Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Photoluminescence spectra of thenardite Na2SO4 activated with rare-earth ions, Ce, Sm, Tb, Dy and Tm

Five Na₂SO₄:RE³⁺ phosphors activated with rare-earth (RE) ions (RE³⁺=Ce³⁺, Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) were synthesized by heating natural thenardite Na₂SO₄ from Ai-Ding Salt Lake, Xinjiang, China with small amounts of rare-earth fluorides, CeF₃, SmF₃, TbF₃, DyF₃ and TmF₃, at 920 °C in air. The photoluminescence (PL) and optical excitation spectra of the obtained phosphors were measured at 300 and 10 K. In the PL spectrum of Na₂SO₄:Ce³⁺ at 300 K, two overlapping bands with peaks at 335 and 356 nm due to Ce³⁺ were first observed. Narrow bands observed in PL and excitation spectra of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors were well identified with the electronic transitions within the 4fⁿ (n=5, 8, 9 and 12) configurations of RE³⁺. The existence of excitation bands with high luminescence efficiency at wavelengths shorter than 230 nm is characteristic of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors. The obtained results suggest that these phosphors are unfavorable as the phosphor for usual fluorescence tubes, i.e., mercury discharge tubes, but may be favorable as the phosphor for UV-LED fluorescent tubes and as cathodoluminescence, X-ray luminescence and thermoluminescence phosphors.     

Crystal structure and photoluminescence of (Y1−xCex)2Si3O3N4

Oxonitridosilicate phosphors with compositions of (Y_1−xCe_x)₂Si₃O₃N₄ (x=0−0.2) have been synthesized by solid state reaction method. The structures and photoluminescence properties have been investigated. Ce³⁺ ions have substituted for Y³⁺ ions in the lattice. The emission and excitation spectra of these phosphors show the characteristic photoluminescence spectra of Ce³⁺ ions. Based on the analyses of the diffuse reflection spectra and the PL spectra, a systematic energy diagram of Ce³⁺ ion in the forbidden band of sample with x=0.02 is given. The best doping Ce content in these phosphors is ∼2 mol%. The quenching temperature is ∼405 K for the 2 mol% Ce content sample. The luminescence decay properties were investigated. The primary studies indicate that these phosphors are potential candidates for application in three-phosphor-converted white LEDs.     

Synthesis and luminescence properties of Eu, Ce and Tb-activated Sr3La2(BO3)4 under UV excitation

The spectroscopic properties in UV-excitable range for the phosphors of Sr₃La₂(BO₃)₄:RE³⁺ (RE³⁺=Eu³⁺, Ce³⁺, Tb³⁺) were investigated. The phosphors were synthesized by conventional solid-state reactions. The photoluminescence (PL) spectra and commission international de I'Eclairage (CIE) coordinates of Sr₃La₂(BO₃)₄:RE³⁺ were investigated. The f-d transitions of Eu³⁺, Ce³⁺ and Tb³⁺ in the host lattices are assumed and corroborated. The PL and PL excitation (PLE) spectra indicate that the main emission wavelength of Sr₃La₂(BO₃)₄:Eu³⁺ is 611 nm, and Sr₃La₂(BO₃)₄:Ce³⁺ shows dominating emission peak at 425 nm, while Sr₃La₂(BO₃)₄:Tb³⁺ displays green emission at 487, 542, 582 and 620 nm. These phosphors were prepared by simple solid-state reaction at 1000 °C. There are lower reactive temperature and more convenient than commercial phosphors. The Sr₃La₂(BO₃)₄:Tb³⁺ applied to cold cathode fluorescent lamp was found to emit green light and have a major peak wavelength at around 542 nm. These phosphors may provide a new kind of luminescent materials under ultraviolet excitation.     

Enhanced photoluminescence properties of Zn2SiO4:Mn co-activated with Y/Li under VUV excitation

A series of green phosphors Zn_1.92−2xY_xLi_xSiO₄:0.08Mn²⁺ (0≤x≤0.03) were prepared by solid-state synthesis method. Phase and lattice parameters of the synthesized phosphors were characterized by powder X-ray diffractometer (XRD) and the co-doped effects of Y³⁺/Li⁺ upon emission intensity and decay time were investigated under 147 nm excitation. The results indicate that the co-doping of Y³⁺/Li⁺ has favorable influence on the photoluminescence properties of Zn₂SiO₄:Mn²⁺, and the optimal photoluminescence intensity of Zn_1.90Y_0.01Li_0.01SiO₄:0.08Mn²⁺ is 103% of that of commercial phosphor when the doping concentration of Y³⁺/Li⁺ is 0.01 mol. Additionally, the decay time of phosphor is much shortened and the decay time of Zn_1.90Y_0.01Li_0.01SiO₄:0.08Mn²⁺ is 3.39 ms, shorter by 1.83 ms than that of commercial product after Y³⁺/Li⁺ co-doping.     

Luminescence in trivalent rare earth activated Sr4Al2O7 phosphor

In this paper we report the combustion synthesis of trivalent rare-earth (RE³⁺ = Dy, Eu and Ce) activated Sr₄Al₂O₇ phosphor. The prepared phosphors were characterized by the X-ray powder diffraction (XRD) and photoluminescence (PL) techniques. Photoluminescence emission peaks of Sr₄Al₂O₇:Dy³⁺ phosphor at 474 nm and 578 nm in the blue and yellow region of the spectrum. The prepared Eu³⁺ doped phosphors were excited by 395 nm then we found that the characteristics emission of europium ions at 615 nm (⁵D₀?⁷F₂) and 592 nm (⁵D₀?⁷F₁). Photoluminescence (PL) peaks situated at wavelengths of 363 and 378 nm in the UV region under excitation at around 326 nm in the Sr₄Al₂O₇:Ce³⁺ phosphor.     

Luminescence investigation of red phosphors Ca0.54Sr0.34−1.5xEu0.08Smx(MoO4)y (WO4)1−y for UV-white LED device

Ca_0.54Sr_0.34−1.5xEu_0.08Sm_x(MoO₄)_y (WO₄)_1−y red phosphors were prepared by solid-state reaction using Na⁺ as a charge compensator for light-emitting diodes (LED). The effects of Na⁺ concentration, synthesis temperature, reaction time and Eu³⁺ concentration were studied for the properties of luminescence and crystal structure of red phosphors. The results show that the optimum reaction condition is 6%, 900 °C, 2 h and 8%. The photoluminescence spectra show that red phosphors are effectively excited at 616 nm by 292, 395 and 465 nm. The wavelengths of 465 nm nicely match the widely applied emission wavelengths of blue LED chips.     

Ionic liquid-assisted hydrothermal synthesis of dendrite-like NaY(MoO4)2:Tb phosphor

Micro-sized NaY(MoO₄)₂:Tb³⁺ phosphors with dendritic morphology was synthesized by a ionic liquid-assisted hydrothermal process. X-ray diffraction (XRD) indicated that the as-prepared product is pure tetragonal phase of NaY(MoO₄)₂. Field emission scanning electron microscopy (FE-SEM) images showed that the as-prepared NaY(MoO₄)₂:Tb³⁺ phosphors have dendritic morphology. The photoluminescent (PL) spectra displayed that the as-prepared NaY(MoO₄)₂:Tb³⁺ phosphors show a stronger green emission with main emission wavelength 545 nm corresponding to the ⁵D₄→⁷F₅ transition of Tb³⁺ ion, and the optimal Tb³⁺ doping concentration for obtaining maximum emission intensity was confirmed to be 10 mol%. Based on Van Uitert's and Dexter's models the electric dipole–dipole (D–D) interaction was confirmed to be responsible for the concentration quenching of ⁵D₄ fluorescence of Tb³⁺ in the NaY(MoO₄)₂:Tb³⁺ phosphors. The intrinsic radiative transition lifetime of ⁵D₄ level is found to be 0.703 ms.     

Color improvement of white-light through Mn-enhancing yellow-green emission of SrSi2O2N2:Eu phosphor for white light emitting diodes

Photoluminescence (PL) enhancement of SrSi₂O₂N₂:Eu and the resultant color improvement of white-light were investigated via co-doping Mn with Eu. We observed that a unique absorption of host lattice of SrSi₂O₂N₂ and its visible band emission peaked at around ∼550 nm for SrSi₂O₂N₂:Mn²⁺ in the wavelength range of 450-600 nm. This highly eye-sensitive ∼550 nm-peaked band emission of SrSi₂O₂N₂ doped with Mn²⁺ happens to overlap the 535 nm-peaked band emission of SrSi₂O₂N₂ doped with Eu²⁺, resulting in an intensified photoluminescence in a maximum by 355%. By combining this as-prepared Mn intensified SrSi₂O₂N₂:Eu phosphor with blue InGaN chip, the quality of white-light was improved to 93.3% for color rendering index and 3584 K for correlated color temperature.     

Characterization, EPR and luminescence studies of ZnAl2O4:Mn phosphors

ZnAl₂O₄:Mn green light emitting powder phosphors have been prepared by urea combustion technique involving furnace temperatures about 500 °C in a short time (<5 min). The prepared powders were characterized by X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectrometry and the surface area measurements by a Brunauer-Emmet-Teller (BET) adsorption isotherms. The EPR spectrum exhibits a resonance signal at g≈2.0, which shows a six-line hyperfine structure (hfs). From the EPR spectra the spin-Hamiltonian parameters have been evaluated at room temperature as well as at 110 K. EPR and photoluminescence (PL) studies revealed that manganese ions were present in divalent state and the site symmetry around Mn²⁺ ions is distorted tetrahedral. The spin concentration (N), the paramagnetic susceptibility (χ) and the zero-field splitting parameter (D) have been evaluated and discussed. The green emission at 511 nm in ZnAl₂O₄:Mn phosphor is assigned to a transition from the upper ⁴T₁→⁶A₁ ground state of Mn²⁺ ions.     

Green emitting long lasting phosphorescence (LLP) properties of Mg2SnO4:Mn phosphor

A novel long-lasting phosphorescence phosphor, Mn²⁺-activated Mg₂SnO₄, has been synthesized and its optical properties have been investigated. The Mg₂SnO₄:Mn²⁺ emits green light with high luminance, upon UV irradiation, centered at 499 nm from the spin forbidden transitions of the d-electrons in Mn²⁺ ions. The CIE chromaticity coordinates of the Mg₂SnO₄:Mn²⁺ phosphor are x=0.0875 and y=0.6083 under 254 nm UV excitation. The phosphorescence can be observed by the naked eyes (0.32 mcd/m²) in the dark clearly for over 5 h after the 5 min UV irradiation. Thermoluminescence has been studied and the mechanism of the long-lasting phosphorescence has been discussed.     

Luminescent properties of Dy doped SrMoO4 phosphor

Trivalent dysprosium ions (Dy³⁺) doped strontium molybdate (SrMoO₄) phosphors were synthesized by solid-state reaction and their photoluminescence (PL) properties were investigated. X-ray powder diffraction (XRD) analysis confirmed the formation of SrMoO₄:Dy³⁺. PL measurements indicated that the phosphor exhibited intense emission at 482, 490 (⁴F_9/2→⁶H_15/2) and 575 nm (⁴F_9/2→⁶H_13/2) under UV excitation. The effect of the doping concentration of Dy³⁺in SrMoO₄:Dy³⁺ on the PL was investigated in detail. Na⁺ ion was a good charge compensator for SrMoO₄:Dy³⁺.     

Luminescence of Ce and Pr doped Sr2Mg(BO3)2 under VUV-UV and X-ray excitation

This report presents the luminescence properties of Ce³⁺ and Pr³⁺ activated Sr₂Mg(BO₃)₂ under VUV-UV and X-ray excitation. The five excitation bands of crystal field split 5d states are observed at about 46 729, 44 643, 41 667, 38 314 and 29 762 cm⁻¹ (i.e. 214, 224, 240, 261 and 336 nm) for Ce³⁺ in the host lattice. The doublet Ce³⁺ 5d→4f emission bands were found at about 25 840 and 24 096 cm⁻¹ (387 and 415 nm). The influence of doping concentration and temperature on the emission characteristics and the decay time of Ce³⁺ in Sr₂Mg(BO₃)₂ were investigated. For Pr³⁺ doped samples, the lowest 5d excitation band was observed at about 42017 cm⁻¹ (238 nm), a dominant band at around 35714 cm⁻¹ (280 nm) and two shoulder bands were seen in the emission spectra. The excitation and emission spectra of Ce³⁺ and Pr³⁺ were compared and discussed. The X-ray excited luminescence studies show that the light yields are ∼3200±230 and ∼1400±100 photons/MeV of absorbed X-ray energy for the samples Sr_1.86Ce_0.07Na_0.07Mg(BO₃)₂ and Sr_1.82Pr_0.09Na_0.09Mg(BO₃)₂ at RT, respectively.     

Emission properties of Eu, Mn in MAl2Si2O8 (M=Sr, Ba)

The emission properties of Eu²⁺ and Mn²⁺ in monoclinic SrAl₂Si₂O₈ (M-SAS) and hexagonal BaAl₂Si₂O₈ (H-BAS), both of which have only one alkaline-earth site, were studied. The emission peaks of both Eu²⁺ (405 nm) and Mn²⁺ (564 nm) in SrAl₂Si₂O₈, are located at longer wavelengths, compared with those in H-BAS (373 nm for Eu²⁺ and 518 nm for Mn²⁺), because of the stronger crystal field strength at the Sr site. EPR spectra showed that the g values of Mn²⁺ are 4.5065 in M-SAS:Mn and 2.0247 in H-BAS:Mn. Magnetic measurements proved that Mn²⁺ was at high-spin state in both hosts. The large g value of Mn²⁺ in M-SAS was ascribed to the mixing of the first excitation state to the ground state, both of which have lower d orbital degeneracy due to the lower symmetry of Mn²⁺ site. The transfer efficiency from Eu²⁺ to Mn²⁺was about 10% in M-SAS, higher than that in H-BAS (5%). This was probably because Eu²⁺ emission overlaps the relatively low excitation level of Mn²⁺ in M-SAS. In order to obtain high transfer efficiency, it was necessary for the Eu²⁺ emission to overlap the lowest excitation level of Mn²⁺. The results obtained in this work may be helpful to design the new white or red phosphors for white-light emitting diode (w-LED) applications.     

Optical characterization of fourfold (Td)- and sixfold (Oh)-transition-metal species in MgAl2O4:Co by time-resolved spectroscopy

This work investigates the origin of novel visible photoluminescence (PL) bands observed in the spinel MgAl₂O₄:Co²⁺. Besides the well-known fourfold-coordinated Co²⁺(T_d) PL at 670 nm [N.V. Kuleshov, V.P. Mikhailov, V.G. Scherbitsky, P.V. Prokoshin and K.V. Yumashev, J. Lumin. 55 (1993) 265.], a rich structured PL band at 686 nm was also observed that we associate with uncontrolled impurities of sixfold coordinated Cr³⁺(O_h) by time-resolved spectroscopy and lifetime measurements and their variation with temperature. We also show that the lifetime of the Co²⁺(T_d) emission at 670 nm varies from τ=6.7 μs to 780 ns on passing from T=10 to 290 K. This unexpected behaviour for T_d systems is related to the excited-state crossover (⁴T₁↔²E), making the emission band to transform from a narrow-like emission from ²E at low temperature to a broad structureless band from ⁴T₁ at room temperature.     

Eu-activated Ba2Mg(BO3)2 yellow-emitting phosphors for near ultraviolet-based light-emitting diodes

A series of Eu²⁺-activated Ba₂Mg(BO₃)₂ yellow phosphors were prepared by a high temperature solid-state reaction. The phosphor emits intense yellow light under near ultraviolet excitation. Large Stokes shift can be attributed to the asymmetric nature of the Eu site and the lack of rigidity in the host. The concentration self-quenching mechanism of Ba₂Mg(BO₃)₂:Eu²⁺ is d-d interaction and the critical transfer distance is calculated to be about 12.29 Å. Prototype light-emitting diodes were fabricated by coating the Ba₂Mg(BO₃)₂:0.07Eu²⁺ phosphor onto ∼370 nm-emitting InGaN chips. The LEDs exhibit intense yellow-emitting under a forward bias of 20 mA. The results indicate that Eu²⁺-activated Ba₂Mg(BO₃)₂ is a candidate as a yellow component for fabrication of near-UV white light-emitting diodes.     

EPR and photoluminescence properties of green light emitting LaAl11O18:Mn phosphors

The LaAl₁₁O₁₈:Mn²⁺ powder phosphor has been prepared using a self-propagating synthesis. Formation and homogeneity of the LaAl₁₁O₁₈:Mn²⁺ phosphor has been verified by X-ray diffraction and energy dispersive X-ray analysis respectively. The EPR spectra of Mn²⁺ ions exhibit resonance signals with effective g values at g≈4.8 and g≈1.978. The signal at g≈1.978 exhibits six-line hyperfine structure and is due to Mn²⁺ ions in an environment close to tetrahedral symmetry, whereas the resonance at g≈4.8 is attributed to the rhombic surroundings of the Mn²⁺ ions. It is observed that the number of spins participating in resonance for g≈1.978 increases with decreasing temperature obeying the Boltzmann law. Upon 451 nm excitation, the photoluminescence spectrum exhibits a green emission peak at 514 nm due to ⁴T₁ (G)→⁶A₁ (S) transition of Mn²⁺ ions. The crystal field parameter Dq and Racah inter-electronic repulsion parameters B and C have been evaluated from the excitation spectrum.     

Novel green-emitting Na2CaPO4F:Eu phosphors for near-ultraviolet white light-emitting diodes

In this study, green-emitting Na₂CaPO₄F:Eu²⁺ phosphors were synthesized by solid-state reactions. The excitation spectra of the phosphors showed a broad hump between 250 and 450 nm; the spectra match well with the near-ultraviolet (NUV) emission spectra of light-emitting diodes (LEDs). The emission spectrum showed an intense broad emission band centered at 506 nm. White LEDs were fabricated by integrating a 390 nm NUV chip comprising blue-emitting BaMgAl₁₀O₁₇:Eu²⁺, green-emitting Na₂CaPO₄F:0.02 Eu²⁺, and red-emitting CaAlSiN₃:Eu²⁺ phosphors into a single package; the white LEDs exhibited white light with a correlated color temperature of 5540 K, a color-rendering index of 90.75, and color coordinates (0.332, 0.365) close to those of ideal white light.     

Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.