Tracer diffusion of ¹⁸O in dense, polycrystalline La_1−xSr_xCoO₃ for x = 0.1 has been measured in the temperature range 400 to 600 °C and at 500 °C for x = 0.2 at an oxygen partial pressure of 1 × 10⁵ Pa. Depth profiles were obtained by secondary ion mass spectrometry. The diffusion coefficient for La_0.9Sr_0.1CoO₃ is given by D = (17–247) exp[(−232 ± 8 kJ/mole)/RT] cm²/s. This value is several orders of magnitude lower than D extrapolated from the results for x = 0.2 measured in the 700–900 °C temperature range. One possible explanation for the discrepancy is that the two measurements reflect different diffusion paths. As expected, La_0.8Sr_0.2CoO₃ exhibits a higher diffusivity at 500 °C than does La_0.9Sr_0.1CoO₃.     

Intercalation thermodynamics and chemical diffusion of oxygen in the solid solution YBa2Cu3−xCoxO6+δ

The equilibrium oxygen content as a function of the temperature and oxygen pressure was measured for the solid solution YBa₂Cu_3−xCo_xO_6+δ, where x=0, 0.2, 0.4, 0.6, 0.8, by using coulometric titration in the temperature range 600–850°C and oxygen pressures between 10⁻⁵ and 1.0 atm. The change in the partial molar enthalpy and entropy of the intercalated oxygen was determined at different oxygen and cobalt contents. The oxygen chemical diffusion was studied by thermogravimetric relaxation in the oxygen-controlled atmosphere. The thermodynamic data were employed to determine how the chemical diffusion coefficient, the thermodynamic factor and the random-diffusion coefficient depend on oxygen content in specimens with different cobalt concentration. The oxygen intercalation thermodynamics and diffusivity results provide evidence of ordering phenomena on a microscopic scale in the basal plane of the tetragonal solid solution YBa₂Cu_3−xCo_xO_6+δ. A model for the oxygen diffusion is suggested to explain the large difference between the random and tracer diffusion coefficients in YBa₂Cu₃O_6+δ     

Properties of nonstoichiometric Pr0.6−xSr0.4MnO3 as the cathodes of SOFCs

A series of samples Pr_0.6−xSr_0.4MnO₃ (x=0, 0.01, 0.05, 0.1, 0.15, 0.2) were synthesized by a solid state reaction method. Pr deficiency at the A site has a great effect on the properties of Pr_0.6−xSr_0.4MnO₃ as the cathode of SOFCs (solid oxide fuel cells). Compared to the commonly used La_0.6Sr_0.4MnO₃ and La_0.55Sr_0.4MnO₃ cathode, Pr_0.6−xSr_0.4MnO₃ is better in the properties of conductivity, overpotential and impedance. In all the samples, the one with x=0.05, Pr_0.55Sr_0.4MnO₃, revealed the best performance in the measured temperature range.     

Crystal structure, electrical and magnetic properties of La1 − xSrxCoO3 − y

The crystal structure and properties of La_{1 − x}Sr_xCoO_{3 − y} with strontium contents ranging from x = 0.1 to x = 0.7 have been studied. The lattice parameters were measured as a function of temperature (4.2–400 K) and the crystal structure was found to change from rhombohedral (at low temperatures and values of x) to cubic. While LaCoO₃ is paramagnetic the oxides in the composition range 0.2 < x < 0.6 are soft ferromagnets. The strontium additions are compensated by the formation of Co⁴⁺ (cobalt ions with one positive effective charge, Co_Co^.) and oxygen vacancies (V_o^..). From the results it is concluded that the relative importance of oxygen vacancies increases with increasing temperature and decreasing oxygen activity. As a result the concentration of electronic charge carriers — and the resultant electrical conductivity — decrease with increasing temperature. The defect structure is discussed and it is concluded that defect associations — probably between oxygen vacancies and strontium ions — and formation of microdomains of perovskite-related phases are important aspects of the overall structure of these perovskite phases.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Perovskite-like system (Sr,La)(Fe,Ga)O3−δ: structure and ionic transport under oxidizing conditions

The maximum solid solubility of gallium in the perovskite-type La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.40–0.80; y=0–0.60) was found to vary in the approximate range y=0.25–0.45, decreasing when x increases. Crystal lattice of the perovskite phases, formed in atmospheric air, was studied by X-ray diffraction (XRD) and neutron diffraction and identified as cubic. Doping with Ga results in increasing unit cell volume, while the thermal expansion and total conductivity of (La,Sr)(Fe,Ga)O_3−δ in air decrease with gallium additions. The average thermal expansion coefficients (TECs) are in the range (11.7–16.0)×10⁻⁶ K⁻¹ at 300–800 K and (19.3–26.7)×10⁻⁶ K⁻¹ at 800–1100 K. At oxygen partial pressures close to atmospheric air, the oxygen permeation fluxes through La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.7–0.8; y=0.2–0.4) membranes are determined by the bulk ambipolar conductivity; the limiting effect of the oxygen surface exchange was found negligible. Decreasing strontium and gallium concentrations leads to a greater role of the exchange processes. As for many other perovskite systems, the oxygen ionic conductivity of La_1−xSr_xFe_1−yGa_yO_3−δ increases with strontium content up to x=0.70 and decreases on further doping, probably due to association of oxygen vacancies. Incorporation of moderate amounts of gallium into the B sublattice results in increasing structural disorder, higher ionic conductivity at temperatures below 1170 K, and lower activation energy for the ionic transport.     

Determination of different oxygen transport mechanisms and measurement of the oxygen ion conductivity of Y1Ba2Cu3O7−x

By undertaking AC electrochemical impedance experiments on yttria stabilised zirconia electrolytes with polished Y₁Ba₂Cu₃O_7−x electrodes, the activation energy for oxygen ion transport within the bulk of Y₁Ba₂Cu₃O_7−x, in air, over the temperature range 823 K–1043 K, was determined to be 1.50 ± 0.05 eV. At 1000 K the oxygen ionic conductivity was calculated to be around one order of magnitude lower than that in yttria stabilised zirconia. Typical calculated values were σ=5×10⁻⁵ (ω cm)⁻¹ and 6×10⁻³ (ω cm)⁻¹ at the respective temperatures 823 K and 1043 K. By employing a similar cell but with Y₁Ba₂Cu₃O_7−x paste electrodes, oxygen transfer between the Y₁Ba₂Cu₃O_7−x and the electrolyte was found to occur via a surface diffusional processes. Over the temperature range 873 K–1098 K, in air, the activation energy for in-diffusion at the surface was found to be 1.4±0.1 eV and that for out-diffusion at the surface to be 1.76±0.05 eV.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

An electrochemical investigation of Li intercalation in the sol-gel LiMn2O4 spinel oxide

An alternative approach for obtaining the LiMn₂O₄ spinel phase is provided by the use of the sol-gel method in aqueous solution. The main electrochemical properties of the sol-gel LiMn₂O₄ phase are reported. In addition to chronopotentiometric and voltammetric experiments, the kinetics of the electrochemical insertion–extraction of lithium in Li_xMn₂O₄ (0.25<x<1) has been investigated using ac impedance spectroscopy. The strong variation of the chemical diffusion coefficient D_Li vs x, in the range 10⁻⁸–10⁻¹¹ cm² s⁻¹ (D_Li is found to be maximum for x=0.55) is critically discussed.     

Superconductivity and crystallographic properties of La2 − xMxCuO4 − δ (M = Na, K)

Superconductivity and crystallographic properties of La_{2 − x}M_xCuO_{4 − δ} (M = Na, K) are studied. In the La_{2 − x}M_xCuO_{4 − δ} system, superconductivity is detected for x 0.2. Oxygen content analysis shows that the system has more oxygen vacancies than the La_{2 − x}Sr_xCuO_{4 − δ} system. These oxygen vacancies may reduce the hole concentration, and high Na-doping is needed to produce superconductivity. In the La_{2 − x}K_xCuO_{4 − δ} system, superconductivity is observed for the first time. Resistivity and magnetic susceptibility measurements show that T_c(onset) is 40 K and the Meissner volume fraction is about 4% for x = 0.7. The system changes from orthorhombic to a tetragonal K₂NiF₄ structure at x ≈ 0.3 and only tetragonal samples show superconductivity.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Oxygen nonstoichiometry and phase transitions of the neodymium-rich Nd1+xBa2−xCu3Oz solid solution

On the basis of chemical, thermal analysis and Cu K-edge X-ray absorption measurements, oxygen content in the Nd_1+xBa_2−xCu₃O_z solid solution was determined between 1000°C in air and 400°C in oxygen for x=0.05–0.9 compositions. It has been observed that the oxygen nonstoichiometry Δz of the Nd_1+xBa_2−xCu₃O_7+x/2−Δz solid solution decreases 2–2.5 times for a large substitution (Δz≈0.3–0.33 for x=0.9), despite of the acclaimed higher total oxygen content. The difference in nonstoichiometry is explained by a higher average value of the copper oxidation state (ACV), which is vital for the solid solution with large x even at elevated temperatures (ACV≈2–2.05 for x>0.3 at 1000°C, PO₂=0.21 atm). On the contrary, the ACV after complete oxygenation is almost constant (about 2.25–2.3) for the whole series. The x-dependence of the oxygen content is not monotonous and structural phase transitions can be observed at x=0.3 and x=0.6, as confirmed by the X-ray diffraction and the Raman scattering spectroscopy. The first well-known transition is connected with the oxygen disorder due to the Nd substitution for Ba at random Ba-sites. In the present work, it is proved by the apical oxygen mode broadening in Raman spectra. Ordering of the Nd and Ba atoms with a subsequent orthorhombic distortion of the lattice may occur even at 1000°C in air due to the second transformation at x≈0.6. The invariable orthorhombicity of the Nd-rich solid solution with x>0.6 is not caused by the oxygen absorption as in the x=0.05 case. Existence of high- and low-temperature orthorhombic modifications of this solid solution has been observed for the first time. Finally, a tentative 3D (z–x–T) diagram is suggested for the Nd_1+xBa_2−xCu₃O_z solid solution up to 1000°C in air, including the new x=0.6–0.9 region.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Structural and compositional analysis of InBixAsySb(1−x−y) films grown on GaAs(0 0 1) substrates by liquid phase epitaxy

The growth of epitaxial InBi_xAs_ySb_(1−x−y) layers on highly lattice mis-matched semi-insulating GaAs substrates has been successfully achieved via the traditional liquid phase epitaxy. Orientation and single crystalline nature of the film have been confirmed by X-ray diffraction. Scanning electron micrograph shows abrupt interface at micrometer resolution. Surface composition of Bi(x) and As(y) in the InBi_xAs_ySb_(1−x−y) film was measured using energy dispersive X-ray analysis and found to be 2.5 and 10.5 at.%, respectively, and was further confirmed with X-ray photoelectron spectroscopy. Variation of the composition with depth of the film was studied by removing the layers with low current (20 μA) Ar⁺ etching. It was observed that with successive Ar⁺ etching, In/Sb ratio remained the same, while the As/Sb and Bi/Sb ratios changed slightly with etching time. However after about 5 min etching the As/Sb and Bi/Sb ratios reached constant values. The room temperature band gap of InBi_0.025As_0.105Sb_0.870 was found to be in the range of 0.113–0.120 eV. The measured values of mobility and carrier density at room temperature are 3.1×10⁴ cm² V⁻¹ s⁻¹ and 8.07×10¹⁶ cm⁻³, respectively.     

Dilatometry of the high-temperature proton conductor Ba3Ca1.18Nb1.82O9 − δ

Firstly, the production of solid bulk specimens of the proton conductor Ba₃Ca_1.18Nb_1.82O_{9 − gd} (BCN18) of known water content up to [H^.] = n_H/n_Ba = 0.16 is described. Secondly, measuring the length change of such samples versus water content [H^.] demonstrated that the sample lengths increased linearly with a slope of (Δl/l)/[H^.] = (2.13 ±0.07) × 10⁻². Thirdly, the density of bulk samples was found to decrease linearly with water content [H^.]. This decrease was in good agreement with the above values derived from the length change. Fourthly, high temperature dilatometry showed that samples reach the thermodynamic solubility values in water vapor atmospheres only at temperatures above 700 °C. Two time scales were observed for the time-dependence of the elongation upon exposure to water vapor. A fast process occurred within minutes above 700 °C, a slow one took several hours. The fast one was identified as the chemical diffusion of the diffusion pair H^. and V_o^. which is required for the water uptake and loss of BCN18. The chemical diffusivity of water is described by the parameters D₀ = (0.022 ± 0.002) cm²/s and ΔH* = (0.79 ± 0.05) eV.     

Niobium based tetragonal tungsten bronzes as potential anodes for solid oxide fuel cells: synthesis and electrical characterisation

In this paper we report studies on a range of niobate based tungsten bronzes, with a view to analysing their potential as anode materials in SOFCs. Six systems were studied, (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃, Sr_0.6−xLa_xTi_0.2+xNb_0.8−xO₃, (Sr_0.4−xBa_x)Na_0.2NbO₃, (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃, Ba_0.5−xA_xNbO₃ (A=Ca, Sr), and Ba_0.3NbO_2.8, and the electrical conductivities were examined over a range of oxygen partial pressures (10⁻²⁰–1 bar). All the systems showed good conductivity in low oxygen partial pressures, with values as high as 8 S cm⁻¹ at 930°C (P(O₂)=10⁻²⁰ bar). As the oxygen partial pressure was raised the conductivity dropped showing in most cases an approximate [P(O₂)]^−1/4 dependence and good re-oxidation kinetics. Of all the samples studied the (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃ and (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃ systems appear most promising for potential use as anode materials in SOFCs.     

Studies of lithium intercalation in 3R-WS2

The lithium intercalation into the layered dichalcogenide 3R-WS₂ has been investigated by electrochemical reduction and by chemical reaction in n-butyl lithium solution. Essential results are (a) a charge transfer of nearly 0.6e⁻/W in Li_xWS₂, (b) a small increase of the c-axis parameter of about 0.6%, and (c) a high mobility of the Li⁺-ions. The chemical diffusion coefficient of Li⁺-ions is estimated to be 8 × 10⁻⁹ cm² s⁻¹ in the composition range 0 ≤ x ≤ 0.25. The appearance of a structural transformation from 3R-WS₂ to 2H-Li_xWS₂ is interpreted on grounds of instabilities in the interlayer structure.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.