Viscoelastic phase diagram of fluorinated and grafted polymer films and proton‐exchange membranes for fuel cell applications

The influence of temperature and moisture activity on the viscoelastic behavior of fluorinated membranes for fuel cell applications was investigated. Uncrosslinked and crosslinked ethylene tetrafluoroethylene (ETFE)‐based proton‐conducting membranes were prepared by radiation grafting and subsequent sulfonation and their behavior was compared with ETFE base film and commercial Nafion^® NR212 membrane. Uniaxial tensile tests and stress relaxation tests at controlled temperature and relative humidity (RH) were carried out at 30 and 50 °C for 10% < RH < 90%. Grafted films were stiffer and exhibited stronger strain hardening when compared with ETFE. Similarly, both uncrosslinked and crosslinked membranes were stiffer and stronger than Nafion^®. Yield stress was found to decrease and moisture sensitivity to increase on sulfonation. The viscoelastic relaxation of the grafted films was found to obey a power‐law behavior with exponent equal to ?0.04 ± 0.01, a factor of almost 2 lower than ETFE, weakly influenced by moisture and temperature. Moreover, the grafted films presented a higher hygrothermal stability when compared with their membranes counterparts. In the case of membranes, a power‐law behavior at RH < 60% was also observed. However, a markedly different behavior was evident at RH > 60%, with an almost single relaxation time exponential. An exponential decrease of relaxation time with RH from 60 s to 10 s was obtained at RH ≥ 70% and 30 °C. The general behavior of grafted films observed at 30 °C was also obtained at 50 °C. However, an anomalous result was noticed for the membranes, with a higher modulus at 50 °C when compared with 30 °C. This behavior was explained by solvation of the sulfonic acid groups by water absorption creating hydrogen bonding within the clusters. A viscoelastic phase diagram was elaborated to map critical conditions (temperature and RH) for transitions in time‐dependent behavior, from power‐law scaling to exponential scaling. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 1139–1148     

A novel approach to prepare proton exchange membranes from fluoropolymer powder by pre-irradiation induced graft polymerization

A novel approach was developed to overcome the non-uniform distribution of grafted polystyrene (PS) chains across proton exchange membranes (PEMs) manufactured using radiation induced graft polymerization of commercialized fluoropolymer films. This process involves the three key steps of grafting of styrene into fluoropolymer powder, processing the grafted powder into membranes, and then obtaining the PEM by sulfonation of these membranes. The structure of the membranes and the PEMs were analyzed by means of infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS) and scanning electron microscope with energy-dispersive X-ray analysis (SEM-EDX) to demonstrate the uniform distribution of poly(styrene-sulfonic acid) (denoted as PSSA) graft-chains across the PEM. The properties of the resulting PEMs, such as their ion exchange capacity (IEC), water uptake (WU), proton conductivity, dimensional stability, oxidative stability and thermal stability, were also investigated.     

Solid polymer electrolytes I,preparation, characterization,and ionic conductivity of gelled polymer electrolytes based on novel crosslinked siloxane/poly(ethylene glycol) polymers

A series of crosslinked siloxane/poly(ethylene glycol) (Si–PEG) copolymers were synthesized from the reactive methoxy‐functional silicone resin (Si resin) and PEGs with different molecular weights via two kinds of crosslinking reactions during an in situ curing stage. One of the crosslinking reactions is the self‐condensation between two methoxy groups in the Si resin, and another one is an alkoxy‐exchange reaction between the methoxy group in the Si resin and the OH group in PEG. The synthesized crosslinked copolymers were characterized by Fourier transform infrared spectroscopy, DSC, and ¹³C NMR. The crosslinked copolymers were stable in a moisture‐free environment, but the Si? O? C linkages were hydrolyzed in humid conditions. The gel‐like solid polymer electrolytes (SPEs) were prepared by impregnating these crosslinked Si–PEG copolymers in a propylene carbonate (LiClO₄/PC) solution. The highest conductivity reached 2.4 × 10^?4 S cm^?1 at 25 °C and increased to 8.7 × 10^?4 S cm^?1 at 85 °C. The conductivities of these gel‐type SPEs were affected by the content of LiClO₄/PC, the molecular weights of PEGs, and the weight fraction of the Si resin. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2051–2059, 2004     

Synthesis of poly(arylene ether sulfone)‐block‐sulfonated polybutadiene: the selective post‐sulfonation of block copolymers as proton exchange membranes

A series of poly(arylene ether sulfone)‐block‐sulfonated polybutadiene (PAES‐b‐sPB) with different ion exchange capacities (IECs) were synthesized and evaluated as proton exchange membranes (PEMs) for possible applications in fuel cells. These sulfonated block copolymers were synthesized via condensation reaction between modified PAES and PB prepolymers, followed by selective post‐sulfonation of PB blocks using acetyl sulfate as the sulfonating reagent. The sulfonic groups were only attached onto PB blocks due to the high reactivity of double bonds to acetyl sulfate. The success of synthesis and selective post‐sulfonation were all confirmed by the Fourier transform infrared (FT‐IR) and nuclear magnetic resonance (NMR) spectra. PAES‐b‐sPB had good film‐forming ability and thermal stability. Mechanical properties of membranes varied with the sulfonation. The presence of sulfonic groups increased the tensile strength and Young's modulus but decreased the elongation at break. Transmission electron microscopy (TEM) images showed large ionic aggregates in membranes. Phase separation as well as the interconnected sulfonate groups which only localized on flexible PB blocks led to these ionic domains. The proton conductivity increased with the increasing IEC and temperature. With relatively low IEC, most membranes still exhibited sufficient proton conductivity. The above results indicated this strategy could be a prospective choice to prepare novel PEMs. Copyright © 2010 John Wiley & Sons, Ltd.     

Novel sulfonated block copolymer containing pendant alkylsulfonic acids: Syntheses,unique morphologies,and applications in proton exchange membrane

In this article, we report the syntheses and characterizations of a series of novel block polyelectrolytes, poly(styrene‐block‐sulfonated hydroxystyrene) (PS‐b‐sPHS), containing pendant sulfonic acid groups attached to the backbone via propyl spacers in the sPHS domain. PS‐b‐sPHS with various compositions were synthesized via anionic polymerization and the following analogous chemistry to achieve accurate control of molecular weight (M_w), narrow polydispersity and high degree of sulfonation. Proton exchange membranes (PEMs) were prepared from PS‐b‐sPHS with sulfonic acids in either potassium salts or tetra‐alkylammonium salts via solvent casting and following treatments. Some unique morphologies, such as hallow channels and lamellar arrangement of strings of beads, were observed as a consequence of equilibrium between microphase separation and columbic interactions between polyelectrolytes. The transportation properties were found to closely relate to the morphologies of the PEMs. The combination of microphase separation of block polyelectrolytes and freedom of movement of pendent alkylsulfonic acids was demonstrated to effectively enhance the proton transport and suppress the methanol crossover for the PEMs, leading to the selectivity higher than Nafion 117 by five times at most. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Preparation and characterization of a poly(vinylbenzyl sulfonic acid)‐grafted FEP membrane

In this study, a novel polymer electrolyte membrane, poly(vinylbenzyl sulfonic acid)‐grafted poly(tetrafluoroethylene‐co‐hexafluoropropylene) (FEP‐g‐PVBSA), has been successfully prepared by simultaneous irradiation grafting of vinylbenzyl chloride (VBC) monomer onto a FEP film and taking subsequent chemical modification steps to modify the benzyl chloride moiety to the benzyl sulfonic acid moiety. The chemical reactions for the sulfonation were carried out via the formation of thiouronium salt with thiourea, base‐catalyzed hydrolysis for the formation of thiol, and oxidation with hydrogen peroxide. Each chemical conversion process was confirmed by FTIR, elemental analysis, and SEM‐EDX. A chemical stability study performed with Fenton's reagent (3% H₂O₂ solution containing 4 ppm of Fe²⁺) at 70 °C revealed that FEP‐g‐PVBSA has a higher chemical stability than the poly(styrene sulfonic acid)‐grafted membranes (FEP‐g‐PSSA). © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 563–569, 2010     

TEMPO addition into pre-irradiated fluoropolymers and living-radical graft polymerization of styrene for preparation of polymer electrolyte membranes

We prepared proton exchange membranes (PEMs) by 2,2,6,6-tetramethylpiperidinyl-1-oxy (TEMPO)-mediated living-radical graft polymerization (LRGP) of styrene into fluoropolymer films and subsequent sulfonation. Poly(vinylidene fluoride) (PVDF) and poly(ethylene-co-tetrafluoroethylene) (ETFE) films were first irradiated and then treated with TEMPO solutions in various solvents. TEMPO addition was confirmed by the test of styrene grafting into TEMPO-treated films at 60 °C, at which the LRGP never proceeds. This test enabled us to differentiate the LRGP from the conventional graft polymerization. In order to gain a deep insight about TEMPO-addition reaction, the TEMPO-penetration behavior into the base polymer films was examined by a permeation experiment and computer simulation. Xylene and dioxane were appropriate solvents for the complete introduction of TEMPO into PVDF and ETFE films, respectively. Then, the LRGP of styrene was performed based on the fully TEMPO-capped films at 125 °C with various solvents. By using an alcoholic solvent, the degree of grafting was enhanced and it reached a maximum of 38%. This grafted film was sulfonated to prepare a PEM showing an ion exchange capacity of 2.2 meq/g and proton conductivity of 1.6×10^?1 S/cm.     

Thermal stability of proton exchange fuel-cell membranes based on crosslinked-polytetrafluoroethylene for membrane-electrode assembly preparation

We investigated thermal properties of proton exchange membranes (PEMs) prepared by the radiation-induced grafting of styrene into crosslinked-polytetrafluoroethylene films and the subsequent sulfonation for fuel-cell applications. A conventional thermogravimetric analysis was found to be unreliable because the resulting curve varied greatly with the heating rate. Thus, in order to obtain accurate information, we performed an ex-situ heat-treatment analysis, which involved heating of the PEMs at fixed temperatures of 200-350 °C and measurement of their remaining weight, ion exchange capacity (IEC) and proton conductivity (σ) after washing in pure water. The IEC and σ did not change at any temperature up to 200 °C, indicating high thermal stability. At 250 °C, however, the PEM properties deteriorated probably via radical cleavage of the C-S bond between a sulfonic acid group and an aromatic ring, and condensation of two sulfonic acid groups. Finally, the PEM was hot-pressed with two electrodes at 200 °C to produce a good membrane-electrode assembly for a fuel cell.     

Synthesis and properties of Q‐silicon crosslinked siloxane networks: H3PO4‐catalyzed sol–gel dehydration/crosslinking of α,ω‐bis(hydroxy)oligodimethylsiloxanes with tetrakis(hydroxydimethylsiloxy)silane

Six silicate‐crosslinked oligodimethylsiloxane thin films were prepared by the phosphoric acid (1 mol %) catalyzed condensation of α,ω‐bis(hydroxy)oligodimethylsiloxane (P) and tetrakis(hydroxydimethylsiloxy)silane (Q). Other acid catalysts were evaluated. P and Q were prepared by the Pd‐catalyzed oxidation of the corresponding Si? H compounds with water. The starting materials were characterized by IR and ¹H, ¹³C, and ²⁹Si NMR. A thermal cure was achieved with H₃PO₄ in 24 h and with poly(phosphoric acid) in 3 h at 110–120 °C. Dynamic mechanical analysis was used to determine the glass‐transition temperatures and to evaluate the mechanical properties of the films. Their thermal stabilities (≥300 °C) in air and N₂ were determined by thermogravimetric analysis. Small amounts of non‐crosslinked P were recovered from the films by Soxhlet extractions with CH₂Cl₂ and analyzed by IR, gel permeation chromatography, and ²⁹Si NMR. The crosslink densities were evaluated by the CH₂Cl₂ absorption capacities of the films. The surface properties of the films were determined by static and dynamic contact‐angle measurements. Electrochemical impedance spectroscopy was carried out to evaluate the corrosion‐protective properties of the coatings on mild steel as a function of the exposure time to 0.5 N NaCl. The biofoul‐release properties of the films were evaluated with sporelings from mature Ulva linza plants and barnacles. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2237–2247, 2006     

PTFE辐射接枝对苯乙烯基三甲氧基硅烷制备质子交换膜

采用聚四氟乙烯(PTFE)膜室温下共辐射接枝单体p-苯乙烯基三甲氧基硅烷(StSi),之后经磺化和水解缩聚制备了含有亲水性的—Si—O—Si—交联结构和Si—OH基团的质子交换膜.研究了溶剂、吸收剂量、吸收剂量率以及单体浓度等参数对接枝率的影响,并对质子交换膜的离子交换容量(IEC)、吸水性、尺寸稳定性及电导率等性能进行了分析.结果表明,实验条件下接枝率随吸收剂量和单体浓度增加而增加,采用3mol·L-1的单体浓度减少均聚物;吸收剂量率为10～43Gy·min-1时,接枝率随剂量率变化不明显;以甲苯做溶剂可获得较高接枝率并保持膜的机械强度;IEC值、吸水性和电导率随接枝率增加而增大,是—SO3H、—Si—O—Si—交联结构和Si—OH基团共同作用的结果.接枝率72.5%时膜的IEC值为1.53mmol·g-1,高于Nafion117(0.89mmol·g-1),90℃吸水率为63%,尺寸稳定(优于Nafion117),质子电导率达1.5×10-2S·cm-1,获得了低于Nafion117的甲醇透过性,接枝率50.1%时甲醇透过系数0.82×10-6cm2·s-1.     

UV radiation induced graft copolymerization of allyl acetate onto poly(ethylene terephthalate) (PET) films for fuel cell membranes

Ultraviolet（UV）-induced graft copolymerization of allyl acetate（AA） monomer onto polyethylene terephthalate) （PET） films and the subsequent sulfonation on the monomer units in the grafting chain using chlorosulfonic acid（ClSO₃H） were carried out to prepare proton exchange membranes（PEMs） for fuel cells.A maximum grafting value of 12.8%was found for 35 vol%allyl acetate after 3 h radiation time.Optimum concentration of C1SO₃H was selected for the sulfonation reaction to be 0.05 mol/L based on the degree of sulfonation and the tensile strength studies of the membrane.The degree of sulfonation increased as the sulfonation reaction temperature and sulfonation time were increasing.The radiation grafting and the sulfonation have been confirmed by titrimetric and gravimetric analyses as well as FTIR spectroscopy.The maximum ion exchange capacity（IEC） of 0.04125 mmol g^-1 was found at 12.1%degree of sulfonation and the maximum proton conductivity was found to be 0.035 S cm^-1 at 30℃and a relative humidity of 60%.The various physical and chemical properties of the PEMs such as water uptake,mechanical strength,thermal durability and oxidative stability were also studied.To investigate the suitability of the prepared membrane for fuel cell applications,its properties were compared with those of Nafion 117.     

Phase separation and crystallinity in proton conducting membranes of styrene grafted and sulfonated poly(vinylidene fluoride)

A series of proton exchange membranes have been prepared by the preirradiation grafting method. Styrene was grafted onto a matrix of poly(vinylidene fluoride) (PVDF) after electron beam irradiation. Part of the samples was crosslinked with divinylbenzene (DVB) or bis(vinylphenyl)ethane (BVPE). Subsequent sulfonation gave membranes grafted with poly(styrene sulfonic acid) and marked PVDF‐g‐PSSA. It was found that the intrinsic crystallinity of the matrix decreased in both the grafting and the sulfonation reaction in all the membranes. The graft penetration and the ion conductivity are influenced strongly by the crosslinker. The ion conductivity is considerably lower in crosslinked membranes than in noncrosslinked ones. Generally, the mechanical strength decreases with crosslinking. The membranes show a regular phase separated structure in which the sulfonated grafts are incorporated in the amorphous parts of the matrix polymer. The phase separated domains are small, of the order of magnitude of 100–250 nm. These were resolved on transmission electron micrographs and on atomic force images but could not be resolved with microprobe Raman spectroscopy. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1741–1753, 1999     

Thermal behavior of poly(vinylbenzyl chloride)‐grafted poly(ethylene‐co‐tetrafluoroethylene) films

The effect of the degree of grafting (DOG) on the thermal behavior of poly(vinylbenzyl chloride)‐grafted poly(ethylene‐co‐tetrafluoroethylene) (ETFE‐g‐PVBC) films was investigated by differential scanning calorimetry (DSC), X‐ray diffraction (XRD), dynamic mechanical analysis ( DMA), FT‐IR, and thermogravimetric analysis (TGA) instruments. Several ETFE‐g‐PVBC films with various degrees of grafting, including 10, 24, 41, 60, and 94%, were prepared using a radiation grafting technique. The DSC and XRD results of the ETFE‐g‐PVBC films revealed that the crystallinity of the films decreased as the DOG increased. The DMA and FT‐IR results of the films indicated that a crosslinking reaction occurred at temperatures above 250 °C. In the thermal properties of the grafted films, an increase in the DOG led to an increase in the decomposition temperature. The activation energy (E_a) of the thermal decomposition was calculated using Kissinger's equation from TGA results. The E_a value of the PVBC graft chain was found to increase as the DOG increased, indicating that the crosslinking reaction of ETFE‐g‐PVBC films increased with an increase in the DOG during the thermal degradation process. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 517–525     

Polymer electrolyte membranes for the direct methanol fuel cell: A review

The direct methanol fuel cell (DMFC) has the potential to replace lithium‐ion rechargeable batteries in portable electronic devices, but currently experiences significant power density and efficiency losses due to high methanol crossover through polymer electrolyte membranes (PEMs). Numerous publications document the synthesis and characterization of new PEMs for the DMFC. This article reviews this research, transport phenomena in PEMs, and experimental techniques used to evaluate new PEMs for the DMFC. Although many PEMs do not show significant improvements over Nafion®, the benchmark PEM in DMFCs, experimental results show that several new PEMs exhibit lower methanol crossover at similar proton conductivities and/or higher DMFC power densities. These results and recommendations for future research are discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Parts B: Polym Phys 44: 2201–2225, 2006     

Dynamic mechanical and dielectric properties of ORMOCER® incorporating functionalized poly(styrene) latexes

Organically modified aluminosilicate hybrid materials incorporating polystyrene and poly(styrene‐co‐hydroxypropyl acrylate) latexes, (3‐glycidyloxypropyl) trimethoxysilane, and aluminum sec‐butoxide [Al(O^sBu)₃] were synthesized by a sol–gel process. The bulk materials obtained were macroscopically homogeneous dispersions with good mechanical properties. Dynamic mechanical and dielectric analyses of these new hybrid materials as a function of the Al(O^sBu)₃ concentration and copolymer composition revealed a series of transitions that represented relaxation processes of the incorporated polymer (glass transition), ?Al? O? Si?, the ?Si? O? Si? part of the network, and segmental motion of unreacted ?Si? (CH₂)₃OCH₂CHCH₂O chains. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 860–867, 2001     

Phosphoric acid‐doped imidazolium ionomers with enhanced stability for anhydrous proton‐exchange membrane applications

Phosphoric acid‐doped crosslinked proton‐conducting membranes with high anhydrous proton conductivity, and good chemical stability in phosphoric acid were synthesized and characterized. The synthetic procedure of the acid‐doped composite membranes mainly involves the in situ crosslinking of polymerizable monomer oils (styrene and acrylonitrile) and vinylimidazole, and followed by the sulfonation of pendant imidazole groups with butanesultone, and further doped with phosphoric acid. The resultant phosphoric acid‐doped composite electrolyte membranes are flexible and show high thermal stability and high‐proton conductivity up to the order of 10^?2 S cm^?1 at 160 °C under anhydrous conditions. The phosphoric acid uptake, swelling degree, and proton conductivity of the composite membranes increase with the vinylimidazole content. The resultant composite membranes also show good oxidative stability in Fenton's reagent (at 70 °C), and quite good chemical stability in phosphoric acid (at 160 °C). The properties of the prepared electrolyte membranes indicate their promising prospects in anhydrous proton‐exchange membrane applications. © 2013 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2013 , 51, 1311–1317     

Surface modification of ethylene‐co‐tetrafluoroethylene films by remote plasmas

The surface modifications of ethylene‐co‐tetrafluoroethylene (ETFE) surfaces by six plasmas (direct H₂, Ar, and O₂ plasmas and remote H₂, Ar, and O₂ plasmas) were investigated with two questions in mind: (1) what plasma could effectively modify ETFE surfaces and (2) which of the CF₂? CF₂ and CH₂? CH₂ components in ETFE was selectively modified? The plasma exposure led to a weight loss from the ETFE surfaces and changes in the chemical composition on ETFE surfaces. The weight‐loss rate showed a strong dependence on what plasma was used for the modification. The remote H₂ plasma led to the lowest rate of weight loss in the six plasma exposures, and the direct O₂ plasma led to the highest rate of weight loss. During exposure to the plasmas, defluorination occurred, and two new C_1s components [? CH₂? CHF? CH₂? and ? CH₂? CH(O? R)? CF_x? , and ? CH₂? CHF? CF₂? , ? CH₂? C(O)? CF_x? , and ? CF_x? C(O)? O? ] were formed on the modified ETFE surfaces. Defluorination was strongly influenced by what plasma was used for the modification. The remote H₂ and Ar plasmas showed high defluorinations of 55 and 51%, respectively. The remote O₂ plasma showed a low defluorination of only 25%. Conclusively, the remote H₂ and Ar plasma exposure effectively modified ETFE surfaces. With the exposure of these surfaces to the remote H₂ plasma, the CF₂? CF₂ component was predominantly modified, rather than the CH₂? CH₂ component. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2871–2882, 2002     

Synthesis of novel polybenzimidazoles with pendant amino groups and the formation of their crosslinked membranes for medium temperature fuel cell applications

A series of new polybenzimidazoles (PBIs) with pendant amino groups have been synthesized via condensation polymerization of 5‐aminoisophthalic acid (APTA), isophthalic acid (iPTA), and 3,3′diaminobenzidine (DAB) in polyphosphoric acid at 190 °C for 20 h. The molar ratios between APTA and iPTA were controlled at 1:0, 2:1, 1:1, and 1:2, respectively, and the copolymerization reactions were carried out via both random and sequenced manners. The resulting polymers showed good solubility in some organic solvents such as dimethylsulfoxide (DMSO) and N,N‐dimethylacetamide (DMAc). The pendant amino groups of the PBIs were utilized to react with two kinds of crosslinkers, 1,3‐dibromopropane and ethylene glycol diglycidyl ether, to yield various crosslinked membranes. The crosslinked membranes generally showed good mechanical properties even at high‐phosphoric acid (PA) doping levels, whereas the uncrosslinked membranes highly swelled or even dissolved in PA. Fenton's test revealed that the crosslinked PBI membranes had excellent radical oxidative stability. The proton conductivities of the PA‐doped crosslinked membranes increased with an increase in temperature and high‐proton conductivity up to 0.14 S/cm at 0% relative humidity at 170 °C was achieved. The membranes with high PA‐doping levels, good mechanical properties, and high‐proton conductivities have been successfully developed. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2009     

In situ polymerization of silicic acid in polyethylene–octene elastomer: Properties and characterization of the hybrid nanocomposites

Silicic acid produced from sodium metasilicate hydrate and metallocene polyethylene–octene elastomer (POE) were chosen as the ceramic precursor and the continuous phase, respectively, for preparation of new hybrids by an in situ sol–gel process. To obtain a better hybrid, the acrylic acid‐grafted polyethylene–octene elastomer (POE‐g‐AA) prepared in our laboratory and used as the continuous phase was also investigated. Characterizations of POE/SiO₂ and POE‐g‐AA/SiO₂ composites were performed by Fourier transform infrared spectroscopy, ²⁹Si solid‐state nuclear magnetic resonance (NMR) spectrometry, X‐ray diffractometry, differential scanning calorimetry, thermogravimetry analysis, and an Instron mechanical tester. The POE‐g‐AA/SiO₂ hybrid could give the positive effect on the properties of POE/SiO₂ hybrid because the carboxylic acid groups of acrylic acid should act as coordination sites for the silica phase to form chemical bonds. The result of ²⁹Si solid‐state NMR spectra showed that Si atom coordination around SiO₄ units is predominantly Q₃ and Q₄. Also, the POE‐g‐AA/SiO₂ hybrid with 15 wt % SiO₂ gave the maximum values of tensile strength and glass‐transition temperature because excess particles might cause the separation between the organic and inorganic phases when the silica content was beyond this point. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 351–359, 2003     

Block copolystyrene derivatives having flexible alkylsulfonated side chains and hydrophobic alkoxy chains as a proton exchange membrane for fuel cell application

A series of block copolystyrene derivatives, poly{[4‐(4‐sulfobutyloxy)styrene]_x‐block‐[4‐(n‐butoxystyrene)]_y} (PSBOS_x‐b‐PnBOS_y), containing a flexible alkylsufonated side chain and hydrophobic alkoxy chain with various ion exchange capacities (IECs) have been synthesized based on living anionic polymerization. The resulting crosslinked membranes were prepared using 4,4′‐methylene‐bis[2,6‐bis(hydroxyethyl)phenol] as the crosslinker in the presence of methanesulfonic acid. The crosslinked PSBOS_2.2‐b‐PnBOS₁ membrane with IEC of 2.89 mequiv g^?1 displays a high proton conductivity (0.01 S cm^?1) at 30% relative humidity and 80 °C, which is comparable to that of Nafion. The well‐developed phase separation and the continuous hydrophilic domains in the crosslinked PSBOS_2.2‐b‐PnBOS₁ membranes have been observed in a transmission electron microscope image. Moreover, the dynamic mechanical analysis measurement and Fenton's reagent testing show that the crosslinked PSBOS_x‐b‐PnBOS_y membranes have good mechanical properties and oxidative stability. These results indicate that the introduction of flexible alkylsulfonated side chains to the polystyrene main chains positively affect both the proton conductivity and oxidative stability. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013