50 MeV Li3+ ion irradiation effect on structural, electrical, and dielectric properties of PVA-based nanocomposite polymer electrolytes

Nanocomposite polymer electrolyte thin films of polyvinyl alcohol (PVA)-orthophosphoric acid (H₃PO₄)-Al₂O₃ have been prepared by solution cast technique. Films are irradiated with 50 MeV Li³⁺ ions having four different fluences viz. 5?×?10¹⁰, 1?×?10¹¹, 5?×?10¹¹, and 1?×?10¹² ions/cm². The effect of irradiation on polymeric samples has been studied and characterized. X-ray diffraction spectra reveal that percent degree of crystallinity of samples decrease with ion fluences. Glass transition and melting temperatures have been also decreased as observed in differential scanning calorimetry. A possible complexation/interaction has been shown by Fourier transform infrared spectroscopy. Temperature-dependent ionic conductivity shows an Arrhenius behavior before and after glass transition temperature. It is observed that ionic conductivity increases with ion fluences and after a critical fluence, it starts to decrease. Maximum ionic conductivity of ～2.3?×?10^?5 S/cm owing to minimum activation energy of ～0.012 eV has been observed for irradiated electrolyte sample at fluence of 5?×?10¹¹ ions/cm². The dielectric constant and dielectric loss also increase with ion fluences while they decrease with frequency. Transference number of ions shows that the samples are of purely ionic in nature before and after ion irradiation.     

Electrical and structural properties of the swift heavy ion irradiated Au/n-GaAs schottky barrier diodes

Abstract

Au/n-GaAs Schottky Barrier Diodes (SBDs) have been fabricated on LEC grown silicon doped (100) GaAs single crystals. The SBDs were irradiated using high energy (120 MeV) silicon ion with fluences of 1 × 10 ¹¹ and 1 × 10¹² ions/cm². Current-Voltage (I-V) characteristics of unirradiated and irradiated diodes were analyzed. The change in the reverse leakage current increases with increasing ion fluence. This is due to the irradiation induced defects at the interface and its increase with the fluence. The diodes were annealed at 573 and 673 K. to study the effect of annealing. The rectifying behavior of the irradiated (fluence of 1 × 10¹² ions/cm¹²) SBDs improves upon as the annealing temperature increases and is attributed to the in situ self-annealing during irradiation. Scanning Electron Microscopic analysis was carried out on the irradiated samples to delineate the projected range and to observe defects.     

Studies of some physical properties of PrFe0.7Ni0.3O3 thin films after 200 MeV Ag15+ irradiation

PrFe_0.7Ni_0.3O₃ thin films (thickness ~ 200 nm) were prepared by pulsed laser ablation technique on LaAlO₃ substrate. These films were irradiated with 200?MeV Ag¹⁵⁺ ions at various fluencies, ranging from 1 × 10¹¹ to 1 × 10¹² ions/cm². These irradiated thin films were characterized by using X-ray diffraction, dc conductivity, dc magnetization and atomic force microscopy. These films exhibit orthorhombic structure and retain it even after irradiations. The crystallite size (110–137?nm), micro strain (1.48 × 10^?2–1.75 × 10^?2 line^?2?m^?4) and dislocation density (79.7 × 10¹⁴–53.2 × 10¹⁴ line/m²) vary with ion fluencies. An enhancement in resistivity at certain fluence and then a decrease in its value (0.22175–0.21813?Ω?cm) are seen. A drastic change in observed magnetism after ion irradiation is seen. With ion irradiation, an increase in surface roughness, due to the formation of hillocks and other factors, is observed. Destruction of magnetic domains after irradiation can also be visualized with magnetic force microscopy and is in close agreement with magnetization data. The impact on various physical properties in these thin films after irradiation indicates a distortion in the lattice structure and consequently on single-particle band width caused by stress-induced defects.     

Swift heavy ion provoked structural, optical and electrical properties in SnO2 thin films

SnO₂ thin films grown on glass substrates at 300 ^°C by reactive thermal evaporation and annealed at 600 ^°C were irradiated by 120 MeV Ag⁹⁺ ions. Though irradiation is known to induce lattice disorder and suppression of crystallinity, we observe grain growth at a certain fluence of irradiation. X-ray diffraction (XRD) revealed the crystalline nature of the films. The particle size estimated by Scherrer’s formula for the irradiated films was in the range 10–25 nm. The crystallite size increases with increase in fluence up to 1×10¹² ions?cm^?2, whereas after that the size starts decreasing. Atomic force microscope (AFM) results showed the surface modification of nanostructures for films irradiated with fluences of 1×10¹¹ ions?cm^?2 to 1×10¹³ ions?cm^?2. The UV–visible spectrum showed the band gap of the irradiated films in the range of 3.56 eV–3.95 eV. The resistivity decreases with fluence up to 5×10¹² ions?cm^?2 and starts increasing after that. Rutherford Backscattering (RBS) reveals the composition of the films and sputtering of ions due to irradiation at higher fluence.     

Micro‐Raman investigation of nanosized zinc ferrite: effect of crystallite size and fluence of irradiation

Zinc ferrite nanoparticles of different sizes ranging from 12 to 62 nm were synthesized by using the nitrate route. These nanoparticles were irradiated by a 100 MeV oxygen beam at two fluences: 1 × 10¹³ and 5 × 10¹³ ions/cm². It was observed that modes corresponding to cubic spinel phase were retained after the irradiation in all the systems. The variation in the parameters of various modes follows phonon confinement, while this effect seems to violate in irradiated specimen. It was found that the irradiation‐induced changes in the modes F_2g(2) and F_2g(3) depend on whether the crystallite size of the pristine sample is less than, equal to or greater than the phonon confinement length, while this length is not dominant for the irradiation‐induced changes in the mode A_1g. The changes in various parameters of the modes are attributed to the combined effect of the restructuring of the chemical species and ion‐induced defects. Copyright © 2011 John Wiley & Sons, Ltd.     

DLTS and in situ C–V analysis of trap parameters in swift 50 MeV Li3+ ion-irradiated Ni/SiO2/Si MOS capacitors

Ni/SiO₂/Si MOS structures were fabricated on n-type Si wafers and were irradiated with 50 MeV Li³⁺ ions with fluences ranging from 1×10¹⁰ to 1×10¹² ions/cm². High frequency C–V characteristics are studied in situ to estimate the build-up of fixed and oxide charges. The nature of the charge build-up with ion fluence is analyzed. Defect levels in bulk Si and its properties such as activation energy, capture cross-section, trap concentration and carrier lifetimes are studied using deep-level transient spectroscopy. Electron traps with energies ranging from 0.069 to 0.523 eV are observed in Li ion-irradiated devices. The dependence of series resistance, substrate doping and accumulation capacitance on Li ion fluence are clearly explained. The study of dielectric properties (tan δ and quality factor) confirms the degradation of the oxide layer to a greater extent due to ion irradiation.     

A selective sensor for nanolevel detection of lead (II) in hazardous wastes using ionic-liquid/Schiff base/MWCNTs/nanosilica as a highly sensitive composite

An effective potentiometric sensor had been fabricated for the rapid determination of Pb²⁺ based on carbon paste electrode consisting of room temperature ionic liquid 1-butyl-3-methylimidazolium hexafluorophosphate (BMIM-PF₆), multiwalled carbon nanotubes (MWCNTs), nanosilica, synthesized Schiff base, as an ionophore, and graphite powder. The constructed nanocomposite electrode showed better sensitivity, selectivity, response time, response stability, and lifetime in comparison with typical Pb²⁺ carbon paste electrode for the successfully determination of Pb²⁺ ions in water and in waste water samples. The best response for nanocomposite electrode was obtained with electrode composition of 18% ionophore, 20% BMIM-PF₆, 49% graphite powder, 10% MWCNT, and 3% nanosilica. The new electrode exhibited a Nernstian response (29.76?±?0.10 mV decade^?1) toward Pb²⁺ ions in the range of 5?×?10^?9?C1.0?×?10^?1 mol L^?1 with a detection limit of 2.51?×?10^?9 mol L^?1. The potentiometric response of prepared sensor is independent of the pH of test solution in the pH range of 4.5?C8.0. It has quick response with response time of about 6 s. The proposed electrode show fairly good selectivity over some alkali, alkaline earth, transition, and heavy metal ions.     

Carbon (70 MeV) and copper (120 MeV) ions irradiation effects in Makrofol-N

Makrofol-N polycarbonate was irradiated with carbon (70 MeV) and copper (120 MeV) ions to analyze the induced effects with respect to optical and structural properties. In the present investigation, the fluence for carbon and copper beams was kept in the range of 1×10¹¹– 1×10¹³ ions/cm² to study the swift heavy ion induced modifications. UV–VIS, FTIR and XRD techniques were utilized to study the induced changes. The analysis of UV–VIS absorption studies revealed that the optical energy gap was reduced by 17% on carbon irradiation, whereas the copper beam leads to a decrease of 52% at the highest fluence of 1×10¹³ ions/cm². The band gap can be correlated to the number of carbon atoms, N, in a cluster with a modified Robertson's equation. In copper (120 MeV) ions irradiated polycarbonate, the number of carbon atoms in a cluster was increased from 63 to 269 with the increase of ion fluence from 0 to 1×10¹³ ions/cm², whereas N is raised only up to 91 when the same polymer films were irradiated with carbon (70 MeV) ions under similar conditions. FTIR analysis showed a decrease in almost all characteristic absorption bands under irradiation. The formation of hydroxyl (? OH) and alkene (C?C) groups were observed in Makrofol-N at higher fluence on irradiation with both types of ions, while the formation alkyne end (R? C≡ CH) group was observed only after copper ions irradiation. The radii of the alkyne production of about 3.3 nm were deduced for copper (120 MeV) ions. XRD measurements show a decrease in intensity of the main peak and an increase of the average intermolecular spacing with the increase of ion fluence, which may be attributed to the structural degradation of Makrofol-N on swift ion irradiation.     

Spectroscopic studies of copper and carbon ion irradiated polypropylene

The samples of polypropylene (PP) have been irradiated with 120 MeV ⁶⁴Cu⁹⁺ and 70 MeV ¹²C⁵⁺ ion beams, with the fluence ranging from 1 × 10¹³ to 1 × 10¹¹ ions/-cm⁻². UV-VIS and FTIR techniques have been used to study the chemical and optical properties of these irradiated polymers. UV spectra revealed that the optical-gap energy decreases by 54 % with copper ion irradiation at the fluence of 1 × 10¹³ ions/cm², whereas at the same fluence, carbon beam decreases the optical-gap energy by 20%. FTIR analysis of ion irradiated samples revealed the presence of -OH, C = O and C = C bonds. Alkyne formation has been observed only in the case of copper ion irradiation.      

Effect of swift heavy ion irradiation on dilute Fe-doped Sb0.95Se0.05 magnetic semiconductor

A thin film of dilute Fe (0.008)-doped Sb_0.95Se_0.05 alloy was grown on silicon substrate using the thermal evaporation technique. This film was irradiated with swift heavy ions (SHIs) Ag⁺¹⁵ having 200?MeV energy at ion fluences of 1?×?10¹² and 5?×?10¹² ions per cm², respectively. The thickness of the thin film was ～500?nm. We study the effect of irradiation on structural, electrical, surface morphology and magnetic properties of this film using grazing angle XRD (GAXRD), DC resistivity, atomic force microscopy (AFM) and magnetic force microscopy (MFM), respectively. GAXRD suggests that no significant change is observed in this system due to SHI irradiation. The average crystallite size increases with fluence, whereas the AFM image shows the rms roughness decreases due to irradiation with respect to the un-irradiated thin film. The MFM image shows that the magnetic interaction in irradiated film decreases due to the irradiation effect. Although the un-irradiated sample shows metal to semiconducting transition, but after irradiation with fluence of 5?×?10¹² ions per cm², the sharpness of the metal to semiconducting phase transition is observed to increase dramatically at ～300?K. This characteristic of the thin film makes it a promising candidate for an electrical switching device after irradiation.     

An investigation on the variations in properties of Ni+ irradiated ZnO thin films

ZnO thin films, irradiated by 80 MeV Ni⁺ ions, were analysed with the help of different characterization techniques like X-ray diffraction, optical absorption, transmission, photoluminescence (PL), electrical resistivity, photosensitivity (PS) and thermally stimulated current (TSC) measurements. Crystallinity and absorption edge were hardly affected by irradiation. PL spectrum of pristine sample showed a broad peak at 517 nm, whereas irradiated film had two emissions at 517 and 590 nm. Intensity ratio between these two emissions (I₅₁₇/I₅₉₀) decreased with the fluence, and finally at a fluence of 3×10¹³ ions/cm², the emission at 517 nm completely disappeared. Electrical resistivity of the sample irradiated with a fluence of 1×10¹³ ions/cm² drastically increased. However, on increasing the fluence to 3×10¹³ ions/cm², resistivity decreased, probably due the onset of hopping conduction through defects. PS also decreased due to irradiation. TSC measurements on pristine sample could reveal only one defect level at 0.6 eV, due to interstitia1 zinc (Zn_I). But, irradiation at a fluence of 1×10¹² ions/cm², resulted in three different defect levels as per TSC studies. Interestingly, the sample irradiated at a fluence of 3×10¹³ ions/cm² had only one defect level corresponding to a deep donor. The possible origin of these defect levels is also discussed in the paper.     

Study of optical band gap and carbon cluster sizes formed in 100 MeV Si8+ and 145 MeV Ne6+ ions irradiated polypropylene polymer

A wide variety of material modifications in polymers have been studied by using ion irradiation techniques. Extensive research has focused on to Swift Heavy Ions (MeV’s energy), probably because of good controllability and the large penetration length in polymers. High energy ion irradiation tends to damage polymers significantly by electronic excitation and ionization. It may result into the creation of latent tracks and can also cause formation of radicals such as ablation, sputtering, chain scission and intermolecular cross-linking, creation of triple bonds and unsaturated bonds and loss volatile fragments. Polypropylene polymer films of thickness 50 μm were irradiated to the fluences of 1 × 10¹⁰, 3 × 10¹⁰, 1 × 10¹¹, 3 × 10¹¹, 6 × 10¹¹ and 1 × 10¹² ions/cm² with Si⁸⁺ ions of 100 MeV energy from Pelletron accelerator at Inter University Accelerator Centre (IUAC), New Delhi and Ne⁶⁺ ions of 145 MeV to the fluences of 10⁸, 10¹⁰, 10¹¹, 10¹² and 10¹³ ions/cm³ from Variable Energy Cyclotron Centre, Kolkata. Optical modifications were characterized by UV towards the red end of the spectrum with the increase of the fluence. Value of optical band gap E _g shows a decreasing trend with ion fluence irradiated with both kinds of ions. Cluster size N, the number of carbon atoms per conjugation length increases with increasing ion dose. Cluster size also increases with the increase of electronic stopping power.      

Combined field ion microscopy and transmission electron microscopy of heavy ion damage in tungsten

Abstract

A field ion microscopy (FIM) and transmission electron microscopy (TEM) investigation of radiation damage in tungsten after heavy ion bombardment has been carried out. Field ion specimens of tungsten were irradiated with 180–230 keV Xe⁺ ions. The irradiation doses were varied between 4 × 10¹¹ and 4 × 10¹² ions/cm². The irradiated specimens were examined in FIM. Experiments combining both TEM and FIM were performed in order to compare the results obtainable by these two methods. The distribution of defects visible by TEM was inhomogeneous. The influence of the imaging field in FIM on the defects visible in TEM is discussed.     

Comparative study on low energy ion beam modification of thermoplastic polymers

ABSTRACT

Polycarbonate (PC) and polyethylene terephthalate (PET) thermoplastic polymer films were irradiated by low energy ion beams such as 100 keV Hydrogen (H⁺) ions and 350 keV Nitrogen (N⁺) ions at varied fluence from 1?×?10¹³ ions/cm² to 5?×?10¹⁴ ions/cm². The depth profile concentration of ions was calculated using Stopping and Range of Ions in Matter (SRIM) software code. Fourier Transform Infrared (FTIR) technique shows decrement in the intensity of peaks and disappearance of peaks mainly related to carbonyl stretching at 1770?cm^?1 and C–C stretching at 1500?cm^?1. Scanning electron microscopy (SEM) of irradiated polymers showed the formation of pores. X-ray diffraction (XRD) analysis has showed decrease in the intensity indicating the decrease in crystallinity after irradiation. Mechanical studies revealed that the molecular weight and microhardness decrease with increase in ion fluence due to increase in chain scission. The contact angle increased with increase in ion fluence indicating the hydrophobic nature of polymer after irradiation. Antibiofilm activity test of irradiated films shows resistance to Salmonella typhi (S. typhi) pathogen responsible for typhoid. The study shows that Nitrogen ion induces more damage compared to Hydrogen ions and PC films get more modified than PET films.     

Interplay of native defect-related photoluminescence response of ZnO nanosticks subjected to 80 keV Ar ion irradiation

We report on the effect of 80 keV Ar⁺ ion irradiation on the luminescence response of zinc oxide (ZnO) nanosticks synthesized using a simple microemulsion route. The formation of nanoscale rods was confirmed from the transmission electron microscopy, whereas the hexagonal wurtzite phase of the nanorods was detected in an X-ray diffraction pattern. The photoluminescence pattern of the nanorods was dominated by various native defect states of ZnO, which are responsible for the quenching of the typical band edge emission of ZnO. Under Ar⁺ ion irradiation at a fluence of 1×10¹³ ions/cm², the band edge emission was recovered owing to the suppression of oxygen vacancy defects. In addition, the formation of new zinc vacancy and ionized zinc interstitial defects were also evident. Conversely, the band edge emission was found to be quenched as a result of the creation of more oxygen vacancy (V_O) defects due to ion irradiation (fluence: 1×10¹⁵ ions/cm²). The nuclear energy loss of the Ar⁺ ions in ZnO is responsible for the formation of point (vacancy-related) defects, while relatively small amount of electronic energy loss of the Ar⁺ ion results in the ionization of the neutral zinc interstitial (Zn_i) defects. The energy deposition scheme of the energetic ions has been elaborated with the help of theoretical modeling that explains the observed features quite satisfactorily.     

Mössbauer study of ferromagnetic metallic glasses irradiated by swift heavy ions at temperatures 100 and 300 K

The effect of swift heavy ion irradiation on ferromagnetic metallic glasses Fe₄₀Ni₃₈Mo₄B₁₈ and Fe₇₈Si₉B₁₃ has been studied. The ion beams used are 100 MeV ¹²⁷I and 180 MeV ¹⁹⁷Au. The specimens were irradiated at fluences ranging from 3 × 10¹² to 1.5 × 10¹⁴ ions/cm². The irradiations have been carried out at temperatures 100 and 300 K. The magnetic moments are sensitive towards the irradiation conditions such as irradiation temperature and stopping power of incident ion beam. The irradiation-induced effects have been monitored, by using Mössbauer spectroscopy. The modifications in magnetic anisotropy and hyperfine magnetic field distributions, as an effect of different irradiation temperature as well as different stopping power have been discussed. After irradiation, all the samples remain amorphous and magnetic anisotropy considerably changes from its original in-plane direction. The results show enhancement in magnetic anisotropy in the specimen irradiated at 100 K, as compared to that of irradiated at 300 K. It is expected that at low temperature, the stresses produced in the material would remain un-annealed, compared to the samples irradiated at room temperature and therefore, the modification in magnetic anisotropy would be enhanced. A distribution of hyperfine magnetic field, of the samples irradiated at low temperature, show a small but distinct peak at ～?11 Tesla, indicating Fe-B pairing.     

Effect of 50 MeV Li+3 and 80 MeV C+5 ions’ beam irradiation on the optical,structural, chemical and surface topographic properties of PMMA films*

The self-standing films of polymethyl methacrylate (PMMA) were irradiated under vacuum with 50?MeV lithium (Li³⁺) and 80?MeV carbon (C⁵⁺) ions to the fluences of 3?×?10¹⁴, 1?×?10¹⁵, 1?×?10¹⁶ and 1?×?10¹⁷ ions µm^?2. The pristine and irradiated samples of PMMA films were studied by using ultraviolet–visible (UV–Vis) spectrophotometry, Fourier transform infrared, X-ray diffractrometer and atomic force microscopy. With increasing ion fluence of swift heavy ion (SHI), PMMA suffers degradation, UV–Vis spectra show a shift in the absorption band from the UV towards visible, attributing the formation of the modified system of bonds. E_g and E_a decrease with increasing ion fluence. The size of crystallite and crystallinity percentage decreases with increasing ion fluence. With SHI irradiation, the intensity of IR bands and characteristic bands of different functional groups are found to shift drastically. The change in (E_g) and (N) in carbon cluster is calculated. Shifting of the absorption band from the UV towards visible along with optical activity and as a result of irradiation, some defects are created in the polymer causing the formation of conjugated bonds and carbon clusters in the polymer, which in turn lead to the modification in optical properties that could be useful in the fabrication of optoelectronic devices, gas sensing, electromagnetic shielding and drug delivery.     

Simulation of high fluence fast neutron damage with heavy ion bombardment

316 stainless steel has been irradiated with 5 MeV Cu ions to a fluence of 2 × 10¹⁶ ions/cm² at 500°C. Transmission electron microscopy of this sample reveals that 6 × 10¹⁵ voids/cm² of average diameter equal to 180 Å were produced. A method for correlating the fluence of ions with equivalent neutron fluences is described. This method predicts that the Cu bombardment in this study should produce a microstructure similar to that found in steel irradiated with 2–5 × 11²² neutrons/cm². A comparison of the ion produced voids with those found after previous neutron irradiation experiments confirms this prediction.     

Effect of swift heavy ion irradiation on surface resistance of DyBa2Cu3O7-δ thin films at microwave frequencies

We report the observation of a propounced peak in surface resistance at microwave frequencies of 4.88 GHz and 9.55 GHz and its disappearance after irradiation with swift ions in laser ablated DyBa₂Cu₃O_7-δ (DBCO) thin films. The measurements were carried out in zero field as well as in the presence of magnetic fields (up to 0.8 T). The films were irradiated using 90 MeV oxygen ions at Nuclear Science Centre, New Delhi at a fluence of 3×10¹³ ions/cm². Introduction of point defects and extended defects after irradiation suppresses the peak at 9.55 GHz whereas no suppression is observed at 4.88 GHz. These results and the vortex dynamics in the films at microwave frequencies before and after irradiation are discussed.     

Kinetics of the radiation-induced hardening of EP-823 steel after Ni++ ion irradiation, annealing, and re-irradiation

The ferritic-martensitic steel 12Cr-MoWSiVNbB (EP-823) was irradiated with Ni⁺⁺ ions with the energy 7 MeV, and fluences of 2.7 × 10²⁰ and 3.9 × 10²⁰ ion/m² at 380 C. The irradiated samples were annealed at 600°C and then re-irradiated under the same conditions. After re-irradiation, the microhardness increased to the maximum value and achieved about 70% of the value corresponding to that after primary irradiation. After primary and secondary irradiation with increasing doses, the hardening reaches its saturation level at approximately similar damaging doses and behaves similar to that obtained in the case of the neutron irradiation of ferritic chromium steels.