Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Luminescence investigation of red phosphors Ca0.54Sr0.34−1.5xEu0.08Smx(MoO4)y (WO4)1−y for UV-white LED device

Ca_0.54Sr_0.34−1.5xEu_0.08Sm_x(MoO₄)_y (WO₄)_1−y red phosphors were prepared by solid-state reaction using Na⁺ as a charge compensator for light-emitting diodes (LED). The effects of Na⁺ concentration, synthesis temperature, reaction time and Eu³⁺ concentration were studied for the properties of luminescence and crystal structure of red phosphors. The results show that the optimum reaction condition is 6%, 900 °C, 2 h and 8%. The photoluminescence spectra show that red phosphors are effectively excited at 616 nm by 292, 395 and 465 nm. The wavelengths of 465 nm nicely match the widely applied emission wavelengths of blue LED chips.     

Crystal structure and photoluminescence of (Y1−xCex)2Si3O3N4

Oxonitridosilicate phosphors with compositions of (Y_1−xCe_x)₂Si₃O₃N₄ (x=0−0.2) have been synthesized by solid state reaction method. The structures and photoluminescence properties have been investigated. Ce³⁺ ions have substituted for Y³⁺ ions in the lattice. The emission and excitation spectra of these phosphors show the characteristic photoluminescence spectra of Ce³⁺ ions. Based on the analyses of the diffuse reflection spectra and the PL spectra, a systematic energy diagram of Ce³⁺ ion in the forbidden band of sample with x=0.02 is given. The best doping Ce content in these phosphors is ∼2 mol%. The quenching temperature is ∼405 K for the 2 mol% Ce content sample. The luminescence decay properties were investigated. The primary studies indicate that these phosphors are potential candidates for application in three-phosphor-converted white LEDs.     

Combustion synthesis and luminescence properties of NaY1−xEux(WO4)2 phosphors

The red phosphors NaY_1−xEu_x(WO₄)₂ with different concentrations of Eu³⁺ were synthesized via the combustion synthesis method. As a comparison, NaEu(WO₄)₂ was prepared by the solid-state reaction method. The phase composition and optical properties of as-synthesized samples were studied by X-ray powder diffraction and photoluminescence spectra. The results show that the red light emission intensity of the combustion synthesized samples under 394 nm excitation increases with increase in Eu³⁺ concentrations and calcination temperatures. Without Y ions doping, the emission spectra intensity of the NaEu(WO₄)₂ phosphor prepared by the combustion method fired at 900 °C is higher than that prepared by the solid-state reaction at 1100 °C. NaEu(WO₄)₂ phosphor synthesized by the combustion method at 1100 °C exhibits the strongest red emission under 394 nm excitation and appropriate CIE chromaticity coordinates (x=0.64, y=0.33) close to the NTSC standard value. Thus, its excellent luminescence properties make it a promising phosphor for near UV InGaN chip-based red-emitting LED application.     

The structure and luminescence properties of long afterglow phosphor Y3−xMnxAl5−xSixO12

A series of phosphors with the composition Y_3−xMn_xAl_5−xSi_xO₁₂ (x=0, 0.025, 0.050, 0.075, 0.150, 0.225, 0.300) were prepared with solid state reactions. The X-ray powder diffraction analysis of samples shows that the substitution of Mn²⁺ and Si⁴⁺ does not change the garnet structure of phosphors, but makes the interplanar distance decrease to a certain extent. The emission spectra show that Mn²⁺ in Y₃Al₅O₁₂ emits yellow-orange light in a broad band. With the increment of substitution content, the emission intensity of the phosphors increases firstly then decreases subsequently, and the emission peak moves to longer wavelength. Afterglow spectra and decay curves show that all the Mn²⁺ and Si⁴⁺ co-doped samples emit yellow-orange light with long afterglow after the irradiation of ultraviolet light. The longest afterglow time is 18 min. Thermoluminescence measurement shows that there exist two kinds of traps with different depth of energy level and their depth decreases with the increment of substitution content.     

Synthesis and luminescence properties of europium doped YBa3B9O18

Europium (Eu³⁺) doped YBa₃B₉O₁₈ were synthesized by conventional solid state solidification methods. (Y_1−xEu_x)Ba₃B₉O₁₈ formed solid solutions in the range of x=0–1.0. The luminescence property measurements upon excitation in ultraviolet–visible range show well-known Eu³⁺ excitation and emission. The charge transfer excitation band of Eu³⁺ dominates the excitation spectra. The emission spectrum of Eu³⁺ ions consists mainly of several groups of lines in the 550–720 nm region, due to the transitions from the ⁵D₀ level to the levels ⁷F_J (J=0, 1, 2, 3, 4) of Eu³⁺ ions. The dependence of luminescence intensity on Eu³⁺ concentration shows no concentration quenching for fully concentrated EuBa₃B₉O₁₈. Eu³⁺ doped YBa₃B₉O₁₈ are promising phosphors for applications in displays and optical devices.     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Crystallinity and morphology dependent luminescence of Li-doped Y2−xGdxO3:Eu thin film phosphors

The influence of lithium doping on the crystallization, the surface morphology, and the luminescent properties of pulsed laser deposited Y_2−xGd_xO₃:Eu³⁺ thin film phosphors was investigated. The crystallinity, the surface morphology, and the photoluminescence (PL) of films depended highly on the Li-doping and the Gd content. The relationship between the crystalline and morphological structures and the luminescent properties was studied, and Li⁺ doping was found to effectively enhance not only the crystallinity but also the luminescent brightness of Y_2−xGd_xO₃:Eu³⁺ thin films. In particular, the incorporation of Li and Gd into the Y₂O₃ lattice could induce remarkable increase in the PL. The highest emission intensity was observed Li-doped Y_1.35Gd_0.6O₃:Eu³⁺ thin films whose brightness was increased by a factor of 4.6 in comparison with that of Li-doped Y₂O₃:Eu³⁺ thin films.     

The structure and luminescence properties of a novel orange emitting phosphor Y3MnxAl5−2xSixO12

A series of phosphors with the composition Y₃Mn_xAl_5−2xSi_xO₁₂ (x=0, 0.05, 0.1, 0.15, 0.2, 0.3, 0.4, 0.5, 0.6) was prepared through solid state reactions. X-ray powder diffraction analysis of samples shows that when co-doping content does not exceed 16% of Al³⁺, equimolar co-doping of Mn²⁺ and Si⁴⁺ does not change the garnet structure of phosphors, but makes the interplanar distance to decrease a certain extent. However, if the co-doping content exceeds 16%, new phases will form in the samples. The excitation and emission spectra of samples show that Mn²⁺ in Y₃Mn_xAl_5−2xSi_xO₁₂ emits broadband orange light (peak wavelength varies from 586 to 593 nm). With an increment in co-doping content, the emission intensity of the phosphors increases when the value of x is lower than 0.1 while it decreases when it is higher than 0.1 and the emission peak moves to a longer wavelength.     

Magnetic properties of YFe12−xMox compounds and magnetocaloric effect of YFe9.5Mo2.5

The characterization and magnetic properties of YFe_12−xMo_x (x=2.0, 2.5 and 3.0) with the ThMn₁₂-type structure, and the magnetocaloric effect of YFe_9.5Mo_2.5 were investigated. A directional growth was observed in YFe₁₀Mo₂ alloy. A broad peak in the zero-field-cooling (ZFC) magnetization curve of the YFe_12−xMo_x compounds is ascribed to the existence of ferromagnetic clusters with different site moments and scattered orientations of the moments. The broad range of the peak is reduced with increasing Mo content. A weak peak is observed near 190 K in the ZFC curve of YFe₉Mo₃, which is associated with the 8i sites being mostly occupied by Mo atoms. YFe_9.5Mo_2.5 has a magnetic entropy change of −1.09 J/kg K for a field change of 5 T at 277 K.     

Highly active Ce1−xCuxO2 nanocomposite catalysts for the low temperature oxidation of CO

A series of Ce_1−xCu_xO₂ nanocomposite catalysts with various copper contents were synthesized by a simple hydrothermal method at low temperature without any surfactants, using mixed solutions of Cu(II) and Ce(III) nitrates as metal sources. These bimetal oxide nanocomposites were characterized by means of XRD, TEM, HRTEM, EDS, N₂ adsorption, H₂-TPR and XPS. The influence of Cu loading (5-25 mol%) and calcination temperature on the surface area, particle size and catalytic behavior of the nanocomposites have been discussed. The catalytic activity of Ce_1−xCu_xO₂ nanocomposites was investigated using the test of CO oxidation reaction. The optimized performance was achieved for the Ce_0.80Cu_0.20O₂ nanocomposite catalyst, which exhibited superior reaction rate of 11.2 × 10⁻⁴ mmol g⁻¹ s⁻¹ and high turnover frequency of 7.53 × 10⁻² s⁻¹ (1% CO balanced with air at a rate of 40 mL min⁻¹, at 90 °C). No obvious deactivation was observed after six times of catalytic reactions for Ce_0.80Cu_0.20O₂ nanocomposite catalyst.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

Abnormal positive thermal expansion in Mo substituted ZrW2O8

ZrW₂O₈ displays the unusual property of an isotropic bulk contraction in volume as a function of temperature. We report here on the positive thermal expansion (PTE) property caused by substituting Mo for W sites in ZrW₂O₈ at room temperature. The room temperature crystal structure of ZrW_2−xMo_xO₈ compounds, which were synthesized using a low temperature route, could be divided into ordered phase with α-ZrW₂O₈ structure (0≤x≤0.5) and disordered phase with β-ZrW₂O₈ (0.5<x≤1.5) and c-ZrMo₂O₈ structure (1.5<x≤2). ZrW_2−xMo_xO₈ adopting β-ZrW₂O₈ structure shows abnormal PTE property at room temperature due to the existence of water molecules, while ZrW_2−xMo_xO₈ adopting the other two structures (α-ZrW₂O₈ and c-ZrMo₂O₈) shows negative thermal expansion (NTE) property from room temperature until decomposition for α-ZrW₂O₈ structure or trigonal phase transition for c-ZrMo₂O₈ structure. The reason lies in the fact that the oxygen migration caused by the Mo substitution leads to the re-arrangement of W(Mo)O₄ tetrahedra lying along the 3-fold axis, only particular W/Mo ratio (0.5<x≤1.5) produces a special crystal structure, which allows the entrance of water molecules.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Photoluminescence properties of Sr1-xSi2O2N2: Eux as green to yellow-emitting phosphor for blue pumped white LEDs

This study evaluated potential applications of green to yellow-emitting phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) in blue pumped white light emitting diodes. Sr_1-xSi₂O₂N₂: Eu²⁺_x was synthesized at different Eu²⁺ doping concentrations at 1450 °C for 5 h under a reducing nitrogen atmosphere containing 5% H₂ using a conventional solid reaction method. The X-ray diffraction patterns of the prepared phosphor (Sr_1-xSi₂O₂N₂: Eu²⁺_x) were indexed to the SrSi₂O₂N₂ phase and an unknown intermediate phase. The photoluminescence properties of these phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) showed that the samples were excited from the UV to visible region due to the strong crystal field splitting of the Eu²⁺ ion. The emission spectra under excitation of 450 nm showed a bright color at 545-561 nm. The emission intensity increased gradually with increasing Eu²⁺ doping concentration ratio from 0.05 to 0.15. However, the emission intensity decreased suddenly when the Eu²⁺ concentration ratio was >0.2. As the doping concentration of Eu²⁺ was increased, there was a red shift in the continuous emission peak. These results suggest that Sr_1-xSi₂O₂N₂: Eu₂⁺_x phosphor can be used in blue-pumped white light emitting diodes.     

BiFeO3/Zn1−xMnxO bilayered thin films

BiFeO₃/Zn_1−xMn_xO (x = 0-0.08) bilayered thin films were deposited on the SrRuO₃/Pt/TiO₂/SiO₂/Si(1 0 0) substrates by radio frequency sputtering. A highly (1 1 0) orientation was induced for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO thin films demonstrate diode-like and resistive hysteresis behavior. A remanent polarization in the range of 2P_r ∼ 121.0-130.6 μC/cm² was measured for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO (x = 0.04) bilayer exhibits a highest M_s value of ∼15.2 emu/cm³, owing to the presence of the magnetic Zn_0.96Mn_0.04O layer with an enhanced M_s value.     

Short-range order analysis and some physical properties of InxSe1−x glasses

Bulk In_xSe_1−x (with x=5-25 at%) glasses were prepared using the melt-quench technique. Short range order(SRO) was examined by the X-ray diffraction using Cu(k_α) radiation in the wave vector interval 0.28≤k≤6.5 A⁰⁻¹.The SRO parameters have been obtained from the radial distribution function. The inter-atomic distance obtained from the first and second peak are r₁=0.263 and r₂=0.460 nm, which is equivalent In-Se and Se-Se bond length. The fundamental structural unit for the studied glasses is In₂Se₃ pyramid. Using the differential scanning calorimetry (DSC), the crystallization mechanism of In_xSe_1−x chalcogenide glass has been studied. The glass transition activation energy (E_g) is 289±0.3 kj/mol.There is a correlation amongst the glass forming ability, bond strength and the number of lone pair electrons. The utility of the Gibbs-Di Marzio relation was achieved by estimating T_g theoretically.     

Red-emitting LiEuMo2−xSixO8 phosphors for white light-emitting diodes

Si⁴⁺ was introduced to the lattice of LiEuMo₂O₈ by solid-state reaction to prepare a new kind of red-emitting LiEuMo_2−xSi_xO₈ (0<x≤0.5) phosphors. The introduction of Si⁴⁺ ion caused the distortion and slight shrinking of the unit cell of LiEuMo₂O₈ material, and the blue-shift of the charge-transfer-absorption (CTA) band of LiEuMo₂O₈. Photoluminescence excitation (PLE) and photoluminescence measurements showed that the introduction of Si⁴⁺ was able to enhance the excitation efficiency of LiEuMo₂O₈ in NUV spectral region (360-400 nm). Consequently the red emission of LiEuMo₂O₈ phosphor was improved by 30% at x=0.2 under 395 nm light excitation, without loss of color purity. The enhanced red emission of LiEuMo_2−xSi_xO₈ was discussed in terms of the blue-shift of CTA band and the relaxation of parity-forbidden selection rules for trivalent europium luminescent centers.