Atypical grain growth for (2 1 1) CdTe films deposited on surface reconstructed (1 0 0) SrTiO3 substrates

The (1 0 0) SrTiO₃ substrate has emerged as the oxide substrate of choice for the deposition of a wide variety of materials. The substrate's unavoidable miscut leads to a step-terrace morphology when heated to high temperatures. This morphological transition is accompanied by an atomic scale repositioning of the uppermost terrace atoms, the nature of which is strongly dependent on the substrate temperature and ambient atmosphere used. Here, we report the deposition of CdTe films on the as-received and reconstructed surfaces of (1 0 0) SrTiO₃. The as-received substrate gives rise to a [1 1 1] CdTe film with four equally distributed in-plane grain orientations. The surface reconstruction, on the other hand, gives rise to an unprecedented reorientation of the film's grain structure. For this case, a [2 1 1] CdTe film emerges having twelve unevenly distributed in-plane orientations. We attribute the film's grain structure to an atomic scale surface reconstruction, with the anisotropic distribution of grain-types arising from a preferential formation due to the step edges.     

Nanostructure of photocatalytic TiO2 films sputtered at temperatures below 200 °C

The article reports on correlations between the process parameters of reactive pulsed dc magnetron sputtering, physical properties and the photocatalytic activity (PCA) of TiO₂ films sputtered at substrate surface temperature T_surf ≤ 180 °C. Films were deposited using a dual magnetron system equipped with Ti (Ø50 mm) targets in Ar + O₂ atmosphere in oxide mode of sputtering. The TiO₂ films with highly photoactive anatase phase were prepared without a post-deposition thermal annealing. The decomposition rate of the acid orange 7 (AO7) solution during the photoactivation of the TiO₂ film with UV light was used for characterization of the film PCA. It was found that (i) the partial pressure of oxygen pO₂ and the total sputtering gas pressure p_T are the key deposition parameters influencing the TiO₂ film phase composition that directly affects its PCA, (ii) the structure of sputtered TiO₂ films varies along the growth direction from the film/substrate interface to the film surface, (iii) ∼500 nm thick anatase TiO₂ films with high PCA were prepared and (iv) the structure of sputtered TiO₂ films is not affected by the substrate surface temperature T_surf when T_surf < 180 °C. The interruption of the sputtering process and deposition in long (tens of minutes) pulses alternating with cooling pauses has no effect on the structure and the PCA of TiO₂ films and results in a decrease of maximum value of T_surf necessary for the creation of nanocrystalline nc-TiO₂ film. It was demonstrated that crystalline TiO₂ films with high PCA can be sputtered at T_surf ≤ 130 °C. Based on obtained results a phase zone model of TiO₂ films was developed.     

Influence of substrate temperature in BiFeO3-CoFe2O4 nanocomposites deposited on SrTiO3 (0 0 1)

BiFeO₃-CoFe₂O₄ epitaxial nanocomposites have been deposited on SrTiO₃ (0 0 1) substrates by pulsed laser deposition. We present here a study of the influence of the deposition temperature (T_S), in the 550-800 °C range, on the film composition, morphology and microstructure. Electron-probe microanalysis shows strong reduction of the Bi content in the films when increasing T_S. Films prepared at T_S=750 °C and above are virtually Bi-free. X-ray diffraction (XRD) data show that, due to the volatility of Bi, there is a progressive reduction in the amount of BiFeO₃. The deposition temperature and the concomitant presence of Fe_xO_y spurious phases in the nanocomposites grown at high temperature promote radical changes in film morphology and magnetization. It thus follows that a temperature range suitable for controlled modification of nanocomposites morphology would be extremely narrow.     

Scanning tunnelling microscopy studies of growth morphology in highly epitaxial c-axis oriented Pt thin film on (0 0 1) SrTiO3

A noble metal Pt thin film was successfully grown on (0 0 1) SrTiO₃ substrate by using a DC-sputtering technique. The surface morphology and growth features of the as-grown Pt films were investigated by scanning tunnelling microscopy. Growth conditions, such as pre-sputtering, deposition ambience, and oxygen ratio are found to greatly affect the orientation, the crystallinity, and the epitaxial behavior of Pt films on (0 0 1) SrTiO₃. Single-crystalline Pt films have been achieved by introducing a few percentage oxygen into the sputtering ambient. The in-plane-relationship of the c-axis oriented Pt thin films on (0 0 1) SrTiO₃ was determined to be (0 0 1)_Pt∥(0 0 1)_SrTiO3 and [0 0 1]_Pt∥[0 0 1]_SrTiO3. Oxygen in the sputtering ambient was found to be a key factor to achieve the epitaxial Pt films.     

Growth of highly-oriented CaCu3Ti4O12 thin films on SrTiO3 (1 0 0) substrates by a chemical solution route

Highly-oriented CaCu₃Ti₄O₁₂ (CCTO) thin films deposited directly on SrTiO₃ (1 0 0) substrates have been developed successfully using a chemical solution coating method. X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM) were employed to characterize the structure and the morphology. It was observed that the CCTO thin films had the 1 μm × 1 μm domain-like microstructure that consists of compact grains of about 0.1 μm in size. The cross sectional SEM image shows that the CCTO grains grow regularly close to the clear interface between the CCTO film and the SrTiO₃ substrate. The result was discussed in terms of lattice mismatch between CCTO and SrTiO₃.     

Role of crystal orientation on the magnetic properties of CoFe2O4 thin films grown on Si (1 0 0) and Al2O3 (0 0 0 1) substrates using pulsed laser deposition

We report the influence of crystal orientation on the magnetic properties of CoFe₂O₄ (CFO) thin films grown on single crystal Si (1 0 0) and c-cut sapphire (Al₂O₃) (0 0 0 1) substrates using pulsed laser deposition technique. The thickness was varied from 200 to 50 nm for CFO films grown on Si substrates, while it was fixed at 200 nm for CFO films grown on Al₂O₃ substrates. We observed that the 200 and 100 nm thick CFO-Si films grew in both (1 1 1) and (3 1 1) directions and displayed out-of-plane anisotropy, whereas the 50 nm thick CFO-Si film showed only an (1 1 1) orientation and an in-plane anisotropy. The 200 nm thick CFO film grown on an Al₂O₃ substrate was also found to show a complete (1 1 1) orientation and a strong in-plane anisotropy. These observations pointed to a definite relation between the crystalline orientation and the observed magnetic anisotropy in the CFO thin films.     

Half Ca-doped LaMnO3 films on (0 0 1) SLAO and STO substrate studied by magnetization and transport measurements

In this study, La_0.5Ca_0.5MnO₃ (LCMO) films, at the boundary between ferromagnetic metallic and charge-ordered antiferromagnetic insulator according to the bulk phase diagram, were epitaxially grown on (0 0 1) SrTiO₃ (STO) and SrLaAlO₄ (SLAO) substrates by pulsed laser deposition technique. The films were analyzed by X-ray diffraction, magnetization and magnetoresistance measurements. A considerably higher magnetization was measured for 290-nm-thick film on SLAO substrate compared to the film on STO substrate, although both films have the same chemical composition, thickness and epitaxial orientation. The film on SLAO shows a metal-insulator (MI) transition, which occurs at higher temperatures with increasing applied magnetic field, whereas only insulating behavior was observed for the 290-nm-thick film on STO except for the highest applied magnetic field (7 T). In addition, transport measurements were performed and analyzed by Mott's variable range hopping (VRH) model to correlate the resistivity of the films with the Jahn-Teller strain (ε_J−T) in the structure.     

Structural characterisation of ultra-thin VOx films on TiO2(1 1 0)

The normal incidence X-ray standing wave (NIXSW) technique has been applied to investigate the structure of ultra-thin VO_x films grown on TiO₂(1 1 0) and pre-characterised by core level photoemission. For a film composed of a sub-monolayer coverage of V deposited in ultra-high vacuum the local structure of two coexistent species, labelled ‘oxidic’ and ‘metallic’, has been investigated independently through the use of chemical-shift-NIXSW. The ‘oxidic’ state is shown to be consistent with a mixture of epitaxial or substitutional sites and chemisorption into sites coordinated to three surface O atoms. The metallic V atoms also involve a mixture of chemisorption and second-layer sites above the substrate surface consistent with the formation of small V clusters. VO_x films up to ∼6 atomic layers were also grown by post-oxidation (sequential V deposition and annealing in oxygen) and by reactive evaporation in a partial pressure of oxygen. While films of around one monolayer or less are consistent with epitaxial VO₂ growth, the film quality deteriorates rapidly with increasing thickness and is worse for reactive evaporation. A possible interpretation of the NIXSW data is increasing contributions of V₂O₃ crystallites. The inferior quality of the reactively evaporated films may be due to an insufficient supply of oxygen.     

Growth and structure of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 thin films prepared by pulsed laser deposition technique

Bi_0.5(Na_0.7K_0.2Li_0.1)_0.5TiO₃ (BNKLT) thin films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition (PLD) technique. The films prepared were examined by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The effects of the processing parameters, such as oxygen pressure, substrate temperature and laser power, on the crystal structure, surface morphology, roughness and deposition rates of the thin films were investigated. It was found that the substrate temperature of 600 °C and oxygen pressure of 30 Pa are the optimized technical parameters for the growth of textured film, and all the thin films prepared have granular structure, homogeneous grain size and smooth surfaces.     

Microstructural and compositional studies of liquid-phase deposition derived PbTiO3 thin films on LaNiO3 substrates

PbTiO₃ thin films were successfully deposited on the LaNiO₃ (LNO) substrates by the liquid-phase deposition (LPD) method and post-annealing at various temperatures. The structure, morphology and composition of the films were investigated by some analytical techniques. The as-deposited films are amorphous and composed of densely packed spherical particles. The films with the grain size of 180 nm start to decompose and crystallize into perovskite structure at 450 °C and show a perovskite single phase with tetragonal structure after annealing at 650 °C. X-ray photoelectron spectroscopy (XPS) analysis reveals that the as-deposited film contains fluorine and carbon as major impurities. Fluorine could be completely eliminated by annealing at 650 °C in air.     

Ultrathin ZrO2 films on Si-rich SiC(0 0 0 1)-(3 × 3): Growth and thermal stability

The growth and thermal stability of ultrathin ZrO₂ films on the Si-rich SiC(0 0 0 1)-(3 × 3) surface have been explored using photoelectron spectroscopy (PES) and X-ray absorption spectroscopy (XAS). The films were grown in situ by chemical vapor deposition using the zirconium tetra tert-butoxide (ZTB) precursor. The O 1s XAS results show that growth at 400 °C yields tetragonal ZrO₂. An interface is formed between the ZrO₂ film and the SiC substrate. The interface contains Si in several chemically different states. This gives evidence for an interface that is much more complex than that formed upon oxidation with O₂. Si in a 4+ oxidation state is detected in the near surface region. This shows that intermixing of SiO₂ and ZrO₂ occurs, possibly under the formation of silicate. The alignment of the ZrO₂ and SiC band edges is discussed based on core level and valence PES spectra. Subsequent annealing of a deposited film was performed in order to study the thermal stability of the system. Annealing to 800 °C does not lead to decomposition of the tetragonal ZrO₂ (t-ZrO₂) but changes are observed within the interface region. After annealing to 1000 °C a laterally heterogeneous layer has formed. The decomposition of the film leads to regions with t-ZrO₂ remnants, metallic Zr silicide and Si aggregates.     

Structure and electronic properties calculation of ultrathin α-Al2O3 films on (0 0 0 1) α-Cr2O3 templates

Ab initio total energy Hartree-Fock calculations of ultrathin films of α-Al₂O₃ on (0 0 0 1) α-Cr₂O₃ templates are presented. The surface relaxation, the in-plane reconstruction and the surface and strain energies of the slabs are studied as a function of alumina film thickness. The surface Al layer is found to relax inwards considerably, with the magnitude of the inwards relaxation depending on the thickness of the ultrathin alumina film in a non-linear manner. The calculations also reveal that ultrathin films of alumina lower the surface energy of (0 0 0 1) α-chromia substrates. This indicates that the (0 0 0 1) α-chromia surface provides favourable conditions for the templated growth of α-alumina. However, increasing the alumina film thickness is found to give rise to a significant increase in strain energy. Finally, the electronic properties at the surface of the (0 0 0 1) α-Al₂O₃/α-Cr₂O₃ slabs are investigated. Here it is found that the alumina coating gives rise to an increase in the covalency of the bonds at the surface of the slabs. In contrast, the influence of an alumina layer on the electrostatic potential at the surface of the chromia slab is relatively minor, which should also be beneficial for the templated growth of α-alumina on (0 0 0 1) α-chromia substrates.     

X-ray multiple diffraction in the characterization of TiNO and TiO2 thin films grown on Si(0 0 1)

TiO₂ and TiN_xO_y thin films grown by low pressure metal-organic chemical vapor deposition (LP-MOCVD) on top of Si(0 0 1) substrate were characterized by X-ray multiple diffraction. X-ray reflectivity analysis of TiO₂[1 1 0] and TiNO[1 0 0] polycrystalline layers allowed to determine the growth rate (−80 Å/min) of TiO₂ and (−40 Å/min) of TiNO films. X-ray multiple diffraction through the Renninger scans, i.e., ?-scans for (0 0 2)Si substrate primary reflection is used as a non-conventional method to obtain the substrate lattice parameter distortion due to the thin film conventional deposition, from where the information on film strain type is obtained.     

Characterization of bicrystalline epitaxial LaNiO3 films fabricated on MgO (1 0 0) substrates by pulsed laser deposition

A series of metallic LaNiO₃ (LNO) thin films were deposited on MgO (1 0 0) substrates by pulsed laser deposition (PLD) under the oxygen pressure of 20 Pa at different substrate temperatures from 450 to 750 °C. X-ray diffraction (XRD) was used to characterize the crystal structure of LNO films. θ-2θ scans of XRD indicate that LNO film deposited at a substrate temperature of 700 °C has a high orientation of (l l 0). At other substrate temperatures, the LNO films have mixed phases of (l l 0) and (l 0 0). Furthermore, pole figure measurements show that LNO thin films, with the bicrystalline structure, were epitaxially deposited on MgO (1 0 0) substrates in the mode of LNO (1 1 0)//MgO (1 0 0) at 700 °C. Reflection high-energy electric diffraction (RHEED) and atomic force microscopy (AFM) were also performed to investigate the microstructure of LNO films with the high (l l 0) orientation. RHEED patterns clearly confirm this epitaxial relationship. An atomically smooth surface of LNO films at 700 °C was obtained. In addition, bicrystalline epitaxial LNO films, fabricated at 700 °C, present a excellent conductivity with a lower electrical resistivity of 300 μ Ω cm. Thus, the obtained results indicate that bicystalline epitaxial LNO films could serve as a promising candidate of electrode materials for the fabrication of ferroelectric or dielectric films.     

Growth and characterization of Y2O3 thin films

Y₂O₃ thin films were grown on silicon (1 0 0) substrates by pulsed-laser deposition at different substrate temperatures and O₂ pressures. The structure and composition of films are studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Y₂O₃ thin films deposited in vacuum strongly oriented their [1 1 1] axis of the cubic structure and the film quality depended on the substrate temperature. The magnitude of O₂ pressure obviously influences the film structure and quality. Due to the silicon diffusion and interface reaction during the deposition, yttrium silicate and SiO₂ were formed. The strong relationship between composition and growth condition was discussed.     

Characteristics of Ni films deposited on SiO2/Si(1 0 0) and MgO(0 0 1) by direct current magnetron sputtering system with the oblique target

280 nm-thick Ni films were deposited on SiO₂/Si(1 0 0) and MgO(0 0 1) substrates at 300 K, 513 K and 663 K by a direct current magnetron sputtering system with the oblique target. The films deposited at 300 K mainly have a [1 1 0] crystalline orientation in the film growth direction. The [1 1 0]-orientation weakens and the [1 1 1]- and [1 0 0]-orientations enhance with increasing deposition temperature. The lattice constant of the Ni films is smaller than that of the Ni bulk, except for the film grown on MgO(0 0 1) at 663 K. Furthermore, as the deposition temperature increases, the lattice constant of the films grown on the SiO₂/Si(1 0 0) decreases whereas that of the films grown on the MgO(0 0 1) increases. The films deposited at 300 K and 513 K grow with columnar grains perpendicular to the substrate. For the films deposited at 663 K, however, the columnar grain structure is destroyed, i.e., an about 50 nm-thick layer consisting of granular grains is formed at the interface between the film and the substrate and then large grains grow on the layer. The Ni films deposited at 300 K consist of thin columnar grains and have many voids at the grain boundaries. The grains become thick and the voids decrease with increasing deposition temperature. The resistivity of the film decreases and the saturation magnetization increases with increasing deposition temperature.     

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Epitaxial growth and structural characterization of Pb(Fe1/2Nb1/2)O3 thin films

We have grown lead iron niobate thin films with composition Pb(Fe_1/2Nb_1/2)O₃ (PFN) on (0 0 1) SrTiO₃ substrates by pulsed laser deposition. The influence of the deposition conditions on the phase purity was studied. Due to similar thermodynamic stability spaces, a pyrochlore phase often coexists with the PFN perovskite phase. By optimizing the kinetic parameters, we succeeded in identifying a deposition window which resulted in epitaxial perovskite-phase PFN thin films with no identifiable trace of impurity phases appearing in the X-ray diffractograms. PFN films having thicknesses between 20 and 200 nm were smooth and epitaxially oriented with the substrate and as demonstrated by RHEED streaks which were aligned with the substrate axes. X-ray diffraction showed that the films were completely c-axis oriented and of excellent crystalline quality with low mosaicity (X-ray rocking curve FWHM?0.09°). The surface roughness of thin films was also investigated by atomic force microscopy. The root-mean-square roughness varies between 0.9 nm for 50-nm-thick films to 16 nm for 100-nm-thick films. We also observe a correlation between grain size, surface roughness and film thickness.     

DFT study of Pt adsorption on low index SrTiO3 surfaces: SrTiO3(1 0 0), SrTiO3(1 1 1) and SrTiO3(1 1 0)

Density Functional Theory has been used to determine the energetically preferred structures of submonolayer, monolayer, and multilayer Pt films on both ideal terminations of SrTiO₃(1 0 0), SrTiO₃(1 1 1), and SrTiO₃(1 1 0). The strength of the resulting metal/metal oxide interfaces was characterized by the adsorption energy of the film and the film’s work of separation. The two polar surfaces, SrTiO₃(1 1 1) and SrTiO₃(1 1 0), form significantly stronger interfaces than the non-polar SrTiO₃(1 0 0) surface. Approximate criteria were applied to predict the growth mode of Pt on each surface.     

The interplay between molecular orientation, film morphology and luminescence properties of tetracene thin films on epitaxial AlOx/Ni3Al(1 1 1)

We report a systematic study of the interplay between molecular orientation, film morphology and luminescence properties of tetracene thin films on epitaxial alumina films on Ni₃Al(1 1 1), employing high resolution electron energy loss spectroscopy (HREELS), X-ray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED), and photoluminescence spectroscopy (PL). If deposited at low temperatures, tetracene forms laterally disordered and compact films in which at least the first monolayer is oriented parallel to the substrate. For thicknesses in the range of 10 Å or below, these as-deposited films show no luminescence, while thicker films exhibit weak luminescence from higher layers. On annealing to 210 K, tetracene films dewet the AlO_x/Ni₃Al(1 1 1) surface and transform into an island morphology. At the same time, molecules tend to re-orient into a more upright configuration. In this island configuration, even thin films show luminescence. We can thus conclude that in spite of the insulating nature of the surface, the interaction of flat-lying tetracene molecules with AlO_x/Ni₃Al(1 1 1) is strong enough to provide at least one efficient non-radiative decay channel.