尿素用量对燃烧法合成CaAl_2O_4∶Eu~(2+),Nd~(3+)长余辉材料发光性能的影响

利用金属硝酸盐和尿素的氧化还原反应,通过燃烧法在600℃的炉温下合成了蓝紫色长余辉发光材料CaA l2O4∶Eu2 ,Nd3 。在金属硝酸盐溶液浓度不变的条件下,通过改变尿素与硝酸根的量的比,合成了多组长余辉材料样品。当尿素用量较少时,Eu3 不能完全被还原为Eu2 ;随尿素用量增加,样品的Eu3 特征发射减弱,余辉初始亮度和持续时间均得到改善;当尿素的用量达到理论用量的5倍时,样品余辉特性最好,继续增加尿素用量,余辉亮度和持续时间反而下降。将燃烧法制备的各组样品用活性炭密封,在1 000℃条件下反应2 h,使Eu3 完全被还原为Eu2 ,同时除去燃烧法反应不完全的杂质,可以一定程度提高材料的余辉发光性能。     

SrAl2O4∶Eu2+,Dy3+长余辉发光材料的喷雾热解制备及其表征

采用喷雾热解两段法制备了SrAl₂O₄∶Eu²⁺ ,Dy³⁺长余辉发光材料,并利用XRD、SEM、荧光长余辉亮度测试等方法分析了不同制备工艺条件下SrAl₂O₄∶Eu²⁺ ,Dy³⁺发光材料的结构、形貌以及发光性能的变化。结果表明:采用喷雾热解两段法可制备出球形SrAl₂O₄∶Eu²⁺ ,Dy³⁺长余辉发光材料,SrAl₂O₄∶Eu²⁺ ,Dy³⁺的晶体结构与α-SrAl₂O₄磷石英晶体结构相同。热解温度、还原温度、添加剂对产物的形貌、粒度分布、发光性能有较大影响。较之高温固相法,喷雾热解法制备的SrAl₂O₄∶Eu²⁺ ,Dy³⁺具有发光性能好、形貌好、粒度分布窄等优点。     

氧空位对Eu2+, Dy3+掺杂的Ca5MgSi3O12发光及余辉性能的影响

利用高温固相法合成了稀土离子Eu²⁺, Dy³⁺掺杂的Ca₅MgSi₃O₁₂长余辉发光材料. 利用光谱学证明了在材料内部存在与氧空位有关的缺陷发光. 通过对比不同条件下合成样品的发光及余辉性能, 发现氧空位对材料的发光及余辉均起到促进作用. 同时发现氧空位发光可以向发光中心传递能量. 利用热释光曲线系统的分析了氧空位对余辉性能的影响. Ca₅MgSi₃O₁₂:Eu²⁺,Dy³⁺是一种潜在的长余辉发光材料. 关键词： 长余辉 氧空位 能量传递 热释光     

发光颜色可调的硅酸盐长余辉发光材料 Ba4(Si3O8)2∶Eu2+,Ce3+,Dy3+

在还原气氛下利用高温固相法制备了Ba_3.982-x(Si₃O₈)₂∶0.008Eu²⁺,xCe³⁺,0.01Dy³⁺系列样品。光谱分析表明,Ce³⁺进入到晶格中将取代不同Ba²⁺格位从而形成不同的发光中心。通过Ce³⁺→Eu²⁺的能量传递,得到了一系列发光颜色可调、余辉颜色为绿色的长余辉发光材料。Ce³⁺的掺入可以增大样品的余辉强度但是同时缩短了样品的余辉时间。热释光谱的分析表明,Ce³⁺的掺入可以同时增加浅陷阱T₁和深陷阱T₃的数量,深陷阱对载流子的再捕获效应导致了样品余辉强度的增大和余辉时间的缩短。     

新型电子俘获型材料β-Sr2SiO4:Eu2+, La3+长余辉和光激励发光性能的研究

通过高温固相法在还原气体保护下制备出β-Sr₂SiO₄: Eu²⁺, La³⁺系列样品. 通过样品光谱显示, 光致发光、余辉及光激励发光中心均来自于Eu²⁺离子; 并且La³⁺ 的掺入有效增强光致发光、余辉及光激励发光强度. 热释光与余辉衰减测试证明, 与单掺Eu²⁺样品所具备的缺陷数量相比, 共掺La³⁺样品在浅陷阱区(T1区)较多的俘获中心数量是导致其余辉性能优化的主要因素; 其光激励发光强度的增强则归因于在深陷阱(T3区)的俘获中心数量增加. 共掺样品放置15h并在980nm红外激光激励后, 表现出光激励长余辉发光现象. 此现象的出现, 为电子俘获型材料的浅陷阱对深陷阱中的载流子再俘获过程的存在提供了直接证据. 因此, β-Sr₂ SiO₄: Eu²⁺, La³⁺ 材料可视为一种潜在的长余辉和光激励发光材料.     

共沉淀法制备Y2O2S：Eu3+,Mg2+,Ti4+红色长余辉材料

用共沉淀法制备了Y₂O₂S:Eu³⁺,Mg²⁺,Ti⁴⁺红色长余辉材料。测量了材料的电子显微形貌、晶体结构和发射光谱。通过与固相法制备的Y₂O₂S:Eu³⁺,Mg²⁺,Ti⁴⁺长余辉材料比较,发现两种方法都可以制备粒度基本相同的纯相Y₂O₂S基质晶体,但共沉淀法样品的颗粒结构更松散。研究了Eu³⁺浓度对两种方法制备样品的谱线发射强度的影响,通过比较共沉淀法和高温固相法制备的样品中Eu³⁺的⁵D₁→⁷F₃较高能级跃迁的587.6nm谱线强度随Eu³⁺浓度的变化,发现共沉淀法更有利于Eu³⁺均匀进入Y₂O₂S基质晶格而形成有效的发光中心。     

激发波长和Eu2+的掺杂量对Sr4Al14O25 ∶ Eu2+ , Dy3+发光性能的影响

采用溶胶-凝胶法在低温、还原气氛下制备了长余辉发光材料Sr₄Al₁₄O₂₅ ∶ Eu²⁺,Dy³⁺。用X射线粉末晶衍射对其进行了物相鉴定,表明在1 200 ℃已经得到纯相的Sr₄Al₁₄O₂₅ 产物。研究了铕和锶的比值、激发光波长对所制备的Sr₄Al₁₄O₂₅ ∶ Eu²⁺, Dy³⁺发光性能的影响并对其影响机理进行了探讨。样品的发光性能测试结果表明:采用溶胶-凝胶法制备长余辉发光材料Sr₄Al₁₄O₂₅ ∶ Eu²⁺, Dy³⁺,其灼烧温度比高温固相法灼烧温度低;激发光谱向长波方向延伸时,在488 nm处发射峰增强,在410 nm处发射峰减弱;在一定范围内发光强度随着Eu²⁺量的增加而增强,Eu²⁺的最佳掺杂量为0.007, Eu²⁺的掺杂量超过0.007时会发生浓度猝灭。     

长余辉发光材料CaAl2O4∶Eu2+,Gd3+ 的制备和发光性能研究

采用高温固相法制备了CaAl₂O₄∶Eu²⁺,Gd³⁺ 长余辉发光材料。利用X射线衍射(XRD)和荧光光谱测试等手段对所制备的样品进行结构表征和发光性能的分析,探究Eu²⁺摩尔分数为3.5%,硼酸质量分数为0.5%,Gd³⁺摩尔分数分别为2%,3%,4%,5%时样品的发光性能。研究结果表明:实验成功地合成了CaAl₂O₄∶Eu²⁺,Gd³⁺粉晶,并且Eu²⁺和Gd³⁺的引入并未引起CaAl₂O₄晶体结构的改变。样品的激发光谱和发射光谱均为宽带谱,且发射光谱的最大峰值位于444 nm左右,属于Eu²⁺的4f⁶5d→4f⁷跃迁,所发光为蓝光。蓝色荧光粉CaAl₂O₄∶3.5%Eu²⁺,3%Gd³⁺的发光强度最好。     

亚微米Sr2MgSi2O7：Eu2+,Dy3+的水热共沉淀制备及发光性能研究

通过水热共沉淀方法制备了亚微米长余辉发光材料Sr₂MgSi₂O₇：Eu²⁺,Dy³⁺,使用X射线衍射、扫描电镜、光致发光以及热释发光光谱对所合成的材料进行了研究。结果表明：在1 000℃下烧结4 h的样品为四方晶系单相,结晶度随着烧结温度的升高而进一步改善,所制备的材料分散性良好,尺寸在200~300 nm之间。在399 nm激发下,样品呈现出主峰位于467 nm的蓝光发射,来自于Eu²⁺的5d-4f跃迁。在1 100℃烧结获得的样品的长余辉发光优于1 000℃烧结的样品。样品的热释光谱为一个不对称分布的宽带,主峰位于330~340 K之间,热释光谱对应的峰值范围有利于产生长余辉发光。     

碱土金属离子对红色长余辉材料Y2O2S：Eu3+, M2+（M=Mg,Ca,Sr,Ba）,Ti4+纳米阵列发光性能的影响

采用溶胶凝胶模板法制备红色长余辉发光材料Y₂O₂S：Eu³⁺,M²⁺（M=Mg,Ca,Sr,Ba）,Ti⁴⁺纳米阵列,利用X射线衍射、扫描电子显微镜和荧光分光光度计、照度计分别研究了不同二价离子掺杂下所合成样品的物相、形貌及发光性能。结果表明：样品排列整齐有序,管径大小统一;不同的二价离子种类没有改变晶体结构和发射峰的位置,但对余辉性能有较大的影响。用324 nm波长光激发样品,由于Eu³⁺的⁵D₀→⁷F₂跃迁,最强的红色发射峰位于626 nm处;不同离子掺杂样品的余辉性能按Ba²⁺、Ca²⁺、Sr²⁺、Mg²⁺的顺序递加,其中二价离子为Mg²⁺ 时,余辉时间长达287 s（≥1 mcd/m²）,表现出最佳的余辉性能。     

Annihilation of the persistent luminescence of MAl2O4:Eu by Sm co-doping

The calcium aluminates doped with the Eu²⁺ and Nd³⁺ ions, CaAl₂O₄:Eu²⁺,Nd³⁺, are a novel and efficient persistent luminescence (i.e. afterglow) material. The Nd³⁺ ions were found to enhance the persistent luminescence. Some other R³⁺ co-dopants had similar or opposite, though weaker, effect. The Sm³⁺ (and Yb³⁺) ions suppressed almost completely the persistent luminescence and thermoluminescence of the Eu²⁺ ion. From the UV-excited luminescence and persistent luminescence spectra it was found that the Eu²⁺ ion acts as a luminescent centre with luminescence at the blue (λ_max=440 nm) region. The Sm³⁺ ion was reduced to the divalent state. The thermoluminescence glow curves of the CaAl₂O₄:Eu²⁺,Sm³⁺ material showed that the high-temperature glow peaks, i.e. deep traps, were suppressed almost completely. The Nd:YAG laser-excited high-resolution photoluminescence of the Sm²⁺ ion confirmed that the Eu²⁺ ion occupies only one Ca²⁺ site. Only weak perturbations were observed in the Sm²⁺ site due to the changes in the environment of the Sm²⁺ site.     

低温燃烧法制备SrMgAl10O17：Eu2+,Er3+高亮度蓝光荧光粉及发光性能研究

采用低温燃烧法合成SrMgAl₁₀O₁₇:Eu²⁺及SrMgAl₁₀O₁₇:Eu²⁺, Er³⁺蓝色发光材料, 通过X射线衍射仪 (XRD)、扫描电子显微镜 (SEM) 和荧光光谱仪 (PL) 等测试手段对所得样品进行表征. XRD及SEM测试结果表明: 利用低温燃烧法合成SrMgAl₁₀O₁₇材料具有较高的结晶度, 且微量的稀土元素掺杂不会破坏其晶体结构; PL测试结果表明: SrMgAl₁₀O₁₇:Eu²⁺ 荧光粉在300–390 nm范围内可以被有效的激发, 该波长范围与近紫外LED芯片匹配, 发射光谱分布在430–520 nm之间, 发射峰位于460 nm, 属蓝光发射材料. 共掺Er³⁺可显著增强SrMgAl₁₀O₁₇:Eu²⁺的发光强度, 且当Er³⁺的掺杂浓度为4%时,样品的发光强度最大, 较单掺Eu²⁺时样品的发光强度高出54.9%, 表明Er³⁺对Eu²⁺的发光具有良好的敏化作用, 该敏化作用的机理可以利用能量传递原理进行解释. 关键词： 低温燃烧法 10O₁₇')" href="#">SrMgAl₁₀O₁₇ 蓝光荧光粉 敏化作用     

Eu3+激活的La2Mo2O9红色荧光粉的制备与性能

利用高温固相法制备了Eu³⁺掺杂的La₂Mo₂O₉红色荧光粉,并对这种荧光粉的结构及发光性质进行了研究。XRD结果表明,实验合成了单一立方相的La₂Mo₂O₉荧光粉体。该荧光粉的激发光谱由一宽带和一系列的锐峰组成;发射光谱由一系列锐峰组成,这些都与Eu³⁺的特征跃迁⁵D_J(J=0,1)和⁷F_J(J=1~4)相对应。结果表明该荧光粉可被395nm的紫外光和470nm的可见光有效激发,并发出峰值位于620nm左右的红光,亮度可达到传统红色荧光粉Y₂O₂S:Eu³⁺的1.5倍以上,这表明它可以作为蓝+黄模式白光LED的红色补光粉,也可以作为UV-LED激发三基色荧光粉体系中的红色荧光粉。研究了Eu³⁺的掺杂浓度以及不同助熔剂对样品发光性质的影响。Eu³⁺的摩尔分数为0.3时,发光强度达到最强。质量分数为3%的NH₄Cl作为助熔剂时效果最好。     

草酸沉淀法制备细颗粒红色荧光粉Y2O3：Eu3+的发光特性

对草酸作为沉淀剂制备的细颗粒红色荧光粉Y₂O₃:Eu³⁺进行结构和发光特性研究,结果表明:其一次粒径为20～30nm,团聚尺寸D₅₀=0.53μm。该荧光粉最大激发峰位于252.2nm,较微米级荧光粉233nm红移了19.2nm;最大的发射峰位于612nm,与微米级的相比几乎没有差别。Eu³⁺离子的掺入构成了发光中心,其最佳掺杂的质量分数为9%,荧光粉发光的猝灭浓度由微米级的6%提高到9%。由于纳米晶存在表面缺陷和悬挂键,其亮度约为微米晶的70%左右,随着团聚尺寸的增加、煅烧温度的提高和助熔剂的加入,荧光粉的发光强度增大。包膜能部分消除表面缺陷和悬挂键,提高发光亮度。荧光粉的色坐标为x=0.6479,y=0.3442。     

蓝色长余辉材料Sr2MgSi2O7：Eu2+,Dy3+及其基质的VUV-UV激发特性

Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺是一种有效的蓝色长余辉材料,采用高温固相法合成了Sr₂MgSi₂O₇,Sr₂MgSi₂O₇:Dy³⁺,Sr₂MgSi₂O₇:Eu²⁺及Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺,利用同步辐射研究了它们的VUV-UV激发特性.在真空紫外光激发下,在基质中发现了稍弱的位于385nm的发射带,在双掺杂的样品中,除了Eu²⁺的4f5d→4f发射带(465nm)外,还观察到了575nm处的发射峰;通过和Dy³⁺单掺杂样品的发射谱比较,发现它是来自于Dy³⁺的4f-4f(⁴F_9/2→6H_13/2)跃迁.在它们的激发谱上可以看出Dy³⁺与基质发射的有效激发均处于真空紫外区,在近紫外及可见区激发下未见到它们发光.另外在Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺中观察到Dy³⁺的发射也说明了Dy³⁺在该类长余辉材料中不仅作为陷阱用来延长余辉,而且也以发光中心形式存在于基质中.     

蓝色长余辉材料CaAl_2O_4∶Eu~(2+),Li~+的发光性质

采用高温固相法制备了CaAl_2O_4∶Eu~(2+),Li~+发光材料,并讨论了掺杂Li+对CaAl_2O_4∶Eu~(2+)发光性质的影响。X射线衍射(XRD)和PL测试分析表明,在CaAl_2O_4∶Eu~(2+)中掺入Li~+后,Eu~(2+)的发光有一定的增强,而余辉时间则延长了4倍左右。通过热释光谱测量,分析了其陷阱能级的数量并估算了陷阱能级深度。结果表明,掺杂Li~+会在发光离子周围产生更多的电子陷阱,使陷阱的密度和深度增加,从而提高荧光粉的余辉性能。     

白光LED用红色荧光粉Gd2Mo3O9：Eu3+的制备及表征

利用Na₂CO₃作为助熔剂,采用高温固相反应方法制备了三价铕离子激活的Gd₂Mo₃O₉红色荧光粉。利用XRD和荧光光谱,研究了助熔剂的量、制备时的温度以及激活剂Eu³⁺的浓度对荧光粉的晶体结构和发光性能的影响。测试结果表明,这种新型的荧光粉可以被紫外光280nm,近紫外光395nm和蓝光465nm有效激发,发射主峰位于613nm,并且证明Eu³⁺离子在晶体结构中占据了非反演对称中心的位置。395,465nm的吸收与目前广泛应用的紫外和蓝光LED芯片的输出波长相匹配。因此,这种荧光粉是一种可能应用在白光LED上的红色荧光粉材料。     

Sr3B2O6：Eu3+,Li+荧光粉的合成与发光性能

采用高温固相法合成Sr₃B₂O₆：Eu³⁺,Li⁺红色荧光粉,考察了激活剂Eu³⁺和电荷补偿剂Li⁺浓度对Sr₃B₂O₆：Eu³⁺,Li⁺荧光粉发光性能的影响。结果表明：适量掺杂Eu³⁺、Li⁺离子并不改变Sr₃B₂O₆的结构。当Eu³⁺掺杂量为4%、Li⁺的掺杂量为8%时,在900 ℃下灼烧2 h可以得到发光性能最佳的Sr_2.9B₂O₆：0.04Eu³⁺,0.08Li⁺红色荧光粉。以394 nm的近紫外光激发时,Sr₃B₂O₆：Eu³⁺,Li⁺荧光粉发射出红光,对应于Eu³⁺的4f-4f 跃迁,其中以614 nm附近的⁵D₀→⁷F₂跃迁发光最强,是一种有潜力用于白光LED的红色荧光粉。