Living anionic polymerization of lauryl methacrylate and synthesis of block copolymers with methyl methacrylate

Anionic polymerization of lauryl methacrylate (LMA) with 1,1‐diphenylhexyl lithium in tetrahydrofuran (THF) at ?40 °C resulted in a multimodal and broad molecular weight distribution (MWD) with poor initiator efficiency. In the presence of additives such as dilithium salt of triethylene glycol (G₃Li₂), LiCl, and LiClO₄, the polymerization resulted in polymers with a narrow MWD (≤ 1.10). Diblock copolymers of methyl methacrylate (MMA) and LMA were synthesized by anionic polymerization using DPHLi as initiator in THF at ?40 °C with the sequential addition of monomers. The molecular weight distribution of the polymers was narrow and without homopolymer contamination when LMA was added to living PMMA chain ends. Diblock copolymers with broad/bimodal MWD were obtained with a reverse‐sequence monomer addition. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 875–882, 2004     

Emulsion atom transfer radical block copolymerization of 2‐ethylhexyl methacrylate and methyl methacrylate

The emulsion atom transfer radical block copolymerization of 2‐ethylhexyl methacrylate (EHMA) and methyl methacrylate (MMA) was carried out with the bifunctional initiator 1,4‐butylene glycol di(2‐bromoisobutyrate). The system was mediated by copper bromide/4,4′‐dinonyl‐2,2′‐bipyridyl and stabilized by polyoxyethylene sorbitan monooleate. The effects of the initiator concentration and temperature profile on the polymerization kinetics and latex stability were systematically examined. Both EHMA homopolymerization and successive copolymerization with MMA proceeded in a living manner and gave good control over the polymer molecular weights. The polymer molecular weights increased linearly with the monomer conversion with polydispersities lower than 1.2. A low‐temperature prepolymerization step was found to be helpful in stabilizing the latex systems, whereas further polymerization at an elevated temperature ensured high conversion rates. The EHMA polymers were effective as macroinitiators for initiating the block polymerization of MMA. Triblock poly(methyl methacrylate–2‐ethylhexyl methacrylate–methyl methacrylate) samples with various block lengths were synthesized. The MMA and EHMA reactivity ratios determined by a nonlinear least‐square method were ～0.903 and ～0.930, respectively, at 70 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1914–1925, 2006     

Hyperbranched polymers generated from oxyanionic vinyl polymerization of commercially available methacrylate inimers

Hyperbranched polymethacrylates were prepared by means of oxyanionic vinyl polymerization of commercially available monomers, including hydroxyethyl methacrylate (HEMA) and poly(ethylene glycol) methacrylate (PEG‐MA). Hyperbranched polymethacrylates with high molecular weight were obtained with the complex of potassium hydride and 18‐crown‐6 as the initiator. The effect of 18‐crown‐6 is very important, and only oligomer can be obtained in the polymerization without 18‐crown‐6. The molecular structure of the hyperbranched polymers was confirmed with ¹H NMR and ¹³C NMR spectra. The ratio of initiator to monomer significantly affects the architecture of the resultant polymers. When the ratio of initiator to monomer equals 1 in the oxyanionic vinyl polymerization of HEMA, the degree of branching of the resulting polymer was calculated to be around 0.49. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3502–3509, 2005     

Magnetic poly(glycidyl methacrylate) microspheres prepared by dispersion polymerization in the presence of electrostatically stabilized ferrofluids

Fine magnetite nanoparticles, both electrostatically stabilized and nonstabilized, were synthesized in situ by precipitation of Fe(II) and Fe(III) salts in alkaline medium. Magnetic poly(glycidyl methacrylate) (PGMA) microspheres with core‐shell structure, where Fe₃O₄ is the magnetic core and PGMA is the shell, were obtained by dispersion polymerization initiated with 2,2′‐azobisisobutyronitrile (AIBN), 4,4′‐azobis(4‐cyanovaleric acid) (ACVA), or ammonium persulfate (APS) in ethanol containing poly(vinylpyrrolidone) or ethylcellulose stabilizer in the presence of iron oxide ferrofluid. The average microsphere size ranged from 100 nm to 2 μm. The effects of the nature of ferrofluid, polymerization temperature, monomer, initiator, and stabilizer concentration on the PGMA particle size and polydispersity were studied. The particles contained 2–24 wt % of iron. AIBN produced larger microspheres than APS or ACVA. Polymers encapsulating electrostatically stabilized iron oxide particles contained lower amounts of oxirane groups compared with those obtained with untreated ferrofluid. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5827–5837, 2004     

Thermosensitive behavior of poly(ethylene glycol)/poly(2‐(N,N‐dimethylamino)ethyl methacrylate) double hydrophilic block copolymers

The poly(ethylene glycol)/poly(2‐(N,N‐dimethylamino)ethyl methacrylate) (PEG/PDMAEMA) double hydrophilic block copolymers were synthesized by atom transfer radical polymerization using mPEG‐Br or Br‐PEG‐Br as macroinitiators. The narrow molecular weight distribution of PEG/PDMAEMA block copolymers was identified by gel permeation chromatography results. The thermosensitivity of PEG/PDMAEMA block copolymers in aqueous solution was revealed to depend significantly on pH, ionic strength, chain structure, and concentration of the block copolymers. By optimizing these factors, the cloud point temperature of PEG/PDMAEMA block copolymers can be limited within body temperature range (30–37 °C), which suggests that PEG/PDMAEMA block copolymers could be a good candidate for drug delivery systems. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 503–508, 2010     

Direct synthesis of amphiphilic block copolymers from glycidyl methacrylate and poly(ethylene glycol) by cationic ring‐opening polymerization and supramolecular self‐assembly thereof

Amphiphilic block copolymers composed of a hydrophilic poly(ethylene glycol) (PEG) block and a hydrophobic poly(glycidyl methacrylate) (PGMA) block were synthesized through cationic ring‐opening polymerization with PEG as the precursor. The model reactions indicated that the reactivity of the epoxy groups was higher than that of the double bonds in the bifunctional monomer glycidyl methacrylate (GMA) under the cationic polymerization conditions. Through the control of the reaction time in the synthesis of block copolymer PEG‐b‐PGMA, a linear GMA block was obtained through the ring‐opening polymerization of epoxy groups, whereas the double bond in GMA remained unreacted. The results showed that the molecular weight of the PEG precursor had little influence on the grafting of GMA, and the PGMA blocks almost kept the same length, despite the difference of the PEG blocks. In addition, the PGMA blocks only consisted of several GMA units. The obtained amphiphilic PEG‐b‐PGMA block copolymers could form polymeric core–shell micelles by direct molecular self‐assembly in water. The crosslinking of the PGMA core of the PEG‐b‐PGMA micelles, induced by ultraviolet radiation and heat instead of crosslinking agents, greatly increased the stability of the micelles. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2038–2047, 2005     

Synthesis,characterization, and biological activity of [2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate and its derivatives

A new type of methacrylate monomer, [2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate (APEMA), was synthesized. The oxime, 2,4‐dinitrophenylhydrazone, and thiosemicarbazone derivatives of poly{[2‐oxo‐2‐(4‐acetyl) phenyl amino] ethylene methacrylate} [poly(APEMA)] were prepared with hydroxylamine hydrochloride, 2,4‐dinitrophenylhydrazine, and thiosemicarbazone hydrochloride, respectively. The radical homopolymerization of APEMA was performed at 65 °C in a 1,4‐dioxane solution with benzoyl peroxide as an initiator. The monomer and its homopolymer were characterized with Fourier transform infrared and NMR techniques. The thermal stabilities of poly(APEMA) and its derivatives were investigated with thermogravimetric analysis and differential scanning calorimetry. The ultraviolet stability of the polymers were compared. The solubility and inherent viscosity of the polymers were also determined. The number‐average and weight‐average molecular weights and polydispersity index of the polymers were determined with gel permeation chromatography. The antibacterial and antifungal effects of the monomer and the polymer and its derivatives were also investigated on various bacteria and fungi. The activation energies of the thermal degradation of the polymers were calculated with the Ozawa method. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3157–3169, 2004     

Synthesis of triblock and multiblock methacrylate polymers and self‐assembly of stimuli responsive triblock polymers

Multisegmented poly(methacrylate)s were synthesized using one pot reversible addition fragmentation chain transfer polymerization. Initially, a series of triblock copolymers were synthesized with different ratios of trimethylsilyl methacrylate, di(ethylene oxide) methacrylate, and oligo(ethylene oxide) methacrylate, and different total polymer molecular weights. Additionally, a polymer containing seven distinct blocks of methacrylic monomers was synthesized in one pot. For the triblock copolymers, the trimethylsilyl group was subsequently hydrolyzed, and the self‐assembly of the triblock copolymer was studied in water, under different pH and thermal conditions. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2548–2555     

Synthesis and characterization of pyrene bearing amphiphilic miktoarm star polymer and its noncovalent interactions with multiwalled carbon nanotubes

A novel amphiphilic miktoarm star polymer, polystyrene‐poly(ethylene glycol)‐poly(methyl methacrylate), bearing a pyrene group at the end of PS arm (Pyrene‐PS‐PEG‐PMMA) was successfully synthesized via combination of atom transfer radical polymerization and click chemistry. The structure and composition of the amphiphilic miktoarm star polymer were characterized by gel permeation chromatography and ¹H NMR. The functionalization of multiwalled carbon nanotubes (MWCNTs) via “π–π” stacking interactions with pyrene‐PS‐PEG‐PMMA miktoarm star polymer was accomplished and the resulting polymer‐MWCNTs hybrid was analyzed by using ¹H NMR, UV–vis, fluorescence spectroscopy, and thermal gravimetric analysis. The high‐resolution transmission electron microscopy and analytical techniques aforementioned confirmed that the noncovalent functionalization of MWCNT's with the amphiphilic miktoarm star polymer was successfully achieved. The MWCNT/pyrene‐PS‐PEG‐PMMA exhibited significant dispersion stability in common organic solvents such as dimethyl formamide, chloroform, and tetrahydrofuran. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Nanosphere formation in copolymerization of methyl methacrylate with poly(ethylene glycol) macromonomers

Polymeric nanospheres consisting of poly(methyl methacrylate) (PMMA) cores and poly(ethylene glycol) (PEG) branches on their surfaces were prepared by free radical copolymerization of methyl methacrylate (MMA) with PEG macromonomers in ethanol/water mixed solvents. PEG macromonomers having a methacryloyl (MMA‐PEG) and p‐vinylbenzyl (St‐PEG) end group were used. It has become clear that the obtained polymer dispersions form three kinds of states, particle dispersion (milky solution), clear solution, and gel/precipitation. It was found that the reaction parameters such as MMA concentration, molecular weight, and concentration of PEG macromonomers, and water content can affect nanosphere formation in a copolymerization system. The water volume fraction of mixed ethanol/water solvents affected the particle size of the nanospheres. These differences in the formation of nanospheres were due to the solvophilic/solvophobic balance between the copolymers and solvents during the self‐assembling process of the copolymers. The sizes of nanospheres can be controlled by varying concentration of PEG macromonomer and water content in solvents. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1811–1817, 2000     

Synthesis of end‐functionalized AB copolymers. II. Synthesis and characterization of carboxyl‐terminated poly(ethylene glycol)–poly(amino acid) block copolymers

AB block copolymers composed of hydrophilic poly(ethylene glycol) (PEG) and hydrophobic poly(amino acid) with a carboxyl group at the end of PEG were synthesized with α‐carboxylic sodium‐ω‐amino‐PEG as a macroinitiator for the ring‐opening polymerization of N‐carboxy anhydride. Characterizations by ¹H NMR, IR, and gel permeation chromatography were carried out to confirm that the diblock copolymers were formed. In aqueous media this copolymer formed self‐associated polymer micelles that have a carboxyl group on the surface. The carboxyl groups located at the outer shell of the polymeric micelle were expected to combine with ligands to target specific cell populations. The diameter of the polymer micelles was in the range of 30–80 nm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3527–3536, 2004     

RAFT copolymerization of methacrylic acid and poly(ethylene glycol) methyl ether methacrylate in the presence of a hydrophobic chain transfer agent in organic solution and in water

RAFT polymerization of poly(ethylene glycol) methyl ether methacrylate (PEGMA, 1100 g mol^?1) was first performed using cyanoisopropyl dithiobenzoate (CPDB). The control of PEGMA homopolymerization, carried out in THF ([PEGMA] = 40 wt %) at 65 °C (reflux) using 2,2′‐Azobis(isobutyronitrile) (AIBN) as initiator, was shown by the linear increase of molar masses and the low polydispersity indices (PDI) observed with conversion and also by the determination of a high chain transfer constant (C_tr = 9.1) for CPDB in this system. Copolymerization of PEGMA with methacrylic acid (MAA) ([PEGMA]/[MAA] = 40/60) was then undertaken first in dioxane at 85 °C. High conversion (89%) was obtained in 3 h without any composition drift and with a good level of control (PDI < 1.40). When the polymerization was performed in water, a strong increase in polymerization rate was observed with almost quantitative conversion (98%) in 2 h without affecting the level of control of the final copolymers (PDI ～ 1.30). These last results were tentatively explained by the formation of hydrophobic domains in which the polymerization occurred as in bulk. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3045–3055, 2009     

Reversible addition–fragmentation chain transfer polymerization of glycidyl methacrylate with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate as a chain‐transfer agent

A reversible addition–fragmentation chain transfer (RAFT) agent, 2‐cyanoprop‐2‐yl 1‐dithionaphthalate (CPDN), was synthesized and applied to the RAFT polymerization of glycidyl methacrylate (GMA). The polymerization was conducted both in bulk and in a solvent with 2,2′‐azobisisobutyronitrile (AIBN) as the initiator at various temperatures. The results for both types of polymerizations showed that GMA could be polymerized in a controlled way by RAFT polymerization with CPDN as a RAFT agent; the polymerization rate was first‐order with respect to the monomer concentration, and the molecular weight increased linearly with the monomer conversion up to 96.7% at 60 °C, up to 98.9% at 80 °C in bulk, and up to 64.3% at 60 °C in a benzene solution. The polymerization rate of GMA in bulk was obviously faster than that in a benzene solution. The molecular weights obtained from gel permeation chromatography were close to the theoretical values, and the polydispersities of the polymer were relatively low up to high conversions in all cases. It was confirmed by a chain‐extension reaction that the AIBN‐initiated polymerizations of GMA with CPDN as a RAFT agent were well controlled and were consistent with the RAFT mechanism. The epoxy group remained intact in the polymers after the RAFT polymerization of GMA, as indicated by the ¹H NMR spectrum. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2558–2565, 2004     

Amphiphilic conetworks. III. Poly(2,3‐dihydroxypropyl methacrylate)–polyisobutylene and poly(ethylene glycol) methacrylate–polyisobutylene based hydrogels prepared by two‐step polymer procedure

This article describes the synthesis and characterization of new amphiphilic polymer conetworks containing hydrophilic poly(2,3‐dihydroxypropyl methacrylate) or poly(ethylene glycol) methacrylate (PEGMA) and hydrophobic polyisobutylene chains. This conetworks were prepared by a two‐step polymer synthesis. In the first step, a cationic copolymer of isobutylene and 3‐isopropenyl‐α,α‐dimethylbenzyl isocyanate (IDI) was prepared. The isocyanate groups of the IB‐IDI random copolymer were subsequently transformed in situ to methacrylate (MA) groups in reaction with 2‐hydroxyethyl methacrylate (HEMA). In the second step, the resulting MA‐multifunctional PIB‐based crosslinker, PIB(MA)_n, with an average functionality of approximately four per chain, was copolymerized with 2,3‐dihydroxypropyl methacrylate or poly(ethylene glycol) methacrylate by radical mechanism in tetrahydrofuran giving rise to amphiphilic conetworks containing 11–60 mol % of DHPMA or 10–12 mol % of PEGMA. The synthesized conetworks were characterized with solid‐state ¹³C‐NMR spectroscopy and differential scanning calorimetry. The amphiphilic nature of the conetworks was proved by swelling in both water and n‐heptane. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4074–4081, 2007     

Reverse atom transfer radical polymerization of methyl methacrylate with a new catalytic system,FeCl3/isophthalic acid

A new catalytic system, FeCl₃/isophthalic acid, was successfully used in the reverse atom transfer radical polymerization (RATRP) of methyl methacrylate (MMA) in the presence of a conventional radical initiator, 2,2′‐azo‐bis‐isobutyrontrile. Well‐defined poly(methyl methacrylate) (PMMA) was synthesized in an N,N‐dimethylformamide solvent at 90–120 °C. The polymerization was controlled up to a molecular weight of 50,000, and the polydispersity index was 1.4. Chain extension was performed to confirm the living nature of the polymer. The kinetics of the RATRP of MMA with FeCl₃/isophthalic acid as the catalyst system was investigated. The apparent activation energy was 10.47 kcal/mol. The presence of the end chloride atom on the resulting PMMA was demonstrated by ¹H NMR spectroscopy. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 765–774, 2001     

Free‐radical polymerization of methyl methacrylate with a tetrafunctional peroxide initiator

This study examined the use of a new tetrafunctional peroxide initiator in the bulk free‐radical polymerization of methyl methacrylate. The objective was to investigate the effect of using a multifunctional initiator through an examination of the rates of polymerization and the polymer properties. The molecular weights and radii of gyration were obtained with a size exclusion chromatograph equipped with an online multi‐angle laser light scattering detector. The performance of the tetrafunctional initiator was compared to that of a monofunctional counterpart [tert‐butylperoxy 2‐ethylhexyl carbonate (TBEC)]. The results showed that the new tetrafunctional peroxide initiator produced a faster rate of polymerization than TBEC at an equivalent concentration but also generated a polymer of a lower molecular weight. This trend was the opposite of what was observed in a previous study with styrene. When TBEC was used at a concentration four times that of the new tetrafunctional peroxide initiator, both produced equal rates of polymerization and similar molecular weights. The degree of branching was also investigated with radius‐of‐gyration plots. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5647–5661, 2004     

Segmented block copolymers of poly(ethylene glycol) and poly(ethylene terephthalate)

A new series of segmented copolymers were synthesized from poly(ethylene terephthalate) (PET) oligomers and poly(ethylene glycol) (PEG) by a two‐step solution polymerization reaction. PET oligomers were obtained by glycolysis depolymerization. Structural features were defined by infrared and nuclear magnetic resonance (NMR) spectroscopy. The copolymer composition was calculated via ¹H NMR spectroscopy. The content of soft PEG segments was higher than that of hard PET segments. A single glass‐transition temperature was detected for all the synthesized segmented copolymers. This observation was found to be independent of the initial PET‐to‐PEG molar ratio. The molar masses of the copolymers were determined by gel permeation chromatography (GPC). © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4448–4457, 2004     

Synthesis of densely branched poly(methyl methacrylate)s via ATR copolymerization of methyl methacrylate and ethylene glycol dimethacrylate

Densely branched poly(methyl methacrylate)s have been synthesized by copolymerization of methyl methacrylate (MMA) and ethylene glycol dimethacrylate (EGDMA) using atom transfer free radical polymerization (ATRP). By employing the phenyl and benzyl esters of 2-bromo-2-methylpropionic acid as the initiators with 2,2-bipyridyl and Cu(I)Cl it has been possible to use high field ¹H nuclear magnetic resonance spectroscopy to evaluate in some detail the composition and structure of the branched PMMAs obtained. Parallel molar mass size exclusion chromatographic analysis using a multi-angle light scattering detector with a refractive index detector (MALS/SEC) has allowed the branched architecture of the products to be confirmed. Rather remarkably, high yields of branched PMMAs can be obtained without crosslinking using MMA/EGDMA molar feed ratios of up to 5/1 by appropriate adjustment of the molar feed of initiator. In particular by maintaining the EGDMA/initiator molar feed ratio ∼1/1 fully soluble products can be obtained that are densely branched since this feed ratio ensures that on average each living primary chain initiated contains on average only one branching EGDMA segment. As might be expected this controlled free radical process offers better control in the synthesis of branched polymer than the corresponding system we have reported using conventional free radical polymerization, and unlike the latter which requires the use of a chain transfer agent, the ATRP system requires no additional chain regulating component. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2375–2386, 2007     

Synthesis and characterization of spherical and hemispherical polyepoxide micrometer‐sized particles of narrow size distribution by a single‐step swelling of uniform polystyrene template microspheres with glycidyl methacrylate

Polystyrene template microspheres of narrow size distribution were prepared by dispersion polymerization of styrene in a mixture of ethanol and 2‐methoxy ethanol. Spherical and hemispherical polystyrene/poly(glycidyl methacrylate) microspheres of narrow size distribution were prepared by a single‐step swelling of the polystyrene template microspheres with the swelling solvent monomer glycidyl methacylate, followed by polymerization of the monomer within the swollen template microspheres at 73 °C. Uniform polystyrene/poly(glycidyl methacylate‐ethylene glycol dimethacrylate) polyepoxide composite microspheres were synthesized similarly, substituting glycidyl methacylate for glycidyl methacylate and ethylene glycol dimethacrylate. Uniform crosslinked poly(glycidyl methacylate‐ethylene glycol dimethacrylate) polyepoxide microspheres have been prepared by dissolution of the PS template polymer of the former composite microspheres. Particles with different properties, for example size, size distribution, shape, surface morphology, surface area, and so forth, were prepared by changing various parameters belonging to the swelling and/or polymerization steps, for example, volume of the swelling monomer/s and/or the swelling solvent dibutyl phthalate. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4612–4622, 2007     

Syntheses and characterization of statistical and block fluorinated copolymers with linear and star-like architectures via ATRP

The synthesis of a fluorinated macroinitiator for copper-catalyzed atom transfer radical polymerization (ATRP) is reported, as well as its use for the controlled living polymerization of poly(propylene glycol) methacrylate (PPGM) in MEK at 80 °C. The ATRP system used was efficient for polymerization of the functionalized monomer and the molecular weight of the polymer estimated by NMR spectroscopy was in close agreement with the theoretical molecular weight, as expected for controlled processes. The statistical copolymerization of PPGM or methyl ether poly(ethylene glycol) methacrylate (MPEGMA) with a perfluoroalkyl ethyl methacrylate by copper-mediated ATRP was also investigated and led to copolymers with essentially random incorporation of monomers. The syntheses and characterization of star-like homopolymers of MPEGMA or the fluorinated monomer via ATRP are also reported, as well as an amphiphilic star-like block copolymer containing ethyleneglycol units as the core and fluorinated moieties in the shell. The micellar behavior of this copolymer was investigated as a function of the external environment.