Synthesis and characterization of GaN nanowires by ammoniating Ga2O3/Cr thin films deposited on Si(1 1 1) substrates

GaN nanowires have been successfully synthesized on Si(1 1 1) substrates by magnetron sputtering through ammoniating Ga₂O₃/Cr thin films at 950 °C. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), FT-IR spectrophotometer, scanning electron microscopy (SEM), high-resolution transmission electron microscopy (TEM), and photoluminescence (PL) spectrum were carried out to characterize the microstructure, morphology, and optical properties of GaN samples. The results demonstrate that the nanowires are single-crystal GaN with hexagonal wurtzite structure and high-quality crystalline, have the size of 30-80 nm in diameter and several tens of microns in length with good emission properties. The growth direction of GaN nanowires is perpendicular to the fringe of (1 0 1) plane. The growth mechanism of GaN nanowires is also discussed in detail.     

Synthesis and characterization of GaN nanowires

In this work, GaN nanowires were fabricated on Si substrates coated with NiCl₂ thin films using chemical vapor deposition (CVD) method by evaporating Ga₂O₃ powder at 1100 °C in ammonia gas flow. X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscope (HRTEM) and photoluminescence (PL) spectrum are used to characterize the samples. The results demonstrate that the nanowires are single-crystal GaN with hexagonal wurtzite structure. The growth mechanism of GaN nanowires is also discussed.     

GaN epilayers on nanopatterned GaN/Si(1 1 1) templates: Structural and optical characterization

Template-based nanoscale epitaxy has been explored to realize high-quality GaN on Si(1 1 1) substrates. We have employed polystyrene-based nanosphere lithography to form the nano-hole array patterns on GaN/Si(1 1 1) template and then, subsequent regrowth of GaN is carried out by metalorganic chemical vapor deposition (MOCVD). During the initial growth stage of GaN on such nanopatterned substrates, we have observed formation of nanoislands with hexagonal pyramid shape due to selective area epitaxy. With further epitaxial regrowth, these nanoislands coalesce and form continuous GaN film. The overgrown GaN on patterned and non-patterned regions is characterized by high-resolution X-ray diffraction (HRXRD) and high-spatial resolution optical spectroscopic methods. Micro-photoluminescence (PL), micro-Raman scattering and scanning electron microscopy (SEM) have been used to assess the microstructural and optical properties of GaN. Combined PL and Raman data analyses show improved optical quality when compared to GaN simultaneously grown on non-patterned bulk Si(1 1 1). Such thicker GaN templates would be useful to achieve III-nitride-based opto- and electronic devices integrated on Si substrates.     

Formation mechanisms of GaN nanorods grown on Si(1 1 1) substrates

Scanning electron microscopy (SEM) images, transmission electron microscopy (TEM) images, and selected-area electron diffraction (SAED) patterns showed that vertically well aligned GaN nanorods with c-axis-oriented crystalline wurzite structures were grown on Si(1 1 1) substrates by using hydride vapor phase epitaxy. The high-resolution TEM (HRTEM) images showed that the crystallized GaN nanorods contained very few defects and that they were consisted of , {0 0 0 1}, and { } facets. The formation mechanisms for the GaN nanorods grown on Si(1 1 1) substrates are described on the basis of the SEM, TEM, SAED pattern, and HRTEM results.     

Synthesis of In-doped Ga2O3 zigzag-shaped nanowires and optical properties

In-doped Ga₂O₃ zigzag-shaped nanowires and undoped Ga₂O₃ nanowires have been synthesized on Si substrate by thermal evaporation of mixed powders of Ga, In₂O₃ and graphite at 1000 °C without using any catalyst via a vapor-solid growth mechanism. The morphologies and microstructures of the products were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence spectroscopy (PL). The nanowires range from 100 nm to several hundreds of nanometers in diameter and several tens of micrometers in length. A broad emission band from 400 to 700 nm is obtained in the PL spectrum of these nanowires at room temperature. There are two blue-emission peaks centering at 450 and 500 nm, which originate from the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.     

Growth of highly-oriented CaCu3Ti4O12 thin films on SrTiO3 (1 0 0) substrates by a chemical solution route

Highly-oriented CaCu₃Ti₄O₁₂ (CCTO) thin films deposited directly on SrTiO₃ (1 0 0) substrates have been developed successfully using a chemical solution coating method. X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM) were employed to characterize the structure and the morphology. It was observed that the CCTO thin films had the 1 μm × 1 μm domain-like microstructure that consists of compact grains of about 0.1 μm in size. The cross sectional SEM image shows that the CCTO grains grow regularly close to the clear interface between the CCTO film and the SrTiO₃ substrate. The result was discussed in terms of lattice mismatch between CCTO and SrTiO₃.     

Epitaxial growth of Nd2Hf2O7(1 1 1) thin films on Ge(1 1 1) substrates by pulsed laser deposition

Nd₂Hf₂O₇ (NHO) thin films have been epitaxially grown by pulsed laser deposition (PLD) on Ge(1 1 1) substrates. In situ reflection high-energy electron diffraction (RHEED) evolution of the (1 1 1)-oriented NHO during the deposition has been investigated and shows that the epilayer has a twin-free character with type-B stacking. Interfacial structure of NHO/Ge has been examined by high-resolution transmission electron microscopy (HRTEM). The results indicate a highly crystalline film with a very thin interface, and the orientation relationship between NHO and Ge can be denoted as (1 1 1)_NHO//(1 1 1)_Ge and . Finally, twin-free epitaxial growth of NHO with type-B orientation displays temperature dependence and the type-B epitaxy is favored at high temperature.     

Characterizations of n-type ferromagnetic GaMnN thin film grown on GaN/Al2O3 (0 0 0 1) by metal-organic chemical vapor deposition

A high-quality ferromagnetic GaMnN (Mn=2.8 at%) film was deposited onto a GaN buffer/Al₂O₃(0 0 0 1) at 885 °C using the metal-organic chemical vapor deposition (MOCVD) process. The GaMnN film shows a highly c-axis-oriented hexagonal wurtzite structure, implying that Mn doping into GaN does not influence the crystallinity of the film. No Mn-related secondary phases were found in the GaMnN film by means of a high-flux X-ray diffraction analysis. The composition profiles of Ga, Mn, and N maintain nearly constant levels in depth profiles of the GaMnN film. The binding energy peak of the Mn 2p_3/2 orbital was observed at 642.3 eV corresponding to the Mn (III) oxidation state of MnN. The presence of metallic Mn clusters (binding energy: 640.9 eV) in the GaMnN film was excluded. A broad yellow emission around 2.2 eV as well as a relatively weak near-band-edge emission at 3.39 eV was observed in a Mn-doped GaN film, while the undoped GaN film only shows a near-band-edge emission at 3.37 eV. The Mn-doped GaN film showed n-type semiconducting characteristics; the electron carrier concentration was 1.2×10²¹/cm³ and the resistivity was 3.9×10⁻³ Ω cm. Ferromagnetic hysteresis loops were observed at 300 K with a magnetic field parallel and perpendicular to the ab plane. The zero-field-cooled and field-cooled curves at temperatures ranging from 10 to 350 K strongly indicate that the GaMnN film is ferromagnetic at least up to 350 K. A coercive field of 250 Oe and effective magnetic moment of 0.0003 μ_B/Mn were obtained. The n-type semiconducting behavior plays a role in inducing ferromagnetism in the GaMnN film, and the observed ferromagnetism is appropriately explained by a double exchange mechanism.     

Epitaxial growth of Au and Pt on Fe3O4(1 1 1) surface

We have studied the epitaxial growth of Au and Pt layers on Fe₃O₄(1 1 1) as a function of the deposition temperature and thickness. The layers were deposited by UHV sputtering and the structural properties were investigated by reflection high energy electron diffraction (RHEED), X-ray experiments and transmission electron microscopy (TEM). The epitaxial growth of both metals was obtained whatever the deposition conditions but the wetting is however different for the two metals. Comparison between the coverage ratios of Au and Pt is correlated with their surface and interfaces energies. The optimum conditions to achieve a 2D flat epitaxial metallic layer are determined.     

GaN/LiNbO3 (0 0 0 1) interface formation calculated from first-principles

The stable adsorption sites for both Ga and N ions on the ideal and on the reconstructed LiNbO₃ (0 0 0 1) surface are determined by means of first-principle total energy calculations. A single N layer is found to be more strongly bound to the substrate than a single Ga layer. The adsorption of a GaN monolayer on the polar substrate within different orientations is then modeled. On the basis of our results, we propose a microscopic model for the GaN/LiNbO₃ interface. The GaN and LiNbO₃ (0 0 0 1) planes are parallel, but rotated by 30° each other, with in-plane epitaxial relationship [1 0 0]_GaN‖ [1 1  0]_LiNbO3. In this way the (0 0 0 1) plane lattice mismatch between GaN and LiNbO₃ is minimal and equal to 6.9% of the GaN lattice constant. The adsorbed GaN and the underlying LiNbO₃ substrate have parallel c-axes.     

Synthesis of GaN nanowires by Tb catalysis

Rare earth metal seed Tb was employed as catalyst for the growth of GaN wires. GaN nanowires were synthesized successfully through ammoniating Ga₂O₃/Tb films sputtered on Si(1 1 1) substrates. The samples characterization by X-ray diffraction and Fourier transform infrared indicated that the nanowires are constituted of hexagonal wurtzite GaN. Scanning electron microscopy, transmission electron microscopy, and high-resolution transmission electron microscopy showed that the samples are single-crystal GaN nanowire structures. The growth mechanism of the GaN nanowires is discussed.     

Structural and magnetic properties of evaporated Fe thin films on Si(1 1 1), Si(1 0 0) and glass substrates

We present experimental results on the structural and magnetic properties of series of Fe thin films evaporated onto Si(1 1 1), Si(1 0 0) and glass substrates. The Fe thickness, t, ranges from 6 to110 nm. X-ray diffraction (XRD) and atomic force microscopy (AFM) have been used to study the structure and surface morphology of these films. The magnetic properties were investigated by means of the Brillouin light scattering (BLS) and magnetic force microscopy (MFM) techniques. The Fe films grow with (1 1 0) texture; as t increases, this (1 1 0) texture becomes weaker for Fe/Si, while for Fe/glass, the texture changes from (1 1 0) to (2 1 1). Grains are larger in Fe/Si than in Fe/glass. The effective magnetization, 4πM_eff, inferred from BLS was found to be lower than the 4πM_S bulk value. Stress induced anisotropy might be in part responsible for this difference. MFM images reveal stripe domain structure for the 110 nm thick Fe/Si(1 0 0) only.     

Structure, dielectric and ferroelectric properties of highly (1 0 0)-oriented BaTiO3 grown under low-temperature conditions

The highly (1 0 0)-oriented BaTiO₃ thin films were fabricated on LaNiO₃(1 0 0)/Pt/Ti/SiO₂/Si substrates under low-temperature conditions. Substrate temperatures throughout the fabrication process remained at or below 400 °C, which allows this process to be compatible with many materials commonly used in integrated circuit manufacturing. X-ray diffraction data provided the evidence for single BaTiO₃ phase. Field-emission scanning electron microscopy was used to study the columnar structure of the films. The dielectric properties as a function of frequency in the range of 1 kHz to 1 MHz was obtained. The room temperature remanent polarization (2P_r) and coercive field were found to be ∼5 μC/cm² and 50 kV/cm, respectively. The BTO film maintains an excellent fatigue-free character even after 10⁹ switching cycles.     

Formation of aligned silicon-nanowire on silicon in aqueous HF/(AgNO3 + Na2S2O8) solution

Highly oriented silicon nanowire (SiNW) layer was fabricated by etching Si substrate in HF/(AgNO₃ + Na₂S₂O₈) solution at 50 °C. The morphology and the photoluminescence (PL) of the etched layer as a function of Na₂S₂O₈ concentration were studied. The SiNW layers formed on silicon were investigated by scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX). It was demonstrated that the morphology of the etched layers depends on the Na₂S₂O₈ concentration. Room-temperature photoluminescence (PL) from etched layer was observed. It was found that the utilisation of Na₂S₂O₈ decreases PL peak intensity. Finally, a discussion on the formation process of the silicon nanowires is presented.     

Growth process of β-FeSi2 epitaxial film on Si(1 1 1) by molecular beam epitaxy

We have reported a one step growth of a high quality β-FeSi₂ epitaxial film on hydrogen terminated Si(1 1 1) by using molecular beam epitaxy (MBE) without template layer or post-growth annealing. In the present work, the growth process was studied by analyzing X-ray diffraction (XRD) spectra, reflective high energy electron diffraction (RHEED) and atomic force microscopy (AFM) observations on the samples grown with different growth times from 10 s to 1 h. A phase transformation from γ-FeSi₂ to β-FeSi₂ was confirmed existing in the crystal film growth, as well as the growth mode changing from three-dimensional (3D) to two-dimensional (2D) mode.     

Si epitaxial growth on LaAlO3(0 0 1)

We report on the growth of Si on c(2 × 2) reconstructed LaAlO₃(0 0 1) surfaces at high substrate temperature (700 °C) by molecular beam epitaxy. An initial Volmer-Weber mode is evidenced using reflection high energy electron diffraction (RHEED), X-ray photoelectron diffraction (XPD) and atomic force microscopy. After the deposition of a few monolayers, the islands coalesce. Using X-ray photoelectron spectroscopy, we demonstrate that Si islands exhibit an abrupt interface with the LaAlO₃ substrate without formation of silicate or silica. Finally, combined RHEED and XPD measurements show the epitaxial growth of Si with a unique Si(0 0 1)//LaAlO₃(0 0 1) and Si<1 0 0>//LAO<1 1 0> relationship.     

Local environment of nitrogen in GaNyAs1−y epilayers on GaAs (0 0 1) studied using X-ray absorption near edge spectroscopy

X-ray absorption near-edge spectroscopy (XANES) is used to study the N environment in bulk GaN and in GaN_yAs_1−y epilayers on GaAs (0 0 1), for y∼5%. Density-functional optimized structures were used to predict XANES via multiple-scattering theory. We obtain striking agreement for pure GaN. An alloy model with nitrogen pairs on Ga accurately predicts the threshold energy, the width of the XANES ‘white line’, and features above threshold, for the given X-ray polarization. The presence of large quantitities of N-pairs may point to a role for molecular N₂ in epitaxial growth kinetics.     

GaN nucleation on (0 0 0 1)-sapphire via ion-induced nitridation of gallium

The growth of epitaxial GaN films on (0 0 0 1)-sapphire has been investigated using X-ray photoelectron spectroscopy (XPS) and low energy electron diffraction (LEED). In order to investigate the mechanism of the growth in detail, we have focused on the nitridation of pre-deposited Ga layers (droplets) using ion beam-assisted molecular beam epitaxy (IBA-MBE). Comparative analysis of XPS core-level spectra and LEED patterns reveals, that nitride films nucleate as epitaxial GaN islands. The wetting of the surface by GaN proceeds via reactive spreading of metallic Ga, supplied from the droplets. The discussed growth model confirms, that excess of metallic Ga is beneficial for GaN nucleation.     

Synthesis and photoluminescence of single-crystal GaN nanorods prepared by sol-gel method

A new method was applied to prepare GaN nanorods. In this method, gallium oxide (Ga₂O₃) gel was firstly formed by a sol-gel processing using gallium ethanol, Ga(OC₂H₅)₃, as a new precursor. GaN nanorods were successfully synthesized after annealing of the Ga₂O₃ gel at 1000 °C for 20 min in flowing ammonia. The as-prepared nanorods were confirmed as single crystalline GaN with wurtzite structure by X-ray diffraction (XRD), selected-area electron diffraction (SAED) and high-resolution transmission electron microscopy (HRTEM). Transmission electron microscopy (TEM) displayed that the GaN nanorods were straight and smooth, with diameters ranging from 200 nm to 1.8 μm and lengths typically up to several tens of microns. When excited by 280 nm light at room temperature, the GaN nanorods had a strong ultraviolet luminescence peak located at 369 nm and a blue luminescence peak located at 462 nm, attributed to GaN band-edge emission and the existence of the defects or surface states, respectively.     

Structural and optical properties of an InxGa1−xN/GaN nanostructure

The structural and optical properties of an In_xGa_1−xN/GaN multi-quantum well (MQW) were investigated by using X-ray diffraction (XRD), atomic force microscopy (AFM), spectroscopic ellipsometry (SE) and photoluminescence (PL). The MQW structure was grown on c-plane (0 0 0 1)-faced sapphire substrates in a low pressure metalorganic chemical vapor deposition (MOCVD) reactor. The room temperature photoluminescence spectrum exhibited a blue emission at 2.84 eV and a much weaker and broader yellow emission band with a maximum at about 2.30 eV. In addition, the optical gaps and the In concentration of the structure were estimated by direct interpretation of the pseudo-dielectric function spectrum. It was found that the crystal quality of the InGaN epilayer is strongly related with the Si doped GaN layer grown at a high temperature of 1090 °C. The experimental results show that the growth MQW on the high-temperature (HT) GaN buffer layer on the GaN nucleation layer (NL) can be designated as a method that provides a high performance InGaN blue light-emitting diode (LED) structure.