Influence of the laser wavelength on the epitaxial growth and electrical properties of La0.8Sr0.2MnO3 films grown by excimer laser-assisted MOD

Epitaxial La_1−xSr_xMnO₃ (LSMO) films were prepared by excimer laser-assisted metal organic deposition (ELAMOD) at a low temperature using ArF, KrF, and XeCl excimer lasers. Cross-section transmission electron microscopy (XTEM) observations confirmed the epitaxial growth and homogeneity of the LSMO film on a SrTiO₃ (STO) substrate, which was prepared using ArF, KrF, and XeCl excimer lasers. It was found that uniform epitaxial films could be grown at 500 °C by laser irradiation. When an XeCl laser was used, an epitaxial film was formed on the STO substrate at a fluence range from 80 to 140 mJ/cm² of the laser fluence for the epitaxial growth of LSMO film on STO substrate was changed. When the LaAlO₃ (LAO) substrate was used, an epitaxial film was only obtained by ArF laser irradiation, and no epitaxial film was obtained using the KrF and XeCl lasers. When the back of the amorphous LSMO film on an LAO substrate was irradiated using a KrF laser, no epitaxial film formed. Based on the effect of the wavelength and substrate material on the epitaxial growth, formation of the epitaxial film would be found to be photo thermal reaction and photochemical reaction. The maximum temperature coefficient of resistance (TCR) of the epitaxial La_0.8Sr_0.2MnO₃ film on an STO substrate grown using an XeCl laser is 4.0%/K at 275 K. XeCl lasers that deliver stabilized pulse energies can be used to prepare LSMO films with good a TCR.     

Direct conversion of a metal organic compound to epitaxial Sb-doped SnO2 film on a (0 0 1) TiO2 substrate using a KrF laser, and its resulting electrical properties

Epitaxial Sb-doped SnO₂ (0 0 1) thin film on a TiO₂ (0 0 1) substrate was successfully prepared by laser-assisted metal organic deposition at room temperature. The effects of the precursor thin film and laser fluence on the resistivity, carrier concentration, and mobility of the Sb-doped SnO₂ film were investigated. The resistivity of the Sb-doped SnO₂ film prepared by direct irradiation to metal organic film is one order of magnitude lower than that of film prepared by irradiation to amorphous Sb-doped SnO₂ film. From an analysis of Hall measurements, the difference between the resistivity of the Sb-doped SnO₂ film prepared using the metal organic precursor film and that of amorphous precursor film appears to be caused by the mobility. Direct conversion of the metal organic compound by excimer laser irradiation was found to be effective for preparing epitaxial Sb-doped SnO₂ film with low resistivity.     

Pulsed-laser crystallization and epitaxial growth of metal-organic films of Ca-doped LaMnO3 on STO and LSAT substrates

Ca-doped LaMnO₃ (LCMO) thin films have been successfully prepared on SrTiO₃ (STO) and [(LaAlO₃)_0.3-(SrAlTaO₆)_0.7] (LSAT) substrates using the excimer laser assisted metal-organic deposition (ELAMOD) process. The crystallization and the epitaxial growth of the amorphous metal-organic LCMO thin films have been achieved using a KrF excimer laser irradiation while the substrates were kept at constant temperature of 500 °C. Epitaxial films were obtained using laser fluence in the interval of 50-120 mJ/cm². The microstructure of the LCMO films was studied using cross-section transmission electron microscopy. High quality of LCMO films having smooth surfaces and sharp interfaces were obtained on both the STO and the LSAT substrates. The effect of the laser fluence on the temperature coefficient of resistance (TCR) was investigated. The largest values of TCR of the LCMO grown on the LSAT and the STO substrates of 8.3% K⁻¹ and 7.46% K⁻¹ were obtained at different laser fluence of 80 mJ/cm² and 70 mJ/cm², respectively.     

Ultra fast melting process in femtosecond laser crystallization of thin a-Si layer

In this paper, we investigated the mechanism of crystallization induced by femtosecond laser irradiation for an amorphous Si (a-Si) thin layer on a crystalline Si (c-Si) substrate. The fundamental, SHG, THG wavelength of a Ti:Sapphire laser was used for the crystallization process. To investigate the processed areas we performed Laser Scanning Microscopy (LSM), Transmission Electron Microscopy (TEM) and Imaging Pump-Probe measurements. Except for 267 nm femtosecond laser irradiation, the crystallization occurred well. The threshold fluences for the crystallization using 800 nm and 400 nm femtosecond laser irradiations were 100 mJ/cm² and 30 mJ/cm², respectively. TEM observation revealed that the crystallization occurred by epitaxial growth from the boundary surface between the a-Si layer and c-Si substrate. The melting depths estimated by Imaging Pump-Probe measurements became shallower when the shorter wavelength was used.     

Epitaxial growth of InN on nearly lattice-matched (Mn,Zn)Fe2O4

We have grown InN films on nearly lattice-matched (Mn,Zn)Fe₂O₄ (111) substrates at low temperatures by pulsed laser deposition (PLD) and investigated their structural properties. InN films grown at substrate temperatures above 400 °C show poor crystallinity, and their in-plane epitaxial relationship is [10-10]InN//[11-2](Mn,Zn)Fe₂O₄, which means that their lattice mismatch is quite large (11%). By contrast, high quality InN films with flat surfaces can be grown at growth temperatures lower than 150 °C with the ideal in-plane epitaxial relationship of [11-20]InN//[11-2](Mn,Zn)Fe₂O₄, which produces lattice mismatches of as low as 2.0%. X-ray reflectivity measurements have revealed that the thickness of the interfacial layer between the InN and the substrates is reduced from 14 to 8.4 nm when the growth temperature is decreased from 400 °C to room temperature. This suppression of the interface reactions by reducing the growth temperature is probably responsible for the improvement in crystalline quality. These results indicate that the use of (Mn,Zn)Fe₂O₄ (111) substrates at low growth temperatures allows us to achieve nearly lattice matched epitaxial growth of InN.     

Preparation and photocatalytic activity of CeO2/TiO2 interface composite film

The CeO₂/TiO₂ and TiO₂/CeO₂ interface composite films were prepared on glass substrates by the sol-gel process via dip-coating and calcining technique. The scanning electron microscopy (SEM) revealed that the TiO₂ layer has a compact and uniformity glasslike surface with 200 nm in thickness, and the CeO₂ layer has a coarse surface with 240 nm in thickness. The X-ray diffractometer (XRD) analysis showed that the TiO₂ layer is made up of anatase phase, and the CeO₂ layer is structured by cubic fluorite phase. Through a series of photo-degradation experiments, the relationship of the photocatalytic activity with the constituents of the films was studied. In virtue of the efficient interfacial charge separation via the process of electron transfer from TiO₂ to CeO₂, the photocatalytic activity of the CeO₂/TiO₂ composite film is high. Contrarily, the photocatalytic activity of the TiO₂/CeO₂ composite film is low, due to its inert surface made up of CeO₂ with broad bandwidth. Apart from the effect of the film structure, the effect of film thickness on photocatalytic activity was also discussed.     

Substrate temperature influence on the properties of nanostructured ZnO transparent ultrathin films grown by PLD

Zinc oxide films of 40 nm thickness have been deposited on glass substrates by pulsed laser deposition using an excimer XeCl laser (308 nm) at different substrate temperatures ranging from room temperature to 650 °C. Surface investigations carried out by using atomic force microscopy have shown a strong influence of temperature on the films surface topography. UV-VIS transmittance measurements have shown that our ZnO films are highly transparent in the visible wavelength region, having an average transmittance of ∼90%. The optical band gap of the films was found to be 3.26 eV, which is lower than the theoretical value of 3.37 eV. Besides the normal absorption edge related to the transition between the valence and the conduction band, an additional absorption band was also recorded in the wavelength region around 364 nm (∼3.4 eV). This additional absorption band may be due to excitonic, impurity, and/or quantum size effects. Photoreduction/oxidation in ozone of the ZnO films lead to larger conductivity changes for higher deposition temperature. In conclusion, the ozone sensing characteristics as well as the optical properties of the ZnO thin films deposited by pulsed laser deposition are strongly influenced by the substrate temperature during growth. The sensitivity of the films towards ozone might be enhanced significantly by the control of the films deposition parameters and surface characteristics.     

Light induced adsorption of Si nano-composites in LiF crystals at 157 nm

Si nano-composites were precipitated on LiF crystals following ablation from Si targets with laser light at 157 nm. The LiF/Si interface was analyzed with scanning electron microscopy, atomic force microscopy and energy dispersive X-ray microanalysis. It was found that Si composites were strongly attached to LiF ionic sites to form inhomogeneous structures consisted of small isotropic crystals 0.1-1 μm long, rich in Si and fluorine, which eventually further agglomerate to form larger structures. The thickness of the LiF/Si interface was increased from 50 nm to 2 μm following laser irradiation at 157 nm, due to accelerated adsorption of Si in the LiF interface by VUV light.     

Formation of silicon nanodots from dysprosium-doped amorphous SiCxOy films grown by hot-filament assisted chemical vapor deposition of CH3SiH3 and Dy(DPM)3 gas jets

We report on Si nanodot formation by chemical vapor deposition (CVD) of ultrathin films and following oxidation. The film growth was carried out by hot-filament assisted CVD of CH₃SiH₃ and Dy(DPM)₃ gas jets at the substrate temperature of 600 °C. The transmission electron microscopy observation and X-ray photoelectron spectroscopy analysis indicated that ∼35 nm Dy-doped amorphous silicon oxycarbide (SiC_xO_y) films were grown on Si(1 0 0). The Dy concentration was 10-20% throughout the film. By further oxidation at 860 °C, the smooth amorphous film was changed to a rough structure composed of crystalline Si nanodots surrounded by heavily Dy-doped SiO₂.     

Epitaxial growth and structural characterization of Pb(Fe1/2Nb1/2)O3 thin films

We have grown lead iron niobate thin films with composition Pb(Fe_1/2Nb_1/2)O₃ (PFN) on (0 0 1) SrTiO₃ substrates by pulsed laser deposition. The influence of the deposition conditions on the phase purity was studied. Due to similar thermodynamic stability spaces, a pyrochlore phase often coexists with the PFN perovskite phase. By optimizing the kinetic parameters, we succeeded in identifying a deposition window which resulted in epitaxial perovskite-phase PFN thin films with no identifiable trace of impurity phases appearing in the X-ray diffractograms. PFN films having thicknesses between 20 and 200 nm were smooth and epitaxially oriented with the substrate and as demonstrated by RHEED streaks which were aligned with the substrate axes. X-ray diffraction showed that the films were completely c-axis oriented and of excellent crystalline quality with low mosaicity (X-ray rocking curve FWHM?0.09°). The surface roughness of thin films was also investigated by atomic force microscopy. The root-mean-square roughness varies between 0.9 nm for 50-nm-thick films to 16 nm for 100-nm-thick films. We also observe a correlation between grain size, surface roughness and film thickness.     

Thickness-dependent magnetization reversal in CoZrNb amorphous films

Structure and magnetization of CoZrNb amorphous films prepared by DC magnetron sputtering have been studied as a function of film thickness (t), from 35 to 840 nm. Using comprehensive characterization, we show that the CoZrNb amorphous films possess a single phase and no nanocrystalline can be detected. The magnetic measurements indicate that the magnetization reversal of CoZrNb films is strongly dependent on t. That is, the coercivity is abruptly reduced to be lower than 4 Oe with t increasing from 35 to 105 nm, and then gradually decreases to ∼0.2 Oe as t increases. This coercivity transition versus t is accompanied by the strong magnetization reversal when t is larger than 105 nm. The results reveal that CoZrNb amorphous films with comparatively large film thickness (>100 nm) are suitable for sensors and anti-faked materials.     

Structural and morphological characterization of TiO2 nanostructured films grown by nanosecond pulsed laser deposition

TiO₂ has attracted a lot of attention due to its photocatalytic properties and its potential applications in environmental purification and self cleaning coatings, as well as for its high optical transmittance in the visible-IR spectral range, high chemical stability and mechanical resistance. In this paper, we report on the growth of TiO₂ nanocrystalline films on Si (1 0 0) substrates by pulsed laser deposition (PLD). Rutile sintered targets were irradiated by KrF excimer laser (λ = 248 nm, pulse duration ∼30 ns) in a controlled oxygen environment and at constant substrate temperature of 650 °C. The structural and morphological properties of the films have been studied for different deposition parameters, such as oxygen partial pressure (0.05-5 Pa) and laser fluence (2- 4 J/cm²). X-ray diffraction (XRD) shows the formation of both rutile and anatase phases; however, it is observed that the anatase phase is suppressed at the highest laser fluences. X-ray photoelectron spectroscopy (XPS) measurements were performed to determine the stoichiometry of the grown films. The surface morphology of the deposits, studied by scanning electron (SEM) and atomic force (AFM) microscopies, has revealed nanostructured films. The dimensions and density of the nanoparticles observed at the surface depend on the partial pressure of oxygen during growth. The smallest particles of about 40 nm diameter were obtained for the highest pressures of inlet gas.     

Particulate assisted growth of ZnO nanorods and microrods by pulsed laser deposition

Zinc oxide (ZnO) thin films were deposited on the gallium nitride (GaN) and sapphire (Al₂O₃) substrates by pulsed laser deposition (PLD) without using any metal catalyst. The experiment was carried out at three different laser wavelengths of Nd:YAG laser (λ = 1064 nm, λ = 532 nm) and KrF excimer laser (λ = 248 nm). The ZnO films grown at λ = 532 nm revealed the presence of ZnO nanorods and microrods. The diameter of the rods varies from 250 nm to 2 μm and the length varies between 9 and 22 μm. The scanning electron microscopy (SEM) images of the rods revealed the absence of frozen balls at the tip of the ZnO rods. The growth of ZnO rods has been explained by vapor-solid (V-S) mechanism. The origin of growth of ZnO rods has been attributed to the ejection of micrometric and sub-micrometric sized particulates from the ZnO target. The ZnO films grown at λ = 1064 nm and λ = 248 nm do not show the rod like morphology. X-ray photoelectron spectroscopy (XPS) has not shown the presence of any impurity except zinc and oxygen.     

Growth process of β-FeSi2 epitaxial film on Si(1 1 1) by molecular beam epitaxy

We have reported a one step growth of a high quality β-FeSi₂ epitaxial film on hydrogen terminated Si(1 1 1) by using molecular beam epitaxy (MBE) without template layer or post-growth annealing. In the present work, the growth process was studied by analyzing X-ray diffraction (XRD) spectra, reflective high energy electron diffraction (RHEED) and atomic force microscopy (AFM) observations on the samples grown with different growth times from 10 s to 1 h. A phase transformation from γ-FeSi₂ to β-FeSi₂ was confirmed existing in the crystal film growth, as well as the growth mode changing from three-dimensional (3D) to two-dimensional (2D) mode.     

AlF3 film deposited by IAD with end-Hall ion source using SF6 as working gas

A novel and effective process to fabricate high quality fluoride thin films was presented. Aluminum fluoride films deposited by a conventional thermal evaporation with an ion-assisted deposition (IAD) using SF₆ as a working gas at around room temperature were investigated. In this study, the optimal voltage and current, 50 V and 0.25 A, were found according to the optical properties of the films: high refractive index (1.489 at 193 nm), low optical absorption and extinction coefficient (<10⁻⁴ at 193 nm) in the UV range. The physical properties of the film are high packing density and amorphous without columnar structure. It was proved that using SF₆ working gas in IAD process is a good choice and significantly improves the quality of AlF₃ films.     

Thickness dependence of electrical properties of ITO film deposited on a plastic substrate by RF magnetron sputtering

Indium tin oxide (ITO) films with various thicknesses in range of 40-280 nm were prepared onto a plastic substrate (PMMA). Deposition was carried out with RF magnetron sputtering method and the substrate temperature was held at ∼70 °C, in lack of the thermal damage to the polymer substrate. Changes in microstructure and electrical properties of ITO films according to their thicknesses were investigated. It was found that amorphous layer with thickness of 80 nm was formed at the interface on the polymer substrate and polycrystalline ITO could be obtained above the thickness. Conductivity of ITO films was found to be strongly dependent on the crystallinity. Consequently, it is suggested that crystallinity of the deposited films should be enhanced at the initial stage of deposition and the thickness of amorphous region be reduced in order to prepare high quality ITO thin films on polymer substrates.     

Enhanced strain relaxation induced by epitaxial layer growth mode of MgO thin films

Growth of MgO films on silicon substrate was conducted by KrF excimer pulsed-laser ablation system. Two kinds of growth mode were revealed in situ by reflection high energy electron diffraction. It was found that the layer growth mode of MgO thin films could remarkably reduce the misfit strain originated from the different lattice constant and thermal expansion coefficiency between MgO films and Si. An enhanced strain relaxation was discovered for MgO films, which were grown with the layer growth mode, in the film thickness range of 40-100 nm. The value of critical thickness for the formation of misfit dislocation agrees well with the calculated one. This exceptional phenomenon should be ascribed to the layer growth mode of epitaxial MgO films.     

Elaboration of (1 1 1)-oriented La-doped PZT thin films on platinized silicon substrates

PLZT thin films with different thickness were deposited in situ on platinum coated silicon substrates using a multi-target sputtering system. The purpose was to grow (1 1 1)-textured PLZT films on Pt (1 1 1). To this aim, the role of some key parameters on both crystalline quality and electrical properties was investigated. An ultra-thin TiO₂ seeding layer was deposited, prior to PLZT, which strongly affected the crystallographic orientation of the films. The relation between temperature deposition and film crystallinity is analysed. TEM observations show the presence of some very small grains of Zr_0.9La_0.1O_1.95 at the film bottom interface. In the range of thickness investigated, the plot of the inverse capacitance as a function of the film thickness split up into two different curves, each with a linear shape, which however allows determination of a single value of interface capacitance. Above a thickness of 400-500 nm a saturation of the dielectric properties seems to be reached.     

The influence of substrate temperature variation on tungsten oxide thin film growth in an HFCVD system

Tungsten oxide (WO₃) thin films were deposited by a modified hot filament chemical vapor deposition (HFCVD) technique using Si (1 0 0) substrates. The substrate temperature was varied from room temperature to 430 °C at an interval of 100 °C. The influence of the substrate temperature on the structural and optical properties of the WO₃ films was studied. X-ray diffraction and Raman spectra show that as substrate temperature increases the film tends to crystallize from the amorphous state and the surface roughness decreases sharply after 230 °C as confirmed from AFM image analysis. Also from the X-ray analysis it is evident that the substrate orientation plays a key role in growth. There is a sharp peak for samples on Si substrate due to texturing. The film thickness also decreases as substrate temperature increases. UV-vis spectra show that as substrate temperature increases the film property changes from metallic to insulating behavior due to changing stoichiometry, which was confirmed by XPS analysis.