Magnetic entropy change in GdCo13−xSix intermetallic compounds

The magnetic entropy change in GdCo_13−xSi_x (x=3.8, 4, 4.1, and 4.2) intermetallic compounds has been investigated by means of magnetic measurements in the vicinity of their Curie temperature. It was found that the magnetic ordering temperatures decrease from 60 K at x=3.8 to 28 K for x=4.2. The magnetic entropy change is calculated from isothermal magnetization versus magnetic field at various temperatures using the Maxwell relation. As a result, the maximum magnetic entropy changes of the investigated compounds, at their Curie temperatures, decrease from 11.5 J/kg K for x=4.2 to 6.86 J/kg K for x=3.8 in a field change of 0-3 T, whereas it decreases from 5.13 J/kg K for x=4.2 to 2.60 J/kg K for x=3.8 in a field change of 0-1 T. Moreover, the maximum value of the magnetic entropy change obtained at a higher field for GdCo_13−xSi_x with x=4 (23.75 J/kg K at 5 T) is comparable to that of various types of compounds with a cubic NaZn₁₃-type structure. Finally, the maximum of the magnetic entropy change is found to decrease with increasing Si content.     

Near room temperature magnetocaloric properties of melt-spun Gd100−xBx (x=0, 5, 10, 15, and 20 at%) alloys

The magnetocaloric properties of melt-spun Gd-B alloys were examined with the aim to explore their potential application as magnetic refrigerants near room temperature. A series of Gd_100−xB_x (x=0, 5, 10, 15, and 20 at%) alloys were prepared by melt spinning. With the decrease in Gd/B ratio, Curie temperature (T_C) remains constant at ∼293 K, and saturation magnetization, at 275 K, decreases from ∼100 to ∼78 emu/g. Negligible magnetic hysteresis was observed in these alloys. The peak value of magnetic entropy change, (−ΔS_M)_max, decreased from ∼9.9 J/kg K (0-5 T) and ∼5.5 J/kg K (0-2 T) for melt-spun Gd to ∼7.7 J/kg K (0-5 T) and ∼4.0 J/kg K (0-2 T), respectively for melt-spun Gd₈₅B₁₅ and Gd₈₀B₂₀ alloys. Similarly, the refrigeration capacity (q) decreased monotonously from ∼430 J/kg (0-5 T) for melt-spun Gd to ∼330 J/kg (0-5 T) for melt-spun Gd₈₀B₂₀ alloy. The near room temperature magnetocaloric properties of melt-spun Gd_100−xB_x (0≤x≤20) alloys were found to be comparable to few first-order transition based magnetic refrigerants.     

Magnetocaloric effect in La0.67Sr0.33MnO3 manganite above room temperature

The La_0.67Sr_0.33MnO₃ composition prepared by sol-gel synthesis was studied by dc magnetization measurements. A large magnetocaloric effect was inferred over a wide range of temperature around the second-order paramagnetic-ferromagnetic transition. The change of magnetic entropy increases monotonically with increasing magnetic field and reaches the value of 5.15 J/kg K at 370 K for Δμ0H=5 T. The corresponding adiabatic temperature change is 3.3 K. The changes in magnetic entropy and the adiabatic temperature are also significant at moderate magnetic fields. The magnetic field induced change of the specific heat varies with temperature and has maximum variation near the paramagnetic-ferromagnetic transition. The obtained results show that La_0.67Sr_0.33MnO₃ could be considered as a potential candidate for magnetic refrigeration applications above room temperature.     

Structure, magneto-structural transitions and magnetocaloric properties in Ni50−xMn37+xIn13 melt spun ribbons

Melt spun Ni_50−xMn_37+xIn₁₃ (2≤x≤5) ribbons were investigated for the structure, microstructure, magneto-structural transitions and inverse magnetocaloric effect (IMCE) associated with the first-order martensitic phase transition. The influence of excess Mn in Ni site (or Ni/Mn content) on the martensite transition and the associated magnetic and magnetocaloric properties are discussed. It was found that with the increase in Mn content, the martensitic transition shifted from 325 to 240 K as x is varied from 2 to 4, and the austenite phase was stabilized at room temperature. The x=5 ribbon did not show the martensitic transition. For the x=3 ribbon, the structural and magnetic transitions are close together unlike in the x=4 ribbon in which they are far (∼60 K) apart. The zero field cooled and field cooled curves support the presence of exchange bias blocking temperature due to antiferromagnetic interactions in the ribbons. A large change in the magnetization between the martensite and austenite phases was observed for a small variation in the Ni/Mn content, which resulted in large IMCE. A large positive magnetic entropy change (ΔS_M) of 32 J/kg K at room temperature (∼ 300 K) for a field change of 5 T with a net refrigeration capacity of 64 J/kg was obtained in the Ni₄₇Mn₄₀In₁₃ ribbon.     

Magnetocaloric effect in high Ni content Ni52Mn48−xInx alloys under low field change

Ni-rich Heusler alloys Ni₅₂Mn_48−xIn_x (x=15.5, 16 and 16.5) were prepared by the arc melting method. X-ray diffraction analysis revealed that the martensite has orthorhombic structure (S.G. Pmm2) at room temperature. The only alloy with x=15.5 has structural transmission from martensite to austenite without any magnetic transmission. The temperature dependence and the field dependence of the magnetization measurement indicated that the magnetization increased with the decreasing of the concerntration of Mn. The lesser the Mn atoms located in the In atom sites, the weaker the total AFM interaction in the system. Giant entropy changes ΔS_M(T, H) were found in Ni₅₂Mn_48−xIn_x alloys with the maximum ΔS_M value of 22.3 J kg K for the sample with x=16.5 at 270 K under the magnetic field change of 1.5 T.     

Magnetic properties of YFe12−xMox compounds and magnetocaloric effect of YFe9.5Mo2.5

The characterization and magnetic properties of YFe_12−xMo_x (x=2.0, 2.5 and 3.0) with the ThMn₁₂-type structure, and the magnetocaloric effect of YFe_9.5Mo_2.5 were investigated. A directional growth was observed in YFe₁₀Mo₂ alloy. A broad peak in the zero-field-cooling (ZFC) magnetization curve of the YFe_12−xMo_x compounds is ascribed to the existence of ferromagnetic clusters with different site moments and scattered orientations of the moments. The broad range of the peak is reduced with increasing Mo content. A weak peak is observed near 190 K in the ZFC curve of YFe₉Mo₃, which is associated with the 8i sites being mostly occupied by Mo atoms. YFe_9.5Mo_2.5 has a magnetic entropy change of −1.09 J/kg K for a field change of 5 T at 277 K.     

Magnetic and magnetocaloric properties of Gd1−xScxNi2 solid solutions

Magnetic and heat capacity measurements have been carried out on the polycrystalline Gd_1−xSc_xNi₂ solid solutions (0≤x≤1), which crystallize in the cubic C15 Laves phases superstructure (space group F4?3m). These solid solutions are ferromagnetic with a Curie temperature below 76 K. Their Curie temperature decreases from 75.4 K for GdNi₂ to 13.6 K for Gd_0.2Sc_0.8Ni₂. At high temperatures, all solid solutions, except ScNi₂, are Curie-Weiss paramagnets. The Debye temperature as well as phonon, conduction electron and magnetic contributions to the heat capacity have been determined from heat capacity measurements. The magnetocaloric effect has been estimated both in terms of isothermal magnetic entropy change and adiabatic temperature change for selected solid solutions in magnetic fields up to 3 T.     

Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

Magnetic properties and room-temperature magnetocaloric effect in the doped antipervoskite compounds Ga1−xAlxCMn3 (0≤x≤0.15)

We report the effects of Al doping on the structure, magnetic properties, and magnetocaloric effect of antiperovskite compounds Ga_1−xAl_xCMn₃ (0≤x≤0.15). Partial substitutions of Al for Ga enhance the Curie temperature (from 250 K for x=0.0 to 312 K for x=0.15) and the saturation magnetization. On increasing the doping level x, the maximum values of the magnetic entropy change (−ΔS_M) decreases while the temperature span of −ΔS_M vs. T plot broadens. Furthermore, the relative cooling power (RCP) is also studied. For 20 kOe, the RCP value tends to saturate at a high doping level (for x=0.12, 119 J/kg at 296 K). However, at 45 kOe, the RCP value increases quickly with increasing x (for x=0.15, 293 J/kg at 312 K). Considering the relatively large RCP and inexpensive raw materials, Ga_1−xAl_xCMn₃ may be alternative candidates for room-temperature magnetic refrigeration.     

Magnetocaloric properties in the Cr-doped La0.7Sr0.3MnO3 manganites

Single-phase polycrystalline samples of La_0.7Sr_0.3Mn_1-xCr_xO₃ with nominal composition of x=0.00, 0.20, 0.40 and 0.50 were prepared by a conventional solid-state reaction method in air. Investigations of magnetization were carried out in the temperature range 5-400 K and magnetic field range 0-8 T. It was found that the Curie temperature T_C decreases with increasing x and the maximum magnetic entropy change (−ΔS_M) for x=0.20 is ∼1.203 and ∼2.653 J/kg K, respectively for 2 and 6 T magnetic field near the temperature of 280 K.     

Magnetocaloric effect in R2Fe17 (R=Sm,Gd, Tb,Dy, Er)

A series of R₂Fe₁₇ (R=Sm, Gd, Tb, Dy, Er) have been synthesized. The magnetocaloric effect (MCE) of these compounds has been investigated by means of magnetic measurements in the vicinity of their Curie temperature. The Curie temperature of Er₂Fe₁₇ is 294 K. The maximum magnetic entropy change of Er₂Fe₁₇ under 5 T magnetic field is ∼3.68 J/kg K. In the R₂Fe₁₇ (R=Sm, Gd, Tb, Dy, Er) system, the maximum magnetic entropy change under 1.5 T magnetic field is 1.72, 0.89, 1.32, 1.59, 1.68 J/kg K corresponding to their Curie temperature (400, 472, 415, 364, 294 K), respectively.     

Magnetocaloric effects in (Gd1−xTbx)Co2

The structures and magnetocaloric effects of (Gd_1−xTb_x)Co₂ (x=0, 0.25, 0.4, 0.5, 0.6, 0.7, 0.8, and 1) pseudobinary compounds were investigated by X-ray powder diffraction and magnetic properties measurement. The results show that the T_c of the alloy is near room temperature when X=0.6. The magnetic entropy changes of the compounds increase from 1.7 to 3.6 J/kg K with increasing the content of Tb under an applied field up to 2 T. All the compounds exhibit second order magnetic change. As a result, the values of their ΔS_M are lower than that of some large magnetocaloric effect materials.     

Metamagnetic transition and magnetocaloric effect in charge-ordered Pr0.68Ca0.32−xSrxMnO3 (x=0, 0.1, 0.18, 0.26 and 0.32) compounds

In this study, magnetic and magnetocaloric properties of Pr_0.68Ca_0.32−xSr_xMnO₃ (x=0, 0.1, 0.18, 0.26 and 0.32) compounds were investigated. X-ray results indicated that all the samples have a single phase of orthorhombic symmetry. The orthorhombic unit cell parameters increase with the increase in Sr content. Large negative magnetic entropy changes (−26.2 J/kg K at 38 K and 5 T for x=0 and −6.5 J/kg K at 83 K and 6 T for x=0.1) were attributed to ultrasharp metamagnetic transitions. The peak value of ΔS_m decreased from −4.1 J/kg K for x=0.18 sample to −2.4 J/kg K for x=0.32 at 1 T magnetic field.     

Effects of high Fe substitution for Mn on phase transition and magnetic properties of YFexMn12−x compounds

YFe_xMn_12−x (x=7-10) compounds were synthesized; their structure and magnetic properties were investigated, the results reveal that a higher Fe concentration x makes the crystal phase change from ThMn₁₂-type to Th₂Zn₁₇-type, with the phase transition point x=9; the Curie temperature increases with increasing x, which becomes 290 K for x=8.8 and 150 K for x=7; and the magnetization also increases monotonically with increasing x until the phase transition point.     

Structural and magnetic properties of sol-gel Co2xNi0.5−x Zn0.5−xFe2O4 thin films

Nanocrystalline Co_2xNi_0.5−xZn_0.5−xFe₂O₄ (x=0−0.5) thin films have been synthesized with various grain sizes by a sol-gel method on polycrystalline silicon substrates. The morphology as well as magnetic and microwave absorption properties of the films calcined at 1073 K were studied using X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and vibrating sample magnetometry. All films were uniform without microcracks. The Co content in the Co-Ni-Zn films resulted in a grain size ranging from 15 to 32 nm while it ranged from 33 to 49 nm in the corresponding powders. Saturation and remnant magnetization increased with increase in grain size, while coercivity demonstrated a drop due to multidomain behavior of crystallites for a given value of x. Saturation magnetization increased and remnant magnetization had a maximum as a function of grain size independent of x. In turn, coercivity increased with x independent of grain size. Complex permittivity of the Co-Ni-Zn ferrite films was measured in the frequency range 2-15 GHz. The highest hysteretic heating rate in the temperature range 315-355 K was observed in CoFe₂O₄. The maximum absorption band shifted from 13 to 11 GHz as cobalt content increased from x=0.1 to 0.2.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

High-temperature electrical properties of magnesiowustite Mg1 − xFexO and spinel Fe3 − x − yMgxCryO4 ceramics

Phase relationships, thermal expansion and electrical properties of Mg_1 − xFe_xO (x = 0.1-0.45) cubic solid solutions and Fe_{3 − x − y}Mg_xCr_yO_4 ± δ (x = 0.7-0.95; y = 0 or 0.5) spinels were studied at 300-1770 K in the oxygen partial pressure range from 10 Pa to 21 kPa. Increasing iron content enlarges the spinel phase stability domain at reduced oxygen pressures and elevated temperatures. The total conductivity of the spinel ceramics is predominantly n-type electronic and is essentially p(O₂)-independent within the stability domain. The computer simulations using molecular dynamics technique confirmed that overall level of ion diffusion remains low even at high temperatures close to the melting point. Temperature dependencies of the total conductivity in air exhibit a complex behavior associated with changing the dominant defect-chemistry mechanism from prevailing formation of the interstitial cations above 1370-1470 K to the generation of cation vacancies at lower temperatures, and with kinetically frozen cation redistribution in spinel lattice below 700-800 K. The average thermal expansion coefficients of the spinel ceramics calculated from dilatometric data in air vary in the range (9.6-10.0) × 10^− 6 K^− 1 at 300-500 K and (13.2-16.1) × 10^− 6 K^− 1 at 1050-1370 K. Mg_1 − xFe_xO solid solutions undergo partial decomposition on heating under oxidizing and mildly reducing conditions, resulting in the segregation of spinel phase and conductivity decrease.     

Magnetic properties of stuffed copper chromium tellurides Cu1+xCr2+yTe4 (x=0-1, y<0.3)

We present a detail study of the effect of excess metal atoms on the magnetic properties of Cu_1+xCr_2+yTe₄ at 2-400 K. With the increase in x=0-1 and y<0.3, these compounds retain metallic behavior, while ferromagnetic ordering temperature reduces from 325 to 160 K. Our low field susceptibility χ_ac measurements reveal a second transition on cooling below the ferromagnetic ordering; the transition at around 160-180 K intensifies with the excess amount of copper and chromium atoms. The value of spontaneous magnetization at 2 K remains between 2.6 and 2.9μ_B across all the compositions and it reduces with temperature as M(T)∼A₀T^3/2+A₁T^5/2, as expected for the excitation of Bloch's spin waves in a model of the Heisenberg ferromagnet. Our terminal composition Cu_1.9Cr_2.25Te₄ showed only second transition at 160 K with short range magnetic order much above the transition temperature and in the absence of the specific heat jump at this temperature. The magnetic properties are explained as a result of random magnetic anisotropy in the excess-metal compositions induced by the interstitial atomic defects in their parent spinel structure. The large stuffing of cations has been made possible in the telluride compounds because of the large size of tellurium and also by the covalent bonding that stabilizes the defect structure.     

Effect of Co or Mn addition on the soft magnetic properties of amorphous Fe89−xZr11Bx (x=5, 10) alloy ribbons

The temperature and field dependent magnetic properties of melt-spun amorphous Fe_89−x−yZr₁₁B_x(Co,Mn)_y (x=5, 10 and 0≤y≤10) alloys in the temperature range 5-1200 K are reported. The Curie temperature and saturation magnetization at room temperature increase (decrease) almost linearly with Co (Mn) addition. With increasing Co concentration, the room temperature coercivity increases at the rate of 2.26 (0.28) A/m per at% for the x=5 (10) samples. The high-field magnetic susceptibility and local magnetic anisotropy decrease (increases) rapidly with increasing Co (Mn) concentration. The thermomagnetic curves show a marked increase in magnetization above 850 K corresponding to the crystallization of α-FeCo (α-Fe) phase in samples containing Co (Mn). The Curie temperature of the crystalline phase increases (remains same) with increasing Co (Mn) concentration with the formation of α-FeCo (α-Fe). Addition of Co up to 10 at% in Fe-Zr-B improves the room temperature saturation magnetization from 0.56 to 1.2 T, and Curie temperature from 315 to 476 K. Also, the coercivity increases with Co addition from 1.27 to 23.88 A/m for x=5 and from 7.64 to 10.35 A/m for x=10 alloy. The non-collinear spin structures that characterize Fe rich Fe-Zr-B amorphous alloys have been used to describe the observed results.     

Structural and magnetic properties of MnxCo1−xFe2O4 ferrite nanoparticles

We report on the structural and magnetic properties of nanoparticles of Mn_xCo_1−xFe₂O₄ (x=0.1, 0.5) ferrites produced by the glycothermal reaction. From the analysis of XRD spectra and TEM micrographs, particle sizes of the samples have been found to be about 8 nm (for x=0.1) and 13 nm (for x=0.5). The samples were characterized by DC magnetization in the temperature range 5-380 K and in magnetic fields of up to 40 kOe using a SQUID magnetometer. Mössbauer spectroscopy results show that the sample with higher Mn content has enhanced hyperfine fields after thermal annealing at 700 °C. There is a corresponding small reduction in hyperfine fields for the sample with lower Mn content. The variations of saturation magnetization, remnant magnetization and coercive fields as functions of temperature are also presented. Our results show evidence of superparamagnetic behaviour associated with the nanosized particles. Particle sizes appear to be critical in explaining the observed properties.