Solid polymer electrolytes based on polystyrene‐polyether block copolymers having branched ether structure

To obtain solid polymer electrolytes (SPEs) having high ionic conductivity together with mechanical integrity, we have synthesized polystyrene (PSt)‐polyether (PE) diblock copolymers via one‐pot anionic polymerization. The PSt block is expected to aggregate to act as hard fillers in the SPE to enhance the mechanical property. The PE block consists of random copolymer (P(EO‐r‐MEEGE)) of ethylene oxide (EO) and 2‐(2‐methoxyethoxy) ethyl glycidyl ether (MEEGE) in different molar ratios ([EO]/[MEEGE] = 100/0, 86/14, 75/25, 68/32, and 41/59). The introduction of the MEEGE moiety in PEO reduced the crystallinity of PEO, and the fast motion of the MEEGE side chain caused plasticization of the PE block, thereby contributing to the fast ion transport. SPEs were fabricated by mixing the obtained diblock copolymer (PSE_x) and lithium bis(trifluoromethanesulfonyl) amide (LiTFSA) with [Li]/[O] = 0.05. Ionic conductivity of the obtained SPEs was dependent on the molar ratio of EO in the PE block (x) as well as the weight fraction of PE block (f_PE) in the block copolymer. PSE_0.86 (f_PE = 0.65) exhibited high ionic conductivity (3.3 × 10^?5 S cm^?1 at 30°C; 1.1 × 10^?4 S cm^?1 at 60°C) comparable with that of P(EO‐r‐MEEGE) (PE_0.85; f_PE = 1.00) (9.8 × 10^?5 S cm^?1 at 30°C; 4.0 × 10^?4 S cm^?1 at 60°C).     

Thermoresponsive PPEGMEA‐g‐PPEGEEMA well‐defined double hydrophilic graft copolymer synthesized by successive SET‐LRP and ATRP

A series of well‐defined double hydrophilic graft copolymers containing poly[poly(ethylene glycol) methyl ether acrylate] (PPEGMEA) backbone and poly[poly(ethylene glycol) ethyl ether methacrylate] (PPEGEEMA) side chains were synthesized by the combination of single electron transfer‐living radical polymerization (SET‐LRP) and atom transfer radical polymerization (ATRP). The backbone was first prepared by SET‐LRP of poly(ethylene glycol) methyl ether acrylate macromonomer using CuBr/tris(2‐(dimethylamino)ethyl)amine as catalytic system. The obtained comb copolymer was treated with lithium diisopropylamide and 2‐bromoisobutyryl bromide to give PPEGMEA‐Br macroinitiator. Finally, PPEGMEA‐g‐PPEGEEMA graft copolymers were synthesized by ATRP of poly(ethylene glycol) ethyl ether methacrylate macromonomer using PPEGMEA‐Br macroinitiator via the grafting‐from route. The molecular weights of both the backbone and the side chains were controllable and the molecular weight distributions kept narrow (M_w/M_n ≤ 1.20). This kind of double hydrophilic copolymer was found to be stimuli‐responsive to both temperature and ion (0.3 M Cl^? and SO). © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 647–655, 2010     

Synthesis and properties of all solid polymer electrolytes based on poly(vinyl acetate‐co‐acetyl ethylene oxide acrylate)

Poly(acetyl ethylene oxide acrylate‐co‐vinyl acetate) (P(AEOA‐VAc)) was synthesized and used as a host for lithium perchlorate to prepare an all solid polymer electrolyte. Introduction of carbonyl groups into the copolymer increased ionic conductivity. All solid polymer electrolytes based on P(AEOA‐VAc) at 14.3 wt% VAc with 12wt% LiClO₄ showed conductivity as high as 1.2 × 10^?4 S cm^?1 at room temperature. The temperature dependence of the ionic conductivity followed the VTF behavior, indicating that the ion transport was related to segmental movement of the polymer. FTIR was used to investigate the effect of the carbonyl group on ionic conductivity. The interaction between the lithium salt and carbonyl groups accelerated the dissociation of the lithium salt and thus resulted in a maximum ionic conductivity at a salt concentration higher than pure PAEO‐salts system. Copyright © 2010 John Wiley & Sons, Ltd.     

Synthesis of well‐defined pH‐responsive PPEGMEA‐g‐P2VP double hydrophilic graft copolymer via sequential SET‐LRP and ATRP

A series of well‐defined double hydrophilic graft copolymers containing poly(poly(ethylene glycol) methyl ether acrylate) (PPEGMEA) backbone and poly(2‐vinylpyridine) (P2VP) side chains were synthesized by successive single electron transfer living radical polymerization (SET‐LRP) and atom transfer radical polymerization (ATRP). The backbone was first prepared by SET‐LRP of poly(ethylene glycol) methyl ether acrylate (PEGMEA) macromonomer using CuBr/tris(2‐(dimethylamino)ethyl)amine as catalytic system. The obtained homopolymer then reacted with lithium diisopropylamide and 2‐chloropropionyl chloride at ?78 °C to afford PPEGMEA‐Cl macroinitiator. poly(poly(ethylene glycol) methyl ether acrylate)‐g‐poly(2‐vinylpyridine) double hydrophilic graft copolymers were finally synthesized by. ATRP of 2‐vinylpyridine initiated by PPEGMEA‐Cl macroinitiator at 25 °C using CuCl/hexamethyldiethylenetriamine as catalytic system via the grafting‐ from strategy. The molecular weights of both the backbone and the side chains were controllable and the molecular weight distributions kept relatively narrow (M_w/M_n ≤ 1.40). pH‐Responsive micellization behavior was investigated by ¹H NMR, dynamic light scattering, and transmission electron microscopy and this kind of double hydrophilic graft copolymer aggregated to form micelles with P2VP‐core while pH of the aqueous solution was above 5.0. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis of ultra‐high‐molecular‐weight ethylene‐propylene copolymer via quasi‐living copolymerization with N‐heterocyclic carbene ligated vanadium complexes

The quasi‐living copolymerization of ethylene with propylene was achieved by using N‐heterocyclic carbene (NHC) ligated vanadium complex ( V3 , VOCl₃[1,3‐(2,6‐ⁱPr₂C₆H₃)₂(NCH?)₂C:]) due to the stabilization of active center by the introduction of bulky and electron rich NHC ligand with bulky isopropyl substituents at the ortho positions of the phenyl rings. The weight‐average molecular weight (M_w) of the resulting copolymer increases linearly with its weight in 20 min. The ultra‐high‐molecular‐weight (UHMW) ethylene‐propylene copolymer (M_w = 1612 kg mol^?1) can be synthesized with V3 /Et₃Al₂Cl₃ catalytic system. The novel complex V4′ (VCl₃[1,3‐(2,4,6‐Me₃C₆H₂)₂(NCH?)₂C:]·2THF) was constructed by the introduction of two coordinated tetrahydrofuran molecules and decrease in steric hindrance at the ortho positions of phenyl rings. The UHMW ethylene‐propylene copolymer (M_w = 1167 kg mol^?1) can also be synthesized by using V4′ /Et₃Al₂Cl₃ catalytic system. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 553–561     

Solid Polymer Electrolyte Based on Pluronic P123 Triblock Copolymer‐Siloxane Organic‐Inorganic Hybrid

A novel organic‐inorganic hybrid electrolyte based on poly(ethylene oxide)‐poly(propylene oxide)‐poly(ethylene oxide) triblock copolymer (Pluronic P123) complexed with LiClO₄ via the co‐condensation of an epoxy trialkoxysilane and tetraethylorthosilicate was prepared. Characterization was made by a variety of techniques including powder X‐ray diffraction, AC impedance, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and multinuclear solid state NMR measurements. The hybrid with [O]/[Li] = 16 exhibited a mesophase with a certain degree of ordering, which arose by the self‐assembly of P123 with the silica network. The P123 triblock copolymer acts as a structure‐directing surfactant to organize with silica networks and as a polymer matrix to dissolve alkali lithium salts as well. The DSC results indicated the formation of transient crosslinking between Li⁺ ions and the ether oxygens of the EO and PO segments, resulting in an increase the T_g with increasing salt concentrations. Variable temperature ⁷Li‐{¹H} MAS NMR spectra revealed the presence of two different local environments for lithium cations, probably due to the lithium cations in the polymer‐rich domain and in the silica‐rich domain, respectively. A combination of XRD and conductivity results suggests that the drastically enhanced conductivity for the ordered hybrid electrolyte is closely related to the formation of mesophase, which may provide unique Li⁺ conducting pathways.     

Salt‐induced microphase separation of amorphous dendritic poly(ethylene oxide)‐block‐linear polystyrene copolymers

We prepared two block copolymers 1 and 2 consisting of a third‐generation dendron with poly(ethylene oxide) (PEO) peripheries and a linear polystyrene (PS) coil. The PS molecular weights were 2000 g/mol and 8000 g/mol for 1 and 2 , respectively. The differential scanning calorimetry (DSC) data indicated that neither of the block copolymers showed glass transition, implying that there was no microphase separation between the PEO and PS blocks. However, upon doping the block copolymers with lithium triflate (lithium concentration per ethylene oxide unit = 0.2), two distinct glass transitions were seen, corresponding to the salt‐doped PEO and PS blocks, respectively. The morphological analysis using small angle X‐ray scattering (SAXS) and transmission electron microscopy (TEM) demonstrated that a hexagonal columnar morphology was induced in salt‐doped sample 1‐Li⁺ , whereas the other sample ( 2‐Li⁺ ) with a longer PS coil revealed a lamellar structure. In particular, in the SAXS data of 2‐Li⁺ , an abrupt reduction in the lamellar thickness was observed near the PS glass transition temperature (T_g), in contrast to the SAXS data for 1‐Li⁺ . This reduction implies that there is a lateral expansion of the molecular section in the lamellar structure, which can be interpreted by the conformational energy stabilization of the long PS coil above T_g. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2372–2376, 2010     

Synthesis of four‐armed poly(ε‐caprolactone)‐block‐poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four‐armed poly(?‐caprolactone)‐block‐poly(ethylene oxide) (PCL‐b‐PEO) copolymers were synthesized by ring‐opening polymerization of ethylene oxide in the presence of four‐armed poly(?‐caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt₂) as a catalyst. The chemical structure of PCL‐b‐PEO copolymer was confirmed by ¹H NMR and ¹³C NMR. The hydroxyl end groups of the four‐armed PCL were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four‐armed architecture of the copolymer. Physicochemical properties of the four‐armed block copolymers differed from their starting four‐armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four‐armed block copolymer increased with PEO length and PEO content. The micelle formation of the four‐armed block copolymer was examined by a fluorescent probe technique, and the existence of the critical micelle concentration (cmc) confirmed the amphiphilic nature of the resulting copolymer. The cmc value increased with increasing PEO length. The absolute cmc values were higher than those for linear amphiphilic block copolymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 950–959, 2004     

PPEGMEA‐g‐PDEAEMA: Double hydrophilic double‐grafted copolymer stimuli‐responsive to both pH and salinity

A series of well‐defined double hydrophilic double‐grafted copolymers, consisting of polyacrylate backbone, hydrophilic poly(2‐(diethylamino)ethyl methacrylate) and poly(ethylene glycol) side chains, were synthesized by successive atom transfer radical polymerization. The backbone, poly[poly(ethylene glycol) methyl ether acrylate] (PPEGMEA) comb copolymer, was firstly prepared by ATRP of PEGMEA macromonomer via the grafting‐through route followed by reacting with lithium diisopropylamide and 2‐bromopropionyl chloride to give PPEGMEA‐Br macroinitiator of ATRP. Finally, poly[poly(ethylene glycol) methyl ether acrylate]‐g‐poly(2‐(diethylamino)ethyl methacrylate) graft copolymers were synthesized by ATRP of 2‐(diethylamino)ethyl methacrylate using PPEGMEA‐Br macroinitiator via the grafting‐from route. Poly(2‐(diethylamino)ethyl methacrylate) side chains were connected to polyacrylate backbone through stable C? C bonds instead of ester connections, which is tolerant of both acidic and basic environment. The molecular weights of both backbone and side chains were controllable and the molecular weight distributions kept relatively narrow (M_w/M_n ≤ 1.39). The results of fluorescence spectroscopy, dynamic laser light scattering and transmission electron microscopy showed this double hydrophilic copolymer was stimuli‐responsive to both pH and salinity. It can aggregate to form reversible micelles in basic surroundings which can be conveniently dissociated with the addition of salt at room temperature. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3142–3153, 2009     

Double hydrophilic block copolymers of sodium(2‐sulfamate‐3‐carboxylate)isoprene and ethylene oxide

Poly(sodium(2‐sulfamate‐3‐carboxylate)isoprene)‐b‐poly(ethylene oxide) and poly(ethylene oxide)‐b‐poly(sodium(2‐sulfamate‐1‐carboxylate)isoprene)‐b‐poly(ethylene oxide) double hydrophilic block copolymers were prepared by selective post polymerization reaction of the polyisoprene block, of poly(isoprene‐b‐ethylene oxide) diblocks or poly(ethylene oxide‐b‐isoprene‐b‐ethylene oxide) triblock precursors, with N‐chlorosulfonyl isocyanate. The precursors were synthesized by anionic polymerization high vacuum techniques and had narrow molecular weight distributions and predictable molecular weights and compositions. The resulting double hydrophilic block copolymers were characterized by FTIR and potentiometric titrations in terms of the incorporated functional groups. Their properties in aqueous solutions were studied by viscometry and dynamic light scattering. The latter techniques revealed a complex dilute solution behavior of the novel block copolymers, resulting from the polyelectrolyte character of the functionalized PI block and showing a dependence on solution ionic strength and pH. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 606–613, 2006     

Synthesis of new amphiphilic diblock copolymers containing poly(ethylene oxide) and poly(α‐olefin)

This article discusses an effective route to prepare amphiphilic diblock copolymers containing a poly(ethylene oxide) block and a polyolefin block that includes semicrystalline thermoplastics, such as polyethylene and syndiotactic polystyrene (s‐PS), and elastomers, such as poly(ethylene‐co‐1‐octene) and poly(ethylene‐co‐styrene) random copolymers. The broad choice of polyolefin blocks provides the amphiphilic copolymers with a wide range of thermal properties from high melting temperature ～270 °C to low glass‐transition temperature ～?60 °C. The chemistry involves two reaction steps, including the preparation of a borane group‐terminated polyolefin by the combination of a metallocene catalyst and a borane chain‐transfer agent as well as the interconversion of a borane terminal group to an anionic (? O^?K⁺) terminal group for the subsequent ring‐opening polymerization of ethylene oxide. The overall reaction process resembles a transformation from the metallocene polymerization of α‐olefins to the ring‐opening polymerization of ethylene oxide. The well‐defined reaction mechanisms in both steps provide the diblock copolymer with controlled molecular structure in terms of composition, molecular weight, moderate molecular weight distribution (M_w/M_n < 2.5), and absence of homopolymer. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3416–3425, 2002     

Tuning amphiphilicity/temperature‐induced self‐assembly and in‐situ disulfide crosslinking of reduction‐responsive block copolymers

New poly(ethylene oxide)‐based block copolymers (ssBCs) with a random copolymer block consisting of a reduction‐responsive disulfide‐labeled methacrylate (HMssEt) and a thermoresponsive di(ethylene glycol)‐containing methacrylate (MEO₂MA) units were synthesized. The ratio of HMssEt/MEO₂MA units in the random P(MEO₂MA‐co‐HMssEt) copolymer block enables the characteristics of well‐defined ssBCs to be amphiphilic or thermoresponsive and double hydrophilic. Their amphiphilicity or temperature‐induced self‐assembly results in nanoaggregates with hydrophobic cores having different densities of pendant disulfide linkages. The effect of disulfide crosslinking density on morphological variation of disulfide‐crosslinked nanogels is investigated. In response to reductive reactions, the partial cleavage of pendant disulfide linkages in the hydrophobic cores converts the physically associated aggregates to disulfide‐crosslinked nanogels. The occurrence of in‐situ disulfide crosslinks provides colloidal stability upon dilution. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2057–2067     

Well‐defined glycopolymer amphiphiles for liquid and supercritical carbon dioxide applications

Well‐defined D ‐glucose‐containing glycopolymers, poly(3‐O‐methacryloyl‐1,2 : 5,6‐di‐O‐isopropylidene‐D ‐glucofuranose) (PMAIpGlc), and diblock copolymers of PMAIpGlc with poly(1,1‐dihydroperfluorooctyl methacrylate) (PFOMA) were synthesized by living anionic polymerization in THF at ?78 °C with 1,1‐diphenylhexyllithium in the presence of lithium chloride. The resulting polymers were found to possess predictable molecular weights and very narrow molecular weight distributions (MWD, M_w/M_n ≤ 1.16). Removal of the acetal protective groups from the protected glycopolymer block copolymer was carried out using 90% trifluoroacetic acid at room temperature, yielding a hydrophilic block copolymer with pendant glucose moieties. Both protected (lipophilic/CO₂‐philic) and deprotected (hydrophilic/CO₂‐philic) fluorocopolymers were proved to be CO₂ amphiphiles. Their solubility in CO₂ was heavily influenced by the amphiphilic structure, such as the copolymer compositions and the polarities of sugar block. Light‐scattering studies showed that, after removal of the protective groups, the deprotected block copolymer formed aggregate structures in liquid CO₂ with an average micellar size of 27 nm. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3841–3849, 2001     

Positioning lithium ions by host–guest chemistry combined with self‐assembly using a thiophene‐based all‐conjugated amphiphilic block copolymer

Self‐assembly of poly(3‐hexylthiophene) ( P3HT) driven by π–π stacking, combined with “Host‐Guest Chemistry” of ethylene glycol oligomer and lithium ion is demonstrated using a thiophene‐based all conjugated amphiphilic block copolymer, containing 93 mol % of P3HT and 7 mol % of poly(3‐(2‐(2‐{2‐[2‐(2‐methoxy‐ethoxy)‐ethoxy]‐ethoxy}‐ethyl))thiophene), P3EGT blocks. An ion chelating ability of ethylene glycol oligomers with lithium ions in the P3EGT block is confirmed using ¹H‐NMR spectrometry. This method could allow positioning lithium ions at the interface between P3HT domains and PC₆₁BM clusters, confirmed using XRD and photoluminescence quenching experiments. The compact lamellar P3HT domains by side repulsion driven self‐assembly of amphiphilic block copolymer and the molecular engineering of the interface with an optimized lithium contents are resulted in the improvement of photovoltaic performance in an organic solar cell (2.1–3.0%). © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1068–1074     

Synthesis of amphiphilic copolymer brushes: Poly(ethylene oxide)‐graft‐polystyrene

A well‐defined amphiphilic copolymer brush with poly(ethylene oxide) as the main chain and polystyrene as the side chain was successfully prepared by a combination of anionic polymerization and atom transfer radical polymerization (ATRP). The glycidol was first protected by ethyl vinyl ether to form 2,3‐epoxypropyl‐1‐ethoxyethyl ether and then copolymerized with ethylene oxide by the initiation of a mixture of diphenylmethylpotassium and triethylene glycol to give the well‐defined polymer poly(ethylene oxide‐co‐2,3‐epoxypropyl‐1‐ethoxyethyl ether); the latter was hydrolyzed under acidic conditions, and then the recovered copolymer of ethylene oxide and glycidol {poly(ethylene oxide‐co‐glycidol) [poly(EO‐co‐Gly)]} with multiple pending hydroxymethyl groups was esterified with 2‐bromoisobutyryl bromide to produce the macro‐ATRP initiator [poly(EO‐co‐Gly)_(ATRP). The latter was used to initiate the polymerization of styrene to form the amphiphilic copolymer brushes. The object products and intermediates were characterized with ¹H NMR, matrix‐assisted laser desorption/ionization time‐of‐flight mass spectrometry, Fourier transform infrared, and size exclusion chromatography in detail. In all cases, the molecular weight distribution of the copolymer brushes was rather narrow (weight‐average molecular weight/number‐average molecular weight < 1.2), and the linear dependence of ln[M₀]/[M] (where [M₀] is the initial monomer concentration and [M] is the monomer concentration at a certain time) on time demonstrated that the styrene polymerization was well controlled. This method has universal significance for the preparation of copolymer brushes with hydrophilic poly(ethylene oxide) as the main chain. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4361–4371, 2006     

Highly ordered nanoporous thin films by blending of PSt‐b‐PMMA block copolymers and PEO additives as structure directing agents

Herein, we present a simple method for producing nanoporous templates with a high degree of lateral ordering by self‐assembly of block copolymers. A key feature of this approach is control of the orientation of polymeric microdomains through the use of hydrophilic additives as structure directing agents. Incorporation of hydrophilic poly(ethylene oxide) (PEO) moieties into poly(styrene‐b‐methyl methacrylate) (PSt‐b‐PMMA) diblock copolymers gives vertical alignment of PMMA cylinders on the substrate after solvent annealing. Because of the miscibility between PEO and PMMA, PEO additives were selectively positioned within PMMA microdomains and by controlling the processing conditions, it was found that ordering of PSt‐b‐PMMA diblock copolymers could be achieved. The perpendicular orientation of PMMA cylinders was achieved by increasing the molecular size of the PEO additives leading to an increased hydrophilicity of the PMMA domains and consequently to control the orientation of microdomains in PSt‐b‐PMMA block copolymer thin films. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 8041–8048, 2008     

Polymer electrolyte membranes by in situ polymerization of poly(ethylene carbonate‐co‐ethylene oxide) macromonomers in blends with poly(vinylidene fluoride‐co‐hexafluoropropylene)

Salt‐containing membranes based on polymethacrylates having poly(ethylene carbonate‐co‐ethylene oxide) side chains, as well as their blends with poly(vinylidene fluoride‐co‐hexafluoropropylene) (PVDF‐HFP), have been studied. Self‐supportive ion conductive membranes were prepared by casting films of methacrylate functional poly(ethylene carbonate‐co‐ethylene oxide) macromonomers containing lithium bis(trifluorosulfonyl)imide (LiTFSI) salt, followed by irradiation with UV‐light to polymerize the methacrylate units in situ. Homogenous electrolyte membranes based on the polymerized macromonomers showed a conductivity of 6.3 × 10^?6 S cm^?1 at 20 °C. The preparation of polymer blends, by the addition of PVDF‐HFP to the electrolytes, was found to greatly improve the mechanical properties. However, the addition led to an increase of the glass transition temperature (T_g) of the ion conductive phase by ～5 °C. The conductivity of the blend membranes was thus lower in relation to the corresponding homogeneous polymer electrolytes, and 2.5 × 10^?6 S cm^?1 was recorded for a membrane containing 10 wt % PVDF‐HFP at 20 °C. Increasing the salt concentration in the blend membranes was found to increase the T_g of the ion conductive component and decrease the propensity for the crystallization of the PVDF‐HFP component. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 79–90, 2007     

Effects of additives and post‐treatment on the thermoelectric performance of vapor‐phase polymerized PEDOT films

Vapor‐phase polymerization (VPP) is an important method for the fabrication of high‐quality conducting polymers, especially poly(3,4‐ethylenedioxythiophene) (PEDOT). In this work, the effects of additives and post‐treatment solvents on the thermoelectric (TE) performance of VPP‐PEDOT films were systematically investigated. The use of 1‐butyl‐3‐menthylinidazolium tetrafluoroborate ([BMIm][BF₄], an ionic liquid) was shown to significantly enhance the electrical conductivity of VPP‐PEDOT films compared with other additives. The VPP‐PEDOT film post‐treated with mixed ethylene glycol (EG)/[BMIm][BF₄] solvent displayed the high power factor of 45.3 μW m^?1 K^?2 which is 122% higher than that prepared without any additive or post‐treatment solvent, along with enhanced electrical conductivity and Seebeck coefficient. This work highlighted the superior effect of the [BMIm][BF₄] additive and the EG/[BMIm][BF₄] solvent post‐treatment on the TE performance of the VPP‐PEDOT film. These results should help with developing the VPP method to fabricate high‐performance PEDOT films. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017 , 55 , 1738–1744     

Polymerization‐induced self‐assembly of block copolymer through dispersion RAFT polymerization in ionic liquid

Polymerization‐induced self‐assembly of block copolymer through dispersion RAFT polymerization has been demonstrated to be a valid method to prepare block copolymer nano‐objects. However, volatile solvents are generally involved in this preparation. Herein, the in situ synthesis of block copolymer nano‐objects of poly(ethylene glycol)‐block‐polystyrene (PEG‐b‐PS) in the ionic liquid of 1‐butyl‐3‐methylimidazolium hexafluorophosphate ([BMIN][PF₆]) through the macro‐RAFT agent mediated dispersion polymerization is investigated. It is found that the dispersion RAFT polymerization of styrene in the ionic liquid of [BMIN][PF₆] runs faster than that in the alcoholic solvent, and the dispersion RAFT polymerization in the ionic liquid affords good control over the molecular weight and the molecular weight distribution of the PEG‐b‐PS diblock copolymer. The morphology of the in situ synthesized PEG‐b‐PS diblock copolymer nano‐objects, e.g., nanospheres and vesicles, in the ionic liquid is dependent on the polymerization degree of the solvophobic block and the concentration of the fed monomer, which is somewhat similar to those in alcoholic solvent. It is anticipated that the dispersion RAFT polymerization in ionic liquid broads a new way to prepare block copolymer nano‐objects. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1517–1525     

Synthesis and characterization of poly(ethylene oxide‐co‐ethylene carbonate) macromonomers and their use in the preparation of crosslinked polymer electrolytes

Methacrylate‐functionalized poly(ethylene oxide‐co‐ethylene carbonate) macromonomers were prepared in two steps by the anionic ring‐opening polymerization of ethylene carbonate at 180 °C, with potassium methoxide as the initiator, followed by the reaction of the terminal hydroxyl groups of the polymers with methacryloyl chloride. The molecular weight of the polymer went through a maximum after approximately 45 min of polymerization, and the content of ethylene carbonate units in the polymer decreased with the reaction time. A polymer having a number‐average molecular weight of 2650 g mol^?1 and an ethylene carbonate content of 28 mol % was selected and used to prepare a macromonomer, which was subsequently polymerized by UV irradiation in the presence of different concentrations of lithium bis(trifluoromethanesulfonyl)imide salt. The resulting self‐supportive crosslinked polymer electrolyte membranes reached ionic conductivities of 6.3 × 10^?6 S cm^?1 at 20 °C. The coordination of the lithium ions by both the ether and carbonate oxygens in the polymer structure was indicated by Fourier transform infrared spectroscopy. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2195–2205, 2006