Multiple melting behavior of poly(butylene succinate). I. Thermal analysis of melt‐crystallized samples

The multiple melting behavior of poly(butylene succinate) (PBSu) was studied with differential scanning calorimetry (DSC). Three different PBSu resins, with molecular weights of 1.1 × 10⁵, 1.8 × 10⁵, and 2.5 × 10⁵, were cooled from the melt (150 °C) at various cooling rates (CRs) ranging from 0.2 to 50 K min^?1. The peak crystallization temperature (T_c) of the DSC curve in the cooling process decreased almost linearly with the logarithm of the CR. DSC melting curves for the melt‐crystallized samples were obtained at 10 K min^?1. Double endothermic peaks, a high‐temperature peak H and a low‐temperature peak L, and an exothermic peak located between them appeared. Peak L decreased with increasing CR, whereas peak H increased. An endothermic shoulder peak appeared at the lower temperature of peak H. The CR dependence of the peak melting temperatures [T_m(L) and T_m(H)], recrystallization temperature (T_re), and heat of fusion (ΔH) was obtained. Their fitting curves were obtained as functions of log(CR). T_m(L), T_re, and ΔH decreased almost linearly with log(CR), whereas T_m(H) was almost constant. Peak H decreased with the molecular weight, whereas peak L increased. It was suggested that the rate of the recrystallization decreased with the molecular weight. T_m(L), T_m(H), T_re, and T_c for the lowest molecular weight sample were lower than those for the others. In contrast, ΔH for the highest molecular weight sample was lower than that for the others. If the molecular weight dependence of the melting temperature for PBSu is similar to that for polyethylene, the results for the molecular weight dependence of PBSu can be explained. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2411–2420, 2002     

Thermal analysis of the double-melting behavior of poly(L-lactic acid)

The melting and crystallization behavior of poly(L -lactic acid) (PLLA; weight-average molecular weight = 3 × 10⁵) was studied with differential scanning calorimetry (DSC). DSC curves for PLLA samples were obtained at various cooling rates (CRs) from the melt (210 °C). The peak crystallization temperature and the exothermic heat of crystallization determined from the DSC curve decreased almost linearly with increasing log(CR). DSC melting curves for the melt-crystallized samples were obtained at various heating rates (HRs). The double-melting behavior was confirmed by the double endothermic peaks, a high-temperature peak (H) and a low-temperature peak (L), that appeared in the DSC curves at slow HRs for the samples prepared with a slow CR. Peak L increased with increasing HR, whereas peak H decreased. The peak melting temperatures of L and H [T_m(L) and T_m(H)] decreased linearly with log(HR). The appearance region of the double-melting peaks (L and H) was illustrated in a CR–HR map. Peak L decreased with increasing CR, whereas peak H increased. T_m(L) and T_m(H) decreased almost linearly with log(CR). The characteristics of the crystallization and double-melting behavior were explained by the slow rates of crystallization and recrystallization, respectively. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 25–32, 2004     

Multiple melting behavior of poly(butylene succinate)

The multiple melting behavior of poly(butylenes succinate) (PBS) isothermally crystallized from the melt was investigated using differential scanning calorimetry (DSC), temperature modulated DSC (MDSC) and polarized optical microscopy. PBS exhibits at most four melting endotherms (denoted as T_m1, T_m2, T_m3, and T_m4 from high to low temperatures) and a crystallization exotherm (denoted as T_re) in the DSC heating trace. Multiple melting endotherms were observed even at high heating rates. The origins of each endothermal and exothermal peak were discussed in detail. It is suggested that: (i) the crystallization exothermic peak, T_re, relates to the recrystallization of the melt of the crystallites with lower thermal stability; (ii) the T_m1 is ascribed to the melting of crystallites formed through recrystallization; (iii) two crystal populations with different thermal stability are responsible for the T_m2 and T_m3; (iv) the T_m4, which is the annealing peak, represents the transition of the rigid amorphous fraction (RAF) from solid-like RAF into liquid-like amorphous fraction.     

New insights into the multiple melting behaviors of the semicrystalline ethylene‐hexene copolymer: Origins of quintuple melting peaks

A semicrystalline ethylene‐hexene copolymer (PEH) was subjected to a simple thermal treatment procedure as follows: the sample was isothermally crystallized at a certain isothermal crystallization temperature from melt, and then was quenched in liquid nitrogen. Quintuple melting peaks could be observed in heating scan of the sample by using differential scanning calorimeter (DSC). Particularly, an intriguing endothermic peak (termed as Peak 0) was found to locate at about 45 °C. The multiple melting behaviors for this semicrystalline ethylene‐hexene copolymer were investigated in details by using DSC. Wide‐angle X‐ray diffraction (WAXD) technique was applied to examine the crystal forms to provide complementary information for interpreting the multiple melting behaviors. Convincing results indicated that Peak 0 was due to the melting of crystals formed at room temperature from the much highly branched ethylene sequences. Direct heating scans from isothermal crystallization temperature (T_c, 104–118 °C) were examined for comparison, which indicated that the multiple melting behaviors depended on isothermal crystallization temperature and time. A triple melting behavior could be observed after a relatively short isothermal crystallization time at a low T_c (104–112 °C), which could be attributed to a combination of melting of two coexistent lamellar stack populations with different lamellar thicknesses and the melting‐recrystallization‐remelting (mrr) event. A dual melting behavior could be observed for isothermal crystallization with both a long enough time at a low T_c and a short or long time at an intermediate T_c (114 °C), which was ascribed to two different crystal populations. At a high T_c (116–118 °C), crystallizable ethylene sequences were so few that only one single broad melting peak could be observed. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2100–2115, 2008     

Characterization,crystallization kinetics,and melting behavior of poly(ethylene succinate) copolyester containing 10 mol % butylene succinate

Copolyester was synthesized and characterized as having 89.9 mol % ethylene succinate units and 10.1 mol % butylene succinate units in a random sequence, as revealed by NMR. Isothermal crystallization kinetics was studied in the temperature range (T_c) from 30 to 73 °C using differential scanning calorimetry (DSC). The melting behavior after isothermal crystallization was investigated using DSC by varying the T_c, the heating rate and the crystallization time. DSC curves showed triple melting peaks. The melting behavior indicates that the upper melting peaks are associated primarily with the melting of lamellar crystals with various stabilities. As the T_c increases, the contribution of recrystallization slowly decreases and finally disappears. A Hoffman‐Weeks linear plot gives an equilibrium melting temperature of 107.0 °C. The spherulite growth of this copolyester from 80 to 20 °C at a cooling rate of 2 or 4 °C/min was monitored and recorded using an optical microscope equipped with a CCD camera. Continuous growth rates between melting and glass transition temperatures can be obtained after curve‐fitting procedures. These data fit well with those data points measured in the isothermal experiments. These data were analyzed with the Hoffman and Lauritzen theory. A regime II → III transition was detected at around 52 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2431–2442, 2008     

Stepwise annealing of poly(butylene terephthalate)

Annealing of poly(butylene terephthalate) (PBT) was studied by differential scanning calorimetry (DSC) and small angle X‐ray scattering (SAXS) measurement. A PBT sample was annealed at a recrystallization temperature where recrystallization occurs with a maximum rate in the heating process of the sample. In the subsequent annealing steps, the annealed sample was annealed repeatedly at the recrystallization temperatures, and the stepwise annealing sample was obtained. Peak melting temperature (T_m) and sharpness of DSC peak of the stepwise annealing sample increased with the annealing step. A high melting‐temperature sample was obtained in a short time, and T_m increased up to 238.5°C which is higher than all the T_m values that appear in the literature. The long period calculated from SAXS curves of the stepwise annealing sample increased with the annealing step. The increase of crystallite size and perfection of the crystal in the stepwise annealing process is suggested. Annealing experiment indicated that T^°_m should be higher than about 235°C. T_m increased linearly with the annealing temperature of the final step in the stepwise annealing (T_a). The equilibrium melting temperature (T^°_m) for PBT was estimated to be 247°C by the application of a Hoffman–Weeks plot to the relation between T_m vs. T_a. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2420–2429, 1999     

Thermodynamic and kinetic behaviour of salicylsalicylic acid

The thermal behaviour of salicylsalicylic acid (CAS number 552-94-3) was studied by differential scanning calorimetry (DSC). The endothermic melting peak and the fingerprint of the glass transition were characterised at a heating rate of 10°C min^-1. The melting peak showed an onset at T _on = 144°C (417 K) and a maximum intensity at T _max = 152°C (425 K), while the onset of the glass transition signal was at T _on = 6°C. The melting enthalpy was found to be Δ_mH = 28.9±0.3 kJ mol^-1, and the heat capacity jump at the glass transition was ΔC _P = 108.1±0.1 J K^-1mol^-1. The study of the influence of the heating rate on the temperature location of the glass transition signal by DSC, allowed the determination of the activation energy at the glass transition temperature (245 kJ mol^-1), and the calculation of the fragility index of salicyl salicylate (m = 45). Finally, the standard molar enthalpy of formation of crystalline monoclinic salicylsalicylic acid at T = 298.15 K, was determined as Δ_fH_m ^o(C₁₄H₁₀O₅, cr) = - (837.6±3.3) kJ mol^-1, by combustion calorimetry. This revised version was published online in August 2006 with corrections to the Cover Date.     

Investigations of the equilibrium melting temperature in PBT and PC/PBT blends

The melting behavior of poly(butylene terephthalate) and its blends with bisphenol-A polycarbonate was investigated with differential scanning calorimetry. The aim of this work was to determine the equilibrium melting temperature and its dependence on the blend composition using the Hoffman-Weeks plots. It is shown that the critical analysis of various influences on the melting peak is necessary for the reorganization processes and crystallized content of blends. The experimental conditions and the corrections of measured temperatures were derived and discussed. It was found that the use of the extrapolated onset temperature T_m,o of the melting peak is more efficient than the maximum temperature T_m for the Hoffman-Weeks plots. The equilibrium values of pure PBT are determined to be T^o_m,o = 501 K and T^o_m = 506 K. The equilibrium temperatures of the blends do not show a depression with increasing PC content. Using the Nishi-Wang relation, the results can be qualitatively interpreted with a polymer-polymer interaction coefficient χ ≥ 0 between both components. A weak increase in the equilibrium temperature with increasing PC content was observed. A hypothesis to explain this is based on the possibility of a changed population of the different spherulites with various melting temperatures in dependence on PC content. © 1996 John Wiley & Sons, Inc.     

High-temperature aging of Halar film. II. Analysis of melting behavior

Melting behavior of an experimental Halar film, a predominantly alternating 1:1 copolymer of ethylene (E) and chlorotrifluoroethylene (CTFE), has been studied. Differential scanning calorimetry (DSC) reveals single or double melting peaks, depending upon the thermal history. The lower-temperature melting peak T_m1 is produced only by the thermal treatment and shows a strong dependence on annealing time and temperature. On the basis of the DSC and x-ray data it can be suggested that T_m1 represents the melting of relatively small crystallites formed upon annealing. The higher-temperature melting peak T_m2 is always shown at 238°C. (Note: the specification for commercial Halar product is 240°C. The slightly lower melting temperature reported in this study is probably due to the fact that we are dealing with an experimental melt-processed material.) On the basis of the heating rate study we propose that Halar crystallizes with stable crystals (T_m2 = 238°C) regardless of the crystallization conditions, i.e., quenching, slow cooling, or even annealing. Crystals of Halar have a heat of fusion of approximately 35 cal/g or 146 kJ/kg. Detailed analysis of the melting behavior of Halar is presented.     

SAXS and DSC studies of the crystallization and melting phenomena of poly(ϵ‐caprolactone)

The relationships between the crystallization temperature, T_c, the crystal thickness, d_c and the melting peak temperature, T_m of poly(ϵ‐caprolactone) have been determined by carrying out time‐ and temperature‐dependent small angle x‐ray scattering experiments. A two‐step melting has been suggested, resulting in the occurrence of two well defined independent boundary lines, indicating the transformation from melt into the partially crystalline state. For crystallization temperatures lower than 40°C, during heating, more pronounced peak shifts are observed with the final melting of the crystallites having the same thickness of d_c ≈︁ 7 nm. In this region, it is evident that crystals have relatively good stabilities, since they have fairly uniform thickness. At higher temperatures, above 40°C, T_m increases with T_c, together with the thickness. The transformation of the melt into the partially crystalline state depicts a two‐step process, beginning with the formation of a well defined initial structure with lower order, which is subsequently stabilized.     

Random copolymers of poly(butylene terephthalate): Effect of thiodiethylene terephthalate units on melting behaviour and crystallization kinetics

The melting behavior and the crystallization kinetics of poly(butylene terephthalate/thiodiethylene terephthalate) copolymers were investigated by DSC technique. The multiple endotherms were influenced both by T _c and composition. By applying the Hoffman—Weeks' method, T _m ⁰ the of the copolymers was derived. The isothermal crystallization kinetics was analyzed according to the Avrami's treatment. Values of the exponent n close to 3 were obtained, independently of T _c and composition. The introduction of thiodiethylene terephthalate units decreased the PBT crystallization rate. H _m was correlated to c _p for samples with different degree of crystallinity and the results were interpreted on the basis of the existence of an interphase.This revised version was published online in November 2005 with corrections to the Cover Date.     

Melting behavior in blends of isotactic polypropylene and a liquid crystalline polymer

The influence of low contents of a liquid crystalline polymer on the crystallization and melting behavior of isotactic polypropylene (iPP) was investigated using electron and optical microscopy, differential scanning calorimetry, and X-ray diffraction. In pure iPP, the α modification was found, whereas for iPP/Vectra blends at Vectra concentration <5%, both α and β forms were observed. The amount of β phase varied from 0.23 to 0.16. Optical microscopy showed that Vectra was able to nucleate both α and β forms. Non-isothermal crystallization produces a material with a strong tendency for recrystallization of the α and β forms (αα′ and ββ′ recrystallization) leading to double endotherms for both crystalline forms in DSC thermograms. Melting thermograms after isothermal crystallization at low temperatures showed a similar behavior. At values of T_c > 119 °C for the α form and T_c > 125 °C for the β form, only one melting endotherm was observed because enough perfect crystals, not susceptible to recrystallization, were obtained. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1949–1959, 2004     

Crystal thickness distributions from melting homopolymers or random copolymers

Differential scanning calorimetry (DSC) can be used to infer the distribution of lamellar crystal thickness l. For homopolymers, the relation between melting temperature T and thickness is described by the Gibbs relation. In this case the weight distribution function of thickness g(l) ∝ P(T)(T − T)², where P(T) is DSC power and T is the melting temperature of an infinitely thick crystal. Copolymer melting is affected by the concentration of noncrystallizable comonomer in the melt as well as lamellar thickness. Unknown melt composition in copolymers with nonequilibrium crystallinity makes determination of the correct distribution g(l) from DSC impossible. An approximate distribution g₂(l) ∝ P(T)(T − T)² is proposed, where T is based on Flory's equilibrium crystallization theory. This approximate distribution is most accurate when crystallinity is small, that is, near the upper end of the melting range. Results are reported for polyethylene homopolymer and model ethylene–butene random copolymers. Corrections were not made for distortion of the DSC endotherms by thermal lag or by melting and recrystallization; these experiments are primarily to illustrate the effect of analysis in terms of an incorrect g₃(l) ∝ P(T). Average crystal thicknesses are about 20 nm for polyethylene and 5 nm for the copolymers. Distributions are characterized by l_w /l_n ≤ 1.1 in all cases. Width of the melting range is not a reliable indicator of the breadth of the thickness distribution. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 3131–3140, 1999     

Unusual recrystallization and melting behaviour in DSC scans of isotactic polypropylene samples

The unusual dependence of the melting peak temperature of the species recrystallized during DSC scans on the isothermal crystallization temperature (T _c ) is discussed for isotactic polypropylene samples. It is pointed out that such a phenomenon is not due to superheating effects; it is believed to be accounted for by assuming that the rates of the recrystallization phenomena at the same temperature are higher for samples obtained at higherT _c values.     

Melting behavior of isotactic polystyrene

The melting behavior of isotactic polystyrene, crystallized from the melt and from dilute solutions in trans-decalin, has been studied by differential scanning calorimetry and solubility measurements. The melting curves show 1, 2, or 3 melting endotherms. At large supercooling, crystallization from the melt produces a small melting endotherm just above the crystallization temperature T_c. This peak originates from secondary crystallization of melt trapped within the spherulites. The next melting endotherm is related to the normal primary crystallization process. Its peak temperature increases linearly with T_c, yielding an extrapolated value for the equilibrium melting temperature T_c° of 242 ± 1°C as found before. By self-seeding, crystallization from the melt could be performed at much higher temperature to obtain melting temperatures as high as 243°C, giving rise to doubt about the value of T_c° found by extrapolation. For normal values of T_c and heating rate, an extra endotherm appears on the melting curve. Its peak temperature is the same for both melt-crystallized and solution-crystallized samples, and independent of T_c, but rises with decreasing heating rate. From the effects of heating rate and partial scanning on the ratio of peak areas and of previous heat treatment on dissolution temperature, it is concluded that this peak arises from the second one by continuous melting and recrystallization during the scan.     

A study of phase separation of crystalline and miscible polymer blends. Poly(ε-caprolactone)/poly(styrene-co-acrylonitrile)

The phase separation of a crystalline and miscible polymer blend, poly(ε-caprolactone) /poly(styrene-co-acrylonitrile) (PCL/SAN), has been studied by differential scanning calorimetry (DSC), using a SAN containing 28.3% of acrylonitrile units. Several phenomena can be associated with the occurrence of phase separation depending upon the composition of the mixture. Following annealing at high temperatures, below and above the phase separation temperature T_c, three cases can be distinguished. In Case I, there is no sign of crystallization during quenching and DSC scanning, but a melting peak is observed at T_c, and above. In Case II, there is no crystallization on quenching but it does occur during the DSC run; the shift of the crystallization peak can then be related to T_c. In Case III, there is crystallization on quenching, and additional crystallization during the DSC run; the change of area of the crystallization peak is indicative of T_c. From these observations, the phase diagram of the system was determined. © 1993 John Wiley & Sons, Inc.     

Behavior of pressure dependence of melting temperatures in aromatic polyesters: Influence of polymer structure

The thermal behavior of three aromatic polyesters in a homologous series, poly(ethylene terephthalate) (PET), poly(trimethylene terephthalate) (PTT), and poly(butylene terephthalate) (PBT) was studied under hydrostatic pressure up to 200 MPa by using a high pressure differential thermal analysis apparatus. Confining fluid high pressure dilatometer was used to establish the volume–temperature curves (in both solid and liquid regions) from which volume change on melting of these polyesters at atmospheric pressure was determined. Single endothermic peak was seen for PET and PTT, whereas PBT showed double peaks above 50 MPa. Pressure coefficient of melting temperature at atmospheric pressure (dT_m/dp₍₀₎), was obtained from the quadratic fit. The dT_m/dp₍₀₎ for PTT was newly determined to be 0.445 KMPa^?1, whereas for PET and PBT were 0.503 and 0.455 KMPa^?1, respectively, comparable to reported values. The dT_m/dp₍₀₎ exhibited the odd‐even behavior corresponding to odd and even number of methylene groups in the repeat unit. Enthalpy and entropy of fusion had the most influence on this coefficient. Entropy related to conformational and volume change were evaluated and the former was found to have a significant impact on the value of dT_m/dp₍₀₎. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1799–1808, 2009     

Crystallization and melting behaviour of poly(m-xylene adipamide)

The melting and crystallisation behaviour of poly(m-xylene adipamide) (MXD6) are investigated by using the conventional DSC, X-ray diffraction and polarised light microscopy. Triple, double or single melting endotherms are obtained in subsequent heating scan for the samples after isothermal crystallisation from the melt state at different temperatures. The lowest melting peak can be ascribed to the melting of secondary crystals. The melting of primary crystals causes the medium melting peak and the highest melting peak is attributed to the melting of recrystallised species formed during heating. Following the Hoffman–Weeks theory, the equilibrium melting temperature is equal to 250°C and the equilibrium melting enthalpy ΔH _m ⁰ to 175 J g^–1. Then, using the Lauritzen–Hoffmann theory of secondary crystallisation, the analyse of the spherulitic growth shows that the temperature of transition between the growing regimes II and III is equal to 176°C. Finally the Gibbs-Thomson relationship allows the determination of the distribution function of crystalline lamellae.     

Crystallization and melting of polyethylene under high pressure. II. Effect of pressure on melting behavior of various types of crystals

The effect of pressure on the melting point and volume of fusion of polyethylene was studied by high-pressure dilatometry. Starting materials were crystallized slowly from the melt under pressures of 1500, 3500, 5130 kg/cm², and 1 atm. It has been shown that the unusual behavior observed at pressures above 4000 kg/cm² is due to crystallization and melting of two kinds of extended-chain crystals differing in thermal stability. These are designated as ordinary extended-chain and highly extended-chain crystals, respectively. The relation between pressure P and melting temperature T_m of folded-chain, ordinary extended-chain, and highly extended-chain polyethylene was determined precisely. At pressures up to about 3000 kg/cm², plots of P against T_m for the crystal forms have almost the same curvature and then become parallel. But at pressures above 4000 kg/cm², ordinary extended-chain crystals show a linear increase of T_m with a constant slope of about 70 atm/deg. Curve for the highly extended-chain crystals changes in slope from 70 to 50 atm/deg at pressures between 3500 and 4300 kg/cm², and then show a sharp increase of T_m with increasing pressure. Experiments show that the meltingpoint curve of the highly extended-chain crystals overlaps that of the ordinary extended-chain crystals at pressures below 4000 kg/cm². Annealing experiments with folded-chain and ordinary extended-chain crystals have been made under high pressure. It is suggested that the formation of highly extended-chain crystals occurs stepwise through the formation and reorganization of ordinary extended-chain crystals from the original folded-chain crystals by a mechanism of partial melting and recrystallization at pressures above 4000 kg/cm².     

Self-nucleation and recrystallization of isotactic polypropylene (α phase) investigated by differential scanning calorimetry

The crystallization behavior after partial or complete melting of the α phase of iPP is examined by combined differential scanning calorimetry (DSC) and optical microscopy: calorimetric results are directly correlated with corresponding morphologies of microtome sections of DSC samples. On partial melting at various temperatures (hereafter referred to as T_s) located in a narrow range (4°C) below and near T_m, the number of nuclei increases (as in classical self-nucleation experiments), by several orders of magnitude; on subsequent cooling, the crystallization peak is shifted by up to 25°C. After partial melting in the lower part of the T_s range and recrystallization, the polymers display a prominent morphology “memory effect” whereby a phantom pattern of the initial spherulite morphology is maintained. After partial melting in the upper part of the T_s range the initial morphology is erased and self-nucleation affects only the total number of nuclei. The present experimental procedures make it possible to define, under “standard” conditions, the crystallization range of the polymer and in particular, the maximum crystallization temperature achievable when “ideally” nucleated. © John Wiley & Sons, Inc.