Microstructure of epitaxial SrRuO3 thin films on MgO substrates

SrRuO₃ thin films have been grown on singular (1 0 0) MgO substrates using pulsed laser deposition (PLD) in 30 Pa oxygen ambient and at a temperature of 400-700 °C. Ex situ reflection high-energy electron diffraction (RHEED) as well as X-ray diffraction (XRD) θ/2θ scan indicated that the films deposited above 650 °C were well crystallized though they had a rough surface as shown by atom force microscopy (AFM). XRD Φ scans revealed that these films were composed of all three different types of orientation domains, which was further confirmed by the RHEED patterns. The heteroepitaxial relationship between SrRuO₃ and MgO was found to be [1 1 0] SRO//[1 0 0] MgO and 45°-rotated cube-on-cube [0 0 1] SRO//[1 0 0] MgO. These domain structures and surface morphology are similar to that of ever-reported SrRuO₃ thin films deposited on the (0 0 1) LaAlO₃ substrates, and different from those deposited on (0 0 1) SrTiO₃ substrates that have an atomically flat surface and are composed of only the [1 1 0]-type domains. The reason for this difference was ascribed to the effect of lattice mismatch across the film/substrate interface. The room temperature resistivity of SrRuO₃ films fabricated at 700 °C was 300 μΩ cm. Therefore, epitaxial SrRuO₃ films on MgO substrate could serve as a promising candidate of electrode materials for the fabrication of ferroelectric or dielectric films.     

RHEED studies during growth of TiN/SiNx/TiN trilayers on MgO(0 0 1)

TiN/SiN_x/TiN(0 0 1) trilayers have been deposited on MgO(0 0 1) substrates using ultra-high vacuum based reactive magnetron sputtering and studied by in situ reflection high energy electron diffraction (RHEED). Depositions were carried out at 500 °C and 800 °C, with SiN_x layer thicknesses between 3 and 300 Å. Here, we find that SiN_x(0 0 1) layers grown at 800 °C exhibit 1 × 4 surface reconstructions along orthogonal 〈1 1 0〉 directions up to a critical thickness of ∼9 Å, where an amorphous phase forms. Growth of TiN overlayers on the reconstructed SiN_x(0 0 1) layers yield RHEED patterns indicating the growth of (0 0 1)-oriented epitaxial layers with a 1 × 1 reconstruction. For the case of amorphous SiN_x layers the TiN overlayers grow polycrystalline.     

The preparation of c-axis epitaxial Bi-2212 films on STO(1 0 0) by sol-gel method

Bi₂Sr₂Ca₁Cu₂O_8+δ (Bi-2212) films were grown on (1 0 0) oriented SrTiO₃ (STO) substrate using sol-gel spin-coating method. The effects of heat treatment conditions and coating times on the phase formation and surface morphology were investigated using thermal analysis, optical microscope, X-ray diffraction, and scanning electronic microscopy. Mixed phases were formed from 820 to 840 °C, and Bi-2212 single phase was obtained at 830 °C for 3 h. c-axis epitaxial films with smooth surfaces were obtained by drying at 600 °C and coating for 5 times.     

Si epitaxial growth on LaAlO3(0 0 1)

We report on the growth of Si on c(2 × 2) reconstructed LaAlO₃(0 0 1) surfaces at high substrate temperature (700 °C) by molecular beam epitaxy. An initial Volmer-Weber mode is evidenced using reflection high energy electron diffraction (RHEED), X-ray photoelectron diffraction (XPD) and atomic force microscopy. After the deposition of a few monolayers, the islands coalesce. Using X-ray photoelectron spectroscopy, we demonstrate that Si islands exhibit an abrupt interface with the LaAlO₃ substrate without formation of silicate or silica. Finally, combined RHEED and XPD measurements show the epitaxial growth of Si with a unique Si(0 0 1)//LaAlO₃(0 0 1) and Si<1 0 0>//LAO<1 1 0> relationship.     

Thickness dependence on thermal stability of sputtered Ag nanolayer on Ti/Si(1 0 0)

Thermal stability of Ag layer on Ti coated Si substrate for different thicknesses of the Ag layer have been studied. To do this, after sputter-deposition of a 10 nm Ti buffer layer on the Si(1 0 0) substrate, an Ag layer with different thicknesses (150-5 nm) was sputtered on the buffer layer. Post annealing process of the samples was performed in an N₂ ambient at a flow rate of 200 ml/min in a temperature range from 500 to 700 °C for 30 min. The electrical property of the heat-treated multilayer with the different thicknesses of Ag layer was examined by four-point-probe sheet resistance measurement at the room temperature. Phase formation and crystallographic orientation of the silver layers were studied by θ-2θ X-ray diffraction analysis. The surface topography and morphology of the heat-treated films were determined by atomic force microscopy, and also, scanning electron microscopy. Four-point- probe electrical measurement showed no considerable variation of sheet resistance by reducing the thickness of the annealed Ag films down to 25 nm. Surface roughness of the Ag films with (1 1 1) preferred crystallographic orientation was much smaller than the film thickness, which is a necessary condition for nanometric contact layers. Therefore, we have shown that the Ag layers with suitable nano-thicknesses sputtered on 10 nm Ti buffer layer were thermally stable up to 700 °C.     

Growth and morphology of the epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) Trilayers

Growth and surface morphology of epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) trilayers constituting a magnetic tunnel junction were investigated by low-energy electron diffraction (LEED) and scanning tunneling microscopy (STM). STM reveals a grain-like growth mode of MgO on Fe(1 1 0) resulting in dense MgO(1 1 1) films at room temperature as well as at 250 °C. As observed by STM, initial deposition of MgO leads to a partial oxidation of the Fe(1 1 0) surface which is confirmed by Auger electron spectroscopy. The top Fe layer deposited on MgO(1 1 1) at room temperature is relatively rough consisting of clusters which can be transformed by annealing to an atomically flat epitaxial Fe(1 1 0) film.     

Stability of MgO(1 1 1) films grown on 6H-SiC(0 0 0 1) by molecular beam epitaxy for two-step integration of functional oxides

Crystalline magnesium oxide (MgO) (1 1 1), 20 Å thick, was grown by molecular beam epitaxy (MBE) on hydrogen cleaned hexagonal silicon carbide (6H-SiC). The films were further heated to 740 °C and 650 °C under different oxygen environments in order to simulate processing conditions for subsequent functional oxide growth. The purpose of this study was to determine the effectiveness and stability of crystalline MgO films and the MgO/6H-SiC interface for subsequent heteroepitaxial deposition of multi-component, functional oxides by MBE or pulsed laser deposition processes. The stability of the MgO films and the MgO/6H-SiC interface was found to be dependent on substrate temperature and the presence of atomic oxygen. The MgO films and the MgO/6H-SiC interface are stable at temperatures up to 740 °C at 1.0 × 10⁻⁹ Torr for extended periods of time. While at temperatures below 400 °C exposure to the presence of active oxygen for extended periods of time has negligible impact, exposure to the presence of active oxygen for more than 5 min at 650 °C will degrade the MgO/6H-SiC interface. Concurrent etching and interface breakdown mechanisms are hypothesized to explain the observed effects. Further, barium titanate was deposited by MBE on bare 6H-SiC(0 0 0 1) and MgO(1 1 1)/6H-SiC(0 0 0 1) in order to evaluate the effectiveness of the MgO as a heteroepitaxial template layer for perovskite ferroelectrics.     

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Four-fold magnetic anisotropy in a Co film on MgO(0 0 1)

The development of devices based on magnetic tunnel junctions has raised new interests on the structural and magnetic properties of the interface Co/MgO. In this context, we have grown ultrathin Co films (≤30 Å) by molecular-beam epitaxy on MgO(0 0 1) substrates kept at different temperatures (T_S). Their structural and magnetic properties were correlated and discussed in the context of distinct magnetic anisotropies for Co phases reported in the literature. The sample characterization has been done by reflection high energy electron diffraction, magneto-optical Kerr effect and ferromagnetic resonance. The main focus of the work is on a sample deposited at T_S=25 °C, as its particular way of growth has enabled a bct Co structure to settle on the substrate, where it is not normally obtained without specific seed layers. This sample presented the best crystallinity, softer magnetic properties and a four-fold in-plane magnetic anisotropy with Co〈1 1 0〉 easy directions. Concerning the samples prepared at T_S=200 and 500° C, they show fcc and polycrystalline structures, respectively and more intricate magnetic anisotropy patterns.     

Surface structures of K on Mo(1 1 0) surface investigated by RHEED

Phase transitions of K on Mo(1 1 0) have been studied by RHEED technique. As Ba and Cs structures on the bcc(1 1 0) surface, surface structures of K were hexagonal from RT to 250 °C for θ > 0.9 ML. The hexagonal structure successively expanded from α to γ structure with Nishiyama-Wassermamm (N-W) orientation relationship. The nearest neighbor spacing in the α structure at RT was 4.50 Å, which is very closed to the atomic distance of K in metal, and stretched to 5.14 Å in the γ structure at T = 200 °C. At temperatures greater than T = 250 °C, the γ structure oriented in N-W and Kurdjumov-Sachs (K-S) relationships at the same time and stayed up to the temperature of 450 °C. These two orientations of γ structure also appeared in all temperature range for 0.4 < θ < 0.9 ML.     

Growth and structure of vanadium oxide on anatase (1 0 1) terraces

The interaction of vanadium oxide with epitaxial anatase films exposing (1 0 1) terraces was characterized. The TiO₂ films were grown on vicinal LaAlO₃ (1 1 0) substrates by oxygen plasma-assisted molecular beam epitaxy (OPA-MBE); reflection high energy and low energy electron diffraction (RHEED and LEED) indicated that the films exposed (1 0 1) terraces of the anatase TiO₂ polymorph. When a vanadium oxide monolayer was deposited onto the anatase surface by OPA-MBE at 725 K, only (1 × 1) RHEED and LEED patterns were observed. The V X-ray photoelectron spectroscopy (XPS) peak intensities indicated that the monolayer wetted the anatase surface and so the diffraction patterns were attributed to an epitaxial vanadia layer. Analysis of the vanadium oxide monolayer by X-ray and ultraviolet photoelectron spectroscopies revealed that the V was predominantly 5+. When the vanadia coverage was increased at 725 K, Auger electron spectra showed only very slow attenuation of the anatase Ti peaks while spots began to develop in RHEED patterns recorded along the LaAlO₃ direction; both indicative of 3-D cluster formation. In the orthogonal direction, the RHEED patterns showed unusual diagonal streaks. Meanwhile, the (1 × 1) LEED pattern persisted even after 30 nm of vanadia was deposited. This was attributed to gaps between the 3-D clusters exposing the epitaxial monolayer. Core level XPS spectra of the 3-D clusters revealed a broad V 2p_3/2 peak that was centered at the position expected for V⁴⁺ but could be deconvoluted into three peaks corresponding to V³⁺, V⁴⁺, and V⁵⁺. It is shown that crystallographic shear that accommodates such variations in the oxygen content of V oxides can lead to the diagonal streaks in RHEED patterns recorded along the LaAlO₃ [0 0 1] direction even as the pattern in the orthogonal direction shows sharp transmission spots. The results show that vanadia growth on anatase (1 0 1) proceeds through the Stranski-Krastanov mode with a strong vanadia-titania interaction stabilizing a dispersed vanadia monolayer. The results are compared with previous data for vanadia growth on anatase (0 0 1) where smooth, epitaxial VO₂ films grow ad infinitum.     

Epitaxial growth of bcc-FexCo100-x thin films on MgO(1 1 0) single-crystal substrates

Fe_xCo_100-x (x=100, 65, 50 at%) epitaxial thin films were prepared on MgO(1 1 0) single-crystal substrates heated at 300 °C by ultra-high vacuum molecular beam epitaxy. The film structure and the growth mechanism are discussed. FeCo(2 1 1) films with bcc structure grow epitaxially on MgO(1 1 0) substrates with two types of variants whose orientations are rotated around the film normal by 180° each other for all compositions. Fe_xCo_100-x film growth follows the Volmer Weber mode. X-ray diffraction analysis indicates the out-of-plane and the in-plane lattice spacings are in agreement with the values of respective bulk Fe_xCo_100-x crystals with very small errors less than ±0.4%, suggesting the strains in the films are very small. High-resolution cross-sectional transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the film at the Fe₅₀Co₅₀/MgO interface along the MgO[1 1¯ 0] direction. The presence of such periodical dislocations decreases the large lattice mismatch of about −17% existing at the FeCo/MgO interface along the MgO[1 1¯ 0] direction.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Granular L10 FePt (0 0 1) thin films for Heat Assisted Magnetic Recording

Granular L1₀ FePt (0 0 1) thin films were deposited on a Si substrate with Ta/MgO underlayers by rf sputtering. The effects of in-situ heating temperatures (350-575 °C), pressures (2-40 mTorr), and sputtering powers (15-75 W) on texture and microstructure were investigated for the FePt films. We obtained films with grain densities approaching 50 teragrains per in.², grains sizes down to 2.2 nm with center-to-center spacing of 4.2 nm and coercivity of 24 kOe. The order parameters for the L1₀ FePt thin films were derived and calculated to be as high as 0.91. Although the grain size is small, the spacing between grains is too large for practical heat assisted magnetic recording media. To reach the desired results, we propose that layer-by-layer growth should be promoted in the FePt layer by inserting another underlayer that provides a better lattice match to L1₀ FePt.     

Microstructure and electrical properties of (Zr, Sn)TiO4 thin film deposited on Si(1 0 0) using a sol-gel process

Polycrystalline zirconium tin titanate (Zr_0.8Sn_0.2TiO₄, ZST) thin films with thickness of 81 nm were deposited successfully along the (1 0 0) on a p-type Si substrate by an improved sol-gel method. The deposited films were crystallized when annealing temperature was up to 450 °C. The thickness and compositions of the interface layer between the ZST films and Si substrate were identified by high-resolution transmission electron microscope (HRTEM). The electrical properties such as leakage current density, flat-band voltage and capacitance of the films were measured and discussed. Furthermore, the mechanism of the leakage current was also investigated.     

Hydrogen adsorption on GaAs(0 0 1)-c(4 × 4)

Exposure of the As-terminated GaAs(0 0 1)-c(4 × 4) reconstructed surface to atomic hydrogen (H) at different substrate temperatures (50-480 °C) has been studied by reflection high-energy electron diffraction (RHEED) and scanning tunnelling microscopy (STM). Hydrogen exposure at low temperatures (∼50 °C) produces a disordered (1 × 1) surface covered with AsH_x clusters. At higher temperatures (150-400 °C) exposure to hydrogen leads to the formation of mixed c(2 × 2) and c(4 × 2) surface domains with H adsorbed on surface Ga atoms that are exposed due to the H induced loss of As from the surface. At the highest temperature (480 °C) a disordered (2 × 4) reconstruction is formed due to thermal desorption of As from the surface. The results are consistent with the loss of As from the surface, either through direct thermal desorption or as a result of the desorption of volatile compounds which form after reaction with H.     

Bimodal growth of manganese silicide on Si(1 0 0)

Two different growth modes of manganese silicide are observed on Si(1 0 0) with scanning tunneling microscopy. 1.0 and 1.5 monolayer Mn are deposited at room temperature on the Si(1 0 0)-(2 × 1) substrate. The as-grown Mn film is unstructured. Annealing temperatures between room temperature and 450 °C lead to small unstructured clusters of Mn or Mn_xSi_y. Upon annealing at 450 °C and 480 °C, Mn reacts chemically with the Si substrate and forms silicide islands. The dimer rows of the substrate become visible again. Two distinct island shapes are found and identified as MnSi and Mn₅Si₃.     

The investigation of room temperature ferromagnetism in (1 0 0) oriented BaNb2O6 PLD films on LaAlO3 (1 0 0) substrate

(1 0 0) oriented BaNb₂O₆ films have been successfully grown on LaAlO₃ (1 0 0) substrate at 750 °C or 450 °C in vacuum by pulsed laser deposition. The deposited BaNb₂O₆ PLD films exhibit room-temperature ferromagnetism. Ab initio calculations demonstrate that stoichiometric BaNb₂O₆ and that with barium vacancy are nonmagnetic, while oxygen and niobium vacancy can induce magnetism due to the spin-polarization of Nb s electrons and O p electrons respectively. Moreover, ferromagnetic coupling is energetically more favorable when two Nb/O vacancies are located third-nearest-neighbored. The observed room temperature ferromagnetism in BaNb₂O₆ films should be mainly induced by oxygen vacancies introduced during vacuum deposition, with certain contribution by Nb vacancies.     

Femtosecond pulsed laser deposition of Ge quantum dot growth on Si(1 0 0)-(2 × 1)

Ge quantum dots were grown on Si(1 0 0)-(2 × 1) by femtosecond pulsed laser deposition at various substrate temperatures using a femtosecond Ti:sapphire laser. In situ reflection high-energy electron diffraction and ex situ atomic force microscopy were used to analyze the film structure and morphology. The morphology of germanium islands on silicon was studied at different coverages. The results show that femtosecond pulsed laser deposition reduces the minimum temperature for epitaxial growth of Ge quantum dots to ∼280 °C, which is 120 °C lower than previously observed in nanosecond pulsed laser deposition and more than 200 °C lower than that reported for molecular beam epitaxy and chemical vapor deposition.     

Influence of substrate temperature on structures and dielectric properties of pyrochlore Bi1.5Zn1.0Nb1.5O7 thin films prepared by pulsed laser deposition

The influence of substrate temperature on structural and dielectric properties of cubic pyrochlore Bi_1.5Zn_1.0Nb_1.5O₇ (BZN) thin films prepared by pulsed laser deposition process has been investigated. BZN thin films were deposited on Pt/Ti/SiO₂/Si(1 0 0) substrate and in situ annealed at 700 °C. The results indicate that the substrate temperature has a significant effect on the structural and dielectric properties of BZN thin films. The films exhibit a cubic pyrochlore structure in the substrate temperature range from 550 °C to 700 °C and at the annealing temperature of 700 °C. With further increase of substrate temperature to 750 °C, the phases of Bi₂O₃, BiNbO₄ and Bi₅Nb₃O₁₅ can be detected in the XRD pattern due to the Zn loss. The dielectric constant and loss tangent of the films deposited at 650 °C are 192 and 6 × 10⁻⁴ at 10 kHz, respectively. The tunability is 10% at a dc bias field of 0.9 MV/cm.