SrTiO3 homoepitaxy by the pulsed laser deposition method: island, layer-by-layer, and step-flow growth

SrTiO₃ homoepitaxy was investigated under various conditions using the pulsed laser deposition method. The growth mode was determined by in-situ reflection high-energy electron diffraction, and the surface of the films was characterized by ex-situ atomic force microscopy. At the laser fluence of 0.68 J/cm², island growth was observed below 500 °C substrate temperature, while the growth mode turned into layer-by-layer growth above 500 °C. On further raising the substrate temperature, the step-flow growth mode prevailed above 800 °C. We thus demonstrated that step-flow growth in SrTiO₃ homoepitaxy is possible at a temperature as low as 800 °C.     

Effects of substrate temperature on properties of NbNx films grown on Nb by pulsed laser deposition

NbN_x films were deposited on Nb substrate using pulsed laser deposition. The effects of substrate deposition temperature, from room temperature to 950 °C, on the preferred orientation, phase, and surface properties of NbN_x films were studied by X-ray diffraction, atomic force microscopy, and electron probe micro analyzer. We find that the substrate temperature is a critical factor in determining the phase of the NbN_x films. For a substrate temperature up to 450 °C the film showed poor crystalline quality. With temperature increase the film became textured and for a substrate temperature of 650−850 °C, mix of cubic δ-NbN and hexagonal phases (β-Nb₂N + δ′-NbN) were formed. Films with a mainly β-Nb₂N hexagonal phase were obtained at deposition temperature above 850 °C. The c/a ratio of β-Nb₂N hexagonal shows an increase with increased nitrogen content. The surface roughness of the NbN_x films increased as the temperature was raised from 450 to 850 °C.     

Fabrication of aligned carbon nanotubes on Cu catalyst by dc plasma-enhanced catalytic decomposition

Aligned multi-walled carbon nanotubes (ACNTs) are deposited using copper (Cu) catalyst on Chromium (Cr)-coated substrate by plasma-enhanced chemical vapor deposition at temperature of 700 °C. Acetylene gas has been used as the carbon source while ammonia is used for diluting and etching. The thicknesses of Cu films on Cr-coated Si (100) substrates are controlled by deposition time of magnetron sputtering. The growth behaviors and quality of ACNTs are investigated by scanning electron microscopy (SEM) and transmission electron microscopy. The different performance of ACNTs on various Cu films is explained by referring to the graphitic order as detected by Raman spectroscopy. The results indicate that the ACNTs are formed in tip-growth model where Cu is used as a novel catalyst, and the thickness of Cu films is responsible to the diameter and quality of synthesized CNTs.     

The effects of substrate temperature on the structure, morphology and photoluminescence properties of pulsed laser deposited SrAl2O4:Eu,Dy thin films

In this study, SrAl₂O₄:Eu²⁺,Dy³⁺ thin film phosphors were deposited on Si (1 0 0) substrates using the pulsed laser deposition (PLD) technique. The films were deposited at different substrate temperatures in the range of 40-700 °C. The structure, morphology and topography of the films were determined by using X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). Photoluminescence (PL) data was collected in air at room temperature using a 325 nm He-Cd laser as an excitation source. The PL spectra of all the films were characterized by green phosphorescent photoluminescence at ∼530 nm. This emission was attributed to 4f⁶5d¹→4f⁷ transition of Eu²⁺. The highest PL intensity was observed from the films deposited at a substrate temperature of 400 °C. The effects of varying substrate temperature on the PL intensity were discussed.     

Crystallization and surface morphology evolution of erbium fluoride films on different substrates

Erbium fluoride (ErF₃) films were thermally deposited on Ge(1 1 1), Si(0 0 1) and copper mesh grid with different substrate temperature. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and morphology of the films. The structure of ErF₃ films deposited on germanium and silicon changed from amorphous to crystalline with increasing the substrate temperature, while the crystallization temperature of the films on silicon is higher than that of on germanium. The infrared optical properties of the films change greatly with the evolution of crystal structure. It is also found that the morphology of ErF₃ film on Ge(1 1 1) at 200 °C is modulated by the stress between the substrate and film. The SEM and TEM results confirmed that the ErF₃ films on copper mesh grid were crystalline even at 100 °C. Interestingly, the ErF₃ films show flower-like surface morphology when deposited on copper mesh at 200 °C. The crystallization temperature (T_c) of ErF₃ films on the three substrates has the relation which is which is induced by the wetting angle of ErF₃ films on different substrates.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Effect of substrate temperature and annealing temperature on the structural, electrical and microstructural properties of thin Pt films by rf magnetron sputtering

Influence of both substrate temperature, T_s, and annealing temperature, T_a, on the structural, electrical and microstructural properties of sputtered deposited Pt thin films have been investigated. X-ray diffraction results show that as deposited Pt films (T_s = 300, 400 °C) are preferentially oriented along (1 1 1) direction. A little growth both along (2 0 0) and (3 1 1) directions are also noticed in the as deposited Pt films. After annealing in air (T_a = 500-700 °C), films become strongly oriented along (1 1 1) plane. With annealing temperature, average crystallite size, D, of the Pt films increases and micro-strain, e, and lattice constant, a₀, decreases. Residual strain observed in the as deposited Pt films is found to be compressive in nature while that in the annealed films is tensile. This change in the strain from compressive to tensile upon annealing is explained in the light of mismatch between the thermal expansion coefficients of the film material and substrate. Room temperature resistivity of Pt films is dependant on both the T_s and T_a of the films. Observed decrease in the film resistivity with T_a is discussed in terms of annihilation of film defects and grain-boundary. Scanning electron microscopic study reveals that as the annealing temperature increases film densification improves. But at an annealing temperature of ∼600 °C, pinholes appear on the film surface and the size of pinhole increases with further increase in the annealing temperature. From X-ray photoelectron spectroscopic analysis, existence of a thin layer of chemisorbed atomic oxygen is detected on the surfaces of the as deposited Pt films. Upon annealing, coverage of this surface oxygen increases.     

In situ growth stresses during the phase separation of immiscible FeCu thin films

This paper addresses the in situ growth stress evolution and post-growth stress relaxation during the phase separation of immiscible Fe_0.51Cu_0.49 thin films at various in situ deposition temperatures. Each film was sputter-deposited onto a 10 nm Si₃N₄ underlayer that was grown on top of Si [0 0 1] substrate at 25 °C, 145 °C, 205 °C, 265 °C or 325 °C. The thin film stress was measured using a wafer curvature technique. The in situ growth stress increased in compression with increasing substrate temperature. The stress relaxation of the Fe_0.51Cu_0.49 was found to have a linear increase with the inverse grain size for films deposited at temperatures greater than 205 °C. The stress state was correlated to the films’ phase and morphology by X-ray diffraction, (scanning) transmission electron microscopy and atomic force microscopy techniques.     

Effect of heat treatment on morphology, crystalline structure and photocatalysis properties of TiO2 nanotubes on Ti substrate and freestanding membrane

Highly ordered titanium oxide (TiO₂) nanotubes were prepared by electrolytic anodization of titanium electrodes. Morphological evolution and phase transformations of TiO₂ nanotubes on a Ti substrate and that of freestanding TiO₂ membranes during the calcinations process were studied by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction microscopy. The detailed results and mechanisms on the morphology and crystalline structure were presented. Our results show that a compact layer exists between the tubular layer and Ti substrate at 600 °C, and the length of the nanotubes shortens dramatically at 750 °C. The freestanding membranes have many particles on their tubes during calcinations from 450 to 900 °C. The TiO₂ nanotubes on the Ti substrate transform to rutile crystals at 600 °C, while the freestanding TiO₂ membranes retain an anatase crystal with increasing temperature to 800 °C. The photocatalytic activity of TiO₂ nanotubes on a Ti substrate annealed at different temperatures was investigated by the degradation of methyl orange in aqueous solution under UV light irradiation. Due to the anatase crystals in the tubular layer and rutile crystals in the compact layer, TiO₂ nanotubes annealed at 450 °C with pure anatase crystals have a better photocatalytic activity than those annealed at 600 °C or 750 °C.     

Characterization of CdTe films with in situ CdCl2 treatment grown by a simple vapor phase deposition technique

A unique vapor phase deposition (VPD) technique was designed and built to achieve in situ CdCl₂ treatment of CdTe film. The substrate temperature was 400 °C, and the temperature of CdTe mixture with CdCl₂ source was 500 °C. The structural and morphological properties of CdTe have been studied as a function of wt.% CdCl₂ concentration by using X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM) and atomic force microscopy (AFM). XRD measurements show that the presence of CdCl₂ vapor induces (1 1 1)-oriented growth in the CdTe film. SEM measurements have shown enhance growth of grains, in the presence of CdCl₂. From AFM the roughness of the films showed a heavy dependence on CdCl₂ concentration. In the presence of 4% CdCl₂ concentration, the CdTe films roughness has a root mean square (rms) value of about 275 Å. This value is about 831 Å for the non-treated CdTe films.     

Fabrication and characterization of CuO-core/TiO2-shell one-dimensional nanostructures

We have fabricated CuO-core/TiO₂-shell one-dimensional nanostructures by coating the CuO nanowires with MOCVD-TiO₂. The structure of the core/shell nanowires has been investigated by using scanning electron microscopy, transmission electron microscopy, and X-ray diffraction analysis techniques. The CuO-cores and the TiO₂-shells of the as-synthesized nanowires have been found to have crystalline monoclinic CuO and crystalline tetragonal anatase TiO₂ structures, respectively. The CuO-core/TiO₂-shell nanowires are winding and has rougher surface, whereas the CuO nanowires are straight and have smoother surface.Influence of the substrate temperature and the growth time on the structure such as the morphology, size, and crystallographic orientation of CuO nanowires synthesized by thermal oxidation of Cu foils have also been investigated. All the nanowires have only the CuO phase synthesized at 600 °C, whereas those synthesized at 400 °C have both CuO and Cu₂O phases. The highest density of CuO nanowires with long thin straight morphologies can be obtained at 600 °C. In addition, the growth mechanism of the CuO nanowires has been discussed.     

Temperature and substrate dependence of structure and growth mechanism of carbon nanofiber

The carbon nanofibers were grown on Ni/Si and Ni/Ti/Si substrates in 1 atm CH₄ atmosphere at 640 °C and 700 °C by thermal chemical vapor deposition method. The carbon nanofibers were characterized by field emission scanning electron microscopy, transmission electron microscopy, and Raman spectrometry for morphology, microstructure, and crystallinity. The electron emission property of carbon nanofibers was also investigated by current-voltage (I-V) measurement. The results showed that the solid amorphous carbon nanofibers could be grown on Ni/Si substrate at 640 °C through tip growth mechanism, the carbon nanotubes could be grown on Ni/Si substrate at 700 °C through tip growth mechanism, and the carbon nanotubes could be grown on Ni/Ti/Si substrate at 700 °C through root growth mechanism.     

Formation of silicon nanodots from dysprosium-doped amorphous SiCxOy films grown by hot-filament assisted chemical vapor deposition of CH3SiH3 and Dy(DPM)3 gas jets

We report on Si nanodot formation by chemical vapor deposition (CVD) of ultrathin films and following oxidation. The film growth was carried out by hot-filament assisted CVD of CH₃SiH₃ and Dy(DPM)₃ gas jets at the substrate temperature of 600 °C. The transmission electron microscopy observation and X-ray photoelectron spectroscopy analysis indicated that ∼35 nm Dy-doped amorphous silicon oxycarbide (SiC_xO_y) films were grown on Si(1 0 0). The Dy concentration was 10-20% throughout the film. By further oxidation at 860 °C, the smooth amorphous film was changed to a rough structure composed of crystalline Si nanodots surrounded by heavily Dy-doped SiO₂.     

Thickness dependence on thermal stability of sputtered Ag nanolayer on Ti/Si(1 0 0)

Thermal stability of Ag layer on Ti coated Si substrate for different thicknesses of the Ag layer have been studied. To do this, after sputter-deposition of a 10 nm Ti buffer layer on the Si(1 0 0) substrate, an Ag layer with different thicknesses (150-5 nm) was sputtered on the buffer layer. Post annealing process of the samples was performed in an N₂ ambient at a flow rate of 200 ml/min in a temperature range from 500 to 700 °C for 30 min. The electrical property of the heat-treated multilayer with the different thicknesses of Ag layer was examined by four-point-probe sheet resistance measurement at the room temperature. Phase formation and crystallographic orientation of the silver layers were studied by θ-2θ X-ray diffraction analysis. The surface topography and morphology of the heat-treated films were determined by atomic force microscopy, and also, scanning electron microscopy. Four-point- probe electrical measurement showed no considerable variation of sheet resistance by reducing the thickness of the annealed Ag films down to 25 nm. Surface roughness of the Ag films with (1 1 1) preferred crystallographic orientation was much smaller than the film thickness, which is a necessary condition for nanometric contact layers. Therefore, we have shown that the Ag layers with suitable nano-thicknesses sputtered on 10 nm Ti buffer layer were thermally stable up to 700 °C.     

Effects of deposition temperature on the structural and morphological properties of SnO2 films fabricated by pulsed laser deposition

Tin oxide (SnO₂) thin films were grown on Si (1 0 0) substrates using pulsed laser deposition (PLD) in O₂ gas ambient (10 Pa) and at different substrate temperatures (RT, 150, 300 and 400 °C). The influence of the substrate temperature on the structural and morphological properties of the films was investigated using X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). XRD measurements showed that the almost amorphous microstructure transformed into a polycrystalline SnO₂ phase. The film deposited at 400 °C has the best crystalline properties, i.e. optimum growth conditions. However, the film grown at 300 °C has minimum average root mean square (RMS) roughness of 3.1 nm with average grain size of 6.958 nm. The thickness of the thin films determined by the ellipsometer data is also presented and discussed.     

The influence of substrate temperature variation on tungsten oxide thin film growth in an HFCVD system

Tungsten oxide (WO₃) thin films were deposited by a modified hot filament chemical vapor deposition (HFCVD) technique using Si (1 0 0) substrates. The substrate temperature was varied from room temperature to 430 °C at an interval of 100 °C. The influence of the substrate temperature on the structural and optical properties of the WO₃ films was studied. X-ray diffraction and Raman spectra show that as substrate temperature increases the film tends to crystallize from the amorphous state and the surface roughness decreases sharply after 230 °C as confirmed from AFM image analysis. Also from the X-ray analysis it is evident that the substrate orientation plays a key role in growth. There is a sharp peak for samples on Si substrate due to texturing. The film thickness also decreases as substrate temperature increases. UV-vis spectra show that as substrate temperature increases the film property changes from metallic to insulating behavior due to changing stoichiometry, which was confirmed by XPS analysis.     

Spray pyrolytic synthesis of samarium doped ceria (Ce0.8Sm0.2O1.9) films for solid oxide fuel cell applications

Uniform, adherent, single phase samarium doped ceria films have been successfully deposited by spray pyrolysis technique for their application in solid oxide fuel cell. These films have been deposited at different substrate temperatures on glass substrate and subsequently heat treated in tube furnace. Effect of substrate temperature and annealing temperature on phase formation was studied with thermo-gravimetric analysis and differential temperature analysis, X-ray diffraction, scanning electron microscope, and energy dispersive X-ray analysis techniques. These studies showed the formation of single phase Ce_0.8Sm_0.2O_1.9 films, at substrate temperature 400 °C and annealing temperature 550 °C. Electrical resistivity of the films, at room temperature was of the order of 10⁷ Ω cm while at 400 °C it is found to be of the order of 10¹ Ω cm. This reveals the use of these films for making low temperature solid oxide fuel cells.     

Synthesis of In-doped Ga2O3 zigzag-shaped nanowires and optical properties

In-doped Ga₂O₃ zigzag-shaped nanowires and undoped Ga₂O₃ nanowires have been synthesized on Si substrate by thermal evaporation of mixed powders of Ga, In₂O₃ and graphite at 1000 °C without using any catalyst via a vapor-solid growth mechanism. The morphologies and microstructures of the products were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence spectroscopy (PL). The nanowires range from 100 nm to several hundreds of nanometers in diameter and several tens of micrometers in length. A broad emission band from 400 to 700 nm is obtained in the PL spectrum of these nanowires at room temperature. There are two blue-emission peaks centering at 450 and 500 nm, which originate from the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.     

Microstructure of epitaxial SrRuO3 thin films on MgO substrates

SrRuO₃ thin films have been grown on singular (1 0 0) MgO substrates using pulsed laser deposition (PLD) in 30 Pa oxygen ambient and at a temperature of 400-700 °C. Ex situ reflection high-energy electron diffraction (RHEED) as well as X-ray diffraction (XRD) θ/2θ scan indicated that the films deposited above 650 °C were well crystallized though they had a rough surface as shown by atom force microscopy (AFM). XRD Φ scans revealed that these films were composed of all three different types of orientation domains, which was further confirmed by the RHEED patterns. The heteroepitaxial relationship between SrRuO₃ and MgO was found to be [1 1 0] SRO//[1 0 0] MgO and 45°-rotated cube-on-cube [0 0 1] SRO//[1 0 0] MgO. These domain structures and surface morphology are similar to that of ever-reported SrRuO₃ thin films deposited on the (0 0 1) LaAlO₃ substrates, and different from those deposited on (0 0 1) SrTiO₃ substrates that have an atomically flat surface and are composed of only the [1 1 0]-type domains. The reason for this difference was ascribed to the effect of lattice mismatch across the film/substrate interface. The room temperature resistivity of SrRuO₃ films fabricated at 700 °C was 300 μΩ cm. Therefore, epitaxial SrRuO₃ films on MgO substrate could serve as a promising candidate of electrode materials for the fabrication of ferroelectric or dielectric films.     

Growth and structure of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 thin films prepared by pulsed laser deposition technique

Bi_0.5(Na_0.7K_0.2Li_0.1)_0.5TiO₃ (BNKLT) thin films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition (PLD) technique. The films prepared were examined by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The effects of the processing parameters, such as oxygen pressure, substrate temperature and laser power, on the crystal structure, surface morphology, roughness and deposition rates of the thin films were investigated. It was found that the substrate temperature of 600 °C and oxygen pressure of 30 Pa are the optimized technical parameters for the growth of textured film, and all the thin films prepared have granular structure, homogeneous grain size and smooth surfaces.