Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Enhanced photoluminescence properties of Zn2SiO4:Mn co-activated with Y/Li under VUV excitation

A series of green phosphors Zn_1.92−2xY_xLi_xSiO₄:0.08Mn²⁺ (0≤x≤0.03) were prepared by solid-state synthesis method. Phase and lattice parameters of the synthesized phosphors were characterized by powder X-ray diffractometer (XRD) and the co-doped effects of Y³⁺/Li⁺ upon emission intensity and decay time were investigated under 147 nm excitation. The results indicate that the co-doping of Y³⁺/Li⁺ has favorable influence on the photoluminescence properties of Zn₂SiO₄:Mn²⁺, and the optimal photoluminescence intensity of Zn_1.90Y_0.01Li_0.01SiO₄:0.08Mn²⁺ is 103% of that of commercial phosphor when the doping concentration of Y³⁺/Li⁺ is 0.01 mol. Additionally, the decay time of phosphor is much shortened and the decay time of Zn_1.90Y_0.01Li_0.01SiO₄:0.08Mn²⁺ is 3.39 ms, shorter by 1.83 ms than that of commercial product after Y³⁺/Li⁺ co-doping.     

Photoluminescence properties of Eu in Y(PO3)3 under VUV excitation

The photoluminescence properties of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) are investigated. The excitation spectrum of Y_0.85(PO₃)₃:0.15Eu₃⁺ shows that both the (PO₃)₃³⁻ groups and the CT bands of O²⁻-Y³⁺ can efficiently absorb the excitation energy in the region of 120-250 nm. Under 147 nm excitation, the optimal emissive intensity of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) is about 36% of the commercial phosphor (Y,Gd)BO₃:Eu³⁺, which hints that the absorbed energy by the host matrix could be efficiently transferred to Eu³⁺. We try to study the concentration quenching mechanism of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) under 147 and 172 nm excitation.     

A novel UV-emitting phosphor: Li6CaB3O8.5:Pb

Pure Li₆CaB₃O_8.5 and Li₆Ca_1−xPb_xB₃O_8.5 (0.005≤x≤0.04) materials were prepared by a solution combustion synthesis method. The phase of synthesized materials was determined using the powder XRD and FTIR. The synthesized materials were investigated using spectrofluorometer at room temperature. The emission and excitation bands of the synthesized phosphors were observed at 307 and 268 nm, respectively. The dependence of the emission intensity on the Pb²⁺ concentration for the Li₆Ca_1−xPb_xB₃O_8.5 (0.005≤x≤0.04) was studied and observed that the optimum concentration of Pb²⁺ in phosphor is 0.01 mol. The Stokes shift of the synthesized phosphor was calculated to be 4740 cm^-1.     

Photoluminescence of Y2O3:Eu thin film phosphors by sol-gel deposition and rapid thermal annealing

Y₂O₃:Eu³⁺ phosphor films have been developed by using the sol-gel process. Comprehensive characterization methods such as Photoluminescent (PL) spectroscopy, X-ray diffraction (XRD) and Fourier Transform Infrared (FTIR) spectroscopy were used to characterize the Y₂O₃:Eu³⁺ phosphor films. In this experiment, the XRD profiles show that the Y₂O₃:Eu³⁺ phosphor films crystallization temperature and optimum annealing temperature occur at about 650 and 750 °C, respectively. The optimum dopant concentration is 12 mol% Eu³⁺ and the critical transfer distance (R_c) among Eu³⁺ ions is calculated to be about 0.84 nm. Vacuum environment is more efficient than oxygen and nitrogen to eliminate the OH content and hence yields higher luminescent phosphor films. The PL emission intensity of Y₂O₃:Eu³⁺ phosphor films is also dependent on the annealing time. It was found that the H₂O impurities were effectively eliminated after annealing time of 25 s at 750 °C in vacuum environment. From the experiment results, the schematic energy band diagram of Y₂O₃:Eu³⁺ phosphor films is constructed.     

Cathodoluminescence characteristics of particles and film of (Y, Zn)2O3:Eu phosphor prepared by spray pyrolysis

Eu-doped Y₂O₃ particles with spherical shape and fine size were prepared by spray pyrolysis. The cathodoluminescence of Y₂O₃:Eu³⁺ powder was optimized by substituting small amount of zinc atoms in place of yttrium sites. As a result, the optimized (Y, Zn)₂O₃:Eu³⁺ phosphor showed 60% improved cathodoluminescence compared with Y₂O₃:Eu³⁺ particles. The prepared (Y, Zn)₂O₃:Eu³⁺ phosphor had spherical shape and 0.726 μm in mean size. Using these particles, the thickness of the phosphor film was controlled by varying the phosphor loading. The brightness and luminous efficiency of phosphor films prepared were monitored with varying the accelerating voltage ranges from 4 to 14 kV. The dependency of the luminous efficiency on the accelerating voltage was very sensitive to the phosphor loading. As increasing the accelerating voltage from 4 to 14 kV, the brightness of phosphor films prepared was monotonically increased from 200 to 1085 cd/cm²_, but the saturation in the luminous efficiency appeared at 10 kV. The highest efficiency was achieved when the number of phosphor-particles layer was about 3. More details about the luminous efficiency and brightness were discussed with changing the phosphor loading.     

Crystallinity and morphology dependent luminescence of Li-doped Y2−xGdxO3:Eu thin film phosphors

The influence of lithium doping on the crystallization, the surface morphology, and the luminescent properties of pulsed laser deposited Y_2−xGd_xO₃:Eu³⁺ thin film phosphors was investigated. The crystallinity, the surface morphology, and the photoluminescence (PL) of films depended highly on the Li-doping and the Gd content. The relationship between the crystalline and morphological structures and the luminescent properties was studied, and Li⁺ doping was found to effectively enhance not only the crystallinity but also the luminescent brightness of Y_2−xGd_xO₃:Eu³⁺ thin films. In particular, the incorporation of Li and Gd into the Y₂O₃ lattice could induce remarkable increase in the PL. The highest emission intensity was observed Li-doped Y_1.35Gd_0.6O₃:Eu³⁺ thin films whose brightness was increased by a factor of 4.6 in comparison with that of Li-doped Y₂O₃:Eu³⁺ thin films.     

Characterization of Y2O3 gate dielectric on n-GaAs substrates

Physical and electrical properties of sputtered deposited Y₂O₃ films on NH₄OH treated n-GaAs substrate are investigated. The as-deposited films and interfacial layer formation have been analyzed by using X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). It is found that directly deposited Y₂O₃ on n-GaAs exhibits excellent electrical properties with low frequency dispersion (<5%), hysteresis voltage (0.24 V), and interface trap density (3 × 10¹² eV⁻¹ cm⁻²). The results show that the deposition of Y₂O₃ on n-GaAs can be an effective way to improve the interface quality by the suppression on native oxides formation, especially arsenic oxide which causes Fermi level pinning at high-k/GaAs interface. The Al/Y₂O₃/n-GaAs stack with an equivalent oxide thickness (EOT) of 2.1 nm shows a leakage current density of 3.6 × 10⁻⁶ A cm⁻² at a V_FB of 1 V. While the low-field leakage current conduction mechanism has been found to be dominated by the Schottky emission, Poole-Frenkel emission takes over at high electric fields. The energy band alignment of Y₂O₃ films on n-GaAs substrate is extracted from detailed XPS measurements. The valence and conduction band offsets at Y₂O₃/n-GaAs interfaces are found to be 2.14 and 2.21 eV, respectively.     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Sol-gel derived Y2O3 as an efficient bluish-white phosphor without metal activator ions

In this paper, Y₂O₃ powder phosphors without metal activators were successfully prepared by the sol-gel method. The obtained sample shows an intense bluish-white emission (ranging from 350 to 600 nm, centered at 416 nm) under a wide range of UV light excitation (235-400 nm). The chromaticity coordinates of the sample are x=0.159, y=0.097, and the quantum yield is as high as 64.6%, which is a high value among the phosphor family without metal activators. The luminescent mechanisms have been ascribed to the carbon impurities in the Y₂O₃ host.     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.     

Highly enhanced photoluminescence and X-ray excited luminescence of Li doped Gd2O3:Eu thin films

Transparent Li-doped Gd₂O₃:Eu³⁺ thin-film phosphors were prepared by a modified sol-gel method. The effect of the Li⁺ ions on luminescent properties of the thin film was investigated. The results indicated that incorporation of Li⁺ ions into Gd₂O₃ lattice could result in a remarkable increase on photoluminescence or X-ray excited luminescence, and the strongest emission was observed from Gd_1.84Li_0.08Eu_0.08O_3−δ film, in which the intensity was increased by a factor of 1.9 or 2.3 in comparison with that of Gd_1.92Eu_0.08O₃ film. And it could be achieved the highest intensity for sintering the Gd_1.84Li_0.08Eu_0.08O_3−δ film at 700 °C. Such a temperature is much lower than the typical solid-state reaction temperature for its powder phosphors. This kind of transparent thin-film phosphors may promise for application to micro X-ray imaging system.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

High-throughput characterization of BixY3−xFe5O12 combinatorial thin films by magneto-optical imaging technique

Bi_xY_3−xFe₅O₁₂ thin films have been grown on GGG (Gd₃Ga₅O₁₂) (1 1 1) substrates by the combinatorial composition-spread techniques under substrate temperature (T_sub) ranging from 410 to 700 °C and O₂ pressure of 200 mTorr. In order to study the effect of substrates on the deposition of Bi_xY_3−xFe₅O₁₂ thin films, garnet substrates annealed at 1300 °C for 3 h were also used. Magneto-optical properties were characterized by our home-designed magneto-optical imaging system. From the maps of Faraday rotation angle θ_F, it was evident that the Faraday effect appears only when T_sub = 430-630 °C. θ_F reaches to the maximum value (∼6°/μm, λ = 632 nm) at 500 °C, and is proportional to the Bi contents. XRD and EPMA analyses showed that Bi ions are easier to substitute for Y sites and better crystallinity is obtained for annealed substrates than for commercial ones.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Synthesis of Y2Si2O7:Eu nanocrystal and its optical properties

Nanocrystalline Y₂Si₂O₇:Eu phosphor with an average size about 60 nm is easily prepared using silica aerogel as raw material under ultrasonic irradiation and annealing temperature at 300-600 °C and this nanocrystalline decomposes into Y₂O₃:Eu and silica by heat treatment at 700-900 °C. The excitation broad band centered at 283 and 254 nm results from Eu³⁺ substituting for Y³⁺ in Y₂Si₂O₇ and Y₂O₃/SiO₂, respectively. Compared with Y₂O₃:Eu/SiO₂ crystalline, the PL excitation and emission peaks of Y₂Si₂O₇:Eu nanocrystalline red-shift and lead to the enhance of its luminescence intensity due to the different chemical surroundings of Eu³⁺ in above nanocrystallines. The decrease of PL intensity may be ascribed to quenching effect resulting from more defects in Y₂O₃:Eu/SiO₂ crystalline.     

Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.     

Combustion synthesis and luminescence properties of NaY1−xEux(WO4)2 phosphors

The red phosphors NaY_1−xEu_x(WO₄)₂ with different concentrations of Eu³⁺ were synthesized via the combustion synthesis method. As a comparison, NaEu(WO₄)₂ was prepared by the solid-state reaction method. The phase composition and optical properties of as-synthesized samples were studied by X-ray powder diffraction and photoluminescence spectra. The results show that the red light emission intensity of the combustion synthesized samples under 394 nm excitation increases with increase in Eu³⁺ concentrations and calcination temperatures. Without Y ions doping, the emission spectra intensity of the NaEu(WO₄)₂ phosphor prepared by the combustion method fired at 900 °C is higher than that prepared by the solid-state reaction at 1100 °C. NaEu(WO₄)₂ phosphor synthesized by the combustion method at 1100 °C exhibits the strongest red emission under 394 nm excitation and appropriate CIE chromaticity coordinates (x=0.64, y=0.33) close to the NTSC standard value. Thus, its excellent luminescence properties make it a promising phosphor for near UV InGaN chip-based red-emitting LED application.     

Preparation and photoluminescence characteristics of Eu-doped MgAl1.8Y0.2O4 nanocrystals

A simple combustion route was employed for the preparation of Eu³⁺-doped MgAl_1.8Y_0.2−xO₄ nanocrystals using metal nitrates as precursors and urea as a fuel in a preheated furnace at 500 °C. The powders thus obtained were then fired at 1000 °C for 3 h to get better luminescent properties. The incorporation of Eu³⁺ activator in these nanocrystals was checked by luminescence characteristics. These nanocrystals displayed bright red color on excitation under 254 nm UV source. The main emission peak was assigned to the transition [⁵D₀→⁷F₂] at 615 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies were carried out to understand surface morphological features and the particle size. Crystal structures of the nanocrystals were investigated by the X-ray diffraction (XRD) technique. The crystallite size of the as-prepared nanocrystals was around 29 nm, which was evaluated from the broad XRD peaks. The crystallite size increased to ∼45 nm on further heat treatment at 1000 °C.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).