Structural and electrical characterization of SxSe100−x thin films

Thin films of samples of the glassy S_xSe_100−x system with 0 ≤ x ≤ 7.28 have been prepared by thermal evaporation technique at room temperature (300 K). X-ray investigations show that the structure of pure selenium (Se) does change seriously by the addition of small amount of sulphur S ≤7.28%. The lattice parameters were determined as a function of sulphur content. Results of differential thermal analysis (DTA) of the glassy compositions of the system S_xSe_100−x were discussed. The characteristic temperatures (T_g, T_c and T_m) were evaluated. Dark electrical resistivities, ρ, of S_xSe_100−x thin films with different thicknesses from 100 to 500 nm, were measured in the temperature range from 300 to 423 K. Two distinct linear parts with different activation energies were observed. The variation of electrical resistivity of examined compositions has been discussed as a function of the film thickness, temperature and the sulphur content. The application of Mott model for the phonon assisted hopping of small polarons gave the same two activation energies obtained from the resistivity temperature calculations.     

Electrodeposition of BixSb2−xTey thermoelectric thin films from nitric acid and hydrochloric acid systems

The electrochemical behaviors of Bi^III, Te^IV and Sb^III single ions and their mixtures were investigated in nitric acid and hydrochloric acid system separately. Based on which, Bi_xSb_2−xTe_y thermoelectric films were prepared by potentiostatic electrodeposition from the solutions with different concentrations of Bi^III, Te^IV and Sb^III in the two acid systems. The morphologies, compositions, structures, Seebeck coefficients and resistivities of the deposited thin films were characterized and compared by ESEM (or FESEM), EDS, XRD, Seebeck coefficient measurement system and four-probe resistivity measuring device respectively. The results show that although Bi_xSb_2−xTe_y thermoelectric thin film which structure is consistent with the standard pattern of Bi_0.5Sb_1.5Te₃ can be gained in both of the two acid solutions by adjusting the deposition potential, their morphologies and thermoelectric properties have big differences in different acid solutions.     

Magnetic phase transitions of antiperovskite Mn3−xFexSnC (0.5≤x≤1.3)

The magnetization and electrical resistivity of Mn_3−xFe_xSnC (0.5≤x≤1.3) were measured to investigate the behavior of the complicated magnetic phase transitions and electronic transport properties from 5 to 300 K. The results obtained demonstrate that Fe doping at the Mn sites of Mn₃SnC induces a more complicated magnetic phase transition than that in its parent phase Mn₃SnC from a paramagnetic (PM) state to a ferrimagnetic (FI) state consisting of antiferromagnetic (AFM) and ferromagnetic (FM) components, while, with the change of Fe-doped content and magnetic field, there is a competition between the AFM component and FM component in the FI state. Both the Curie temperature (T_C) and the saturated magnetization M_s increase with increasing x. The FM component region becomes broader with further increasing Fe-doped content x. The external magnetic field easily creates a saturated FM state (and increased T_C) when . Fe doping quenches the negative thermal expansion (NTE) behavior from 200 to 250 K reported in Mn₃SnC.     

Phase stability,elastic, electronic,thermal and optical properties of Ti3Al1−xSixC2 (0≤x≤1): First principle study

The structural parameters with stability upon Si incorporation and elastic, electronic, thermodynamic and optical properties of Ti₃Al_1−xSi_xC₂ (0≤x≤1) are investigated systematically by the plane wave pseudopotential method based on the density functional theory (DFT). The increase of some elastic parameters with increasing Si-content renders the alloys to possess higher compressive and tensile strength. The Vickers hardness value obtained with the help of Mulliken population analysis increases as x is increased from 0 to 1. The solid solutions considered are all metallic with valence and conduction bands, which have a mainly Ti 3d character, crossing the Fermi level. The temperature and pressure dependences of bulk modulus, normalized volume, specific heats, thermal expansion coefficient, and Debye temperature are all obtained through the quasi-harmonic Debye model with phononic effects for T=0−1000 K and P=0−50 GPa. The obtained results are compared with other results available. Further an analysis of optical functions for two polarization vectors reveals that the reflectivity is high in the visible–ultraviolet region up to ∼10.5 eV region showing promise as a good coating material.     

Structural and magnetic properties in Bi1−xRxFeO3 (x=0-1, R=La, Nd, Sm, Eu and Tb) polycrystalline ceramics

A series of rare-earth doped BiFeO₃ samples, Bi_1−xR_xFeO₃ (x=0-1, R=La, Nd, Sm, Eu and Tb), were prepared in this work. X-ray diffraction analysis showed that the structure of rare-earth doped BiFeO₃ was transformed from rhombohedral lattice to orthorhombic one by increasing x. The lattice constants and unit-cell volume decreased with the increasing of the doping content, while both the Néel temperature and magnetization were enhanced. A magnetic phase transition was observed at about 35 K for BiFeO₃. The variation of the magnetization with temperature depended on applied field strength and magnetizing history, which was explained according to the antiferromagnetic exchange interaction between Fe and R sites in Bi_1−xR_xFeO₃(x>0). The magnetocrystalline anisotropy contributed by Fe sublattice gave rise to a large coercivity in Bi_xNd_1−xFeO₃ with an orthorhombic structure.     

Highly active Ce1−xCuxO2 nanocomposite catalysts for the low temperature oxidation of CO

A series of Ce_1−xCu_xO₂ nanocomposite catalysts with various copper contents were synthesized by a simple hydrothermal method at low temperature without any surfactants, using mixed solutions of Cu(II) and Ce(III) nitrates as metal sources. These bimetal oxide nanocomposites were characterized by means of XRD, TEM, HRTEM, EDS, N₂ adsorption, H₂-TPR and XPS. The influence of Cu loading (5-25 mol%) and calcination temperature on the surface area, particle size and catalytic behavior of the nanocomposites have been discussed. The catalytic activity of Ce_1−xCu_xO₂ nanocomposites was investigated using the test of CO oxidation reaction. The optimized performance was achieved for the Ce_0.80Cu_0.20O₂ nanocomposite catalyst, which exhibited superior reaction rate of 11.2 × 10⁻⁴ mmol g⁻¹ s⁻¹ and high turnover frequency of 7.53 × 10⁻² s⁻¹ (1% CO balanced with air at a rate of 40 mL min⁻¹, at 90 °C). No obvious deactivation was observed after six times of catalytic reactions for Ce_0.80Cu_0.20O₂ nanocomposite catalyst.     

Structure and electrical properties of Bi5GexSe95−x thin films

Bi₅Ge_xSe_95−x (30, 35, 40 and 45 at.%) thin films of thickness 200 nm were prepared on glass substrates by the thermal evaporation technique. The influence of composition and annealing temperature, on the structural and electrical properties of Bi₅Ge_xSe_95−x films was investigated systematically using X-ray diffraction (XRD), energy dispersive X-ray analysis (EDX). The XRD patterns showed that the as-prepared films were amorphous in nature with few tiny crystalline peaks of relatively low intensity for 30 and 45 at.% and the Bi₅Ge₄₀Se₅₅ annealed film was polycrystalline. The chemical composition of the Bi₅Ge₃₀Se₆₅ film has been checked using energy dispersive X-ray spectroscopy (EDX). The electrical conductivity was measured in the temperature range 300-430 K for the studied compositions. The effect of composition on the activation energy (ΔE) and the density of localized states at the Fermi level N(E_F) were studied, moreover the electrical conductivity was found to increase with increasing the annealing temperature and the activation energy was found to decrease with increasing the annealing temperature. The results were discussed on the basis of amorphous-crystalline transformations.     

Structural, optical and electrical properties of Zn1−xCdxO thin films prepared by PLD

Ternary polycrystalline Zn_1−xCd_xO semiconductor films with cadmium content x ranging from 0 to 0.23 were obtained on quartz substrate by pulse laser deposited (PLD) technique. X-ray diffraction measurement revealed that all the films were single phase of wurtzite structure grown on c-axis orientation with its c-axis lattice constant increasing as the Cd content x increasing. Atomic force microscopy observation revealed that the grain size of Zn_1−xCd_xO films decreases continuously as the Cd content x increases. Both photoluminescence and optical measurements showed that the band gap decreases from 3.27 to 2.78 eV with increasing the Cd content x. The increase in Cd content x also leads to the broadening of the emission peak. The resistivity of Zn_1−xCd_xO films decreases evidently for higher values of Cd content x. The shift of PL emission to visible light as well as the decrease of resistivity makes the Zn_1−xCd_xO films potential candidate for optoelectronic device.     

Effect of substrate temperature on the morphology, structural and optical properties of Zn1−xCoxO thin films

Zn_1−xCo_xO thin films with c-axis preferred orientation were deposited on sapphire (0 0 0 1) by pulsed laser deposition (PLD) technique at different substrate temperatures in an oxygen-deficient ambient. The effect of substrate temperature on the microstructure, morphology and the optical properties of the Zn_1−xCo_xO thin films was studied by means of X-ray diffraction (XRD), atomic force microscopy (AFM), UV-visible-NIR spectrophotometer, fluorescence spectrophotometer. The results showed that the crystallization of the films was promoted as substrate temperature rose. The structure of the samples was not distorted by the Co incorporating into ZnO lattice. The surface roughness of all samples decreased as substrate temperature increased. The Co concentration in the film was higher than in the target. Emission peak near band edge emission of ZnO from the PL spectra of the all samples was quenched because the dopant complexes acted as non-radiative centers. While three emission bands located at 409 nm (3.03 eV), 496 nm (2.5 eV) and 513 nm (2.4 eV) were, respectively, observed from the PL spectra of the four samples. The three emission bands were in relation to Zn interstitials, Zn vacancies and the complex of V_O and Zn_i (V_OZn_i). The quantity of the Zn interstitials maintained invariable basically, while the quantity of the V_OZn_i slightly decreased as substrate temperature increased.     

Structural and optical properties of an InxGa1−xN/GaN nanostructure

The structural and optical properties of an In_xGa_1−xN/GaN multi-quantum well (MQW) were investigated by using X-ray diffraction (XRD), atomic force microscopy (AFM), spectroscopic ellipsometry (SE) and photoluminescence (PL). The MQW structure was grown on c-plane (0 0 0 1)-faced sapphire substrates in a low pressure metalorganic chemical vapor deposition (MOCVD) reactor. The room temperature photoluminescence spectrum exhibited a blue emission at 2.84 eV and a much weaker and broader yellow emission band with a maximum at about 2.30 eV. In addition, the optical gaps and the In concentration of the structure were estimated by direct interpretation of the pseudo-dielectric function spectrum. It was found that the crystal quality of the InGaN epilayer is strongly related with the Si doped GaN layer grown at a high temperature of 1090 °C. The experimental results show that the growth MQW on the high-temperature (HT) GaN buffer layer on the GaN nucleation layer (NL) can be designated as a method that provides a high performance InGaN blue light-emitting diode (LED) structure.     

Properties of MgxZn1−xO thin films sputtered in different gases

Mg_xZn_1−xO alloy films were prepared on sapphire substrates using Ar and N₂ as the sputtering gases. The effect of the sputtering gas on the structural, optical and electrical properties of the Mg_xZn_1−xO films was studied. By using N₂ as the sputtering gas, the Mg_xZn_1−xO film shows p-type conductivity and the band gap is larger than that employing Ar as the sputtering gas. The reason for this phenomenon is thought to be related to the reaction between N-O or N-Zn, and the N-doping.     

Characterization and properties of ZnO1−xSx alloy films fabricated by radio-frequency magnetron sputtering

A series of ZnO_1−xS_x alloy films (0 ≤ x ≤ 1) were grown on quartz substrates by radio-frequency (rf) magnetron sputtering of ZnS ceramic target, using oxygen and argon as working gas. X-ray diffraction measurement shows that the ZnO_1−xS_x films have wurtzite structure with (0 0 2) preferential orientation in O-rich side (0 ≤ x ≤ 0.23) and zinc blende structure with (1 1 1) preferential orientation in S-rich side (0.77 ≤ x ≤ 1). However, when the S content is in the range of 0.23 < x < 0.77, the ZnO_1−xS_x film consists of two phases of wurtzite and zinc blende or amorphous ZnO_1−xS_x phase. The band gap energy of the films shows non-linear dependence on the S content, with an optical bowing parameter of about 2.9 eV. The photoluminescence (PL) measurement reveals that the PL spectrum of the wurtzite ZnO_1−xS_x is dominated by visible band and its PL intensity and intensity ratio of UV to visible band decrease greatly compared with undoped ZnO. All as-grown ZnO_1−xS_x films behave insulating, but show n-type conductivity for w-ZnO_1−xS_x and maintain insulating properties for β-ZnO_1−xS_x after annealed. Mechanisms of effects of S on optical and electrical properties of the ZnO_1−xS_x alloy are discussed in the present work.     

Magnetic properties of the Lu2Fe17−xMnx single crystals

Magnetic properties of the single-crystalline Lu₂Fe_17−xMn_x compounds, in which x=0, 0.5, and 2, with the Th₂Ni₁₇-type crystal structure are reported. The Lu₂Fe_17−xMn_x compounds with x=0 and 0.5 are ferromagnets at low temperatures and antiferromagnets at high temperatures. The compound with x=2 is always a ferromagnet. The easy-plane magnetic anisotropy in the Lu₂Fe_17−xMn_x ferromagnets drastically weakens with increase in Mn content up to x=2. The temperature dependence of the first magnetic anisotropy constant was obtained and compared with the single-ion model prediction.     

Structural,optical, FTIR and photoluminescence properties of Zn0.96−xCo0.04CuxO (x=0.03, 0.04 and 0.05) nanopowders

Un-hydrogenated and hydrogenated Cu, Co co-doped ZnO (Zn_0.96−xCo_0.04Cu_xO, x=0.03, 0.04 and 0.05) nanopowders have been synthesized by co-precipitation method. The synthesized samples have been characterized by powder X-ray diffraction, energy dispersive X-ray spectra, UV–Visible spectrophotometer and Fourier transform infrared spectroscopy. The calculated average crystalline size increases from 37.3 to 50.6 nm for un-hydrogenated samples from x=0.03 to 0.05 and it changes from 29.4 to 34.9 nm for hydrogenated samples. The change in lattice parameters, micro-strain, a small shift of X-ray diffraction peaks towards lower angles and reduction in energy gap reveal the substitution of Cu²⁺ ions into Zn–Co–O lattice. The hydrogenation effect reduces the particle size and induces the more uniform distribution of particles than the un-hydrogenated samples which is confirmed by SEM micrographs. Photoluminescence spectra of Zn_0.96−xCo_0.04Cu_xO system shows that red shift in near band edge ultraviolet emission from 393 to 403 nm with suppressing intensity and a blue shift in green band emission from 537 to 529 nm with enhancing intensity confirms the substitution of Cu into the Zn–Co–O lattice.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Magnetic properties and room-temperature magnetocaloric effect in the doped antipervoskite compounds Ga1−xAlxCMn3 (0≤x≤0.15)

We report the effects of Al doping on the structure, magnetic properties, and magnetocaloric effect of antiperovskite compounds Ga_1−xAl_xCMn₃ (0≤x≤0.15). Partial substitutions of Al for Ga enhance the Curie temperature (from 250 K for x=0.0 to 312 K for x=0.15) and the saturation magnetization. On increasing the doping level x, the maximum values of the magnetic entropy change (−ΔS_M) decreases while the temperature span of −ΔS_M vs. T plot broadens. Furthermore, the relative cooling power (RCP) is also studied. For 20 kOe, the RCP value tends to saturate at a high doping level (for x=0.12, 119 J/kg at 296 K). However, at 45 kOe, the RCP value increases quickly with increasing x (for x=0.15, 293 J/kg at 312 K). Considering the relatively large RCP and inexpensive raw materials, Ga_1−xAl_xCMn₃ may be alternative candidates for room-temperature magnetic refrigeration.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Theoretical research on optical properties and quantum efficiency of Ga1−xAlxN photocathodes

In order to design the optimal component structure of transmission-mode (t-mode) Ga_1−xAl_xN photocathode, the optical properties and quantum efficiency of Ga_1−xAl_xN photocathodes are simulated. Based on thin film principle, optical model of t-mode Ga_1−xAl_xN photocathodes is built. And the quantum efficiency formula is put forward. Results show that Ga_1−xAl_xN photocathodes can satisfy the need of detectors with “solar blind” property when the Al component is bigger than 0.375. There is an optimal thickness of Ga_1−xAl_xN layer to get highest quantum efficiency, and the optimal thickness is 0.3 μm. There is close relation between absorptivity and quantum efficiency, which is in good agreement with the “three-step” model. This work gives a reference for the experimental research on the Ga_1−xAl_xN photocathodes.     

Annealing effect on the structural and optical properties of a Cd1−xZnxS thin film for photovoltaic applications

Herein is a report of a study on a Cd_1−xZn_xS thin film grown on an ITO substrate using a chemical bath deposition technique. The as-deposited films were annealed in air at 400 °C for 30 min. The composition, surface morphology and structural properties of the as-deposited and annealed Cd_1−xZn_xS thin films were studied using EDX, SEM and X-ray diffraction techniques. The annealed films have been observed to possess a crystalline nature with a hexagonal structure. The optical absorption spectra were recorded within the range of 350-800 nm. The band gap of the as-deposited thin films varied from 2.46 to 2.62 eV, whereas in the annealed film these varied from 2.42 to 2.59 eV. The decreased band gap of the films after annealing was due to the improved crystalline nature of the material.     

Thickness study of Al:ZnO film for application as a window layer in Cu(In1−xGax)Se2 thin film solar cell

Structural, electrical and optical properties of Al doped ZnO (Al:ZnO) thin film of various thicknesses, grown by radio-frequency magnetron sputtering system were studied in relation to the application as a window layer in Cu(In_1−xGa_x)Se₂ (CIGS) thin film solar cell. It was found that the electrical and structural properties of Al:ZnO film improved with increasing its thickness, however, the optical properties degraded. The short circuit current density, J_sc of the fabricated CIGS based solar cells was significantly influenced by the variation of the Al:ZnO window layer thickness. Best efficiency was obtained when CIGS solar cell was fabricated with electrically and optically optimized Al:ZnO window layer.