. Isothermal crystallization experiments allowed the determination of equilibrium melting points (T) by the Hoffman–Weeks extrapolation method. A T depression was found for both PCL and PC components as the content of the other blend component was increased. The Avrami equation was closely obeyed by both blend components during the isothermal overall crystallization kinetics up to crystalline conversion degrees of 60–70% and with values of Avrami indices ranging from 3 to 4, depending on the crystallization temperature employed. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 771–785, 2001     

Solid‐state nuclear magnetic resonance relaxation times in crosslinked macroporous polymer particles of divinylbenzene homopolymers

Monodisperse porous particles of poly(divinylbenzene) prepared by the activated swelling method have been investigated by solid‐state ¹³C crosspolarization magic‐angle spinning (CPMAS) nuclear magnetic resonance (NMR) relaxation measurements. Homopolymeric combinations of two porogens (toluene and 2‐ethylhexanoic acid) and two monomers (meta‐ and para‐divinylbenzene) were studied. Residual vinyl groups were systematically reacted with increasing amounts of bromine, producing 20 different polymers samples for which we measured crosspolarization times, T_CH, proton rotating frame spin‐lattice relaxation, T, ¹³C spin‐lattice relaxation, T, and proton spin‐lattice relaxation, T. These parameters were chosen to reflect expected changes in a wide range of frequencies of motion as a function of structure. Relative differences in the molecular mobility of the major functional groups (aromatic, vinyl and aliphatic) is related to initial reactants used, vinyl concentration, relative reactivity of vinyl groups, distribution of vinyl groups, pore structure, and degree of crosslinking. Variable temperature ¹H combined rotation and multiple pulse NMR (CRAMPS) was used to derive activation energies for selected samples via measurement of the proton spin‐lattice relaxation time, T. Irreversible thermal effects were observed in ambient temperature relaxation after heating to temperatures in the range of 393–418 K. Simple univariate statistical analyses failed to reveal consistent correlations among the known variables. However, the application of more sophisticated multivariate and neural network analyses allowed excellent structure–property predictions to be made from the relaxation time data. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 1307–1328, 1999     

Determination of the crystallinity of polyethylene/α‐olefin copolymers by thermal analysis: Relationship of the heat of fusion of 100% polyethylene crystal and the density

The heat of fusion measured with differential scanning calorimetry (DSC) is typically divided by a constant value of the heat of fusion of 100% polyethylene (PE) crystal (ΔH) for the estimation of the fraction crystallinity of PE copolymers, regardless of the density [i.e., the short‐chain branching (SCB) concentration]. In this work, values of ΔH of about 288 J/g were determined with a combined DSC and X‐ray diffraction (XRD) method for a series of PE copolymers containing SCB from 0 to 50 Br/1000 C (density = 0.965–0.865 g/cc). There was no systematic change in ΔH observed across this density range. This result supports the suitability of determining the fraction crystallinity of PE of any density by the simple division of the observed heat of fusion determined by DSC by a constant value of ΔH. This DSC method yielded values of PE crystallinity in good agreement with corresponding values determined by XRD for a series of PE copolymers. The determination of ΔH involved a small precision error for higher density (lower SCB) PEs, but the precision error increased for lower density (i.e., higher SCB) PEs. This was due to the difficulty in measuring the heat of fusion for lower density PEs, which exhibited low values of the heat of fusion and melted only slightly above room temperature, and due to the difficulty of measuring lower values of crystallinity by XRD. The crystal thickness measured by small‐angle X‐ray scattering for this series of PE copolymers decreased exponentially from about 280 to 6 Å. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1637–1643, 2002     

Linear versus nonlinear determinations of equilibrium melting temperatures of poly(trimethylene terephthalate) and miscible blend with poly(ether imide) exhibiting multiple melting peaks

Multiple melting peaks in some semicrystalline polymers such as poly(trimethylene terephthalate) (PTT) have caused some difficulty in estimating accurately the equilibrium melting points. PTT forms a miscible blend with amorphous poly(ether imide) (PEI); for comparison purposes, a miscible system of a fixed composition (PTT/PEI of weight ratio = 9/1) was determined. PTT and its miscible blend both exhibited dual melting peaks (labeled as low and high peaks: T_m,L, T_m,H), and the first peaks (T_m,L), not the second peak (T_m,H), should be used for extrapolation. The equilibrium melting temperatures (T) of neat PTT and its blend PTT/PEI (9/1) were 245.2 and 242.4 °C, respectively, by the linear Hoffman–Weeks treatment using the corrected values of T_m,L (i.e., values obtained using a heating rate close to zero). Linear and nonlinear treatments led to a significant difference in estimated T, and the relative validity of these two methods is discussed. The nonlinear estimate yielded a higher value by about 27.3 °C for neat PTT and 23.1 °C for the PTT/PEI (9/1) blend, respectively (also the correction in T_m,L at the same condition mentioned previously). Results showed melting depression in miscible PTT/PEI (9/1). In addition, the T value of neat PTT was higher than that of PTT/PEI (9/1) owing to much thicker and more‐perfect crystals in neat PTT. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1571–1581, 2002     

Determination of molecular weight and its distribution of rigid‐rod polymers determined by phase‐modulated flow birefringence technique

The phase‐modulated flow birefringence (PMFB) method is widely accepted as one of the most sensitive and accurate techniques suitable for experimental tests on the molecular theory of polymer solutions. The objective of this study is to develop a systematic method to determine molecular weight and distribution of rigid‐rod polymers by the PMFB technique. Using molecular theory for rigid polymers, birefringence Δn and orientation angle χ have been expressed as a function of molecular weight and distribution. Δn has been shown to be proportional to Σc_iM, and cot 2χ turned out to have a linear relationship with Σc_iM/Σc_iM. From the experimental results for PBLG solutions, birefringence and orientation angle data were in some degree matched with the theory presented. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 509–515, 2000     

Melt‐state polymer chain dimensions as a function of temperature

The unperturbed chain dimensions (〈R²〉_o/M) of cis/trans‐1,4‐polyisoprene, a near‐atactic poly(methyl methacrylate), and atactic polyolefins were measured as a function of temperature in the melt state via small‐angle neutron scattering (SANS). The polyolefinic materials were derived from polydienes or polystyrene via hydrogenation or deuteration and represent structures not encountered commercially. The parent polymers were prepared via lithium‐based anionic polymerizations in cyclohexane with, in some cases, a polymer microstructure modifier present. The polyolefins retained the near‐monodisperse molecular weight distributions exhibited by the precursor materials. The melt SANS‐based chain dimension data allowed the evaluation of the temperature coefficients [dln 〈R²〉_o/dT(κ)] for these polymers. The evaluated polymers obeyed the packing length (p)‐based expressions of the plateau modulus, G = kT/np³ (MPa), and the entanglement molecular weight, M_e = ρN_anp³ (g mol^?1), where n_t denotes the number (～21) of entanglement strands in a cube with the dimensions of the reptation tube diameter (d_t) and ρ is the chain density. The product np³ is the displaced volume (V_e) of an entanglement that is also expressible as pd or kT/G. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1768–1776, 2002     

New simple method of measuring the surface glass transition temperature of polymers

A lap‐shear joint mechanical testing method has been probed to measure the surface glass transition temperature (T) of the thick bulk films of high‐molecular‐weight polymers. As T, the temperature transition “occurrence of autoadhesion–nonoccurrence of autoadhesion” has been proposed. The influence of chain flexibility, of molecular architecture, of polymer morphology, and of chain ends concentration on the T has been investigated. The correlation between the reduction in T with respect to the glass transition temperature of the bulk (T) and the intensity of the intermolecular interaction in the polymer bulk in amorphous polymers has been found. The effect of surface roughness on T has been discussed. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 2012–2021, 2010     

Nonlinear rheology of highly entangled polymer solutions in start‐up and steady shear flow

Orientation angle and stress‐relaxation dynamics of entangled polystyrene (PS)/diethyl phthalate solutions were investigated in steady and step shear flows. Concentrated (19 vol %) solutions of 0.995, 1.81, and 3.84 million molecular weight (MW) PS and a semidilute (6.4 vol %) solution of 20.6 million MW PS were used to study the effects of entanglement loss on dynamics. A phase‐modulated flow birefringence apparatus was developed to facilitate measurements of time‐dependent changes in optical equivalents of shear stress (n₁₂ ≈ Cσ) and first normal stress differences (n₁ = n₁₁ ? n₂₂ ≈ CN₁) in a planar‐Couette shear‐flow geometry. Flow birefringence results were supplemented with cone‐and‐plate mechanical rheometry measurements to extend the range of shear rates over which entangled polymer dynamics are studied. In slow (τ > ) steady shear‐flow experiments using the ultrahigh MW polymer sample (20.6 × 10⁶ MW PS), steady‐state n₁₂ and n₁ results manifest unusual power‐law dependencies on shear rate [n_12,ss ～ ^0.4 and n_1,ss ～ ^0.8]. At shear rates in the range τ < < τ, steady‐state orientation angles χ_SS are found to be nearly independent of shear rate for all but the most weakly entangled materials investigated. For solutions containing the highest MW PS, an approximate plateau orientation angle χ_p in the range 20–24° is observed; χ_p values ranging from 14 to 16° are found for the other materials. In the start‐up of fast steady shear flow (γ˙ ≥ τ), transient undershoots in orientation angle are also reported. The molecular origins of these observations were examined with the help of a tube model theory that accommodates changes in polymer entanglement density during flow. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2275–2289, 2001     

Phase behavior and crystallization analysis in binary crystalline blends of syndiotactic polypropylene and ethylene—Propylene random copolymer

The effects of liquid–liquid (L–L) phase separation on the crystallization behavior of binary syndiotactic polypropylene (sPP) and ethylene–propylene random copolymer (PEP) mixtures are examined by phase‐contrast microscopy (PCM), differential scanning calorimetry (DSC), and cloud point measurements. The PCM experiments reveal that blends of sPP and PEP exhibit a lower critical solution temperature behavior in the melt. The L–L phase diagram, constructed in terms of temperature (T) and composition by cloud point measurements, follows the prediction of the Flory–Huggins theory with the interaction parameter between sPP and PEP [χ(T) = 0.01153 ? 4.5738/T (K)]. When the blends are melted within the two liquid‐phase (α and β) regions, because of the fact that each phase domain reaches the equilibrium concentration ? and ? as well as the phase volume fraction ν^α and ν^β, the crystallinity of each component obeys the equation X_C,I = ν^α X + ν^β X, I = PEP, sPP. Also, the equilibrium melting temperatures of both components remain constants, slightly lower than those of neat polymers. For the sPP/PEP blends crystallized from one homogeneous phase in the melt, we observe that the crystallizability of the major component is not greatly affected upon blending. However, the crystallization behavior of the minority component in the presence of the major component is strongly dependent on the crystallization temperature (T_c). When T_c is high, because the decreasing degree of the minority mobility is much greater than the increasing degree of the formed nuclei, the crystallizability of the minor component is depressed significantly. On the other hand, the promotion of the minority crystallizability in the intermediate regime of T_c is mainly because of the large increase of the heterogeneous nuclei upon blending with a major component. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2995–3005, 2004     

Crystal thickness distributions from melting homopolymers or random copolymers

Differential scanning calorimetry (DSC) can be used to infer the distribution of lamellar crystal thickness l. For homopolymers, the relation between melting temperature T and thickness is described by the Gibbs relation. In this case the weight distribution function of thickness g(l) ∝ P(T)(T − T)², where P(T) is DSC power and T is the melting temperature of an infinitely thick crystal. Copolymer melting is affected by the concentration of noncrystallizable comonomer in the melt as well as lamellar thickness. Unknown melt composition in copolymers with nonequilibrium crystallinity makes determination of the correct distribution g(l) from DSC impossible. An approximate distribution g₂(l) ∝ P(T)(T − T)² is proposed, where T is based on Flory's equilibrium crystallization theory. This approximate distribution is most accurate when crystallinity is small, that is, near the upper end of the melting range. Results are reported for polyethylene homopolymer and model ethylene–butene random copolymers. Corrections were not made for distortion of the DSC endotherms by thermal lag or by melting and recrystallization; these experiments are primarily to illustrate the effect of analysis in terms of an incorrect g₃(l) ∝ P(T). Average crystal thicknesses are about 20 nm for polyethylene and 5 nm for the copolymers. Distributions are characterized by l_w /l_n ≤ 1.1 in all cases. Width of the melting range is not a reliable indicator of the breadth of the thickness distribution. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 3131–3140, 1999     

A procedure for predicting sorption equilibrium in ternary polymer systems from Flory–Huggins binary interaction parameters and the inversion point of preferential solvation

A procedure has been developed, based on the Flory–Huggins theory as generalized by Pouchlý, which permits the calculation of preferential (λ) and total (Y) sorption coefficients from previous information on the binary interaction parameters, χ, χ, and g₁₂(?₁₀) and on the mixture composition at which the sign of λ inverts. The expressions obtained were applied to 10 cosolvent polymer systems for which experimental values of λ and Y are known. Practically in all the studied systems, the theoretical predictions are in fair accordance with the experimental data.     

Miscibility and thermal properties of melt‐mixed poly(trimethylene terephthalate)/amorphous copolyester blends

This work examined the miscibility, crystallization kinetics, and melting behavior of melt‐mixed poly(trimethylene terephthalate) (PTT)/poly(ethylene‐co‐cyclohexane 1,4‐dimethanol terephthalate) (PETG) blends. Differential scanning calorimetry (DSC) and wide‐angle X‐ray diffraction techniques were used to approach the goals. The single composition‐dependent glass‐transition temperatures of the blends and the equilibrium melting temperature (T) depression of PTT in the blends indicated the miscible characteristic of the blend system at all compositions. T of pure PTT, determined with a conventional extrapolative method, was 525.8 K. Furthermore, the Flory–Huggins interaction parameter was estimated to be ?0.38. The dynamic and isothermal crystallization abilities of PTT were hindered by the incorporation of PETG. A complex melting behavior was observed for pure PTT and its blends. The observed complex melting behavior resulted mainly from the recrystallization and/or reorganization of the originally formed crystals during the heating scans. For the samples crystallized under the same conditions, the degree of recrystallization and/or reorganization declined with increasing PETG contents in the blends. The preliminary results obtained from the DSC experiments suggested that untraceable interchange reactions occurred in the studied blends. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 2264–2274, 2003     

Counterion binding to poly(allylammonium) cation

Chloride ion activity coefficients in aqueous solutions of poly(allylamine) hydrochloride (PAA · HCl) have been determined both in the absence and the presence of simple salts. Without added salt, the activity coefficient depends on the polymer concentration. With added salt, the binding of added counterions by PAAH⁺ is evaluated from the release of chloride ion. The extent of interaction between counterions and PAAH⁺ at a given polymer concentration decreases in the order SO ? ClO > NO > Cl^? > Br^? > I^?. This order of counterion selectivity agrees with the previous estimation of potentiometric titrations. The result shows that the hydration of the counterion, as well as its charge, plays an important part in counterion binding to the polyion.