High magnetostriction at low fields of (Tb1−xDyx)0.2Pr0.8(Fe0.4Co0.6)1.88C0.05 intermetallic compounds

The structure and magnetostriction of the (Tb_1−xDy_x)_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 intermetallic compounds (0≤x≤1) were studied by X-ray diffraction and magnetic measurements. The formation of an approximate single Laves phase with a MgCu2-type cubic structure was observed in this series of compounds. It was found that the Curie temperature and the saturation magnetization of the compounds would decrease with increase in the Dy content up to x=1. The magnetostriction λ_a (λ_a=λ_‖-λ_⊥) gently rises when x≤0.6, and follows with a precipitous fall when x exceeds 0.6, with the highest value of λ_a being reached in the compounds with x=0.6. The magnetostriction of all the samples was observed to approach their own saturation in the magnetic fields higher than 4 kOe. This indicates that the addition of a small amount of Dy could effectively improve the low-field magnetostriction of the Tb_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 compounds, which could become a kind of promising magnetostrictive material.     

The effect of boron on the structure and magnetic properties of Pr0.15Tb0.3Dy0.55Fe1.85 alloy

The structure, Curie temperature and magnetostriction of Pr_0.15Tb_0.3Dy_0.55Fe_1.85−xB_x   (x=0–0.3$x=0–0.3$) alloys have been investigated using X-ray diffraction, AC susceptibility and standard strain gauge techniques. It was found that all the samples possess entirely MgCu₂-type cubic Laves structure. With increasing B concentration, the lattice parameter decreases, while the Curie temperature remains unchanged. The magnetostriction of Pr_0.15Tb_0.3Dy_0.55Fe_1.85−xB_x alloys at room temperature increases with increasing B concentration firstly, and then decreases slightly.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Giant forced volume magnetostriction in polycrystalline Tb0.3Dy0.7Fe1.95 alloys under magnetomechanical loading

The axial and transversal linear magnetostrictions (λ_∥ and λ_⊥) in [1 1 0] oriented polycrystalline Tb_0.3Dy_0.7Fe_1.95 alloys were measured simultaneously under uniaxial magnetomechanical loading to get the forced volume magnetostriction (ω=λ_∥+2λ_⊥). Despite the almost zero ω observed in Terfenol-D single crystals, it reaches up to 1000×10⁻⁶ in polycrystalline Tb_0.3Dy_0.7Fe_1.95 alloys near the saturation magnetic field under a stress above 50 MPa.     

Photoluminescence properties and effects of dopant concentration in Bi2ZnB2O7:Tb phosphor

A novel green phosphor, Tb³⁺ doped Bi₂ZnB₂O₇ was synthesized by conventional solid state reaction method. The phase of synthesized materials was determined using the XRD, DTA/TG and FTIR. The photoluminescence characteristics were investigated using spectrofluorometer at room temperature. Bi₂ZnB₂O₇:Tb³⁺ phosphors excited by 270 nm and 485 nm wavelengths. The emission spectra were composed of three bands, in which the dominated emission of green luminescence Bi₂ZnB₂O₇:Tb³⁺ attributed to the transition ⁵D₄ → ⁷F₅ is centered at 546 nm. The dependence of the emission intensity on the Tb³⁺ concentration for the Bi_2−xTb_xZnB₂O₇ (0.01 ≤ x ≤ 0.15) was studied and observed that the optimum concentration of Tb³⁺ in phosphor was 13 mol% for the highest emission intensity at 546 nm.     

Phase composition, microstructures and magnetic properties of melt-spun Nd1.2Fe10.5Mo1.5 ribbons and their nitrides

The effect of wheel speed on the phase compositions and microstructures of melt-spun Nd_1.2Fe_10.5Mo_1.5 ribbon was investigated. It is found that the Nd(Fe,Mo)₁₂ phase can be obtained at the wheel speed of 10 m/s, and TbCu₇-type Nd(Fe,Mo)₇ phase is formed with the wheel speed higher than 10 m/s. The amorphous phase is achieved at 65 m/s. The average grain size of phases decreases linearly with increasing wheel speed. The Nd(Fe,Mo)₁₂N_1.0 nitride obtained from annealed ribbons quenched at 65 m/s shows a coercivity much higher than that from the ribbons quenched at 10 m/s, which is due to the smaller grain size in the former ribbons.     

Effect of Mn on the magnetic properties of Fe3B/Nd2Fe14B nanocomposites

The magnetic properties of Nd_4.5Fe_77−xMn_xB_18.5 (x=0, 1 and 2) nanocomposites prepared by the crystallization of amorphous precursors were investigated. Addition of Mn is found to decrease the crystallization temperature of the amorphous ribbons. The intrinsic coercivity _iH_c and maximum energy product (BH)_max increase from 2.6 kOe and 9.1 MGOe for x=0 to 3.1 kOe and 10.3 MGOe for x=1, respectively, and the remanence ratio M_r/M_s increases from 0.70 to 0.72. The effect of Mn on Curie temperature T_C and the thermal stability of M_r and _iH_c were also studied. ⁵⁷Fe Mössbauer spectra have been recorded for x=0, 1 and 2 ribbons at room temperature and site preference of the Mn atoms in Fe₃B and Nd₂Fe₁₄B phases is discussed using the Mössbauer spectroscopy.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

Influence of boron on the giant magnetocaloric effect of La(Fe0.9Si0.1)13

The influences of boron addition on the phase formation, Curie temperature and magnetic entropy change of the NaZn₁₃-type La(Fe_0.9Si_0.1)₁₃ compound have been investigated. Eight boron containing La(Fe_0.9Si_0.1)₁₃B_x samples were prepared with x=0, 0.03, 0.06, 0.1, 0.2, 0.3, 0.5 and 0.6, respectively. Experimental results show that a small amount of B addition in La(Fe_0.9Si_0.1)₁₃ forms the solid solution NaZn₁₃-type structure phase by substituting B for Si or doping B into interstitial position of the lattice, preserves its giant magnetocaloric effects due to their first-order structural/magnetic transition, as well as increase its Curie temperature T_c slightly. The maximum magnetic entropy changes in the magnetic field change of 0–1.6 T are around 20 J kg^–1 K^–1 for the samples with Boron addition less than 0.3, while improving the Curie temperatures by 2 K.     

Structure, spin reorientation and M?ssbauer effect studies of Tb0.3Dy0.7(Fe1?xAlx)1.95 alloys

The effect of Al substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb_0.3Dy_0.7(Fe_1−x Al_x)_1.95 alloys (x = 0, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, 0.35) at room temperature and 77 K was investigated systematically. It was found that the primary phase of Tb_0.3Dy_0.7(Fe_1−x Al_x)_1.95 is the MgCu₂-type cubic Laves phase structure when x < 0.4 and the lattice constant a of Tb_0.3Dy_0.7(Fe_1−x Al_x)_1.95 increases approximately and monotonically with the increase of x. The substitution of Al leads to the fact that the magnetostriction λ inceases slightly in a low magnetic field (H ⩽ 40 kA/m), but decreases sharply and is easily close to saturation in a high applied field as x increases, showing that a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. It was also found that the spontaneous magnetostriction λ ₁₁₁ decreases greatly with x increasing. The analysis of the M?ssbauer spectra indicated that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the changes of composition and temperature, namely spin reorientation. A small amount of non-magnetic phase exists for x = 0.15 in Tb_0.3Dy_0.7(Fe_1−x Al_x)_1.95 alloys and the alloys become paramagnetic for x > 0.15 at room temperature, but at 77 K the alloys still remain magnetic phase even for x = 0.2. At room temperature and 77 K, the hyperfine field decreases and the isomer shifts increase with Al concentration increasing.     

A magnetic, magnetostrictive and Mössbauer study of Tb0.3Dy0.7−xPrx(Fe0.9Al0.1)1.95 alloys

The effect of Pr substitution for Dy on the magnetization, magnetostriction, anisotropy and spin reorientation of a series of Tb_0.3Dy_0.7−xPr_x(Fe_0.9Al_0.1)_1.95 alloys (x=0, 0.1, 0.20, 0.25, 0.30, 0.35) at room temperature has been investigated. It was found that the magnetization and magnetostriction of the homogenized Tb_0.3Dy_0.7−xPr_x(Fe_0.9Al_0.1)_1.95 alloys decreases drastically with increasing x and the magnetostrictive effect disappears for x>0.2, but the spontaneous magnetostriction λ₁₁₁ increases approximately linearly with increasing x. Moreover, the magnetostriction exhibits slightly bigger value at x=0.1 than the free alloys and is saturated more easily with the magnetic field H, showing that a small amount of Pr substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The analysis of the Mössbauer spectra indicated that the easy magnetization direction in the {1 1 0} plane deviates slightly from the main axis of symmetry with Pr concentration x, namely spin reorientation. Comparing with the Al substitution, the effect of Pr substitution for Dy on the spin reorientation is smaller.     

Mössbauer effect studies of Tb<Subscript>0.27</Subscript>Dy<Subscript>0.73</Subscript>(Fe<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Co<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>)2 intermetallics at 295 K

The synthesis of materials and the studies of crystal structure and ⁵⁷Fe Mössbauer effect were performed for Tb_0.27Dy_0.73(Fe_1?x Co _x )₂ intermetallics. Terfenol-D (Tb_0.27Dy_0.73Fe₂) is the starting compound of this Fe/Co-substituted series. X-ray measurements showed evidence of a pure cubic Laves phase C15, MgCu₂-type, and unit cell parameters were determined across the series. A Co substitution introduced local area, at sub-nanoscale, with random Fe/Co neighbourhoods of the ⁵⁷Fe atoms.Mössbauer effect spectra for the Tb_0.27Dy_0.73(Fe_1?x Co _x )₂ series at room temperature are composed of a number of locally originated subspectra due to the random distribution of Fe and Co atoms in the transition metal sublattice, and due to [1 1 1] an easy axis of magnetization. Isomer shift, magnetic hyperfine field and quadrupole interaction parameter were obtained from the spectra, both for the local area and for the bulk sample.As a result of Fe/Co substitution, a Slater-Pauling-type curve for the average magnetic hyperfine field vs. Co content was observed. It was found that the magnetic hyperfine fields corresponding to the local area also create a dependence of the Slater-Pauling-type vs. Co contribution in the Fe/Co neighbourhoods.     

Magnetic properties of YFe12−xMox compounds and magnetocaloric effect of YFe9.5Mo2.5

The characterization and magnetic properties of YFe_12−xMo_x (x=2.0, 2.5 and 3.0) with the ThMn₁₂-type structure, and the magnetocaloric effect of YFe_9.5Mo_2.5 were investigated. A directional growth was observed in YFe₁₀Mo₂ alloy. A broad peak in the zero-field-cooling (ZFC) magnetization curve of the YFe_12−xMo_x compounds is ascribed to the existence of ferromagnetic clusters with different site moments and scattered orientations of the moments. The broad range of the peak is reduced with increasing Mo content. A weak peak is observed near 190 K in the ZFC curve of YFe₉Mo₃, which is associated with the 8i sites being mostly occupied by Mo atoms. YFe_9.5Mo_2.5 has a magnetic entropy change of −1.09 J/kg K for a field change of 5 T at 277 K.     

Conductivity and sintering property of LaNi1 − xFexO3 ceramics prepared by Pechini method

Preparation of LaNi_1 − xFe_xO₃, which is one of the candidate materials of solid oxide fuel cell cathode, current collecting layer and interconnect coating was examined with Pechini method and solid state reaction method. Single phase LaNi_1 − xFe_xO₃ with large Ni content has successfully been prepared by low temperature sintering as 750 °C with Pechini method, whereas large amount of raw materials has remained with solid state reaction method by sintering at the same temperature. It can be ascribed to more homogenous cation distribution in raw powder material prior to sintering with Pechini method. It has also been revealed that LaNi_1 − xFe_xO₃ with x lower than 0.3 is thermodynamically unstable in air above 1000 °C. LaNi_0.6Fe_0.4O₃ showed superior property as cathode material with high electrical conductivity, thermodynamic stability and appropriate sintering property.     

Structure and magnetostrictive properties of melt-spun Pr(Fe0.4Co0.6)1.93 alloys

Pr(Fe_0.4Co_0.6)_1.93 ribbons were prepared by a melt-spinning method. Their structure and magnetic properties are investigated as functions of wheel speed and annealing temperature. The as-spun ribbon consists of a Pr(Fe, Co)₂ cubic Laves phase and an amorphous phase at a wheel speed of v≥35 m/s, while the non-cubic phases of PuNi₃-type and rare earth appear when the speed lower than 30 m/s. A single Pr(Fe, Co)₂ phase with MgCu₂-type structure has been synthesized by the process for the wheel speed of v≥35 m/s and subsequent annealing at 500 °C for 30 min. The epoxy/Pr(Fe_0.4Co_0.6)_1.93 composite has been produced by a cold isostatic pressing technique, and the magnetic properties have been investigated. The composite rod sample possesses good magnetostrictive properties, i.e., a large magnetostriction (λ_a=λ_∥−λ_⊥) of 710 ppm at 800 kA/m and a dynamic coefficient d₃₃ of 0.67 nm/A at 100 kA/m, and is of practical value.     

Synthesis and magnetic properties of melt-spun high Pr-content magnetostrictive alloys

Pseudobinary high Pr-content Tb_1−xPr_x(Fe_0.4Co_0.6)_1.93 (0.70≤x≤1.00) magnetostrictive alloys have been fabricated by a melt-spinning method. The effects of the composition, spinning, and annealing processes on the structure, thermal stability, and magnetic properties are investigated. At a wheel speed of v≤30 m/s, the as-spun ribbons consist of a mixture of (Tb,Pr)(Fe,Co)₂ cubic Laves phase and some non-cubic phases. A single (Tb,Pr)(Fe,Co)₂ phase with MgCu₂-type structure is formed with the process for the speed of v≥35 m/s and subsequent annealing at 500 °C for 30 min. The lattice parameter of the Tb_1−xPr_x(Fe_0.4Co_0.6)_1.93 Laves phase increases from 0.7354 nm for x=0.70 to 0.7384 nm for x=1.00 and approximately follows the linear Vegard's law. The Curie temperature decreases, while the saturation magnetization increases as increasing Pr content. The Pr-rich alloys possess the relatively lower coercivity and the faster saturation of magnetostriction as compared with the Tb-rich alloys, which can be understood by their lower magnetic anisotropy.     

Magnetic properties enhancement of Nd2Fe14B/α-Fe nanocomposites by Ta substitution

Nanostructured Nd_9.5Fe_84−xB_6.5Ta_x (x=0, 0.5, 1, 1.5, and 2) ribbons composed of Nd₂Fe₁₄B and α-Fe phases with a high coercivity and maximum energy product are fabricated by direct melt spinning. The effects of Ta addition on the structures and magnetic properties of melt-spun Nd_9.5Fe_84−xB_6.5Ta_x (x=0, 0.5, 1, 1.5, and 2) ribbons have been investigated. Compared with addition-free ribbons, small addition of Ta is found to reduce the grain sizes of the samples and improve their magnetic properties due to a strong exchange coupling between the Nd₂Fe₁₄B hard phase and α-Fe soft phase. A coercive field of 750 kA/m and a maximum energy product of 158 kJ/m³ in melt-spun Nd_9.5Fe_82.5B_6.5Ta_1.5 ribbons are obtained at room temperature.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Magnetostriction, Curie temperature and microstructure of Tb0.29(Dy1−xPrx)0.71Fe1.97 oriented alloys

The Tb_0.29(Dy_1−xPr_x)_0.71Fe_1.97 (x=0, 0.1, 0.2 and 0.3) alloys were prepared by directional solidification method. The orientation, magnetostriction λ, Curie temperature T_c and microstructure of alloys were characterized by XRD, standard resistant strain gauge technique, VSM and SEM-EDS. The results reveal that the alloys have a preferred orientation of 〈1 1 0〉 and 〈1 1 3〉 direction when x>0. With the increase in Pr content, the T_c of alloys decreases gradually and the non-cubic phase appears, resulting in the decline of λ dramatically, from 1935.2×10⁻⁶ for x=0 to 695.9×10⁻⁶ for x=0.3 at a compressive stress of 6 MPa and a magnetic field of H=240 kA m⁻¹.     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.