Synthesis and Properties of a Novel Cycloaliphatic Epoxide

The novel cycloaliphatic epoxide 3,4‐epoxycyclohexylmethyl‐2′,3′‐epoxycyclohexyl ether ( II ) containing an unsymmetrical epoxycyclohexyl moiety linked via an ether bond, and its precursor 3‐cyclohexene‐1‐methyl‐2′‐cyclohexene ether ( I ) were synthesized. Their structure was confirmed by means of elemental analysis, FT‐IR and ¹H NMR spectroscopy. Compared with commercial epoxide ERL‐4221, the newly synthesized epoxide II shows a higher epoxy value (0.85 eq/g) and lower viscosity (86 mpa·s/25°C). The cured product, based on epoxide II and curing agent hexahydro‐4‐methylphthalic anhydride (HMPA), showed higher glass transition temperature (162°C), higher storage modulus at the glass transition region (2.95 GPa), higher crosslinking density (1.60×10^–3 mol/cm³) and a lower coefficient of thermal expansion (6.22×10^–5/°C).     

Poly‐Schiff bases. V. Synthesis and characterization of novel soluble fluorine‐containing polyether azomethines

A new dialdehyde monomer, 4,4′‐(hexafluoroisopropylidine) bis(p‐phenoxy) benzaldehyde, was prepared; it led to a number of novel poly‐Schiff bases in reactions with different diamines, such as 4,4′‐diaminidiphenyl ether, 4,4′‐(isopropylidine) bis(p‐phenoxy) dianiline, 4,4′‐(hexafluoroisopropylidine) bis(p‐phenoxy) dianiline, and benzidine. The polymers were characterized with viscosity measurements, nitrogen analyses, and IR and ¹H NMR spectroscopy. These poly‐Schiff bases showed good thermal stability up to 491 °C for 10% weight loss in thermogravimetric analysis under air and high glass‐transition temperatures up to 215 °C in differential scanning calorimetry. These polymers were soluble in a wide range of organic solvents, such as CHCl₃, dimethylformamide (DMF), dimethyl sulfoxide, and 1‐methyl‐2‐pyrrolidon (NMP), and were insoluble in toluene and acetone. Thin films of these polymers cast from DMF exhibited tensile strengths up to 38 MPa. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 383–388, 2001     

Synthesis and characterization of fluorinated poly(amide imide)s derived from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and aromatic diamines

A series of fluorinated poly(amide imide)s were prepared from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and various aromatic diamines [3,3′,5,5′‐tetramethyl‐4,4′‐diaminediphenylmethane, α,α‐bis(4‐amino‐3,5‐dimethyl phenyl)‐3′‐trifluoromethylphenylmethane, 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene, 4‐(3′‐trifluoromethylphenyl)‐2,6‐bis(3′‐aminophenyl)pyridine, and 1,1‐bis(4′‐aminophenyl)‐1‐(3′‐trifluoromethylphenyl)‐2,2,2‐trifluoroethane]. The fluorinated poly(amide imide)s, prepared by a one‐step polycondensation procedure, had good solubility both in strong aprotic solvents, such as N‐methyl‐2‐pyrrolidinone, dimethylacetamide, dimethylformamide, dimethyl sulfoxide, and cyclopentanone, and in common organic solvents, such as tetrahydrofuran and m‐cresol. Strong and flexible polymer films with tensile strengths of 84–99 MPa and ultimate elongation values of 6–9% were prepared by the casting of polymer solutions onto glass substrates, followed by thermal baking. The poly(amide imide) films exhibited high thermal stability, with glass‐transition temperatures of 257–266 °C and initial thermal decomposition temperatures of greater than 540 °C. The polymer films also had good dielectric properties, with dielectric constants of 3.26–3.52 and dissipation factors of 3.0–7.7 × 10^?3, and acceptable electrical insulating properties. The balance of excellent solubility and thermal stability associated with good mechanical and electrical properties made the poly(amide imide)s potential candidates for practical applications in the microelectronics industry and other related fields. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1831–1840, 2003     

Synthesis and characterization of siloxane resins derived from silphenylene‐siloxane copolymers bearing benzocyclobutene pendant groups

Two bis(dimethylamimo)silanes with benzocyclobutene (BCB) groups, bis(dimethylamino)methyl(4′‐benzocyclobutenyl)silane ( 2 ) and bis(dimethylamino)methyl [2′‐(4′‐benzocyclobutenyl)vinyl]silane ( 4 ), were synthesized from different synthetic routes, which were then employed to prepare two novel silphenylene‐siloxane copolymers (SiBu and SiViBu) bearing latent reactive BCB groups by polycondensation procedure with 1,4‐bis(hydroxydimethylsilyl)benzene. At elevated temperatures these copolymers were readily converted to highly crosslinked films and molding disks with network structures by polymer chain crosslinking, which followed the first‐order kinetic reaction model. The final resins of SiBu and SiViBu demonstrated excellent thermal stability with high glass transition temperatures (218 and 256 °C) and high temperatures at 5% weight loss (553 and 526 °C in N₂, 530 and 508 °C in air). After aging at 300 °C in air for 100 h, the cured resins showed weight loss lower than 4%. The films of cured SiBu and SiViBu also exhibited relatively low dielectric constants of 2.66 and 2.64, low dissipation factors of 2.23 and 2.12 × 10^?3, low water absorptions (≤0.28%), and high transparence in the visible region with cutoff wavelengths of 321 and 314 nm. Moreover, the aged films exhibited good dielectric properties and low water absorptions. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7868–7881, 2008     

Synthesis and characterization of novel polyimide from bis‐(3‐aminophenyl)‐4‐(trifluoromethyl)phenyl phosphine oxide

A novel diamine, bis‐(3‐aminophenyl)‐4‐(trifluoromethyl)phenyl phosphine oxide (mDA3FPPO), containing phosphine oxide and fluorine moieties was prepared via the Grignard reaction from an intermediate, 4‐(trifluoromethyl)phenyl diphenyl phosphine oxide, that was synthesized from diphenylphosphinic chloride and 4‐(trifluoromethyl)bromobenzene, followed by nitration and reduction. The monomer was characterized by Fourier transform infrared (FTIR), ¹H NMR, ³¹P NMR, ¹⁹F NMR spectroscopies; elemental analysis; melting point measurements; and titration and was used to prepare polyimides with a number of dianhydrides such as pyromellitic dianhydride (PMDA), 5,5′‐[2,2,2‐trifluoro‐1‐(trifluoromethyl)ethyliden]‐bis‐1,3‐isobenzofuranedione (6FDA), 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA), and 4,4′‐oxydiphthalic dianhydride (ODPA). Polyimides were synthesized via a conventional two‐step route; preparation of polyamic acids, followed by solution imidization, and the molecular weight were controlled to 20,000 g/mol. Resulting polyimides were characterized by FTIR, NMR, DSC, and intrinsic viscosity measurements. Refractive‐index, dielectric constant, and adhesive properties were also determined. The properties of polyimides were compared with those of polyimides prepared from 1,1‐bis‐(4‐aminophenyl)‐1‐phenyl‐2,2,2‐trifluoroethane (3FDAm) and bis‐(3‐aminophenyl) phenyl phosphine oxide (mDAPPO). The polyimides prepared from mDA3FPPO provided high glass‐transition temperatures (248–311 °C), good thermal stability, excellent solubility, low birefringence (0.0030–0.0036), low dielectric constants (2.9–3.1), and excellent adhesive properties with Cu foils (107 g/mm). © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3335–3347, 2001     

Synthesis of fluorinated polybenzoxazoles with low dielectric constants

Two fluorinated aromatic bis(o‐aminophenol)s, 1,1‐bis(3′‐amino‐4′‐hydroxyphenyl)‐1‐(3′‐trifluoromethylphenyl)‐2,2,2‐trifluoroethane (6FAP) and 1,1‐bis(3′‐amino‐4′‐hydroxyphenyl)‐1‐(3′,5′‐ditrifluoromethylphenyl)‐2,2,2‐trifluoroethane (9FAP) were synthesized, which were allowed to polycondense with aromatic diacyl chlorides to afford the fluorinated aromatic polybenzoxazoles (PBOs) via a conventional two‐step procedure in which the low‐temperature solution polycondensation process was first performed to yield poly(o‐hydroxyamide)s (PHAs) followed by the thermal cyclodehydration to give the PBOs. Experimental results indicated that the PHAs had inherent viscosities in the range of 0.29–0.68 dL/g, showing excellent solubility in organic solvents. The PHAs could be thermally cyclodehydrated into the corresponding PBOs at 260–370 °C. The obtained PBOs exhibited enhanced glass‐transition temperature but decreased solubility with respect to the PHAs. The PBOs showed glass‐transition temperatures in the range of 315–337 °C and excellent thermal stabilities with 5% original weight‐loss temperatures (T₅) of >513 °C. Additionally, the PBO films had average refractive index of 1.5298–1.5656, birefringence of 0.0051–0.0092, and low dielectric constants of 2.57–2.70. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Synthesis and characterization of aromatic cyclolinear phosphazene polyetherketones containing bis‐Spiro‐substituted cyclotriphosphazene unit

A novel monomer, 2,2‐bis‐(4′‐fluorobenzoylphenoxy)‐4,4,6,6‐bis[spiro‐(2′,2″‐dioxy‐1′, 1′‐biphenylyl)] cyclotriphosphazene, was synthesized and polymerized with 4,4′‐difluorobenzophenone as a comonomer and 4,4′‐isopropylidenediphenol or 4,4′‐(hexafluoroisopropylidene) diphenol in N,N‐dimethylacetamide at 162 °C for 4 h to give two series of aromatic cyclolinear phosphazene polyetherketones containing bis‐spiro‐substituted cyclotriphosphazene groups. The structure of the monomer was confirmed by ¹H, ¹³C, and ³¹P NMR. The effect of the incorporation of the bis‐spiro‐substituted cyclotriphosphazene group on the thermal properties of these polymers was investigated by DSC and thermogravimetric analysis. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2993–2997, 2001     

Copolymerization of fluorene‐based main‐chain benzoxazine and their high performance thermosets

A series of fluorene‐based benzoxazine copolymers were synthesized from the mixture of 9,9‐bis(4‐hydroxyphenyl)fluorene and bisphenol A, and 4,4′‐diaminodiphenyloxide and paraformaldehyde. And the cured polybenzoxazine films derived from these copolymers were also obtained. Fourier transform infrared spectroscopy (FTIR) and hydrogen nuclear magnetic resonances confirmed the structure of these benzoxazines. Their molecular weight was estimated by gel permeation chromatography. The curing behavior of the precursors was monitored by FTIR and differential scanning calorimetry. Dynamic mechanical analysis and thermogravimetric analysis were performed to study the thermal properties of the cured polymers. The cured polybenzoxazines exhibit excellent heat resistance with glass transition temperatures (T_g) of 286–317°C, good thermal stability along with the values of 5% weight loss temperatures (T₅) over 340°C, and high char yield over 50% at 800°C. The mechanical properties of the cured polymers were also measured by bending tests. Copyright © 2015 John Wiley & Sons, Ltd.     

Synthesis,characterization, and thermal properties of ladderlike polyepoxysiloxanes

Starting from trichlorosilanes and using 1,4‐phenylenediamine as a template, we have synthesized some ladderlike poly(glycidyl‐co‐alkyl/aryl)siloxanes (polyepoxysiloxanes or polyepoxies for short). The structures of copolymers were confirmed through IR, ¹H NMR, elemental analyses, and gel permeation chromatography. Curing behaviors of these polyepoxies in the absence and presence of a curing agent have been studied with DSC. It was shown that these epoxies could be cured without any curing agent. Copolymers having aromatic groups showed higher curing reactivity than those having alkyl groups. The experimental results also demonstrate that the curing reaction occurred solely via epoxy functionality, not via the condensation reaction of the hydroxy groups located at the end of polymer main chains. The thermal stability of the cured polymers was examined by thermogravimetric analysis. The results confirm that polyepoxies with aromatic groups had better thermal stability than those with alkyl groups. It was also found that polyepoxies cured with a diamine have a higher thermal stability than those cured in the absence of a curing agent. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2215–2222, 2001     

Synthesis and properties of vinyl‐terminated and silicon‐containing polysulfones and polyketones

4‐Fluorophenylsulfonylphenyl‐terminated polysulfone and 4‐fluorobenzoylphenyl ketone were prepared with bisphenol A and an excess of bis‐(4‐fluorophenyl)sulfone or 4,4′‐difluorobenzophenone, respectively, at 160 °C using potassium carbonate in N,N‐dimethylacetamide. The resulting polymers were reacted with 4‐hydroxystyrene to synthesize vinyl‐terminated polysulfones and ketones. The silicon‐containing polysulfones and ketones were prepared from the vinyl‐terminated polymer precursor and various H‐functional silanes or siloxanes. The synthesis of silicon‐containing polymers was achieved by hydrosilation with a rhodium catalyst. It was shown that the hydrosilation reaction proceeds with 55:45 chemoselectivity. The resulting polymers were investigated by ¹H NMR spectroscopy, DSC, and thermogravimetric analysis. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2937–2942, 2001     

Ferrocenophanes with Interannular Nitrogen–Gallium Bridges. 1,3,2‐Diazagalla‐[3]Ferrocenophanes and an 1‐Aza‐3‐Azonia‐2‐Gallata‐[3]Ferrocenophane. Synthesis and Structure

1,1′‐Bis(trimethylsilylamino)ferrocene reacts with trimethyl‐ and triethylgallium to give the μ‐[ferrocene‐1,1′‐diyl‐bis(trimethylsilylamido)]tetraalkyldigallanes. These were converted into the 1,3‐bis(trimethylsilyl)‐2‐alkyl‐2‐pyridine‐1,3,2‐diazagalla‐[3]ferrocenophanes, of which the ethyl derivative was characterized by X‐ray structural analysis. Treatment of gallium trichloride with N,N′‐dilithio‐1,1′‐bis(trimethylsilylamino)ferrocene affords μ‐[ferrocene‐1,1′‐diyl‐bis(trimethylsilylamido)]tetrachlorodigallane along with bis(trimethylsilyl)‐2,2‐dichloro‐1‐aza‐3‐azonia‐2‐gallata‐[3]ferrocenophane as a side product, and both were structurally characterized by X‐ray analysis. The solution‐state structures of the new gallium compounds and aspects of their molecular dynamics in solution were studied by NMR spectroscopy (¹H, ¹³C, ²⁹Si NMR).     

Synthesis and characterization of novel 3,6‐di[3′,5′‐bis(trifluoromethyl)phenyl]pyromellitic dianhydride for polyimide synthesis

A novel dianhydride monomer, 3,6‐di[3′,5′‐bis(trifluoromethyl)phenyl]pyromellitic dianhydride (12FPMDA), was synthesized via a three‐step process: (1) the preparation of 3,5‐bis(trifluoromethyl)benzene boronic acid (6FBB) and 3,6‐dibromo‐1,2,4,5‐tetramethylbenzene (2B4MB) via Grignard and bromination reactions, respectively; (2) the Suzuki cross‐coupling reaction of 6FBB and 2B4MB, resulting in 3,6‐di[3′,5′‐bis(trifluoromethyl)phenyl]tetramethylbenzene (12F4MB); and (3) the oxidation and cyclodehydration of 12F4MB to afford 12FPMDA. 12FPMDA was then characterized by Fourier transform infrared (FTIR), ¹H NMR, ¹⁹F NMR, elemental analysis, and a melting‐point apparatus, and it was used to prepare polyimides with aromatic diamines such as 1,1‐bis(4‐aminophenyl)‐2,2,2‐trifluoroethane and 4,4′‐diaminodiphenylether. Polyimides were synthesized via a two‐step process: (1) the preparation of poly(amic acid) in p‐chlorophenol with isoquinoline and (2) solution imidization at the reflux temperature for 12 h. They were designed to have molecular weights of 20,000 g/mol via off‐stoichiometry. The resulting polyimides were characterized by FTIR, NMR, gel permeation chromatography, differential scanning calorimetry, and thermogravimetric analysis, and their solubility, solution viscosity, water absorption, coefficients of thermal expansion (CTEs), and dielectric constants were also evaluated. The polyimides exhibited excellent solubility even in acetone and toluene, high glass‐transition temperatures (>311 °C), good thermal stability (>518 °C in air), and well‐controlled molecular weights (19,000–21,000 g/mol). They also provided low CTEs (35–50 ppm/°C), water absorption (1.26–1.35 wt %), and dielectric constants (2.49–2.52). © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 4217–4227, 2002     

Preparation and characterization of branched and linear sulfonated poly(ether ketone sulfone) proton exchange membranes for fuel cell applications

Branched sulfonated poly(ether ketone sulfone)s (Br‐SPEKS) were prepared with bisphenol A, bis(4‐fluorophenyl)sulfone, 3,3′‐disodiumsulfonyl‐4,4′‐difluorobenzophenone, and THPE (1,1,1‐tris‐p‐hydroxyphenylethane), respectively, at 180 °C using potassium carbonate in NMP (N‐methylpyrrolidinone). THPE, as a branching agent, was used with 0.4 mol % of bisphenol A to synthesize branched copolymers. Copolymers containing 10–50 mol % disulfonated units were cast from dimethylsulfoxide solutions to form films. Linear sulfonated poly(ether ketone sulfone)s (SPEKS) were also synthesized without THPE. The films were converted from the salt to acid forms with dilute hydrochloric acid. A series of copolymers were studied by Fourier transform infrared, ¹H‐NMR spectroscopy, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion‐exchange capacity (IEC), a measure of proton conductivity, was evaluated. The synthesized Br‐SPEKS and SPEKS membranes exhibit conductivities (25 °C) from 1.04 × 10^?3 to 4.32 × 10^?3 S/cm, water swell from 20.18 to 62.35%, IEC from 0.24 to 0.83 mequiv/g, and methanol diffusion coefficients from 3.2 × 10^?7 to 4.7 × 10^?7 cm²/S at 25 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1792–1799, 2008     

Synthesis of polyphosphonates containing pendant chloromethyl groups by the polyaddition of bis(oxetane)s with phosphonic dichlorides

The polyaddition of 4,4′‐bis[(3‐ethyl‐3‐oxetanyl)methoxy]biphenyl (4,4′‐BEOBP) and phenylphosphonic dichloride (PPDC) with quaternary onium salts as catalysts proceeded under mild reaction conditions to afford a polymer containing phosphorous atoms in its main chain. A polyphosphonate with a high number‐average molecular weight (10,300) was obtained by the reaction of 4,4′‐BEOBP and PPDC in the presence of tetraphenylphosphonium chloride (TPPC) in o‐dichlorobenzene at 130 °C for 24 h. The structure of the resulting polymer was confirmed with IR, ¹H NMR, and ³¹P NMR spectroscopy. Furthermore, it was proved that the polyaddition of certain bis(oxetane)s with phosphonic dichlorides proceeded smoothly to give corresponding polyphosphonates with TPPC as the catalyst. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3835–3846, 2002     

Preparation,thermal properties,and flame retardance of epoxy–silica hybrid resins

A novel epoxy system was developed through the in situ curing of bisphenol A type epoxy and 4,4′‐diaminodiphenylmethane with the sol–gel reaction of a phosphorus‐containing trimethoxysilane (DOPO–GPTMS), which was prepared from the reaction of 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO) with 3‐glycidoxypropyltrimethoxysilane (GPTMS). The preparation of DOPO–GPTMS was confirmed with Fourier transform infrared, ¹H and ³¹P NMR, and elemental analysis. The resulting organic–inorganic hybrid epoxy resins exhibited a high glass‐transition temperature (167 °C), good thermal stability over 320 °C, and a high limited oxygen index of 28.5. The synergism of phosphorus and silicon on flame retardance was observed. Moreover, the kinetics of the thermal oxidative degradation of the hybrid epoxy resins were studied. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2354–2367, 2003     

Synthesis and properties of a cyanate ester containing dicyclopentadiene(II)

A 2,6‐dimethyl phenol‐dicyclopentadiene novolac (DCPDNO) was synthesized from dicyclopentadiene and 2,6‐dimethyl phenol, and the resultant DCPDNO was reacted with cyanogen bromide into 2,6‐dimethyl phenol‐dicyclopentadiene cyanate ester (DCPDCY). The structures of the novolac and cyanate ester were confirmed with Fourier transform infrared spectroscopy, elemental analysis, mass spectrometry (MS), and nuclear magnetic resonance. For the purpose of increasing the mobility of residual DCPDCY during the final stage of curing and achieving a complete reaction of cyanate groups, a small quantity of a monofunctional cyanate ester, 4‐tert‐butylphenol cyanate ester (4TPCY), was added to DCPDCY to form the cyanate ester copolymer. The synthesized DCPDCY was then cured with 4TPCY at various molar ratios. The thermal properties of the cured cyanate ester resins were studied with dynamic mechanical analysis, dielectric analysis, and thermogravimetric analysis. These data were compared with those of the commercial bisphenol A cyanate ester system. Compared with the bisphenol A cyanate ester system, the cured DCPDCY resins exhibited lower dielectric constants (2.52–2.67 at 1 GHz), dissipation factors (0.0054–0.0087 at 1 GHz), glass‐transition temperatures (261–273 °C), thermal stability (5% degradation temperature at 406–450 °C), thermal expansion coefficients (4.8–5.78 × 10^?5/°C before the glass‐transition temperature), and moisture absorption (0.8–1.1%). © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 671–681, 2005     

Synthesis of diallyl‐containing polyimide and the effect of allyl groups on properties

A diallyl‐containing bisphenol, 1,1‐bis(3‐allyl‐4‐hydroxyphenyl)‐1‐(6‐oxido‐6H ‐dibenzo [c,e][1,2] oxaphosphorin‐6‐yl) ethane ( 1 ), was prepared by a two‐step procedure. Then, a diallyl‐containing diamine, 1,1‐bis(3‐allyl‐4‐(4‐aminophenoxy)‐phenyl)‐1‐(6‐oxido‐6H‐dibenzo [c,e][1,2] oxaphosphorin‐6‐yl)ethane ( 3 ), was prepared from the nucleophilic substitution of ( 1 ) with 4‐fluoronitrobenzene, followed by the reduction by Fe/HCl. A flexible polyimide ( 4 ) with curable diallyl linkages was prepared from the condensation of ( 3 ) and 4,4′‐oxydiphthalic anhydride in m‐cresol in the presence of isoquinoline. Curing polyimide ( 4 ) at 300 °C leads to thermosetting polyimide ( 5 ). We discussed the amounts of allyl group on T_g, coefficient of thermal expansion, and thermal stability of thermosetting polyimides, and found that thermal properties and dimensional stability of thermosetting polyimides increase with the amounts of cured allyl moieties. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 513–520     

Preparation and properties of polybenzoxazine/poly(imide‐siloxane) alloys: In situ ring‐opening polymerization of benzoxazine in the presence of soluble poly(imide‐siloxane)s

Benzoxazine monomer (Ba) was blended with soluble poly(imide‐siloxane)s in various weight ratios. The soluble poly(imide‐siloxane)s with and without pendent phenolic groups were prepared from the reaction of 2,2′‐bis(3,4‐dicarboxylphenyl)hexafluoropropane dianhydride with α,ω‐bis(aminopropyl)dimethylsiloxane oligomer (PDMS; molecular weight = 5000) and 3,3′‐dihydroxybenzidine (with OH group) or 4,4′‐diaminodiphenyl ether (without OH group). The onset and maximum of the exotherm due to the ring‐opening polymerization for the pristine Ba appeared on differential scanning calorimetry curves around 200 and 240 °C, respectively. In the presence of poly(imide‐siloxane)s, the exothermic temperatures were lowered: the onset to 130–140 °C and the maximum to 210–220 °C. The exotherm due to the benzoxazine polymerization disappeared after curing at 240 °C for 1 h. Viscoelastic measurements of the cured blends containing poly(imide‐siloxane) with OH functionality showed two glass‐transition temperatures (T_g's), at a low temperature around ?55 °C and at a high temperature around 250–300 °C, displaying phase separation between PDMS and the combined phase consisting of polyimide and polybenzoxazine (PBa) components due to the formation of AB‐crosslinked polymer. For the blends containing poly(imide‐siloxane) without OH functionalities, however, in addition to the T_g due to PDMS, two T_g's were observed in high‐temperature ranges, 230–260 and 300–350 °C, indicating further phase separation between the polyimide and PBa components due to the formation of semi‐interpenetrating networks. In both cases, T_g increased with increasing poly(imide‐siloxane) content. Tensile measurements showed that the toughness of PBa was enhanced by the addition of poly(imide‐siloxane). Thermogravimetric analysis showed that the thermal stability of PBa also was enhanced by the addition of poly(imide‐siloxane). © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2633–2641, 2001     

Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton‐exchange membranes for fuel cells

A novel sulfonated diamine monomer, 2,2′‐bis(p‐aminophenoxy)‐1,1′‐binaphthyl‐6,6′‐disulfonic acid (BNDADS), was synthesized. A series of sulfonated polyimide copolymers containing 30–80 mol % BNDADS as a hydrophilic component were prepared. The copolymers showed excellent solubility and good film‐forming capability. Atomic force microscopy phase images clearly showed hydrophilic/hydrophobic microphase separation. The relationship between the proton conductivity and degree of sulfonation was examined. The sulfonated polyimide copolymer with 60 mol % BNDADS showed higher proton conductivity (0.0945–0.161 S/cm) at 20–80 °C in liquid water. The membranes exhibited methanol permeability from 9 × 10^?8 to 5 × 10^?7 cm²/s at 20 °C, which was much lower than that of Nafion (2 × 10^?6cm²/s). The copolymers were thermally stable up to 300 °C. The sulfonated polyimide copolymers with 30–60 mol % BNDADS showed reasonable mechanical strength; for example, the maximum tensile strength at break of the sulfonated polyimide copolymer with 40 mol % BNDADS was 80.6 MPa under high moisture conditions. The optimum concentration of BNDADS was found to be 60 mol % from the viewpoint of proton conductivity, methanol permeability, and membrane stability. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 222–231, 2007     

Synthesis and characterization of novel fully aliphatic polyimidosiloxanes based on alicyclic or adamantyl diamines

A series of fully aliphatic polyimidosiloxanes (APISiO) were prepared by poly(addition/condensation) reaction of bicyclo [2,2,2] oct‐7‐ene‐2,3,5,6‐tetracarboxylic dianhydride or cyclobutane‐1,2,3,4‐tetracarboxylic dianhydride and varying compositions of 1,3‐bis (3‐amino propyl)‐tetra methyl disiloxane and rigid adamantyl diamines (1,3‐diaminoadamantane or 3,3′‐diamino‐1,1′‐diadamantane) or flexible alicyclic diamines (4,4′‐methylene bis(cyclohexylamine) or 4,4′‐methylene bis(2‐methylcyclohexylamine)). High temperature one‐step synthesis in m‐cresol was employed to obtain APISiOs with intrinsic viscosity in the range of 0.28–0.59 dL/g. The final materials were characterized by ¹H and ¹³C NMR, ²⁹Si‐MAS‐NMR and IR spectroscopic analysis, thermogravimetric and differential scanning calorimetric analysis, and wide angle X‐ray diffractometry. UV–visible spectra revealed the optical behavior of the polyimides. It was found that the APISiOs containing appropriate ratio of adamantyl moieties together with flexible aliphatic siloxane groups exhibit good thermal and mechanical stabilities, solubility, fair transparency, and low dielectric constant (2.4–2.7). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5254–5270, 2006