High c-axis preferred orientation ZnO thin films prepared by oxidation of metallic zinc

Thin films of zinc oxide were grown on glass substrates by thermal oxidation. The metallic zinc films were thermally oxidized at different temperatures ranging from 300 to 600 °C to yield ZnO thin films. The structural property of the thin films was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The X-ray diffraction measurements showed that the films oxidized at 300 °C were not oxidized entirely, and the films deposited at 600 °C had better crystalline quality than the rest. When the oxidation temperature increased above 400 °C, the films exhibited preferred orientation along (002) and high transmittance ranging from 85% to 98% in vis–near-infrared band. Meanwhile, the films showed a UV emission at about 377 nm and green emission. With the increasing of oxidation temperature, the intensity of green emission peak was enhanced, and then decreased, disappearing at 600 °C, and the case of UV emission increased. Furthermore, a strong green emission was observed in the film sintered in pure oxygen atmosphere.     

XRD study on the effect of the deposition condition on pulsed laser deposition of ZnO films

Using a pulsed laser deposition (PLD) process on a ZnO target in an oxygen atmosphere, thin films of this material have been deposited on Si(111) substrates. An Nd: YAG pulsed laser with a wavelength of 1064 nm was used as the laser source. The influences of the deposition temperature, laser energy, annealing temperature and focus lens position on the crystallinity of ZnO films were analyzed by X-ray diffraction. The results show that the ZnO thin films obtained at the deposition temperature of 400°C and the laser energy of 250 mJ have the best crystalline quality in our experimental conditions. The ZnO thin films fabricated at substrate temperature 400°C were annealed at the temperatures from 400°C to 800°C in an atmosphere of N₂. The results show that crystalline quality has been improved by annealing, the optimum temperature being 600°C. The position of the focusing lens has a strong influence on pulsed laser deposition of the ZnO thin films and the optimum position is 59.5 cm from the target surface for optics with a focal length of 70 cm.      

Optical properties of PMN–PT thin films prepared using pulsed laser deposition

(1 ? x)Pb(Mg_1/3Nb_2/3)O₃–xPbTiO₃ (PMN–PT) thin films have been deposited on quartz substrates using pulsed laser deposition (PLD). Crystalline microstructure of the deposited PMN–PT thin films has been investigated with X-ray diffraction (XRD). Optical transmission spectroscopy and Raman spectroscopy are used to characterize optical properties of the deposited PMN–PT thin films. The results show that the PMN–PT thin films of perovskite structure have been formed, and the crystalline and optical properties of the PMN–PT thin films can be improved as increasing the annealing temperature to 750 °C, but further increasing the annealing temperature to 950 °C may lead to a degradation of the crystallinity and the optical properties of the PMN–PT thin films. In addition, a weak second harmonic intensity (SHG) has been observed for the PMN–PT thin film formed at the optimum annealing temperature of 750 °C according to Maker fringe method. All these suggest that the annealing temperature has significant effect on the structural and optical properties of the PMN–PT thin films.     

Substitution mechanism of Ga for Zn site depending on deposition temperature for transparent conducting oxides

High quality transparent conductive gallium-doped zinc oxide (GZO) thin films were deposited on glass substrates using rf-magnetron sputtering system at the temperature ranging from room temperature (RT) to 500 °C. The temperature-dependence of Ga doping effect on the structural, optical and electrical properties in ZnO has been investigated. For the GZO thin films deposited at over 200 °C, (103) orientation was strongly observed by X-ray diffraction analysis, which is attributed to the substitution of Ga elements into Zn site. X-ray photoelectron spectroscopy measurements have confirmed that oxygen vacancies were generated at the temperature higher than 300 °C. This might be due to the effective substitution of Ga³⁺ for Zn site at higher temperature. It was also found that the optical band gap increases with deposition temperature. The optical transmittance of GZO thin films was above 87% in the visible region. The GZO thin films grown at 500 °C showed a low electrical resistivity of 4.50 × 10^?4 Ω cm, a carrier concentration of 6.38 × 10²⁰ cm^?3 and a carrier mobility of 21.69 cm²/V.     

Effects of oxygen pressures on pulsed laser deposition of ZnO films

Zinc oxide (ZnO) thin films on Si (1 1 1) substrates were deposited by pulsed laser ablation of ZnO target at different oxygen pressures. A pulsed Nd:YAG laser with wavelength of 1064 nm was used as laser source. The deposited thin films have been characterized by X-ray diffraction (XRD), Atomic force microscopy (AFM), and Raman spectroscopy. XRD measurements indicate that the ZnO thin films deposited at the oxygen pressure of 1.3 Pa have the best crystalline quality. AFM results show that the surface roughness of ZnO film increases with the increase of oxygen pressure. The Raman results indicate that oxygen ambient plays an important role in removing defects due to excess zinc.     

Effect of temperature on pulsed laser deposition of ZnO films

ZnO thin films have been deposited on Si(1 1 1) substrates at different substrate temperature by pulsed laser deposition (PLD) of ZnO target in oxygen atmosphere. An Nd:YAG pulsed laser with a wavelength of 1064 nm was used as laser source. The influences of the deposition temperature on the thickness, crystallinity, surface morphology and optical properties of ZnO films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), selected area electron diffraction (SAED), photoluminescence (PL) spectrum and infrared spectrum. The results show that in our experimental conditions, the ZnO thin films deposited at 400 °C have the best surface morphology and crystalline quality. And the PL spectrum with the strongest ultraviolet (UV) peak and blue peak is observed in this condition.     

Influence of deposition temperature on amorphous structure of PECVD deposited a-Si:H thin films

The effect of deposition temperature on the structural and optical properties of amorphous hydrogenated silicon (a-Si:H) thin films deposited by plasma-enhanced chemical vapour deposition (PECVD) from silane diluted with hydrogen was under study. The series of thin films deposited at the deposition temperatures of 50–200°C were inspected by XRD, Raman spectroscopy and UV Vis spectrophotometry. All samples were found to be amorphous with no presence of the crystalline phase. Ordered silicon hydride regions were proved by XRD. Raman measurement analysis substantiated the results received from XRD showing that with increasing deposition temperature silicon-silicon bond-angle fluctuation decreases. The optical characterization based on transmittance spectra in the visible region presented that the refractive index exhibits upward trend with increasing deposition temperature, which can be caused by the densification of the amorphous network. We found out that the scale factor of the Tauc plot increases with the deposition temperature. This behaviour can be attributed to the increasing ordering of silicon hydride regions. The Tauc band gap energy, the iso-absorption value their difference were not particularly influenced by the deposition temperature. Improvements of the microstructure of the Si amorphous network have been deduced from the analysis.     

Comparative study on structural and optical properties of ZnO thin films prepared by PLD using ZnO powder target and ceramic target

Zinc oxide thin films have been obtained in O₂ ambient at a pressure of 1.3 Pa by pulsed laser deposition (PLD) using ZnO powder target and ceramic target. The effect of temperature on structural and optical properties of ZnO thin films was investigated systematically by XRD, SEM, FTIR and PL spectra. The results show that the best structural and optical properties can be achieved for ZnO thin film fabricated at 700 °C using powder target and at 400 °C using ceramic target, respectively. The PL spectrum reveals that the efficiency of UV emission of ZnO thin film fabricated by using powder target is low, and the defect emission of ZnO thin film derived from Zn_i and O_i is high.     

Surface morphology of ZnO buffer layer and its effects on the growth of GaN films on Si substrates by magnetron sputtering

ZnO thin films were first prepared on Si(111) substrates using a radio frequency magnetron sputtering system. Then the as-grown ZnO films were annealed in oxygen ambient at temperatures of 700, 800, 900, and 1000°C , respectively. The morphologies of ZnO films were studied by an atom force microscope (AFM). Subsequently, GaN epilayers about 500 nm thick were deposited on the ZnO buffer layers. The GaN/ZnO films were annealed in NH₃ ambient at 900°C. The microstructure, morphology and optical properties of GaN films were studied by x-ray diffraction (XRD), AFM, scanning electron microscopy (SEM) and photoluminescence (PL). The results are shown, their properties having been investigated particularly as a function of the ZnO layers. For better growth of the GaN films, the optimal annealing temperature of the ZnO buffer layers was 900°C.     

Properties of Eu-doped zinc oxide thin films grown on glass substrates by radio-frequency magnetron sputtering

Eu-doped ZnO (EZO) thin films were prepared on glass substrates at various growth temperatures by radio-frequency magnetron sputtering. The properties of deposited thin films showed a significant dependence on the growth temperature. The preferential growth orientation of all the thin films was occurred along the ZnO (002) plane. The maximum crystallite size and the minimum average transmittance in the wavelength range of 450–1100 nm were observed for the EZO thin film deposited at 25 °C. A red shift of the optical band gap was observed in the growth temperature range of 25–300 °C. The highest figure of merit, an index for evaluating the performance of transparent conducting thin films, was obtained at 200 °C of growth temperature. These results indicated that the high-quality EZO film was obtained at a growth temperature of 200 °C.     

The comparison between CdS thin films grown on Si(111) substrate and quartz substrate by femtosecond pulsed laser deposition

Two kinds of cadmium sulfate (CdS) thin films have been grown at 600 °C onto Si(111) and quartz substrates using femtosecond pulsed laser deposition (PLD). The influence of substrates on the structural and optical properties of the CdS thin films grown by femtosecond pulsed laser deposition have been studied. The CdS thin films were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), photoluminescence (PL) and Raman spectroscopy. Although CdS thin films deposited both on Si(111) and quartz substrates were polycrystalline and hexagonal as shown by the XRD , SEM and AFM results, the crystalline quality and optical properties were found to be different. The size of the grains for the CdS thin film grown on Si(111) substrate were observed to be larger than that of the CdS thin film grown on quartz substrate, and there is more microcrystalline perpendicularity of c-axis for the film deposited on the quartz substrate than that for the films deposited on the Si substrate. In addition, in the PL spectra, the excitonic peak is more intense and resolved for CdS film deposited on quartz than that for the CdS film deposited on Si(111) substrate. The LO and TO Raman peaks in the CdS films grown on Si(111) substrate and quartz substrate are different, which is due to higher stress and bigger grain size in the CdS film grown on Si(111) substrate, than that of the CdS film grown on the amorphous quartz substrate. All this suggests that the substrates have a significant effect on the structural and optical properties of thin CdS films. PACS 81.15.Fg; 81.05.Ea; 78.20.-e; 78.67.-n; 42.62.-b     

Effects of aluminum doping and substrate temperature on zinc oxide thin films grown by pulsed laser deposition

Aluminum-doped zinc oxide (AZO) thin films have been deposited on amorphous fused silica substrates by pulsed laser ablation of a Zn:Al metallic targets. We varied the film growth condition such as the substrate temperature and Al concentrations. The films were deposited at substrate temperatures ranging from 20 to 600°C with oxygen partial pressure of 1 torr. The characteristics of the deposited films were examined by analyzing their photoluminescence (PL), X-ray diffraction (XRD), and UV–visible spectra. It is observed that the optical bandgap energy of the deposited films increased with the increase of Al concentration and substrate temperature. Besides, the PL peak energy shifted to blue and the Stokes shift became larger as the Al content increased.     

Investigation on the structural properties and correlation of the optical constants of Cd1-xZnxS thin films with bath deposition temperature

Cd_1-xZn_xS thin films were deposited by chemical bath deposition (CBD) technique, which is simple and cost effective, in a chemical bath containing appropriate amount of cadmium acetate, zinc acetate, and thiourea as precursors, in a clean glass substrate. The deposition was carried out by varying the bath temperatures (70 °C, 75 °C, 80 °C, and 85 °C) of the precursor solution. The XRD results indicate the existence of hexagonal structures of Cd_1-xZn_xS with an average crystallite size of ∼ 27–41 nm. EDX studies confirm the presence of Cd, Zn, and S in the films. HRTEM and SAED patterns show the crystalline nature of the films with the coexistence of the hexagonal phase. The optical constants viz; optical band gap, Urbach energy, static refractive index, and optical conductivity were studied by using UV- Vis transmission spectra as a function of CBD temperature. It was observed that with the increase of bath temperature in the above range, there were concomitant decreases in optical band gap from ∼3.3 to 2.8 eV. The Urbach energy, optical conductivity, and static refractive index of the films increase with the increase in bath deposition temperature. FTIR studies confirm the formation of ternary Cd_1-xZn_xS thin films.     

Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

Metalorganic chemical vapor deposition of ZnO:N using NO as dopant

Highly c-axis orientated ZnO was grown by metal organic chemical vapor deposition (MOCVD) using NO as both oxidant and nitrogen dopant source. The properties of the deposited material are investigated by X-ray diffraction to study the crystalline quality of the thin films. Photoluminescence measurements are used to determine the optical properties of the material as a function of VI/II ratio and post growth-annealing temperature. Two transitions appear at 3.228 and 3.156 eV and are interpreted as involving active nitrogen acceptors. An increase in the NO flow increases the concentration of nitrogen in the films, which are activated by subsequent annealing at 600 °C in an oxygen ambient.     

Structural and optical properties of Mn-doped ZnO nanocrystalline thin films with the different dopant concentrations

The transparent nanocrystalline thin films of undoped zinc oxide and Mn-doped (Zn_1−xMn_xO) have been deposited on glass substrates via the sol–gel technique using zinc acetate dehydrate and manganese chloride as precursor. The as-deposited films with the different manganese compositions in the range of 2.5–20 at% were pre-heated at 100 °C for 1 h and 200 °C for 2 h, respectively, and then crystallized in air at 560 °C for 2 h. The structural properties and morphologies of the undoped and doped ZnO thin films have been investigated. X-ray diffraction (XRD) spectra, scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) were used to examine the morphology and microstructure of the thin films. Optical properties of the thin films were determined by photoluminescence (PL) and UV/Vis spectroscopy. The analyzed results indicates that the obtained films are of good crystal quality and have smooth surfaces, which have a pure hexagonal wurtzite ZnO structure without any Mn related phases. Room temperature photoluminescence is observed for the ZnO and Mn-doped ZnO thin films.     

Low-temperature growth of epitaxial ZnO films on (001) sapphire by ultraviolet- assisted pulsed laser deposition

ZnO thin films have been grown on thin Si₃N₄ membranes and (001) sapphire substrates by an ultraviolet-assisted pulsed laser deposition (UVPLD) technique. The microstructure of the films grown on Si₃N₄ membranes, investigated by transmission electron microscopy, showed that crystalline and textured films can be grown by UVPLD at a substrate temperature of only 100 °C. For deposition temperatures higher than 400 °C, ZnO films grown on sapphire substrates were found to be epitaxial by Rutherford backscattering (RBS) and X-ray diffraction measurements. The minimum yield of channeling RBS spectra recorded from films deposited at 550 °C was around 2% and the FWHM of the rocking curve for the (002) diffraction peak was 0.17°; these values are similar to those recorded from ZnO layers grown by conventional PLD at 750 °C.     

Photocatalytic and optical properties of titanium dioxide thin films prepared by metalorganic chemical vapor deposition

Titanium dioxide thin films have been deposited by metalorganic chemical vapor deposition (MOCVD) over sodalime glass substrates at substrate temperatures ranging from 250 °C to 450 °C. The effect of deposition temperature on the structure and microstructure of the obtained films has been studied by x-rays diffraction (XRD) and scanning electron microscopy (SEM), respectively. Diffraction patterns show the existence of a pure anatase phase beside a texture change with the increase of deposition temperature. Micrographs show grain fragmentation with the increase in deposition temperature. UV–Vis. spectra have been recorded by spectrophotometery. The optical energy gap has been calculated for the deposited films from the spectrophotometrical data. Photocatalytic experiments have been carried out. The photocatalytic activity has been found to decrease with the increase in deposition temperature.     

Mn doped ZnO nanostructured thin films prepared by ultrasonic spray pyrolysis method

Mn-doped ZnO thin films with different percentage of Mn content (0, 1, 3 and 5 at.%) and substrate temperature of 350 °C, were deposited by a simple ultrasonic spray pyrolysis method under atmospheric pressure. We have studied the structural and optical properties by using X-ray diffraction (XRD), Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR) and ultra-violet visible near infrared (UV–Vis-NIR) spectroscopy. The lattice parameters calculated for the Mn-doped ZnO from XRD pattern were found to be slightly larger than those of the undoped ZnO, which indicate substitution of Mn in ZnO lattice. Compared with the Raman spectra for ZnO pure films, the Mn-doping effect on the spectra is revealed by the presence of additional peak around 524 cm⁻¹ due to Mn incorporation. With increasing Mn doping the optical band gap increases indicating the Burstein–Moss effect.     

Optical properties of ZnO and ZnO:Ce layers grown by spray pyrolysis

In this paper, zinc oxide (ZnO) and cerium-doped zinc oxide (ZnO:Ce) films were deposited by reactive chemical pulverization spray pyrolysis technique using zinc and cerium chlorides as precursors. The effects of Ce concentration on the structural and optical properties of ZnO thin films were investigated in detail. These films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence (PL) measurements. All deposited ZnO layers at the temperature 450 °C are polycrystalline and indicate highly c-axis oriented structure. The dimension of crystallites depends on incorporation of Ce atoms into the ZnO films. The photoluminescence spectra of the films have been studied as a function of the deposition parameters such as doping concentrations and post grows annealing. Photoluminescence spectra were measured at the temperature range from 13 K to 320 K.