Phase equilibria in the system LaMnO<Subscript>3</Subscript>-SrMnO<Subscript>3</Subscript>-SrCrO<Subscript>4</Subscript>-LaCrO<Subscript>3</Subscript>

A continuous solid solution LaMn_1?y Cr _y O₃ with an orthorhombic structure is found to exist in the range of 0.0 ≤ y ≤ 1.0. An orthorhombic solid solution La_1?x Sr _x CrO₃ exists in the range of 0.0 ≤ x ≤ 0.1. The stability boundaries are determined for the perovskite phase La_1?x Sr _x Mn_1?y Cr _y O₃. An isobaric-isothermal section LaMnO₃-SrMnO₃-SrCrO₄-LaCrO₃ of the system La₂O₃-SrO-Mn₃O₄-Cr₂O₃ in air at 1100°C is designed.     

A study of phase formation in the subsolidus region of the system Na<Subscript>2</Subscript>MoO<Subscript>4</Subscript>-MnMoO<Subscript>4</Subscript>-Cr<Subscript>2</Subscript>(MoO<Subscript>4</Subscript>)<Subscript>3</Subscript>

Phase relationships in the subsolidus region of the system Na₂MoO₄-MnMoO₄-Cr₂(MoO₄)₃ were studied by means of X-ray diffraction and differential-thermal analyses. The possibility of obtaining a variablecomposition phase Na_1?x Mn_1?x Cr_1+x (MoO₄)₃ (0 ≤ x ≤ 0.5) and ternary molybdate NaMn₃Cr(MoO₄)₅ was examined. The temperature dependence of the conductivity of the phase Na_1?x Mn_1?x Cr_1+x (MoO₄)₃ was analyzed.     

Phase formation in the Ag<Subscript>2</Subscript>MoO<Subscript>4</Subscript>-MgMoO<Subscript>4</Subscript>-Al<Subscript>2</Subscript>(MoO<Subscript>4</Subscript>)<Subscript>3</Subscript> system

The subsolidus region of the Ag₂MoO₄-MgMoO₄-Al₂(MoO₄)₃ ternary salt system has been studied by X-ray phase analysis. The formation of new compounds Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ (0 ≤ x ≤ 0.4) and AgMg₃Al(MoO₄)₅ has been determined. The Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ variable-composition phase is related to the NASICON type structure (space group R \(\bar 3\) c). AgMg₃Al(MoO₄)₅ is isostructural to sodium magnesium indium molybdate of the same formula unit and crystallizes in triclinic system (space group P \(\bar 1\), Z = 2) with the following unit cell parameters: a = 9.295(7) Å, b = 17.619(2) Å, c = 6.8570(7) Å, α = 87.420(9)°, β = 101.109(9)°, γ = 91.847(9)°. The compounds Ag_{1 ? x} Mg_{1 ? x} Al_{1 + x} (MoO₄)₃ and AgMg₃Al(MoO₄)₅ are thermally stable up to 790 and 820°C, respectively.     

Phase composition,formation parameters,and morphology of precipitates in the LiVO<Subscript>4</Subscript>-VOSO<Subscript>4</Subscript>-H<Subscript>2</Subscript>O system

The phase and chemical compositions of the precipitates formed in the LiVO₃-VOSO₄-H₂O system at initial pH within 1 ≤ pH ≤ 4 and 90°C were studied. The following phases were prepared: an α phase Li_1.4(VO)_1.3[H₂V₁₀O₂₈] · nH₂O and a β phase Li_{0.6 ? x} H_{1.4 + x} [V₁₂O_{31 ? y/2}] · nH₂O (0 ≤ x ≤ 0.5, 1.3 ≤ y ≤ 2.0) with a layered structure. Li_0.4V₂O₅ · H₂O nanorods with the interlayer distance 10.30 ± 0.08 Å were synthesized at 180°C in an autoclave. The morphology, IR spectra, and main formation processes for these polyvanadates were studied.     

Synthesis,structure, and properties of M<Subscript>3</Subscript>VO<Subscript>2</Subscript>(SO<Subscript>4</Subscript>)<Subscript>2</Subscript> (M = Rb,Cs)

Vanadium(V) complexes of general composition M₃VO₂(SO₄)₂ (M = Rb, Cs) were synthesized by a solid-state route. The individuality of the synthesized compounds was proved by X-ray and neutron diffraction, vibrational spectroscopy, and microscopic analysis. The X-ray diffraction patterns of M₃VO₂(SO₄)₂ were indexed to fit the monoclinic system (space group P2/c, Z = 4) with the following unit cell parameters: a = 11.6487(2) Å, b = 8.4469(2) Å, c = 12.1110(2) Å, β = 109.483(1)°, V = 1123.43 ų (Rb); a = 12.0546(3) Å b = 8.7706(2) Å, c = 12.6496(3) Å, β = 109.843(2)°, V = 1257.99 ų (Cs). In the crystal structure of M₃VO₂(SO₄)₂, [VO₂(SO₄)₂]^3? complex anions can be discerned in which the vanadium atom is surrounded by five oxygen atoms: two oxygen atoms form short terminal V–O bonds, and three oxygen atoms are from the two sulfato groups, one of which acts as a monodentate ligand and the other acts as a bidentate chelating ligand.     

High-temperature heat capacity and thermodynamic properties of pyrovanadate Pb<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> and orthovanadate Pb<Subscript>3</Subscript>(VO<Subscript>4</Subscript>)<Subscript>2</Subscript>

The heat capacities of Pb₂V₂O₇ and Pb₃(VO₄)₂ as a function of temperature in the range 350–965 K have been studied by the differential scanning calorimetry method. The C_P = f(T) curve for Pb₂V₂O₇ is described by the equation C_p = (230.76 ± 0.51) + (73.60 ± 0.50)×10^-3T ? (18.38 ± 0.54)×10⁵T^-2 in the entire temperature range. For Pb₃(VO₄)₂, there is a well-pronounced extreme point in the C_P = f(T) curve at T = 371.5 K, which is caused by the existence of a structural phase transition. The thermodynamic properties of the oxide compounds have been calculated.     

Synthesis and crystal structure of two complexes [Cu<Subscript>2</Subscript>(NiL)<Subscript>2</Subscript>Cl<Subscript>4</Subscript>] and [Cd<Subscript>2</Subscript>(CuL)<Subscript>2</Subscript>Cl<Subscript>4</Subscript>]

Macrocyclic and supermolecular complexes [Cu₂(NiL)₂Cl₄] (I) and [Cd₂(CuL)₂Cl₄] (II) (H₂L = 2,3-dioxo-5,6,14,15-dibenzo-1,4,8,12-tetraazacyclo-pentadeca-7,13-diene) have been synthesized and structurally determined by X-ray diffraction and IR spectrum. Complex I crystallizes in the monoclinic system with P2₁/n group, a = 10.9019(15), b = 14.3589(19), c = 12.4748(17) 0A, β = 108.645(2)°, Z = 4. Complex II crystallizes in the monoclinic system with P2₁/n group, a = 10.9784(16), b = 14.580(2), c = 12.8904(18) Å, β = 109.339(2)°, Z = 4.     

Crystal structures of <Emphasis Type="Italic">trans</Emphasis>-[Re<Subscript>6</Subscript>S<Subscript>8</Subscript>(CN)<Subscript>2</Subscript>L<Subscript>4</Subscript>] complexes,L = pyridine or 4-methylpyridine

The structures of three novel octahedral rhenium cluster compounds [Re₆S₈(CN)₂(py)₄]·H₂O (1), [Re₆S₈(CN)₂(4-Mepy)₄] (2), [Re₆S₈(CN)₂(4-Mepy)₄]·4-Mepy (3) (py = pyridine, 4-Mepy = 4-methylpyridine) are determined by X-ray crystallography. Crystal data are: C2/m space group, a = 14.813(1) Å, b = 14.772(1) Å, c = 9.2122(6) Å, β = 119.085(2)°, V = 1761.7(2) ų, d _x = 3.318 g/cm³, R = 0.0585 (1); I4₁/amd space group, a = 16.0018(3) Å, c = 14.7186(5) Å, V = 3768.81(16) ų, d _x = 3.169 g/cm³, R = 0.0489 (2); P2₁/c space group, a = 9.0452(4) Å, b = 15.8065(7) Å, c = 15.2951(6) Å, β = 103.700(2)°, V = 2124.57(16) ų, d _x = 2.957 g/cm³, R = 0.0245 (3). Molecular cluster complexes interact via π-π stacking affording 3D frameworks in 1 and 2 and chains in 3.     

K<Subscript>3</Subscript>VO<Subscript>2</Subscript>(SO<Subscript>4</Subscript>)<Subscript>2</Subscript>: Formation conditions,crystal structure,and physicochemical properties

Potassium oxosulfatovanadate(V) K₃VO₂(SO₄)₂ has been obtained by solid-phase synthesis from K₂SO₄, K₂S₂O₇, and V₂O₅ (2: 1: 1), and its formation conditions, crystal structure, and physiochemical properties have been studied. The conversions of K₃VO₂(SO₄)₂ in contact with potassium vanadates and other potassium oxosulfatovanadates(V) are considered in terms of phase relations in the K₂O-V₂O₅-SO₃ system, which models the active component of vanadium catalysts for sulfur dioxide oxidation into sulfur trioxide. The X-ray diffraction pattern of K₃VO₂(SO₄)₂ is indexed in the monoclinic system (space group P2₁) with unit cell parameters of a = 10.0408(1) Å, b = 7.2312(1) Å, c = 7.3821(1) Å, β = 104.457(1)°, Z = 2, and V = 519.02 ų. The crystal structure of K₃VO₂(SO₄)₂ is built from [VO₂(SO₄)₂]^3? complex anions, in which the vanadium atom is in an octahedral oxygen environment formed by two terminal oxygen atoms (V-O(6) = 1.605(7) Å, V-O(10) = 1.619(7) Å and four oxygen atoms of the two chelating sulfate anions. The vibrational spectra of K₃VO₂(SO₄)₂ are analyzed using these structural data.     

Structure and some properties of [UO<Subscript>2</Subscript>(SeO<Subscript>4</Subscript>)(C<Subscript>5</Subscript>H<Subscript>12</Subscript>N<Subscript>2</Subscript>O)<Subscript>2</Subscript>(H<Subscript>2</Subscript>O)]

The complex [UO₂(SeO₄)(C₅H₁₂N₂O)₂(H₂O)] (I) was synthesized and studied by thermal analysis, IR spectroscopy, and X-ray crystallography. The crystals are orthorhombic: a = 13.1661(3) Å, b = 16.4420(5) Å, c = 17.4548(6) Å, Pbca, Z = 8, R = 0.0423. The structural units of crystal I are chains with the composition coinciding with that of the compounds of the AB₂M ₃ ¹ crystal chemical group of the uranyl complexes (A = UO ₂ ²⁺ , B² = SeO ₄ ^2? , M¹ = C₅H₁₂N₂O and H₂O).     

The synthesis and properties of solid solutions based on Ba<Subscript>4</Subscript>Ca<Subscript>2</Subscript>Nb<Subscript>2</Subscript>O<Subscript>11</Subscript>

(Ba_{1 ? x} Ca _x )₆Nb₂O₁₁ solid solutions were synthesized. The compositions were shown to be single-phase at 0.23 ≤ x ≤ 0.47 and have a double perovskite cubic structure with an incomplete oxygen sublattice. The interaction of solid solutions with water vapor and their electrical properties were studied. In dry atmosphere, these complex oxides were mixed oxygen-hole conductors. In humid atmosphere, they intercalated water and exhibited protonic conductivity. The influence of Ba/Ca isovalent substitution, the dynamics of the oxygen sublattice, and the concentration of intercalated water on the value and contribution of protonic and hole conductivity was analyzed.     

Synthesis,structural, spectral,thermal and comparative biological activity studies of [V<Subscript>2</Subscript>O<Subscript>2</Subscript>(SO<Subscript>4</Subscript>)<Subscript>2</Subscript>(H<Subscript>2</Subscript>O)<Subscript>6</Subscript>]

The hydrothermal reaction of a mixture of V₂O₅, VCl₃, 2,5-pyridinedicarboxylic acid and diluted H₂SO₄ for 68 h at 180°C gives a blue colored solution which yields prismatic blue crystals of IV ₂ ^IV O₂(SO₄)₂(H₂O)₆] (1) in 32% yield (based on V). Complex 1 was investigated by means of elemental analysis (C, H and S), TGA, FT-IR, manganometric titration, Single Crystal X-ray Diffraction Methods and also comparative antimicrobial activities. Crystal data for the compound: monoclinic space group P2₁/c and unit cell parameters are a = 7.3850(12) Å, b = 7.3990(7) Å, c = 12.229(2) Å, β = 108.976(12)° and Z = 2. Although structure of 1 as a natural mineral has been previously determined, this work covers new preparation method and full characterization of 1 along with comparison of antibacterial activity between 1 and the commercial vanadium(IV) oxide sulfate hydrate compounds, VOSO₄ · xH₂O (Riedel-de Haën and Alfa Aesar brand names). 1 was evaluated for the antimicrobial activity against gram-positive, gram-negative bacteria, yeasts and mould compared with the commercial VOSO₄ · xH₂O compounds. 1 showed weak activity against bacteria Bacillus cereus, Nocardia asteroides and yeast Candida albicans. A good antimicrobial activity was recorded against Cirtobacter freundii (15 mm). There are only a few reproducible well-defined vanadium(IV) starting materials to use for exploring the synthesis of new materials. VCl₄, VO(acac)₂, VOSO₄ · xH₂O and [V(IV)OSO₄(H₂O)₄] · SO₄ · [H₂N(C₂H₄)₂NH₂] are common starting materials for such applications. In addition to these compounds, 1 can be used as an oxovanadium precursor.     

Synthesis and crystal structure of a 1D coordination polymer [Cd(NITpPy)<Subscript>2</Subscript>(N(CN)<Subscript>2</Subscript>)<Subscript>2</Subscript>)]<Subscript><Emphasis Type="Italic">n</Emphasis></Subscript>

A novel one-dimensional chain complex [Cd(NITpPy)₂(N(CN)₂)₂)] _n (NITpPy = 2-(4′-pyridyl)-4,4,5,5-tetramethylimidazoline-1-oxyl-3-oxide) has been synthesized and characterized structurally. It crystallizes in the triclinic space group P \(\bar 1\) with a = 7.1742(13), b = 9.4913(17), c = 13.208(2) Å, α = 71.020(2)°, β=87.308(2)°, γ = 70.503(2)°, V = 799.8(3) ų, C₂₈H₃₂CdN₁₂O₄, Mr = 713.06, Z = 1, ρ _c = 1.48 g/cm³, μ(MoK _α) = 0.736 mm^?1, F(000) = 364, R = 0.0275 and wR = 0.0605 for 2702 observed reflections with I > 2σ(I). The crystal structure consists of infinite chains of [Cd(NITpPy)₂(N(CN)₂)₂)] units linked by dicyanamide anions [N(CN)₂]^?. Each Cd²⁺ ion is six-coordinated with the geometry of a distorted octahedron.     

Effect of phosphate doping on electric properties and chemical stability of Ba<Subscript>4</Subscript>Ca<Subscript>2</Subscript>Nb<Subscript>2</Subscript>O<Subscript>11</Subscript> protonic conductor

Conductivity of perovskite phosphate–substituted solid solutions of Ba₄Ca₂Nb_{2 –x} P _x O₁₁ (0.0 ≤ x ≤ 0.5) was studied as a function of temperature, partial pressure of oxygen and water vapors. It is proved that the studied systems are protonic conductors at the temperatures below 600°C in the atmosphere with elevated content of water vapors (pH₂O = 1.92 × 10^–2 atm). Introduction of the tetrahedral [PO₄] group in the complex oxide matrix of Ba₄Ca₂Nb₂O₁₁ results in an increase in the oxygen–ionic (dry air, pH₂O = 1.91 × 10^–4 atm) and protonic conductivities (wet air, pH₂O = 1.92 × 10^–2 atm). Is it found that the doping causes a considerable increase in chemical stability of phases with respect to carbon dioxide.     

A novel metal chalcogenide: HgCd<Subscript>4</Subscript>S<Subscript>5</Subscript>

A novel metal chalcogenide HgCd₄S₅ (1) was synthesized from solid-state reactions and structurally characterized. Compound 1 crystallizes in the space group C222₁ of the orthorhombic system with four formula units in a cell: a = 12.5661(5) Å, b = 7.2551(5) Å, c = 10.7520(7) Å, V = 980.2(1) ų, Cd₄HgS₅, M _r = 810.49, D _c = 5.492 g/cm³, S = 1.010, μ(MoK _α) = 25.128 mm^?1, F(000) = 1408, R = 0.0611 and wR = 0.1495. Compound 1 is characterized by a 3-D cadmium sulfide framework structure with the infinite mercury sulfide chains located in the cavities.     

NaF-CaF<Subscript>2</Subscript>-YbF<Subscript>3</Subscript> phase diagram

Vertical sections CaF₂-Na_0.4Yb_0.6F_2.2 and NaF-Ca_0.75Yb_0.25F_2.25 of the system NaF-CaF₂-YbF₃ were studied by differential thermal analysis. A fluorite solid solution belt between phases of variable composition Ca_1?x Yb _x F_2+x and Na_0.5?x Yb_0.5+x F_2+2x was discovered. A liquidus-surface projection was constructed. The solidification character of the solid solution is unfavorable for growth of optical-quality ternary mixed crystals.     

Uranyl cyanoacetate [UO<Subscript>2</Subscript>(H<Subscript>2</Subscript>O)<Subscript>2</Subscript>(NCCH<Subscript>2</Subscript>COO)<Subscript>2</Subscript>]: Synthesis,crystal structure,and absorption spectra

The U(VI) complex with cyanoacetic acid, [UO₂(H₂O)₂(NCCH₂COO)₂] (I), was synthesized from an aqueous solution, and its X-ray diffraction analysis was carried out. The crystals are orthorhombic: space group Pca2 ₁, a = 25.9605(7) Å, b = 6.7634(2) Å, c = 6.3398(2) Å, V = 1113.15(6) ų at 100 K, and Z = 4. The coordination polyhedron of the uranium atom is a distorted pentagonal bipyramid. The cations UO ₂ ²⁺ are bound into infinite zigzag chains by the bridging carboxyl groups of one of the anions of cyanoacetic acid. The carboxyl oxygen atom of the second anion, which is not involved in coordination, and the nitrogen atoms of the cyano groups form hydrogen bonds with the coordination water molecules. The layer structure of the compound is formed through the hydrogen bonds. The absorption spectra in the visible and infrared ranges of the crystalline compound are measured and analyzed.     

Effects of Cr doping on the electrochemical performance of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> cathode material for lithium ion batteries

A series of Cr-doped Li₃V_2???x Cr _x (PO₄)₃ (x?=?0, 0.1, 0.25, and 0.5) samples are prepared by a sol–gel method. The effects of Cr doping on the physical and chemical characteristics of Li₃V₂(PO₄)₃ are investigated. Compared with the XRD pattern of the undoped sample, the XRD patterns of the Cr-doped samples have no extra reflections, which indicates that Cr enters the structure of Li₃V₂(PO₄)₃. As indicated by the charge–discharge measurements, the Cr-doped Li₃V_2???x Cr _x (PO₄)₃ (x?=?0.1, 0.25, and 0.5) samples exhibit lower initial capacities than the undoped sample at the 0.2 C rate. However, both the discharge capacity and cycling performance at high rates (e.g., 1 and 2 C) are enhanced with proper amount of Cr doping (x?=?0.1). The highest discharge capacity and capacity retention at the rates of 1 and 2 C are obtained for Li₃V_1.9Cr_0.1(PO₄)₃. The improvement of the electrochemical performance can be attributed to the higher crystal stability and smaller particle size induced by Cr doping.     

Crystal structure of [Ir(NH<Subscript>3</Subscript>)<Subscript>5</Subscript>Cl]<Subscript>2</Subscript>[OsCl<Subscript>6</Subscript>]Cl<Subscript>2</Subscript>. Crystal-chemical analysis of the iridium-osmium system

The [Ir(NH₃)₅Cl]₂[OsCl₆]Cl₂ binary complex salt has been prepared, and its structure was investigated by single crystal X-ray diffraction. Crystal data: a = 11.1901(13) Å, b = 7.9138(13) Å, c = 13.4384(18) Å; β = 99.640(3)°, V = 1190.0(2), space group C2/m, Z = 2, FW = 1099.47, d _x = 3.068 g/cm³. Thermolysis products of [Ir(NH₃)₅Cl]₂[OsCl₆]Cl₂, [Ir(NH₃)₅Cl][OsBr₆], (NH₄)₂[OsCl₆]_x[IrCl₆]_1?x , and K₂[OsCl₆]_x[IrCl₆]_1?x were studied by X-ray phase analysis; the unit cell parameters were refined, and the dependence of volume per atom (V/Z) on the composition of the Ir Os_1?x solid solution has been plotted.     

Structural investigation of [Au(en)<Subscript>2</Subscript>]Cl(ReO<Subscript>4</Subscript>)<Subscript>2</Subscript> and [Au(en)<Subscript>2</Subscript>](ReO<Subscript>4</Subscript>)<Subscript>3</Subscript> complexes

Novel complex salts [Au(en)₂]Cl(ReO₄)₂ (I) and [Au(en)₂](ReO₄)₃ (II), en = ethylenediamine, are obtained. Their crystal structures are determined by single crystal X-ray diffraction. Complex I crystallizes in the triclinic crystal system: a = 6.2172(7) Å, b = 7.1644(8) Å, c = 8.8829(8) Å, α = 96.605(4)°, β = 110.000(4)°, γ = 97.802(4)°, P-1 space group, Z = 1, d _x = 3.905 g/cm³; complex II crystallizes in the monoclinic crystal system: a = 15.244(2) Å, b = 7.6809(8) Å, c = 9.3476(12) Å, β = 127.004(3)°, C2 space group, Z = 4, d _x = 4.057 g/cm³.