Effect of synthesis conditions on the preparation of titanium dioxides from peroxotitanate solution and their photocatalytic activity

Nanosized TiO₂ particles were prepared by the hydrothermal method from the amorphous powders which were precipitated in an aqueous peroxotitanate solution. The physical properties of the nanosized TiO₂ particles prepared were investigated. We also examined the activity of TiO₂ particles as a photocatalyst on the decomposition of orange II. The titania sol can be successfully crystallized to the anatase phase through hydrothermal aging at temperatures higher than 160°C. The particle size increases from 18 to 26 nm as the synthesis temperature increases from 140 to 200°C. Titania particles prepared at 180°C show the highest activity, and titania particles calcined at 400°C show also the highest activity on the photocatalytic decomposition of orange II.     

Sensor Performance of Nanostructured TiO<Subscript>2</Subscript>–SnO<Subscript>2</Subscript> Films Prepared by an Aqueous Sol–Gel Process

Nanostructured TiO₂–SnO₂ thin films and powders were prepared by a facile aqueous particulate sol–gel route. The prepared sols showed a narrow particle size distribution with hydrodynamic diameter in the range 17.2–19.3 nm. Moreover, the sols were stable over 5 months, since the constant zeta potential was measured during this period. The effect of Sn:Ti molar ratio was studied on the crystallisation behaviour of the products. X-ray diffraction analysis revealed that the powders were crystallised at the low temperature of 400 °C containing anatase-TiO₂, rutile-TiO₂ and cassiterite-SnO₂ phases, depending on annealing temperature and Sn:Ti molar ratio. Furthermore, it was found that SnO₂ retarded the anatase to rutile transformation up to 800 °C. The activation energy of crystallite growth was calculated in the range 0.96–6.87 kJ/mol. Transmission electron microscope image showed that one of the smallest crystallite sizes was obtained for TiO₂–SnO₂ binary mixed oxide, being 3 nm at 600 °C. Field emission scanning electron microscope analysis revealed that the deposited thin films had nanostructured morphology with the average grain size in the range 20–40 nm at 600 °C. Thin films produced under optimized conditions showed excellent microstructural properties for gas sensing applications. They exhibited a remarkable response towards low concentrations of CO gas at low operating temperature of 200 °C, resulting in increased thermal stability of sensing films as well as a decrease in their power consumption.     

Preparation of highly stable TiO<Subscript>2</Subscript> sols and nanocrystalline TiO<Subscript>2</Subscript> films via a low temperature sol–gel route

Highly stable TiO₂ sols were prepared by adjusting the water-to-titanium molar ratio to ~4 in the process of hydrolysis and condensation of titanium isopropoxide in ethanol with HNO₃. Particularly, long-term stable TiO₂ sols were prepared without adding any chemical additives. Anatase TiO₂ nanocrystallites with sizes of 3–5 nm in diameter were uniformly dispersed in the stable sol. Crystallized TiO₂ films were successfully deposited on Si (100) using the stable sol via a dip-coating process with low temperature curing at as low as 100 °C. The synthesized TiO₂ sols and films are promising for use in flexible or dye-sensitized solar cells.     

Preparation and characterization of TiO2 sols and their UV-cured hybrid thin films on plastic substrates

In this research, TiO₂ sols were synthesized via a sol?Cgel reaction at room temperature followed by heating under reflux. Hybrid thin films were prepared using the TiO₂ sols and dipentaerythritol hexacrylate on poly(methyl methacrylate) substrates via spin coating followed by UV-curing. The images of transmission electron microscopy (TEM) and results of dynamic light scattering (DSL) showed that some originally synthesized TiO₂ nanoparticles aggregated while many small-sized (~5?nm) TiO₂ nanoparticles still existed after reflux heating. The synthesized TiO₂ sols showed poor photocatalytic ability, which might avoid degradation of organic moieties in the hybrids. The refractive indices of the hybrid thin films were increased from 1.66 to 1.82 while the water contact angles on the thin films were increased from 70.2° to 87.7° with the increment of TiO₂ content. Increasing the heating time of the TiO₂ sol resulted in an increase in the refractive index and contact angle.     

Ultra-low expansion glass from gels

Pyrolysis of mixed titanium and silicon metal halides produces a commercial glass (7.4% TiO₂) with ultra-low thermal expansion that is essentially zero over the temperature range of 0 to 300°C. A colloidal particulate gel process involving potassium silicate, titania sol and formamide gel reagent was found to produce glass compositions with similar low expansion behavior. Due to the strongly basic nature of the precursor solutions, special titania sols had to be prepared that were stable in these alkali silicate solutions. The preferred TiO₂ sols were those containing quaternary ammonium stabilizing counter-ions. These sols served not only as the source of homogeneously distributed titania, but they may also serve as nucleating species that contribute to particle growth and pore size control of the gel network. The large pore (0.3 µm) TiO₂/SiO₂ gel structures were easily dealkalized, dried and sintered to uncracked glass shapes. Plates up to 9.5 cm×6.6 cm× 0.5 cm thick and some intricate cast shapes were produced and their glass properties evaluated.     

Effect of calcination temperature on the microstructure of porous TiO<Subscript>2</Subscript> film

To obtain porous TiO₂ film, the precursor sol was prepared by hydrolysis of Ti isopropoxide and then complexed with trehalose dihydrate. The porous TiO₂ film was fabricated by the dip-coating technique on glass substrates using this solution. The TiO₂ film was calcined at 500 °C. The maximum thickness of the film from one-run dip-coating was ca. 740 nm. The film was composed of nanosized particle and pores. The porosity of the TiO₂ film was increased by addition of trehalose dihydrate to the sol. The porous TiO₂ films were calcined at different temperatures. The effects of calcination temperature on the microstructure of the porous TiO₂ film were investigated. The porous film prepared from sol containing trehalose still kept the porous structure after calcination at 950 °C. The phase transition temperature of the film from anatase to rutile was shifted from 650 to 700 °C by addition of trehalose to the sol.     

Synthesis of nanostructured titania/zirconia membrane and investigation of its physical separation and photocatalytic properties in treatment of textile industries wastewater

Nanostructured TiO₂/ZrO₂ composite membranes with varying compositions were obtained by sol–gel technique. The influence of 0–30 mol% zirconia doping on microstructure, water permeability, photocatalytic and physical separation properties, removal of methyl violet of textile industries wastewater and thermal and mechanical stability of titania/zirconia composite membranes was described. Firstly, alumina supports were coated with TiO₂ intermediate layers using the colloidal sol–gel route. The TiO₂/ZrO₂ composite sols were prepared via a polymeric sol–gel method and dip-coated on TiO₂ intermediate layer. The samples were characterized by DLS, TG-DTA, XRD, FTIR, BET-BJH, UV–visible, SEM, TEM and AFM. It was shown that zirconia retards the phase transformation of anatase to rutile until at least 700 °C. The minimum pore size and maximum surface area obtained were 1.2 nm and 153 m²/g, respectively, attributed to the sample with 20 mol% zirconia. The mechanical strength of titania membranes was significantly improved by addition of zirconia. The most methyl violet removal efficiency obtained, with and without UV-irradiation, is 80.8 and 72.6%, respectively, attributed to the sample with 20 mol% zirconia.     

The photocatalytic properties of Ti–Mo oxides prepared by a simple sol–gel route

Powders containing mixtures of titania and molybdite in different ratios were prepared by sol–gel processing. The sols were dried and subsequently calcined at 300, 500 and 700 °C. Depending on the ratio of Ti and Mo in the initial sol and the calcination temperature, Ti-doped MoO₃, TiO₂/MoO₃ or Mo-doped TiO₂ have been formed. The as prepared samples were characterised by scanning electron microscopy with attached X-ray dispersive energy analysis, X-ray diffractometry, Raman spectroscopy, gas adsorption and optical characterisation by ultraviolet/visible spectroscopy. The latter was used for the analysis of the photocatalytic properties on the decolourisation of methylene blue solutions under visible light irradiation. The phase composition, the specific surface and the photocatalytic activity were influenced by the molybdenum content and the calcination temperature. The final molybdenum content in the samples additionally depends on the calcination temperature. The optimum photocatalytic properties were observed or Ti-doped MoO₃.     

Synthesis of highly pure nanocrystalline and mesoporous CaTiO3 by a particulate sol–gel route at the low temperature

The low temperature perovskite-type calcium titanate (CaTiO₃) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol–gel route. The prepared sol had a narrow particle size distribution about 17 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that, the synthesized powders had highly pure and crystallized CaTiO₃ structure with preferable orientation growth along (1 2 1) direction at 400–800 °C. The activation energy of crystal growth was calculated 5.73 kJ/mol. Furthermore, transmission electron microscope images showed that the average crystallite size of the powders annealed at 400 °C was around 3.5 nm. Field emission scanning electron microscope analysis and atomic force microscope images revealed that, the deposited thin films had uniform, mesoporous and nanocrystalline structure with the average grain size in the range 33–39 nm depending on annealing temperature. Based on Brunauer–Emmett–Teller (BET) analysis, the synthesized powders showed mesoporous structure with BET surface area in the range 51–21 m²/g at 400–800 °C. One of the smallest crystallite size and one of the highest surface areas reported in the literature is obtained which can be used in many applications, such as photocatalysts.     

Low temperature nanostructured lithium titanates: controlling the phase composition, crystal structure and surface area

Low temperature lithium titanate compounds (i.e., Li₄Ti₅O₁₂ and Li₂TiO₃) with nanocrystalline and mesoporous structure were prepared by a straightforward aqueous particulate sol–gel route. The effect of Li:Ti molar ratio was studied on crystallisation behaviour of lithium titanates. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders were crystallised at the low temperature of 500 °C and the short annealing time of 1 h. Moreover, it was found that Li:Ti molar ratio and annealing temperature influence the preferable orientation growth of the lithium titanate compounds. Transmission electron microscope (TEM) images showed that the average crystallite size of the powders annealed at 400 °C was in the range 2–4 nm and a gradual increase occurred up to 10 nm by heat treatment at 800 °C. Field emission scanning electron microscope (FE-SEM) analysis revealed that the deposited thin films had mesoporous and nanocrystalline structure with the average grain size of 21–28 nm at 600 °C and 49–62 nm at 800 °C depending upon the Li:Ti molar ratio. Moreover, atomic force microscope (AFM) images confirmed that the lithium titanate films had columnar like morphology at 600 °C, whereas they showed hill-valley like morphology at 800 °C. Based on Brunauer–Emmett–Taylor (BET) analysis, the synthesized powders showed mesoporous structure containing pores with needle and plate shapes. The surface area of the powders was enhanced by increasing Li:Ti molar ratio and reached as high as 77 m²/g for the ratio of Li:Ti = 75:25 at 500 °C. This is one of the smallest crystallite size and the highest surface areas reported in the literature, and the materials could be used in many applications such as rechargeable lithium batteries and tritium breeding materials.     

Crystallization behaviour of TiO2–ZrO2 composite nanoparticles

Nano-composite TiO₂?CZrO₂ materials were prepared via sol?Cgel processes by hydrolysis of mixtures of titanium- and zirconium-containing alkoxides with TiO₂:ZrO₂ ratios of 1:2, 1:1, 2:1, and 10:1. Precipitated powders were dried at room temperature and annealed in ambient air at temperatures between 350 and 500?°C for 4?h. Pure TiO₂ and ZrO₂ powders were synthesized for comparison. Samples were characterized with X-ray diffraction (XRD) and X-ray absorption near edge fine structure (XANES). The detailed analysis of those data provides the crystalline and amorphous phase composition as well as the crystallite particle size. According to XRD and XANES analysis, only the two pure oxide samples and one of the composite samples with a composition TiO₂:ZrO₂?=?10:1, crystallized. Both titania containing powders, the pure TiO₂ and the TiO₂:ZrO₂?=?10:1 composite, were found to crystallize in the anatase structure. ZrO₂ was found to stay amorphous in the composites but crystalline in the pure oxide. In the crystallized composite TiO₂:ZrO₂?=?10:1 sample, the concentration of the amorphous phase remains larger than in pure TiO₂ samples, but the crystallite size was found to be nearly constant with increasing annealing temperature in contrast to the increasing particle size of pure TiO₂-samples. Pure TiO₂ precipitates are amorphous directly after preparation, however they crystallize after 6?month storage at ambient conditions by aging. Such an aging was not observed for the TiO₂:ZrO₂ composites.     

Synthesis of nanosized TiO2/SiO2 particles using microwave processes and their photocatalytic activity on the decomposition of orange II

The nanosized titania and TiO₂/SiO₂ particles were prepared by the microwave-hydrothermal method. The effect of physical properties TTIP/TEOS ratio and calcination temperature has been investigated. The major phase of the pure TiO₂ particle is of the anatase structure, and a rutile peak was observed above 800°C. In TiO₂/SiO₂ particles, however, no significant rutile phase was observed, although the calcination temperature was 900°C. No peaks for the silica crystal phase were observed at either silica/titania ratio. The crystallite size of TiO₂/SiO₂ particles decreases as compared to pure TiO₂ at high calcination temperatures. The TiO₂/SiO₂ particles show higher activity on the photocatalytic decomposition of orange II as compared to pure TiO₂ particles.     

Low-temperature synthesis of photocatalytic TiO2 thin film from aqueous anatase precursor sols

Anatase TiO₂ sols (RS) were synthesized by peptizing the hydrolysis of titanyl sulfate in abundant hydrogen peroxide solution and subsequent reflux to enhance crystallization. The influences of various reflux time on crystallinity, morphology, and size of the obtained TiO₂ sol and dried TiO₂ film particles were investigated. At room temperature, crystalline TiO₂ thin film was deposited on glass silde from the as prepared TiO₂ sol by dip-coating method. No further thermal posttreatment was required to eliminate organics from the film or to induce titania crystallization. TiO₂ thin film on substrates could be thickened by means of consecutive dip-coating process. Titania film thus obtained was transparent and showed proper adherence. The photocatalytic activities of the TiO₂ thin film was assessed by the degradation of methyl orange in aqueous solution. The preparation process of photocatalytic TiO₂ thin film was quite simple and a low-temperature route.     

Synthesis of bimodal porous structured TiO2 microsphere with high photocatalytic activity for water treatment

In this work bimodal structured titanium dioxide (TiO₂) microsphere has been prepared from commercial TiO₂ powder and nano-sized titania gel via sol–gel spray-coating technique. Crystallization and transformation behavior of titania gel were investigated. The results revealed that the crystallization and transformation of anatase particles were substantially affected by the concentration of solvent and calcination temperature. Anatase crystallite size of 10 nm was obtained at mole ratio of solvent/precursor 50/1 and calcination temperature of 450 °C. The prepared nano-sized titania gel was embedded within the core (commercial TiO₂, P25) during the spraying process. The prepared TiO₂ microsphere was characterized using X-ray diffractometer (XRD), scanning electron microscope (SEM), field emission electron microscope (FESEM) and micropore analysis. The photocatalytic activity was monitored by following the degradation of phenol with activity benchmarked against commercial P25 (Degussa). The increase of photocatalytic activity of TiO₂ microsphere was attributed to the nano-sized anatase crystallite which has been incorporated into the TiO₂ microsphere.     

Mesoporous and nanocrystalline sol–gel derived NiTiO3 at the low temperature: Controlling the structure,size and surface area by Ni:Ti molar ratio

Nanocrystalline nickel titanate (NiTiO₃) thin films and powders with mesoporous structure were produced at the low temperature of 500 °C by a straightforward particulate sol–gel route. The sols were prepared in various Ni:Ti molar ratios. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained mixtures of the NiTiO₃ and NiO phases, as well as the anatase-TiO₂ and the rutile-TiO₂ depending on the annealing temperature and Ni:Ti molar ratio. Moreover, it was found that Ni:Ti molar ratio influences the preferable orientation growth of the nickel titanate, being on (202) planes for the nickel dominant powders (Ni:Ti ≥ 75:25) and on (104) planes for the rest of the powders (Ni:Ti: ≤ 50:50). The average crystallite size of the powders annealed at 500 °C was in the range 1.5–2.4 nm and a gradual increase occurred up to 8 nm by heat treatment at 800 °C. The activation energy of crystal growth decreased with an increase of Ni:Ti molar ratio, calculated in the range 24.93–37.17 kJ/mol. Field emission scanning electron microscope analysis revealed that the deposited thin films had mesoporous and nanocrystalline structure with the average grain size of 20–35 nm. Moreover, atomic force microscope images presented that the thin films had a hill-valley like morphology with roughness mean square in the range 41–57 nm. Based on Brunauer–Emmett–Taylor analysis, the synthesized powders showed mesoporous structure containing pores with needle and plate like shapes. The mesoporous structure of the powders was stable at high annealing temperatures and one of the highest surface areas (i.e., 156 m²/g) reported in the literature was obtained for the powder containing Ni:Ti = 50:50 at 500 °C.     

Titania-lanthanum phosphate photoactive and hydrophobic new generation catalyst

Titania-lanthanum phosphate nanocomposites with multifunctional properties have been synthesized by aqueous sol-gel method. The precursor sols with varying TiO₂:LaPO₄ ratios were applied as thin coating on glass substrates in order to be transparent, hydrophobic, photocatalytically active coatings. The phase compositions of the composite powders were identified by powder X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM). The anatase phase of TiO₂ in TiO₂-LaPO₄ composite precursors was found to be stable even on annealing at 800 °C. The glass substrates, coated with TL1 (TiO₂-LaPO₄ composition with 1 mol% LaPO₄) and TL50 (composite precursor containing TiO₂ and LaPO₄ with molar ratio 1:1) sols and annealed at 400 °C, produced contact angles of 74° and 92°, respectively, though it is only 62° for pure TiO₂ coating. The glass substrates, coated with TL50 sol, produced surfaces with relatively high roughness and uneven morphology. The TL1 material, annealed at 800 °C, has shown the highest UV photoactivity with an apparent rate constant, k_app=24×10⁻³ min⁻¹, which is over five times higher than that observed with standard Hombikat UV 100 (k_app=4×10⁻³ min⁻¹). The photoactivity combined with a moderate contact angle (85.3°) shows that this material has a promise as an efficient self-cleaning precursor.     

Preparation and characterization of highly photoactive nanocrystalline TiO<Subscript>2</Subscript> powders by solvent evaporationinduced crystallization method

Highly photoactive bi-phase nanocrystalline TiO₂ photocatalyst was prepared by a solvent evaporation-induced crystallization (SEIC) method, and calcined at different temperatures. The obtained TiO₂ photocatalyst was characterized with X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET surface areas. The photocatalytic activity was evaluated by the photocatalytic oxidation of acetone in air. The results show that solvent evaporation can promote the crystallization and phase transformation of TiO₂ at 100°C. When calcination temperatures are below 600°C, the prepared TiO₂ powders show bimodal pore size distributions in the mesoporous region. At 700°C, the pore size distributions exhibit monomodal distribution of the inter-aggregated pores due to the collapse of the intra-aggregated pores. At 100°C, the obtained TiO₂ photocatalyst by this method shows good photocatalytic activity, and at 400°C, its photocatalytic activity exceeds that of Degussa P25. This may be attributed to the fact that the prepared TiO₂ photocatalyst has higher specific surface areas, smaller crystallite size and bimodal pore size distribution.     

Sol–gel synthesis,characterization and photocatalytic activity of mesoporous TiO<Subscript>2</Subscript>/γ-Al<Subscript>2</Subscript>O<Subscript>3 </Subscript>granules

Mesoporous TiO₂/γ-Al₂O₃ composite granules were prepared by combining sol–gel/oil-drop method, using various titania solution. The product granules can be used as a photocatalyst or adsorbent in moving, fluidized bed reactors. The phase composition and pore structure of the granules can be controlled by calcination temperature and using different titania solution. In the photocatalysis of NH₃ decomposition, TiO₂/γ-Al₂O₃ granules using Degussa P25 powder treated thermally at 450 °C showed the highest catalytic ability. However, TiO₂/γ-Al₂O₃ granules using titania made by hydrothermal method had comparable performance in NH₃ decomposition.     

High surface area sol–gel alumina–titania nanocatalyst

Alumina–titania mixed oxide nanocatalysts with molar ratios = 1:0.5, 1:1, 1:2, 1:5 have been synthesized by adopting a hybrid sol–gel route using boehmite sol as the precursor for alumina and titanium isopropoxide as the precursor for titania. The thermal properties, XRD phase analysis, specific surface area, adsorption isotherms and pore size details along with temperature programmed desorption of ammonia are presented. A specific surface area as high as 291 m²/g is observed for 1:5 Al₂O₃/TiO₂ composition calcined at 400 °C, but the same composition when calcined at 1,000 °C, resulted in a surface area of 4 m²/g, while 1:0.5 composition shows a specific surface area of 41 m²/g at 1,000 °C. Temperature programmed desorption (of ammonia) results show more acidic nature for the titania rich mixed oxide compositions. Transmission electron microscopy of low and high titania content samples calcined at 400 °C, shows homogeneous distribution of phases in the nano range. In the mixed oxide, the particle size ranges between 10–20 nm depending on titania content. The detailed porosity data analysis contributes very much in designing alumina–titania mixed oxide nanocatalysts.     

Influence of sintering on the structural and electronic properties of TiO2 nanoporous layers prepared via a non-sol–gel approach

In this work, a nonaqueous method is used to fabricate thin TiO₂ layers. In contrast to the common aqueous sol–gel approach, our method yields layers of anatase nanocrystallites already at low temperature. Raman spectroscopy, electron microscopy and charge extraction by linearly increasing voltage are employed to study the effect of sintering temperature on the structural and electronic properties of the nanocrystalline TiO₂ layer. Raising the sintering temperature from 120 to 600?°C is found to alter the chemical composition, the layer’s porosity and its surface but not the crystal phase. The room temperature mobility increases from 2?×?10^?6 to 3?×?10^?5?cm²/Vs when the sinter temperature is increased from 400 to 600?°C, which is explained by a better interparticle connectivity. Solar cells comprising such nanoporous TiO₂ layers and a soluble derivative of cyclohexylamino-poly(p-phenylene vinylene) were fabricated and studied with regard to their structural and photovoltaic properties. We found only weak polymer infiltration into the oxide layer for sintering temperatures up to 550?°C, while the polymer penetrated deeply into titania layers that were sintered at 600?°C. Best photovoltaic performance was reached with a nanoporous TiO₂ film sintered at 550?°C, which yielded a power conversion efficiency of 0.5?%. Noticeably, samples with the TiO₂ layer dried at 120?°C displayed short-circuit currents and open circuit voltages only about 15–20?% lower than for the most efficient devices, meaning that our nonaqueous route yields titania layers with reasonable transport properties even at low sintering temperatures.