Preparation and structural characterization of nanosized BiFe<Subscript>0.6</Subscript>Mn<Subscript>0.4</Subscript>O<Subscript>3</Subscript> as a novel material with high sensitivity towards LPG

Nanocrystalline BiFe_0.6Mn_0.4O₃ powders were synthesized by sol–gel citrate method and studied for gas sensing behavior to reducing gases such as LPG, CO, CH₄ and NH₃. The composition and the structure of the powders have been investigated by means of XRD and TEM. The result shows that the BiFe_0.6Mn_0.4O₃ powders have a rhombohedral distorted perovskite structure with an average crystallite size of 35–40 nm. The BiFe_0.6Mn_0.4O₃-based LPG sensor shows better sensitivity at an operating temperature of 250 °C. The dispersion of Pd on BiFe_0.6Mn_0.4O₃ in the ratio of 0.8 wt.% improved the sensitivity, selectivity and response time. In addition, it reduced the operating temperature from 250 to 210 °C for LPG sensor. The response time for LPG was less than 1 min.     

Synthesis and electrochemical properties of Ca-doped LiNi<Subscript>0.8</Subscript>Co<Subscript>0.2</Subscript>O<Subscript>2</Subscript> cathode material for lithium ion battery

LiNi_0.8Co_0.2O₂ and Ca-doped LiNi_0.8Co_0.2O₂ cathode materials have been synthesized via a rheological phase reaction method. X-ray diffraction studies show that the Ca-doped material, and also the discharged electrode, maintains a hexagonal structure even when cycled in the range of 3.0–4.35 V (vs Li⁺/Li) after 100 cycles. Electrochemical tests show that Ca doping significantly improves the reversible capacity and cyclability. The improvement is attributed to the formation of defects caused by the partial occupancy of Ca²⁺ ions in lithium lattice sites, which reduce the resistance and thus improve the electrochemical properties.     

Thermal oxide synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanorods and Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanowires

Fe₃O₄ nanorods and Fe₂O₃ nanowires have been synthesized through a simple thermal oxide reaction of Fe with C₂H₂O₄ solution at 200–600°C for 1 h in the air. The morphology and structure of Fe₃O₄ nanorods and Fe₂O₃ nanowires were detected with powder X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The influence of temperature on the morphology development was experimentally investigated. The results show that the polycrystals Fe₃O₄ nanorods with cubic structure and the average diameter of 0.5–0.8 μm grow after reaction at 200–500°C for 1 h in the air. When the temperature was 600°C, the samples completely became Fe₂O₃ nanowires with hexagonal structure. It was found that C₂H₂O₄ molecules had a significant effect on the formation of Fe₃O₄ nanorods. A possible mechanism was also proposed to account for the growth of these Fe₃O₄ nanorods. Supported by the Fund of Weinan Teacher’s University (Grant No. 08YKZ008), the National Natural Science Foundation of China (Grant No. 20573072) and the Doctoral Fund of Ministry of Education of China (Grant No. 20060718010)     

Phase relations in the CoO–V<Subscript>2</Subscript>O<Subscript>5</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> system in subsolidus area

Thermal properties of Co₂FeV₃O₁₁ have been reinvestigated. It has been proved that this compound does not exhibit polymorphism. It melts incongruently at the temperature of 770±5°C and the phase with lyonsite type structure is the solid product of this melting. Phase relations in the whole subsolidus area of the CoO–V₂O₅–Fe₂O₃ system have been determined. The solidus area projection onto the component concentration triangle plane of this system has been constructed using the DTA and XRD methods. 15 subsidiary subsystems can be distinguished in this system.     

Effect of heat treatment on particle growth and magnetic properties of electrospun Sr<Subscript>0.8</Subscript>La<Subscript>0.2</Subscript>Zn<Subscript>0.2</Subscript>Fe<Subscript>11.8</Subscript>O<Subscript>19</Subscript> nanofibers

Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉/poly(vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol–gel assisted electrospinning. Subsequently, the M-type ferrite Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers with diameters about 120 nm were obtained by calcination of these precursors at different heat treatment conditions. The precursor and resultant Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectrometer and vibrating sample magnetometer. With the calcination temperature increased up to 1,000 °C for 2 h or the holding time prolonged to 12 h at 900 °C, the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ particles gradually grow into a hexagonal elongated plate-like morphology due to the dimensional control along the nanofiber length. These elongated plate-like particles will be linked one by one to form the nanofiber with a necklace-like morphology. The magnetic properties of the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers are closely related to grain sizes, impurities and defects in the ferrite, which are influenced by the calcination temperature, holding time and heating rate. After calcined at 900 °C for 12 h with a heating rate of 3 °C/min, the optimized magnetic properties are achieved with the specific saturation magnetization 75.0 A m² kg⁻¹ and coercivity 426.3 kA m⁻¹ for the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers.     

Formation and properties of the Fe<Subscript>8</Subscript>V<Subscript>10</Subscript>W<Subscript>16–x</Subscript>Mo<Subscript>x</Subscript>O<Subscript>85</Subscript> type solid solution

Solid solution phases of a formula Fe₈V₁₀W_16–xMo_xO₈₅ where 0≤x≤4, have been obtained, possessing a structure of the compound Fe₈V₁₀W₁₆O₈₅. It was found on the base of XRD and DTA investigations that these solution phases melted incongruently, with increasing the value of x, in the temperature range from 1108 (x=0) to 1083 K (x=4) depositing Fe₂WO₆ and WO₃. The increase of the Mo⁶⁺ ions content in the crystal lattice of Fe₈V₁₀W₁₆O₈₅ causes the lattice parameters a=b contraction with cbeing almost constant. IR spectra of the Fe₈V₁₀W_16–xMo_xO₈₅ solid solution phases have been recorded.     

Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Preparation of Ca<Subscript>3</Subscript>Co<Subscript>4</Subscript>O<Subscript>9</Subscript> by polyacrylamide gel processing and its thermoelectric properties

Ca₃Co₄O₉ powder was prepared by a polyacrylamide gel route in this paper. The effect of the processing on microstructure and thermoelectric properties of Ca₃Co₄O₉ ceramics via spark plasma sintering were investigated. Electrical measurement shows that the Seebeck coefficient and conductivity are 170 μV/K and 128 S/cm, respectively, at 700 °C, yielding a power factor value of 3.70 × 10⁻⁴ W m⁻¹ K⁻² at 700 °C, which is larger than that of Ca₃Co₄O₉ ceramics via solid-state reaction processing. The polyacrylamide gel processing is a fast, cheap, reproducible and easily scaled up chemical route to improve the thermoelectric properties of Ca₃Co₄O₉ ceramics by preparing the homogeneous and pure Ca₃Co₄O₉ phase.     

Sol-gel synthesized semiconducting LaCo0.8Fe0.2O3-based powder for thick film NH3 gas sensor

Perovskite type LaCo_xFe_1−xO₃ nanoparticles was synthesized by a sol-gel citrate method. The structural, electrical and sensing characteristics of the LaCo_xFe_1−xO₃ system were investigated. The structural characteristics were performed by using X-ray diffraction (XRD) and transmission electron microscopy (TEM) to examine the phase and morphology of the resultant powder. The XRD pattern shows nanocrystalline solid solution of LaCo_xFe_1−xO₃ with perovskite phase. Electrical properties of synthesized nanoparticles are studied by DC conductivity measurement. The sensor shows high response towards ammonia gas in spite of other reducing gases when x = 0.8. The effect of 0.3 wt.% Pd-doped LaCo_0.8Fe_0.2O₃ on the response and a recovery time was also addressed.     

Synthesis and characterization of Co<Subscript>0.8</Subscript>Zn<Subscript>0.2</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles

Cobalt zinc ferrite, Co_0.8Zn_0.2Fe₂O₄, nanoparticles have been synthesized via autocatalytic decomposition of the precursor, cobalt zinc ferrous fumarato hydrazinate. The X-ray powder diffraction of the ‘as prepared’ oxide confirms the formation of single phase nanocrystalline cobalt zinc ferrite nanoparticles. The thermal decomposition of the precursor has been studied by isothermal, thermogravimetric and differential thermal analysis. The precursor has also been characterized by FTIR, and chemical analysis and its chemical composition has been determined as Co_0.8Zn_0.2Fe₂(C₄H₂O₄)₃·6N₂H_4. The Curie temperature of the ‘as-prepared oxide’ was determined by AC susceptibility measurements.     

Preparation and adsorption of magnetic Co<Subscript>0.5</Subscript>Ni<Subscript>0.5</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript>-chitosan nanoparticles

In this paper, magnetic chitosan microspheres were prepared by the emulsification cross-linking technique, with glutaraldehyde as the cross-linking agent, liquid paraffin as the dispersant, and the Span-80 as emulsifier. The time of cross-linking and the ratio of Co_0.5Ni_0.5Fe₂O₄/chitosan were investigated. The morphology was studied by different instruments. The adsorption performance was investigated and the effects of initial concentration of methyl orange, the time of cross-linking, and the amount of adsorbent were discussed. It is found that the product has uniform morphology when the ratio of magnetic Co_0.5Ni_0.5Fe₂O₄/chitosan is 1 : 2 and the time of cross-linking is 5 h; At room temperature, magnetic Co_0.5Ni_0.5Fe₂O₄–chitosan has a good adsorption toward methyl orange when the magnetic Co_0.5Ni_0.5Fe₂O₄/chitosan dosage is 20 mg.     

Synthesis and characterization of La<Subscript>0.8</Subscript>Sr<Subscript>0.2</Subscript>Co<Subscript>0.5</Subscript>Fe<Subscript>0.5</Subscript>O<Subscript>3±δ</Subscript> nanopowders by microwave assisted sol–gel route

Nano-crystalline La_0.8Sr_0.2Co_0.5Fe_0.5O_3±δ powder has been successfully synthesized by microwave assisted sol–gel (MWSG) method. The decomposition and crystallization behavior of the gel-precursor was studied by Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD) analysis. From the result of FT-IR and X-ray diffraction patterns, it is found that a perovskite La_0.8Sr_0.2Co_0.5Fe_0.5O_3±δ was formed by irradiating the precursor at 700 W for 3 min, but the well-crystalline perovskite La_0.8Sr_0.2Co_0.5Fe_0.5O_3±δ was obtained at 700 W for 35 min. Morphological and specific area analysis of the powder were done by transmission electron microscopy (TEM), scanning electron microscope (SEM) and Brunauer–Emmett–Teller (BET). The surface areas measured was 38.9 m²/g and the grain size was ∼23 nm. Electrochemical properties of pure LSCF cathode on YSZ electrolyte at intermediate temperatures were investigated by using AC impedance analyzer, which shows a low area specific resistance (0.077 Ω cm² at 1073 K and 0.672 Ω cm² at 953 K). Moreover, the synthesis period of 20 h usually observed for conventional heating mode is reduced to a few minutes. Thus, the MWSG method is proved to be a novel, extremely facile, time-saving and energy-efficient route to synthesize LSCF powders.     

Electrochemical properties of perovskite and A<Subscript>2</Subscript>MO<Subscript>4</Subscript>-type oxides used as cathodes in protonic ceramic half cells

Three selected materials have been prepared and shaped as cathode of half cells using the proton-conducting electrolyte BaCe_0.9Y_0.1O_3 − δ (BCY10): two perovskite compounds, Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 − δ (BSCF) and La_0.6Sr_0.4Fe_0.8Co_0.2O_3 − δ (LSFC), and the praseodymium nickelate Pr₂NiO_4 + δ (PRN) having the K₂NiF₄-type structure. The electrochemical properties of these compounds have been studied under zero current conditions (two-electrode cell) and under polarization (three-electrode cell). Their measured area-specific resistances were about 1–2 Ω cm² at 600 °C. Under direct current polarization, it appears that the three compounds show almost similar values of current densities at 625 °C; however, at lower temperatures, BSCF appears to be the most efficient cathode material.     

The microstructure and magnetic properties of Ni<Subscript>0.4</Subscript>Zn<Subscript>0.6</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> films prepared by spin-coating method

Nickel zinc ferrite (Ni_0.4Zn_0.6Fe₂O₄) films on Si (100) substrate were synthesized using a spin-coating method. The crystallinity of the Ni_0.4Zn_0.6Fe₂O₄ films with the thickness of about 386 nm became better as the annealing temperature increased. The films have smooth surface, relatively good packing density and uniform thickness. The volatilization of Zn is serious at 900 °C. With the increase of annealing temperature, the saturation magnetization M _s increases in the temperature ranging from 400 to 700 °C, however, decreases above 700 °C, and the coercivity H _c increases in the temperature range 400–800 °C, decreases above 800 °C. After annealed at 700 °C for 2 h in air with the heating rate 2 °C/min, the film shows a maximum saturation magnetization M _s of 349 emu/cc and low coercivity H _c of 66 Oe. The M _s is higher than others which prepared by this method, however, the H _c is lower. The M _s of Ni_0.4Zn_0.6Fe₂O₄ films annealed at 700 °C increases with increasing annealing time and the H _c changes slightly.     

LiNi<Subscript>0.8</Subscript>Co<Subscript>0.2−x</Subscript>Ti<Subscript>x</Subscript>O<Subscript>2</Subscript> nanoparticles: synthesis,structure, and evaluation of electrochemical properties for lithium ion cell application

Layered Ti-doped lithiated nickel cobaltate, LiNi_0.8Co_{0.2 − x}Ti_xO₂ (where x = 0.01, 0.03, and 0.05) nanopowders were prepared by wet-chemistry technique. The structural properties of synthesized materials were characterized by X-ray diffraction (XRD) and thermo-gravimetric/differential thermal analysis (TG/DTA). The morphological changes brought about by the changes in composition of LiNi_0.8Co_{0.2 − x}Ti_xO₂ particles were examined through surface examination techniques such as scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses. Electrochemical studies were carried out using 2016-type coin cell in the voltage range of 3.0–4.5 V (vs carbon) using 1 M LiClO₄ in ethylene carbonate and diethyl carbonate as the electrolyte. Among the various concentrations of Ti-doped lithiated nickel cobaltate materials, C/LiNi_0.8Co_0.17Ti_0.03O₂ cell gives stable charge–discharge features.     

Comparative study of the synthesis of CoFe<Subscript>2</Subscript>O<Subscript>4</Subscript> and NiFe<Subscript>2</Subscript>O<Subscript>4</Subscript> in silica through the polymerized complex route of the sol–gel method

In this work the synthesis of CoFe₂O₄-SiO₂ and NiFe₂O₄-SiO₂ nanocomposites was studied via the sol–gel method, using the polymerized complex route. The polymerized precursors obtained by the reaction of citric acid, ethylene glycol, tetraethylorthosilicate, ferric nitrate, and cobalt nitrate or nickel chloride were characterized by nuclear magnetic resonance (NMR) and infrared (IR) spectroscopy. NMR and IR spectra of the precursors, without and with metallic ions, show the formation of polymeric chains with ester and ether groups and complexes of metal-polymeric precursor. The nanocomposites were obtained by the thermal decomposition of the organic fraction and characterized by X-ray diffraction (XRD) and vibrating sample magnetometry (VSM). XRD patterns show the formation of CoFe₂O₄ and NiFe₂O₄ in an amorphous silica matrix above 400 °C in both cases. When the calcination temperature was 800 °C the particle size of the crystalline phases, calculated using the Scherrer equation, reached ∼35 nm for the two oxides. VSM plots show the ferrimagnetic behavior that is expected for this type of magnetic material; the magnetization at 12.5 KOe of the CoFe₂O₄-SiO₂ and NiFe₂O₄-SiO₂ compounds was 29.5 and 17.4 emu/g, respectively, for samples treated at 800 °C.     

Effect of metal substitution for cobalt on the oxygen adsorption properties of YBaCo<Subscript>4</Subscript>O<Subscript>7</Subscript>

YBaCo₄O₇ compound is capable to intake and release a large amount of oxygen in the temperature range of 200–400°C. In the present study, the effect of Zn, Ga and Fe substitution for Co on the oxygen adsorption/desorption properties of YBaCo₄O₇ were investigated by thermogravimetry (TG) method. Due to fixed oxidation state of Zn2+ ions, the substitution of Zn²⁺ for Co²⁺ suppresses the oxygen adsorption of YBaCo_4−xZn_xO₇. The substitution of Ga³⁺ for Co³⁺ also decreases the oxygen absorption capacity of YBaCo_4−xGa_xO₇. This can be explained by the strong affinity of Ga³⁺ ions towards the GaO₄ tetrahedron. Compared with Zn- and Ga-substituted samples, the drop of oxygen adsorption capacity is smallest for Fe-substituted samples because of the similar changeability of oxidation states of Co and Fe ions.     

Cellulose scaffolds modulated synthesis of Co<Subscript>3</Subscript>O<Subscript>4</Subscript> nanocrystals: preparation,characterization and properties

Magnetic Co₃O₄ nanoparticles were prepared by using microporous regenerated cellulose films as sacrificial scaffolds. The cellulose macromolecules and the porous structure of the films made them used as spatially confined reacting sites where Co(OH)₂ nanoparticles could be synthesized in situ. When the cellulose matrix was removed by sintering at 500 °C, Co₃O₄ nanoparticles were obtained. XRD and XPS indicated that the prepared nanoparticles were pure Co₃O₄ without any impurity. TEM and SEM images revealed that the particle size of the nanoparticles was smaller than 100 nm. The nanoparticles had weak ferromagnetic properties at 25 °C. Furthermore, the pronounced quantum confinement effects of the synthesized nanoparticles have been observed, the optical bandgap energies determined were about 1.92 ~ 2.12 and 2.74 ~ 2.76 eV for O²⁻ → Co³⁺ and O²⁻ → Co²⁺ charge-transfer processes, respectively. Furthermore, the resulted Co₃O₄ nanoparticles behaved stable electrochemical performance with promising applications in the electrode for lithium ion battery.     

Synthesis and characterization of submicron size particles of LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> by microemulsion route

Among the various positive electrode materials investigated for Li-ion batteries, spinel LiMn₂O₄ is one of the most important materials. Small particles of the active materials facilitate high-rate capability due to large surface to mass ratio and small diffusion path length. The present work involves the synthesis of submicron size particles of LiMn₂O₄ in a quaternary microemulsion medium. The precursor obtained from the reaction is heated at different temperatures in the range from 400 to 900 °C. The samples heated at 800 and 900 °C are found to possess pure spinel phase with particle size <200 nm, as evidenced from XRD, SEM, and TEM studies. The electrochemical characterization studies provide discharge capacity values of about 100 mAh g⁻¹ at C/5 rate, and there is a moderate decrease in capacity by increasing the rate of charge–discharge cycling. Studies also include charge–discharge cycling and ac impedance studies in temperature range from −10 to 40 °C. Impedance data are analyzed with the help of an equivalent circuit and a nonlinear least squares fitting program. From temperature dependence of charge-transfer resistance, a value of 0.62 eV is obtained for the activation energy of Mn³⁺/Mn⁴⁺ redox process, which accompanies the intercalation/deintercalation of the Li⁺ ion in LiMn₂O₄.     

Structure and Catalytic Properties of Ceria-based Nickel Catalysts for CO<Subscript>2</Subscript> Reforming of Methane

Carbon dioxide reforming (CDR) of methane to synthesis gas over supported nickel catalysts has been reviewed. The present review mainly focuses on the advantage of ceria based nickel catalysts for the CDR of methane. Nickel catalysts supported on ceria–zirconia showed the highest activity for CDR than nickel supported on other oxides such as zirconia, ceria and alumina. The addition of zirconia to ceria enhances the catalytic activity as well as the catalyst stability. The catalytic performance also depends on the crystal structure of Ni–Ce–ZrO₂. For example, nickel catalysts co-precipitated with Ce_0.8Zr_0.2O₂ having cubic phase gave synthesis gas with CH₄ conversion more than 97% at 800 °C and the activity was maintained for 100 h during the reaction. On the contrary, Ni–Ce–ZrO₂ having tetragonal phase (Ce_0.8Zr_0.2O₂) or mixed oxide phase (Ce_0.5Zr_0.5O₂) deactivated during the reaction due to carbon formation. The enhanced catalytic performance of co-precipitated catalyst is attributed to a combination effect of nano-crystalline nature of cubic Ce_0.8Zr_0.2O₂ support and the finely dispersed nano size NiO _x crystallites, resulting in the intimate contact between Ni and Ce_0.8Zr_0.2O₂ particles. The Ni/Ce–ZrO₂/θ–Al₂O₃ also exhibited high catalytic activity during CDR with a synthesis gas conversion more than 97% at 800 °C without significant deactivation for more than 40 h. The high stability of the catalyst is mainly ascribed to the beneficial pre-coating of Ce–ZrO₂ resulting in the existence of stable NiO _x species, a strong interaction between Ni and the support, and an abundance of mobile oxygen species in itself. TPR results further confirmed that NiO _x formation was more favorable than NiO or NiAl₂O₄ formation and further results suggested the existence of strong metal-support interaction (SMSI) between Ni and the support. Some of the important factors to optimize the CDR of methane such as reaction temperature, space velocity, feed CO₂/CH₄ ratio and H₂O and/or O₂ addition were also examined.