Synthesis of dual‐functional poly(6‐azidohexylmethacrylate) brushes by a RAFT agent carrying carboxylic acid end groups

Novel types of dual‐functional surface‐attached polymer brushes were developed by interface‐mediated reversible addition‐fragmentation chain transfer (RAFT) polymerization of 6‐azidohexylmethacrylate using the surface‐immobilized RAFT agent and the free initiator. The interface‐mediated RAFT polymerization produced silicon substrate coated with dual‐functional (azido groups from monomer and carboxylic acid groups from RAFT agent) poly(6‐azidohexylmethacrylate) [poly (AHMA)] with a grafting density as high as 0.59 chains/nm². Dual‐functional polymer brushes can represent an attractive chemical platform to deliberately introduce other molecular units at specific sites. The azido groups of the poly(AHMA) brushes can be modified with alkyl groups via click reaction, known for their DNA hybridization, while the carboxylic acid end groups can be reacted with amine groups via amide reaction, known for their antifouling properties. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1696–1706     

Synthesis of cationic N‐[3‐(dimethylamino)propyl]methacrylamide brushes on silicon wafer via surface‐initiated RAFT polymerization

Surface‐initiated reversible addition‐fragmentation chain transfer (SI‐RAFT) polymerization of N‐[3‐(dimethylamino)propyl]methacrylamide (DMAPMA) on the silicon wafer was conducted in attempt to create controllable cationic polymer films. The RAFT agent‐immobilized substrate was prepared by the silanization of hydroxyl groups on silicon wafer with 3‐aminopropylthriethoxysilane (APTS) and by the amide reaction of amine groups of APTS with ester groups of 4‐cyano‐4‐((thiobenzoyl) sulfanyl) pentanoic succinimide ester (CPSE); followed by the RAFT polymerization of DMAPMA using a “free” RAFT agent, that is, 4‐cyanopentanoic acid dithiobenzoate (CPAD) and an initiator, that is, 4,4′‐azobis‐4‐cyanopentanoic acid (CPA). The formation of homogeneous tethered poly(N‐[3‐(dimethylamino)propyl]methacrylamide) [poly(DMAPMA)] brushes, whose thickness can be tuned by reaction time varying, is evidenced by using the combination of grazing angle attenuated total reflectance‐Fourier transform infrared spectroscopy, X‐ray photoelectron spectroscopy, atomic force microscopy, and water contact‐angle measurements. The calculation of grafting parameters from the number‐average molecular weight, M _n (g/mol) and ellipsometric thickness, h (nm) values indicated the synthesis of densely grafted poly(DMAPMA) films and allowed us to predict a polymerization time for forming a “brush‐like” conformation for the chains. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Surface‐initiated single‐electron transfer reversible addition–fragmentation chain transfer polymerization of 2‐hydroxyethyl acrylamide on silicon substrate at ambient temperature

2‐Hydroxyethyl acrylamide was successfully polymerized via single‐electron transfer initiation on the silicon surface and propagation through the reversible addition–fragmentation chain transfer (SET‐RAFT) polymerization at ambient temperature for different polymerization times. This work is the first time application of the surface‐initiated SET‐RAFT mechanism to afford the preparation of well‐defined poly(2‐hydroxyethyl acrylamide) [poly(HEAAm)] brushes at ambient temperature. The polymerization was well controlled and produced poly(HEAAm) brushes on the silicon surface with a well‐defined target molecular weight. The controlled nature of the polymerization was further demonstrated in the presence of sulfur atoms at the chain ends in X‐ray photoelectron spectroscopy experiments. The grafting density (σ, chains nm^?2) and the average distance between grafting points (D, nm) were found to be 0.42 chains nm^?2 and 1.74 nm, respectively, indicating moderate grafting density. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 1140–1146     

High density cationic polymer brushes from combined “click chemistry” and RAFT‐mediated polymerization

A simple method for preparing cationic poly[(ar‐vinylbenzyl)trimethylammonium chloride)] [poly(VBTAC)] brushes was used by combined technology of “click chemistry” and reversible addition‐fragmentation chain transfer (RAFT) polymerization. Initially, silicon surfaces were modified with RAFT chain transfer agent by using a click reaction involving an azide‐modified silicon wafer and alkyne‐terminated 4‐cyanopentanoic acid dithiobenzoate (CPAD). A series of poly(VBTAC) brushes on silicon surface with different molecular weights, thicknesses, and grafting densities were then synthesized by RAFT‐mediated polymerization from the surface immobilized CPAD. The immobilization of CPAD on the silicon wafer and the subsequent polymer formation were characterized by X‐ray photoelectron spectroscopy, water contact angle measurements, grazing angle‐Fourier transform infrared spectroscopy, atomic force microscopy, and ellipsometry analysis. The addition of free CPAD was required for the formation of well‐defined polymer brushes, which subsequently resulted in the presence of free polymer chains in solution. The free polymer chains were isolated and used to estimate the molecular weights and polydispersity index of chains attached to the surface. In addition, by varying the polymerization time, we were able to obtain poly(VBTAC) brushes with grafting density up to 0.78 chains/nm² with homogeneous distributions of apparent needle‐like structures. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis of low grafting density molecular brush from a poly(N‐alkyl urea peptoid) backbone

The synthesis of a molecular brush was accomplished by combining step‐growth polymerization and reversible addition fragmentation chain transfer (RAFT) polymerization in a “grafting from” methodology. A symmetrical N‐alkyl urea peptoid sixmer containing alkyne functional groups was prepared using a divergent strategy, and the structure of the product was confirmed using NMR spectroscopy and mass spectrometry. A step‐growth process was used to prepare a linear poly(N‐alkyl urea peptoid) by reacting the diamine‐functionalized N‐alkyl urea peptoid sixmer with a diisocyanate. RAFT chain transfer agents were coupled to the poly(N‐alkyl urea peptoid) backbone through a copper‐catalyzed azide/alkyne cycloaddition reaction. The afforded macro‐RAFT agent was used to sequentially polymerize styrene and tert‐butyl acrylate block copolymer arms from the poly(N‐alkyl urea peptoid) backbone. The tert‐butyl groups were removed using dilute trifluoroacetic acid affording hydrophilic polyacrylic acid segments. The molecular brushes were observed to generate micelles in aqueous solution. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Stimuli‐responsive diblock copolymer brushes via combination of “click chemistry” and living radical polymerization

pH‐ and temperature‐responsive poly(N‐isopropylacrylamide‐block?4‐vinylbenzoic acid) (poly(NIPAAm‐b‐VBA)) diblock copolymer brushes on silicon wafers have been successfully prepared by combining click reaction, single‐electron transfer‐living radical polymerization (SET‐LRP), and reversible addition‐fragmentation chain‐transfer (RAFT) polymerization. Azide‐terminated poly(NIPAAm) brushes were obtained by SET‐LRP followed by reaction with sodium azide. A click reaction was utilized to exchange the azide end group of a poly(NIPAAm) brushes to form a surface‐immobilized macro‐RAFT agent, which was successfully chain extended via RAFT polymerization to produce poly(NIPAAm‐b‐VBA) brushes. The addition of sacrificial initiator and/or chain‐transfer agent permitted the formation of well‐defined diblock copolymer brushes and free polymer chains in solution. The free polymer chains were isolated and used to estimate the molecular weights and polydispersity index of chains attached to the surface. Ellipsometry, contact angle measurements, grazing angle‐Fourier transform infrared spectroscopy, and X‐ray photoelectron spectroscopy were used to characterize the immobilization of initiator on the silicon wafer, poly(NIPAAm) brush formation via SET‐LRP, click reaction, and poly(NIPAAm‐b‐VBA) brush formation via RAFT polymerization. The poly(NIPAAm‐b‐VBA) brushes demonstrate stimuli‐responsive behavior with respect to pH and temperature. The swollen brush thickness of poly(NIPAAm‐b‐VBA) brush increases with increasing pH, and decreases with increasing temperature. These results can provide guidance for the design of smart materials based on copolymer brushes. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2677–2685     

An efficient way to tune grafting density of well‐defined copolymers via an unusual Br‐containing acrylate monomer

A series of well‐defined amphiphilic graft copolymers, containing hydrophilic poly(acrylic acid) backbone and hydrophobic poly(butyl acrylate) side chains, were synthesized by sequential reversible addition fragmentation chain transfer (RAFT) polymerization and atom transfer radical polymerization (ATRP) without any postpolymerization functionality modification followed by selective acidic hydrolysis of poly(tert‐butyl acrylate) backbone. tert‐Butyl 2‐((2‐bromopropanoyloxy)methyl)‐acrylate was first homopolymerized or copolymerized with tert‐butyl acrylate by RAFT in a controlled way to give ATRP‐initiation‐group‐containing homopolymers and copolymers with narrow molecular weight distributions (M_w/M_n < 1.20) and their reactivity ratios were determined by Fineman‐Ross and Kelen‐Tudos methods, respectively. The density of ATRP initiation group can be regulated by the feed ratio of the comonomers. Next, ATRP of butyl acrylate was directly initiated by these macroinitiators to synthesize well‐defined poly(tert‐butyl acrylate)‐g‐poly(butyl acrylate) graft copolymers with controlled grafting densities via the grafting‐from strategy. PtBA‐based backbone was selectively hydrolyzed in acidic environment without affecting PBA side chains to provide poly(acrylic acid)‐g‐poly(butyl acrylate) amphiphilic graft copolymers. Fluorescence probe technique was used to determine the critical micelle concentrations in aqueous media and micellar morphologies are found to be spheres visualized by TEM. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2622–2630, 2010     

Effect of rate retardation in RAFT grafting polymerization from silicon wafer surface

Polystyrene and poly(butyl acrylate) were grafted from silicon wafer surface by reversible addition‐fragmentation chain transfer (RAFT) polymerization. Three RAFT agents were immobilized onto silicon wafer through their leaving/initiating groups (R group). Grafting polymerization of butyl acrylate (BA) and styrene (St) was then carried out from the immobilized RAFT agents. The immobilization of the RAFT agents and the subsequent grafting polymerization of St and BA were evaluated by ellipsometry and X‐ray photoelectron spectroscopy. It was found that type of monomer, structure of RAFT agent, and local RAFT concentration on the surface have dramatic influences on the thickness of grafted polymer layer. The grafting polymerization with more severe rate retardation effect yielded thinner polymer films on the silicon wafer. Selection of a RAFT agent with little rate retardation was critical in the grafting polymerization to achieve thick films. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 970–978, 2008     

Synthesis of poly(tert‐butyl acrylate‐block‐vinyl acetate) copolymers by combining ATRP and RAFT polymerizations

The synthesis of poly(tert‐butyl acrylate‐block‐vinyl acetate) copolymers using a combination of two living radical polymerization techniques, atom transfer radical polymerization (ATRP) and reversible addition‐fragmentation chain transfer (RAFT) polymerization, is reported. The use of two methods is due to the disparity in reactivity of the two monomers, viz. vinyl acetate is difficult to polymerize via ATRP, and a suitable RAFT agent that can control the polymerization of vinyl acetate is typically unable to control the polymerization of tert‐butyl acrylate. Thus, ATRP was performed to make poly(tert‐butyl acrylate) containing a bromine end group. This end group was subsequently substituted with a xanthate moiety. Various spectroscopic methods were used to confirm the substitution. The poly(tert‐butyl acrylate) macro‐RAFT agent was then used to produce (tert‐butyl acrylate‐block‐vinyl acetate). © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7200–7206, 2008     

Functionalization and patterning of reactive polymer brushes based on surface reversible addition and fragmentation chain transfer polymerization

We present the synthesis of reactive polymer brushes prepared by surface reversible addition–fragmentation chain transfer polymerization of pentafluorophenyl acrylate. The reactive ester moieties can be used to functionalize the polymer brush film with virtually any functionality by simple post‐polymerization modification with amines. Dithiobenzoic acid benzyl‐(4‐ethyltrimethoxylsilyl) ester was used as the surface chain transfer agent (S‐CTA) and the anchoring group onto the silicon substrates. Reactive polymer brushes with adjustable molecular weight, high grafting density, and conformal coverage through the grafting‐from approach were obtained. Subsequently, the reactive polymer brushes were converted with amino‐spiropyrans resulting in reversible light‐responsive polymer brush films. The wetting behavior could be altered by irradiation with ultraviolet (UV) or visible light. Furthermore, a patterned surface of polymer brushes was obtained using a lithography technique. UV irradiation of the S‐CTA‐modified substrates leads to a selective degradation of S‐CTA in the exposed areas and gives patterned activated polymer brushes after a subsequent RAFT polymerization step. Conversion of the patterned polymer brushes with 5‐((2‐aminoethyl)amino)naphthalene‐1‐sulfonic acid resulted in patterned fluorescent polymer brush films. The utilization of reactive polymer brushes offers an easy approach in the fabrication of highly functional brushes, even for functionalities whose introduction is limited by other strategies. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis of random polyampholyte brushes by atom transfer radical polymerization

We report the synthesis of random polyampholyte brushes containing 2‐(dimethylamino)ethyl methacrylate (DMAEMA) and methacrylic acid (MAA). The preparation of polyampholyte brushes is performed by the “grafting from” strategy using surface‐initiated atom transfer radical polymerization (ATRP). The first step consists in the formation of the self‐assembled monolayer of the ATRP initiator. Secondly, the chains are grown from the surface by controlled/“living” radical polymerization. The random copolymer brushes and the corresponding homopolymers brushes containing 2‐(dimethylamino)ethyl methacrylate and tert‐butyl methacrylate (^tBuMA) are prepared. The last step is the deprotection of the ^tBuMA form to the MAA segment by in situ hydrolysis reaction. The annealed DMAEMA group can also be converted to the quenched form by in situ quaternization reaction. This results in the formation of “annealed” and “semiannealed” polyampholyte brushes. The “annealed” polyampholyte corresponds to the random copolymer that contains only annealed units, weak acid and weak base. The “semiannealed” polyampholyte consists of the mixture of annealed (weak acid) and quenched (quaternized segment) units. Polyampholyte brushes with various grafting densities are synthesized and carefully characterized using surface techniques such as ellipsometry and FTIR‐ATR. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4305–4319, 2008     

Macromolecular brushes synthesized by “grafting from” approach based on “click chemistry” and RAFT polymerization

Well‐defined macromolecular brushes with poly(N‐isopropyl acrylamide) (PNIPAM) side chains on random copolymer backbones were synthesized by “grafting from” approach based on click chemistry and reversible addition‐fragmentation chain transfer (RAFT) polymerization. To prepare macromolecular brushes, two linear random copolymers of 2‐(trimethylsilyloxy)ethyl methacrylate (HEMA‐TMS) and methyl methacrylate (MMA) (poly(MMA‐co‐HEMA‐TMS)) were synthesized by atom transfer radical polymerization and were subsequently derivated to azide‐containing polymers. Novel alkyne‐terminated RAFT chain transfer agent (CTA) was grafted to polymer backbones by copper‐catalyzed 1,3‐dipolar cycloaddition (azide‐alkyne click chemistry), and macro‐RAFT CTAs were obtained. PNIPAM side chains were prepared by RAFT polymerization. The macromolecular brushes have well‐defined structures, controlled molecular weights, and molecular weight distributions (M_w/M_n ≦ 1.23). The RAFT polymerization of NIPAM exhibited pseudo‐first‐order kinetics and a linear molecular weight dependence on monomer conversion, and no detectable termination was observed in the polymerization. The macromolecular brushes can self‐assemble into micelles in aqueous solution. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 443–453, 2010     

Preparation of nanocomposites by reversible addition‐fragmentation chain transfer polymerization from the surface of quantum dots in miniemulsion

Herein, we report the synthesis of quantum dots (QDs)/polymer nanocomposites by reversible addition‐fragmentation chain transfer (RAFT) polymerization in miniemulsions using a grafting from approach. First, the surfaces of CdS and CdSe QDs were functionalized using a chain transfer agent, a trisalkylphosphine oxide incorporating 4‐cyano‐4‐(thiobenzoylsulfanyl)pentanoic acid moieties. Using a free radical initiator (AIBN) to activate the RAFT process, a polystyrene (PS) block was grafted from the surface of the QDs. Quantum confinement effects were identified for the nanocomposite obtained, so attesting to the integrity of the QDs after the polymerization. Free PS chains were also present in the final nanocomposite, indicating that the RAFT polymerization from the surface of the QDs was accompanied by conventional free radical polymerization. After isolating the nanocomposite particles, a second poly(n‐butyl acrylate) block was tentatively grown from the initial PS block. The first results indicated a successful polymerization of the second polymer and show the potential of the current strategy to prepare block copolymers from the surface of the RAFT‐modified QDs. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5367–5377, 2009     

The preparation and characterization of carboxylic acid‐coated silica nanoparticles

The preparation of carboxylic acid‐coated silica nanoparticles was investigated. A monolayer of carboxylic acid residues with controllable graft density was anchored to the nanoparticle by a ring‐opening reaction with succinic anhydride. Poly(methacrylic acid) [poly(MAA)] grafted nanoparticles were prepared via a polymerization–deprotection strategy. Tert‐butyl methacrylate was polymerized from the surface of silica nanoparticles in a predictable manner and with excellent control over the molecular weight distribution. Subsequent removal of the tert‐butyl group resulted in poly (MAA) grafted nanoparticles. The polymer nanoparticles were also functionalized with dyes, which may be useful in tracking the particles in biological systems. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis and characterization of block copolymers containing poly(di(ethylene glycol) 2‐ethylhexyl ether acrylate) by reversible addition–fragmentation chain transfer polymerization

Reversible addition–fragmentation chain transfer (RAFT) polymerization has emerged as one of the important living radical polymerization techniques. Herein, we report the polymerization of di(ethylene glycol) 2‐ethylhexyl ether acrylate (DEHEA), a commercially‐available monomer consisting of an amphiphilic side chain, via RAFT by using bis(2‐propionic acid) trithiocarbonate as the chain transfer agent (CTA) and AIBN as the radical initiator, at 70 °C. The kinetics of DEHEA polymerization was also evaluated. Synthesis of well‐defined ABA triblock copolymers consisting of poly(tert‐butyl acrylate) (PtBA) or poly(octadecyl acrylate) (PODA) middle blocks were prepared from a PDEHEA macroCTA. By starting from a PtBA macroCTA, a BAB triblock copolymer with PDEHEA as the middle block was also readily prepared. These amphiphilic block copolymers with PDEHEA segments bearing unique amphiphilic side chains could potentially be used as the precursor components for construction of self‐assembled nanostructures. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5420–5430, 2007     

RAFT‐mediated synthesis of poly[(oligoethylene glycol) methyl ether acrylate] brushes for biological functions

The synthesis of poly[(oligoethylene glycol) methyl ether acrylate] [poly(OEGA)] brushes was achieved via reversible addition‐fragmentation chain transfer (RAFT) polymerization and used to selectively immobilize streptavidin proteins. Initially, gold surfaces were modified with a trithiocarbonate‐based RAFT chain transfer agent (CTA) by using an ester reaction involving a gold substrate modified with 11‐mercapto‐1‐undecanol and bis(2‐butyric acid)trithiocarbonate. poly(OEGA) brushes were then prepared via RAFT‐mediated polymerization from the surface‐immobilized CTA. The immobilization of CTA on the gold surface and the subsequent polymer formation were followed by ellipsometry, X‐ray photoelectron spectroscopy, grazing angle‐Fourier transform infrared spectroscopy, atomic force microscopy, and water contact‐angle measurements. RAFT‐mediated polymerization method gave CTA groups to grafted poly(OEGA) termini, which can be converted to various biofunctional groups. The terminal carboxylic acid groups of poly(OEGA) chains were functionalized with amine‐functionalized biotin units to provide selective attachment points for streptavidin proteins. Fluorescence microscopy measurements confirmed the successful immobilization of streptavidin molecules on the polymer brushes. It is demonstrated that this fabrication method may be successfully applied for specific protein recognition and immobilization. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Influence of nitroxide structure on polystyrene brushes “grafted‐from” silicon wafers

Alkoxyamine derivatives based on 2,2,6,6‐tetramethyl‐1‐piperidinyloxy (TEMPO), N‐tert‐butyl‐N‐(1‐diethylphosphono‐(2,2‐dimethylpropyl)) nitroxide (SG1) and N‐tert‐butyl‐N‐(2‐methyl‐1‐phenylpropyl) nitroxide (TIPNO) containing a C₁₁ hydrophobic spacer and a reactive triethoxysilyl polar head, were synthesized and anchored to silicon wafers by the Langmuir–Blodgett reactive deposition technique at surface pressures ranging from 15 to 32 mN/m. Polystyrene brushes (M_n ～ 8500–66,400 g/mol) were grown from the alkoxyamine functionalized silicon wafers by nitroxide mediated radical polymerization and characterized by ellipsometry and water contact angle measurements. The main parameters influencing the grafting density and the degree of stretching of the brushes are the nitroxide polarity and, therefore, the behavior of the corresponding alkoxyamines at the air/water interface of the Langmuir–Blodgett trough. Depending on the alkoxyamine chemical structure and the surface pressure during Langmuir–Blodgett deposition, polystyrene brushes with grafting densities of 0.3–1.0 chains/nm² and stretching values of 40–70% were obtained. Regarding alkoxyamines deposited at high surface pressures, size exclusion chromatography experiments performed on both cleaved polystyrene brushes and chains simultaneously grown in the bulk revealed that the polymerization degree of the bulk and surface chains are significantly different, suggesting that steric constrains affect the polymerization kinetics occurring at the silicon surface. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3367–3374, 2008     

Convenient synthesis of thermo‐responsive PtBA‐g‐PPEGMEMA well‐defined amphiphilic graft copolymer without polymeric functional group transformation

A series of well‐defined amphiphilic graft copolymers bearing hydrophobic poly(tert‐butyl acrylate) backbone and hydrophilic poly[poly(ethylene glycol) methyl ether methacrylate)] (PPEGMEMA) side chains were synthesized by sequential reversible addition fragmentation chain transfer (RAFT) polymerization and single‐electron‐transfer living radical polymerization (SET‐LRP) without any polymeric functional group transformation. A new Br‐containing acrylate monomer, tert‐butyl 2‐((2‐bromoisobutanoyloxy)methyl)acrylate (tBBIBMA), was first prepared, which can be homopolymerized by RAFT to give a well‐defined PtBBIBMA homopolymer with a narrow molecular weight distribution (M_w/M_n = 1.15). This homopolymer with pendant Br initiation group in every repeating unit initiated SET‐LRP of PEGMEMA at 45 °C using CuBr/dHbpy as catalytic system to afford well‐defined PtBBIBMA‐g‐PPEGMEMA graft copolymers via the grafting‐from strategy. The self‐assembly behavior of the obtained graft copolymers in aqueous media was investigated by fluorescence spectroscopy and TEM. These copolymers were found to be stimuli‐responsive to both temperature and ions. Finally, poly(acrylic acid)‐g‐PPEGMEMA double hydrophilic graft copolymers were obtained by selective acidic hydrolysis of hydrophobic PtBA backbone while PPEGMEMA side chains kept inert. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Arborescent micelles: Dendritic poly(γ‐benzyl l‐glutamate) cores grafted with hydrophilic chain segments

Amphiphilic copolymers were obtained by grafting arborescent poly(γ‐benzyl l ‐glutamate) (PBG) cores of generations G1–G3 with polyglycidol, poly(ethylene oxide) (PEO), or poly(l ‐glutamic acid) (PGA) chain segments. The PBG substrates were synthesized by two methods: (1) subjecting PBG samples with a dispersity ? = M_w/M_n < 1.1 to partial acidolysis of the benzyl ester groups, to produce randomly distributed carboxylic acid functionalities, and (2) using PBG chains containing a glutamic acid di‐tert‐butyl ester initiator fragment in the last grafting cycle of the PBG core synthesis, and selective acidolysis of the tert‐butyl ester groups to obtain substrates with carboxylic acid termini. Linear polymers with ? < 1.20 and a primary amine terminus were also synthesized to serve as hydrophilic shell materials: Polyglycidol and PEO by anionic polymerization, and PGA by N‐carboxyanhydride ring‐opening polymerization. These polymers, combined with the two different PGB substrate types, allowed the evaluation of the usefulness of random versus chain‐end grafting in producing arborescent copolymers useful as unimolecular micelles in organic and aqueous media. Size exclusion chromatography served to determine the grafting yield, molar mass, dispersity, and branching functionality of the copolymers. Dynamic light scattering measurements provided information on their aggregation behavior in aqueous environments. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1197–1209     

Hairy polymeric nanocapsules with ph‐responsive shell and thermoresponsive brushes: Tunable permeability for controlled release of water‐soluble drugs

The hairy poly(methacrylic acid‐co‐divinylbenzene)‐g‐poly(N‐isopropylacrylamide) (P(MAA‐co‐DVB)‐g‐PNIPAm) nanocapsules with pH‐responsive P(MAA‐co‐DVB) inner shell and temperature‐responsive PNIPAm brushes were prepared by combined distillation–precipitation copolymerization and surface thiol‐ene click grafting reaction using 3‐(trimethoxysilyl)propyl methacrylate‐modified silica (SiO₂‐MPS) nanospheres as a sacrificial core material. The well‐defined PNIPAm was synthesized by a reversible addition fragmentation chain transfer (RAFT) polymerization. The chain end was converted to a thiol by chemical reduction. The PNIPAm was integrated into the nanocapsules via thiol‐ene click reaction. The surface thiol‐ene click reaction conduced to tunable grafting density of PNIPAm brushes. The grafting densities decreased from 0.70 chains nm^?2 to 0.15 chains nm^?2 with increasing the molecular weight of grafted PNIPAm chains. Using water soluble doxorubicin hydrochloride (DOX·HCl) as a model molecular, the tunable shell permeability of the nanocapsule was investigated in detail. The permeability constant can be tuned by controlling the thickness of the P(MAA‐co‐DVB) inner shell, the grafting density of PNIPAm brushes, and the environmental pH and temperature. The tunable shell permeability of these nanocapsules results in the release of the loaded guest molecules with manipulable releasing kinetics. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2202–2216