Effect of temperature on pulsed laser deposition of HgCdTe films

HgCdTe thin films have been deposited on Si(1 1 1) substrates at different substrate temperatures by pulsed laser deposition (PLD). An Nd:YAG pulsed laser with a wavelength of 1064 nm was used as laser source. The influences of the substrate temperature on the crystalline quality, surface morphology and composition of HgCdTe thin films were characterized by X-ray diffraction (XRD), selected area electron diffraction (SAED), atomic force microscopy (AFM) and energy dispersive X-ray spectroscopy (EDS). The results show that in our experimental conditions, the HgCdTe thin films deposited at 200 °C have the best quality. When the substrate temperature is over 250 °C, the HgCdTe film becomes thermodynamically unstable and the quality of the film is degraded.     

Amorphous film thickness dependence for epitaxy of perovskite oxide films under excimer laser irradiation

We have studied the epitaxial growth of perovskite manganite LaMnO₃ (LMO) on SrTiO₃(1 0 0) in the excimer laser assisted metal organic deposition process. The LMO was preferentially grown from the substrate surface by the KrF laser irradiation. The study of amorphous LMO film thickness dependence on epitaxial growth under the excimer laser irradiation revealed that the photo-thermal heating effect strongly depended on the amorphous film thickness due to a low thermal conductivity of amorphous LMO: the ion-migration for chemical bond-forming at the reaction interface would be strongly enhanced in the amorphous LMO film with the large film thickness about 210 nm. On the other hand, the photo-chemical effect occurred efficiently for the amorphous film thickness in the range of 35-210 nm. These results indicate that the epitaxial growing rate was dominated by the photo-thermal heating after the photo-chemical activation at the growth interface.     

Structural and morphological characterization of TiO2 nanostructured films grown by nanosecond pulsed laser deposition

TiO₂ has attracted a lot of attention due to its photocatalytic properties and its potential applications in environmental purification and self cleaning coatings, as well as for its high optical transmittance in the visible-IR spectral range, high chemical stability and mechanical resistance. In this paper, we report on the growth of TiO₂ nanocrystalline films on Si (1 0 0) substrates by pulsed laser deposition (PLD). Rutile sintered targets were irradiated by KrF excimer laser (λ = 248 nm, pulse duration ∼30 ns) in a controlled oxygen environment and at constant substrate temperature of 650 °C. The structural and morphological properties of the films have been studied for different deposition parameters, such as oxygen partial pressure (0.05-5 Pa) and laser fluence (2- 4 J/cm²). X-ray diffraction (XRD) shows the formation of both rutile and anatase phases; however, it is observed that the anatase phase is suppressed at the highest laser fluences. X-ray photoelectron spectroscopy (XPS) measurements were performed to determine the stoichiometry of the grown films. The surface morphology of the deposits, studied by scanning electron (SEM) and atomic force (AFM) microscopies, has revealed nanostructured films. The dimensions and density of the nanoparticles observed at the surface depend on the partial pressure of oxygen during growth. The smallest particles of about 40 nm diameter were obtained for the highest pressures of inlet gas.     

Morphology and photoluminescence properties of zinc oxide films grown by pulsed laser deposition

Zinc oxide films with different morphologies have been grown by pulsed laser deposition, varying substrate temperature and oxygen pressure. At low oxygen pressure and low substrate temperature continuous films with different roughness have been obtained, while at high substrate temperature a film with sparse hexagonal pyramids has been observed. Increasing the oxygen pressure the film became rougher and at 100 Pa a rod-array has been deposited. The columns of this rod-array grew along the wurtzite c-axis perpendicularly to the substrate surface as proved by X-ray diffraction measurements. Near to the sample borders the columns were slightly tilted towards the center of the sample. The possible growth mechanisms giving rise to the different morphologies have been discussed. Low-temperature photoluminescence measurements allowed to get information about the film quality, showing the variations of the excitonic peak and two defect bands (green and violet-blue) with the different deposition parameters.     

Growth of a textured quasicrystalline phase in Ti-Ni-Zr films prepared by pulsed laser deposition

The preparation in thin film form of the known icosahedral phase in Ti-Ni-Zr bulk alloys has been investigated as a function of substrate temperature. Films were deposited by pulsed laser deposition on sapphire substrates at temperatures ranging from room temperature to 350 °C. Morphological and structural modifications have been followed by grazing-incidence and θ–2θ X-ray diffraction, transmission electron diffraction and imaging. Chemical composition has been analyzed by electron probe microanalysis. The in-depth variation of composition has been studied by secondary neutral mass spectroscopy. We show that pulsed laser deposition at 275 °C makes the formation of a 1-μm-thick film of Ti-Ni-Zr quasicrystalline textured nanocrystallites possible. Received: 7 June 2001 / Accepted: 18 February 2002 / Published online: 3 June 2002 RID="*" ID="*"Corresponding author. Fax: +33-3/8357-6300, E-mail: brien@mines.u-nancy.fr     

Influence of direct current plasma magnetron sputtering parameters on the material characteristics of polycrystalline copper films

Physical vapor processes using glow plasma discharge are widely employed in microelectronic industry. In particular magnetron sputtering is a major technique employed for the coating of thin films. This paper addresses the influence of direct current (DC) plasma magnetron sputtering parameters on the material characteristics of polycrystalline copper (Cu) thin films coated on silicon substrates. The influence of the sputtering parameters including DC plasma power and argon working gas pressure on the electrical and structural properties of the thin Cu films was investigated by means of surface profilometer, four-point probe and atomic force microscopy.     

Particulate assisted growth of ZnO nanorods and microrods by pulsed laser deposition

Zinc oxide (ZnO) thin films were deposited on the gallium nitride (GaN) and sapphire (Al₂O₃) substrates by pulsed laser deposition (PLD) without using any metal catalyst. The experiment was carried out at three different laser wavelengths of Nd:YAG laser (λ = 1064 nm, λ = 532 nm) and KrF excimer laser (λ = 248 nm). The ZnO films grown at λ = 532 nm revealed the presence of ZnO nanorods and microrods. The diameter of the rods varies from 250 nm to 2 μm and the length varies between 9 and 22 μm. The scanning electron microscopy (SEM) images of the rods revealed the absence of frozen balls at the tip of the ZnO rods. The growth of ZnO rods has been explained by vapor-solid (V-S) mechanism. The origin of growth of ZnO rods has been attributed to the ejection of micrometric and sub-micrometric sized particulates from the ZnO target. The ZnO films grown at λ = 1064 nm and λ = 248 nm do not show the rod like morphology. X-ray photoelectron spectroscopy (XPS) has not shown the presence of any impurity except zinc and oxygen.     

Heteroepitaxial growth of gallium nitride on muscovite mica plates by pulsed laser deposition

We have grown GaN films on mica substrates using pulsed laser deposition for the first time and investigated their structural properties using electron beam and X-ray diffraction. We found that GaN (000-1) grows on mica (001) with an in-plane alignment of [11-20] GaN//[010] mica. Despite the large lattice mismatch between GaN and mica, 6 and 43% along the [100] mica and [010] mica directions, respectively, cubic GaN phase or 30° rotated domains are scarcely observed in the film. This phenomenon can be attributed to the enhanced surface migration of film precursors due to the large atomically flat terraces and the weak Van der Waals bonding on the mica surface.     

Atomic layer deposition of PbZrO3 thin films

In this paper, we report on the preparation of lead zirconate films for the first time using atomic layer deposition in an attempt to investigate some of the film properties and also to evaluate possible use of the precursor combination to prepare more complex lead titanate zirconate. In the depositions tetraphenyl lead (Ph₄Pb) was used as the lead and zirconium 2,2,6,6-tetramethyl-3,5-heptadionato (Zr(thd)₄) as the zirconium precursor, while ozone was used as the oxygen source. Film growth, stoichiometry and quality were studied using different pulsing ratios at deposition temperatures of 275 and 300 °C. According to X-ray diffraction, the crystalline perovskite phase was observed when films deposited on SrTiO₃(1 0 0) were annealed at 600 °C. Surface roughness was reduced for lead deficient films as well as in annealed samples.     

Growth and thermal stability of epitaxial BiFeO3 thin films

We have investigated the oxygen pressure and the temperature dependence on BiFeO₃ thin films deposited on SrTiO₃ substrates by pulsed laser deposition. Reflection high energy electron diffraction (RHEED), atomic force microscopy (AFM) and X-ray diffraction measurements indicate that high-quality epitaxial thin films are obtained for and T=650 °C. Outside of this pressure-temperature window, parasitic peaks attributed to β-Bi₂O₃ appear. We find an increase of the out-of-plane lattice parameter with oxygen pressure that we ascribe to Bi-deficiency due to its high volatility at low pressure. Ex-situ anneals have been performed and results show that as-grown single-phase BiFeO₃ thin films degrade after annealing, whereas as-grown BiFeO₃ containing impurity phases evolve toward a single-phase structure. These experiments demonstrate that parasitic phases can stabilize compounds which are usually unstable in air at elevated temperatures.     

Diamond-like-carbon films produced by magnetically guided pulsed laser deposition

We have compared the quality of carbon films deposited with magnetically guided pulsed laser deposition (MGPLD) and conventional pulsed laser deposition (PLD). In MGPLD, a curved magnetic field is used to guide the plasma but not the neutral species to the substrate to deposit the films while, in conventional PLD, the film is deposited with a mixture of ions, neutral species and clusters. A KrF laser pulse (248 nm) was focused to intensities of 10 GW/cm² on a carbon source target and a magnetic field strength of 0.3 T was used to steer the plasma around a curved arc to the deposition substrate. Electron energy loss spectroscopy was used in order to measure the fraction of sp³ bonding in the films produced. It is shown that the sp³ fraction, and hence the diamond-like character of the films, increased when deposited only with the pure ion component by MGPLD compared with films produced by the conventional PLD technique. The dependence of film quality on the laser intensity is also discussed. Received: 7 December 2000 / Accepted: 20 August 2001 / Published online: 2 October 2001     

The influence of substrate on the properties of Er2O3 films grown by magnetron sputtering

The structural properties and the room temperature luminescence of Er₂O₃ thin films deposited by RF magnetron sputtering have been studied. Films characterized by good morphological properties have been obtained by using a SiO₂ interlayer between the film and the Si substrate. The evolution of the properties of the Er₂O₃ films due to rapid thermal annealing processes in O₂ ambient performed at temperatures in the range 800-1200 °C has been investigated in details. The existence of well-defined annealing conditions (temperature of 1100 °C or higher) allowing to avoid the occurrence of extensive chemical reactions with the oxidized substrate has been demonstrated and an increase of the photoluminescence (PL) intensity by about a factor of 40 with respect to the as deposited material has been observed. The enhanced efficiency of the photon emission process has been correlated with the longer lifetime of the PL signal. The same annealing processes are less effective when Er₂O₃ is deposited on Si. In this latter case interfacial reactions and pit formation occur, leading to a material characterized by stronger non-radiative phenomena that limit the PL efficiency.     

c-Axis orientation control of YBa2Cu3O7−x films grown on inclined-substrate-deposited MgO-buffered metallic substrates

Biaxially textured YBa₂Cu₃O_7−x (YBCO) films were grown on non-textured metal substrates with inclined-substrate-deposited (ISD) MgO as template. The biaxial texture feature of the films was examined by X-ray pole-figure analysis, φ-scan, and 2θ-scan. A tilt angle of 32° of the MgO[001] with respect to the substrate normal was observed. Epitaxial growth of YBCO films with c-axis tilt angle of 32° with respect to the substrate normal was obtained on these substrates with SrTiO₃(STO) as buffer layer. Whereas, by choosing yttria-stabilized ZrO₂ and CeO₂ instead of STO as buffer layer, a c-axis untilted YBCO film was obtained. Higher values of T_c=91 K and J_c=5.5×10⁵ A/cm² were obtained on the c-axis untilted YBCO films with 0.46 μm thickness at 77 K in zero field. Comparative studies revealed a unique role of CeO₂ in controlling the orientation of the YBCO films grown on ISD-MgO buffered metal substrates.     

Aluminium oxide thin films prepared by plasma-enhanced chemical vapour deposition

Thin films of aluminium oxide have been deposited on glass, quartz, Si(100), steel, nickel, and aluminium by plasma-enhanced chemical vapour deposition (PECVD) using aluminium acetylacetonate (Al(acac)₃) as precursor. The deposits are hard (up to 2370 HK) and show good adherence to the substrates. The influence of various experimental parameters on deposition rate, film composition and hardness has been studied. The bias turned out to be the most effective parameter.On leave from Beijing Solar Energy Research Institute, Beijing, P.R. China     

Magnetic properties of CoFeP films prepared by electroless deposition

Structure and magnetization of CoFeP films prepared by the electroless deposition were systematically investigated by varying the bath composition and deposition parameters to optimize soft magnetic properties. The cobalt content in the CoFeP films varies from 40.4 to 94.9 wt% by controlling the bath composition. Increase of the metallic ratio FeSO₄·7H₂O/(CoSO₄·7H₂O+FeSO₄·7H₂O) affects the films’ microstructure, which switches from amorphous to crystalline structure. The magnetic properties of CoFeP films reveal that the coercivity (H_c) values range from 80 up to 185 A/m and the saturation magnetization (M_s) from 82 to 580 eum/g depending on the bath composition, deposition parameters and heat-treatment conditions. Increase of M_s and remanent magnetization (M_r) as well as decrease of H_c are observed for the CoFeP films with bath pH, temperature and the metallic molar ratio increasing. It is also found that the H_c is enhanced with the increase of NaH₂PO₂·H₂O concentration. CoFeP films showing good soft magnetic properties with coercivities less than 140 A/m and M_s close to 600 emu/g can be obtained in high pH bath and thereafter heat treatment. The deposit is found to be suitable as soft magnetic materials for core materials.     

Formation of Pt-C films by ion beam assisted deposition for the application of suppression thermo-electron emission

Platinum and carbon were deposited onto the surface of molybdenum grids simultaneously by ion beam assisted deposition. The structure of the Pt-C films was studied by XRD and Raman spectroscopy. The XRD results showed that Pt exhibited mixed strong (1 1 1) and weak (2 0 0) orientations. The Raman spectra showed that the carbon existed in the form of graphite-like phase. Electron emission characteristics from the Mo grid with and without Pt-C films were measured using analogous diode method. The results showed that electron emission from the Mo grid coated with Pt-C films was much less than that from the Mo grid without Pt-C films. The obtained results demonstrated that the Pt-C films are effective grid-coating materials for the application of suppression thermo-electron emission.     

Preparation and photocatalytic activity of CeO2/TiO2 interface composite film

The CeO₂/TiO₂ and TiO₂/CeO₂ interface composite films were prepared on glass substrates by the sol-gel process via dip-coating and calcining technique. The scanning electron microscopy (SEM) revealed that the TiO₂ layer has a compact and uniformity glasslike surface with 200 nm in thickness, and the CeO₂ layer has a coarse surface with 240 nm in thickness. The X-ray diffractometer (XRD) analysis showed that the TiO₂ layer is made up of anatase phase, and the CeO₂ layer is structured by cubic fluorite phase. Through a series of photo-degradation experiments, the relationship of the photocatalytic activity with the constituents of the films was studied. In virtue of the efficient interfacial charge separation via the process of electron transfer from TiO₂ to CeO₂, the photocatalytic activity of the CeO₂/TiO₂ composite film is high. Contrarily, the photocatalytic activity of the TiO₂/CeO₂ composite film is low, due to its inert surface made up of CeO₂ with broad bandwidth. Apart from the effect of the film structure, the effect of film thickness on photocatalytic activity was also discussed.     

Enhanced strain relaxation induced by epitaxial layer growth mode of MgO thin films

Growth of MgO films on silicon substrate was conducted by KrF excimer pulsed-laser ablation system. Two kinds of growth mode were revealed in situ by reflection high energy electron diffraction. It was found that the layer growth mode of MgO thin films could remarkably reduce the misfit strain originated from the different lattice constant and thermal expansion coefficiency between MgO films and Si. An enhanced strain relaxation was discovered for MgO films, which were grown with the layer growth mode, in the film thickness range of 40-100 nm. The value of critical thickness for the formation of misfit dislocation agrees well with the calculated one. This exceptional phenomenon should be ascribed to the layer growth mode of epitaxial MgO films.     

Alumina capped ZnO quantum dots multilayer grown by pulsed laser deposition

To extend the applicability of ZnO, with the bulk band gap of about 3.3 eV, into deep UV region, we have grown a multilayer of alumina capped ZnO quantum dots of mean in-plane sizes in the range of ∼1.8-3.6 nm at room temperature using alternate Pulsed Laser Deposition. Size dependent blue shift of the band gap of these dots up to ∼4.5 eV is observed in the optical absorbance spectra. The observed blue shift can be understood using the effective mass approximation in weak and strong confinement regimes.     

Influence of inert gas pressure on deposition rate during pulsed laser deposition

The deposition rates of permalloy and Ag are monitored during pulsed laser deposition in different inert gas atmospheres. Under ultrahigh vacuum conditions, resputtering from the film surface occurs due to the presence of energetic particles in the plasma plume. With increasing gas pressure, a reduction of the particle energy is accompanied with a decrease of resputtering and a rise in the deposition rate for materials with high sputtering yield. In contrast, at higher gas pressures, scattering of ablated material out of the deposition path between target and substrate is observed, leading to a decrease in the deposition rate. While in the case of Xe and Ar these processes strongly overlap, they are best separated in He. A He pressure of about 0.4 mbar should be used to reduce the kinetic energy of the deposited particles, to reach the maximum deposition rate and to avoid implantation of the particles. This is helpful for the preparation of stoichiometric metallic alloy films and multilayers with sharp interfaces. Received: 27 March 2002 / Accepted: 3 April 2002 / Published online: 5 July 2002