Synthesis, physical and photo electrochemical characterization of La-doped SrSnO3

The transport properties of Sr_0.98La_0.02SnO_3−δ in the system Sr_1−xLa_xSnO_3−δ, after which the pyrochlore La₂Sn₂O₇ appears, were investigated over the temperature range 4.2-300 K. The oxide was found to be n-type semiconductor with concomitant reduction of Sn⁴⁺ into Sn²⁺. The magnetic susceptibility was measured down to 4.2 K and is less than 3×10⁻⁵ emu cgs mol⁻¹ consistent with itinerant electron behavior. The electron is believed to travel in a narrow band of Sn:5s character with an effective mass ∼4 m_o. The highest band gap is 4.32 eV and the optical transition is directly allowed. A further indirect transition occurs at 4.04 eV. The electrical conductivity follows an Arrhenius-type law with a thermal activation of 40 meV and occurs by small polaron hopping between nominal states Sn^4+/2+. The linear increase of thermo-power with temperature yields an electron mobility μ_300 K (2×10⁻⁴ cm² V⁻¹ s⁻¹) thermally activated. The insulating-metal transition seems to be of Anderson type resulting from random positions of lanthanum sites and oxygen vacancies. At low temperatures, the conduction mechanism changes to a variable range hopping with a linear plot Ln ρ⁻¹ vs. T⁻⁴. The photo electrochemical (PEC) measurements confirm the n-type conductivity and give an onset potential of −0.46 V_SCE in KOH (1 M). The Mott-Schottky plot C⁻²-V shows a linear behavior from which the flat band potential V_fb=+0.01 V_SCE at pH 7 and the doping density N_D=1.04×10²¹ cm⁻³ were determined.     

Physical properties of the delafossite LaCuO2

High-quality LaCuO₂, elaborated by solid-state reaction in sealed tube, crystallizes in the delafossite structure. The thermal analysis under reducing atmosphere (H₂/N₂: 1/9) revealed a stoichiometric composition LaCuO_2.00. The oxide is a direct band-gap semiconductor with a forbidden band of 2.77 eV. The magnetic susceptibility follows a Curie-Weiss law from which a Cu²⁺ concentration of 1% has been determined. The oxygen insertion in the layered crystal lattice induces p-type conductivity. The electrical conduction occurs predominantly by small polaron hopping between mixed valences Cu^+/2+ with an activation energy of 0.28 eV and a hole mobility (μ_300 K=3.5×10⁻⁷ cm² V⁻¹ s⁻¹), thermally activated. Most holes are trapped in surface-polaron states upon gap excitation. The photoelectrochemical study, reported for the first time, confirms the p-type conduction. The flat band potential (V_fb=0.15 V_SCE) and the hole density (N_A=5.8×10¹⁷ cm⁻³) were determined, respectively, by extrapolating the curve C⁻² versus the potential to their intersection with C⁻²=0 and from the slope of the linear part in the Mott-Schottky plot. The valence band is made up of Cu-3d orbital, positioned at 4.9 eV below vacuum. An energy band diagram has been established predicting the possibility of the oxide to be used as hydrogen photocathode.     

Synthesis, structure and luminescence of LaSi3N5:Ce phosphor

In this work, new LaSi₃N₅:Ce³⁺ phosphors have been synthesized by solid-state reaction. Rietveld refinement of the crystal structure of La_1−xCe_xSi₃N₅ reveals that Ce atoms substituted for La atoms occupy 4a crystallographic positions. Broad emission and excitation bands observed were attributed to the transitions between the doublet ground state of the 4f¹ configuration and the crystal field components of the 5d¹ excited state. At 77 K, the centroid and crystal field splitting ε_cfs of the 5d levels of Ce³⁺ in LaSi₃N₅:Ce³⁺ compounds were valuated at 33.4×10³ and 11.3×10³ cm⁻¹, respectively. The zero-phonon line and the Stokes shift were measured to be 26.0×10³ and 5.0×10³ cm⁻¹, respectively.     

Structure and low-temperature properties of Ba8Ni6Ge40

Structural, magnetic, heat capacity, electrical and thermal transport properties are reported on polycrystalline Ba₈Ni₆Ge₄₀. Ba₈Ni₆Ge₄₀ crystallizes in a cubic type I clathrate structure with unit cell a=10.5179 (4) Å. It is diamagnetic with susceptibility χ_dia=−1.71×10^-6 emu/g Oe. An Einstein temperature 75 K and a Debye temperature 307 K are estimated from heat capacity data. It exhibits n-type conducting behavior below 300 K. It shows high Seebeck coefficients (−111×10^-6 V/K), low thermal conductivity (2.25 W/K m), and low electrical resistivity (8.8 mΩ cm) at 300 K.     

Low-temperature thermoelectric properties of Bi85Sb15−xNbx alloys prepared by high-press sintering

The nanocrystalline materials with the general formula Bi₈₅Sb_15−xNb_x (x=0, 0.5, 1, 2, 3) were prepared by mechanical alloying and subsequent high-pressure sintering. Their transport properties involving electrical conductivity, Seebeck coefficient and thermal conductivity have been investigated in the temperature range of 80-300 K. The absolute value of Seebeck coefficient of Bi₈₅Sb₁₃Nb₂ reaches a maximum of 161 μV/K at 105 K, which is 69% larger than that of Bi₈₅Sb₁₅ at the same temperature. The power factor and figure-of-merit are 4.45×10⁻³ WK⁻²m⁻¹ at 220 K and 1.79×10⁻³ K⁻¹ at 196 K, respectively. These results suggest that thermoelectric properties of Bi₈₅Sb₁₅ based material can be improved by Nb doping.     

Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

Effects of lattice and local dynamics in EPR spectra and electron spin relaxation of vibronic Cu(imidazole)6 complexes in Zn(imidazole)6Cl2·4H2O crystals

Cu(im)₆ complexes in Zn(im)₆Cl₂·4H₂O exhibit a strong Jahn-Teller effect which is static below 100 K and the complex in localized in the two low-energy potential wells. We have reinvestigated electron paramagnetic resonance (EPR) spectra in the temperature range 4.2-300 K and determined the deformation directions produced by the Jahn-Teller effect, energy difference 11 cm⁻¹ between the wells and energy 300 cm⁻¹ of the third potential well. The electron spin relaxation was measured by electron spin echo (ESE) method in the temperature range of 4.2-45 K for single crystal and powder samples. The spin-lattice relaxation is dominated by a local mode of vibration with energy 11 cm⁻¹ at low temperatures. We suppose that this mode is due to reorientations (jumps) of the Cu(im)₆ complex between the two lowest energy potential wells. At intermediate temperatures (15-35 K), the T₁ relaxation is determined by the two-phonon Raman processes in acoustic phonon spectrum with Debye temperature Θ_D=167 K, whereas at higher temperatures the relaxation is governed by the optical phonon of energy 266 cm⁻¹. The ESE dephasing is produced by an instantaneous diffusion below 15 K with the temperature-independent phase memory time , then it grows exponentially with temperature with an activation energy of 97 cm⁻¹. This is the energy of the first excited vibronic level. The thermal population of this level leads to a transition from anisotropic to isotropic EPR spectrum observed around 90 K. FT-ESE gives ESEEM spectrum dominated by quadrupole peaks from non-coordinating ¹⁴N atom of the imidazole rings and the peak from double quantum transition ν_dq. We show that the amplitude of the ν_dq transition can be used to determine the number of non-coordinating nitrogen atoms.     

Single crystal EPR and optical absorption study of Cr doped l-histidine hydrochloride monohydrate

EPR study of the Cr³⁺ ion doped l-histidine hydrochloride monohydrate single crystal is done at room temperature. Two magnetically inequivalent interstitial sites are observed. The hyperfine structure for Cr⁵³ isotope is also obtained. The zero field and spin Hamiltonian parameters are evaluated from the resonance lines obtained at different angular rotations and the parameters are: D=(300±2)×10⁻⁴ cm⁻¹, E=(96±2)×10⁻⁴ cm⁻¹, g_x=1.9108±0.0002, g_y=1.9791±0.0002, g_z=2.0389±0.0002, A_x=(252±2)×10⁻⁴ cm⁻¹, A_y=(254±2)×10⁻⁴ cm⁻¹, A_z=(304±2)×10⁻⁴ cm⁻¹ for site I and D=(300±2)×10⁻⁴ cm⁻¹, E=(96±2)×10⁻⁴ cm⁻¹, g_x=1.8543±0.0002, g_y=1.9897±0.0002, g_z=2.0793±0.0002, A_x=(251±2)×10⁻⁴ cm⁻¹, A_y=(257±2)×10⁻⁴ cm⁻¹, A_z=(309±2)×10⁻⁴ cm⁻¹ for site II, respectively. The optical absorption studies of single crystals are also carried out at room temperature in the wavelength range 195-925 nm. Using EPR and optical data, different bonding parameters are calculated and the nature of bonding in the crystal is discussed. The values of Racah parameters (B and C), crystal field parameter (Dq) and nephelauxetic parameters (h and k) are: B=636, C=3123, Dq=2039 cm⁻¹, h=1.46 and k=0.21, respectively.     

Molecular dynamics and phase transitions in paramagnetic [Mn(H2O)6][SiF6] investigated by H NMR

The temperature dependences of ²H NMR spectra and spin-lattice relaxation time T₁ have been measured for paramagnetic [Mn(H₂O)₆][SiF₆]. The obtained ²H NMR spectra were simulated by considering the quadrupole interaction and paramagnetic shift. The variation of the spectra measured in phase III was explained by the 180° flip of water molecules. The activation energy E_a and the jumping rate at infinite temperature k₀ for the 180° flip of H₂O were obtained as 35 kJ mol⁻¹ and 4×10¹⁴ s⁻¹, respectively. The spectral change in phases I and II was ascribed to the reorientation of [Mn(H₂O)₆]²⁺ around the C₃ axis where the E_a and k₀ values were estimated as 45 kJ mol⁻¹ and 1×10¹³ s⁻¹, respectively. From the almost temperature independent and short T₁ value, the correlation time for electron-spin flip-flops, τ_e, and the exchange coupling constant J were obtained as 3.0×10⁻¹⁰ s and 2.9×10⁻³ cm⁻¹, respectively. The II-III phase transition can be caused by the onset of the jumping motion of [Mn(H₂O)₆]²⁺ around the C₃ axis.     

Preparation, structure and oxide ion conductivity in Ce6−xYxMoO15−δ (x=0.1-1.4) solid solutions

The Ce_6−xY_xMoO_15−δ solid solution with fluorite-related structure have been characterized by differential thermal analysis/thermogravimetry (DTA/TG), X-ray diffraction (XRD), IR, Raman, scanning electric microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) methods. The electric conductivity of samples is investigated by Ac impedance spectroscopy. An essentially pure oxide-ion conductivity of the oxygen-deficiency was observed in pure argon, oxygen and air. The highest oxygen-ion conductivity was found in Ce_5.5Y_0.5MoO_15−δ ranging from 5.9×10⁻⁵ (S cm⁻¹) at 300 °C to 1.3×10⁻² (S cm⁻¹) at 650 °C, respectively. The oxide-ion conductivities remained stable over 80 h-long test at 800 °C. These properties suggested that significant oxide-ionic conductivity exists in these materials at moderately elevated temperatures.     

Growth and spectroscopic characterization of Er: Sr3Y(BO3)3 crystal

This paper reports the growth and spectroscopic characterization of Er³⁺:Sr₃Y(BO₃)₃ crystal. Er³⁺:Sr₃Y(BO₃)₃ crystal with dimensions up to ∅20×35 mm³ has been grown by Czochralski method. The polarized spectroscopic properties of Er³⁺:Sr₃Y(BO₃)₃ crystal were investigated. Based on the Judd-Ofelt theory, the effective intensity parameters Ω_t were obtained: Ω₂=1.71×10⁻²⁰ cm², Ω₄=1.39×10⁻²⁰ cm², Ω₆=0.74×10⁻²⁰ cm² for π-polarization, and Ω₂=1.77×10⁻²⁰ cm², Ω₄=1.44×10⁻²⁰ cm², Ω₆=0.65×10⁻²⁰ cm² for σ-polarization. The emission cross-section σ_em was calculated to be 4.75×10⁻²¹ cm² for π-polarization at 1536 nm and 6.30×10⁻²¹ cm² for σ-polarization at 1537 nm. The investigated results showed that Er³⁺:Sr₃Y(BO₃)₃ crystal may be regarded as a potential laser host material for 1.55 μm IR solid-state lasers.     

Spectral properties of Nd:Ca2Nb2O7 crystal

This paper reports the spectral properties of Nd³⁺:Ca₂Nb₂O₇. The spectral parameters of Nd³⁺ in Nd³⁺:Ca₂Nb₂O₇ crystal have been investigated based on Judd-Ofelt theory. The spectral parameters were obtained. The parameters of line strengths Ω_λ are Ω₂=4.967×10⁻²⁰ cm², Ω₄=5.431×10⁻²⁰ cm², Ω₆=5.693×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 122 μs, 103 μs and 84.4%, respectively. The fluorescence branch ratios calculated: β₁=0.425, β₂=0.479, β₃=0.091, β₄=0.004. The emission cross section at 1068 nm is 6.204×10⁻²⁰ cm².     

Physical properties of the cubic spinel LiMn2O4

We have performed an ab initio study of structural, electronic, magnetic, vibrational and thermal properties of the cubic spinel LiMn₂O₄ by employing the density functional theory, the linear-response formalism, and the plane-wave pseudopotential method. An analysis of the electronic structure with the help of electronic density of states shows that the density of states at the Fermi level (N (E_F)) is found to be governed by the Mn 3d electrons with some contributions from the 2p states of O atoms. It is important to note that the contribution of Mn 3d states to N(_EF)$N\left(E_F\right)$ is as much as 85%. From our phonon calculations, we have obtained that the main contribution to phonon density of states (below 250 cm⁻¹) comes from the coupled motion of Mn and O atoms while phonon modes between 250 cm⁻¹ and 375 cm⁻¹ are characterized by the vibrations of all the three types of atoms. The contribution from Li increases rapidly at higher frequency (above 375 cm⁻¹) due to the light mass of this atom. Finally, the specific heat and the Debye temperature at 300 K are calculated to be 249.29 J/mol K and 820.80 K respectively.     

Magnetic and electrical properties of amorphous Ge1−xCrx thin films grown by low temperature vapor deposition

Amorphous Ge_1−xCr_x thin films are deposited on (1 0 0)Si by using a thermal evaporator. Amorphous phase is obtained when Cr concentration is lower than 30.7 at%. The electrical resistivities are 1.89×10⁻³–0.96×10² Ω cm at 300 K, and decrease with Cr concentration. The Ge_1−xCr_x thin films are p-type. The hole concentrations are 5×10¹⁶–7×10²¹ cm⁻³ at 300 K, and increase with Cr concentration. Magnetizations are 7.60–1.57 emu/cm³ at 5 K in the applied field of 2 T. The magnetizations decrease with Cr concentration and temperature. Magnetization characteristics show that the Ge_1−xCr_x thin films are paramagnetic.     

Electron hopping mechanism in hematite (α-Fe2O3)

The frequency dependence of the real (?′) and imaginary (?″) parts of the dielectric constant of polycrystalline hematite (α-Fe₂O₃) has been investigated in the frequency range 0-100 kHz and the temperature range 190-350 K, in order to reveal experimentally the electron hopping mechanism that takes place during the Morin transition of spin-flip process. The dielectric behaviour is described well by the Debye-type relaxation (α-dispersion) in the temperature regions T<233 K and T>338 K. In the intermediate temperature range 233 K<T<338 K a charge carrier mechanism takes place (electron jump from the O²⁻ ion into one of the magnetic ions Fe³⁺) which gives rise to the low frequency conductivity and to the Ω-dispersion. The temperature dependence of relaxation time (τ) in the −ln τ vs 10³/T plot shows two linear regions. In the first, T<238 K, τ increases with increasing T implying a negative activation energy −0.01 eV, and in the second region T>318 K τ decreases as the temperature increases implying a positive activation energy 0.12 eV. The total reorganization energy (0.12-0.01) 0.11 eV is in agreement with the adiabatic activation energy 0.11 eV given by an ab initio model in the literature. The temperature dependence of the phase shift in the frequencies 1, 5, 10 kHz applied shows clearly an average Morin temperature T_Mo=284±1 K that is higher than the value of 263 K corresponding to a single crystal due to the size and shape of material grains.     

On the high-resistivity contacts to YBa2Cu3O7 thin films, electrical behavior in the regime of high temperatures and high-bias voltages

We prepared in-situ Au contacts on high-quality epitaxial YBa₂Cu₃O₇ (YBCO) films. Very high specific contact resistivity values up to ∼10⁻² Ω cm² at 4.2 K were obtained on 12×5 μm² contact areas. This resistivity value decreased by two orders of magnitude as the temperature was raised to room temperature. In the temperature range T<200 K, the contacts showed non-ohmic behavior suggesting the presence of a well-defined insulating native Y-Ba-Cu-O barrier between the two electrodes. The electrical transport in this barrier layer was analyzed in the limit of high temperatures and high voltages to follow Mott's variable-range hopping conduction mechanism with physically reasonable parameters describing the localized states in the barrier. The high-resistivity contacts were tested successfully in quasiparticles injection experiments where the critical current I_c of the YBCO microbridge could be strongly suppressed on injection of an additional current through the contact into the superconducting channel.     

Antiferromagnetic phase transition in garnet-type AgCa2Co2V3O12 and AgCa2Ni2V3O12

Antiferromagnetic phase transition in two vanadium garnets AgCa₂Co₂V₃O₁₂ and AgCa₂Ni₂V₃O₁₂ has been found and investigated extensively. The heat capacity exhibits sharp peak due to the antiferromagnetic order with the Néel temperature T_N=6.39 K for AgCa₂Co₂V₃O₁₂ and 7.21 K for AgCa₂Ni₂V₃O₁₂, respectively. The magnetic susceptibilities exhibit broad maximum, and these T_N correspond to the inflection points of the magnetic susceptibility χ a little lower than T(χ_max). The magnetic entropy changes from zero to 20 K per mol Co²⁺ and Ni²⁺ ions are 5.31 J K⁻¹ mol-Co²⁺-ion⁻¹ and 6.85 J K⁻¹ mol-Ni²⁺-ion⁻¹, indicating S=1/2 for Co²⁺ ion and S=1 for Ni²⁺ ion. The magnetic susceptibility of AgCa₂Ni₂V₃O₁₂ shows the Curie-Weiss behavior between 20 and 350 K with the effective magnetic moment μ_eff=3.23 μ_B Ni²⁺-ion⁻¹ and the Weiss constant θ=−16.4 K (antiferromagnetic sign). Nevertheless, the simple Curie-Weiss law cannot be applicable for AgCa₂Co₂V₃O₁₂. The complex temperature dependence of magnetic susceptibility has been interpreted within the framework of Tanabe-Sugano energy diagram, which is analyzed on the basis of crystalline electric field. The ground state is the spin doublet state ²E(t₂⁶e) and the first excited state is spin quartet state ⁴T₁(t₂⁵e²) which locates extremely close to the ground state. The low spin state S=1/2 for Co²⁺ ion is verified experimentally at least below 20 K which is in agreement with the result of the heat capacity.     

Low-energy excitations and stripes in superconducting cuprate La1.87Sr0.13CuO4

The conductivity and dielectric permittivity spectra of single-crystalline La_1.87Sr_0.13CuO₄ are directly measured with the electric field polarized perpendicular to the CuO planes (E∥c) covering the frequency range 10-40 cm⁻¹ and temperatures 5-300 K. We observe in the superconducting state a well pronounced excitation with strongly temperature dependent parameters. We suggest that the excitation is caused by the transverse Josephson plasma mode that appears due to the different strengths of Josephson coupling between the superconducting charge stripes in the neighboring and next-nearest neighboring copper-oxygen planes of La_1.87Sr_0.13CuO₄. A strongly enhanced low-frequency (below 15 cm⁻¹) absorption is seen in the superconducting state that is assigned to delocalized quasiparticles of as yet unknown origin.     

Trap levels in layered semiconductor Ga2SeS

Trap levels in nominally undoped Ga₂SeS layered crystals have been characterized by thermally stimulated current (TSC) measurements. During the measurements, current was allowed to flow along the c-axis of the crystals in the temperature range of 10-300 K. Two distinct TSC peaks were observed in the spectra, deconvolution of which yielded three peaks. The results are analyzed by curve fitting, peak shape and initial rise methods. They all seem to be in good agreement with each other. The activation energies of three trapping centers in Ga₂SeS are found to be 72, 100 and 150 meV. The capture cross section of these traps are 6.7×10⁻²³, 1.8×10⁻²³ and 2.8×10⁻²² cm² with concentrations of 1.3×10¹², 5.4×10¹² and 4.2×10¹² cm⁻³, respectively.     

MgB2 fabrication by diffusion-controlled three layered (B-Mg-B) technique

MgB₂ was successfully fabricated through diffusion-controlled three-layered (B-Mg-B) technique under high pressure. Due to melting temperature of Mg, the material was pre-heat treated at 600 °C between 1 and 48 h. Optimum pre-heat treatment condition was found to be 600 °C for 48 h. Then, the compacted material was grinded and pelletized under pressure of 2 ton. The pellets were heat treated at 600-900 °C for 1-48 h. Optimum heat treatment condition was determined to be 800 °C for 1 h for formation of almost pure MgB₂. Diffusion coefficient was determined with Fick's law and EDX data. Diffusion coefficient value for B in Mg matrix and Mg in B matrix was determined to be 1.66×10⁻⁷ and 3.14×10⁻⁸ cm²/sn, respectively. Best T_c value (39.4 K) was obtained for material heat treated at 800 °C for 1 h. A symmetric hysteresis was obtained for the best MgB₂ material and magnetization decreased with increase in the temperature and the applied magnetic field.