Excitation energy dependent chromaticity of BaZr(BO3)2:Eu

The luminescence properties of BaZr(BO₃)₂:5% Eu were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) excitation and different luminescence behaviors were observed by different excitation energies. After the analyses of the luminescence spectra, the result indicates that Eu³⁺ occupying non-centrosymmetric sites Ba²⁺ can be excited preferentially under 254 nm excitation, while Eu³⁺ occupying centrosymmetric sites Zr⁴⁺ can be excited preferentially under 147 nm excitation.     

Luminescent properties of (Y,Gd)BO3:Bi,RE (RE=Eu, Tb) phosphor under VUV/UV excitation

Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors were prepared and their luminescent properties under vacuum ultraviolet (VUV)/UV excitation were investigated. Strong red emission for (Y,Gd)BO₃:Bi³⁺,Eu³⁺ and strong green emission for (Y,Gd)BO₃:Bi³⁺,Tb³⁺ are observed under VUV excitation from 147 to 200 nm with a much broader excitation region than that of single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃ phosphor. Strong emissions are also observed under UV excitation around 265 nm where as nearly no luminescence is observed for single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃. The luminescence enhancement of Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors is due to energy transfer from Bi³⁺ ion to Eu³⁺ or Tb³⁺ ion not only in the VUV region but also in the UV region. Besides, host sensitization competition between Bi³⁺ and Eu³⁺ or Tb³⁺ is also observed. The investigated phosphors may be preferable for devices with a VUV light 147-200 nm as an excitation source such as PDP or mercury-free fluorescent lamp.     

New red phosphors BaZr(BO3)2 and SrAl2B2O7 doped with Eu for PDP applications

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) characteristics of Eu³⁺ ion doped borate phosphors; BaZr(BO₃)₂:Eu³⁺ and SrAl₂B₂O₇:Eu³⁺ are studied. The excitation spectra show strong absorption in the VUV region with the absorption band edge at ca. 200 nm for BaZr(BO₃)₂:Eu³⁺ and 183 nm for SrAl₂B₂O₇:Eu³⁺, respectively, which ensures the efficient absorption of the Xe plasma emission lines. In BaZr(BO₃)₂:Eu³⁺, the charge transfer band of Eu³⁺ does not appear strongly in the excitation spectrum, which can be enhanced by co-doping Al³⁺ ion into the BaZr(BO₃)₂ lattices. The luminescence intensity of BaZr(BO₃)₂:Eu³⁺ is also increased by Al³⁺ incorporation into the lattices. The PL spectra show the strongest emission at 615 nm corresponding to the electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺ in both BaZr(BO₃)₂ and SrAl₂B₂O₇, similar to that in YAl₃(BO₃)₄, which results in a good color purity for display applications.     

Synthesis and luminescence properties of Eu, Ce and Tb-activated Sr3La2(BO3)4 under UV excitation

The spectroscopic properties in UV-excitable range for the phosphors of Sr₃La₂(BO₃)₄:RE³⁺ (RE³⁺=Eu³⁺, Ce³⁺, Tb³⁺) were investigated. The phosphors were synthesized by conventional solid-state reactions. The photoluminescence (PL) spectra and commission international de I'Eclairage (CIE) coordinates of Sr₃La₂(BO₃)₄:RE³⁺ were investigated. The f-d transitions of Eu³⁺, Ce³⁺ and Tb³⁺ in the host lattices are assumed and corroborated. The PL and PL excitation (PLE) spectra indicate that the main emission wavelength of Sr₃La₂(BO₃)₄:Eu³⁺ is 611 nm, and Sr₃La₂(BO₃)₄:Ce³⁺ shows dominating emission peak at 425 nm, while Sr₃La₂(BO₃)₄:Tb³⁺ displays green emission at 487, 542, 582 and 620 nm. These phosphors were prepared by simple solid-state reaction at 1000 °C. There are lower reactive temperature and more convenient than commercial phosphors. The Sr₃La₂(BO₃)₄:Tb³⁺ applied to cold cathode fluorescent lamp was found to emit green light and have a major peak wavelength at around 542 nm. These phosphors may provide a new kind of luminescent materials under ultraviolet excitation.     

Eu-activated Ba2Mg(BO3)2 yellow-emitting phosphors for near ultraviolet-based light-emitting diodes

A series of Eu²⁺-activated Ba₂Mg(BO₃)₂ yellow phosphors were prepared by a high temperature solid-state reaction. The phosphor emits intense yellow light under near ultraviolet excitation. Large Stokes shift can be attributed to the asymmetric nature of the Eu site and the lack of rigidity in the host. The concentration self-quenching mechanism of Ba₂Mg(BO₃)₂:Eu²⁺ is d-d interaction and the critical transfer distance is calculated to be about 12.29 Å. Prototype light-emitting diodes were fabricated by coating the Ba₂Mg(BO₃)₂:0.07Eu²⁺ phosphor onto ∼370 nm-emitting InGaN chips. The LEDs exhibit intense yellow-emitting under a forward bias of 20 mA. The results indicate that Eu²⁺-activated Ba₂Mg(BO₃)₂ is a candidate as a yellow component for fabrication of near-UV white light-emitting diodes.     

Photoluminescence properties of Eu in Y(PO3)3 under VUV excitation

The photoluminescence properties of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) are investigated. The excitation spectrum of Y_0.85(PO₃)₃:0.15Eu₃⁺ shows that both the (PO₃)₃³⁻ groups and the CT bands of O²⁻-Y³⁺ can efficiently absorb the excitation energy in the region of 120-250 nm. Under 147 nm excitation, the optimal emissive intensity of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) is about 36% of the commercial phosphor (Y,Gd)BO₃:Eu³⁺, which hints that the absorbed energy by the host matrix could be efficiently transferred to Eu³⁺. We try to study the concentration quenching mechanism of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) under 147 and 172 nm excitation.     

Luminescence of Ce and Pr doped Sr2Mg(BO3)2 under VUV-UV and X-ray excitation

This report presents the luminescence properties of Ce³⁺ and Pr³⁺ activated Sr₂Mg(BO₃)₂ under VUV-UV and X-ray excitation. The five excitation bands of crystal field split 5d states are observed at about 46 729, 44 643, 41 667, 38 314 and 29 762 cm⁻¹ (i.e. 214, 224, 240, 261 and 336 nm) for Ce³⁺ in the host lattice. The doublet Ce³⁺ 5d→4f emission bands were found at about 25 840 and 24 096 cm⁻¹ (387 and 415 nm). The influence of doping concentration and temperature on the emission characteristics and the decay time of Ce³⁺ in Sr₂Mg(BO₃)₂ were investigated. For Pr³⁺ doped samples, the lowest 5d excitation band was observed at about 42017 cm⁻¹ (238 nm), a dominant band at around 35714 cm⁻¹ (280 nm) and two shoulder bands were seen in the emission spectra. The excitation and emission spectra of Ce³⁺ and Pr³⁺ were compared and discussed. The X-ray excited luminescence studies show that the light yields are ∼3200±230 and ∼1400±100 photons/MeV of absorbed X-ray energy for the samples Sr_1.86Ce_0.07Na_0.07Mg(BO₃)₂ and Sr_1.82Pr_0.09Na_0.09Mg(BO₃)₂ at RT, respectively.     

Photoluminescence properties of Sr(Y, Gd)2O4:Euunder VUV excitation

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) properties of Sr(Y, Gd)₂O₄ doped with Eu³⁺ were studied. The excitation spectra of SrY_1.9Eu_0.1O₄ and SrY_1.0Gd_0.9Eu_0.1O₄ had absorption in the VUV region with the absorption band edge at 149 nm, while the absorption of SrGd_1.9Eu_0.1O₄ in the VUV region was weak, which could be due to the narrow host band gap and no efficient energy transfer occurred in the VUV region. The PL spectra of all samples exhibited the characteristic emission of Eu³⁺ with the red ⁵D₀-⁷F₂ transition (611 nm) being the most prominent group.     

VUV sensitisation of Eu emission by Tb in Ba3Tb(PO4)3-Eu

The luminescence properties of Ba₃Tb_0.9Eu_0.1(PO₄)₃ and Ba₃Gd_0.9Eu_0.1(PO₄)₃ phosphors were studied for excitation over the 120-300 nm wavelength range. It is found that Tb³⁺, which exhibits a strong vacuum-ultraviolet (VUV) absorption band, provides sensitisation of Eu³⁺ emission in this host. This effect can be used to develop phosphors with enhanced conversion efficiency of the VUV radiation into visible light.     

Synthesis of Y2Si2O7:Eu nanocrystal and its optical properties

Nanocrystalline Y₂Si₂O₇:Eu phosphor with an average size about 60 nm is easily prepared using silica aerogel as raw material under ultrasonic irradiation and annealing temperature at 300-600 °C and this nanocrystalline decomposes into Y₂O₃:Eu and silica by heat treatment at 700-900 °C. The excitation broad band centered at 283 and 254 nm results from Eu³⁺ substituting for Y³⁺ in Y₂Si₂O₇ and Y₂O₃/SiO₂, respectively. Compared with Y₂O₃:Eu/SiO₂ crystalline, the PL excitation and emission peaks of Y₂Si₂O₇:Eu nanocrystalline red-shift and lead to the enhance of its luminescence intensity due to the different chemical surroundings of Eu³⁺ in above nanocrystallines. The decrease of PL intensity may be ascribed to quenching effect resulting from more defects in Y₂O₃:Eu/SiO₂ crystalline.     

Investigation of host-to-activator energy transfer and surface losses in SrY2O4:Eu under VUV excitation

We have completed a study of the optical properties of SrY₂O₄:Eu³⁺ under vacuum ultraviolet (VUV) excitation. Reflectance measurements on the undoped material yield a calculated band gap of about 6.1 eV. Studies on the doped material indicate that Eu³⁺ occupies the Y(1) and Y(2) sites in this host. Host-to-activator energy transfer calculations indicate a preference for transfer to Eu³⁺ at the Y(2) site. Modeling of the transfer efficiency data leads us to estimate that about 35% of absorbed radiation is lost to the surface under excitation near the band edge.     

Effect of concentration on the luminescence of Eu ions in nanocrystalline La2O3

Nanocrystalline powders with various Eu³⁺ concentration (from 1 to 10 mol %) doped La₂O₃ were prepared via a combustion route. Their structure and morphology were characterized using X-ray diffraction (XRD) and High-resolution transmission electron microscopy. The emission spectra of the as-synthesized samples show that the strongest emission position is centered at 626 nm corresponding to ⁵D₀→⁷F₂ transition of Eu³⁺ ions and the intensity change of 626 nm emission is considered as a function of ultraviolet (240 nm) irradiation time. The excitation spectra at 626 nm monitoring indicate that the charge transfer state band is varies with different Eu³⁺ ion concentration. These results are attributed to the surface defects of the nanocrystals.     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.     

Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.     

Preparation and luminescent properties of cubic Eu:Y2O3 nanocrystals and comparison to bulk Eu:Y2O3

Y₂O₃:Eu³⁺ nanocrystals were prepared by combustion synthesis. The particle size estimated by X-ray powder diffraction (XRD) was about 10 nm. A blue-shift of the charge-transfer (CT) band in excitation spectra was observed in Y₂O₃:Eu³⁺ nanocrystals compared with bulk Y₂O₃:Eu³⁺. The electronic structure of Y₂O₃ is calculated by density functional method and exchange and correlation have been treated by the generalized gradient approximation (GGA) within the scheme due to Perdew-Burke-Ernzerhof (PBE). The calculated results show that the energy centroid of 5d orbital in nanocrystal has increasing trend compared with that in the bulk material. The bond length and bond covalency are calculated by chemical bond theory. The bond lengths of Y₂O₃:Eu³⁺ nanocrystal are shorter than those of the bulk counterpart and the bond covalency of Y₂O₃:Eu³⁺ nanocrystal also has an increasing trend. By combining centroid shift and crystal-field splitting, the blue-shift of the CT band is interpreted.     

Luminescent properties of RE-activated CaAl2B2O7 (RE=Tb, Ce) in VUV-visible region

RE³⁺-activated α- and β-CaAl₂B₂O₇ (RE=Tb, Ce) were synthesized with the method of high-temperature solid-state reaction. Their VUV excitation and VUV-excited emission spectra are measured and discussed in the present article. The charge transfer band of Tb³⁺ and Ce³⁺ is respectively calculated to be at 151±2 and 159±3 nm. All the samples show an activator-independent excitation peak at about 175 nm and an emission peak at 350-360 nm ascribed to the host absorption and emission band, respectively.     

Luminescence characteristics of Eu3+ activated borate phosphor for white light emitting diode

In this paper, the Sr₃Y₂ (BO₃)₄:Eu³⁺ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613nm corresponding to the electric dipole ⁵D₀--⁷F₂ transition of Eu³⁺ under 365nm excitation, this is because Eu³⁺ substituted for Y³⁺ occupied the non-centrosymmetric position in the crystal structure of Sr₃Y₂ (BO₃)₄. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet (254nm, 365nm and 400nm) and blue (470nm) light. The effect of Eu³⁺ concentration on the red emission of Sr₃Y₂ (BO₃)₄:Eu³⁺ was measured, the result shows that the emission intensities increase with increasing Eu³⁺ concentration, then decrease. The Commission Internationale del'Eclairage chromaticity (x, y) of Sr₃Y₂(BO₃)₄:Eu³⁺ phosphor is (0.640,0.355) at 15 mol% Eu³⁺.     

Luminescence properties of novel NaBa4(BO3)3:Ce, Eu phosphors

Novel Eu³⁺, Ce³⁺ activated NaBa₄(BO₃)₃ phosphors were synthesized by solid-state reactions. The excitation spectrum of NaBa₄(BO₃)₃:Ce³⁺ consists of an intense band peaking at 350 nm and a weak band in the higher energy side, and the emission spectrum exhibits a blue band with a maximum at about 420 nm. The Eu³⁺ emission in NaBa₄(BO₃)₃ consists of the transitions from ⁵D₀ to ⁷F_J, and the excitation spectrum consists of broad excitation band peaking at 270 nm and some intense narrow lines. The optimum doped concentration, the critical distance of the concentration quenching, and the fluorescence lifetime have also been investigated.     

Characterization of host-lattice emission and energy transfer in BaMgAl10O17:Eu

Host-lattice emission, energy transfer and degradation processes are characterized in undoped and Eu-doped BaMgAl₁₀O₁₇. Undoped BaMgAl₁₀O₁₇ exhibits a broad emission centered at 265 nm when excited at wavelengths shorter than 190 nm. This emission is assigned to exciton recombination at Ba-O groups in the cation layer of the lattice. The emission exhibits excellent overlap with the excitation band of Eu²⁺ in this host, providing a means of host-to-activator energy transfer in the doped phosphor. The exciton emission is relatively stable to thermal damage, but undergoes a peak shift and significant decrease in intensity after exposure to VUV radiation. Heating of VUV-damaged materials in air leads to some repair of the spectral properties.     

The luminescent properties of CaYBO4:Ln(Ln=Eu, Tb) under UV-VUV range

The luminescent properties of CaYBO₄:Ln(Ln=Eu³⁺, Tb³⁺) were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) region. The CT band of Eu³⁺ at about 245 nm blue-shifted to 230 nm in VUV excitation spectrum; the band with the maximum at 183 nm was considered as the host lattice absorption. For the sample of CaYBO₄:0.08Tb³⁺, the bands at about 235 and 263 nm were assigned to the f-d transitions of Tb³⁺ and the CT band of Tb³⁺ was calculated according to Jφrgensen's theory. Under UV and VUV excitation, the main emission of Eu³⁺ corresponding to the ⁵D₀-⁷F₂ transition located at about 610 nm and two intense emission of Tb³⁺ from the ⁵D₄-⁷F₅ transition had been observed at about 542 and 552 nm, respectively. With the incorporation of Gd³⁺ into the host lattice of CaYBO₄, the luminescence of Tb³⁺ was enhanced while that of Eu³⁺ was decreased because of their different excitation mechanism.