Preparation and characterization of polyoxymethylene‐copolymer/hydroxyapatite nanocomposites for long‐term bone implants

In this work, new polyoxymethylene (POM)/hydroxyapatite (HAp) nanocomposites for long‐term bone implants have been obtained via extrusion and injection molding processes and characterized by differential scanning calorimetry (DSC), temperature‐modulated DSC (TMDSC), scanning electron microscopy (SEM), transmission electron microscopy (TEM), wide‐angle X‐ray diffraction (WAXD), Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG), and tensile mechanical and in vitro stability tests. Based on the DSC results, it was found that the degree of crystallinity increases for POM/0.5% HAp sample and decreases for POM/1.0% HAp and POM/2.5% HAp. SEM and TEM observations for POM/HAp nanocomposites indicated that the dispersion of HAp in the polymer matrix was uniform and the diameter of the HAp particles was less than 100 nm for most of them. Young's modulus increases with increasing HAp concentration, whereby elongation at break decreases. On the contrary, HAp concentration does not have a significant influence on the tensile strength. TG results show that for POM/0.5% HAp, POM/1.0% HAp, and POM/2.5% HAp, thermal stability slightly increases in comparison to pure POM, whereas for POM/5.0 HAp and POM/10.0% HAp, lower thermal stability was observed. In vitro data reveal that with an increase of HAp content, bioactivity of nanocomposites increases; a good in vitro chemical stability of POM and POM nanocomposites was confirmed. Copyright © 2011 John Wiley & Sons, Ltd.     

Influence of gamma irradiation on high density polyethylene/ethylene‐vinyl acetate/clay nanocomposites

The study of high density polyethylene (HDPE)/ethylene‐vinyl acetate (EVA)/and organically‐modified montmorillonite (OMT) nanocomposites prepared by melt intercalation followed by exposure to gamma‐rays have been carried out. The morphology and properties of the nanocomposites were studied using X‐ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric analysis (TGA) and cone calorimetry. The purpose of the study focuses on the influence of gamma irradiation on the morphology, thermal stability and flammability properties of the nanocomposites. XRD studies and TEM images verified that the ordered intercalated nanomorphology of the nanocomposites was not disturbed by gamma irradiation. TGA data showed that the nano‐dispersion of clay throughout the polymer inhibited the irradiation degradation of HDPE/EVA blend, which led to the nanocomposites exhibiting superior irradiation‐resistant properties than that of the pure blend. Cone calorimetry results indicated that the improvement in heat release rate (HRR) for irradiated HDPE/EVA blend was suppressed efficiently when clay was present. Increasing clay loading from 2 to 10% was beneficial by improving the flammability properties of the nanocomposites, but promoted a rapid increase in the sub‐peak HRR at high irradiation dose level. Copyright © 2004 John Wiley & Sons, Ltd.     

Effect of Organic Nano Carboncapsule Incorporated Modified Clay on Fire‐Retardancy of PMMA Nanocomposites

Here we investigate a new type of highly flame retardant poly(methyl methacrylate) (PMMA) nanocomposite by bulk polymerization of methyl methacrylate (MMA) in the presence of organic nano carboncapsule (OCNC/NCNC)‐incorporated modified montmorillonites (CL120, CL42). The morphology of the modified clay was confirmed by X‐ray diffraction (XRD), and Fourier transform infrared (FT‐IR) spectroscopy was used to identify the functional groups in the clay. The nano morphological characterization of the clay in the PMMA matrix was confirmed by XRD and transmission electron microscopy (TEM). The thermal and mechanical properties of the PMMA nanocomposites were investigated by thermogravimetry and dynamic mechanical analysis, respectively. PMMA containing organo nano carboncapsule‐doped CL42 modified cocoamphodipropionate (K2) (P‐O‐CL42) could achieve very high thermal stability compared to pristine PMMA. The 5% thermal decomposition temperature (T _5d) increased by 63.2°C. Storage modulus of PMMA nanocomposites measured by DMA analysis. An enhancement of storage modulus and significant reduction in the peak heat release (PHR) rate were observed in the almost all PMMA nanocomposites as compared to pristine PMMA. Moreover, these results suggest that PMMA nanocomposites can have potential applications in the building industry and the medical field.     

Influence of alumina reinforcement on nano-hydroxyapatite/biopolymer composite for biomedical applications

The foremost material that closely mimics the mineral part of the bone tissue, and is therefore suitable for bone replacement, is nano-hydroxyapatite (nHAp) which exhibits low fracture toughness, and can be used for load-bearing scaffolds in biomedical applications. Therefore, for improved biomechanical features, composite materials are developed. This work focuses on the influence and contribution of bioactive alumina and nHAp on the biopolymer, i.e., gelatin matrix for the fabrication of load-bearing bone replacement composites. Incorporation of bioceramics alumina at the strengthening phase is essential for the improvement of mechanical properties for biomedical applications. The porosity of scaffolds varied from 79 to 85%. Fourier transform infrared (FTIR) and X-ray powder diffraction (XRD) analyses showed the presence of molecular interactions and chemical linkages between gelatin matrix, alumina, and nHAp particles. The compressive strength of alumina-reinforced nanocomposites scaffolds is three times higher than those of nHAp/gelatin. The elemental composition of the chemically synthesized nHAp particles was determined by SEM, FTIR, and XRD analyses.     

Imidazolium‐modified clay‐based ABS nanocomposites: a comparison between melt‐blending and solution‐sonication processes

Acrylonitrile–butadiene–styrene (ABS) nanocomposites containing imidazolium‐modified montmorillonite have been prepared by melt‐blending (MB) and solution‐sonication in order to study the effects of processing on the morphology and properties of the polymer/clay composites. The structure‐property relationships of the prepared composites have been studied by means of X‐ray diffraction (XRD), transmission electron microscopy (TEM), mechanical testing, dynamic‐mechanical analyses (DMA), thermal gravimetrical analyses (TGA), fluorescence probe confocal microscopy, and fluorescence spectroscopy (FS). X‐Ray and TEM show that both nanocomposites have a mixed intercalated/exfoliated structure. Fluorescence probe confocal microscopy reveals that the sonicated sample has a more homogeneous dispersion: this result is confirmed by the values of elongation at break and flexural elastic modulus measured for the composites. Fluorescence spectroscopy has also been used to investigate the distribution of clay in the composites and results indicate that clay layers in ABS are preferentially located in the styrene‐acrylonitrile (SAN) phase, independent of the dispersion process used. Published in 2008 by John Wiley & Sons, Ltd.     

Brominated poly(isobutylene‐co‐para‐methylstyrene) (BIMS)‐clay nanocomposites: Synthesis and characterization

In this work, preparation and properties of different nanoclays modified by organic amines (octadecyl amine, a primary amine, and hexadecyltrimethylammonium bromide, a tertiary amine) and brominated polyisobutylene‐co‐paramethylstyrene (BIMS)‐clay nanocomposites are reported. The clays and the rubber nanocomposites have been characterized with the help of Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), and X‐ray diffraction (XRD). The X‐ray diffraction peaks observed in the range of 3 °–10 ° for the modified clays disappear in the rubber nanocomposites. TEM photographs show predominantly exfoliation of the clays in the range of 12 ± 4 nm in the BIMS. In the FTIR spectra of the nanocomposites, there are common peaks of virgin rubber as well as those of the clays. Excellent improvement in mechanical properties like tensile strength, elongation at break, and modulus is observed on incorporation of the nanoclays in the BIMS. Structure‐property correlation in the above nanocomposites is attempted. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4489–4502, 2004     

Preparation and Characteration of UV-cured EA/MMT Nanocomposites Via In-Situ Polymerization

A long-chain surfactant, enzoylbenzyl-N,N-dimethyl-N-octadecylammonium bromide (BDOB) with a benzophenone group, was synthesized to modify the montmorillonites (MMT) for the preparation of nanocomposites via photo-induced polymerization. The BDOB-modified MMT was characterized by the fourier transform infrared spectrometer (FTIR), thermal gravimetric analyzer (TGA) and X-ray diffraction (XRD), and the results of XRD indicated that the intercalated structures of BDOB-modified MMT was obtained. The conversion of the bisphenol A epoxy diacrylate (EA) was quantified by the FTIR, and the results indicated that conversion increased with an increase in the amount of BDOB-modified MMT. The morphologies of the UV-cured EA/MMT nanocomposites prepared from this organically modified MMT were studied by means of XRD and TEM, and the results showed that all the samples contained an intercalated structure with partial exfoliated structure. The results of TGA and mechanical properties also indicated that the thermal and mechanical properties of UV-cured nanocomposites were significantly enhanced due to the presence of the long chain surfactant organically modified MMT.     

Synthesis,morphology, and properties of hydroxyl terminated‐POSS/polyimide low‐k nanocomposite films

Polyhedral oligomeric silsequioxane (POSS), having eight hydroxyl groups for the preparation of nanocomposites with polyimide (PI) was synthesized by the direct hydrosilylation of allyl alcohol with octasilsesquioxane (Q₈M₈^H) with platinum divinyltetramethyl disiloxane Pt(dvs) as a catalyst. The structure of allyl alcohol terminated‐POSS (POSS‐OH) was confirmed by FTIR, NMR, and XRD. A high performance, low‐k PI nanocomposite from pyromellitic dianhydride (PMDA)‐4,4'‐oxydianiline (ODA) polyamic acid cured with POSS‐OH was also successfully synthesized. The incorporation of POSS‐OH into PI matrix reduced dielectric constant of PI without loosing mechanical properties. Furthermore, the effects of POSS‐OH on the morphology and properties of the PI/POSS‐OH nanocomposites were investigated using UV–vis, FTIR, XRD, SEM, AFM, transmission electron microscope (TEM), TGA, and contact angle. The homogeneous dispersion of POSS particles was confirmed by SEM, AFM, and TEM. The nanoindentation showed that the modulus increased upon increasing the concentration of POSS‐OH in PI, whereas the hardness did not increase very much with respect to loading of POSS, due to soft‐interphase around POSS molecules in the resulting nanocomposites. Overall results demonstrated the nanometer‐level integration of the polymer and POSS‐OH. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5887–5896, 2008     

Effect of polymerically‐modified clay structure on the morphology and properties of UV‐cured polyurethane acrylate/clay nanocomposites

Polyurethane acrylate (PUA)/clay nanocomposites were prepared by UV‐curing from a series of styrene‐based polymerically‐modified clays and PUA resin. Effect of the chemical structure of the polymeric surfactants on the morphology and tensile properties of nanocomposites has been explored. X‐ray diffraction (XRD) and transmission electron microscopy (TEM) experimental results indicated that surfactants having hydroxyl or amino groups show better dispersion and some of the clay platelets were fully exfoliated. However, the composites formed from pristine clay and other polymerically‐modified clays without hydroxyl or amino groups typically contained both tactoids and intercalated structure. The mechanical properties of PUA composites were greatly improved where the organoclays dispersed well. Thermogravimetric analysis (TGA) and differential scanning calorimeter (DSC) were carried out to examine the thermal properties of the composites. The results showed that the loading of polymerically‐modified clays do not effect the thermal stability, but increased the Tgs of PUA/clay composites. Copyright © 2010 John Wiley & Sons, Ltd.     

Preparation and Characterization of Composites that Contain Small Carbon Nano‐Onions and Conducting Polyaniline

Small multilayer fullerenes, also known as carbon nano‐onions (CNOs; 5–6 nm in diameter, 6–8 shells), show higher reactivity than other larger carbon nanostructures. Here we report the first example of an in situ polymerization of aniline on phenyleneamine‐terminated CNO surfaces. The green, protonated, conducting emeraldine polyaniline (PANI) was directly synthesized on the surface of the CNO. The functionalized and soluble CNO/PANI composites were characterized by TEM, SEM, DSC, Raman, and infrared spectroscopy. The electrochemical properties of the conducting CNO/PANI films were also investigated. In comparison with pristine CNOs, functionalized carbon nanostructures show dramatically improved solubility in protic solvents, thus enabling their easy processing for coatings, nanocomposites, and biomedical applications.     

Thermomechanical properties and crystallization behavior of layered double hydroxide/poly(ethylene terephthalate) nanocomposites prepared by in‐situ polymerization

Thermomechanical properties and crystallization behavior of poly(ethylene terephthalate) (PET) nanocomposites containing layered double hydroxide (LDH) were investigated. To enhance the compatibility between PET matrix and LDH, dimethyl 5‐sulfoisophthalate (DMSI) anion intercalated LDH (LDH‐DMSI) was synthesized by coprecipitation method, and its structure was confirmed by Fourier transform infrared (FTIR) spectrometer and X‐ray diffraction (XRD) measurements. Then, PET nanocomposites with LDH‐DMSI content of 0, 0.5, 1.0, and 2.0 wt% were prepared by in‐situ polymerization. The dispersion morphologies were observed by transmission electron microscopy (TEM) and XRD, showing that LDH‐DMSI was exfoliated in PET matrix. Thermal and mechanical properties, such as thermal stability, tensile modulus, and tensile yield strength of nanocomposites, were enhanced by exfoliated LDH‐DMSI nanolayers. However, elongation at break was drastically decreased with LDH loading owing to the increased stiffness and microvoids. The effect of exfoliated nanolayers, which acted as a nucleating agent confirmed by differential scanning calorimeter (DSC), on the microstructural parameters during isothermal crystallization, was analyzed by synchrotron small‐angle X‐ray scattering (SAXS). It is believed that nanocomposites could be crystallized more easily owing to the increased nucleation sites, which lead to the decrease of average amorphous region size and the long period with the increase of LDH‐DMSI content. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 28–40, 2007     

Non‐Covalent Functionalization of Graphene with Bisphenol A for High‐Performance Supercapacitors

The reduced graphene oxide (RGO)/bisphenol A (BPA) composites were prepared by an adsorption‐reduction method. The composites are characterized by X‐ray diffraction (XRD), UV‐vis, thermogravimetric (TG) analysis, field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM). The results confirm that BPA is adsorbed on the basal plane of RGO by π‐π stacking interaction. Furthermore, the electrochemical behaviors were evaluated by cyclic voltammetry, galvanostatic charge/discharge techniques and electrochemical impedance spectroscopy (EIS). The results show that the RGO/BPA nanocomposites exhibit ultrahigh specific capacitance of 466 F·g^?1 at a current density of 1 A·g^?1, excellent rate capability (more than 81% retention at 10 A·g^?1 relative to 1 A·g^?1) and superior cycling stability (90% capacitance decay after 4000 cycles). Consequently, the RGO/BPA nanocomposites can be regarded as promising electrode materials for supercapacitor applications.     

Influence of Fe‐MMT on crosslinking and thermal degradation in silicone rubber/clay nanocomposites

In this article, silicone rubber (SR)/clay nanocomposites were synthesized by a melt‐intercalation process using synthetic Fe‐montmorillonite (Fe‐MMT) and natural Na‐MMT which were modified by cetyltrimethyl ammonium bromide (CTAB). This study has been designed to determine if the presence of structural iron in the matrix can result in radical trapping and then enhance thermal stability, affect the crosslinking degree and elongation. The SR/clay nanocomposites were characterized by X‐ray diffraction (XRD) patterns and transmission electron microscopy (TEM). Exfoliated and intercalated nanocomposites were obtained. Thermo gravimetric analysis (TGA) and mechanical performance were applied to test the properties of the SR/clay nanocomposites. The presence of iron significantly increased the onset temperature of thermal degradation in SR/Fe‐MMT nanocomposites. The thermal stability, gel fraction and mechanical property of SR/Fe‐MMT were different from the SR/Na‐MMT nanocomposites. So the iron not only in thermal degradation but in the vulcanization process acted as an antioxidant and radicals trap. Copyright © 2006 John Wiley & Sons, Ltd.     

Analysis of structure–properties relationship in nitrile‐butadiene rubber/phenolic resin/organoclay ternary nanocomposites using simple model system

The present study deals with the structure–property relationship of organoclay (OC) filled nanocomposites based on rubber blend comprising of nitrile‐butadiene rubber (NBR) and phenolic resin (PH). To obtain a better insight into the characteristics of the NBR/PH/OC hybrid system, a simple model system consisting of NBR/OC nanocomposites is also taken into consideration. A series of NBR/OC and NBR/PH/OC nanocomposites containing a wide range of OC concentrations (2.5–30 phr) are prepared by using traditional open two‐roll mill. Structural analysis performed by X‐ray diffraction (XRD), scanning electron microscope (SEM), and transmission electron microscope (TEM) exhibits mixed exfoliated and intercalated morphology at low OC content, below 7.5 phr, and a well‐ordered intercalated morphology at higher OC loading. It is shown that the dispersion of OC is also influenced by mixing time and order of mixing of components. Analysis of the cure characteristics, mechanical, and thermal properties of both the NBR/OC and NBR/PH/OC nanocomposites reveals that the OC is dispersed mainly in the NBR continuous phase, even though some is likely localized in the rubber–resin interface. Copyright © 2009 John Wiley & Sons, Ltd.     

Studies of ABS-graft-maleic anhydride/clay nanocomposites: Morphologies, thermal stability and flammability properties

ABS-g-MAH (maleic anhydride) with different grafting degree, ABS/OMT (organo montmorillonite) and ABS-g-MAH/OMT nanocomposites were prepared via melt blending. The grafting reaction, phase morphology, clay dispersion, thermal properties, dynamic mechanical properties and flammability properties were investigated. FTIR spectra results indicate that maleic anhydride was successfully grafted onto butadiene chains of the ABS backbone in the molten state using dicumyl peroxide as the initiator and styrene as the comonomer and the relative grafting degree increased with increasing loading of MAH. TEM images show the size of the dispersed rubber domains of ABS-g-MAH increased and the dispersion is more uniform than that of neat ABS resin. XRD and TEM results show that intercalated/exfoliated structure formed in ABS-g-MAH/OMT nanocomposites and the rubber phase intercalated into clay layers distributed in both SAN phase and rubber phase. TGA results reveal the intercalated/exfoliated structure of ABS-g-MAH/OMT nanocomposites has better barrier properties and thermal stability than intercalated ones of ABS/OMT nanocomposites. The T_g of ABS-g-MAH/OMT nanocomposites was also higher than that of neat ABS/OMT nanocomposites. The results of cone measurements show that ABS-g-MAH/OMT nanocomposites exhibit significantly reduced flammability when compared to ABS/OMT nanocomposites even at the same clay content. The chars of ABS-g-MAH/OMT nanocomposites were tighter, denser, more integrated and fewer surface microcracks than ABS/OMT residues.     

Preparation and characterization of rigid poly(vinyl chloride)/MMT nanocomposites. II. XRD,morphological and mechanical characteristics

A Haake torque rheometer equipped with an internal mixer is used to study the influence of the amount of sodium montmorillonite (Na⁺‐MMT) and organically modified MMT (O‐MMT) on X‐ray diffraction (XRD), morphology, and mechanical characteristics of rigid poly (vinyl chloride) (PVC)/Na⁺‐MMT and PVC/O‐MMT nanocomposites, respectively. Results of XRD and transmission electron microscopy (TEM) indicate that MMT is partially encapsulated and intercalated in the rigid PVC/Na⁺‐MMT nanocomposites. However, results of XRD and TEM show MMT is partially intercalated and exfoliated in the rigid PVC/O‐MMT nanocomposites. Tensile strength, yield strength, and elongation at break of the rigid PVC/MMT nanocomposites were improved simultaneously with adding 1–3 wt % Na⁺‐MMT or O‐MMT with respect to that of pristine PVC. However, the addition of Na⁺‐MMT or O‐MMT should be kept as not more than 3 wt % to optimize the mechanical properties and the processing stability of the rigid PVC/MMT nanocomposites. SEM micrographs of the fractured surfaces of the rigid PVC/Na⁺‐MMT and PVC/O‐MMT nanocomposites both before and after tensile tests were also illustrated and compared. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2145–2154, 2006     

Fabrication of graphene‐silver/polyurethane nanofibrous scaffolds for cardiac tissue engineering

The graphene‐based nanocomposites are considered as great candidates for enhancing electrical and mechanical properties of nonconductive scaffolds in cardiac tissue engineering. In this study, reduced graphene oxide‐silver (rGO‐Ag) nanocomposites (1 and 2 wt%) were synthesized and incorporated into polyurethane (PU) nanofibers via electrospinning technique. Next, the human cardiac progenitor cells (hCPCs) were seed on these scaffolds for in vitro studies. The rGO‐Ag nanocomposites were studied by X‐ray diffraction (XRD), Raman spectroscopy, and transmission electron microscope (TEM). After incorporation of rGO‐Ag into PU nanofibers, the related characterizations were carried out including scanning electron microscope (SEM), TEM, water contact angle, and mechanical properties. Furthermore, PU and PU/nanocomposites scaffolds were used for in vitro studies, wherein hCPCs showed good cytocompatibility via 3‐(4, 5‐dimethylthiazol‐2‐yl)‐2,5‐diphenyl tetrazolium bromide (MTT) assay and considerable attachment on the scaffold using SEM studies. Real‐time polymerase chain reaction (PCR) and immunostaining studies confirmed the upregulation of cardiac specific genes including GATA‐4, T‐box 18 (TBX 18), cardiac troponin T (cTnT), and alpha‐myosin heavy chain (α‐MHC) in the PU/rGO‐Ag scaffolds in comparison with neat PU ones. Therefore, these nanofibrous rGO‐Ag–reinforced PU scaffolds can be considered as suitable candidates in cardiac tissue engineering.     

Biodegradable poly(p‐dioxanone) reinforced and toughened by organo‐modified vermiculite

Poly(p‐dioxanone) (PPDO)/vermiculite (VMT) nanocomposites with exfoliated structure were prepared successfully by in situ intercalative polymerization of p‐dioxanone (PDO) in the presence of organo‐modified vermiculite (OVMT) with the aid of ultrasonic action. The nano‐structure of the nanocomposites was established using X‐ray diffraction (XRD) analysis and transmission electron microscopy (TEM) observations. The investigation of crystallization behavior by differential scanning calorimetry (DSC) and polarized optical microscopy (POM) proved that exfoliated OVMT platelets acted as a template for spherulite growth. The thermal stability of nanocomposites was enhanced than that of pure PPDO. Dynamic mechanical analysis (DMA) indicated nanoscale OVMT platelets restricted the motion of PPDO segments, which benefitted the increase of storage and loss modulus. The tensile properties showed that nanocomposites were reinforced and toughened significantly by the addition of nanoscale OVMT platelets. Copyright © 2009 John Wiley & Sons, Ltd.     

Flow‐induced particle orientation and rheological properties of suspensions of organoclays in thermoplastic resins

The influence of nano‐scale particles on the viscoelastic properties of polymer suspensions is investigated. We have developed a simulation technique for the particle orientation and polymer conformation tensors to study various features of the suspensions. The nano‐particles are modeled as thin rigid oblate spheroid particles and the polymers as FENE‐P type viscoelastic and Newtonian fluid. Both interparticle and polymer‐particle interactions have been taken into account in our numerical computations. The nonlinear viscoelastic properties of nanocomposites of layered silicate particles in non‐Newtonian fluids are examined at the start‐up of shear flow and are interpreted using the model to examine the effects of model parameters as well as flow conditions on particle orientation, viscosity, and first normal stress difference of the suspensions. We have studied the microstructure of polymer‐clay nanocomposites using X‐ray diffraction (XRD) scattering and transmission electron microscopy (TEM). The rheology of these nanocomposites in step‐shear is shown to be fairly well predicted by the model. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 2003–2011, 2010     

Self‐Healing Polyester Urethane Supramolecular Elastomers Reinforced with Cellulose Nanocrystals for Biomedical Applications

Stretchable self‐healing urethane‐based biomaterials have always been crucial for biomedical applications; however, the strength is the main constraint of utilization of these healable materials. Here, a series of novel, healable, elastomeric, supramolecular polyester urethane nanocomposites of poly(1,8‐octanediol citrate) and hexamethylene diisocyanate reinforced with cellulose nanocrystals (CNCs) are introduced. Nanocomposites with various amounts of CNCs from 10 to 50 wt% are prepared using solvent casting technique followed by the evaluation of their microstructural features, mechanical properties, healability, and biocompatibility. The synthesized nanocomposites indicate significantly higher tensile modulus (approximately 36–500‐fold) in comparison to the supramolecular polymer alone. Upon exposure to heat, the materials can reheal, but nevertheless when the amount of CNC is greater than 10 wt%, the self‐healing ability of nanocomposites is deteriorated. These materials are capable of rebonding ruptured parts and fully restoring their mechanical properties. In vitro cytotoxicity test of the nanocomposites using human dermal fibroblasts confirms their good cytocompatibility. The optimized structure, self‐healing attributes, and noncytotoxicity make these nanocomposites highly promising for tissue engineering and other biomedical applications.