Copolymerization behavior of direct polycondensation of AB2 and AB monomers that forms hyperbranched aromatic polyamide copolymers

The copolymerization behavior of the one‐step direct polycondensation of 3,5‐bis‐(4‐aminophenoxy)benzoic acid (AB₂ monomer) and 3‐(4‐aminophenoxy)benzoic acid (AB monomer) was investigated by IR and ¹³C NMR measurements. IR measurements revealed that the content of the AB₂ units in the polymer was higher in the early stages of polymerization. ¹³C NMR spectra of the polymers indicated that the number of dendritic units increased slowly with increasing reaction time. The stepwise copolymerization of the AB₂ and AB monomers was also carried out, and the structure was analyzed by ¹³C NMR measurements. Copolymer synthesized stepwise by adding AB₂ monomer first (polymer II ) had more dendritic units and less terminal units as compared with the one‐step copolymer (polymer I ). Copolymer synthesized stepwise by adding AB monomer first gave a resulting copolymer (polymer III ) composed of long AB chains. The solubility of the stepwise copolymers was low, and the inherent viscosity was high in comparison with the one‐step copolymer as a result of the difference in architecture of the copolymers. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3304–3310, 2001     

Thioxanthone–anthracene‐9‐carboxylic acid as radical photoinitiator in the presence of atmospheric air

Thioxanthone–anthracene‐9‐carboxylic acid (TX‐ANCA) namely 14‐oxo‐14H‐naphthol [2,3‐b]thioxanten‐12‐carboxylic acid, is synthesized and characterized as part of our continuing interest for syntheses of polyaromatic initiators. Photoinitiator, TX‐ANCA have good absorption properties in the UV and visible region of the electromagnetic spectrum (ɛ₃₇₀: 9080 M⁻¹cm⁻¹, ɛ₄₃₀: 6151 M⁻¹ cm⁻¹). The fluorescence quantum yield is calculated as 0.1 which is slightly higher than of the parent thioxanthone compound (φ_f: 0.07). The phosphorescence lifetime is found to be 39 ms. The possible initiating mechanism of TX‐ANCA is based on photoexcitation of TX‐ANCA and quenching of triplet excited states of TX‐ANCA by molecular oxygen generates singlet oxygen. Singlet oxygen reacts with the anthracene moiety of TX‐ANCA possibly forms an endoperoxide. The endoperoxides undergoes photochemical or thermal decomposition to form radicals which are able to initiate free radical polymerization. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 1878–1883     

Synthesis and characterization of novel fluorinated polyimides derived from 4,4′‐[2,2,2‐trifluoro‐1‐(3‐trifluoromethylphenyl)ethylidene]diphthalic anhydride and aromatic diamines

A novel fluorinated aromatic dianhydride, 4,4′‐[2,2,2‐trifluoro‐1‐(3‐trifluoromethyl‐phenyl)ethylidene]diphthalic anhydride (TFDA) was synthesized by coupling of 3′‐trifluoromethyl‐2,2,2‐trifluoroacetophenone with o‐xylene under the catalysis of trifluoromethanesulfonic acid, followed by oxidation of KMnO₄ and dehydration. A series of fluorinated aromatic polyimides derived from the novel fluorinated aromatic dianhydride TFDA with various aromatic diamines, such as p‐phenylenediamine (p‐PDA), 4,4′‐oxydianiline (ODA), 1,4‐bis(4‐aminophenoxy)benzene (p‐APB), 1,3‐bis(4‐amino‐phenoxy)benzene (m‐APB), 4‐(4‐aminophenoxy)‐3‐trifluoromethylphenylamine (3FODA) and 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzene (6FAPB), were prepared by polycondensation procedure. All the fluorinated polyimides were soluble in many polar organic solvents such as NMP, DMAc, DMF, and m‐cresol, as well as some of low boiling point organic solvents such as CHCl₃, THF, and acetone. Homogeneous and stable polyimide solutions with solid content as high as 35–40 wt % could be achieved, which were prepared by strong and flexible polyimide films or coatings. The polymer films have good thermal stability with the glass transition temperature of 232–322 °C, the temperature at 5% weight loss of 500–530 °C in nitrogen, and have outstanding mechanical properties with the tensile strengths of 80.5–133.2 MPa as well as elongations at breakage of 7.1–12.6%. It was also found that the polyimide films derived from TFDA and fluorinated aromatic diamines possess low dielectric constants of 2.75–3.02, a low dissipation factor in the range of 1.27–4.50 × 10^?3, and low moisture absorptions <1.3%. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4143–4152, 2004     

Effects of diamines and their fluorinated groups on the color lightness and preparation of organosoluble aromatic polyimides from 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]‐hexafluoropropane

To investigate the position and amount of the CF₃ group affecting the coloration of polyimides (PIs), we prepared 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]hexafluoropropane ( 2 ) with four CF₃ groups with 2‐chloro‐5‐nitrobenzotrifluoride and 2,2‐bis(4‐hydroxyphenol)hexafluoropropane. A series of soluble and light‐colored fluorinated PIs ( 5 ) were synthesized from 2 and various aromatic dianhydrides ( 3a – 3f ). 5a – 5f had inherent viscosities ranging from 0.80 to 1.19 dL/g and were soluble in amide polar solvents and even in less polar solvents. The glass‐transition temperatures of 5 were 221–265 °C, and the 10% weight‐loss temperatures were above 493 °C. Their films had cutoff wavelengths between 343 and 390 nm, b* values (a yellowness index) ranging from 5 to 41, dielectric constants of 2.68–3.01 (1 MHz), and moisture absorptions of 0.03–0.29 wt %. In a comparison of the PI series 6 – 8 based on 2,2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane, 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]propane, and 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane, we found that the CF₃ group close to the imide group was more effective in lowering the color; this means that CF₃ of 5 , 7 , and 8f was more effective than that of 6c . The color intensity of the four PI series was lowered in the following order: 5 > 7 > 6 > 8 . The PI 5f , synthesized from diamine 2 and 4,4′‐hexafluoroisopropylidenediphthalic anhydride, had six CF₃ groups in a repeated segment, so it exhibited the lightest color among the four series. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 922–938, 2003     

Hyperbranched poly(ether–urea)s using AB2‐type blocked isocyanate monomer and azide monomer: Synthesis,characterization, reactive end functionalization,and copolymerization with AB monomer

3,5‐bis(4‐aminophenoxy)phenyl phenylcarbamate—a novel AB₂‐type blocked isocyanate monomer and 3,5‐bis{ethyleneoxy(4‐aminophenoxy)}phenyl carbonyl azide—a novel AB₂‐type azide monomer were synthesized in high yield. Step‐growth polymerization of these monomers were found to give a first example of hyperbranched poly (aryl‐ether‐urea) and poly(aryl‐alkyl‐ether‐urea). Molecular weights (M_w) of the polymer were found to vary from 1,858 to 52,432 depending upon the monomer and experimental conditions used. The polydispersity indexes were relatively narrow due to the controlled regeneration of isocyanate functional groups for the polymerization reaction. The degree of branching (DB) was determined using ¹H‐NMR spectroscopy and the values ranged from 87 to 54%. All the polymers underwent two‐stage decomposition and were stable up to 300 °C. Functionalized end‐capping of poly(aryl‐ether‐urea) using phenylchloroformate and di‐t‐butyl dicarbonate (Boc)₂O changed the thermal properties and solubility of the polymers. Copolymerization of AB₂‐type blocked isocyante monomer with functionally similar AB monomer were also carried out. The molecular weights of copolymers were found to be in the order of 6 × 10⁵ with narrow dispersity. It was found that the T_g's of poly(aryl‐alkyl‐ether‐urea)s were significantly less (46–49 °C) compared to poly(aryl‐ether‐urea)s. Moreover the former showed melting transition at 154 °C, which was not observed in the latter case. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2959–2977, 2007     

Facile synthesis of controlled‐structure primary amine‐based methacrylamide polymers via the reversible addition‐fragmentation chain transfer process

We report here a novel direct method for the syntheses of primary aminoalkyl methacrylamides that requires mild reagents and no protecting group chemistry. The reversible addition‐fragmentation chain transfer polymerization (RAFT) of the aminoalkyl methacrylamide revealed to be highly efficient with 4‐cyanopentanoic acid dithiobenzoate (CTP) as chain transfer agent and 4,4′‐azobis(4‐cyanovaleric acid) (ACVA) as initiator. Cationic amino‐based homopolymers of reasonably narrow polydispersities (M_w/M_n < 1.30) and predetermined molecular weights were obtained without recourse to any protecting group chemistry. A range of block and random copolymers were also synthesized via the RAFT process. The homopolymers and copolymers were characterized by aqueous conventional and triple detection gel permeation chromatography systems. Furthermore, the primary amine‐based methacrylamide monomers and polymers revealed to be highly stable both with the primary amino group in the protonated and deprotonated form. We have also demonstrated that stabilized gold nanoparticles can be generated with the RAFT‐synthesized amine‐based polymers via a photochemical process. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4984–4996, 2008     

Well‐defined amphiphilic polymethylene‐b‐poly(acrylic acid) diblock copolymers: New synthetic strategy and their self‐assembly

Well‐defined amphiphilic polymethylene‐b‐poly (acrylicacid) diblock copolymers have been synthesized via a new strategy combining polyhomologation and atom transfer radical polymerization (ATRP). Hydroxyl‐terminated polymethylenes (PM‐OH) with different molecular weights and narrow molecular weight distribution are obtained through the polyhomologation of dimethylsulfoxonium methylides following quantitative oxidation via trimethylamine‐N‐oxide dihydrate. Subsequently, polymethylene‐based macroinitiators (PM‐MIs M_n = 1,300 g mol^?1 [M_w/M_n = 1.11] and M_n = 3,300 g mol^?1 [M_w/M_n = 1.04]) are synthesized by transformation of terminal hydroxyl group of PM‐OH to α‐haloester in ～100% conversion. ATRPs of tert‐butyl acrylate (t‐BuA) are then carried out using PM‐MIs as initiator to construct PM‐b‐P(t‐BuA) diblock copolymers with controllable molecular weight (M_n = 8,800–15,800 g mol^?1 M_w/M_n = 1.04–1.09) and different weight ratio of PM/P(t‐BuA) segment (1:1.7–1:11.2). The amphiphilic PM‐b‐PAA diblock copolymers are finally prepared by hydrolysis of PM‐b‐P(t‐BuA) copolymers and their self‐assembly behavior in water is preliminarily investigated via the determination of critical micelle concentrations, dynamic light scattering, and transmission electron microscope (TEM). © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis of ultra‐high‐molecular‐weight ethylene‐propylene copolymer via quasi‐living copolymerization with N‐heterocyclic carbene ligated vanadium complexes

The quasi‐living copolymerization of ethylene with propylene was achieved by using N‐heterocyclic carbene (NHC) ligated vanadium complex ( V3 , VOCl₃[1,3‐(2,6‐ⁱPr₂C₆H₃)₂(NCH?)₂C:]) due to the stabilization of active center by the introduction of bulky and electron rich NHC ligand with bulky isopropyl substituents at the ortho positions of the phenyl rings. The weight‐average molecular weight (M_w) of the resulting copolymer increases linearly with its weight in 20 min. The ultra‐high‐molecular‐weight (UHMW) ethylene‐propylene copolymer (M_w = 1612 kg mol^?1) can be synthesized with V3 /Et₃Al₂Cl₃ catalytic system. The novel complex V4′ (VCl₃[1,3‐(2,4,6‐Me₃C₆H₂)₂(NCH?)₂C:]·2THF) was constructed by the introduction of two coordinated tetrahydrofuran molecules and decrease in steric hindrance at the ortho positions of phenyl rings. The UHMW ethylene‐propylene copolymer (M_w = 1167 kg mol^?1) can also be synthesized by using V4′ /Et₃Al₂Cl₃ catalytic system. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 553–561     

Efficient synthesis of β‐(1,6)‐linked oligosaccharides through microwave‐assisted glycosylation

A microwave‐assisted glycosylation method was developed for efficient synthesis of oligosaccharides. Di‐functional AB monomers, 2,3,4‐tri‐O‐acetyl‐α‐d ‐galactopyranosyl bromide ( 3a ) and 2,3,4‐tri‐O‐acetyl‐α‐d ‐glucopyranosyl bromide ( 3b ) were designed and synthesized as weakly reactive monomers to avoid unwanted glycosylation or degradation during preparation and storage. The glycosylations of these monomers gave low conversions and low molecular weight oligosaccharides at rt, reflux, and under low microwave energy irradiation. However, the glycosylation became very effective when high microwave energy was applied, giving 100% conversion and producing oligosaccharides with M_n = 4.76 kDa for 3a and M_n = 4.05 kDa for 3b. The acetylated oligosaccharides were further subjected to deprotection for structural analysis, which indicated the oligosaccharides contain predominantly linear β‐(1,6)‐glycosyl linkages. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 3693–3699     

Synthesis of well‐defined,soluble poly(3‐alkyl‐4‐benzamide) by chain‐growth condensation polymerization

Well‐defined poly(3‐alkyl‐4‐benzamide) was synthesized by means of chain‐growth condensation polymerization of phenyl 3‐octyl‐4‐(4‐octyloxybenzyl(OOB)amino)benzoate ( 1c ) from initiator 2 , followed by removal of the OOB groups on amide nitrogen of poly 1c . Polymerization of 1c with phenyl 4‐(trifluoromethyl)benzoate ( 2b ) in the presence of 1,1,1,3,3,3‐hexamethyldisilazide (LiHMDS) and LiCl in THF at ?10 °C gave poly 1c with a narrow molecular weight distribution (M_w/M_n ≤ 1.08) and a well‐defined molecular weight (M_n = 4480–12,700) determined by the feed ratio of monomer to initiator (from 10 to 30). The OOB groups of poly 1c were removed with H₂SO₄ to give the corresponding N‐unsubstituted poly(p‐benzamide) (poly 1c′ ) with low polydispersity. The solublity of poly 1c′ in polar organic solvents was dramatically higher than that of poly(p‐benzamide), demonstrating that introduction of an alkyl group on the aromatic ring is very effective for improving the solubility of poly(p‐benzamide). © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 360–365     

Formation of polymeric micelles with amino surfaces from amphiphilic AB‐type diblock copolymers composed of poly(glycolic acid lysine) segments and polylactide segments

Amphiphilic AB‐type diblock copolymers composed of hydrophobic poly(L ‐lactide) (PLA) segments and hydrophilic poly(glycolic acid lysine) [poly(Glc‐Lys)] segments with amino side‐chain groups self‐associated to form PLA‐based polymeric micelles with amino surfaces in an aqueous solution. The average diameter of the loose core–shell polymeric micelles for poly(Glc‐Lys) [number‐average molecular weight (M_n) = 1240]‐b‐PLA (M_n = 7000) obtained by a dimethyl sulfoxide/water dialysis method was estimated to be about 50 nm in water by dynamic light scattering measurements. The size and shape of the obtained polymeric micelles were further observed with transmission electron microscopy and atomic force microscopy. To investigate the possibility of applying the obtained PLA‐based polymeric micelles as bioabsorbable vehicles for hydrophobic drugs, we tested the entrapment of drugs in poly(Glc‐Lys) (M_n = 1240)‐b‐PLA (M_n = 7000) micelles and their release with doxorubicin as a hydrophobic drug. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1426–1432, 2002     

Synthesis and characterization of model polybutadiene‐1,4‐b‐polydimethylsiloxane‐b‐polybutadiene‐1,4 copolymers

Model copolymers of poly(butadiene) (PB) and poly(dimethylsiloxane) (PDMS), PB‐b‐PDMS‐b‐PB, were synthesized by sequential anionic polymerization (high vacuum techniques) of 1,3‐butadiene and hexamethylciclotrisiloxane (D₃) on sec‐BuLi followed by chlorosilane‐coupling chemistry. The synthesized copolymers were characterized by nuclear magnetic resonance (¹H NMR), size‐exclusion chromatography (SEC), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). SEC and ¹H NMR results showed low polydispersity indexes (M_w/M_n) and variable siloxane compositions, whereas DSC and TGA experiments indicated that the thermal stability of the triblock copolymers depends on the PDMS composition. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2726–2733, 2007     

Three‐arm star block copolymers of aromatic polyether and polystyrene from chain‐growth condensation polymerization,atom transfer radical polymerization,and click reaction

Well‐defined (AB)₃ type star block copolymer consisting of aromatic polyether arms as the A segment and polystyrene (PSt) arms as the B segment was prepared using atom transfer radical polymerization (ATRP), chain‐growth condensation polymerization (CGCP), and click reaction. ATRP of styrene was carried out in the presence of 2,4,6‐tris(bromomethyl)mesitylene as a trifunctional initiator, and then the terminal bromines of the polymer were transformed to azide groups with NaN₃. The azide groups were converted to 4‐fluorobenzophenone moieties as CGCP initiator units by click reaction. However, when CGCP was attempted, a small amount of unreacted initiator units remained. Therefore, the azide‐terminated PSt was then used for click reaction with alkyne‐terminated aromatic polyether, obtained by CGCP with an initiator bearing an acetylene unit. Excess alkyne‐terminated aromatic polyether was removed from the crude product by means of preparative high performance liquid chromatography (HPLC) to yield the (AB)₃ type star block copolymer (M_n = 9910, M_w/M_n = 1.10). This star block copolymer, which contains aromatic polyether segments with low solubility in the shell unit, exhibited lower solubility than A₂B or AB₂ type miktoarm star copolymers. In addition, the obtained star block copolymer self‐assembled to form spherical aggregates in solution and plate‐like structures in film. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis and characterization of novel fluorinated polyimides based on 2,7‐bis(4‐amino‐2‐trifluoromethylphenoxy)naphthalene

A new trifluoromethyl‐substituted bis(ether amine) monomer, 2,7‐bis(4‐amino‐2‐trifluoromethylphenoxy)naphthalene, was synthesized. It led to a series of novel fluorinated polyimides by thermal and chemical imidization routes when reacted with various commercially available aromatic tetracarboxylic dianhydrides. Most of the polyimides obtained from both routes were soluble in many organic solvents, such as N,N‐dimethylacetamide. All the polyimides could afford transparent, flexible, and strong films with low moisture absorptions of 0.3–0.6%, low dielectric constants of 2.52–3.27 at 10 kHz, and an ultraviolet–visible absorption cutoff wavelength at 377–436 nm. The glass‐transition temperatures of the polyimides were in the range of 244–297 °C, and the 5% weight‐loss temperatures were higher than 550 °C. For a comparative study, a series of analogous polyimides based on 2,7‐bis(4‐aminophenoxy)naphthalene were also prepared and characterized. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2001–2018, 2003     

Synthesis and properties of blue light‐emitting,silicon‐containing,regio‐ and stereoregular conjugated polymers

This article concerns the hydrosilylation polyaddition of 1,4‐bis(dimethylsilyl)benzene ( 1 ) with 4,4′‐diethynylbiphenyl, 2,7‐diethynylfluorene ( 2b ), and 2,6‐diethynylnaphthalene with RhI(PPh₃)₃ catalyst. Trans‐rich polymers with weight‐average molecular weights (M_w's) ranging from 19,000 to 25,000 were obtained by polyaddition in o‐Cl₂C₆H₄ at 150–180 °C, whereas cis‐rich polymers with M_w's from 4300 to 34,000 were obtained in toluene at 0 °C–r.t. These polymers emitted blue light in 4–81% quantum yields. The cis polymers isomerized into trans polymers upon UV irradiation, whereas the trans polymers did not. The device having a layer of polymer trans‐ 3b obtained from 1 and 2b demonstrated electroluminescence without any dopant. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2774–2783, 2004     

High Tg and high organosolubility of novel unsymmetric polyimides

A series of new polyimides (PIs) containing di‐tert‐butyl side groups were synthesized via a polycondensation of 1‐(4‐aminophenoxy)‐4‐(4‐amino‐2‐methylphenyl)‐2,6‐di‐tert‐butylbenzene ( 3 ) with various aromatic tetracarboxylic dianhydrides. The novel unsymmetric PIs exhibited a low dielectric constants (2.78–3.02), low moisture absorption (0.53–1.35%), excellent solubility, and high glass transition temperature (308–450 °C). The PI derived from the new diamine and the very rigid naphthalene‐1,4,5,8‐tetracarboxylic dianhydride (NTDA) was soluble in N‐methyl‐2‐pyrrolidone, chloroform, m‐cresol, and cyclohexanone. The unsymmetric di‐tert‐butyl pendent groups significantly enhance the rotational barrier of the polymer chains; thus these PIs had high T_gs. The ¹H NMR spectrum of the diamine 3 revealed that the protons of 4‐aminophenoxy moiety are not chemical shift equivalent. This is because the steric hindrance of the bulky di‐tert‐butyl groups prevents the benzene ring of 4‐aminophenoxy moiety from rotating freely. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 2443–2452, 2009     

Macrocyclization of polymers via ring‐closing metathesis and azide/alkyne‐“click”‐reactions: An approach to cyclic polyisobutylenes

The end‐to‐end cyclization of telechelic polyisobutylenes (PIB's) toward cyclic polyisobutylenes is reported, using either ring‐closing metathesis (RCM) or the azide/alkyne‐“click”‐reaction. The first approach uses bisallyl‐telchelic PIB's (M_n = 1650, 3680, 9770 g mol^?1) and Grubbs 1st‐, 2nd‐, and 3rd‐generation catalyst leading to cyclic PIB's in 60–80% yield, with narrow polydispersities (M_w/M_n = 1.25). Azide/alkyne‐“click”‐reactions of bisalkyne‐telechelic PIB's (M_n = 3840 and 9820 g mol^?1) with excess of 1,11‐diazido‐undecane leads to the formation of mixtures of linear/cyclic PIB's under formation of oligomeric cycles. Subsequent reaction of the residual azide‐moieties in the linear PIB's with excess of alkyne‐telechelic PEO enables the chromatographic removal of the resulting linear PEO‐PIB‐block copolymers by column chromatography. Thus pure cyclic PIB's can be obtained using this double‐“click”‐method, devoid of linear contaminants. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 671–680, 2010     

Soluble fluorinated polyimides derived from 1,4‐ (4′‐aminophenoxy)‐2‐(3′‐trifluoromethylphenyl)benzene and aromatic dianhydrides

New fluorinated aromatic polyimides were prepared from 1,4‐(4′‐aminophenoxy)‐2‐(3′‐trifluoromethylphenyl)benzene and aromatic dianhydrides via the polycondensation of one‐step high‐temperature and two‐step thermal or chemical imidization methods. Experimental results indicated that some of the polyimides were soluble both in strong dipolar solvents (N‐methyl‐2‐pyrrolidone or N,N‐dimethylacetamide) and in common organic solvents such as tetrahydrofuran, CHCl₃, and acetone. The polyimides showed exceptional thermal and thermooxidative stability and good mechanical properties. No weight loss was detected before a temperature of 520 °C in nitrogen, and the glass‐transition temperatures ranged from 208 to 251 °C. Low dielectric constants (2.55–2.71 at 1 MHz), low refractive indices, and low water absorption were also observed. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2404–2413, 2001     

Synthesis and properties of ortho‐linked aromatic polyimides based on 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene

A bis(ether amine) containing the ortho‐substituted phenylene unit and pendant tert‐butyl group, 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene, was synthesized and used as a monomer to prepare polyimides with six commercial dianhydrides via a conventional two‐stage procedure. The intermediate poly(amic acid)s had inherent viscosities of 0.78–1.44 dL/g, and most of them could be thermally converted into transparent, flexible, and tough polyimide films. The inherent viscosities of the resulting polyimides were in the range of 0.46–0.87 dL/g. All polyimides were noncrystalline, and most of them showed excellent solubility in polar organic solvents. The glass‐transition temperatures of these polyimides were in the range of 222–259 °C in differential scanning calorimetry and 212–282 °C in thermomechanicl analysis. These polyimides showed no appreciable decomposition up to 500 °C in thermogravimetric analysis in air or nitrogen. A comparative study of the properties with the corresponding polyimides without pendant tert‐butyl groups derived from 1,2‐bis(4‐aminophenoxy)benzene is also presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1551–1559, 2000     

Membranes from poly(aryl ether)‐based ionomers containing multiblock segments of randomly distributed nanoclusters of 18 sulfonic acid groups

Multiblock copolymers 1a (M_n = 31,500–47,400) of sulfonated poly(aryl ether)s were synthesized by polycondensation of 4,4′‐difluorobenzophenone (DFBP), bis(4‐hydroxyphenyl)sulfone (BHPS), and an hydroxy‐terminated sulfonated oligomer, which was synthesized from DFBP and 2,2′,3,3′,5,5′‐hexaphenyl‐4,4′‐dihydroxybiphenyl a . The copolymerization of trimeric monomer b with DFBP and BHPS gave a series of copolymers 1b (M_n = 26,200–45,900). The copolymers were then sulfonated with chlorosulfonic acid to give ionomers 3a with hydrophilic multiblock segments and ionomers 3b with segments containing clusters of 18 sulfonic acid groups. The proton exchange membranes cast from ionomers 3a and 3b were characterized with regard to thermal stability, water uptake, proton conductivity, and morphology. Transmission electron microscopy images of 3a‐1 and 3b‐1 revealed a phase separation similar to that of Nafion that may explain their higher proton conductivities compared with randomly sulfonated copolymers. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4762–4773, 2009