Gas‐forming poly(ethylene glycol)‐b‐poly(L‐lactic acid) micelles

In this study, a novel drug‐carrying micelle composed of methoxy poly(ethylene glycol) (mPEG)‐b‐poly(L‐lactic acid) (PLLA) with gas‐forming carbonate linkage was fabricated. Here, the gas‐forming carbonate linkage was formed by the chemical coupling of the terminal hydroxyl group of the PLLA block and benzyl chloroformate (BC). mPEG‐b‐PLLA‐BC was self‐organized in aqueous solution: the PEG block on the hydrophilic outer shell and the PLLA‐BC block in the hydrophoboic innor core. The cleavage of carbonate linkage by hydrolysis and formation of carbon dioxide nanobubbles in the micellar core enabled an accelerated release of the encapsulated anticancer drug (doxorubicin: DOX) from the mPEG‐b‐PLLA‐BC micelles. The amount of drug (DOX) released from the mPEG‐b‐PLLA‐BC micelle was higher than that from the conventional mPEG‐b‐PLLA micelle, which allowed for increased in vitro toxicity against KB tumor cells. Copyright © 2013 John Wiley & Sons, Ltd.     

Synthesis of star‐shaped poly(D,L‐lactic acid‐alt‐glycolic acid)‐b‐poly(L‐lactic acid) with the poly(D,L‐lactic acid‐alt‐glycolic acid) macroinitiator and stannous octoate catalyst

Two types of three‐arm and four‐arm, star‐shaped poly(D,L ‐lactic acid‐alt‐glycolic acid)‐b‐poly(L ‐lactic acid) (D,L ‐PLGA50‐b‐PLLA) were successfully synthesized via the sequential ring‐opening polymerization of D,L ‐3‐methylglycolide (MG) and L ‐lactide (L ‐LA) with a multifunctional initiator, such as trimethylolpropane and pentaerythritol, and stannous octoate (SnOct₂) as a catalyst. Star‐shaped, hydroxy‐terminated poly(D,L ‐lactic acid‐alt‐glycolic acid) (D,L ‐PLGA50) obtained from the polymerization of MG was used as a macroinitiator to initiate the block polymerization of L ‐LA with the SnOct₂ catalyst in bulk at 130 °C. For the polymerization of L ‐LA with the three‐arm, star‐shaped D,L ‐PLGA50 macroinitiator (number‐average molecular weight = 6800) and the SnOct₂ catalyst, the molecular weight of the resulting D,L ‐PLGA50‐b‐PLLA polymer linearly increased from 12,600 to 27,400 with the increasing molar ratio (1:1 to 3:1) of L ‐LA to MG, and the molecular weight distribution was rather narrow (weight‐average molecular weight/number‐average molecular weight = 1.09–1.15). The ¹H NMR spectrum of the D,L ‐PLGA50‐b‐PLLA block copolymer showed that the molecular weight and unit composition of the block copolymer were controlled by the molar ratio of L ‐LA to the macroinitiator. The ¹³C NMR spectrum of the block copolymer clearly showed its diblock structures, that is, D,L ‐PLGA50 as the first block and poly(L ‐lactic acid) as the second block. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 409–415, 2002     

Design of a poly(L‐histidine)‐carbohydrate conjugate for a new pH‐sensitive drug carrier

A poly(L ‐histidine) (PLH)‐carbohydrate conjugate has been synthesized as a new macromolecule extracting pH‐dependent properties of PLH with imidazole groups. Because of poor water solubility at physiological pH, the application of PLH with a pK_a around 6.0 has been limited in spite of the native possession of the pH‐dependent property change at endosomal pH. Although the PLH modified with aliphatic primary amino groups suddenly precipitated out of the aqueous medium above pH 6.0 as a result of the deprotonation of the imidazole groups, the water solubility of PLH was improved at physiological pH by the conjugation of the aminated PLH with hydrophilic maltopentaose. The resulting PLH‐maltopentaose conjugates and metalloporphyrins formed the complexes which varied their assembling structure below pH 6.0. The PLH‐maltopentaose would be the fundamental compound for designing various drug carriers with the pH sensitivity at endosomal pH. Copyright © 2004 John Wiley & Sons, Ltd.     

Carboxymethyl poly(L‐histidine) as a new pH‐sensitive polypeptide at endosomal/lysosomal pH

A carboxymethyl poly(L ‐histidine) has been synthesized as a new pH‐sensitive polypeptide at endosomal/lysosomal pH. Because of its poor water solubility at physiological pH, an application of poly(L ‐histidine) with a pK_a around 6.0 has been limited in spite of the native possession of the pH‐dependent property change at endosomal pH. Although the unmodified poly(L ‐histidine) suddenly precipitates out of the aqueous medium above pH 6.0 as the result of the deprotonation of the imidazole groups, the water solubility of the resulting carboxymethyl poly(L ‐histidine) has been improved at physiological pH. A solution turbidity measurement proved that no significant effect on a rapid aggregate formation or phase separation of serum proteins is induced by carboxymethyl poly(L ‐histidine). Hemolysis assay showed that the carboxymethyl poly(L ‐histidine) enhances membrane disruptive ability at endosomal/lysosomal pH. The cellular uptake of luciferase in the presence of the carboxymethyl poly(L ‐histidine) increases intracellular luciferase activity, which suggests that the carboxymethyl poly(L ‐histidine) makes the luciferase escape from lysosomal degradation. The carboxymethyl poly(L ‐histidine) would be the fundamental compound for designing various drug carriers with the pH sensitivity at endosomal/lysosomal pH. Copyright © 2007 John Wiley & Sons, Ltd.     

Drug release and biocompatibility of self‐assembled micelles prepared from poly (ɛ‐caprolactone/glycolide)‐poly (ethylene glycol) block copolymers

A series of poly(?‐caprolactone/glycolide)‐poly(ethylene glycol) (P(CL/GA)‐PEG) diblock copolymers were prepared by ring opening polymerization of a mixture of ?‐caprolactone and glycolide using mPEG as macro‐initiator and stannous octoate as catalyst. Self‐assembled micelles were prepared from the copolymers using nanoprecipitation method. The micelles were spherical in shape. The micelle size was larger for copolymers with longer PEG blocks. In contrast, the critical micelle concentration of copolymers increased with decreasing the overall hydrophobic block length. Drug loading and drug release studies were performed under in vitro conditions, using paclitaxel as a hydrophobic model drug. Higher drug loading was obtained for micelles with longer poly(ε‐caprolactone) blocks. Faster drug release was obtained for micelles of mPEG2000 initiated copolymers than those of mPEG5000 initiated ones. Higher GA content in the copolymers led to faster drug release. Moreover, drug release rate was enhanced in the presence of lipase from Pseudomonas sp., indicating that drug release is facilitated by copolymer degradation. The biocompatibility of copolymers was evaluated from hemolysis, dynamic clotting time, and plasma recalcification time tests, as well as MTT assay and agar diffusion test. Data showed that copolymer micelles present outstanding hemocompatibility and cytocompatibility, thus suggesting that P(CL/GA)‐PEG micelles are promising for prolonged release of hydrophobic drugs.     

Synthesis and characterization of multiblock copolymers based on L‐lactic acid,citric acid,and poly(ethylene glycol)

Because poly(L ‐lactic acid) (PLLA) is a biodegradable polyester with low immunogenicity and good biocompatibility, it is used as a biomaterial. However, hydrophobic PLLA does not have any reactive groups. Thus, its application is limited. To increase the hydrophilicity of PLLA and accelerate its degradation rate, functionalized pendant groups and blocks were introduced through copolymerization with citric acid and poly(ethylene glycol) (PEG), respectively. This article describes the synthesis and characterization of poly(L ‐lactic‐co‐citric acid) (PLCA)‐PLLA and PLCA‐PEG multiblock copolymers. The results indicated that the hydrolysis rate was enhanced, and the hydrophilicity was improved because of the incorporation of carboxyl groups in PLCA‐PLLA. The joining of the PEG block led to improved hydrophilicity of PLCA, and the degradation rate of PLCA‐PEG accelerated as compared with that of PLCA‐PLLA. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2073–2081, 2003     

Effect of PEO‐PPO‐PEO copolymer on the mechanical and thermal properties and morphological behavior of biodegradable poly (L‐lactic acid) (PLLA) and poly (butylene succinate‐co‐L‐lactate) (PBSL) blends

A blend of two biodegradable and semi‐crystalline polymers, poly (L‐lactic acid) (PLLA; 70 wt%) and poly (butylene succinate‐co‐L‐lactate) (PBSL; 30 wt%), was prepared in the presence of various polyethylene oxide‐polypropylene oxide‐polyethylene oxide (PEO‐PPO‐PEO) triblock copolymer contents (0.5, 1, 2 wt%). Mechanical, thermal properties, and Fourier transform infrared (FTIR) analysis of the blends were investigated. It was found that the addition of copolymer to PLLA/PBSL improved the fracture toughness of the blends as shown by mode I fracture energies. It was supported by morphological analysis where the brittle deformation behavior of PLLA changed to ductile deformation with the presence of elongated fibril structure in the blend with copolymer system. The glass transition temperature (T_g), melting temperature (T_m) of PLLA, and PBSL shift‐closed together indicated that some compatibility exists in the blends. In short, PEO‐PPO‐PEO could be used as compatibilizer to improve the toughness and compatibility of the PLLA/PBSL blends. Copyright © 2010 John Wiley & Sons, Ltd.     

Biodegradable electrospun mat: Novel block copolymer of poly (p‐dioxanone‐co‐L‐lactide)‐block‐poly(ethylene glycol)

Ultrafine fibers of a laboratory‐synthesized new biodegradable poly(p‐dioxanone‐co‐L ‐lactide)‐block‐poly(ethylene glycol) copolymer were electrospun from solution and collected as a nonwoven mat. The structure and morphology of the electrospun membrane were investigated by scanning electron microscopy, differential scanning calorimetry (DSC), wide‐angle X‐ray diffraction (WAXD), and a mercury porosimeter. Solutions of the copolymer, ranging in the lactide fraction from 60 to 80 mol % in copolymer composition, were readily electrospun at room temperature from solutions up to 20 wt % in methylene chloride. We demonstrate the ability to control the fiber diameter of the copolymer as a function of solution concentration with dimethylformamide as a cosolvent. DSC and WAXD results showed the relatively poor crystallinity of the electrospun copolymer fiber. Electrospun copolymer membrane was applied for the hydrolytic degradation in phosphate buffer solution (pH = 7.5) at 37 °C. Preliminary results of the hydrolytic degradation demonstrated the degradation rate of the electrospun membrane was slower than that of the corresponding copolymers of cast film. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1955–1964, 2003     

Synthesis of poly(D,L‐lactic acid‐alt‐glycolic acid) from D,L‐3‐methylglycolide

D ,L ‐3‐Methylglycolide (MG) was synthesized via two step reactions with a good yield (42%). It was successfully polymerized in bulk with stannous octoate as a catalyst at 110 °C. The effects of the polymerization time and catalyst concentration on the molecular weight and monomer conversion were studied. Poly(D ,L ‐lactic acid‐co‐glycolic acid) (D ,L ‐PLGA50; 50/50 mol/mol) copolymers were successfully synthesized from the homopolymerization of MG with high polymerization rates and high monomer conversions under moderate polymerization conditions. ¹H NMR spectroscopy indicated that the bulk ring‐opening polymerization of MG conformed to the coordination–insertion mechanism. ¹³C NMR spectra of D ,L ‐PLGA50 copolymers obtained under different experimental conditions revealed that the copolymers had alternating structures of lactyl and glycolyl. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 4179–4184, 2000     

Synthesis and pH‐responsive assembly of methoxy poly(ethylene glycol)‐b‐poly(ε‐caprolactone) with pendant carboxyl groups

pH‐responsive methoxy poly(ethylene glycol)‐b‐poly(ε‐caprolactone) bearing pendant carboxyl groups mPEG‐b‐P(2‐CCL‐co‐6‐CCL) was synthesized based on our newly monomer benzyloxycarbonylmethly functionalized ε‐caprolactone. Their structure was confirmed by ¹H NMR, ¹³C NMR, and Fourier transform infrared spectrum spectra. In addition, SEC results indicated that the copolymers had a relatively narrow polydispersity. WXRD and DSC demonstrated that the introduction of carboxymethyl groups had significant effect on the crystallinity of the copolymers. Furthermore, the solution behavior of mPEG‐b‐P(2‐CCL‐co‐6‐CCL) has been studied by various methods. The results indicated that mPEG‐b‐P(2‐CCL‐co‐6‐CCL) had a rich pH‐responsive behavior and the micelles could be formed by pH induction, and the mPEG‐b‐P(2‐CCL‐co‐6‐CCL) could existed as unimers, micelles or large aggregates in different pH range accordingly. The mechanism of which was supposed to depend on the counteraction between the hydrophobic interaction from PCL and the ionization of the carboxyl groups along the polymer chain. Moreover, the mPEG‐b‐P(2‐CCL‐co‐6‐CCL) copolymers displayed good biocompatibility according to the preliminary cytotoxicity study. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 188–199     

Preparation and characterization of biodegradable poly(lactic acid)‐ block‐poly(ε‐caprolactone) multiblock copolymer

Biodegradable copolymers of poly(lactic acid)‐block‐poly(ε‐caprolactone) (PLA‐b‐PCL) were successfully prepared by two steps. In the first step, lactic acid monomer is oligomerized to low molecular weight prepolymer and copolymerized with the (ε‐caprolactone) diol to prepolymer, and then the molecular weight is raised by joining prepolymer chains together using 1,6‐hexamethylene diisocyanate (HDI) as the chain extender. The polymer was carefully characterized by using ¹H‐NMR analysis, gel permeation chromatography (GPC), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and Fourier transform infrared spectroscopy (FTIR). The results of ¹H‐NMR and TGA indicate PLA‐b‐PCL prepolymer with number average molecular weights (M_n) of 4000–6000 were obtained. When PCL‐diols are 10 wt%, copolymer is better for chain extension reaction to obtain the polymer with high molecular weight. After chain extension, the weight average molecular weight can reach 250,000 g/mol, as determined by GPC, when the molar ratio of –NCO to –OH was 3:1. DSC curve showed that the degree of crystallization of PLA–PCL copolymer was low, even became amorphous after chain extended reaction. The product exhibits superior mechanical properties with elongation at break above 297% that is much higher than that of PLA chain extended products. Copyright © 2009 John Wiley & Sons, Ltd.     

Isothermal crystallization behavior of poly(L‐lactide) in poly(L‐lactide)‐block‐poly(ethylene glycol) diblock copolymers

The crystal unit‐cell structures and the isothermal crystallization kinetics of poly(L ‐lactide) in biodegradable poly(L ‐lactide)‐block‐methoxy poly(ethylene glycol) (PLLA‐b‐MePEG) diblock copolymers have been analyzed by wide‐angle X‐ray diffraction and differential scanning calorimetry. In particular, the effects due to the presence of MePEG that is chemically connected to PLLA as well as the PLLA crystallization temperature T_C are examined. Though we observe no variation of both the PLLA and MePEG crystal unit‐cell structures with the block ratio between PLLA and MePEG and T_C, the isothermal crystallization kinetics of PLLA is greatly influenced by the presence of MePEG that is connected to it. In particular, the equilibrium melting temperature of PLLA, T, significantly decreases in the diblock copolymers. When the T_C is high so that the crystallization is controlled by nucleation, because of the decreasing T and thereafter the nucleation density with decreasing PLLA molecular weight, the crystallinity of PLLA also decreases with a decrease in the PLLA molecular weight. While, for the lower crystallization temperature regime controlled by the growth mechanism, the crystallizability of PLLA in copolymers is greater than that of pure PLLA. This suggests that the activation energy for the PLLA segment diffusing to the crystallization site decreases in the diblocks. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2438–2448, 2006     

Self‐assembly of thermo‐ and pH‐responsive poly(acrylic acid)‐b‐poly(N‐isopropylacrylamide) micelles for drug delivery

Self‐assembled thermo‐ and pH‐responsive poly(acrylic acid)‐b‐poly(N‐isopropylacrylamide) (PAA‐b‐PNIPAM) micelles for entrapment and release of doxorubicin (DOX) was described. Block copolymer PAA‐b‐PNIPAM associated into core‐shell micelles in aqueous solution with collapsed PNIPAM block or protonated PAA block as the core on changing temperature or pH. Complexation of DOX with PAA‐b‐PNIPAM triggered by the electrostatic interaction and release of DOX from the complexes due to the changing of pH or temperature were studied. Complex micelles incorporated with DOX exhibited pH‐responsive and thermoresponsive drug release profile. The release of DOX from micelles was suppressed at pH 7.2 and accelerated at pH 4.0 due to the protonation of carboxyl groups. Furthermore, the cumulative release of DOX from complex micelles was enhanced around LCST ascribed to the structure deformation of the micelles. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5028–5035, 2008     

Vibrational dynamics and heat capacity in poly(L‐lactic acid)

Poly(L ‐lactic acid) (PLLA) (? CH(CH₃) ? COO? )_n is a biodegradable polymer, which exhibits many applications in the biomedical field and where thermoplastics are employed. A comprehensive study of the normal modes and their dispersion in PLLA using Wilson′s GF matrix method as modified by Higgs is being reported. Assignments of calculated normal modes have been made and characteristic features of dispersion curves are discussed. Heat capacity has been calculated via density‐of‐states using Debye relation in the temperature range 10–250 K, which is in fairly good agreement with the experimental data. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 175–182, 2010     

Novel temperature‐ and pH‐responsive graft copolymers composed of poly(L‐glutamic acid) and poly(N‐isopropylacrylamide)

A series of novel temperature‐ and pH‐responsive graft copolymers, poly(L ‐glutamic acid)‐g‐poly(N‐isopropylacrylamide), were synthesized by coupling amino‐semitelechelic poly(N‐isopropylacrylamide) with N‐hydroxysuccinimide‐activated poly(L ‐glutamic acid). The graft copolymers and their precursors were characterized, by ESI‐FTICR Mass Spectrum, intrinsic viscosity measurements and proton nuclear magnetic resonance (¹H NMR). The phase‐transition and aggregation behaviors of the graft copolymers in aqueous solutions were investigated by the turbidity measurements and dynamic laser scattering. The solution behavior of the copolymers showed dependence on both temperature and pH. The cloud point (CP) of the copolymer solution at pH 5.0–7.4 was slightly higher than that of the solution of the PNIPAM homopolymer because of the hydrophilic nature of the poly(glutamic acid) (PGA) backbone. The CP markedly decreased when the pH was lowered from 5 to 4.2, caused by the decrease in hydrophilicity of the PGA backbone. At a temperature above the lower critical solution temperature of the PNIPAM chain, the copolymers formed amphiphilic core‐shell aggregates at pH 4.5–7.4 and the particle size was reduced with decreasing pH. In contrast, larger hydrophobic aggregates were formed at pH 4.2. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4140–4150, 2008     

Preparation of poly (L‐lactic acid) with aligned structures by unidirectional freezing

Honeycomb monolith structured porous poly (L‐lactic acid, PLA) was simply fabricated by employing a unidirectional freeze‐casting technique. Dimethyl sulfoxide (DMSO) was used as a solvent for PLA, and the solution was unidirectionally frozen. The DMSO was nucleated in the solution and was grown in the freezing direction. The PLA was solidified and structured with the DMSO crystal as a template. Then DMSO was leached by water, ethanol, or the mixture of them, and subsequently the porous PLA was dried by oven. It was found that the freeze‐casting protocol can significantly influence the morphological features such as the tube diameter and wall thickness of tube can be tuned by varying of PLA concentration, freezing temperature, and the nature of leaching solvent. Because DMSO has a special solubility of a number of polymers, this method may be a general way for designing and preparing aligned porous materials. Copyright © 2015 John Wiley & Sons, Ltd.     

Preparation of hybrid triple‐stimuli responsive nanogels based on poly(L‐histidine)

A series of novel multi‐responsive disulfide cross‐linked polypeptide nanogels has been synthesized by a one‐step ring‐opening polymerization process. The pH‐responsive core of the prepared nanogels was based on poly(L‐histidine), the difunctional N‐carboxy anhydride of l ‐cystine (l ‐Cys‐NCA) was used as a reduction‐cleavable cross‐linking agent, while the outer hydrophilic corona was comprised of a poly(ethylene oxide) block. Extensive molecular characterization studies were conducted in order to confirm the formation of the desired polymeric nanostructures and also to prove their responsiveness to external stimuli within the physiological values of healthy and cancer tissues. Furthermore, the disruption of the disulfide‐bond linkages between the polymeric chains was achieved by the presence of the reductive tripeptide glutathione (GSH), leading to size variations that were monitored by dynamic light scattering (DLS) and size‐exclusion chromatography (SEC). “Stealth” properties of the formed nanostructures were examined by zeta potential measurements. The described nanogels are clearly promising candidates for drug delivery applications. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1278–1288     

Vibrational dynamics of poly(L‐histidine)

Normal mode analysis and their dispersion for poly(L ‐histidine) (PLH) are reported by using Urey Bradley force field and Fourier Transform IR PLH exists in the α helical form. There are 17 atoms in one residue, which gives rise to 51 dispersion curves. To simplify, it is convenient to discuss the normal frequencies under three separate heads namely amide modes, side chain modes, and mixed mode. The calculated frequencies are found to be in reasonably good agreement with the Fourier Transform IR spectra. There exists exchange of character, attraction, and repulsion for selective dispersion curves with change in the phase value. Contributions to the heat capacity were calculated separately for the side chain, backbone, and mixed modes. The major contribution comes from the side chain and mixed modes. The sum of these three contributions gives the total heat capacity, which is in agreement with the reported experimental value. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 128–137, 2010     

Synthesis,characterization, effect of architecture on crystallization,and spherulitic growth of poly(L‐lactide)‐b‐poly(ethylene oxide) copolymers with different branch arms

Well‐defined poly(L ‐lactide)‐b‐poly(ethylene oxide) (PLLA‐b‐PEO) copolymers with different branch arms were synthesized via the controlled ring‐opening polymerization of L ‐lactide followed by a coupling reaction with carboxyl‐terminated poly(ethylene oxide) (PEO); these copolymers included both star‐shaped copolymers having four arms (4sPLLA‐b‐PEO) and six arms (6sPLLA‐b‐PEO) and linear analogues having one arm (LPLLA‐b‐PEO) and two arms (2LPLLA‐b‐PEO). The maximal melting point, cold‐crystallization temperature, and degree of crystallinity (X_c) of the poly(L ‐lactide) (PLLA) block within PLLA‐b‐PEO decreased as the branch arm number increased, whereas X_c of the PEO block within the copolymers inversely increased. This was mainly attributed to the relatively decreasing arm length ratio of PLLA to PEO, which resulted in various PLLA crystallization effects restricting the PEO block. These results indicated that both the PLLA and PEO blocks within the block copolymers mutually influenced each other, and the crystallization of both the PLLA and PEO blocks within the PLLA‐b‐PEO copolymers could be adjusted through both the branch arm number and the arm length of each block. Moreover, the spherulitic growth rate (G) decreased as the branch arm number increased: G_{6sPLLA‐b‐PEO} < G_{4sPLLA‐b‐PEO} < G_{2LPLLA‐b‐PEO} < G_{LPLLA‐b‐PEO}. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2034–2044, 2006     

Structure and mechanical properties of poly(L‐lactic acid) crystals and fibers

The elastic constants of poly(L ‐lactic acid) (PLLA) crystals are reported on the basis of a commercial software package and the published crystal structure of the α form. A chain modulus of 36 GPa and a shear modulus of 3 GPa have been obtained for cylindrically symmetric aggregates of perfectly oriented crystals. The helical conformation of the PLLA molecule reduces the stiffness in the chain axis direction because bond rotation plays a significant role in the deformation. X‐ray crystal strain measurements suggest that shear of the α crystal parallel to the helix axis is the easiest mode of deformation, in agreement with the expectations obtained from the low shear modulus of 3 GPa obtained from the theoretical calculations. A combination of small‐ and wide‐angle X‐ray scattering, differential scanning calorimetry, dynamic mechanical thermal analysis, and shrinkage measurements has been used to characterize the structure that develops and the crystal transformation that occurs during fiber processing. The structure that develops during processing very much depends on the crystal transformation, and a structural model is proposed for fibers at different degrees of plastic deformation. The transformation of the α crystal into the β form and vice versa is governed primarily by shear along the helix axis because the chains must shear past each other during the crystal transformation, disrupting the lamellar packing. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 892–902, 2007