Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

TiO2 thick films supported on reticulated macroporous Al2O3 foams and their photoactivity in phenol mineralization

TiO₂ thick films deposited on macroporous reticulated Al₂O₃ foams with pore size of 10 ppi and 15 ppi were prepared using dip coating from slurries of Aeroxide^® P25 nanopowder and precipitated titania. All prepared films have sufficiently good adhesion to the surface of the substrate also in case of strongly cracked films. No measurable release of deposited TiO₂ after repeated photocatalytic cycles was observed. The photocatalytic activity was characterized as the rate of mineralization of aqueous phenol solution under irradiation of UVA light by TOC technique. The best activity was obtained with Aeroxide^® P25 coated Al₂O₃ foam with the pore size of 10 ppi, annealed at 600 °C. The optimal annealing temperature for preparation of films from precipitated titania could be determined at 700 °C. Films prepared by sol-gel deposition technique were considerably thinner compared to coatings made of suspensions and their photocatalytic activity was significantly smaller.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

Stabilization of a very high-k crystalline ZrO2 phase by post deposition annealing of atomic layer deposited ZrO2/La2O3 dielectrics on germanium

The impact of the ZrO₂/La₂O₃ film thickness ratio and the post deposition annealing in the temperature range between 400 °C and 600 °C on the electrical properties of ultrathin ZrO₂/La₂O₃ high-k dielectrics grown by atomic layer deposition on (1 0 0) germanium is investigated. As-deposited stacks have a relative dielectric constant of 24 which is increased to a value of 35 after annealing at 500 °C due to the stabilization of tetragonal/cubic ZrO₂ phases. This effect depends on the absolute thickness of ZrO₂ within the dielectric stack and is limited due to possible interfacial reactions at the oxide/Ge interface. We show that adequate processing leads to very high-k dielectrics with EOT values below 1 nm, leakage current densities in the range of 0.01 A/cm², and interface trap densities in the range of 2-5 × 10¹² eV⁻¹ cm⁻².     

Influence of postdeposition annealing on structural properties and electrical characteristics of thin Tm2O3 and Tm2Ti2O7 dielectrics

We describe the structural properties and electrical characteristics of thin thulium oxide (Tm₂O₃) and thulium titanium oxide (Tm₂Ti₂O₇) as gate dielectrics deposited on silicon substrates through reactive sputtering. The structural and morphological features of these films were explored by X-ray diffraction, X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and atomic force microscopy, measurements. It is found that the Tm₂Ti₂O₇ film annealed at 800 °C exhibited a thinner capacitance equivalent thickness of 19.8 Å, a lower interface trap density of 8.37 × 10¹¹ eV⁻¹ cm⁻², and a smaller hysteresis voltage of ∼4 mV than the other conditions. We attribute this behavior to the Ti incorporated into the Tm₂O₃ film improving the interfacial layer and the surface roughness. This film also shows negligible degrees of charge trapping at high electric field stress.     

Photocatalytic behavior of heavy La-doped TiO2 films deposited by pulsed laser deposition using non-sintered target

We have investigated the control of photocatalytic behavior under deposited conditions of non-sintered target of different molar ratios with TiO₂ and La₂O₃ from 1:0 to 1:2 for heavily La doping, and post-annealing temperature from 600 °C to 1000 °C for crystallizing by pulsed laser deposition. We have successfully crystallized heavily La-doped TiO₂ films with post-annealing temperature over 800 °C and with molar ratio of TiO₂:La₂O₃ over 1:1 on a quartz substrate. Heavily La-doped TiO₂ films are observed the decomposition of methylene blue and a water-splitting reaction in photocatalytic behavior under Xe light irradiation. When stoichiometric La-doped TiO₂ (TiO₂:La₂O₃ = 1: 1) is synthesized with heat-treatment at 900 °C, the best results are obtained under photocatalytic behavior and pure La₂Ti₂O₇ crystalline were obtained.     

Chemical quenching of positronium in Fe2O3/Al2O3 catalysts

Fe₂O₃/Al₂O₃ catalysts were prepared by solid state reaction method using α-Fe₂O₃ and γ-Al₂O₃ nano powders. The microstructure and surface properties of the catalyst were studied using positron lifetime and coincidence Doppler broadening annihilation radiation measurements. The positron lifetime spectrum shows four components. The two long lifetimes τ₃ and τ₄ are attributed to positronium annihilation in two types of pores distributed inside Al₂O₃ grain and between the grains, respectively. With increasing Fe₂O₃ content from 3 wt% to 40 wt%, the lifetime τ₃ keeps nearly unchanged, while the longest lifetime τ₄ shows decrease from 96 ns to 64 ns. Its intensity decreases drastically from 24% to less than 8%. The Doppler broadening S parameter shows also a continuous decrease. Further analysis of the Doppler broadening spectra reveals a decrease in the p-Ps intensity with increasing Fe₂O₃ content, which rules out the possibility of spin-conversion of positronium. Therefore the decrease of τ₄ is most probably due to the chemical quenching reaction of positronium with Fe ions on the surface of the large pores.     

Interfacial reactions and oxidation behavior of Al2O3 and Al2O3/Al coatings on an orthorhombic Ti2AlNb alloy

The uniform and dense Al₂O₃ and Al₂O₃/Al coatings were deposited on an orthorhombic Ti₂AlNb alloy by filtered arc ion plating. The interfacial reactions of the Al₂O₃/Ti₂AlNb and Al₂O₃/Al/Ti₂AlNb specimens after vacuum annealing at 750 °C were studied. In the Al₂O₃/Ti₂AlNb specimens, the Al₂O₃ coating decomposed significantly due to reaction between the Al₂O₃ coating and the O-Ti₂AlNb substrate. In the Al₂O₃/Al/Ti₂AlNb specimens, a γ-TiAl layer and an Nb-rich zone came into being by interdiffusion between the Al layer and the O-Ti₂AlNb substrate. The γ-TiAl layer is chemically compatible with Al₂O₃, with no decomposition of Al₂O₃ being detected. No internal oxidation or oxygen and nitrogen dissolution zone was observed in the O-Ti₂AlNb alloy. The Al₂O₃/Al/Ti₂AlNb specimens exhibited excellent oxidation resistance at 750 °C.     

Immobilization of glucose oxidase using CoFe2O4/SiO2 nanoparticles as carrier

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. Glucose oxidase (GOD) was immobilized on CoFe₂O₄/SiO₂ NPs via cross-linking with glutaraldehyde (GA). The optimal immobilization condition was achieved with 1% (v/v) GA, cross-linking time of 3 h, solution pH of 7.0 and 0.4 mg GOD (in 3.0 mg carrier). The immobilized GOD showed maximal catalytic activity at pH 6.5 and 40 °C. After immobilization, the GOD exhibited improved thermal, storage and operation stability. The immobilized GOD still maintained 80% of its initial activity after the incubation at 50 °C for 25 min, whereas free enzyme had only 20% of initial activity after the same incubation. After kept at 4 °C for 28 days, the immobilized and free enzyme retained 87% and 40% of initial activity, respectively. The immobilized GOD maintained approximately 57% of initial activity after reused 7 times. The K_M (Michaelis-Menten constant) values for immobilized GOD and free GOD were 14.6 mM and 27.1 mM, respectively.     

The electrical properties of dielectric stacks of SiO2 and Al2O3 prepared by atomic layer deposition method

We produced dielectric stacks composed of ALD SiO₂ and ALD Al₂O₃, such as SiO₂/Al₂O₃, Al₂O₃/SiO₂, and SiO₂/Al₂O₃/SiO₂, and measured the leakage currents through the stacks in comparison with those of the single oxide layers. SiO₂/Al₂O₃ shows lowest leakage current for negative bias region below 6.4 V, and Al₂O₃/SiO₂ showed highest current under negative biases below 4.5 V. Two distinct electron conduction regimes are observed for Al₂O₃ and SiO₂/Al₂O₃. Poole-Frenkel emission is dominant at the high-voltage regime for both dielectrics, whereas the direct tunneling through the dielectric is dominant at the low-voltage regime. The calculated transition voltage between two regimes for SiO₂ (6.5 nm)/Al₂O₃ (12.6 nm) is −6.4 V, which agrees well with the experimental observation (−6.1 V). For the same EOT of entire dielectric stack, the transition voltage between two regimes decreases with thinner SiO₂ layer.     

Deposition and characterization of binary Al2O3/SiO2 coating layers on the surfaces of rutile TiO2 and the pigmentary properties

Binary Al₂O₃/SiO₂-coated rutile TiO₂ composites were prepared by a liquid-phase deposition method starting from Na₂SiO₃·9H₂O and NaAlO₂. The chemical structure and morphology of binary Al₂O₃/SiO₂ coating layers were investigated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, TG-DSC, Zeta potential, powder X-ray diffraction, and transmission electron microscopy techniques. Binary Al₂O₃/SiO₂ coating layers both in amorphous phase were formed at TiO₂ surfaces. The silica coating layers were anchored at TiO₂ surfaces via Si-O-Ti bonds and the alumina coating layers were probably anchored at the SiO₂-coated TiO₂ surfaces via Al-O-Si bonds. The formation of continuous and dense binary Al₂O₃/SiO₂ coating layers depended on the pH value of reaction solution and the alumina loading. The binary Al₂O₃/SiO₂-coated TiO₂ composites had a high dispersibility in water. The whiteness and brightness of the binary Al₂O₃/SiO₂-coated TiO₂ composites were higher than those of the naked rutile TiO₂ and the SiO₂-coated TiO₂ samples. The relative light scattering index was found to depend on the composition of coating layers.     

Reasons for the deactivation of Pt/TiO2 photocatalyst treated by inert gas N2

The effect of N₂ treatment on the photocatalytic activity of Pt⁰/TiO₂ was investigated. The results showed that after treatment at 500 °C in N₂, 70% of the photocatalytic activity of 1.0 wt.% Pt⁰/TiO₂ was lost by the evaluation of photocatalytic oxidation reaction of C₃H₆. Transmission electron microscopy (TEM) and Ar⁺ ion sputtering tests revealed that in the course of high-temperature N₂ treatment, the size of Pt⁰ particles on TiO₂ increases and a strong interaction between metal and support, i.e. Pt⁰ particles encapsulated by Ti_xO_y, happens, which are the reasons for the deactivation of Pt⁰/TiO₂ photocatalyst treated by high-temperature N₂.     

Structural and optical properties of SrCu2O2 films deposited on sapphire substrates by pulsed laser deposition

We deposited SrCu₂O₂ (SCO) films on sapphire (Al₂O₃) (0 0 0 1) substrates by pulsed laser deposition. The crystallographic orientation of the SCO thin film showed clear dependence on the growth temperature. X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis showed that the film deposited at 400 °C was mainly oriented in the SCO [2 0 0] direction, whereas when the growth temperature was increased to 600 °C, the SCO film showed a dominant orientation of SCO [1 1 2]. The SCO film deposited at 500 °C was obvious polycrystalline, showing multi peaks from (2 0 0), (1 1 2), and (2 1 1) diffraction in the XRD spectrum. The SCO film deposited at 600 °C showed a band gap energy of 3.3 eV and transparency up to 80% around 500 nm. The photoluminescence (PL) spectra of the SCO films grown at 500 °C and 600 °C mainly showed blue-green emission, which was attributed to the intra-band transition of the isolated Cu⁺ and Cu⁺–Cu⁺ pairs according to the temperature dependent-PL analysis.     

Characterization of CuAlO2 thin film prepared by rapid thermal annealing of an Al2O3/Cu2O/sapphire structure

CuAlO₂ thin film was successfully prepared by rapid thermal annealing of an Al₂O₃/Cu₂O/sapphire structure in air above 1000 °C. The film was mostly with single crystalline structure as verified by X-ray diffraction methods. We found that crystal quality and electrical conductivity of the films were affected by the cooling rate after annealing. The highest conductivity obtained in this work was 0.57 S/cm. Optical gap of this film was determined to be 3.75 eV.     

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Stability of La2O3 and GeO2 passivated Ge surfaces during ALD of ZrO2 high-k dielectric

La₂O₃ grown by atomic layer deposition (ALD) and thermally grown GeO₂ are used to establish effective electrical surface passivations on n-type (1 0 0)-Ge substrates for high-k ZrO₂ dielectrics, grown by ALD at 250 °C substrate temperature. The electrical characterization of MOS capacitors indicates an impact of the Ge-surface passivation on the interfacial trap density and the frequency dependent capacitance in the inversion regime. Lower interface trap densities can be obtained for GeO₂ based passivation even though a chemical decomposition of the oxidation states occur during the ALD of ZrO₂. As a consequence the formation of a ZrGeO_x compound inside the ZrO₂ matrix and a decline of the interfacial GeO₂ are observed. The La₂O₃ passivation provides a stable amorphous lanthanum germanate phase at the Ge interface but also traces of Zr germanate are indicated by X-ray-Photoelectron-Spectroscopy and Transmission-Electron-Microscopy.     

Nanostructure of photocatalytic TiO2 films sputtered at temperatures below 200 °C

The article reports on correlations between the process parameters of reactive pulsed dc magnetron sputtering, physical properties and the photocatalytic activity (PCA) of TiO₂ films sputtered at substrate surface temperature T_surf ≤ 180 °C. Films were deposited using a dual magnetron system equipped with Ti (Ø50 mm) targets in Ar + O₂ atmosphere in oxide mode of sputtering. The TiO₂ films with highly photoactive anatase phase were prepared without a post-deposition thermal annealing. The decomposition rate of the acid orange 7 (AO7) solution during the photoactivation of the TiO₂ film with UV light was used for characterization of the film PCA. It was found that (i) the partial pressure of oxygen pO₂ and the total sputtering gas pressure p_T are the key deposition parameters influencing the TiO₂ film phase composition that directly affects its PCA, (ii) the structure of sputtered TiO₂ films varies along the growth direction from the film/substrate interface to the film surface, (iii) ∼500 nm thick anatase TiO₂ films with high PCA were prepared and (iv) the structure of sputtered TiO₂ films is not affected by the substrate surface temperature T_surf when T_surf < 180 °C. The interruption of the sputtering process and deposition in long (tens of minutes) pulses alternating with cooling pauses has no effect on the structure and the PCA of TiO₂ films and results in a decrease of maximum value of T_surf necessary for the creation of nanocrystalline nc-TiO₂ film. It was demonstrated that crystalline TiO₂ films with high PCA can be sputtered at T_surf ≤ 130 °C. Based on obtained results a phase zone model of TiO₂ films was developed.     

Promotion of surface SOx on the selective catalytic reduction of NO by hydrocarbons over Ag/Al2O3

The promotion of sulfur oxides on the selective catalytic reduction (SCR) of NO by hydrocarbons in the presence of a low concentration of sulfur oxides over Ag/Al₂O₃ has been investigated by a flow reaction test and in situ infrared spectroscopy. When the C₃H₆ (or C₁₀H₂₂) + NO + O₂ feed-flow reaction was tested, maximum NO reduction was below 30% over fresh Ag/Al₂O₃. After the addition of SO₂ to the feed flow, conversion increased slightly. Conversion increased further after SO₂ was cut-off from the feed flow. This demonstrated that the increase in NO reduction activity of the catalyst was related to SO_x adsorbed on the catalyst. SO_x adsorbed on the catalytic surface (1375 cm⁻¹) was detected by IR spectroscopy and was stable within the temperature range. NCO species, as an intermediate in NO reduction, on SO_x-adsorbed Ag/Al₂O₃ in a C₃H₆ + NO + O₂ feed flow was observed in in situ IR spectra during the elevation of the reaction temperature from 473 to 673 K, while it was only observed at 673 K on fresh Ag/Al₂O₃ under the same experimental conditions. We suggest that SO_x in low concentrations depressed the combustion of reductants by contaminating hydrocarbon combustion active sites on the catalyst, resulting in an increase in NO reduction efficiency of the reductants.     

Response improvement for In2O3-TiO2 thick film gas sensors

In₂O₃ is introduced into TiO₂ by sol-gel method to improve the response/recovery rate and expand the operating temperature, when the In₂O₃-TiO₂ mixed system is exposed to H₂/O₂. The sensor is fabricated by thick film technology. Influence of In₂O₃ on the film phase composition, microstructure and sensing characteristics is discussed. Dynamic response properties show that the operating temperature of the mixed system is at 500-800 °C, which is about 600-800 °C for pure TiO₂. Response time of the sensor is about 200-260 ms (millisecond) while recovery time is in a narrow range of 60-280 ms at 600-800 °C. The promoting mechanism is suggested to arise from the introduction of In₂O₃ and grain size effect of the sensing film. Then In₂O₃-TiO₂ thick films are surface-modified by Pt using chloroplatinic acid. The promoting effect of Pt dispersed on the mixed system is also investigated.     

Synthesis and ion conductivity of (Bi2O3)0.75(Dy2O3)0.25 ceramics with grain sizes from the nano to the micro scale

Using (Bi₂O₃)_0.75(Dy₂O₃)_0.25 nano-powder synthesized by reverse titration co-precipitation method as raw material, dense ceramics were sintered by both Spark Plasma Sintering (SPS) and pressureless sintering. According to the predominance area diagram of Bi-O binary system, the sintering conditions under SPS were optimized. (Bi₂O₃)_0.75(Dy₂O₃)_0.25 ceramics with relative density higher than 95% and an average grain size of 20 nm were sintered in only 10 min up to 500 °C. During the pressureless sintering process, the grain growth behavior of (Bi₂O₃)_0.75(Dy₂O₃)_0.25 followed a parabolic trend, expressed as D² − D₀² = Kt, and the apparent activation energy of grain growth was found to be 284 kJ mol^− 1. Dense (Bi₂O₃)_0.75(Dy₂O₃)_0.25 ceramics with different grain sizes were obtained, and the effect of grain size on ion conductivity was investigated by impedance spectroscopy. It was shown that the total ion conductivity was not affected by the grain size down to 100 nm, however lower conductivity was measured for the sample with the smallest grain size (20 nm). But, although only the δ phase was evidenced by X-ray diffraction for this sample, a closer inspection by Raman spectroscopy revealed traces of α-Bi₂O₃.