Preparation and properties of new poly(amide‐imide)s based on 1,4‐bis(4‐trimellitimidophenoxy)naphthalene and aromatic diamines

A diimide dicarboxylic acid, 1,4‐bis(4‐trimellitimidophenoxy)naphthalene (1,4‐BTMPN), was prepared by condensation of 1,4‐bis(4‐aminophenoxy)naphthalene and trimellitic anhydride at a 1 : 2 molar ratio. A series of novel poly(amide‐imide)s (IIa–k) with inherent viscosities of 0.72 to 1.59 dL/g were prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid 1,4‐BTMPN with various aromatic diamines (Ia–k) in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. The poly(amide‐imide)s showed good solubility in NMP, N,N‐dimethylacetamide, and N,N‐dimethylformamide. The thermal properties of the obtained poly(amide‐imide)s were examined with differential scanning calorimetry and thermogravimetry analysis. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures in the range of 215 to 263°C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses at temperatures in the range of 538 to 569°C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s also is presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1–8, 2000     

Synthesis and characterization of new soluble poly(amide‐imide)s derived from 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane

A series of new soluble poly(amide‐imide)s were prepared from the diimide‐dicarboxylic acid 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane with various diamines by direct polycondensation in N‐methyl‐2‐pyrrolidinone containing CaCl₂ with triphenyl phosphite and pyridine as condensing agents. All the polymers were obtained in quantitative yields with inherent viscosities of 0.52–0.86 dL · g^?1. The poly(amide‐imide)s showed an amorphous nature and were readily soluble in various solvents, such as N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide (DMAc), N,N‐dimethylformamide, pyridine, and cyclohexanone. Tough and flexible films were obtained through casting from DMAc solutions. These polymer films had tensile strengths of 71–107 MPa and a tensile modulus range of 1.6–2.7 GPa. The glass‐transition temperatures of the polymers were determined by a differential scanning calorimetry method, and they ranged from 242 to 279 °C. These polymers were fairly stable up to a temperature around or above 400 °C, and they lost 10% of their weight from 480 to 536 °C and 486 to 537 °C in nitrogen and air, respectively. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3498–3504, 2001     

Heat stable and organosoluble benzoxazole or benzothiazole-containing poly(imide-ester)s and poly(etherimide-ester)s: synthesis and characterization

Two series of poly(imide-ester)s (PIEs) and poly(ether-imide-ester)s (PEIEs), having benzoxazole or benzothiazole pendent groups, were conveniently prepared by the diphenylchlorophosphate-activated direct polyesterification of two bis(imide-carboxylic acid)s (1), such as 2-[3,5-bis(N-trimellitimidoyl)phenyl]benzoxazole (1 _O ) and 2-[3,5-bis(Ntrimellitimidoyl) phenyl]benzothiazole (1 _S ) and two bis(imide-ether-carboxylic acid)s (2), such as 2-[3,5-bis(4-trimellitimidophenoxy)-phenyl]benzoxazole (2 _O ), and 2-[3,5-bis(4-trimellitimidophenoxy)-phenyl]benzothiazole (2 _S ) with various aromatic dihydroxy compounds in the presence of pyridine and lithium chloride. The structures, solubilities and thermal properties of obtained polymers were investigated in detail. All of the resulting polymers were characterized by FTIR and ¹H-NMR spectroscopy and elemental analysis. All of the resulting polymers exhibited excellent solubility in common organic solvents, such as pyridine, tetrahydrofuran and m-cresol, as well as in polar organic solvents, such as N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide and dimethyl sulfoxide. The modified polymers were obtained in quantitative yields with inherent viscosities between 0.47 and 0.67 dl·g^?1. Experimental results indicated that all the polymers had glass transition temperature between 198 °C and 262 °C, the decomposition temperature at 10% weight loss between 398 °C and 531 °C under nitrogen.     

Synthesis and properties of organosoluble poly(amide‐imide)s with propeller‐shaped 1,1,1‐triphenylethane units in the main chain

A dicarboxylic acid {1,1‐bis[4‐(4‐trimellitimidophenoxy)phenyl]‐1‐phenylethane ( II )} bearing two performed imide rings was prepared from the condensation of 1,1‐bis[4‐(4‐aminophenoxy)phenyl]‐1‐phenylethane and trimellitic anhydride in a 1/2 molar ratio. A novel family of poly(amide‐imide)s with inherent viscosities of 0.83–1.51 dL/g was prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid II with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. Because the 1,1,1‐triphenylethane group of II was unsymmetrical, most of the resulting polymers showed an amorphous nature and were readily soluble in polar solvents such as NMP and N,N‐dimethylacetamide. All the soluble poly(amide‐imide)s afforded tough, transparent, and flexible films, which had tensile strengths ranging from 88 to 102 MPa, elongations at break from 6 to 11%, and initial moduli from 2.23 to 2.71 GPa. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures from 250 to 287 °C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses from 501 to 534 °C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s is also presented. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 775–787, 2001     

Soluble poly(amide–imide)s prepared by one‐pot solution condensation

A new one‐pot procedure for imide–acid monomer synthesis and polymerization is reported for four new poly(amide–imide)s. Bisphenol A dianhydride (BPADA) was reacted with twice the molar amount of 3‐aminobenzoic acid (3ABA) or 3‐amino‐4‐methylbenzoic acid (3A4MBA) in 1‐methyl‐2‐pyrrolidinone (NMP) and toluene mixture, and the amic acid intermediates cyclized in solution to give two diimide‐containing dicarboxylic acid monomers. Without isolation, the diacid monomers were then polymerized with either 1,3‐diaminomesitylene (DAM) or 1,5‐diaminonaphthalene (1,5NAPda) using triphenyl phosphite‐activation to give a series of four soluble poly(amide–imide)s, PAI. Isolation and purification of the dicarboxylic acid monomers was not necessary for formation of high molecular weight polymers as indicated by intrinsic viscosities of 0.64–1.04 dL/g determined in N,N‐dimethylacetamide (DMAc). All of the PAI were soluble in polar aprotic solvents such as NMP, DMAc, and dimethyl sulfoxide (DMSO). Glass transition temperatures ranged from 243 to 279°C by DSC, and 5% weight loss temperatures were above 400°C in both air and nitrogen. Flexible films cast from DMAc were light yellow, transparent, and tough. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1183–1188, 1999     

Partially bio‐based poly(amide imide)s by polycondensation of aromatic diacylhydrazides based on lignin‐derived phenolic acids and aromatic dianhydrides: Synthesis,characterization, and computational studies

Two new bio‐based diacylhydrazide monomers, namely, 4,4′‐(propane‐1,3‐diylbis(oxy))bis(3‐methoxybenzohydrazide) and 4,4′‐(propane‐1,3‐diylbis(oxy))bis(3,5‐dimethoxybenzohydrazide) were synthesized starting from lignin‐derived phenolic acids, namely, vanillic acid and syringic acid. A series of poly(amide imide)s was synthesized by polycondensation of these diacylhydrazide monomers with commercially available aromatic dianhydrides. Poly(amide imide)s showed inherent viscosity in the range 0.44–0.56 dL g^?1 and exhibited good solubility in organic solvents. Poly(amide imide)s could be cast into transparent, flexible, and tough films from their N ,N‐dimethylacetamide solutions. Poly(amide imide)s showed 10% weight loss in the temperature range 340–364 °C indicating their good thermal stability. Glass transition temperature (T _g) of poly(amide imides)s were measured by DSC and DMA which were in the range 201–223 °C and 214–248 °C, respectively. The T _g values of poly(amide imide)s were dependent on the number methoxy substituents on aromatic rings of diacylhydrazide monomers. Molecular dynamics simulation studies revealed that chain rigidity is the dominant factor for observed trends in T _g. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 3636–3645     

New poly(amide–imide)s syntheses. XXIII. Synthesis and properties of poly(amide–imide)s derived from 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline and various bis(trimellitimide)s

A series of poly(amide–imide)s III_a–m containing flexible isopropylidene and ether groups in the backbone were synthesized by the direct polycondensation of 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline (PIDA) with various bis(trimellitimide)s II_a–m in N‐methyl‐2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents. The resulting poly(amide–imide)s had inherent viscosities in the range of 0.80–1.36 dL/g. Except for those from the bis(trimellitimide)s of p‐phenylenediamine and benzidine, all the polymers could be cast from DMAc into transparent and tough films. They exhibited excellent solubility in polar solvents. The 10% weight loss temperatures of the polymers in air and in nitrogen were all above 495°C, and their T_g values were in the range of 201–252°C. Some properties of poly(amide–imide)s III were compared with those of the corresponding poly(amide–imide)s V prepared from the bis(trimellitimide) of diamine PIDA and various aromatic diamines. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 69–76, 1999     

Synthesis and characterization of new poly(amide–imide)s from 1,4-bis(4-trimellitimidophenoxy)-2-tert-butylbenzene with various diamines

New poly(amide–imide)s were prepared from a diimide–dicarboxylic acid, 1,4-bis(4-trimellitimidophenoxy)-2-tert-butylbenzene ( BTTB ), with various diamines by the direct polycondensation in N-methyl-2-pyrrolidinone (NMP) using triphenyl phosphite and pyridine as condensing agents. The new diimide–dicarboxylic acid BTTB containing an ether linkage and tert-butyl substituent was synthesized by the condensation reaction of 1,4-bis(4-aminophenoxy)-2-tert-butylbenzene with trimellitic anhydride. All the polymers were obtained in quantitative yields with inherent viscosities of 0.62–1.06 dL g⁻¹. The polymers were amorphous, and most of them were readily soluble in aprotic polar solvents such as NMP, N,N-dimethylacetamide (DMAc), and N,N-dimethylformamide (DMF), as well as in less polar solvents such as dimethyl sulfoxide (DMSO), m-cresol, pyridine, and γ-butyrolactone, and also even in tetrahydrofuran. The glass transition temperatures of the polymers were determined by DSC method, and they were in the range of 238–279°C. These polymers were stable up to 408–449°C in air and 451–483°C in nitrogen and lose 10% weight in the range of 479–525°C in air and 480–528°C in nitrogen atmosphere. The polymer films had a tensile strength range of 71–115 MPa, an elongation at break range of 4–14%, and a tensile modulus range of 2.3–3.1 GPa. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2301–2307, 1998     

Synthesis and characterization of novel aromatic poly(imide–benzoxazole) copolymers

New poly(imide–benzoxazole) copolymers were prepared directly from a dianhydride, a diacid chloride, and a bis(o‐diaminophenol) monomer in a two‐step method. In the first step, poly(amic acid–hydroxyamide) precursors were synthesized by low‐temperature solution polymerization in an organic solvent. Subsequently, the thermal cyclodehydration of the poly(amic acid–hydroxyamide) precursors at 350 °C produced the corresponding poly(imide–benzoxazole) copolymers. The inherent viscosities of the precursor polymers were around 0.19–0.33 dL/g. The cyclized poly(imide–benzoxazole) copolymers had glass‐transition temperatures in the range of 331–377 °C. The 5% weight loss temperatures ranged from 524 to 535 °C in nitrogen and from 500 to 514 °C in air. The poly(imide–benzoxazole) copolymers were amorphous, as evidenced by the wide‐angle X‐ray diffraction measurements. The structures of the precursor copolymers and the fully cyclized copolymers were characterized by Fourier transform infrared, ¹H NMR, and elemental analysis. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 6020–6027, 2005     

Thiol–ene polymerizations using imide‐based monomers

New diene and dithiol monomers, based on aromatic imides such as benzophenone‐3,3′,4,4′‐tetracarboxylic diimide were synthesized and used in thiol‐ene polymerizations which yield poly(imide‐co‐thioether)s. These linear polymers exhibit limited solubility in various organic solvents. The molecular weights of the polymers were found to decrease with increasing imide content. The glass transition temperature (T_g) of these polymers is dependent on imide content, with T_g values ranging from ?55 °C (with no imide) up to 13 °C (with 70% imide). These thermal property improvements are due to the H‐bonding and rigidity of the aromatic imide moieties. Thermal degradation, as studied by thermogravimetric analysis, was not significantly different to the nonimide containing thiol‐ene polymers made using trimethyloylpropane diallyl ether and 3,5‐dioxa‐1,8‐dithiooctane. It is expected that such monomers may lead to increased glass transition temperatures in other thiol‐ene polymer systems as these normally exhibit low glass transition temperatures. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4637–4642     

Synthesis and properties of novel aromatic polyhydrazides and poly(amide–hydrazide)s based on the bis(ether benzoic acid)s from hydroquinone and substituted hydroquinones

4,4′‐(1,4‐Phenylenedioxy)dibenzoic acid as well as the 2‐methyl‐, 2‐tert‐butyl‐, or 2‐phenyl‐substituted derivatives of this dicarboxylic acid were synthesized in two main steps from p‐fluorobenzonitrile and hydroquinone or its methyl‐, tert‐butyl‐, or phenyl‐substituted derivatives. Polyhydrazides and poly(amide–hydrazide)s were prepared from these bis(ether benzoic acid)s or their diacyl chlorides with terephthalic dihydrazide, isophthalic dihydrazide, or p‐aminobenzoyl hydrazide by means of the phosphorylation reaction or low‐temperature solution polycondensation. Most of the hydrazide polymers and copolymers are amorphous and readily soluble in various polar solvents such as N‐methyl‐2‐pyrrolidone (NMP) and dimethyl sulfoxide. They could be solution‐cast into transparent, flexible, and tough films. These polyhydrazides and poly(amide–hydrazide)s had T_gs in the range of 167–237°C and could be thermally cyclodehydrated into the corresponding poly(1,3,4‐oxadiazole)s and poly(amide–1,3,4‐oxadiazole)s approximately in the region of 250–350°C, as evidenced by the DSC thermograms. All the tert‐butyl‐substituted oxadiazole polymers and those derived from isophthalic dihydrazide were organic soluble. The thermally converted oxadiazole polymers exhibited T_gs in the range of 208–243°C and did not show significant weight loss before 450°C either in nitrogen or in air. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1169–1181, 1999     

Thermally stable and organosoluble binaphthylene‐based poly(urea‐ether‐imide)s: one‐pot preparation and characterization

A new family of wholly aromatic poly(urea‐ether‐imide)s ( 4a–4f ) possessing binaphthylene‐twisted rings was prepared by diphenyl azidophosphate (DPAP)‐activated one‐pot polyaddition reaction of a preformed imide heterocyclic ring‐containing dicarboxylic acid, 2,2′‐bis(4‐trimellitimidophenoxy)‐ 1,1′‐binaphthyl ( 1 ) with various kinds of aromatic diamines ( 3a–3f ). At first, with due attention to structural similarity and to compare the characterization data, a model compound 2 was synthesized by the reaction of diimide‐dicarboxylic acid 1 with two mole equivalents of aniline. In this direct method, the polymers were prepared by polyaddition reactions of the in situ‐formed diisocyanate with the aromatic diamines. Molecular weights of the poly(urea‐ether‐imide)s obtained were evaluated viscometrically, and the inherent viscosities (η_inh) measured were in the range 0.10– 0.25 dl/g. All of the polymers were characterized by FT‐IR spectroscopic method and elemental analysis. All of the resulting polymers exhibited an excellent solubility in common polar solvents such as N‐methyl‐2‐pyrrolidone (NMP), dimethyl sulfoxide (DMSO), N,N‐dimethylformamide (DMF), and N,N‐dimethylacetamide (DMAc). Crystallinity of the resulted polymers was evaluated by wide‐angle X‐ray diffraction (WXRD) method, and they exhibited nearly a non‐crystalline nature as evidenced by their diffractograms. The glass transition temperatures (T_g) of the polymers determined by differential scanning calorimetry (DSC) thermograms were in the range of 274–302°C. The temperatures at 10% weight loss (T_d10%) from their thermogravimetric analysis (TGA/DTG) curves were found to be in the range of 389–414°C in nitrogen atmosphere. Copyright © 2008 John Wiley & Sons, Ltd.     

Synthesis and properties of soluble and light‐colored poly(amide‐imide‐imide)s on the basis of tetraimide‐dicarboxylic acid condensed from 4,4′‐oxydiphthalic anhydride, 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane,and m‐aminobenzoic acid,and various aromatic diamines

A new type of tetraimide‐dicarboxylic acid ( I ) was synthesized starting from the ring‐opening addition of m‐aminobenzoic acid, 4,4′‐oxydiphthalic anhydride, and 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane at a 2:2:1 molar ratio in N‐methyl‐2‐pyrrolidone (NMP), followed by cyclodehydration to the diacid I . A series of soluble and light‐colored poly(amide‐imide‐imide)s ( III _a–j) was prepared by triphenyl phosphite‐activated polycondensation from I with various aromatic diamines ( II _a–j). All films cast from N,N‐dimethylacetamide (DMAc) had cutoff wavelengths shorter than 390 nm (374–390 nm) and b* values between 25.26 and 43.61; these polymers were much lighter in color than the alternating trimellitimide series. All of the polymers were readily soluble in a variety of organic solvents such as NMP, DMAc, N,N‐dimethylformamide, dimethyl sulfoxide, and even in less polar m‐cresol and pyridine. Polymers III _a–j afforded tough, transparent, and flexible films that had tensile strengths ranging from 96 to 118 MPa, elongations at break from 9 to 11%, and initial moduli from 2.0 to 2.5 GPa. The glass‐transition temperatures of the polymers were recorded at 240–268 °C. They had 10% weight loss at a temperature above 540 °C and left more than 55% residue even at 800 °C in nitrogen. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 707–718, 2002; DOI 10.1002/pola.10153     

Fluorinated polyamides and poly(amide imide)s based on 1,4‐bis(4‐amino‐2‐trifluromethylphenoxy)benzene,aromatic dicarboxylic acids,and various monotrimellitimides and bistrimellitimides: Syntheses and properties

A CF₃‐containing diamine, 1,4‐bis(4‐amino‐2‐trifluromethylphenoxy) benzene ( I ), was prepared from hydroquinone and 2‐chloro‐5‐nitrobenzotrifluoride. Imide‐containing diacids ( V _a–h and VI _a,b ) were prepared through the condensation reaction of amino acids, aromatic diamines, and trimellitic anhydride. Then, a series of soluble fluorinated polyamides ( VII _a–h ) and poly(amide imide)s ( VIII _a–h and X _a,b ) were synthesized from I with various aromatic diacids ( II _a–h ) and imide‐containing diacids ( V _a–h and VI _a,b ) via direct polycondensation with triphenyl phosphate and pyridine. The polyamides and poly(amide imide)s had inherent viscosities of 1.00–1.70 and 0.79–1.34 dL/g, respectively. All the synthesized polymers showed excellent solubility in amide‐type solvents such as N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide, and N‐dimethylformamide and afforded transparent and tough films via solvent casting. Polymer films of VII _a–h , VIII _a–h , and X _a,b had tensile strengths of 91–113 MPa, elongations to break of 8–40%, and initial moduli of 2.1–2.8 GPa. The glass‐transition temperatures of the polyamides and poly(amide imide)s were 254–276 and 255–292 °C, respectively, and the imide‐containing poly(amide imide)s had better thermal stability than the polyamides. The polyamides showed higher transparency and were much lighter in color than the poly(amide imide)s, and their cutoff wave numbers were below 400 nm. In comparison with isomeric IX _{c – h} , poly(amide imide)s VIII _c–h exhibited less coloring and showed lower yellowness indices. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3116–3129, 2004     

Preparation and characterization of thermally stable poly(amide‐urea)s functionalized with anthraquinone chromophore

Two new diamines containing bulky anthraquinone pendant units were prepared via reactions of 1‐ and 2‐aminoanthraquinone with 3,5‐dinitrobenzoylchloride and a subsequent reduction of their nitro groups. A novel series of highly organosoluble poly(amide‐urea)s were synthesized from the reactions of the prepared diamines with various commercially available diisocyanates via a step‐growth addition reaction process in N‐methyl‐2‐pyrrolidone (NMP). The effects of two factors (time and temperature) on the reaction were studied to optimize the conditions for the preparation of high molecular weight polymers. All poly(amide‐urea)s were characterized by Fourier Transform Infrared (FTIR) and ¹H‐nuclear magnetic resonance (NMR) spectroscopies and elemental analysis. The resulting poly(amide‐urea)s had inherent viscosities in the range of 0.54–0.73 dl/g. They exhibited excellent solubility in polar solvents. The temperature for 10% weight loss of the polymers in air was all above 285°C, their residues were more than 36% at 700°C in air, and their T_g values were in the range of 148–190°C. According to the wide‐angle X‐ray diffraction (WAXD), the polymers were almost amorphous. The optical properties of poly(amide‐urea)s measured by ultraviolet–visible (UV–Vis) spectroscopy showed absorption maxima at 303–429 nm. Copyright © 2008 John Wiley & Sons, Ltd.     

New poly(amide-imide) syntheses. V. Preparation and properties of poly(amide-imide)s based on the diimide—diacid condensed from 2,2-bis[4-(4-aminophenoxy)phenyl]propane and trimellitic anhydride

A dicarboxylic acid ( 1 ) bearing two pre-formed imide rings, was prepared from the condensation of 2,2-bis[4-(4-aminophenoxy)phenyl]propane and trimellitic anhydride. A new family of poly(amide-imide)s having inherent viscosities of 0.53–1.68 dL/g was prepared by the triphenyl phosphite activated polycondensation from the diimide—diacid I with various aromatic diamines in a medium consisting of N-methyl-2-pyrolidone (NMP), pyridine, and calcium chloride. Most of the resulting polymers showed an amorphous nature and were readily soluble in polar solvents such as NMP and N,N-dimethylacetamide. All the soluble poly(amide-imide)s afforded transparent, flexible, and tough films. The glass transition temperatures of these poly(amide-imide)s were in the range of 237–293°C and the 10% weight loss temperatures were above 508°C in nitrogen. © 1993 John Wiley & Sons, Inc.     

Novel method for preparation of poly(benzoxazinone‐imide)

A novel method was developed to prepare poly(benzoxazinone‐imide) by the dealcoholization of poly(amide‐imide), having pendent ethoxycarbonyl groups, which was prepared from poly(amide acid). The poly(amide acid) was prepared from the reaction of pyromellitic dianhydride and 4,4′‐diamino‐6‐ethoxycarbonyl benzanilide. The curing behavior of the poly(amide acid) was monitored by DSC, which indicated the presence of two broad endotherms, one with maximum at 153 °C due to imide‐ring formation and the other with maximum at 359 °C due to benzoxazinone‐ring formation. The poly(amide acid) was thermally treated at 300 °C/1 h to get poly(amide‐imide) with pendent ester groups, then at 350 °C/2 h to convert into poly(benzoxazinone‐imide) by dealcoholization. Viscoelastic measurements of the poly(amide‐imide) showed that the storage modulus dropped at about 280 °C with glass‐transition temperature (T_g ) at about 340 °C. The storage modulus of poly(benzoxazinone‐imide), however, was almost constant up to 400 °C and no T_g was detected below 400 °C. Also, the tensile modulus and tensile strength of the poly(benzoxazinone‐imide) was much higher than that of the poly(amide‐imide). The 5% decomposition of poly(benzoxazinone‐imide) film was at 535 °C, which reflects its excellent thermal stability. Also, poly(benzoxazinone‐imide) showed more hydrolytic stability against alkali in comparison to polyimides. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1647–1655, 2000     

New poly(amide–imide) syntheses. XXI. Synthesis and properties of aromatic poly(amide–imide)s based on 2,6-bis(4-trimellitimidophenoxy)naphthalene and aromatic diamines

A novel polymer-forming diimide–diacid, 2,6-bis(4-trimellitimidophenoxy)naphthalene, was prepared by the condensation reaction of 2,6-bis(4-aminophenoxy)naphthalene with trimellitic anhydride (TMA). A series of novel aromatic poly(amide–imide)s containing 2,6-bis(phenoxy)naphthalene units were prepared by the direct polycondensation of the diimide–diacid with various aromatic diamines using triphenyl phosphite (TPP) in N-methyl-2-pyrrolidone (NMP)/pyridine solution containing dissolved calcium chloride. Thirteen of the obtained polymers had inherent viscosities above 1.01 dL/g and up to 2.30 dL/g. Most of polymers were soluble in polar solvents such as DMAc and could be cast from their DMAc solutions into transparent, flexible, and tough films. These films had tensile strengths of 79–117 MPa, elongation-at-break of 7–61%, and initial moduli of 2.2–3.0 GPa. The wide-angle X-ray diffraction revealed that some polymers are partially crystalline. The glass transition temperatures of some polymers could be determined with the help of differential scanning calorimetry (DSC) traces, which were recorded in the range 232–300°C. All the poly(amide–imide)s exhibited no appreciable decomposition below 450°C, and their 10% weight loss temperatures were recorded in the range 511–577°C in nitrogen and 497–601°C in air. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 919–927, 1998     

Synthesis and properties of organosoluble poly(amide imide imide)s based on tetraimide dicarboxylic acid condensed from 4,4′‐(hexafluoroisopropylidene)diphthalic anhydride, 4,4′‐oxydianiline,and trimellitic anhydride and various aromatic diamines

A novel tetraimide dicarboxylic acid was synthesized with the ring‐opening addition of 4,4′‐(hexafluoroisopropylidene)diphthalic anhydride, 4,4′‐oxydianiline, and trimellitic anhydride in a 1/2/2 molar ratio in N‐methyl‐2‐pyrrolidone followed by azeotropic condensation to tetraimide dicarboxylic acid. A series of poly(amide imide imide)s (PAIIs) with inherent viscosities of 0.8–1.1 dL/g were prepared from tetraimide dicarboxylic acid with various aromatic diamines by direct polycondensation. Most of the PAIIs were readily soluble in a variety of amide polar solvents and even in less polar m‐cresol and pyridine. Solvent‐cast films had tensile strengths ranging from 99 to 106 MPa, elongations at break ranging from 8 to 13%, and initial moduli ranging from 2.0 to 2.3 GPa. The glass‐transition temperatures of these PAIIs were recorded at 244–276 °C. They had 10% weight losses at temperatures above 520 °C in air or nitrogen atmospheres. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1092–1102, 2002     

Synthesis and properties of new aromatic poly‐(ether benzoxazole)s from 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl and aromatic dicarboxylic acid chlorides

A new bis(o‐aminophenol) with a crank and twisted noncoplanar structure and ether linkages, 2,2′‐bis(4‐amino‐3‐hydroxyphenoxy)biphenyl, was synthesized by the reaction of 2‐benzyloxy‐4‐fluoronitrobenzene with biphenyl‐2,2′‐diol, followed by reduction. Biphenyl‐2,2′‐diyl‐containing aromatic poly(ether benzoxazole)s with inherent viscosities of 0.52–1.01 dL/g were obtained by a conventional two‐step procedure involving the polycondensation of the bis(o‐aminophenol) monomer with various aromatic dicarboxylic acid chlorides, yielding precursor poly(ether o‐hydroxyamide)s, and subsequent thermal cyclodehydration. These new aromatic poly(ether benzoxazole)s were soluble in methanesulfonic acid, and some of them dissolved in m‐cresol. The aromatic poly(ether benzoxazole)s had glass‐transition temperatures of 190–251 °C and were stable up to 380 °C in nitrogen, with 10% weight losses being recorded above 520 °C. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2656–2662, 2002