Organosoluble and light‐colored fluorinated polyimides from 4,4′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl and aromatic dianhydrides

A novel fluorinated diamine monomer based on 4,4′‐biphenol was synthesized via a straightforward, high‐yielding two‐step procedure. 4,4′‐Biphenol was reacted with 2‐chloro‐5‐nitrobenzotrifluoride in the presence of potassium carbonate to yield the intermediate dinitro compound, which was subsequently reduced to afford the fluorinated diamine, 4,4′‐bis(4‐amino‐3‐trifluoromethylphenoxy)biphenyl. A series of organosoluble fluorinated polyimides were prepared from the diamine with various aromatic dianhydrides via a conventional two‐step thermal imidization method. All polyimides were soluble in strong dipolar solvents such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylacetamide. The polyimides showed excellent thermal and thermooxidative stability and good mechanical properties. No significant weight loss was observed below a temperature of 520 °C in nitrogen or in air, and the glass‐transition temperatures ranged from 247 to 313 °C. Low dielectric constants (2.57–3.65 at 10 kHz), low moisture absorption (0.1–0.7 wt %), and low color intensity were also observed. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 524–534, 2002; DOI 10.1002/pola.10113     

Soluble fluorinated polyimides derived from 1,4‐ (4′‐aminophenoxy)‐2‐(3′‐trifluoromethylphenyl)benzene and aromatic dianhydrides

New fluorinated aromatic polyimides were prepared from 1,4‐(4′‐aminophenoxy)‐2‐(3′‐trifluoromethylphenyl)benzene and aromatic dianhydrides via the polycondensation of one‐step high‐temperature and two‐step thermal or chemical imidization methods. Experimental results indicated that some of the polyimides were soluble both in strong dipolar solvents (N‐methyl‐2‐pyrrolidone or N,N‐dimethylacetamide) and in common organic solvents such as tetrahydrofuran, CHCl₃, and acetone. The polyimides showed exceptional thermal and thermooxidative stability and good mechanical properties. No weight loss was detected before a temperature of 520 °C in nitrogen, and the glass‐transition temperatures ranged from 208 to 251 °C. Low dielectric constants (2.55–2.71 at 1 MHz), low refractive indices, and low water absorption were also observed. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2404–2413, 2001     

Synthesis and properties of aromatic polyimides derived from 2,2,′3,3′‐biphenyltetracarboxylic dianhydride

2,2,′3,3′‐Biphenyltetracarboxylic dianhydride (2,2,′3,3′‐BPDA) was prepared by a coupling reaction of dimethyl 3‐iodophthalate. The X‐ray single‐crystal structure determination showed that this dianhydride had a bent and noncopolanar structure, presenting a striking contrast to its isomer, 3,3,′4,4′‐BPDA. This dianhydride was reacted with aromatic diamines in a polar aprotic solvent such as N,N‐dimethylacetamide (DMAc) to form polyamic acid intermediates, which imidized chemically to polyimides with inherent viscosities of 0.34–0.55 dL/g, depending on the diamine used. The polyimides from 2,2,′3,3′‐BPDA exhibited a good solubility and were dissolved in polar aprotic solvents and polychlorocarbons. These polyimides have high glass transition temperatures above 283°C. Thermogravimetric analyses indicated that these polyimides were fairly stable up to 500°C, and the 5% weight loss temperatures were recorded in the range of 534–583°C in nitrogen atmosphere and 537–561°C in air atmosphere. All polyimides were amorphous according to X‐ray determination. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1425–1433, 1999     

New organo‐soluble aromatic polyimides based on 3,3′,5,5′‐tetrabromo‐2,2‐bis[4‐(3,4‐dicarboxyphenoxy)phenyl]propane dianhydride and aromatic diamines

New aromatic tetracarboxylic dianhydride, having isopropylidene and bromo‐substituted arylene ether structure 3,3′,5,5′‐tetrabromo‐2,2‐bis[4‐(3,4‐dicarboxyphenoxy)phenyl]propane dianhydride, was synthesized by the reaction of 4‐nitrophthalonitrile with 3,3′,5,5′‐tetrabromobisphenol A, followed by alkaline hydrolysis of the intermediate bis(ether dinitrile) and subsequent dehydration of the resulting bis(ether diacid). The novel aromatic polyetherimides having inherent viscosities up to 1.04 dL g⁻¹ were obtained by either a one‐step or a conventional two‐step polymerization process starting from the bis(ether anhydride) and various aromatic diamines. All the polyimides showed typical amorphous diffraction patterns. Most of the polyimides were readily soluble in common organic solvents such as N,N‐dimethylacetamide (DMAc), N‐methyl‐2‐pyrrolidone (NMP), pyridine, and even in less polar solvents like chloroform and tetrahydrofuran (THF). These aromatic polyimides had glass transition temperatures in the range of 256–303°C, depending on the nature of the diamine moiety. Thermogravimetric analysis (TGA) showed that all polymers were stable, with 10% weight loss recorded above 470°C in nitrogen. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1673–1680, 1999     

Synthesis and characterization of soluble polyimides derived from 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride

The synthesis of aromatic poly(ether imide)s containing spirobifluorene units in the polymer backbone is described. 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride, which was used as a new monomer, was synthesized with 2,2′‐dihydroxy‐9,9′‐spirobifluorene as the starting material. In the spiro‐segment, the rings of the connected bifluorene were orthogonally arranged. This bis(ether anhydride) monomer was employed in reactions with a variety of aromatic diamines to furnish poly(ether imide)s, involving an initial ring‐opening polycondensation and subsequent chemically induced cyclodehydration. Excellent solubility in common organic solvents at room temperature, good optical transparency, and high thermal stability are the prominent characteristic features of these new polymers, which can be attributed to the presence of spiro‐fused orthogonal bifluorene segments along the polymer chain. The glass‐transition temperatures of the polyimides were 240–293 °C, and the 5% weight‐loss temperatures were greater than 500 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 262–268, 2002     

Synthesis and properties of new soluble aromatic polyamides and polyimides on the basis of N,N′‐bis(3‐aminobenzoyl)‐N,N′‐diphenyl‐1,4‐phenylenediamine

A new N‐phenylated amide (N‐phenylamide) unit containing aromatic diamine, N,N′‐bis(3‐aminobenzoyl)‐N,N′‐diphenyl‐1,4‐phenylenediamine, was prepared by the condensation of N,N′‐diphenyl‐1,4‐phenylenediamine with 3‐nitrobenzoyl chloride, followed by catalytic reduction. Two series of organosoluble aromatic poly(N‐phenylamide‐imide)s and poly(N‐phenylamide‐amide)s with inherent viscosities of 0.58–0.82 and 0.56–1.21 dL/g were prepared by a conventional two‐stage method and the direct phosphorylation polycondensation, respectively, from the diamine with various aromatic dianhydrides and aromatic dicarboxylic acids. All polyimides and polyamides are amorphous and readily soluble in many organic solvents such as N,N‐dimethylacetamide and N‐methyl‐2‐pyrrolidone. These polymers could be solution cast into transparent, tough, and flexible films with high tensile strengths. These polyimides and polyamides had glass‐transition temperatures in the ranges of 230–258 and 196–229 °C, respectively. Decomposition temperatures of the polyimides for 10% weight loss all occurred above 500 °C in both nitrogen and air atmospheres. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2564–2574, 2002     

Novel,organosoluble, light‐colored fluorinated polyimides based on 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl or 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl

Two series of fluorinated polyimides were prepared from 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl ( 2 ) and 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl ( 4 ) with various aromatic dianhydrides via a conventional, two‐step procedure that included a ring‐opening polyaddition to give poly(amic acid)s, followed by chemical or thermal cyclodehydration. The inherent viscosities of the polyimides ranged from 0.54 to 0.73 and 0.19 to 0.36 dL/g, respectively. All the fluorinated polyimides were soluble in many polar organic solvents, such as N,N‐dimethylacetamide and N‐methylpyrrolidone, and afforded transparent and light‐colored films via solution‐casting. These polyimides showed glass‐transition temperatures in the ranges of 222–280 and 257–351 °C by DSC, softening temperatures in the range of 264–301 °C by thermomechanical analysis, and a decomposition temperature for 10% weight loss above 520 °C both in nitrogen and air atmospheres. The polyimides had low moisture absorptions of 0.23–0.58%, low dielectric constants of 2.84–3.61 at 10 kHz, and an ultraviolet–visible absorption cutoff wavelength at 351–434 nm. Copolyimides derived from the same dianhydrides with an equimolar mixture of 4,4′‐oxydianiline and diamine 2 or 4 were also prepared and characterized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2416–2431, 2004     

Polyimides based on 2,5‐bis(4‐aminophenoxy)biphenyl

A diamine monomer II , 2,5‐bis(4‐aminophenoxy)biphenyl, was prepared through a nucleophilic substitution reaction of phenylhydroquinone and p‐chloronitrobenzene in the presence of potassium carbonate in N,N‐dimethylformamide, followed by catalytic reduction with hydrazine and Pd/C. A series of all‐aromatic, organosoluble polyimides bearing pendent phenyl groups were synthesized from the diamine with six kinds of commercial dianhydrides via a conventional two‐stage process. For improving solubility of polypyromellitimide, copolypyromellitimides with arbitrary solubilities were prepared from II and a pair of dianhydrides, which were mixed at certain molar ratios. These polymers showed good solubilities in N‐methyl‐2‐pyrrolidone and m‐cresol. The softening temperatures of these polyimides were recorded between 206 and 269 °C. Polymers had glass‐transition temperatures at 230–286 °C and 10% weight‐loss temperatures above 521 °C in air or nitrogen atmospheres. Their films had high tensile moduli and strengths. Excellent properties of these polyimides are attributed to the incorporation of the pendent phenyl group in diamine II . © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 429–438, 2002; DOI 10.1002/pola.10116     

Synthesis and characterization of polyimides derived from (3‐amino‐2,4,6‐trimethylphenyl)‐(3′‐aminophenyl)methanone and aromatic dianhydrides

A series of new polyimides were prepared via the polycondensation of (3‐amino‐2,4,6‐trimethylphenyl)‐(3′‐aminophenyl)methanone and aromatic dianhydrides, that is, 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA), 4,4′‐oxydiphthalic anhydride, 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride, and 2,2′‐bis(3,4‐dicarboxyphenyl) hexafluoropropane dianhydride. The structures of the polyimides were characterized by Fourier transform infrared and NMR measurements. The properties were evaluated by solubility tests, ultraviolet–visible analysis, differential scanning calorimetry, and thermogravimetric analysis. The two different meta‐position‐located amino groups with respect to the carbonyl bridge in the diamine monomer provided it with an unsymmetrical structure. This led to a restriction on the close packing of the resulting polymer chains and reduced interchain interactions, which contributed to the solubility increase. All the polyimides except that derived from BPDA had good solubility in strong aprotic solvents, such as N‐methyl‐2‐pyrrolidinone, N,N′‐dimethylacetamide, N,N‐dimethylformamide, and dimethyl sulfone, and in common organic solvents, such as cyclohexanone and chloroform. In addition, these polyimides exhibited high glass‐transition values and excellent thermal properties, with an initial thermal decomposition temperature above 470 °C and glass‐transition temperatures in the range of 280–320 °C. The polyimide films also exhibited good transparency in the visible‐light region, with transmittance higher than 80% at 450 nm and a cutoff wavelength lower than 370 nm. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1291–1298, 2006     

Synthesis and properties of polyimides derived from 9,10‐dialkyloxy‐1,2,3,4,5,6,7,8‐octahydro‐2,3,6,7‐anthracenetetracarboxylic 2,3:6,7‐dianhydrides

A series of new polyimides containing alicyclic units and alkyloxy side chains were prepared from 9,10‐dialkyloxy‐1,2,3,4,5,6,7,8‐octahydro‐2,3,6,7‐anthracenetetracarboxylic 2,3:6,7‐dianhydrides and various aromatic diamines. Their physical properties and structures were investigated. Polymers were obtained with inherent viscosities of 0.24–0.53 dL/g. In comparison with the aromatic polyimides, most polymers were readily soluble in common organic solvent such as N‐methylpyrrolidone and m‐cresol. These polymers had glass‐transition temperatures between 111 and 296 °C depending on the structure of the repeating unit and 10% weight‐loss temperatures of 418–477 °C in nitrogen. Wide‐angle X‐ray diffractometry for as‐polymerized samples revealed very low crystallinity and layered structures, which were better developed in the polymers with longer side chains. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1764–1774, 2002     

Synthesis and properties of fluorinated polyimides from a new unsymmetrical diamine: 1,4‐(2′‐Trifluoromethyl‐4′,4′‐diaminodiphenoxy)benzene

A new aromatic, unsymmetrical ether diamine with a trifluoromethyl pendent group, 1,4‐(2′‐trifluoromethyl‐4′,4″‐diaminodiphenoxy)benzene, was successfully synthesized in three steps with hydroquinone as a starting material and polymerized with various aromatic tetracarboxylic acid dianhydrides, including 4,4′‐oxydiphthalic anhydride, 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride, 2,2′‐bis(3,4‐dicarboxyphenyl)‐hexafluoropropane dianhydride, and pyromellitic dianhydride, via a conventional two‐step thermal or chemical imidization method to produce a series of fluorinated polyimides. The polyimides were characterized with solubility tests, viscosity measurements, IR, ¹H NMR, and ¹³C NMR spectroscopy, X‐ray diffraction studies, and thermogravimetric analysis. The polyimides had inherent viscosities of 0.56–0.77 dL/g and were easily dissolved in both polar, aprotic solvents and common, low‐boiling‐point solvents. The resulting strong and flexible polyimide films exhibited excellent thermal stability, with decomposition temperatures (at 5% weight loss) above 522 °C and glass‐transition temperatures in the range of 232–272 °C. Moreover, the polymer films showed outstanding mechanical properties, with tensile strengths of 74.5–121.7 MPa, elongations at break of 6–13%, and initial moduli of 1.46–1.95 GPa, and good dielectric properties, with low dielectric constants of 1.82–2.53 at 10 MHz. Wide‐angle X‐ray diffraction measurements revealed that these polyimides were predominantly amorphous. These outstanding combined features ensure that the polymers are desirable candidate materials for advanced microelectronic applications. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6836–6846, 2006     

Synthesis and properties of soluble aromatic polyimides from 2,2′-bis(3,4-dicarboxyphenoxy)-1,1′-binaphthyl dianhydride and aromatic diamines

Aromatic tetracarboxylic dianhydride having crank and twisted noncoplanar structure, 2,2′-bis(3,4-dicarboxyphenoxy)-1,1′-binaphthyl dianhydride, was synthesized by the reaction of 4-nitrophthalonitrile with 2,2′-dihydroxy-1,1′-binaphthyl, followed by alkaline hydrolysis of the intermediate bis(ether dinitrile) and subsequent dehydration of the resulting bis(ether diacid). Binaphthyl-2,2′-diyl–containing novel aromatic polyimides having inherent viscosities up to 0.67 dL/g were obtained by the one-step polymerization process starting from the bis(ether anhydride) and various aromatic diamines. All the polyimides showed typical amorphous diffraction patterns. Most of the polyimides were readily soluble in common organic solvents such as N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), and pyridine. These aromatic polyimides had glass transition temperatures in the range of 280–350°C, depending on the nature of the diamine moiety. All polymers were stable up to 400°C, with 10% weight loss being recorded above 485°C in air. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 1937–1943, 1998     

Photoimageable polyimides derived from α,α‐(4‐amino‐3,5‐dimethylphenyl)phenylmethane and aromatic dianhydride

Soluble and inherent photoimageable polyimides with improved photopatterning features were prepared from α,α‐(4‐amino‐3,5‐dimethylphenyl)phenylmethane and 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride. The polyimides possessed good combined chemical and physical properties: thermal stability was observed, with an initial thermal decomposition temperature of 565 °C and a high glass‐transition temperature of 318 °C. Homogeneous polyimide solutions in common organic solvents with solid contents as high as 20 wt % were prepared. These solutions had a shelf life greater than 3 months. The polyimides had high electric insulating properties and low dielectric constants and dissipation factors. Fine patterns were processed by direct exposure of the polyimide coatings to UV i‐line, followed by development with an organic developer. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3012–3020, 2002     

Preparation and properties of molecular‐weight‐controlled polyimides derived from 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene and 4,4′‐oxydiphthalic anhydride

A series of molecular‐weight‐controlled fluorinated aromatic polyimides were synthesized through the polycondensation of a fluorinated aromatic diamine, 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene, with 4,4′‐oxydiphthalic anhydride in the presence of phthalic anhydride as the molecular‐weight‐controlling and end‐capping agent. Experimental results demonstrated that the resulting polyimides could melt at temperatures of 250–300 °C to give high flowing molten fluids, which were suitable for melt molding to give strong and flexible polyimide sheets. Moreover, the aromatic polyimides also showed good solubility both in polar aprotic solvents and in common solvents. Polyimide solutions with solid concentrations higher than 25 wt % could be prepared with relatively low viscosity and were stable in storage at the ambient temperature. High‐quality polyimide films could be prepared via the casting of the polyimide solutions onto glass plates, followed by baking at a relatively low temperature. The molten behaviors and organosolubility of the molecular‐weight‐controlled aromatic polyimides depended significantly on the polymer molecular weights. Both the melt‐molded polyimide sheets and the solution‐cast polymer films exhibited outstanding combined mechanical and thermal properties. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1997–2006, 2006     

High solubility,low‐dielectric constant,and optical transparency of novel polyimides derived from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4″‐isopropyltoluene

A series of novel polyimides (PIs) ( 3a–d ) were prepared from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4 ″ ‐isopropyltoluene ( 1 ) with four aromatic dianhydrides via a one‐step high temperature polycondensation procedure. The obtained PIs showed excellent solubility, with most of them dissoluble at a concentration of 10 wt % in amide polar solvents and chlorinated solvents. Their films were nearly colorless and exhibited high‐optical transparency, with the UV cutoff wavelength in the range of 328–353 nm and the transparency at 450 nm >80%. They also showed low‐dielectric constant (2.49–2.94 at 1 MHz) and low‐water absorptions (0.44–0.65%). Moreover, these PIs possessed high‐glass transition temperatures (T_g) beyond 327 °C and excellent thermal stability with 10% weight loss temperatures in the range of 530–555 °C in nitrogen atmosphere. In comparison with some fluorinated poly(ether imide)s derived from the trifluoromethyl‐substituted bis(ether amine)s, the resultant PIs 3a–d showed better solubility, lower cutoff wavelength, and higher T_g. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3309–3317, 2009     

Synthesis of highly refractive and transparent polyimides derived from 4,4′‐thiobis[2″,6″‐dimethyl‐4″‐(p‐phenylenesulfanyl)aniline]

New sulfur‐containing aromatic diamines with methyl groups at the ortho position of amino groups have been developed to prepare highly refractive and transparent aromatic polyimides (PIs) in the visible region. All aromatic PIs derived from 4,4′‐thiobis[2″‐methyl‐4″‐(p‐phenylenesulfanyl)aniline ( 2 ), 4,4′‐thiobis[2,″6″‐dimethyl‐4″‐(p‐phenylenesulfanyl)aniline ( 5 ), and aromatic dianhydride, 4,4′‐[p‐thiobis(phenylenesulfanyl)]diphthalic anhydride ( 6 ) were prepared via a two‐step polycondensation. All PIs showed good thermal properties, such as 10% weight loss temperature in the range of 497–500 °C and glass transition temperatures above 196 °C. In addition, the PIs showed good optical properties, such as optical transparency above 75% at 450 nm with a 10‐μm film thickness, high refractive indices ranging from 1.7135 to 1.7301, and small in‐plane/out‐of‐plane birefringences between 0.0066 and 0.0076. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 656–662, 2010     

Synthesis and Characterization of Fluorinated Polyimide Derived from 3,3′‐Diisopropyl‐4,4′‐diaminodiphenyl‐3′′,4′′‐difluorophenylmethane

A novel aromatic diamine monomer, 3,3′‐diisopropyl‐4,4′‐diaminodiphenyl‐3′′,4′′‐difluorophenylmethane (PAFM), was successfully synthesized by coupling of 2‐isopropylaniline and 3,4‐difluorobenzaldehyde. The aromatic diamine was adopted to synthesize a series of fluorinated polyimides by polycondensation with various dianhydrides: pyromellitic dianhydride (PMDA), 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA), 4,4′‐oxydiphthalic anhydride (ODPA) and 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA) via the conventional one‐step method. These polyimides presented excellent solubility in common organic solvents, such as N,N‐dimethylformamide (DMF), N,N‐dimethyl acetamide (DMAc), dimethyl sulfoxide (DMSO), N‐methyl‐2‐pyrrolidone (NMP), chloroform (CHCl₃), tetrahydrofuran (THF) and so on. The glass transition temperatures (T_g) of fluorinated polyimides were in the range of 260–306°C and the temperature at 10% weight loss in the range of 474–502°C. Their films showed the cut‐off wavelengths of 330–361 nm and higher than 80% transparency in a wavelength range of 385–463 nm. Moreover, polymer films exhibited low dielectric properties in the range of 2.76–2.96 at 1 MHz, as well as prominent mechanical properties with tensile strengths of 66.7–97.4 MPa, a tensile modulus of 1.7–2.1 GPa and elongation at break of 7.2%–12.9%. The polymer films also showed outstanding hydrophobicity with the contact angle in the range of 91.2°–97.9°.     

Preparation and properties of new soluble aromatic polyimides from 2,2′-bis(3,4-dicarboxyphenoxy)biphenyl dianhydride and aromatic diamines

A new aromatic tetracarboxylic dianhydride having a crank and twisted noncoplannar structure, 2,2′-bis(3,4-dicarboxyphenoxy)biphenyl dianhydride, was synthesized by the reaction of 4-nitrophthalonitrile with biphenyl-2,2′-diol, followed by hydrolysis and cyclodehydration. The biphenyl-2,2′-diyl-containing aromatic polyimides having inherent viscosities up to 0.66 dL/g were obtained by the conventional two-step procedure starting from the dianhydride monomer and various aromatic diamines. Most of the polyimides were readily soluble in amide-type solvents such as N,N-dimethylacetamide and N-methyl-2-pyrrolidone. The aromatic polyimides had glass transition temperatures in the range of 205–242°C, and began to lose weight around 415°C, with 10% weight loss being recorded at about 500°C in air. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2021–2027, 1998     

Preparation and physical properties of poly(4,4′‐diamino‐3′‐carbamoylbenzanilide terephthalamide) and poly(4,4′‐diamino‐3′‐carbamoylbenzanilide isophthalamide) films

To prepare thermally stable and high‐performance polymeric films, new solvent‐soluble aromatic polyamides with a carbamoyl pendant group, namely poly(4,4′‐diamino‐3′‐carbamoylbenzanilide terephthalamide) (p‐PDCBTA) and poly(4,4′‐diamino‐3′‐carbamoylbenzanilide isophthalamide) (m‐PDCBTA), were synthesized. The polymers were cyclized at around 200 to 350 °C to form quinazolone and benzoxazinone units along the polymer backbone. The decomposition onset temperatures of the cyclized m‐ and p‐PDCBTAs were 457 and 524 °C, respectively, lower than that of poly(p‐phenylene terephthalamide) (566 °C). For the p‐PDCBTA film drawn by 40% and heat‐treated, the tensile strength and Young's modulus were 421 MPa and 16.4 GPa, respectively. The film cyclized at 350 °C showed a storage modulus (E′) of 1 × 10¹¹ dyne/cm² (10 GPa) over the temperature range of room temperature to 400 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 775–780, 2000     

Synthesis and properties of new aromatic poly‐(ether benzoxazole)s from 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl and aromatic dicarboxylic acid chlorides

A new bis(o‐aminophenol) with a crank and twisted noncoplanar structure and ether linkages, 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl, was synthesized by the reaction of 2‐benzyloxy‐4‐fluoronitrobenzene with biphenyl‐2,2′‐diol, followed by reduction. Biphenyl‐2,2′‐diyl‐containing aromatic poly(ether benzoxazole)s with inherent viscosities of 0.52–1.01 dL/g were obtained by a conventional two‐step procedure involving the polycondensation of the bis(o‐aminophenol) monomer with various aromatic dicarboxylic acid chlorides, yielding precursor poly(ether o‐hydroxyamide)s, and subsequent thermal cyclodehydration. These new aromatic poly(ether benzoxazole)s were soluble in methanesulfonic acid, and some of them dissolved in m‐cresol. The aromatic poly(ether benzoxazole)s had glass‐transition temperatures of 190–251 °C and were stable up to 380 °C in nitrogen, with 10% weight losses being recorded above 520 °C. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2656–2662, 2002