Effect of partial Nd-substitution on the magnetic and magnetocaloric properties in spin-reorientation PrCo<Subscript>4</Subscript>Al alloy

Partial Nd-substitution effects on the magnetic and magnetocaloric properties in spin-reorientation Pr_1−x Nd _x Co₄Al (x = 0, 0.2, 0.4, 0.6, 0.8) alloys are investigated. All these alloys undergo two successive spin-reorientation transitions. Accordingly, the successive positive and negative magnetic entropy changes (Δ S _M ) for all these alloys are obtained. With the increase of Nd content, the spin reorientation transition temperatures increase from about 170 and 186 K for x = 0 to room temperature (276 and 294 K) for x = 0.8, covering a wide temperature interval. More interestingly, the values of positive Δ S _M values increase gradually from 0.1 to 0.9 J/kg K⁻¹, while the negative Δ S _M decrease from 1.3 to 0.2 J/kg K⁻¹ in the field change of 10 kOe. In addition, the series has an appreciable relative cooling power, which is therefore suitable to be used in a magnetic refrigerator.     

Quantum oscillations of the resistivity and hall coefficient and the quantum limit in Bi<Subscript>0.93</Subscript>Sb<Subscript>0.07</Subscript> alloys in a magnetic field along the trigonal axis

The dependences of the electrical resistivity ρ and the Hall coefficient R on the magnetic field have been measured for single-crystal samples of the n-Bi_0.93Sb_0.07 semiconductor alloys with electron concentrations in the range 1 × 10¹⁶ cm⁻³ < n < 2 × 10¹⁸ cm⁻³. It has been found that the measured dependences exhibit Shubnikov-de Haas quantum oscillations. The magnetic fields corresponding to the maxima of the quantum oscillations of the electrical resistivity are in good agreement with the calculated values of the magnetic fields in which the Landau quantum level with the number N intersects the Fermi level. The quantum oscillations of the Hall coefficient with small numbers are characterized by a significant spin splitting. In a magnetic field directed along the trigonal axis, the quantum oscillations of the resistivity ρ and the Hall coefficient R are associated with electrons of the three-valley semiconductor and are in phase with the magnetic field. In the case of a magnetic field directed parallel to the binary axis, the quantum oscillations associated both with electrons of the secondary ellipsoids in weaker magnetic fields and with electrons of the main ellipsoid in strong magnetic fields (after the overflow of electrons from the secondary ellipsoids to the main ellipsoid) are also in phase. In magnetic fields of the quantum limit ħω _c /2 ≥ E _F, the electrical conductivity increases with an increase in the magnetic field: σ₂₂(H) ∼ H ^k . A theoretical evaluation of the exponent in this expression for a nonparabolic semiconductor leads to values of k close to the experimental values in the range 4 ≤ k ≤ 4.6, which were obtained for samples of the semiconductor alloys with different electron concentrations. A further increase in the magnetic field results in a decrease of the exponent k and in the transition to the inequality σ₂₂(H) ≤ σ₂₁(H).     

Anomalies of the specific heat near the quantum critical point in Tm<Subscript>0.74</Subscript>Yb<Subscript>0.26</Subscript>B<Subscript>12</Subscript>

The behavior of the specific heat near the quantum critical point x ∼ 0.3 in the Tm_{1 − x} Yb _x B₁₂ system has been studied. Detailed measurements have been performed on high-quality single-crystalline Tm_0.74Yb_0.26B₁₂ samples within a wide temperature range of 1.9–300 K in a magnetic field up to 9 T. The temperature dependence of the magnetic contribution to the specific heat has a logarithmic divergence of the form C/T ∼ lnT at T < 4 K, which can be attributed to the quantum critical behavior regime suppressed by the external magnetic field. The Schottky anomaly of the magnetic contribution to the specific heat in Tm_0.74Yb_0.26B₁₂ has been analyzed.     

Magnetotransport properties of La<Subscript>0.67</Subscript>Ca<Subscript>0.33</Subscript>MnO<Subscript>3</Subscript> with different grain sizes

The magnetotransport and magnetoresistive (MR) properties of manganese-based La_0.67Ca_0.33MnO₃ perovskite with different grain sizes are reported. The electrical resistivity was measured as a function of temperature in magnetic fields of 0.5 and 1 T. The insulator–metal transition temperature, T _IM, shifted to a higher temperature with the application of the magnetic field. In zero field, T _IM is almost constant (∼271 K) for all samples except for the sample with the largest grain size, where T _IM=265 K. The temperature dependence of resistivity was fitted with several equations in the metallic (ferromagnetic) region and the insulating (paramagnetic) region. The density of states at the Fermi level, N(E _F), and the activation energy of electron hopping were estimated by fitting the resistivity versus temperature curves. The ρ–T ² curves are nearly linear in the metallic regime, but the ρ–T ^2.5 curves exhibit a deviation from linearity. The variable range hopping model and small polaron hopping model fit the data well in the high-temperature region, indicating the existence of the Jahn–Teller distortion that localizes the charge carriers. MR was found to increase with an increase in the magnetic field, an effect which is attributed to the intergrain spin tunneling effect.     

Anisotropy of amorphous nanogranular composites CoNbTa-SiO<Subscript><Emphasis Type="Italic">n</Emphasis></Subscript> and CoFeB-SiO<Subscript><Emphasis Type="Italic">n</Emphasis></Subscript>

A comparative investigation of the magnetic properties of amorphous nanogranular composites (Co₄₁Fe₃₉B₂₀) _x (SiO _n )_{100 − x} and (Co₈₆Nb₁₂Ta₂) _x (SiO _n )_{100 − x} has been performed in the subpercolation region at temperatures in the range 4.2–300 K. The thermomagnetic dependences in the range 4.2–300 K and the processes of magnetization reversal and remanent magnetization relaxation at liquid-helium temperatures have been studied. It has been established that the average anisotropy constants of amorphous nanograins are equal to 3.6–7.0 kJ/m³ for the (Co₄₁Fe₃₉B₂₀) _x (SiO _n )_{100 − x} composites and 5–8 kJ/m³ for the (Co₈₆Nb₁₂Ta₂) _x (SiO _n )_{100 − x} composites. The fundamental differences in the concentration dependences of the anisotropy constant K _eff and the coercive force H _C have been revealed for the two systems under investigation. It has been demonstrated that, as the concentration of the metal phase increases, the quantities K _eff and H _C increase for the (Co₈₆Nb₁₂Ta₂) _x (SiO _n )_{100 − x} composites and decrease for the (Co₄₁Fe₃₉B₂₀) _x (SiO _n )_{100 − x} composites.     

Magnetic properties of nonstoichiometric Ni<Subscript>2</Subscript>MnIn Heusler alloys

Results from studies of the crystal structure, resistivity, susceptibility, and magnetization of nonstoichiometric Ni₅₀Mn_{50 − x} In _x Heusler alloys are presented. Anomalous effects discovered in temperature dependences can be interpreted as the influence of the frustrated magnetic state exhibited by manganese moments in the martensitic phase. A field-induced phase transition to the austenitic phase was observed for several concentrations around room temperature.     

Universal behavior of CePd<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Rh<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript> ferromagnet at the quantum critical point

The heavy-fermion metal CePd_1−x Rh _x can be tuned from ferromagnetism at x = 0 to the nonmagnetic state at some critical concentration x _c . The non-Fermi liquid behavior (NFL) at x ≃ x _c is recognized by the power-law dependence of the specific heat C(T) given by the electronic contribution susceptibility X(T) and volume expansion coefficient α(T) at low temperatures: C/T ∝ X(T) ∝ α(T)/T∝ 1/ √T. We also demonstrate that the behavior of the normalized effective mass M _N ^* observed in CePd_1−x Rh _x at x ≃ 0.8 agrees with that of M _N ^* observed in paramagnetic CeRu₂Si₂ and conclude that these alloys exhibit the universal NFL thermodynamic behavior at their quantum critical points. We show that the NFL behavior of CePd_1−x Rh _x can be accounted for within the frameworks of the quasiparticle picture and fermion condensation quantum phase transition, while this alloy exhibits a universal thermodynamic NFL behavior that is independent of the characteristic features of the given alloy such as its lattice structure, magnetic ground state, dimension, etc. The text was submitted by the authors in English.     

Spin-dependent electron dynamics and recombination in GaAs<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>N<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript> alloys at room temperature

Conduction-electron spin polarization dynamics achieved by pulsed optical pumping at room temperature in GaAs_1−x N _x alloys with a small nitrogen content (x = 2.1, 2.7, and 3.4%) is studied both experimentally and theoretically. It is found that the photoluminescence circular polarization determined by the mean spin of free electrons reaches 40–45% and this giant value persists within 2 ns. Simultaneously, the total free-electron spin decays rapidly with the characteristic time ≈ 150 ps. The results are explained by spin-dependent capture of free conduction electrons on deep paramagnetic centers resulting in the dynamical polarization of bound electrons. A nonlinear theory of spin dynamics in the coupled system of spin-polarized free and localized carriers has been developed which describes the experimental dependencies, in particular, the electron spin quantum beats observed in a transverse magnetic field. The text was submitted by the authors in English.     

Magnetic state of the structural separated anion-deficient La<Subscript>0.70</Subscript>Sr<Subscript>0.30</Subscript>MnO<Subscript>2.85</Subscript> manganite

The results of neutron diffraction studies of the La_0.70Sr_0.30MnO_2.85 compound and its behavior in an external magnetic field are stated. It is established that in the 4–300 K temperature range, two structural perovskite phases coexist in the sample, which differ in symmetry (groups R[`3]cR\bar 3c and I4/mcm). The reason for the phase separation is the clustering of oxygen vacancies. The temperature (4–300 K) and field (0–140 kOe) dependences of the specific magnetic moment are measured. It is found that in zero external field, the magnetic state of La_0.70Sr_0.30MnO_2.85 is a cluster spin glass, which is the result of frustration of Mn³⁺-O-Mn³⁺ exchange interactions. An increase in external magnetic field up to 10 kOe leads to fragmentation of ferromagnetic clusters and then to an increase in the degree of polarization of local spins of manganese and the emergence of long-range ferromagnetic order. With increasing magnetic field up to 140 kOe, the magnetic ordering temperature reaches 160 K. The causes of the structural and magnetic phase separation of this composition and formation mechanism of its spin-glass magnetic state are analyzed.     

Polarization modes in the Ba<Subscript>2</Subscript>Mg<Subscript>2</Subscript>Fe1<Subscript>2</Subscript>O<Subscript>22</Subscript> multiferroic

The spectra of complex permittivity of a Ba₂Mg₂Fe₁₂O₂₂ single crystal belonging to the family of Y-type hexaferrites have been measured over a wide temperature range (10–300 K) with the aim of determining the dynamic parameters of the phonon and magnetic subsystems in the terahertz and infrared frequency ranges (3–4500 cm⁻¹). A factor-group analysis of the vibrational modes has been performed, and the results obtained have been compared with the experimentally observed resonances. The oscillator parameters of all nineteen phonon modes of E _u symmetry, which are allowed by the symmetry of the Ba₂Mg₂Fe₁₂O₂₂ crystal lattice, have been calculated. It has been found that, at temperatures below 195 and 50 K, the spectral response exhibits new absorption lines due to magnetic excitations.     

Photoluminescence of nanoparticles of (Ga<Subscript>2</Subscript>S<Subscript>3</Subscript>)<Subscript>0.95</Subscript>(Eu<Subscript>2</Subscript>O<Subscript>3</Subscript>)<Subscript>0.05</Subscript> solid solution

We have ground bulk samples to obtain nanoparticles of (Ga₂S₃)_1–x (Eu₂O₃) _x solid solutions, the sizes of which were determined using an atomic force microscope. The photoluminescence spectra of the nanoparticles were studied in the temperature interval 77–300 K. We have established the mechanisms for emission and transfer of energy from the matrix to the rare-earth ion, and we determined the Stokes shift (ΔS = 0.7 eV), the Huang–Rhys parameter (S = 16), and the optical phonon energy (ħ−ω = 23 meV).     

Dielectric and polar order behaviors of BaTiO<Subscript>3</Subscript>-Bi(Mg<Subscript>1/2</Subscript>Ti<Subscript>1/2</Subscript>)O<Subscript>3</Subscript> ceramics

New perovskite solid solution ceramics of (1−x)BaTiO₃-xBi(Mg_1/2Ti_1/2)O₃ ((1−x)BT-xBMT, x≤0.09) were synthesized by the solid-state reaction technique. X-ray diffraction studies have revealed a stable single perovskite structure for all samples. Dielectric measurements were carried out at different frequencies and temperatures. The polarization evolutions with temperatures were measured to investigate the ferroelectric properties. All the compositions show features of ferroelectrics with diffuse phase transition, though the temperature T _m of their dielectric constant maximum ε _m is frequency dependent. The dielectric constant peak ε(T) of (1−x)BT-xBMT ceramics become broad with increasing BMT content. During the temperature range of ε(T) peak summit, (1−x)BT-xBMT ceramics present quasi-linear dielectric phenomenon under high electric field with very high dielectric constant.     

Manganese-doped ZnSiAs<Subscript>2</Subscript> chalcopyrite: A new advanced material for spintronics

A new spintronics material with the Curie temperature above room temperature, the ZnSiAs₂ chalcopyrite doped with 1 and 2 wt % Mn, is synthesized. The magnetization, electrical resistivity, magnetoresistance, and the Hall effect of these compositions are studied. The temperature dependence of the electrical resistivity follows a semiconducting pattern with an activation energy of 0.12–0.38 eV (in the temperature range 124 K ≤ T ≤ 263 K for both compositions). The hole mobility and concentration are 1.33, 2.13 cm²/V s and 2.2 × 10¹⁶, 8 × 10¹⁶ cm⁻³ at T = 293 K for the 1 and 2 wt % Mn compositions, respectively. The magnetoresistance of both compositions, including the region of the Curie point, does not exceed 0.4%. The temperature dependence of the magnetization M(T) of both compositions exhibits a complicated character; indeed, for T ≤ 15 K, it is characteristic of superparamagnets, while for T > 15 K, spontaneous magnetization appears which correspond to a decreased magnetic moment per formula unit as compared to that which would be observed upon complete ferromagnetic ordering of Mn²⁺ spins or antiferromagnetic ordering of spins of the Mn²⁺ and Mn³⁺ ions. Thus, for T > 15 K, it is a frustrated ferro- or ferrimagnet. It is found that, unlike the conventional superparamagnets, the cluster moment μ _c in these compositions depends on the magnetic field: ∼12000–20000μ_B for H = 0.1 kOe, ∼52–55μ_B for H = 11 kOe, and ∼8.6–11.0μ_B at H = 50 kOe for the compositions with 1 and 2 wt % Mn, respectively. The specific features of the magnetic properties are explained by the competition between the carrier-mediated exchange and superexchange interactions.     

Electrical and electrochemical behaviour of several LiFe<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Co<Subscript>1 − <Emphasis Type="Italic">x</Emphasis></Subscript>PO<Subscript>4</Subscript> solid solutions as cathode materials for lithium ion batteries

Several olivine phosphates were investigated in the last years as cathode materials for secondary lithium ion batteries. Among these compounds, LiFe _x Co_1 − x PO₄ solid solutions might be interesting candidates because they should combine the high potential value of Co³⁺/Co²⁺ (higher than 4.5 V vs Li⁺/Li) with the relatively high charge–discharge rate of LiFePO₄. Solid solutions were prepared by solid-state route and characterised by X-ray powder diffraction, cyclic voltammetry, impedance spectroscopy and the Hebb–Wagner method. The results show that also low amount of iron induces high electronic conductivity in the solid solutions.     

Optical properties of the ternary compound Cd<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Hg<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Se:Co

We present the results of experimental studies of the optical properties of cobalt-doped Cd _x H_1−x Se (x = 0.18) single crystals with cobalt ion concentrations of NCo = 5·10¹⁸, 5·10¹⁹, and 1·10²⁰ cm⁻³ at T = 90 K and 300 K. The composition (x = 0.18) of the Cd _x Hg_1−x Se solid solution was selected so that the hypothetical resonance level is found on the bottom of the conduction band. We show that the cobalt ions in the mercury selenide can form a resonance donor level only for cobalt concentrations N_Co < 5·10¹⁸ cm⁻³. For N_Co ∼ 5·10¹⁸ cm⁻³, the cobalt ions substitute for mercury atoms, forming a solid solution and leading to an increase in the bandgap width and a change in the physical properties. The solubility of cobalt in the HgSe lattice can be greater than 5%–10%. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 74, No. 1, pp. 73–77, January–February, 2007.     

Electrical characterization of the [N(CH<Subscript>3</Subscript>)<Subscript>4</Subscript>][N(C<Subscript>2</Subscript>H<Subscript>5</Subscript>)<Subscript>4</Subscript>]ZnCl<Subscript>4</Subscript> compound

The [N(CH₃)₄][N(C₂H₅)₄]ZnCl₄ compound has been synthesized by a solution-based chemical method. The X-ray diffraction study at room temperature revealed an orthorhombic system with P2₁2₁2 space group. The complex impedance has been investigated in the temperature and frequency ranges 420–520 K and 200 Hz–5 MHz, respectively. The grain interior and grain boundary contribution to the electrical response in the material have been identified. Dielectric data were analyzed using the complex electrical modulus M ^* for the sample at various temperature. The modulus plots can be characterized by full width at half height or in terms of a non-exponential decay function ϕ(t) = exp[(−t/τ) ^β ]. The detailed conductivity study indicated that the electrical conduction in the material is a thermally activated process. The variation of the AC conductivity with frequency at different temperatures obeys the Almond and West universal law.     

Nonlinear properties and paramagnet-to-ferromagnet transition in Nd<Subscript>0.7</Subscript>Ba<Subscript>0.3</Subscript>MnO<Subscript>3</Subscript> single crystal with metallic ground state

We present the results from studying the magnetic properties (linear and nonlinear susceptibilities and the depolarization of polarized neutrons) of Nd_{1 − x} Ba _x MnO₃ manganite, x = 0.3, with Curie temperature T _C ≈ 140 K and dielectric-to-metal transition temperature T _DM ≈ 129 K. Its critical behavior corresponds to that of an isotropic 3-D ferromagnet at temperatures above T*≈ 144 K, but a strong nonlinear response in weak magnetic fields and depolarization are observed at temperatures below T*. It is shown that this nontraditional behavior is related to the generation of ferromagnetic clusters in the paramagnetic matrix that form a conducting percolative network at temperatures near T _DM.     

Effect of high pressure on the crystal and magnetic structures of La<Subscript>0.5</Subscript>Ca<Subscript>0.5</Subscript>CoO<Subscript>3</Subscript> cobaltite

The atomic and magnetic structures of La_0.5Ca_0.5CoO₃ cobaltite have been studied by the neutron diffraction technique at high pressures of up to 4 GPa in the 10- to 300-K temperature range. The pressure dependences of the structural parameters have been obtained. The Curie temperature increases with the pressure with the coefficient dT _C/dP = 1 K/GPa, demonstrating the stability of the ground ferromagnetic (FM) state. The pressure dependence of the ground FM state in La_0.5Ca_0.5CoO₃ is in drastic contrast with that for La_{1 − x} Ca _x CoO₃ at a lower calcium content (x < 0.3). For the latter compound, the pressure suppressed the ground FM state and a large negative pressure coefficient of the Curie temperature (dT _C/dP ∼ −10 K/GPa) was observed. The nature of such a phenomenon is analyzed in the framework of the double exchange model also taking into account the changes in the electron configuration of Co³⁺ ions.     

Role of surface phenomena in the magnetoresistivity of polycrystalline manganites La1−x CaxMnO3

The dc electrical resistivity and magnetoresistivity of polycrystalline manganites La_1−x Ca_xMnO₃ (x=0–0.3) are investigated as functions of the temperature, magnetic field and electric field, along with the microwave surface resistance. The investigations show that the dc electrical resistivity and magnetoresistivity are governed by the surface properties of the intergranular boundaries. The dc electrical resistivity is observed to decrease substantially (tenfold) for a comparatively small electric field (E⋟100 V/cm). Estimates are obtained for the internal electrical resistivity of the granules, the thickness of the contact layer (which depends on the temperature and the magnetic field), and the height of the potential barrier between the interfaces separating the surface layer and inner layer of a granule. Fiz. Tverd. Tela (St. Petersburg) 40, 1881–1884 (October 1998)     

Specific features of the properties of half-metallic ferromagnetic Heusler alloys Fe<Subscript>2</Subscript>MnAl,Fe<Subscript>2</Subscript>MnSi,and Co<Subscript>2</Subscript>MnAl

The structural, magnetic, and electrical properties of half-metallic Heusler alloys Fe₂MnAl, Fe₂MnSi, and Co₂MnAl have been investigated in the temperature range of 4–900 K. According to the X-ray diffraction analysis, these alloys have the B2 and L2₁ structures with different degrees of atomic order. The magnetic state of the alloys is considered as a two-sublattice ferrimagnet. The electrical resistivity and thermoelectric power have been discussed in the framework of the two-current conduction model taking into account the existence of an energy gap in the electronic spectrum of the alloys near the Fermi level for the subband with spin-down (minority) electrons.