Effect of post-annealing temperature on the microstructure and magnetic properties of Ce:YIG thin films deposited on Si substrates

Amorphous Ce₁Y₂Fe₅O₁₂ (Ce:YIG) thin films deposited on single crystal Si(1 0 0) and thermally oxidized Si(1 0 0) substrates by pulsed laser deposition were annealed in the temperature range of 700-1000 °C in air. The annealing temperature dependence of microstructure and magnetic properties of Ce:YIG films was studied using X-ray diffraction combined with vibrating sample magnetometer. The results show that single phase of polycrystalline Ce:YIG thin films can be obtained by the post-annealing of as-deposited films at the temperature of 700 °C. However, two steps of phase segregation of Ce:YIG occur as the post-annealing temperature increases: at first, Ce:YIG is decomposed into YIG and non-magnetic CeO₂ when annealed at 800 °C; then YIG continues to be decomposed forming Fe₂O₃ when the temperature is increased up to 900 °C. Consequently, the saturation magnetization of Ce:YIG films decreases first and then increases with the post-annealing temperature going up, which indicates that the saturation magnetization of Ce:YIG films is mainly related to the phase composition of the films. Meanwhile, the presence of SiO₂ buffer layer can significantly enhance the saturation magnetization of Ce:YIG films.     

Growth and characterization of Y2O3 thin films

Y₂O₃ thin films were grown on silicon (1 0 0) substrates by pulsed-laser deposition at different substrate temperatures and O₂ pressures. The structure and composition of films are studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Y₂O₃ thin films deposited in vacuum strongly oriented their [1 1 1] axis of the cubic structure and the film quality depended on the substrate temperature. The magnitude of O₂ pressure obviously influences the film structure and quality. Due to the silicon diffusion and interface reaction during the deposition, yttrium silicate and SiO₂ were formed. The strong relationship between composition and growth condition was discussed.     

F2 laser induced oxidation of inorganic material

Transparent SiO₂ thin films were selectively fabricated on Si wafer by 157 nm F₂ laser in N₂/O₂ gas atmosphere. The F₂ laser photochemically produced active O(¹D) atoms from O₂ molecules in the gas atmosphere; strong oxidation reaction could be induced to fabricate SiO₂ thin films only on the irradiated areas of Si wafer. The oxidation reaction was sensitive to the single pulse fluence of F₂ laser. The irradiated areas were swelled and the height was approximately 500-1000 nm at the 205-mJ/cm² single pulse fluence for 60 min laser irradiation. The fabricated thin films were analytically identified to be SiO₂ by the Fourier-transform IR spectroscopy. The SiO₂ thin films could be also removed by subsequent chemical etching to fabricate micro-holes 50 nm in depth on Si wafer for microfabrication.     

Dielectric properties of continuous composition spreaded MgO-Ta2O5 thin films

The dielectric properties of MgO-Ta₂O₅ continuous composition spread (CCS) thin films were investigated. The MgO-Ta₂O₅ CCS thin films were deposited on Pt/Ti/SiO₂/Si substrates by off-Axis RF magnetron sputtering system, and then the films were annealed at 350 °C with rapid thermal annealing system in vacuum. The dielectric constant and loss of MgO-Ta₂O₅ CCS thin films were plotted via 1500 micron-step measuring. The specific point of Ta₂O₅-MgO CCS thin film (post annealed at 350 °C) showing superior dielectric properties of high dielectric constant (k ∼ 28) and low dielectric loss (tan δ < 0⋅004) at 1 MHz were found in the area of 3-5 mm apart from Ta₂O₅ side on the substrate. The cation's composition of thin film was Mg:Ta = 0.4:2 at%.     

Effects of substrates on the structure and dielectric properties of Ba(Sn0.15Ti0.85)O3 thin films

Ba(Sn_0.15Ti_0.85)O₃ (BTS) thin films were grown on Pt(1 1 1)/Ti/SiO₂/Si and LaNiO₃(LNO)/Pt(1 1 1)/Ti/SiO₂/Si substrates by a sol-gel processing technique, respectively. The BTS thin films deposited on annealed Pt(1 1 1)/Ti/SiO₂/Si and annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrates exhibited strong (1 1 1) and perfect (1 0 0) orientations, respectively. The BTS thin films grown on un-annealed Pt(1 1 1)/Ti/SiO₂/Si substrates showed random orientation with intense (1 1 0) peak, while the films deposited on un-annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrate exhibited random orientation with intense (1 0 0) peak, respectively. The dielectric constant of the BTS films deposited on annealed Pt(1 1 1)/Ti/SiO₂/Si, annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si, un-annealed Pt(1 1 1)/Ti/SiO₂/Si and un-annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrates was 512, 565, 386 and 437, respectively, measured at a frequency of 100 kHz. A high tunability of 49.7% was obtained for the films deposited on annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrate, measured at the frequency of 100 kHz with an applied electric field of 200 kV/cm. The high tunability has been attributed to the (1 0 0) texture of the films and larger grain sizes.     

Trap-controlled behavior in ultrathin Lu2O3 high-k gate dielectrics

Amorphous Lu₂O₃ high-k gate dielectrics were grown directly on n-type (100) Si substrates by the pulsed laser deposition (PLD) technique. High-resolution transmission electron microscope (HRTEM) observation illustrated that the Lu₂O₃ film has amorphous structure and the interface with Si substrate is free from amorphous SiO₂. An equivalent oxide thickness (EOT) of 1.1 nm with a leakage current density of 2.6×10⁻⁵ A/cm² at 1 V accumulation bias was obtained for 4.5 nm thick Lu₂O₃ thin film deposited at room temperature followed by post-deposition anneal (PDA) at 600 °C in oxygen ambient. The effects of PDA process and light illumination were studied by capacitance-voltage (C-V) and current density-voltage (J-V) measurements. It was proposed that the net fixed charge density and leakage current density could be altered significantly depending on the post-annealing conditions and the capability of traps to trap and release charges.     

Influence of MgO and ZrO2 buffer layers on dielectric properties of Ba(Zr0.20Ti0.80)O3 thin films prepared by sol-gel processing

Ba(Zr_0.20Ti_0.80)O₃ (BZT) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si, MgO and ZrO₂ buffered Pt(1 1 1)/Ti/SiO₂/Si substrates by a sol-gel process. The BZT thin films directly grown on Pt(1 1 1)/Ti/SiO₂/Si substrates exhibit highly (1 1 1) preferred orientation, while the films deposited on Pt(1 1 1)/Ti/SiO₂/Si substrates with MgO and ZrO₂ buffer layers show highly (1 1 0) preferred orientation. At 100 kHz, dielectric constants are 417, 311 and 321 for the BZT thin films grown on Pt(1 1 1)/Ti/SiO₂/Si, MgO and ZrO₂ buffered Pt(1 1 1)/Ti/SiO₂/Si substrates, respectively. The difference in dielectric properties of three BZT films can be attributed to the series capacitance effect, interface conditions and their orientations.     

Characteristics of sandwich-structured Al2O3/HfO2/Al2O3 gate dielectric films on ultra-thin silicon-on-insulator substrates

Sandwich-structure Al₂O₃/HfO₂/Al₂O₃ gate dielectric films were grown on ultra-thin silicon-on-insulator (SOI) substrates by vacuum electron beam evaporation (EB-PVD) method. AFM and TEM observations showed that the films remained amorphous even after post-annealing treatment at 950 °C with smooth surface and clean silicon interface. EDX- and XPS-analysis results revealed no silicate or silicide at the silicon interface. The equivalent oxide thickness was 3 nm and the dielectric constant was around 7.2, as determined by electrical measurements. A fixed charge density of 3 × 10¹⁰ cm⁻² and a leakage current of 5 × 10⁻⁷A/cm² at 2 V gate bias were achieved for Au/gate stack /Si/SiO₂/Si/Au MIS capacitors. Post-annealing treatment was found to effectively reduce trap density, but increase in annealing temperature did not made any significant difference in the electrical performance.     

Cluster size dependence of SiO2 thin film formation by O2 gas cluster ion beams

Cluster size effects of SiO₂ thin film formation with size-selected O₂ gas cluster ion beams (GCIBs) irradiation on Si surface were studied. The cluster size varied between 500 and 20,000 molecules/cluster. With acceleration voltage of 5 kV, the SiO₂ thickness was close to the native oxide thickness by irradiation of (O₂)_20,000 (0.25 eV/molecule), or (O₂)_10,000 (0.5 eV/molecule). However, it increased suddenly above 1 eV/molecule (5000 molecules/cluster), and increased monotonically up to 10 eV/molecule (500 molecules/cluster). The SiO₂ thickness with 1 and 10 eV/molecule O₂-GCIB were 2.1 and 5.0 nm, respectively. When the acceleration voltage was 30 kV, the SiO₂ thickness has a peak around 10 eV/molecule (3000 molecules/cluster), and it decreased gradually with increasing the energy/molecule. At high energy/molecule, physical sputtering effect became more dominant process than oxide formation. These results suggest that SiO₂ thin film formation can be controlled by energy per molecule.     

Reduced dielectric loss and leakage current in CaCu3Ti4O12/SiO2/CaCu3Ti4O12 multilayered films

The CaCu₃Ti₄O₁₂/SiO₂/CaCu₃Ti₄O₁₂ (CCTO/SiO₂/CCTO) multilayered films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition method. It has been demonstrated that the dielectric loss and the leakage current density were significantly reduced with the increase of the SiO₂ layer thickness, accompanied with a decrease of the dielectric constant. The CCTO film with a 20 nm SiO₂ layer showed a dielectric loss of 0.065 at 100 kHz and the leakage current density of 6×10⁻⁷ A/cm² at 100 kV/cm, which were much lower than those of the single layer CCTO films. The improvement of the electric properties is ascribed to two reasons: one is the improved crystallinity; the other is the reduced free carriers in the multilayered films.     

Multiferroic properties of Bi0.8La0.2FeO3/CoFe2O4 multilayer thin films

Bi_0.8La_0.2FeO₃/CoFe₂O₄ (BLFO/CFO) multilayer thin films (totally 20 layers BLFO and 19 layers CFO) were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and transmission electron microscope measurements show that the films are polycrystalline and consisted of multilayered structure. Ferroelectric hysteresis loops with remnant polarization and saturated polarization of 4.2 and 13.3 μC/cm², respectively, were observed. On the other hand, the films show well-shaped magnetization hysteresis loops with saturated and remnant magnetization of 34.7 and 11.4 emu/cm³, respectively, which are significantly larger than pure BLFO thin films deposited under the same conditions. These results indicate that constructing epitaxial superlattice might be a promising way to fabricate multiferroics with improved properties.     

The effect of annealing on the room temperature ferromagnetism in co-sputtered In2O3: C thin films

In this paper, we report investigation of room temperature (RT) ferromagnetism in In₂O₃ (InO) thin films doped with carbon prepared by the co-sputtering method. InO thin films both undoped and C doped with varied thicknesses in the range of 45 to 80 nm were synthesized on Si substrates with varied C concentrations. The carbon concentration was varied from 1.6 to 9.3 at%. The undoped InO films showed no trace of ferromagnetism. Carbon doped films (InO:C) exhibited ferromagnetism at RT, which was of the orders of 10⁻⁵ emu and varied strongly with C concentrations. It is observed that the magnetization reached a maximum value of 5.7 emu/cm³ at 4 at% C. Annealing of the InO:C films in an oxygen environment resulted in a decrease in the magnetization, indicating the crucial role of oxygen vacancies in the films. It is concluded that the oxygen vacancies were important and compete with C substitution for the RT ferromagnetism.     

Infrared optical properties of Ba(Zr0.20Ti0.80)O3 and Ba(Zr0.30Ti0.70)O3 thin films prepared by sol-gel method

Ba(Zr_xTi_1−x)O₃ (BZT) (x = 0.20 and 0.30) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrate by sol-gel method. X-ray diffraction patterns show that the thin films have a good crystallinity. Optical properties of the films in the wavelength range of 2.5-12 μm are studied by infrared spectroscopic ellipsometry (IRSE). The optical constants of the BZT thin films are determined by fitting the IRSE data using a classical dispersion formula. As the wavelength increases, the refractive index decreases, while the extinction coefficients increase. The effective static ionic charges are derived, which are smaller than that in a purely ionic material for the BZT thin films.     

XPS analysis for degraded Y2SiO5:Ce phosphor thin films

X-ray photoelectron spectroscopy (XPS) results were obtained for standard Y₂SiO₅:Ce phosphor powders as well as undegraded and 144 h electron degraded Y₂SiO₅:Ce pulsed laser deposited (PLD) thin films. The two Ce 3d peaks positioned at 877.9 ± 0.3 and 882.0 ± 0.2 eV are correlated with the two different sites occupied by Ce in the Y₂SiO₅ matrix. Ce replaced the Y in the two different sites with coordination numbers of 9 and 7. The two Ce 3d XPS peaks obtained during the thin film analysis were also correlated with the luminescent mechanism of the broad band emission spectra of the Y₂SiO₅:Ce X₁ phase. These two different sites are responsible for the two main sets of cathodoluminescent (CL) and photoluminescence (PL) peaks situated at wavelengths of 418 and 496 nm. A 144 h electron degradation study on the Y₂SiO₅:Ce thin film yielded an increase in the CL intensity with a second broad emission peak emerging between 600 and 700 nm. XPS analysis showed the presence of SiO₂ on the surface that formed during prolonged electron bombardment. The electron stimulated surface chemical reaction (ESSCR) model is used to explain the formation of this luminescent SiO₂ layer.     

Anomalous Hall effect in Cu and Fe codoped In2O3 and ITO thin films

We present a systematic study of the structure, magnetization, resistivity, and Hall effect properties of pulsed laser deposited Fe- and Cu-codoped In₂O₃ and indium-tin-oxide (ITO) thin films. Both the films show a clear ferromagnetism and anomalous Hall effect at 300 K. The saturated magnetic moments are almost the same for the two samples, but their remanent moments M_r and coercive fields H_C are quite different. M_r and H_C values of ITO film are much smaller than that of In₂O₃. The ITO sample shows a typical semiconducting behavior in whole studied temperature range, while the In₂O₃ thin film is metallic in the temperature range between 147 and 285 K. Analysis of different conduction mechanisms suggest that charge carriers are not localized in the present films. The profile of the anomalous Hall effect vs. magnetic field was found to be identical to the magnetic hysteresis loops, indicating the possible intrinsic nature of ferromagnetism in the present samples.     

Structural and electrical transport properties of ZnxFe3−xO4 thin film deposited on Si (1 1 1) by pulsed-laser deposition

Polycrystalline thin films of Fe_3−xZn_xO₄ (x = 0.0, 0.01 and 0.02) were prepared by pulsed-laser deposition technique on Si (1 1 1) substrate. X-ray diffraction studies of parent as well as Zn doped magnetite show the spinel cubic structure of film with (1 1 1) orientation. The order–disorder transition temperature for Fe₃O₄ thin film with thickness of 150 nm are at 123 K (Si). Zn doping leads to enhancement of resistivity by Zn²⁺ substitution originates from a decrease of the carrier concentration, which do not show the Verwey transition. The Raman spectra for parent Fe₃O₄ on Si (1 1 1) substrate shows all Raman active modes for thin films at energies of T_2g¹, T_2g³, T_2g², and A_1g at 193, 304, 531 and 668 cm⁻¹. It is noticed that the frequency positions of the strongest A_1g mode are at 668.3 cm⁻¹, for all parent Fe₃O₄ thin film shifted at lower wave number as 663.7 for Fe_2.98Zn_0.02O₄ thin film on Si (1 1 1) substrate. The integral intensity at 668 cm⁻¹ increased significantly with decreasing doping concentration and highest for the parent sample, which is due to residual stress stored in the surface.     

High-throughput characterization of BixY3−xFe5O12 combinatorial thin films by magneto-optical imaging technique

Bi_xY_3−xFe₅O₁₂ thin films have been grown on GGG (Gd₃Ga₅O₁₂) (1 1 1) substrates by the combinatorial composition-spread techniques under substrate temperature (T_sub) ranging from 410 to 700 °C and O₂ pressure of 200 mTorr. In order to study the effect of substrates on the deposition of Bi_xY_3−xFe₅O₁₂ thin films, garnet substrates annealed at 1300 °C for 3 h were also used. Magneto-optical properties were characterized by our home-designed magneto-optical imaging system. From the maps of Faraday rotation angle θ_F, it was evident that the Faraday effect appears only when T_sub = 430-630 °C. θ_F reaches to the maximum value (∼6°/μm, λ = 632 nm) at 500 °C, and is proportional to the Bi contents. XRD and EPMA analyses showed that Bi ions are easier to substitute for Y sites and better crystallinity is obtained for annealed substrates than for commercial ones.     

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi_1.5Zn_1.0Nb_1.5O₇/Ba_0.6Sr_0.4TiO₃/Bi_1.5Zn_1.0Nb_1.5O₇ tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2 nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO₂/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 °C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications.     

Characteristic properties of Y2SiO5:Ce thin films grown with PLD

Three different gases (nitrogen (N₂), oxygen (O₂) and argon (Ar)) were used as background gases during the growth of pulsed laser deposition (PLD) Y₂SiO₅:Ce thin films. A Krypton fluoride laser (KrF), 248 nm was used for the PLD of the films on silicon (Si) (1 0 0) substrates. The effect of the background gases on the surface morphology, crystal growth and luminescent properties were investigated. All the experimental parameters, the gas pressure (455 mT), the substrate temperature (600 °C), the pulse frequency (8 Hz), the number of pulses (4000) and the laser fluence (1.6±0.2) J/cm² were kept constant. The only parameter that was changed during the deposition was the ambient gas species. The surface morphology and average particle sizes were monitored with scanning electron microscopy (SEM) and atomic force microscopy (AFM). X-ray diffraction (XRD) and Auger electron spectroscopy (AES) were used to determine the crystal structure and composition, respectively. Cathodo- (CL) and photoluminescence (PL) were used to measure the luminescent intensities for the different phosphor thin films. The nature of the particles, ablated on the substrate, is related to the collisions between the ejected particles and the ambient gas particles. The CL and PL intensities also depend on the particle sizes. A 144 h (coulomb dose of 1.4×10⁴ C cm⁻²) electron degradation study on the thin films ablated in the Ar gas environment resulted in a decrease in the main CL intensity peak at 440 nm and to the development of a new very broad luminescent peak spectra ranging from 400 to 850 nm due to the growth of a SiO₂ layer on the surface.     

Magnetoelectric properties of Mn-substituted BiFeO3 thin films with a TiO2 barrier

Multiferroic thin films with the general formula TiO₂/BiFe_1−xMn_xO₃ (x=0.00, 0.05, 0.10 and 0.15) (TiO₂/BFMO) were synthesized on Au/Ti/SiO₂/Si substrates using a chemical solution deposition (CSD) method assisted with magnetron sputtering. X-ray diffraction analysis shows the thin films contained perovskite structures with random orientations. Compared with BFMO films, the leakage current density of the TiO₂/BFMO thin films was found to be lower by nearly two orders of magnitude, and the remnant polarizations were increased by nearly ten times. The enhanced ferroelectric properties may be attributed to the lower leakage current caused by the introduction of the TiO₂ layer. The J-E characteristics indicated that the main conduction mechanism for the TiO₂/BFMO thin film was trap-free Ohmic conduction over a wide range of electric fields (0-500 kV/cm). In addition, ferromagnetism was observed in the Mn doped BFO thin films at room temperature. The origin of ferromagnetism is related to the competition between distortion of structure and decrease of grain size and decreasing net magnetic moment in films due to Mn doping.