Crystal growth and properties of lead pyrophosphate,Pb2P2O7

Single crystals of Pb₂P₂O₇ have been grown by the Czochralski technique. They have the triclinic space group $\text{P}\text{1}$ with cell dimensions a = 6.9627 Å, b = 6.9754Å, c = 12.764 Å, α = 96.78°, β = 91.16°, γ = 89.68°. There are four molecules per unit cell. Dielectric properties for this compound have been measured and are discussed.     

Crystal structures of the fluorite-related phases CaHf4O9 and Ca6Hf19O44

Crystal structures for the fluorite-related phases CaHf₄O₉$\text{ф}{}_1$) and Ca₆Hf₁₉O₄₄ ($\text{ф}{}_2$) have been determined from X-ray powder diffraction data. qf₁ is monoclinic, $\text{C2}\text{c}$, with a = 17.698 Å, b = 14.500Å, c = 12.021 Å, β = 119.47° and Z = 16. qf₂ is rhombohedral, $\text{R}\text{3}\text{c}$, with a = 12.058 Å, α = 98.31° and Z = 2.Both phases are superstructures derived from the defect fluorite structure by ordering of the cations and of the anion vacancies. The ordering is such that the calcium ions are always 8-coordinated by oxygen ions, while the hafnium ions may be 6-, 7-, or 8-coordinated. The closest approach of anion vacancies is a $\text{1}\text{2}\text{〈111〉}$ fluorite subcell vector, and in each structure vacancies with this separation form strings.     

KxP2W2O16: A bronze with a tunnel structure built up from PO4 tetrahedra and WO6 octahedra

The structure of a $\text{K}{}_{\mathrm{x}}\text{P}{}_2\text{W}{}_4\text{O}{}_{16}\text{(x ? 0.4)}$ crystal was established by X-ray analysis. The solution in the cell of symmetry $\text{P2}{}_1\text{m}$, with a = 6.6702(5), b = 5.3228(8), c = 8.9091(8) Å, β = 100.546(7)°, Z = 1, has led to R = 0.033 and R_w = 0.036 for 2155 reflections with $\text{σ(I)}\text{I}\text{≤ 0.333}$. This structure can be described as two octahedra-wide ReO₃-type slabs connected through “planes” of PO₄ tetrahedra. A new structural family K_xP₂W_2nO_6n+4 can be foreseen which is closely related to the orthorhombic P₄W₈O₃₂ and the monoclinic Rb_xP₈W_8nO_24n+16 series.     

New SbS2 strings in the BaSb2S4 structure

The new compound BaSb₂S₄ crystallizes in the monoclinic system (space group: $\text{P2}{}_1\text{c}$, No. 14) with a = 8.985(2) Å, b = 8.203(3) Å, c = 20.602(5) Å, β = 101.36(3)°. SbS₃ ψ tetrahedra and ψ-trigonal SbS₄ bipyramids are connected by common corners and edgers to infinite strings. These are arraged cross-wise in sheets perpendicular to the c axis.     

Crystal structure of Fe2P2O7

Fe₂P₂O₇ crystallizes in the $\text{C}\text{1}$ space group with lattice parameters a = 6.649(2)Å, b = 8.484(2)Å, c = 4.488(1)Å, α = 90.04°, β = 103.89(3)°, γ = 92.82(3)°, and ?_cal = 3.86 g/cc. It is essentially isostructural with β-Zn₂P₂O₇. As in the Zn compound, the bridging oxygen atom in the P₂O₇ group shows a high anisotropic thermal motion. It appears that the P-O-P bond angle is linear as a result of extensive π bonding with the p orbitals on the bridging oxygen atom. The high thermal motion is vibration of the atom into cavities in the structure.     

Bronzes with a tunnel structure KxP4O8(WO3)2m: The tenth member of the series—KP8W40O136

The crystal structure of KP₈W₄₀O₁₃₆, the tenth member of the series K_xP₄O₈(WO₃)_2m, has been resolved by three-dimensional single-crystal X-ray analysis. The space group is $\text{P2}{}_1\text{c}$ and the cell parameters are a = 19.589(3) Å, b = 7.5362(4) Å, c = 16.970(3) Å and β = 91.864(14)°. The framework is built up from ReO₃-type slabs connected through pyrophosphate groups. The structure is compared to those of the other members of the series: although the ReO₃-type slabs show a different type of tilting of the WO₆ octahedra, the dispersion of WO distances is always higher for the octahedra linked to one or two P₂O₇ groups and decreases in proportion as W is farther from these groups. The perovskite cages of the slabs are described and compared to those encountered in the structures of WO₃ and of the bronzes A_xWO₃.     

Phase equilibrium relations in the binary systems LiPO3CeP3O9 and NaPO3CeP3O9

The LiPO₃CeP₃O₉ and NaPO₃CeP₃O₉ systems have been investigated for the first time by DTA, X-ray diffraction, and infrared spectroscopy. Each system forms a single 1:1 compound. LiCe(PO₃)₄ melts in a peritectic reaction at 980°C. NaCe(PO₃)₄ melts incongruently, too, at 865°C. These compounds have a monoclinic unit cell with the parameters: a = 16.415(6), b = 7,042(6), c = 9.772(7)Å; β = 126.03(5)°; Z = 4; space group $\text{C}{}_2\text{c}$ for LiCe (PO₃)₄; and a = 9.981(4), b = 13.129(6), c = 7.226(5) Å, β = 89.93(4)°, Z = 4, space group $\text{P2}{}_1\text{n}$ for NaCe(PO₃)₄. It is established that both compounds are mixed polyphosphates with chain structure of the type |M^I_IM^III_II (PO₃)₄|_∞M^I_I: alkali metal, M^III_II: rare earth.     

Etude de la tétracoordination de l'etain dans deux orthothiostannates: Na4SnS4 et Ba2SnS4 (α)

The crystal structure of Na₄SnS₄ and Ba₂SnS₄ (α) were determined.Na₄SnS₄ crystallizes in tetragonal system, space group $\text{P}\text{4}\text{2}{}_1\text{c}$ with parameters a = 7.837 Å, c = 6.950 Å, Z = 2 and Ba₂SnS₄ (α) in the monoclinic system, space group $\text{P2}{}_1\text{c}$ with a = 8.481 Å, b = 8.526 Å, c = 12.280 Å, β = 112.97° and Z = 4.In these compounds, the crystal structure is built up from discrete orthothiostannate tetrahedra SnS₄. The structure of Ba₂SnS₄ (α) is modified K₂SO₄β type.     

Dimorphisme et structure du disulfure de lanthane LaS2

The stoichiometric lanthanum disulfide LaS₂ presents a reversible phase transition at about 750°C. The α low-temperature form is monoclinic with the LaSe₂ type. All the crystals are twinned with the same twin law (100). The cell parameters are a = 8.18, b = 8.13, c = 4.03Å, γ = 90°, space group $\text{P2}{}_1\text{a}$. The β high-temperature form has the orthorhombic structure previously described with the parameters a = 8.13, b = 16.34, c = 4.14 Å; space group Pnma. The two structures are compared.     

L'oxyde double TeVO4 II. Structure cristalline de TeVO4-β-relations structurales

β-TeVO₄ crystallizes in the monoclinic system with the space group $\text{P2}{}_1\text{c}$ and the parameters: a = 4.379 Å, b = 13.502 Å, c = 5.446 Å, and β = 91.72°. Vanadium occupies the center of a square pyramid of oxygens, an extra oxygen is at VO = 2.77 Å. These distorted octahedra share corners forming puckered sheets parallel to (010). The sheets are held together by [Te₂O₆]^4? groups in which tellurium is one-side coordinated by four oxygen atoms.     

Synthese et structure cristalline d'un nouvel oxyde mixte “FeV3O8” (FexV1−xO2; x ⋍ 0.25)

Single crystals of a new oxide “FeV₃O₈” ($\text{Fe}{}_{\mathrm{x}}\text{V}{}_{\mathrm{1?x}}\text{O}{}_2\text{: x ? 0.25}$) have been synthesized by slowly cooling a melted mixture with the composition, 8VO₂, 3V₂O₅, Fe₂O₃. The chemical formula has been determined by electron microprobe analysis. The compound, isostructural with AlNbO₄ and VO₂(B), has a monoclinic symmetry, space group $\text{C2}\text{m}$; the unit cell dimensions are a = 12.13Å, b = 3.679 Å, c = 6.547 Å, β = 106.85°. A structural refinement based on single crystal data has been carried out. It gave an R-factor of 1.9%. This refinement indicated that the iron and vanadium cations are partially ordered, although the average cation-oxygen distances for the two six-coordinated cations were exactly the same (1.961 Å). This conjecture was supported by the calculation of the cation valences.     

High pressure and high temperature investigations in the system MgOSiO2H2O

The system MgOSiO₂H₂O was investigated at pressures between 40 and 95 kbar and at temperatures between 500 and 1400°C. The reaction products were examined by X-ray, optical and thermal analysis techniques and the density of phase A discovered by Ringwood and Major was also measured. It was found that phase A was hydrated and its chemical formula was H₆Mg₇Si₂O₁₄. When the $\text{Mg}\text{Si}$ ratio of the system is 2, phase A + clinoenstatite, and forsterite are stable at temperatures lower and higher than a boundary curve T (°C) = 10P (kbar), respectively. When the $\text{Mg}\text{Si}$ ratio of the system is 3, phase A + phase D (which is completely different from the phases, A, B and C discovered by Ringwood and Major, and any other known phases of magnesium silicate) and phase D + brucite are stable at temperatures lower and higher than a boundary curve T(°C) = 10P (kbar) + 200. Phase A has approximately an hexagonal symmetry and the space group and the lattice parameters are determined as P6₃ or $\text{P6}{}_3\text{m}$ and a = 7.866(2) Å and c = 9.600(3) Å, respectively. The measured density is 2.96 ± 0.02 g/cm³. The optical observations show that phase A is biaxial positive crystal with refractive indices α = 1.638 ± 0.001, β = 1.640 ± 0.002, and γ = 1.649 ± 0.001. Some interpretation is given on the inconsistency between the symmetry determined by the X-ray diffraction and the optical observation. The new phase D belongs to the space group $\text{P2}{}_1\text{c}$ with lattice parameters a = 7.914(2)Å, b = 4.752(1) Å, c = 10.350(2) Å and β = 108.71(5)° and is a biaxial crystal with refractive indices α = 1.630 ± 0.002, β = 1.642 ± 0.002 and γ = 1.658 ± 0.001.     

Crystal structure of Na3PO4 · 12H2O

The crystal structure of trisodium monophosphate hemihydrate was determined. The space group is $\text{C2}\text{c}$ and a unit cell contains eight formula units. The unit cell dimensions of $\text{Na}{}_3\text{PO}{}_4\text{·}\text{1}\text{2}\text{H}{}_2\text{O}$ are a = 9.631(3), b = 5.416(2), c = 16.938(8) Å, β = 102.60(5)°. The final R value is 0.027 for a set of 1430 independent reflections. This atomic arrangement is mainly a three-dimensional network of distorted NaO₆ octahedra. The hydrogen bonding scheme is given.     

The pyrophosphate NaFeP2O7: A cage structure

The high-temperature form of NaFeP₂O₇ crystallizes in the monoclinic $\text{P2}{}_1\text{c}$ space group with a = 7.3244(13), b = 7.9045(7), c = 9.5745(15), Å, β = 111.858(13)°, and Z = 4. The structure has been refined from 3842 reflections leading to R = 0.040 and R_w = 0.047. The structure of II-NaFeP₂O₇ can be described by alternately stacking layers containing the FeO₆ octahedra and layers formed by the P₂O₇ groups, parallel to (001). Elongated cages are formed where two Na⁺ ions are located. The structure is compared with that of KAlP₂O₇. Both structures are built up from blocks of three polyhedra, [FeP₂O₁₁] or [AlP₂O₁₁], including a small O_octO_tetO_oct angle. These blocks are connected in such a way that several types of tunnels appear in each structure.     

Crystal structure of a barium-zinc decametaphosphate Ba2Zn3P10O30

Barium-zinc decametaphosphate, Ba₂Zn₃P₁₀O₃₀, is monoclinic, $\text{P2}\text{n}$, with the unit cell parameters a = 21.738(15), b = 5.356(5), c = 10.748(8) Å, β = 99.65(3)° and Z = 2. The crystal structure was solved with a final R value of 0.041. This salt provides the first structural evidence for the existence of a 10-phosphorus ring anion.     

Etude structurale d'un nouveau tellurate alcalin: Na2TeO4. Evolution de la coordination du tellure(VI) et du cation quand on passe du cation lithium au sodium

Single crystal Na₂TeO₄ has been prepared by hydrothermal synthesis and its structure determined from three dimensional X-ray analysis. The crystal is monoclinic, space group $\text{P}\text{P2}{}_1\text{c}$ with a = 10.632(5)Å, b = 5.161(2)Å; c = 13.837(11)Å, and β = 103.27(4)°. The crystal structure is built up of chains of Te(VI)O₆ octahedra parallel to the [010] axis which can be formulated as [TeO₄]_n^2n?. All sodium cations are in very distorted octahedral coordination.     

Etudes cristallographique magnétique et par résonance Mössbauer de la variété de haute température du pyrophosphate NaFeP2O7

Single crystals of the high-temperature form of NaFeP₂O₇ have been grown by a flux technique. II-NaFeP₂O₇ crystallizes in the monoclinic $\text{P2}{}_1\text{c}$ space group with lattice parameters: a = 7.298(2) Å, b = 7.874(2) Å, c = 9.536(3) Å, β = 111.85(2)°. The structure refined from 1481 independent reflections leads to R = 0.044 and confirms the work previously published by M. Gabelica-Robert, M. Goreaud, P. Labbe, and B. Raveau (J. Solid State Chem.45, 389, 1982). Magnetic Mössbauer resonance studies have shown the existence of antiferromagnetic ordering with a weak ferromagnetic component below 30 K. The FeO bond is markedly ionic in character due to the highly polarizing power of phosphorus in tetrahedral site.     

Crystal structures of NaBaCr2F9 and NaBaFe2F9: Structural correlations with other enneafluorides,particularly with KPbCr2F9

NaBaCr₂F₉ and NaBaFe₂F₉ are monoclinic (SG $\text{P2}{}_1\text{n}$, No. 14). Lattice constants are found to be a = 7.318(2) Å, b = 17.311(4) Å, c = 5.398(1) Å, β = 91.14°(3) for chromium, and a = 7.363(2) Å, b = 17.527(4) Å, c = 5.484(1) Å, β = 91.50°(5) for iron. The structures were solved from 507 and 1113 X-ray reflections, respectively, for the Cr and Fe compounds; the corresponding R_w values are 0.025 and 0.037. The network is built from tilted double cis chains of octahedra (M₂F₉)^3n?_n [M = Cr, Fe], linked by Na⁺ and Ba²⁺ ions. The structures are compared to the previously described structures, particularly KPbCr₂F₉, whose symmetry and parameters are different. The difference is analyzed first in terms of tilted octahedra, but principally in terms of bond strengths and steric activity of the Pb²⁺ lone pair. A mechanism is proposed for the transformation between the structures of NaBaCr₂F₉ and KPbCr₂F₉.     

Crystal structures of phosphomolybdyl salts: Pb(MoO2)2(PO4)2 and Ba(MoO2)2(PO4)2

Crystal structures of Pb(MoO₂)₂(PO₄)₂ and Ba(MoO₂)₂(PO₄)₂ were determined. Both compounds contain the molybdyl group MoO₂. The monoclinic unit-cell parameters are a = 6.353(7), b = 12.289(4), c = 11.800 Å, β = 92°56(6), and Z = 4 for the lead salt and a = 6.383(8), b = 7.142(7), c = 9.953(8) Å, β = 95°46(8), and Z = 2 for the barium salt. $\text{P2}{}_1\text{c}$ is the common space group. The R values are respectively R = 0.027 and R = 0.031 for 1964 and 1714 independent reflections. The frameworks built up by a three-dimensional network of monophosphate PO₄ and molybdyl MoO₂ groups are similar, characterized mainly by corner-sharing PO₄ and MoO₆ polyhedra. Two oxygen atoms of each MoO₆ group are bonded to the molybdenum atom only as in other molybdyl salts.     

The crystal structure and some properties of Eu2Sb3

The Mooser-Pearson phase Eu₂Sb₃ crystallizes in a new monoclinic structure type, space group $\text{P2}{}_1\text{c}$ (No. 14) with a = 6.570(1) Å, b = 12.760(2) Å, c = 15.028(2) Å, β = 90.04(1)°; Z = 8. The Sb atoms form six-membered twisted chain fragments oriented along the b-axis. The Eu atoms are eight- and nine-coordinated by Sb. The Eu₂Sb₃ structure is closely related to the structure of Ca₂As₃. The relations between their space-group symmetries are derived and hypothetical higher-symmetry structures are discussed. The semiconducting Eu₂Sb₃ is antiferromagnetic below T_N = 14.4°K. An Eu₂Sb₃-type structure was found also for Sr₂Sb₃.